« PreviousContinue »
308 + x axis
TE P 3
Amount Cs (arb units)
5.5 5 I I I I I 0 100 200 300 400 500 Temperature of Annealing (°C) ,0? 5 -E’ 4 _ 406 ‘T C Y X E 3 - X A l m I A (J A 2 2 ‘ 408 C E 1 ' < 0 I I I I I 0 100 200 300 400 500 600
Temperature of Annealing (°C)
1 METHOD OF MAKING LOW WORK FUNCTION COMPONENT
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH & DEVELOPMENT
This invention was made with Government support under contract number DE-FC26-04NT42324 awarded by The United States Department of Energy. The Government has certain rights in the invention.
The invention relates generally to the area of low work function (LWF) materials. More specifically, the invention relates to a method of fabricating LWF components, such as electrodes.
Processing steps involved in the fabrication of a particular member of an electronic component may be detrimental to the fabrication efficiency and reliability of other members constituting the component. One situation in point relates to the fabrication of components that display a low work function. Development of cost effective methodologies that can be used to fabricate LWF components such as LWF electrodes reliably and which are compatible with an infrastructure as is conventionally used for the fabrication of LWF components is one of the challenges facing present day LWF component fabrication technology.
Methodologies that allow for the fabrication of robust and reliable LWF components, and at the same time, that are compatible with the existing fabrication methodologies employed to fabricate other parts of a component would therefore be highly desirable.
One of the current paradigms in ensuring the quality of fabrication devices containing LWF components consists in fabricating the LWF components separately from any other parts constituting the device, and integrating the LWF component into the device upon completion of all those steps involved in the fabrication of the other parts of the device that are detrimental to the LWF component.
Any fabrication methodology that aims to improve the health of fabricated LWF components while adversely impacting or limiting the efficiency of fabrication of the other parts of a device may not be economically viable.
A fabrication methodology that is compatible with the existing infrastructure as has been used conventionally to fabricate LWF components such as, thin film deposition systems such as sputtering systems, and ion implantation systems, and does not place adverse restrictions on the existing methodologies used in the fabrication of the other parts, such as requiring changes in such existing methodologies would therefore, be highly desirable.
Embodiments of the invention are directed towards a method for fabricating the LWF component.
In accordance with one exemplary embodiment of the invention, a method for fabricating a component is disclosed. The method includes: providing a member having an effective work function of an initial value, disposing a sacrificial layer on a surface of the member, disposing a first agent within the member to obtain a predetermined concentration of the agent at said surface of the member, annealing the member, and removing the sacrificial layer to expose said
surface of the member, wherein said surface has a post-process effective work function that is different from the initial value.
These and other advantages and features will be more readily understood from the following detailed description of preferred embodiments of the invention that is provided in connection with the accompanying drawings.
FIG. 1 is a flow chart of a process for fabricating a LWF component in accordance with an exemplary embodiment of the invention.
FIG. 2 is a schematic representation of a member-sacrificial layer-complex (MSLC) during an intermediate stage of a fabrication of a LWF component.
FIG. 3 is a schematic representation of a MSLC during an intermediate stage of a fabrication of a LWF component showing a depth profile of disposed agent within the MSLC.
FIG. 4 is a graphical representation of an amount of implanted cesium within a member as a function of kinetic energy of incident flux of cesium, and as a function temperature of annealing of the member, in accordance with an exemplary embodiment of the invention.
In the following description, whenever a particular aspect or feature of an embodiment of the invention is said to comprise or consist of at least one element of a group and combinations thereof, it is understood that the aspect or feature may comprise or consist of any of the elements of the group, either individually or in combination with any of the other elements of that group.
In the following specification and the claims that follow, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise.
As used herein, the term “effective work function” refers to the minimum energy (usually expressed in electron volts) needed to remove an electron from a neutral solid to a point immediately outside the solid surface (or energy needed to move an electron from the Fermi energy level into vacuum). Here “immediately” means that the final electron position is far from the surface on the atomic scale but still close to the solid on the macroscopic scale. Extraction of electrons from the surface of a metal can be induced via several methods of excitation based on different phenomena, such as photoelectric phenomena, thermionic phenomena, and electric field phenomena.
As used herein, the term “agent” refers to any material that is to be disposed within the bulk or on the surface of a member. The means for such disposal include, but are not limited to, diffusion via for instance thin film deposition techniques such as sputtering or evaporation, or ion implantation. Suitable non-limiting examples of agents include, chemical entities, particulate matter, or combinations thereof .
As used herein, the term “member” refers to any part of a component within which it is desired to dispose agents. It may sometimes also be referred to as “substrate” in line with conventional usage in thin film deposition technology. The member or substrate will be understood to mean any entity, a change in whose work function is being attempted.
As used herein, the term “manufacturing” refers to any operation that could potentially disrupt the surface chemistry, and/or surface morphology, and/or surface properties of the member. Examples of such operations include, but are not
limited to, etching, cleaning, masking, coating, heat treatment, annealing, or combinations thereof.
As used herein, the term “combine” refers to any chemical or physical mechanism or operation whereby two physical or chemical entities are placed or disposed in vicinity of each other. Suitable non-limiting examples of such processes include, physical adhesion, chemical reaction, or combinations thereof.
As used herein, the term “sacrificial layer” refers to a layer that is disposed on any substrate with an intent to cover and thereby segregate said surface of the substrate from ambient conditions. The purpose of such segregation may be to protect said surface from the ambient. As the name may suggest, the sacrificial layer, while providing such protection, may get sacrificed, i.e., damaged or destroyed. Also, the sacrificial layer may or may not be removed after all manufacturing operations of said component and/or other parts constituting the device (of which the component is a part) have been completed.
As used herein the term “post-process,” when used in the context of discussion of a component indicates that all manufacturing operations of said component and/ or other parts constituting the device (of which the component is a part) have been completed. In similar vein, the term “pre-process,” when used in the context of discussion of a component indicates that all manufacturing operations of said component and/ or other parts constituting the device are yet to be completed.
As used herein, the term “member-sacrificial-layer-complex” (MSLC) refers quite generally to an entity that includes a member, a sacrificial layer, and an interface between the member and the sacrificial layer.
As used herein, the term “within,” when used in the context of discussion of any physical entity may refer to the bulk of the physical entity or it may refer to a surface of the physical entity, or it may refer to both the bulk and the surface of the physical entity.
As used herein, the term “green,” when used in the context of a discussion a physical entity, such as a component, conveys that the component is as yet in its pristine “pre-processed” state, i.e., none of the fabrication steps that eventually result in the component displaying new changed properties, such as, an effective work function that is lower than its initial value, have as yet been initiated. For example, a “green component” refers to a component on which no processing steps, that cause the component to display desired properties, have been performed.
In one embodiment of the invention, a method 100 for fabricating a component is provided as shown in FIG. 1. Step 102 of the method 100 includes providing a green component or “member” having an effective work function of an initial value. This is followed by step 104, which includes disposing a sacrificial layer on a surface of the member. As per a definition mentioned earlier, the combined entity resulting after this step 104, containing an interface between the member and sacrificial layer is referred to as the MSLC. The next step 106 includes disposing a first LWF agent within the MSLC to obtain a predetermined concentration of the first LWF agent at said surface of the member. It is likely that such disposition of the agent within the member will result in a change in the electrical properties of the member. Step 106 is now followed by step 108 that includes annealing the MSLC. The final step 110 includes removing the sacrificial layer to expose the surface of the member, wherein the member now contains, within itself, the LWF agent. The surface at this post-process stage, has an effective work function value that is different from the initial value.
In one embodiment of the method 100, the green component can include semiconductors, or metals, or insulators, or combinations thereof. Suitable non-limiting examples of semiconductors include, silicon, germanium, gallium nitride, silicon carbide, gallium arsenide, and indium nitride. Suitable, non-limiting examples of metals include, aluminum, copper, silver, and gold. Suitable, non-limiting examples of insulators include, glass, quartz, and sapphire. The green component can also include a combination of different layers of different materials such as, a layer of metal on semiconductor, non-limiting examples of which are a layer of gold on silicon, a layer of aluminum on silicon, and or a layer of copper on silicon. The green component can also include a layer of metal on insulator, wherein the metal includes a material selected from the list consisting of aluminum, copper, silver, and gold, and the insulator includes a material selected from the list consisting of glass, quartz, and sapphire.
The green member has an initial work function, the modification of which, for example, to a lower value may be desired. In one embodiment of the method 100 above, such a modification may be achieved by disposing, within the green member, a suitable first LWF agent which by itself has a suitable work function, such that the disposition of the first LWF agent within the green component results in a lowering of the work function of the member. Now, by their very nature LWF materials are reactive and/or volatile, and it is likely that in improperly controlled environments, the LWF material will combine with one or more species present in the environment to give products that impede the development of LWF properties within the member. Further, the LWF component likely forms, or is likely intended to be, a part of a device that contains other parts as well. It is possible that some of the steps involved in the manufacture of the other parts are detrimental to the LWF component. Again, the fabrication of such LWF components often itself involves surface treatments and/or surface coatings with different materials before the component displays the desired work function. These surface treatments and/or surface coatings are susceptible to damage during the fabrication of the other parts constituting the component. It may be unviable to modify, for a variety of technological, economic, or environmental reasons, processes that are followed for the manufacture of the other parts. Similar reasons may also limit the ability to integrate the LWF component with the other parts constituting the device until all such manufacturing operations of these other parts are complete and a favorable ambient environment has been provided/restored. A method of fabricating a LWF component that does not impede or require unnecessary modifications of the manufacturing processes of other parts constituting the device would therefore be highly desirable. For the reasons mentioned above, in one embodiment of the invention, a sacrificial layer is disposed on to the component before disposing the LWF agent within it. The sacrificial layer serves as a protective layer, shielding the component and the agent that is disposed within the component, from potentially harmful exposure to harsh ambient environments.
The sacrificial layer can be disposed on the green component by any known means, including, but not limited to, plasma enhanced chemical vapor deposition (PECVD), low pressure chemical vapor deposition (LPCVD), sputtering, thermal evaporation, pulsed laser deposition, or spin or spray coating. It is likely that the composition of the sacrificial layer is one of the factors determining a choice of the disposition method.
In one embodiment of the invention, the sacrificial layer includes a material selected from the group consisting of
oxides, nitrides, carbides and polymers. These oxides, nitrides, and carbides, may be formed via the processes of oxidizing, nitriding, and carburizing respectively. Non-limiting examples of materials from Which the sacrificial layer may be composed include, silicon dioxide, silicon carbide, silicon nitride, polysilicon, and photoresists. In one embodiment of the method 100, the sacrificial layer may be disposed to have a thickness Within the range from about 10 nm to about 500 nm. In one embodiment of the method 100, the sacrificial layer may be disposed to have a thickness Within the range from about 500 nm to about 1000 nm. In one embodiment of the method 100, the sacrificial layer may be disposed to have a thickness Within the range from about 1000 nm to about 5000 nm.
Once the sacrificial layer has served its purpose, it may be removed via any suitable physical and/or chemical process. Non-limiting examples of such processes include, Wet etching, plasma etching, and sputtering.
As Was mentioned above, it is the presence of a LWF agent Within the member that results in a desired modification, such as a reduction of the Work function of the member. An agent may be disposed Within the member using a variety of techniques that are Well knoWn in the art, such as diffusion and/or ion implantation (discussed beloW). Via the technique of ion implantation, it is possible to dispose ions of the agent at desired depths Within a substrate. In the presently disclosed embodiments of the method 100, the substrate includes the MSLC. Further, the LWF agent may be deposited on the member using any knoWn film deposition techniques, provided they include or are folloWed by a step that facilitates diffusion of the LWF agent Within the member. These techniques for disposing a LWF agent Within the MSLC are discussed later Within this description. It is likely that the concentration of the agent at the surface of the member is one of the factors determining the effective Work function of the component. In one embodiment of the method 100, the concentration of the agent on the surface of the member is Within the range from about 50% to about 100%. In another embodiment, the concentration of the agent on the surface of the member is Within the range from about 25% to about 50%. In yet another embodiment, the concentration of the agent on the surface of the member is Within the range from about 1% to about 25%.
The concentration of the first agent at the surface is a function of a plurality of factors that may be interdependent. For instance, it may depend on the kinetic energy of the incident flux of agent, because the kinetic energy of the incident flux of agent is one of the factors determining the depth profile of the agent Within the member. Another factor on Which the concentration depends is the annealing protocol that is folloWed subsequent to disposing the agent Within the member. Any manufacturing steps that need to be taken in connection With the fabrication of the LWF component or otherWise, may dictate, at least partially, the depth profile requirement of the disposed agent. Thus, in one embodiment of the method 100, the agent is disposed Within the member so that a maxima of the concentration, Within the MSLC, of the first agent, is located Within a distance of about 1 nanometer (nm) from the interface betWeen the member and the sacrificial layer.
In accordance With the method 100 of fabricating a LWF component, a predetermined concentration of an agent is achieved on a surface of the component. The agent can be present in the form of a layer at the surface the component. (In this sense, the electrical contact serves as a “substrate” for the layer.) Such layers may be monoatomic, or they may be thin film layers containing up to hundreds of monoatomic layers.
Suitable examples of agents include, but are not limited to, alkali metals such as cesium, sodium, potassium, and other materials such as, carbon, tungsten, tungsten carbide, lanthanum hexaboride, barium oxide, strontium oxide, strontium, rubidium, barium oxide, barium nitride, titanium dioxide, diamond like carbon (DLC), and combinations thereof. Suitable examples of materials from Which such substrates may be composed include, but are not limited to, silicon, platinum, gold, and combinations thereof. A suitable non-limiting example of a material from Which a monoatomic layer may be composed is cesium. Specific examples of layer-substrate combinations suitable for use in some embodiments include, but are not limited to, barium oxide deposited on silicon, barium nitride deposited on silicon, titanium dioxide deposited onplatinum, DLC deposited on silicon, cesium deposited on gold, LaB6 and ZrO deposited on tungsten.
In one embodiment of the method 100, a further step of disposing a second agent at the surface is included. This second agent may result in a further change in the effective Work function of the member. In another embodiment of the method 100, the first agent may be made to combine With other species present Within the member to form neW agents. It is also possible that the incident flux of agent is composed of a plurality of chemical entities that combine together, during the passage to the MSLC, or at the surface of the MSLC, or at the interface Within the MSLC, or Within the bulk of the MSLC, to form neW species. The presence of such neW species may themselves serve as agents and may result in a change in the Work function displayed by the member.
There are several factors, Which can be interrelated, Which together determine the final distribution of the agent Within the MSLC or Within the final LWF member. In certain operational conditions of fabrication, some of these factors may be more important than others. These factors include, but are not limited to, the kinetic energy of the incident beam of agent, the choice of agent, Whether there are present a plurality of agents in the incident flux of agent, and if so, then Whether said plurality of agents undergo combination to produce neW agents, the temperature of the MSLC during the disposition of the agent Within it, the annealing protocol that is folloWed during the process of fabrication of the LWF component, amongst others.
According to an embodiment of the method 100, a LWF component may be fabricated. Such an in-process LWF component at the intermediate MSLC stage 104 is shoWn in FIG. 2. As per step 102 of the method 100, a member 202 has been provided earlier. The member is oriented so that one of its physical dimensions, say, a height lies substantially along a positive (+) y axis 204 of coordinate system 206. A depth direction of the member 202 may therefore be understood to be substantially along the negative (—) y axis 208. The member 202 can be composed ofany ofthe materials, as discussed herein. As per step 104 of the method 100, on this member 202, also along the height direction 204, is disposed a sacrificial layer 210 Which can be composed of any of the materials as discussed herein. The disposition of the sacrificial layer 210 on to the member 202 results in the formation of an interface 212 betWeen the sacrificial layer 210 and the member 202. Quite generally, the member 202, the sacrificial layer 210, and the interface 212 may together be referred to as a member-sacrificial-layer-complex (MSLC) 214. As per step 106 of the method 100, a flux 216 of a desired agent is then made to contact a region 217 of surface 218 of the MSLC. The flux of agent can be provided through any of the techniques, as described herein. As a result of such contact, the agent gets disposed Within the MSLC 214.A thus obtainable disposition of the agent Within the MSLC 214 is indicated by reference