WO2008094428A1 - Ophthalmic lens mold having vent portion around a circumference - Google Patents
Ophthalmic lens mold having vent portion around a circumference Download PDFInfo
- Publication number
- WO2008094428A1 WO2008094428A1 PCT/US2008/000881 US2008000881W WO2008094428A1 WO 2008094428 A1 WO2008094428 A1 WO 2008094428A1 US 2008000881 W US2008000881 W US 2008000881W WO 2008094428 A1 WO2008094428 A1 WO 2008094428A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mold part
- lens
- mold
- prepolymer
- vent
- Prior art date
Abstract
Description
Claims