WO2005034208A2 - METHOD TO REDUCE STACKING FAULT NUCLEATION SITES AND REDUCE Vf DRIFT IN BIPOLAR DEVICES - Google Patents
METHOD TO REDUCE STACKING FAULT NUCLEATION SITES AND REDUCE Vf DRIFT IN BIPOLAR DEVICES Download PDFInfo
- Publication number
- WO2005034208A2 WO2005034208A2 PCT/US2004/030041 US2004030041W WO2005034208A2 WO 2005034208 A2 WO2005034208 A2 WO 2005034208A2 US 2004030041 W US2004030041 W US 2004030041W WO 2005034208 A2 WO2005034208 A2 WO 2005034208A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- epitaxial layer
- substrate
- etch
- etched
- etching
- Prior art date
Abstract
Description
Claims