WO2002031539A2 - An improved optical device having continuous and disperse phases - Google Patents
An improved optical device having continuous and disperse phases Download PDFInfo
- Publication number
- WO2002031539A2 WO2002031539A2 PCT/US2001/021355 US0121355W WO0231539A2 WO 2002031539 A2 WO2002031539 A2 WO 2002031539A2 US 0121355 W US0121355 W US 0121355W WO 0231539 A2 WO0231539 A2 WO 0231539A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- optical body
- copolymer
- degree
- randomness
- homopolymers
- Prior art date
Abstract
Description
Claims