WO2006065315A1 - Embossed nonwoven fabric - Google Patents
Embossed nonwoven fabric Download PDFInfo
- Publication number
- WO2006065315A1 WO2006065315A1 PCT/US2005/034658 US2005034658W WO2006065315A1 WO 2006065315 A1 WO2006065315 A1 WO 2006065315A1 US 2005034658 W US2005034658 W US 2005034658W WO 2006065315 A1 WO2006065315 A1 WO 2006065315A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nonwoven
- embossing
- nonwoven fibrous
- fibers
- composite
- Prior art date
Abstract
Description
Claims