WO2004046828A1 - Antireflective compositions for photoresists - Google Patents
Antireflective compositions for photoresists Download PDFInfo
- Publication number
- WO2004046828A1 WO2004046828A1 PCT/EP2003/012383 EP0312383W WO2004046828A1 WO 2004046828 A1 WO2004046828 A1 WO 2004046828A1 EP 0312383 W EP0312383 W EP 0312383W WO 2004046828 A1 WO2004046828 A1 WO 2004046828A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- composition
- photoresist
- carbon atoms
- hydrocarbyl
- Prior art date
Abstract
Description
Claims