US20040221614A1

US20040221614A1 - Shape memory device for changing shape at small temperature changes

Info

Publication number: US20040221614A1
Application number: US10/275,446
Authority: US
Inventors: Thierry Holemans; Rudy Stalmans
Original assignee: BARSAMIAN PHILIPPE
Current assignee: BARSAMIAN PHILIPPE
Priority date: 2001-03-08
Filing date: 2002-03-06
Publication date: 2004-11-11
Also published as: DE60204398D1; ATE296553T1; EP1286606A1; EP1238600A1; JP2004518509A; DE60204398T2; WO2002069750A1; CN1458831A; CN1226954C; EP1367918A1; EP1286606B1; WO2002069749A1; CN1458830A; ES2243720T3; GB0201720D0; JP2004518510A; US20040025984A1

Abstract

With the use of shape memory elements a series of devices can be made which change shape at small changes of the environmental temperature. The devices may be composed of a shape memory element and a bias element, in such a way that the thermal hysteresis of the device becomes lower than the intrinsic thermal hysteresis or the shape memory element. The devices may be used in jewelry that is adapted to change shape or configuration when subjected to temperatures in the region of the body of a wearer.

Description

FIELD OF THE INVENTION

The invention relates to devices incorporating shape memory elements, and to improvements therein, especially to the use with devices which are worn close to a living human or animal body or are located within such a body, such as jewelry, piercings or medical devices and implants.

BACKGROUND OF THE INVENTION

Materials, both organic and metallic, capable or possessing shape memory and/or superelasticity are well known. An article made of materials showing shape memory can be deformed from an original, heat-stable configuration to a second, heat-unstable configuration. The article is said to have shape memory for the reason that, upon the application of the heat alone, it can be caused to revert or attempt to revert from its heat-unstable configuration to its original heat-stable configuration, i.e., it “remembers” its original shape.

Among metallic alloys, the ability to possess shape memory is a result of the fact that the alloy undergoes a reversible transformation from an austenitic state to a martensitic state with a change of temperature. The transformation from the austenitic phase to the martensitic phase shows a temperature hysterisis, illustrated in FIG. 1. It follows that the transformation cannot be characterized by a single value of temperature, but has to be characterized by four temperatures: M _Sand M_F, respectively, A_Sand A_Fto indicate the temperatures at which the martensitic and the reverse martensitic transformation start and finish. Thus, an article made from such an alloy is easily deformed from its original configuration to a new configuration when cooled to a temperature below Mf. When an article thus deformed is warmed, the deformed object will return to its original configuration starting at As and finishing at Af. A shape memory material can be formed into a shape memory element (SME) which may be used to activate depending upon temperature. Many shape memory alloys (SMA) are known to show also superelasticity.

When an SMA sample exhibiting superelasticity is stressed at temperature above Af (so that the austenitic state is stable), but below Md (the maximum temperature at which martensitic formation can occur even under stress) it first deforms elastically and then, at a critical stress, begins to transform by the formation of stress-induced martensite. When the stress is released, the martensite becomes unstable and transforms back to austenite, with the sample returning to its original shape. Similarly, as the thermally induced transformation, the stress induced transformation shows a stress hysterisis.

Shape memory alloys can now be found in a wide range of applications and products that take advantage of the shape memory and superelastic properties. However the application of shape memory elements for actuation of devices is accompanied by several disadvantages, of which two are particularly relevant with respect to the presented invention.

Firstly, in many shape memory alloys there is a large hysteresis as the alloy is transformed between austenitic and martensitic states. Moreover, the transformation ranges, {A _S-A_F} and {M_S-M_F}, can be quite substantial. As a result, reversing of the state of an SMA element may require a temperature excursion of several tens of degrees Celsius, or a stress excursion of several hundreds of MPa. It follows that a temperature excursion of several tens of degrees (or hundreds of MPa) is required for activation and deactivation of a device incorporating shape memory elements. For example, the commercially available near equi-atomic binary nickel-titanium alloys can have a hysteresis width of about 40° C. The total transformation range {A_F-M_F} can be easily above 60° C. For example, if the activation temperature of a device to be worn such as jewelry would be close to body temperature (say 30 to 35° C.), the deactivation temperature would be below −20° C., which would limit the practical use of such a device. To remove the device would require immersion of the respective body part in a salt/ice mixture, in a deep freeze or similar which is not only impractical but also not very pleasant for the wearer of jewelry.

Second, it is difficult to control the transformation temperatures of shape memory alloys with accuracy as they are usually extremely composition- and processing-sensitive. The result is that the activation and deactivation temperatures of devices incorporating SMA-elements, are difficult to control.

The combination of these factors limits the practical application of devices actuated by shape memory elements in many fields. In many cases, it is desirable that the device can be actuated in a small temperature range and that the actuation temperatures can be easily controlled or more correctly accurately set.

It would thus be desirable to develop a way for easy control of the activation and deactivation temperatures of SMA devices and for decreasing the hysteresis and the transformation ranges. This is especially relevant for devices used in or close to a mammalian body.

One attempt to vary the shape of the hysteresis of a shape memory device is discussed in GB-2142724 in relation to Nitinol. In most currently available commercialized Nitinol alloys, two transformations usually occur:

an R-phase transformation with a thermal hysteresis of 2 to 5° C. and a maximum shear strain of about 1.5 to 2%; and

a martenisitic transformation with a thermal hysteresis of typically 20 to 30° C. and a maximum shear strain of over 10%.

In most shape memory applications, the martensitic transformation is used as the basis of the shape memory element. This is because the much higher shear strains that can be obtained enable higher deflections to be achieved. The R-phase transformation is often considered an anomaly because it is less useful due to the intrinsically low shear strain. In most cases, this R-phase transformation will precede the martensitic transformation by some way, e.g. to about 30° C. during cooling, but may coincide during heating. This proximity in temperature makes it difficult to use only the R-phase transformation for practical applications, although GB-2142724 proposes the use of a reversible R-phase transformation in Nitinol for actuator applications.

Use of bias elements is known in proposals for altering the activation temperature of devices incorporating shape memory elements, as discussed for example in U.S. Pat. No. 5,261,597 and U.S. Pat. No. 4,523,605. In these cases, the use of a bias element slightly alters the hysteresis, but still leaves a difference of some tens of degrees centigrade between activation and deactivation temperatures. For example, in U.S. Pat. No. 4,523,605 even with the use of a mechanical bias, the temperature hysteresis of a complete transformation in Nitinol is still likely to exceed 20° C.

It is known to use shape memory materials in jewelry and examples of some current proposals may be found in DE-19934312, EP-0313070 and U.S. Pat. No. 6,183,490.

In DE-19934312 a shape memory material is used in a super-elastic state to hold decorative pieces for display. The super elastic properties are used in particular to allow bending or flexing of the jewelry with good quality return to original shape having no work hardening or residual creases or similar from the deformation. The items displayed may be varied but, after having been configured and put on, the jewelry looks the same unless and until manually reconfigured to hold a different display.

In EP-031070 jewelry bands such as rings or bracelets are formed from overlapping wound sections of shape memory wire. These bands may carry ornamentation and use shape memory material in a super-elastic state so as to retain shape whilst being worn, temperature changes not being necessary for fitting, wearing or removal. Once it has been put on, in similar fashion to DE-19934312, the jewelry of EP-0313070 acts as a static display. Although it may be temporarily deformed during fitting, this jewelry uses only the super-elastic properties of shape memory material and then only for its configuration into a condition suitable for being worn and for shape retention. It will be noted that the gauge of wire used in this arrangement is quite thin (e.g. 0.7 mm diameter) and that the bands can be expanded for fitting using a low force. Removal of this low force allows the bands to return towards their original shape, which in free space they should achieve. Since only a low force is required to open the super elastic element, the jewelry can be worn by people having different sizes or body part, e.g. finger or wrist. In the event that a body part such as a finger/wrist is thicker than the inner diameter of the ring/bracelet, then the super elastic element will only exert a gentle pressure on that body part due to the thin gauge of the constituent shape memory wire.

In U.S. Pat. No. 6,183,490 a stud arrangement is disclosed for keeping a body piercing open after initial formation. In this arrangement, a projection from the back of the stud deforms inside a captive member behind the earlobe so as to invisibly capture the stud in place. The shape memory material is used only to provide mechanical holding properties and is only one embodiment amongst the holding means discussed.

In the world of jewelry, it is a continuous problem to seek expressions of fashion and style that are appealing to the wearer and it is an object of the present invention to provide improved jewelry arrangements. It is another object of the present invention to provide improved jewelry arrangements that incorporate an element formed from a shape memory material, such as a shape memory alloy. It is also an object of the present invention to provide an improved method of producing such jewelry.

SUMMARY OF THE INVENTION

In one aspect of the present invention includes a device incorporating at least one shape memory element is provided offering (i) a substantially decreased temperature range between the activation and deactivation temperature and (ii) an easy method for control of the activation and deactivation temperatures. Specific shape memory alloys show a small hysteresis and a small transformation range. By integrating SMA elements made of such low hysteresis alloys into the said devices, an improved device results. The alloys may be metal alloys.

The present invention may provide a device comprising a shape memory element and a bias element, the shape memory element and the bias element co-operating together to provide the device with an activation temperature and a deactivation temperature, wherein the difference between the activation temperature T _Aand the deactivation temperature T_Dis 10° C. or less, preferably 7° C. or less or most preferably 5° C. or less. The bias element may co-operate with the shape memory element so that the stress on the shape memory element is lower in the activated state compared to the deactivated state resulting in a lowering of the transformation range of the device compared to the transformation range of the shape memory element alone. The stress may be a bending stress. The device may also comprise a blocking element so that said shape memory element has a restricted movement, resulting in a lowering of the transformation range of the device. The shape memory element and the bias element may be adapted so that the shape memory element buckles under the action of the bias element, resulting in a lowering of the transformation range of the device. The shape memory element and the bias element may be adapted so that the bias element buckles under the action of the shape memory element, resulting in a lowering of the transformation range of the device. The transformation range of the device may be such that when placed in a thermal gradient the device is repeatedly activated and deactivated. The device preferably exhibits a thermal hysteresis with a deactivation temperature in the range 20 to 32° C. The device may have an activation temperature in the range 25° C. to 35° C. Any such devices are preferably included in a piece of jewelry such as a necklace or a bracelet or brooch.

The present invention also provides a piece of jewelry including a plurality of parts which are adapted for relative movement between each other so as to vary an externally visible shape or configuration of said jewelry, said jewelry further comprising a shape memory element and a bias element adapted to co-operate so as to cause said relative movement, said shape memory element exhibiting a thermal hysteresis having upper and lower temperature transformation ranges, said upper temperature transformation comprising a range of 10° C. or less, preferably 7° C. or less and more preferably 5° C. or less.

Said shape memory element may have an upper transformation start temperature A _Sin the range 18 to 25° C. Said shape memory element may have an upper transformation finish temperature A_Fin the range 23° C. to 30° C.

Said parts may be adapted to cycle automatically between at least two different said externally visible shapes or configurations. Said parts may be adapted to move or cycle automatically between different said shapes or configurations when said piece of jewelry is located in the region of a wearer's body.

Said jewelry piece may comprise a broach or a necklace and said relative movement may be adapted to move or cycle said parts between an externally visible closed or folded shape or configuration and an externally visible open shape or configuration. Said shape memory element and said bias element may comprise a device according to the present invention.

Accordingly, this invention provides improved devices with a very low temperature difference between the activation and deactivation temperature and with easily controllable activation and deactivation temperatures.

The invention will now be described with reference to the following drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a schematic illustration of a property change (such as length) versus temperature for a shape memory element. The hysteresis, the activation temperature T[0028] _A, the deactivation temperature T_Dand the transformation temperatures M_S, M_F, A_S, A_Fare indicated.
FIG. 2 shows the effect of a bias force schematically. The property P is shown versus temperature T. By applying a higher bias force, the transformation temperatures will shift to higher temperatures. [0029]
FIG. 3 shows an embodiment of the present invention—the use of partial transformation to reduce hysteresis. The movement from [0030] position 1 to position 2 and vice versa involves only a partial transformation. The difference between the activation temperature T_Aand the deactivation temperature T_Dbecomes lower due to this partial transformation.
FIG. 4 is an illustration of the effects of different biasing systems on the transformation ranges. [0031]
FIGS. 5[0032] a and b show two states of a device in accordance with an embodiment of the present invention using a snap mechanism.
FIG. 5[0033] c show the hysteresis loop for the devices shown in FIGS. 5a and b when placed close to a heat source indicating cyclic behavior.
FIGS. 5[0034] d to 5 i show alternative embodiments of the present invention all having a lower stress in the shape memory element in the activated state.
FIGS. 6[0035] a and b show two states of a device in accordance with an embodiment of the present invention not using a snap mechanism.
FIG. 6[0036] c show the hysteresis loop for the devices shown in FIGS. 5a and b when placed close to a heat source showing two semi-stable positions P1 and P2.
FIGS. 7[0037] a and b show two states of a brooch in accordance with an embodiment of the present invention.
FIGS. 7[0038] c and d show the two states of the activating devices for the brooch of FIGS. 7a and b.
FIG. 8[0039] a shows a necklace having moveable flowers in accordance with an embodiment of the present invention.
FIGS. 8[0040] b and c show the two states of the activating device for the necklace of FIG. 8a which activate cyclically when placed in a temperature gradient.

DETAILED DESCRIPTION OF THE ILLUSTRATIVE EMBODIMENTS

The present invention will be described with respect to certain embodiments and drawings but the present invention is not limited thereto but only by the claims. Although, allowance is granted for the publication of this patent application all rights such as copyright or design rights especially of the jewelry shown in the drawings is maintained with reference to other third parties. [0041]
The present invention will be discussed by describing in detail the hysteresis and the transformation ranges of the shape memory element, and how the difference between the activation and deactivation temperature of the device can be lowered. In accordance with an aspect of the present invention the difference between T[0042] _Aand T_Dis 10° C. or less, preferably 7° C. or less, most preferably 5° C. or less. The following methods, optionally in combination can achieve these levels. An additional advantage of the presented embodiments is that they result in a very compact design. This is of critical importance in the design of jewelry where any moving parts must be so small that they do not disturb the aesthetic appearance of the piece.
The transformation Range of a Shape Memory Element: use of Shape Memory Alloys with a Low Hysteresis. [0043]
Shape memory alloys exhibit a hysteresis between the forward and reverse transformation, as shown in FIG. 1. Accordingly, devices actuated by shape memory elements, will exhibit a temperature hysteresis between a forward and reverse shape change which may be defined as a difference of temperature, e.g. at the center or midline (horizontal) of the hysteresis curve shown in FIG. 1. The intrinsic hysteresis of the shape memory elements will thus be reflected in any device making use of such materials. Many applications of shape memory alloys nowadays are using near equiatomic binary nickel-titanium alloys. Such nickel-titanium alloys typically have a hysteresis width of about 40° C. Specific alloys processed properly show however a much lower hysteresis. Examples thereof are: [0044]
Cu-based shape memory alloys, such as Cu—Zn—Al and Cu—Al—Ni, and especially single crystals hereof [0045]
Ni—Ti—X alloys, and especially Ni—Ti—Cu—X based alloys (X being Fe, Cr and the like), and single crystals hereof [0046]
Ni—Ti alloys and Ni—Ti—X alloys, by use of the R-phase transition in these alloys, and especially Ni—Ti—Fe alloys [0047]
Au based shape memory alloys, and single crystals hereof [0048]
By integrating elements of such low hysteresis alloys into devices, these devices will also show a much lower hysteresis. [0049]
Another important point is that the upper and lower transformation ranges of the hysteresis curve, {As-Af} and {Ms-Mf}, can be quite substantial. FIG. 1 shows that in order to switch from the ‘on’ state at the activation temperature Ta to the ‘off’ state at the deactivation temperature Td and vice versa, the hysteresis and the two transformation ranges have to be overcome. Large transformation temperature ranges result in a slow/sluggish action of such devices. [0050]
Accordingly, in order to minimize the difference between the activation and deactivation temperature, the transformation ranges should also be minimized. These transformation ranges can be minimized, for example, in one aspect by proper alloy selection and proper processing. This minimization can be done based on the knowledge of the skilled person. Thus, by selecting elements of shape memory alloys with low hysteresis and/or small transformation ranges, a device will be obtained in which the difference between the activation and deactivation temperature will be lower. However, setting the exact activation temperatures still remains a problem. [0051]
Adjusting the Transformation Temperatures and Decreased Hysteresis by using a Bias Element [0052]
The transformation temperatures of shape memory alloys are composition and processing dependent. It follows that the transformation temperatures can be controlled to some extent by controlling the composition and the processing. However, it is difficult to control the transformation temperatures of shape memory alloys in this way with sufficient accuracy. [0053]
In most devices actuated by shape memory elements, the shape memory elements work against a bias element. The SMA element therefore generates force and motion, and thus work, on heating. The simplest mode of operation is an SMA wire acting against a constant force. It is known that the transformation temperatures will increase when the bias force is increased, as schematically illustrated in FIG. 2. It follows immediately that by proper selection of the bias element, and/or installing an adjustable bias element, the activation and deactivation temperature of the device can be further adjusted. [0054]
An accurate control of the transformation temperatures in accordance with embodiments of the present invention is thus obtained by a proper selection of composition and processing of the shape memory element, with a final adjustment via a proper selection of the bias element and/or installing an adjustable bias element, e.g. a bias element such as a compression spring and a screw for adjusting the initial bias of the spring. It has been found that the hysteresis (in ° C. difference) in a biased system will in general be lower than in a stress-free shape memory element. Application of a bias element can thus be used also for lowering the hysteresis of the device. [0055]
Reducing the Hysteresis and Reducing the Transformation Ranges by Use of a Partial Transformation [0056]
In a first approximation, the hysteresis (in ° C. difference) is proportional to the amount of involved transformation. A cyclic partial transformation will thus show a smaller hysteresis and a partial transformation range, as illustrated in FIG. 3. The difference between T[0057] _Dand T_Ais also reduced. A partial transformation can be imposed basically in two ways.
1. The device can be designed in such a way that a further shape change is impeded during heating and/or during cooling by a blocking element. Accordingly, the difference between activation and deactivation temperature will be lowered. [0058]
2. The external conditions can also cause a partial transformation. For example, a shape memory element can be put onto or into or onto a warm object, e.g. the mammalian body. In case heating, respectively cooling is used, body temperature will be the minimum, respectively maximum temperature of the SMA element. In case body temperature is located between M[0059] _Sand M_F, respectively A_Sand A_F, a partial transformation will be obtained involving a smaller difference between activation and deactivation temperatures.
Reduced Transformation Range by Applying a Decreasing Bias Stress [0060]
In most devices incorporating SMA-elements, the bias element exerts (i) constant or (ii) increasing bias stresses on the SMA element as the SME element is activated, as illustrated in FIG. 4. In the case of a constant bias, the transformation temperature ranges {A[0061] _F-A_S} and {M_S-M_F} will nearly not be affected. In the second case, the transformation range increases. Accordingly, the temperature difference between activation temperature and deactivation temperature also increases.
In accordance with an embodiment of the present invention, bias systems are provided in which the bias element co-operates with shape memory element so that there is a decreased biasing stress on the SMA-element at a higher temperature. In such cases, transformation temperature ranges {A[0062] _F-A_S} and {M_S-M_F} will decrease. Accordingly, the temperature difference between activation temperature T_Aand the deactivation temperature T_Dalso decreases. The reduction in the transformation ranges results in an activation action which is closer to a “snap-action” as well as reducing the temperature change required to change states of the SME.
Reduction of the Transformation Range by Buckling: Snap-Action Mechanisms [0063]
A further embodiment of the present invention includes devices in which one of the biasing element and the SMA element will buckle during cooling and will ‘reverse-buckle’ during heating. The shape change of the SMA-element during cooling will occur nearly at constant temperature (the deactivation temperature) and the reverse shape change during heating will also occur nearly at a constant temperature (the activation temperature), as shown in FIG. 5[0064] c when referring to devices schematically shown in FIGS. 5a and b for the example of a shape memory plate which is compressed by a bias element which may be a pre-biased compression spring. The stable state of the SME is a flat plate as shown in FIG. 5a. A support 2 is provided to which is attached a compression biasing element 4 such as a spring which acts on a coplanar elongate SME 6. Above the activation temperature, this elongate SME 6 such as a plate or rod will be straight. During cooling, because of the compressive stresses applied by the biasing element 4 the straight shape will become unstable due to weakening of the SME 6. Hence, at a critical temperature the SME 6 will buckle to a curved shape as shown in FIG. 5b. During subsequent heating, the reverse will occur at a higher temperature and the curved SME 6 gains mechanical strength and ‘reverse-buckles’ to the original straight shape. In summary, because of this snap-action mechanism both transformation ranges are reduced to nearly a constant single temperature—as indicated in FIG. 5c.
Included within the present invention are also ways to enhance or adjust the buckling effect. For example, for the case of the elongate SMA-element [0065] 6 (e.g. plate or rod shaped), the buckling can be enhanced and adjusted by weakening, e.g. thinning, the middle part of the SME 6. The application of this snap-action mechanism to devices incorporating SMA elements is not limited to the presented example, but can be applied in many different devices and the involved SMA-elements are not limited to plate- or rod-shaped SMA-elements.
Various designs of biasing elements are shown in FIGS. 5[0066] d to i. In FIG. 5d a biasing element 4 e.g. of a tension spring is shown attached to both ends of an elongate SME 6. The tension spring exerts a compressive force on the SME 6 causing it to buckle below the critical temperature as shown in FIG. 5e. In FIG. 5f a weight 8 is placed on the elongate SME 6 as a biasing element. As shown in FIG. 5g the SME 6 buckles below the critical temperature. Despite the fact the force exerted by the weight 8 is constant, the bending moment (and therefore stress) on the SME 6 at its center is larger at the lower temperature.
Instead of the SME buckling, additional useful effects can be produced by the biasing element being made to buckle or lower its biasing force. An embodiment is shown in FIGS. 5[0067] h and i. The biasing element 4 is a spring strip which is buckled when the elongate SME 6 (e.g. rod, strip or plate) is in the activated state (high temperature, stiff properties) as shown in FIG. 5h. As the temperature drops the SME 6 becomes weaker and buckles as shown in FIG. 5i. By attaching mechanical linkages to the SME 6 and the bias element 4, movements can be actuated in both the activated and deactivated states. This results in a double action switch which is very compact and efficient. Where a heat source 8 is provided close to the SME 6, a cyclic action can be achieved (see below).
The snap-action mechanism may be also used in so-called on-off actuators. [0068]
Action of the Device in a Temperature Gradient: a Device Acting/Reacting at Constant Thermal Conditions [0069]
Embodiments of the present invention include devices in which the SMA element moves in the opposite direction to a decreasing thermal gradient, i.e. it moves towards a heat source whose temperature is higher than the environment. There is a temperature gradient in which the temperature drops with increasing distance from the heat source. The behavior of the device is especially relevant in combination with the above presented snap-action mechanism. The embodiment of FIG. 5, placed close to a [0070] heat source 8, as illustrated in FIGS. 5a and b shows this behavior. In the deactivated state, the elongate SME 6 is curved (FIG. 5b) and is close to the heat source 8. As a result of heat transfer from the heat source 8 the temperature of the SME 6 will increase. At the critical activation temperature, the SME 6 will ‘buckle back’ and moves away from the heat source 8 (FIG. 5a). Due to the temperature gradient, the SME 6 will now start to cool. At the critical deactivation temperature, the SME 6 will buckle again. This cyclic movement (ABDC of FIG. 5c, the temperature gradient experienced by the SME is shown as the curve from Te to temperature Ts) will be repeated as long as the temperature gradient exists. The periodic time of the cycle will depend on the thermal gradient, but can also be controlled via the design of the device and the selection and processing of the shape memory elements, as explained above, as well as the thermal mass of the complete device. Evidently, in case the thermal gradient is relatively small, shape memory elements with a very low hysteresis will have to be selected, optionally in combination with the methods presented above for a farther lowering of the hysteresis and of the transformation ranges.
As FIGS. 6[0071] a to c show, the snap-action mechanism (small transformation ranges) is preferable in order to obtain a sharp and definite cyclic movement of the device in a thermal gradient. In FIGS. 6a and b a shape memory element 6 is constrained within cavity in a block support 2, the block 2 having a groove 3 near its upper surface into which the SME 6 fits. The SME 6 is biased by a biasing device 4 such as a compression spring acting perpendicularly to the SME 6 at its center. The transformation ranges are larger than in FIG. 5c (no snap action). In this situation the SME 6 may find one of two semi-stable positions: either the position of SME 6 determined by position B of the hysterisis loop (position P2 in a bent position). Otherwise the SME 6 takes a position determined by D on the hysteresis loop position P1). Note that the force exerted by the spring 4 is lower in the deactivated state (low temperature state) and the bending stress in the SME 6 is lower despite the large amount of bend. Such a device can make a movement to one of the two semi-stable positions depending upon whether device starts at position C or A. When the environmental conditions change again the device can take on the other semi-stable position. The device is a mechanical bi-stable flip-flop or switch.
Brooch Reacting on Small Changes of the Environmental Temperature [0072]
Conventional brooches have a fixed shape. In accordance with the present embodiment a brooch is provided with thermally activated moving parts. These parts should move when there are changes of the local temperature. An example is that the brooch is positioned on a dress but below a coat (or the like). In that case, the temperature of the brooch will be relatively close to body temperature. When the coat is removed, the local temperature at the brooch will decrease to a temperature closer to room temperature—this will result in activation of the moving parts of the brooch, either closing or opening. [0073]
Other sources of such small temperature changes can also be used. For example, when the person is walking around the local temperature will be closer to room temperature than when the person is sitting quietly on a chair. Another example is that the person goes from a warmer room to a colder place and vice versa or if the temperature of the room itself changes. [0074]
The moving parts of the brooch should react on small temperature differences. As an embodiment of the present invention, a [0075] brooch 12 has a decorative design, e.g. the shape of a peacock 14 with moving feathers 16 as shown in FIGS. 7a and b. These feathers 16 are actuated by a device in accordance with an embodiment of the present invention—a combination of a bias element 4 such as a bent wire acting against small elongate, e.g. beam-shaped, shape memory element 6 as shown schematically in FIGS. 7c and d. The brooch 12 is a mechanical bi-stable flip-flop device similar, in principle, but not in detail, to that shown in FIG. 6. As shown in FIG. 7c, the wire spring 4 is bent and exerts a large bending moment on the shape memory element 6 when the temperature is high (activated state of the shape memory element). The SME 6 is mounted on a support 2. In this state the shape memory element 6 is very stiff and is almost straight. As the temperature is reduced the shape memory element 6 becomes weak and bends easily (FIG. 7d). This movement is used to move one of the feathers 16 by a linkage 7. To limit the movement (partial transformation) a blocking element 9 is used which is forced against a stop 11 which may be part of support 2.
This embodiment makes use of the following features to obtain a difference of T[0076] _A−T_Dof 10° C. or less, more preferably 7° C. or less or most preferably 5° C. or less:
Use of a shape memory element with a very low hysteresis. [0077]
Cu—Zn—Al single crystals were obtained from ‘Centro Atomico Bariloche’ (Av. Bustillo 9,500; 8400 San Carlos de Bariloche, Argentina, contact person: Marcos Sade). Small beam shaped elements were cut from these Cu—Zn—Al single crystals. Appropriate heat treatments were carried out, e.g. 825° C. for 30 minutes followed by 120° C. for 50 minutes). [0078]
Adjusting the transformation range by applying a bias stress. This is achieved by selecting the pre-biasing of the spring. By adjusting the initial bias strain, the activation and deactivation temperature can be shifted to appropriate values. [0079]
Reducing the hysteresis and the transformation ranges by use of a partial transformation. The shape change of the shape memory plates is limited since the wing movement only allows a limited displacement. For this purpose the movement is limited by a blocking element. By adjusting the size of the displacement, and by adjusting the dimensions and the exact positioning of the shape memory beams, the degree of partial transformation can be controlled. Optionally, a snap mechanism can be built into this devices. [0080]
Necklace Actuator Moving Cyclically in a Small Temperature Gradient [0081]
An embodiment of the present invention provides a necklace as shown schematically in FIG. 8[0082] a containing at least one flower 18 whose petals 19 should be opened and closed by a mechanism. In this embodiment the flower 18 opens and closes repeatedly, in a cyclic manner, due to a slight thermal gradient close to the human body of the wearer of the necklace even when the global room temperature is constant. The biasing element is one or more tension springs 4 in parallel with the elongate shape memory element 6 as shown in FIGS. 8b and c. The SME 6 is mounted on a support 2. In the activated state (high temperature state), the shape memory material is stiff and the SME 6 is straight. The bending stress on the shape memory element 6 is small (FIG. 8b) as the tension spring 4 is hardly offset from the shape memory element 6. In this state the SME 6 is furthest away from the human body or other heat source 8. As the temperature drops, the shape memory material weakens and it bends resulting in a high bending stress at the lower temperature (FIG. 8c). This movement opens and closes the petals 19 of the flowers 18. The SME 6 moves closer to the heat source 8 and begins to warm again thus resulting in a cyclic action. A blocking element 9 may be used which interferes with a stop 9 (e.g. part of support 2) to restrict the movement and thus reduce the hysteresis.
In this embodiment, the following features of the present invention have been integrated in the device to obtain a difference of T[0083] _A−T_Dof 10° C. or less, more preferably 7° C. or less or most preferably 5° C. or less:
Use of a shape memory element with a very low hysteresis. [0084]
Cu—Zn—Al single crystals were obtained from ‘Centro Atomico Bariloche’ (Av. Bustillo 9,500; 8400 San Carlos de Bariloche, Argentina, contact person: Marcos Sade). Plate shaped elements were cut from these Cu—Zn—Al single crystals. Appropriate heat treatments have been given afterwards (825° C. for 30 minutes followed by 120° C. for 50 minutes). [0085]
Reduced transformation range by applying a decreasing bias stress. The bias element is placed in such a way that the bias stresses decreases as the SME element becomes activated (comparable to the design presented in FIGS. 5[0086] a and b). This results in a smaller difference between activation and deactivation temperature. By adjusting the initial bias strain, the activation and deactivation temperature can be shifted to appropriate values.
Reducing the hysteresis and the transformation ranges by use of a partial transformation. The shape change of the shape memory plates is limited since the petal movement is restricted to a limited displacement. By adjusting the size of the displacement, e.g. by appropriate blocking or restraining elements, and by adjusting the dimensions and the exact positioning of the shape memory plate, the degree of partial transformation can be controlled. [0087]
Snap mechanism in combination with a temperature gradient. The shape memory plate is shaped in such a way (preferably with some thinning in the middle) and the bias springs are placed appropriately (comparable to the design presented in FIGS. 5[0088] a and b) in order to obtain the snap mechanism. The device is placed in such a way that the shape memory plate is positioned close to the body in order to use the temperature gradient from body temperature to room temperature. Buckling (as a result of cooling) will result in a movement of the shape memory elements towards the body. Thus, the shape memory plate comes closer to the body and the temperature of the shape memory element will increase due to the body heat. At the critical activation temperature, the shape memory plate will ‘buckle back’ and move away from the body and thus to an environment at lower temperatures. Accordingly, the temperature of the shape memory plate will decrease. At the critical deactivation temperature, the shape memory plate will buckle and move towards the body and thus to an environment at higher temperatures. This sequence of ‘buckling back’ and budding will continue.
Further Embodiments of the Present Invention [0089]
The features of the present invention described above can be used to provide opening and closing actuators for many medical applications. Repeated actuation can be achieved using very small temperature differences, e.g. body heat, as well as providing a snap actuation. [0090]
These features provide: [0091]
Actuator which reacts on very small temperature differences [0092]
Actuator which acts/reacts repeatedly at a constant environmental temperature, by using local temperature differences, e.g. close to the body [0093]
Actuator which acts/reacts repeatedly at a constant environmental temperature, by using local temperature differences, e.g. close to the body, in combination with an integrated snap-mechanism. [0094]
Bands [0095]
Embodiments of the present invention include bands such as bracelets and necklaces to be worn by mammals such as dogs or humans. These bands can be opened to place around the respective body part when subjected to a low temperature and then close when they are heated by the body warmth of the mammal. [0096]
The opening and closing mechanism can be applied also for any band-like product (inclusive medical applications) of which the following is non-exhaustive list: bracelets, rings (inclusive earrings, piercings, medical implants, etc), necklaces, couplings (industrial, medical), sealing and closing mechanisms, etc. [0097]
Such bands should ideally have the following features [0098]
the band (which might be integrated in another element) may be fitted nicely around or inside an object, without any hinges, locks, screws and the like. [0099]
the band will close or expand at high temperatures and can be opened or shrunk at lower temperatures. [0100]
the band's shape changes with temperature differences. [0101]
The shape memory alloy and the processing of the shape memory wire is performed in order to have the transformation temperatures A[0102] _S, A_F, M_Sand M_F, in the necessary range (see below). For the example of the bracelet, the following is considered as ideal.
1. The ideal solution is that the bracelet can be opened at lower temperatures, and keeps the open shape at temperatures at or slightly above room temperature. In this way the bracelet with the open shape can be stored and transported easily. The technical corresponding request is that A[0103] _Sand A_Fshould be sufficiently high.
2. The larger the temperature difference between body temperature and AF, the faster will be the shape change from the cold shape to the hot shape. A sufficiently fast action is required for practical and aesthetic reasons. It follows that A[0104] _Fhas to be sufficiently below body temperature.
3. For practical reasons, it should be possible to open the bracelet at sufficiently high temperatures. It follows that As should be sufficiently high. [0105]
4. Combining the requests above, it also follows that a small temperature range for the reverse transformation is preferred, as well for aesthetic reasons and for practical reasons. [0106]
5. As an example, an A[0107] _Sclose to 22° C. (between 118° C. and 25° C.) and an A_Fclose to 28° C. (between 23° C. and 30° C.) is preferred.
6. The difference between A[0108] _Fand A_Sis preferably 10° C. or less, more preferably 7° C. or less and most preferably 5° C. or less. The reason for this is that such a bracelet can be opened at some ° C. below A_S. Hence, A_Sshould not be too low otherwise a low temperature will have to be applied which may be inconvenient for the wearer.
The shape memory element can be made of many shape memory materials. Some examples: [0109]
binary Nickel Titanium (abbreviated to Ni—Ti) [0110]
Nickel Titanium with other alloying elements [0111]
Nickel Titanium Copper with other alloying elements [0112]
Nickel Titanium Copper Chromium [0113]
Cu based shape memory alloys, such as CuZnAl and CuAlNi with further alloying elements [0114]
Au based shape memory alloys [0115]
The transformation temperatures of most shape memory alloys are composition and processing dependent. In order to obtain the appropriate transformation temperatures, alloys of appropriate composition and which underwent appropriate processing have to be selected. This can be done by persons skilled in the art. [0116]
Production of the Bands [0117]
The starting material is wire, strip and the like with correct dimensions and made of appropriate alloys which have undergone appropriate processing (see above). The further production of the bands can involve several steps, such as (i) shape setting treatments, (ii) extra heat treatments, (iii) polishing and coloring processes, and (iv) adding other objects. The sequence given here is only indicative; other sequences can be followed. All the processes and procedures can be done by persons experienced in developing and making of products of shape memory alloys. [0118]
Shape Setting Treatment [0119]
In this step, the hot shape is given to the shape memory element. It typically involves (i) the production of a mandrel with the appropriate shape, (ii) fixing the shape memory element on or around the mandrel, (iii) putting the mandrel with the fixed shape memory element in a furnace or the like (molten salt bath or similar) for appropriate times and at appropriate temperatures, and (iv) cooling and removing the shape memory element from the mandrel. Afterwards, the shape memory element will have the required hot shape. Taking the example of Ni—Ti based elements, the heat treatment temperature and time will be typically 400-550° C. for 2 to 30 minutes, although other procedures can be followed. [0120]
Additional Heat Treatments [0121]
Additional heat treatments might be required to shift the transformation temperatures or to change the ductility of the shape memory elements. [0122]
Polishing and Coloring [0123]
For aesthetic reasons, polishing and coloring treatments might be required. Grinding and polishing (electropolishing or mechanical polishing) will give a metal color. For the case of Ni—Ti based elements, yellow, blue, black and intermediate surface colors can be obtained by appropriate heat treatment. Different colors can be also obtained via coatings and paints. [0124]
Adding Other Objects [0125]
Other objects can be connected to the shape memory elements. For example diamonds, golden balls and the like can be put on the shape memory element for aesthetic reasons. [0126]
While the invention has been shown and described with reference to preferred embodiments, it will be understood by those skilled in the art that various changes or modifications in form and detail may be made without departing from the scope and spirit of this invention. [0127]

Claims

1-17. Cancelled.

18. A device comprising a shape memory element and a bias element, the shape memory element and the bias element co-operating together to provide the device with a thermal hysteresis having a mechanical property activation temperature and a mechanical property deactivation temperature, wherein the difference between the activation temperature T_Aand the deactivation temperature T_Dis 10° C. or less, preferably 7° C. or less or most preferably 5° C. or less.

19. The device according to claim 18, wherein the bias element co-operates with the shape memory element so that the stress on the shape memory element is lower in the activated state compared to the deactivated state resulting in a lowering of a transformation range of the device compared to a transformation range of the shape memory element alone.

20. The device according to claim 19 wherein the stress is a bending stress

21. A device according to claim 18, further comprising a blocking element so that said shape memory element has a restricted movement, resulting in a lowering of the thermal hysteresis of the device.

22. A device according to claim 18, wherein said shape memory element and the bias element are adapted so that the shape memory element buckles under the action of the bias element, resulting in a lowering of the transformation ranges of the device.

23. A device according to claim 18, wherein said shape memory element and the bias element are adapted so that the bias element buckles under the action of the shape memory element.

24. A device according to claim 18, wherein the transformation range of the device is such that when placed in a thermal gradient the device is repeatedly activated and deactivated.

25. A device according to claim 18, wherein the device exhibits thermal hysteresis with a deactivation temperature in the range 20 to 32° C.

26. A device according to claim 18, wherein the device exhibits thermal hysteresis and has an activation temperature in the range 25° C. to 35° C.

27. A piece of jewelry comprising at least one device according to claim 18.

28. A piece of jewelry including a plurality of parts which are adapted for relative movement between each other so as to vary an externally visible shape or configuration of said jewelry, said jewelry further comprising a shape memory element and a bias element adapted to co-operate so as to cause said relative movement, said shape memory element exhibiting a thermal hysteresis having upper and lower temperature transformation ranges, said upper temperature transformation comprising a range of 10° C. or less, preferably 7° C. or less and more preferably 5° C. or less.

29. The jewelry piece according to claim 28, wherein the shape memory element has an upper transformation start temperature A_Sin the range 18 to 25° C.

30. The jewelry piece according to claim 28, wherein the shape memory element has an upper transformation finish temperature A_Fin the range 23° C. to 30° C.

31. The jewelry piece according to claims 28, wherein said parts are adapted to cycle automatically between at least two different said externally visible shapes or configurations.

32. The jewelry piece according to claim 28, wherein said parts are adapted to move or cycle automatically between different said shapes or configurations when said piece of jewelry is located in the region of a wearer's body.

33. The jewelry piece according claim 28, wherein said jewelry piece comprises a broach or a necklace and said relative movement is adapted to move or cycle said parts between an externally visible closed or folded shape or configuration and an externally visible open shape or configuration.

34. A piece of jewelry according to claim 28, wherein said shape memory element and said bias element comprise a device comprising a shape memory element and a bias element, the shape memory element and the bias element co-operating together to provide the device with a thermal hysteresis having a mechanical property activation temperature and a mechanical property deactivation temperature, wherein the difference between the activation temperature T_Aand the deactivation temperature T_Dis 10° C. or less, preferably 7° C. or less or most preferably 5° C. or less.