WO2001079368A2 - Kratzfeste beschichtung - Google Patents
Kratzfeste beschichtung Download PDFInfo
- Publication number
- WO2001079368A2 WO2001079368A2 PCT/EP2001/003809 EP0103809W WO0179368A2 WO 2001079368 A2 WO2001079368 A2 WO 2001079368A2 EP 0103809 W EP0103809 W EP 0103809W WO 0179368 A2 WO0179368 A2 WO 0179368A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- compounds
- epoxy
- scratch
- group
- resistant layer
- Prior art date
Abstract
Description
Claims