WO2006060714A1 - Wood fiber plastic composites - Google Patents
Wood fiber plastic composites Download PDFInfo
- Publication number
- WO2006060714A1 WO2006060714A1 PCT/US2005/043735 US2005043735W WO2006060714A1 WO 2006060714 A1 WO2006060714 A1 WO 2006060714A1 US 2005043735 W US2005043735 W US 2005043735W WO 2006060714 A1 WO2006060714 A1 WO 2006060714A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- composition according
- silane
- weight
- percent
- Prior art date
Abstract
Description
Claims