WO2008085604A2 - Reel-to-reel reaction of precursor film to form solar cell absorber - Google Patents
Reel-to-reel reaction of precursor film to form solar cell absorber Download PDFInfo
- Publication number
- WO2008085604A2 WO2008085604A2 PCT/US2007/084432 US2007084432W WO2008085604A2 WO 2008085604 A2 WO2008085604 A2 WO 2008085604A2 US 2007084432 W US2007084432 W US 2007084432W WO 2008085604 A2 WO2008085604 A2 WO 2008085604A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- chamber
- gas
- continuous flexible
- heating chamber
- flexible workpiece
- Prior art date
Abstract
Description
Claims