WO2004007443A2 - Corrosion resistant films based on ethylenically unsaturated monomer modified epoxy emulsions - Google Patents
Corrosion resistant films based on ethylenically unsaturated monomer modified epoxy emulsions Download PDFInfo
- Publication number
- WO2004007443A2 WO2004007443A2 PCT/US2003/021774 US0321774W WO2004007443A2 WO 2004007443 A2 WO2004007443 A2 WO 2004007443A2 US 0321774 W US0321774 W US 0321774W WO 2004007443 A2 WO2004007443 A2 WO 2004007443A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- epoxy
- dispersion
- ethylenically unsaturated
- autodepositing
- unsaturated monomer
- Prior art date
Abstract
Description
Claims