WO2005029576A2 - Glass-based soi structures - Google Patents
Glass-based soi structures Download PDFInfo
- Publication number
- WO2005029576A2 WO2005029576A2 PCT/US2004/004746 US2004004746W WO2005029576A2 WO 2005029576 A2 WO2005029576 A2 WO 2005029576A2 US 2004004746 W US2004004746 W US 2004004746W WO 2005029576 A2 WO2005029576 A2 WO 2005029576A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- semiconductor
- oxide glass
- glass
- insulator structure
- Prior art date
Abstract
Description
Claims