WO2001053387A1

WO2001053387A1 - Coating having macroscopic texture and process for making same

Info

Publication number: WO2001053387A1
Application number: PCT/US2001/001805
Authority: WO
Inventors: Richard C. Macqueen; Loyd J. Burcham; Anthony A. Parker; Deborah A. Sciangola; Donald B. Henry; Donald C. Ferguson
Original assignee: Congoleum Corporation
Priority date: 2000-01-21
Filing date: 2001-01-19
Publication date: 2001-07-26
Also published as: CA2398746C; CN1419579A; CA2398746A1; US20080113182A1; TWI278477B; EP1250380A1; US6399670B1; EP1250380A4; US6790512B2; DE01908636T1; US6730388B2; US20050009943A1; US20030180558A1; AU2001236483A1; US20010038910A1

Abstract

In one embodiment the present invention provides a coated substrate comprising a substrate, a radiation-cured coating or a thermally-cured on at least a portion of the substrate, wherein the coating comprises an inherent macroscopic texture. In another embodiment, the present invention provides a pre-cured coating mixture comprising a radiation-curable resin and an initiator, or a thermally-curable resin and thermal initiator, wherein the radiation- or thermally-curable resin and the respective initiator form a pre-cured coating mixture capable of forming a macroscopic texture upon application of the mixture on a substrate. In another embodiment the present invention provides a pre-cured coating mixture comprising a radiation- or thermally-curable resin, an initiator, and texture-producing particles having an effective size to provide a macroscopic texture upon application of the mixture on a substrate. In another embodiment, the present invention provides a coated substrate comprising a substrate and a radiation- or thermally-cured coating on at least a portion of the substrate, wherein the coating comprises an inherent macroscopic texture. In addition, the present invention provides a process for making a coating on a substrate, comprising the steps of distributing a pre-cured coating mixture comprising a radiation-curable resin and an initiator or a thermally-curable resin and thermal initiator over at least a portion of a substrate to form a pre-cured coating having a macroscopic texture, and radiation-curing or thermally curing, respectively, the pre-cured coating to form a radiation-cured or thermally-cured coating having the macroscopic texture.

Description

COATING HAVING MACROSCOPIC TEXTURE AND PROCESS FOR MAKING SAME

BACKGROUND OF THE INVENTION

_<. This application is a continuation-in-part of U.S. Application No. 09/489,420 filed

January 21, 2000.

Field ofthe Invention

The invention relates generally to a coating composition and process for _{1 n} making and applying the coating. More specifically, the invention relates to radiation-cured and thermally-cured coatings having a macroscopic texture that provides superior abrasion resistance and unique aesthetic qualities.

Description of Related Art

₁ ~ Radiation-curable coatings are used in many applications throughout the coatings industry, such as protective coatings for various substrates, including plastic, metal, wood, ceramic, and others, and the advantages of radiation-curing compared to thermal curing are well known in the art. These coatings are typically resin-based mixtures that are usually cured using ultraviolet (UV) radiation. The resins are typically mixtures of

~„ oligomers and monomers that polymerize upon exposure to UV radiation resulting in a cured coating.

Various other components may be added to the resin mixture. A photosensitizer or photoinitiator may be added to cause cross-linkage ofthe polymers upon exposure to UV radiation. Flatting agents, such as silica, may be added to reduce or control r _e the level of gloss in the cured coating; however, U.S. Patent No. 4,358,476 discloses that excessive concentrations of flatting agents may result in undesirably high viscosities impeding proper application ofthe coating to a substrate, potential separation ofthe resin into separate phases, and a deleterious effect on the efficacy ofthe UV radiation. U.S. Patent No. 5,585,415 describes the use of a pigmented composition and various

, „ photoinitiators that produce a uniform microscopic surface wrinkling that provides a low gloss surface without the use of flatting agents. Various other components, such as fillers, plasticizers, antioxidants, optical brighteners, defoamers, stabilizers, wetting agents, mildewcides and fungicides, surfactants, adhesion promoters, colorants, dyes, pigments, slip agents, fire and flame retardants, and release agents, may also be added to the resin mixture o₅ to provide additional functionality. An important aspect of these coatings is their level of scratch or abrasion resistance. Good abrasion resistance is desirable so that the integrity and appearance ofthe coating is maintained. For example, a superior abrasion-resistant coating would be desirable for a flooring substrate, since flooring is typically exposed to a variety of abrasives. Improvements in the abrasion-resistance of coatings has been accomplished

_<- through various techniques. U.S. Patent No. 4,478,876 describes the addition of colloidal silica to hydrolyzable silanes and polymers derived from a combination of acryloxy functional silanes and polyfunctional acrylate monomers. Another technique is the use of compositions containing acrylate or methacrylate functionalities on a monomer, oligomer, or resin. U.S. Patent No. 5,104,929 describes the use of colloidal silica dispersions in

, certain acrylate or methacrylate ester monomers or mixtures thereof. U.S. Patent No. 5,316,855 describes the use of a cohydrolyzed metal alkoxide sol with a trialkoxysilane- containing organic component having the trialkoxysilane.

These radiation-cured coatings generally have a substantially smooth, exposed surface such that there is no macroscopic texture or texture visible to the naked

, ^ eye. This type of smooth surface provides for ease of cleaning. Some radiation-cured coatings have a microscopic texture as described in US Patent No.5,585,415. The individual features of this texture are not visible to the naked eye, but the combined effect of the microscopic texture results in the scattering of visible light that results in a matte or low gloss appearance. This texture is provided by the coating curing process which results in

2 microscopic wrinkles on the surface ofthe coating. While the microscopic dimensions of this texture provide a matte finish, these dimensions also make the coating susceptible to particle entrapment within the microscopic wrinkles. This particle entrapment results in a visibly dirty surface that is difficult to clean. Another microscopic texture found in radiation-curable coatings results from the addition of flatting agents to the uncured coating r_ye mixture. During the curing process these flatting agents, which are small inorganic or organic particles, concentrate at the coating surface to form a microscopically rough surface that scatters visible light resulting in a matte finish. The size ofthe particle used is typically such that it is no larger in diameter than the average thickness ofthe cured coating. Particles much larger than the coating thickness do not result in a matte finish and are not

₃Q desired. Since most radiation-cured coatings are no more than 75-100 μm thick, and since UV radiation can not typically penetrate any deeper, typical flatting agent particles for UV- cured coatings range in size from 0.1-100 μm, depending upon average coating thickness. Flatting agents are well known in the art as described, for example, in F.D.C. Gallouedec et al., "Optimization of Ultrafine Microporous Powders to Obtain Low-Gloss UV Curable

₃₅ Coatings," Radtech Report, Sept./Oct. 1995, pp 18-24. To produce such macroscopically smooth surfaces requires the application of a coating mixture that can be easily distributed across the substrate to be coated. If the coating mixture has a high viscosity, for example, the coating will not distribute smoothly. Therefore, it is preferable to use a lower viscosity coating to produce such a macroscopically smooth coating surface.

- Thermally-cured coatings are also used in many applications throughout the coatings industry for various substrates such as plastic, metal, wood, ceramic, and others. Thermally-cured coatings are similar to radiation-cured coatings in that they typically comprise resin-based mixtures of oligomers and monomers that polymerize upon curing. Instead of using radiation to cure or polymerize the resin, however, heat is used to affect

, r, polymerization. As such, a thermally-activated initiator is used to initiate polymerization, rather than a photosensitizer or photoinitiator. However, various other components may be added to the thermally-curable resin mixture, including the same components that are added to radiation-curable resin mixture, such as flatting agents, fillers, plasticizers, antioxidants, optical brighteners, defoamers, stabilizers, wetting agents, mildewcides and fungicides,

, r surfactants, adhesion promoters, colorants, dyes, pigments, slip agents, fire and flame retardants, and release agents.

Similar to the radiation-cured coatings, however, thermally-cured coatings are also substantially smooth from a macroscopic perspective. Also, to produce such macroscopically smooth surfaces requires the application of a coating mixture that can be _Q easily distributed across the substrate to be coated. If the coating mixture has a high viscosity, for example, the coating will not distribute smoothly. Therefore, as with radiation-cured coatings, it is preferable to use a lower viscosity coating to produce such a macroscopically smooth coating surface.

Other coatings provide a macroscopically textured surface but by methods r_ye- other than radiation-curing or thermal-curing, hi chemical embossing, for example, a macroscopic texture is formed based upon the use of various chemicals added to the substrate. In mechanical embossing, the substrate itself is imprinted with the desired textural pattern. In both types of embossing, the subsequently applied coating naturally conforms to the shape ofthe substrate textural pattern. However, any desired change to the _Q textural pattern requires changes in the amount and type of chemicals added to the substrate and/or the replacement ofthe roller used to mechanically imprint the pattern on the substrate, which can be significantly expensive and time consuming. Furthermore, neither the coating itself or its application are inherently providing the desired texture. In another form of mechanical embossing, texture may be achieved by impressing a given pattern on o the cured coating itself. Similarly, however, the texture is not produced inherently by the coating itself or its application.

Based on the foregoing, there is a need for a superior abrasion-resistant, radiation-cured and thermally-cured coatings for various substrates including plastic, metal, wood, and ceramic, among others, having a macroscopic texture. In addition, there is a need for a coating having a macroscopic texture that is easily cleanable and that provides certain aesthetic properties. Further, there is a need for a method to produce such a superior r abrasion-resistant, radiation-cured coating having a macroscopic texture using a high viscosity pre-cured coating mixture and/or texture-producing particles.

SUMMARY OF THE INVENTION In one embodiment the present invention provides a coated substrate

1 r. comprising a substrate, a radiation-cured coating on at least a portion ofthe substrate, wherem the coating comprises an inherent macroscopic texture. In another embodiment, the present invention provides a pre-cured coating mixture comprising a radiation-curable resin and an initiator, wherein the radiation-curable resin and the initiator form a pre-cured coating mixture capable of forming a macroscopic texture upon application ofthe mixture

, on a substrate. In another embodiment the present invention provides a pre-cured coating mixture comprising a radiation-curable resin, an initiator, and texture-producing particles having an effective size to provide a macroscopic texture upon application ofthe mixture on a substrate.

In yet another embodiment, the present invention provides a coated substrate _jrs comprising a substrate, a thermally-cured coating on at least a portion ofthe substrate, wherein the coating comprises an inherent macroscopic texture. In another embodiment, the present invention provides a pre-cured coating mixture comprising a thermally-curable resin and a thermal initiator, wherein the thermally-curable resin and the thermal initiator form a pre-cured coating mixture capable of forming a macroscopic texture upon r_ye application ofthe mixture on a substrate. In another embodiment the present invention provides a pre-cured coating mixture comprising a thermally-curable resin, a thermal initiator, and texture-producing particles having an effective size to provide a macroscopic texture upon application ofthe mixture on a substrate.

In addition, the present invention provides a process for making a coating on

-ry a substrate, comprising the steps of distributing a pre-cured coating mixture comprising a radiation-curable resin and an initiator or a thermally-curable resin and thermal initiator over at least a portion of a substrate to form a pre-cured coating having a macroscopic texture, and radiation-curing or thermally curing, respectively, the pre-cured coating to form a radiation-cured or thermally-cured coating having the macroscopic texture. r The coating ofthe present invention provides a top coat or protective coating having a macroscopic texture to substrates containing plastic such as polyvinyl chloride, metal, cellulose, fiberglass, wood, and ceramic, among others, hi a preferred embodiment the coating ofthe present invention is used in connection with sheet flooring. In an additionally preferred embodiment, the coating ofthe present invention is used in connection with floor tiles. The coating ofthe present invention provides superior scratch or abrasion resistance and good transparency. In addition, the coating ofthe present _<- invention is easily cleanable, and the macroscopic texture provides an aesthetic aspect to the coating.

Other embodiments and features ofthe present invention will appear from the following description in which the preferred embodiments are set forth in detail in conjunction with the accompanying drawings.

10

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a perspective view of a coated substrate 10 according to one embodiment ofthe present invention;

FIG. 2 illustrates a cross-sectional view of a coated substrate according to , another embodiment ofthe present invention;

FIG. 3 illustrates a cross-sectional view of a coated substrate according to yet another embodiment ofthe present invention;

FIG. 4 is a process flow diagram of a process for making a coating according to one embodiment ofthe present invention; 2^ FIG. 4B illustrates a cross-sectional view of a coated substrate according to yet another embodiment ofthe present invention;

FIG. 4C is a cross-sectional view of a vinyl tile according to one embodiment ofthe present invention;

FIG. 4D is a process flow diagram of a process for applying a coating ofthe r_ye present invention to a tile substrate according to one embodiment ofthe present invention; FIG. 4E illustrates a cross-sectional view of a coated substrate according to yet another embodiment ofthe present invention;

FIG. 5 is a graph ofthe viscosity as a function ofthe shear rate for a pre- cured coating mixture made according to one embodiment ofthe present invention; _on FIG. 6 is a graph ofthe viscosity as a function of he shear rate for a pre- cured coating mixture made according to another embodiment ofthe present invention;

FIG. 7 is a graph ofthe viscosity as a function of time for a pre-cured coating mixture made according to one embodiment ofthe present invention;

FIG. 8 is a graph ofthe viscosity as a function ofthe silane concentration in a ₅ pre-cured coating mixture made according to one embodiment ofthe present invention; FIG. 9 is a photograph ofthe top of a portion ofthe coated substrate produced according to one embodiment ofthe present invention;

FIG. 10 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention;

FIG. 11 is an illustration ofthe coated texture of FIG. 9; e FIG. 12 is an illustration ofthe coated texture of FIG. 10;

FIG. 13 is an illustration ofthe general type of macroscopic texture according to one embodiment ofthe present invention;

FIG. 14 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention; , r, FIG. 15 is a photograph of the top of a portion of the coated substrate produced according to another embodiment ofthe present invention;

FIG. 16 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention;

FIG. 17 is a photograph ofthe top of a portion ofthe coated substrate , , produced according to another embodiment ofthe present invention;

FIG. 18 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention;

FIG. 19 is an illustration ofthe coated texture of FIG. 14;

FIG. 20 is an illustration ofthe coated texture of FIG. 15; _jr, FIG. 21 is an illustration ofthe coated texture of FIG. 16;

FIG. 22 is an illustration ofthe coated texture of FIG. 17;

FIG. 23 is an illustration ofthe coated texture of FIG. 18;

FIG. 24 is an illustration ofthe general type of macroscopic texture according to another embodiment ofthe present invention; ₂₅ FIG. 25 is an enlarged view of a portion of FIG. 24;

FIG. 26 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention;

FIG. 27 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention; O_Q FIG. 28 is a photograph ofthe top of a portion ofthe coated substrate produced according to another embodiment ofthe present invention;

FIG. 29 is an illustration ofthe coated texture of FIG. 26;

FIG. 30 is an illustration ofthe coated texture of FIG. 27;

FIG. 31 is an illustration ofthe coated texture of FIG. 28; r.e FIG. 32 is an illustration ofthe general type of macroscopic texture according to another embodiment ofthe present invention; and FIG. 33 is a graph ofthe results of scratch resistance tests for several coatings made according to various embodiments ofthe present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention provides a coating having a macroscopic texture that

- exhibits superior abrasion-resistance, aesthetic value, and ease of cleaning. It should be appreciated that an important aspect ofthe present invention is that the macroscopic texture is provided inherently by the coating itself. In addition, the present invention provides a pre-cured coating mixture and a process for using the pre-cured coating mixture to generate the coating ofthe present invention on a substrate.

, . It should be appreciated that the term "coating" refers to the cured coating that typically would reside as an outer or exposed layer on a substrate after it has been cured or finally processed. The terms "radiation-cured" and "thermally-cured" mean after curing has occurred; therefore, the coating ofthe present invention, for example, may also be referred to as a "radiation-cured coating" or a "thermally-cured coating." The terms

, - "radiation-curable" and"thermally-curable" mean prior to curing or capable of being cured, and the term "pre-cured" means prior to curing.

In one embodiment ofthe present invention, the pre-cured coating mixture generally comprises a radiation-curable resin and an initiator. The radiation-curable resin may be any resin capable of being cured using radiant energy. Radiant energy can be r_yr, transferred through wave phenomenon and subatomic particle movement. Most preferred forms of radiant energy are ultraviolet (UV) and electron beam energy. Preferably, the radiation-curable resin comprises organic monomers, oligomers, or both. U.S. Patent Nos. 4,169,167, 4,358,476, 4,522,958, 5,104,929, 5,585,415, 5,648,40, and 5,858,809, incorporated herein by reference, describe various resins, including crosslinkable r_ye (thermosetting) resins, that may be used in the present invention.

More preferably, the radiation-curable resin comprises a mixture of crosslinkable monomers and oligomers that contain on average from 1-20 reactive groups per molecule of monomer or oligomer, where the reactive group provides the functionality for polymerization upon exposure to radiation. More preferably, the number of reactive

_™ groups per molecular is from 1-6. Preferred reactive groups include acrylate, vinyl, lactone, oxirane, vinyl ether, and hydroxyl. More preferred reactive groups include acrylate, oxirane, vinyl ether, and hydroxyl. The most preferred monomers and oligomers, however, are acrylates. Acrylates have the following structure:

35 CH₂=CR-CO- where R can be hydrogen, or alkyl, including, but not limited to, methyl, ethyl, propyl, butyl, etc. These radiation-curable resins are readily available or may be synthesized by procedures well known to one of skill in the art. It is noted that the term "radiation-cured groups" refers to these reactive groups after they have been cured.

The oligomers and monomers can also have 1-100 non-radiation-curable

- functional groups per molecule of monomer or oligomer. Preferred non-radiation-curable functional groups include urethane, melamine, triazine, ester, amide, ethylene oxide, propylene oxide, and siloxane. More preferred non-reactive groups are urethane ester, ethylene oxide, and propylene oxide.

As will be further described below in connection with the process for making

, r, the coating ofthe present invention, the concentration ofthe radiation-curable resin is dependent upon several factors. In one preferred embodiment, the concentration ofthe radiation-curable resin is selected to provide an effective or desired viscosity ofthe pre- cured coating mixture. The effective viscosity ofthe pre-cured coating mixture is that viscosity capable of producing a macroscopic texture, described below, upon application of

₁ e the pre-cured coating mixture to a substrate and subsequent curing. Preferably, the viscosity ofthe pre-cured coating mixture is approximately 100,000-1,000,000 cPs at a shear rate of 0.150 s^"1 at the application temperature. Therefore, the radiation-cured resin may comprise approximately 50-99%, by weight ofthe pre-cured coating mixture to provide the desired viscosity. Preferably, the radiation-cured resin comprises approximately 70-99%, by

2_Q weight, ofthe pre-cured coating mixture. Of course, the viscosity ofthe pre-cured coating mixture, and, therefore, the concentration ofthe radiation-curable resin, will be affected by the use of additional components in the pre-cured coating mixture such as rheological control agents, which will be described below. Other factors that affect the concentration of the radiation-curable resin are well known to one of skill in the art. . e The initiator may be any chemical capable of assisting or catalyzing the polymerization and crosslinking ofthe radiation-curable resin upon exposure to radiation. The initiator may generally be a photoinitiator or photosensitizer. Such initiators are well known in the art and may be selected based upon the curing conditions used (e.g., curing in an inert environment or in air). Specifically, the initiator may be a free radical _n photoinitiator, a cationic photoinitiator, and mixtures of both of these. Preferred free radical photoinitiators include acyl phosphine oxide derivatives, benzophenone derivatives, and mixtures thereof. Preferred cationic photoinitiators include triarylsulphonium salts, diaryliodonium salts, ferrocenium salts, and mixtures thereof. It should be appreciated that the initiator refers to the initiator both before and after curing. Therefore, the initiator may r have a different chemical structure or composition in the radiation-cured coating after exposure to radiation. The concentration of a particular initiator is that amount necessary to provide satisfactory curing for a given pre-cured resin based upon the properties of that particular initiator. Such concentrations can be readily identified by one of skill in the art. A preferred concentration ofthe initiator is 0.01-10 parts per hundred resin (phr), and a more preferred concentration is 0.1-4 phr. The pre-cured coating mixture may also comprise a rheological control agent

(RCA), particularly if the pre-cured coating mixture does not have an inherent viscosity that is high enough to form a macroscopic texture upon application ofthe pre-cured coating mixture to a substrate. The RCA may be inorganic particles, organic solids, and mixtures of both.

. _ft The inorganic particles may be any inorganic solid having a size that is small enough to be included in the pre-cured coating mixture without deleteriously affecting the pre-cured coating mixture's ability to cure and adhere to a substrate. The particle should also be sufficiently small and/or closely match the refractive index ofthe cured coating such that the opacity ofthe cured coating is minimized. The particle should also not

, r deleteriously affect the cured coating's abrasion resistance and in some cases it can improve that property. Additionally, the particle should not deleteriously affect thie resistance ofthe cured coating to chemical attack by strongly basic aqueous media (i.e., the alkali resistance ofthe coating), since such alkali resistance is important in flooring materials. It should be appreciated that the size of these particles is such that they do not ryrx directly provide or contribute to the macroscopic texture. Preferred sizes ofthe inorganic particles are 1-100 nm, where 10-60 nm are most preferred.

Preferably, the inorganic particles are metal oxides, metals, or carbonates, where metal oxides are preferred. More preferably, the inorganic particles are alumina, aluminosilicates, alumina coated on silica, silica, firmed alumina, fumed silica, calcium rye carbonate, and clays. Still more preferred is alumina due to its superior hardness (for abrasion resistance) and for its greater alkali resistance relative to silica. Most preferred is nanometer-sized alumina with a particle size range of 27-56 nm due to the enhanced cured coating transparency afforded by such small particles when they are well-dispersed (e.g., through the use of an appropriate amount and type of coupling agent). However, since o alumina has a higher refractive index (i.e., ~1.7) than most organic coatings and silica (both ~1.5), it may be envisioned that a nanometer-sized aluminosilicate material will give the optimal combination of transparency, abrasion resistance, and alkali resistance.

The inorganic particles may comprise approximately 1-80%, by weight, of the pre-cured coating mixture, more preferably 1-50%, by weight, and most preferably 1- o e 25%, by weight. Even more preferably, if nanometer-sized alumina is used, its concentration is approximately 1-40%, by weight, ofthe pre-cured coating mixture. If fumed silica is used, its concentration is approximately 1-10%, by weight, ofthe pre-cured coating mixture. If nanometer-sized crystalline silica is used, its concentration is approximately 10-30%, by weight, ofthe pre-cured coating mixture. If exfoliated clay is used, its concentration is approximately 10-30%, by weight, of the pre-cured coating mixture. e Similarly, the organic solids may be any organic solid having a size that is small enough to be included in the pre-cured coating mixture without deleteriously affecting the pre-cured coating mixture's ability to cure and adhere to a substrate. As with the inorganic particles, the organic particles should also not deleteriously affect the cured coating's transparency or abrasion resistance. Unlike the inorganic particles, the organic

, particles may dissolve or partially dissolve into the pre-cured resin at elevated temperature and thicken the pre-cured coating mixture upon cooling. The organic solids may be low molecular weight waxes containing functionality such as acid, amine, amide, hydroxyl, urea; polymers of ethylene glycol; polymers of propylene glycol; natural polymers such as guar, gelatin, and corn starch; polyamides; polypropylene; and mixtures of any of these.

₁ - Most preferred are functional waxes. The organic solids may comprise approximately 1- 50%, by weight, ofthe pre-cured coating mixture. More preferably, the organic solids comprise between approximately 1-20%, by weight. Most preferably, if functional waxes are used, their concentration is approximately 1-10%, by weight, ofthe pre-cured coating mixture. As will be described below in connection with the process for making the coating

2 ofthe present invention, the RCA may added for several purposes.

A coupling agent or dispersing agent may also be added for purpose of aiding the dispersion ofthe RCA in the pre-cured coating mixture. The coupling agent may be any material that provides surfactant-like properties and is capable of enhancing the dispersion ofthe RCA in the pre-cured coating mixture, in particular, the dispersion of r inorganic particles. The coupling agent ideally forms a chemical and/or physical bond with the pre-cured coating mixture and the inorganic particle, which improves the adhesion of the particle to the pre-cured coating mixture. Generally, the coupling agent is a organo- silicon or organo-fluorine containing molecule or polymer. Preferred organo-silicon materials are organosilanes and more preferably a prehydrolyzed organosilane. The n coupling agent may also be vinyl phosphonic acid or mixtures of phosphonic acid with the prehydrolyzed organosilane. The concentration ofthe dispersing agent may be approximately 0.1-20%, by weight, in the pre-cured coating mixture, and more preferably approximately 0.1-15%, by weight.

A flatting agent may also be added to the pre-cured coating mixture ofthe

05 present invention. Flatting agents are well known in the art. Preferred flatting agents include organic particles having a size of approximately 0.1-100 microns, inorganic particles having a size of approximately 0.1-100 microns, and mixtures of both. When flatting agents are used, a coupling agent may be needed to obtain good dispersion in the pre-cured coating mixture and good adhesion between the particle and the cured coating. For inorganic flatting agents, preferred coupling agents are organosilanes, mixtures of organosilanes, and low surface tension monomers and oligomers. For organic flatting

_<- agents, preferred coupling agent include organosilanes, mixtures of organosilanes, and low surface tension monomers and oligomers. The particle size selected is such that it is about the same size as the coating thickness or smaller. More preferred flatting agents include silica, alumina, polypropylene, polyethylene, waxes, ethylene copolymers, polyamide, polytefrafluoroetliylene, urea-formaldehyde and combinations thereof. The concentration of

₁ r. the flatting agent may be approximately 2-25%, by weight, ofthe pre-cured coating mixture, and more preferably is 5-20%, by weight.

In addition to the foregoing components ofthe pre-cured coating mixture, texture-producing particles may also be added. Such texture-producing particles have an effective size or an average diameter that is larger than the pre-cured coating thickness after

, e it has been applied to a substrate. These texture-producing particles, therefore, may act to provide the macroscopic texture ofthe coating ofthe present invention. It should be appreciated that these texture-producing particles may be added to a pre-cured coating mixture that has an effective viscosity for macroscopic texture or to a pre-cured coating mixture that does not have an effective viscosity for macroscopic texture, h the latter case,

2^ the macroscopic texture would be produced only by the texture-producing particles. The degree of texture provided by the texture-producing particles is controlled by the ratio ofthe particle size to the thickness ofthe cured coating. As this ratio increases from 1, the texture becomes macroscopic and can be made more aggressive (visibly more rough) as the ratio is increased. The degree of aggressiveness ofthe texture is r_ye determined by the desired end use properties such as abrasion resistance and cleanability. It is important that the particles selected have good adhesion to the cured coating. These particles can be inorganic or organic materials. A coupling agent may be necessary to obtain good dispersion in the pre-cured coating mixture and good adhesion between the particle and the cured coating. Preferred inorganic particles are glass, ceramic, alumina, on silica, aluminosilicates, and alumina coated on silica. Preferred coupling agents for inorganic texture-producing particles are organosilanes. Preferred organic particles are thermoplastic and thermosetting polymers. For inorganic flatting agents, preferred coupling agents are organosilanes, mixtures of organosilanes, and low surface tension monomers and oligomers. For organic flatting agents, preferred coupling agents include organosilanes, o mixtures of organosilanes, and low surface tension monomers and oligomers. Most preferred organic particles are polyamide, including nylons, specifically, nylon 6 and nylon 12 (although one of skill in the art will recognize that other nylons may be used in the present invention), polypropylene, polyethylene, polytefrafluoroetliylene, ethylene copolymers, waxes, epoxy, and urea-formaldehyde. Preferred average particle size of both organic and inorganic particles is 30-350 μm. Most preferred is 30-150 μm. Preferred concentration of particles in the pre-cured coating mixture is 1-30%, by weight. The most preferred concentration is 5 - 15 % by weight.

A preferred embodiment of a pre-cured coating mixture ofthe present invention comprises, by weight, 79.44% of a resin mixture comprising, by weight, 53.4% urethane acrylate (Alua 1001, available from Congoleum Corporation, Mercerville, NJ), 8.8% ethoxylated diacrylate (SR 259 available from Sartomer, Exton, PA), 24.3%

- r, propoxylated diacrylate (SR 306 available from Sartomer, Exton, PA), 13.4% ethoxylated trimethlyolpropane triacrylate (SR 454 available from Sartomer, Exton, PA), and 0.1% acylphosphine oxide (Luceirin TPO available from BASF, Charlotte NC); 12.00% flatting agent comprising 5 micron nylon particles (Orgasol 2001 UD available from Atofma, Philadelphia, PA); 6.25% texture-producing particles comprising 60 micron nylon 12

, particles (Orgasol 2002 ES 6 available from Atofma, Philadelphia, PA); 2.00% alumina RCA having a particle size distribution in the range of 27-56 nm (Nanotek Alumina #0100 available from Nanophase Technologies Corp. Burr Ridge, IL); and 0.31% prehydrolyzed silane as an RCA coupling agent comprising 0.21% 3-methacryloxypropyltrimethoxysilane (Z-6030 available from Dow Corning, Midland, MI), 0.015% glacial acetic acid, 0.015%

2^ deionized water, and 0.07% ethanol, prehydrolyzed as described in Example 1 below. As such, a preferred cured coating according to the present invention is that coating produced using the above preferred pre-cured coating mixture. In particular, this pre-cured coating mixture and the resulting cured coating are preferred for use on sheet flooring as a substrate. An even more preferred embodiment of a pre-cured coating mixture ofthe > present invention comprises, by weight, 84.59% of a resin mixture comprising, by weight, 53.4% urethane acrylate (Alua 1001, available from Congoleum Corporation, Mercerville, NJ), 8.8% ethoxylated diacrylate (SR 259 available from Sartomer, Exton, PA), 24.3% propoxylated diacrylate (SR 306 available from Sartomer, Exton, PA), 13.3% ethoxylated trimethlyolpropane triacrylate (SR 454 available from Sartomer, Exton, PA), and 0.2% on acylphosphine oxide (Luceirin TPO available from BASF, Charlotte, NC); 8.0% flatting agent comprising 5 micron nylon particles (Orgasol 2001 UD available from Atofma, Philadelphia, PA); 6.25% texture-producing particles comprising 60 micron nylon 12 particles (Orgasol 2002 ES 6 available from Atofma, Philadelphia, PA); 1.0% alumina RCA having a particle size distribution in the range of 27-56 nm (Nanotek Alumina #0100

₃₅ available from Nanophase Technologies Corp. Burr Ridge, IL); and 0.16% prehydrolyzed silane as an RCA coupling agent comprising 0.21% 3-methacryloxypropyltrimethoxysilane (Z-6030 available from Dow Corning, Midland, MI), 0.015% glacial acetic acid, 0.015% deionized water, and 0.07% ethanol, prehydrolyzed as described in Example 1 below. As such, a preferred cured coating according to the present invention is that coating produced using the above preferred pre-cured coating mixture. In particular, this pre-cured coating mixture and the resulting cured coating are preferred for use on sheet flooring as a substrate. r In another preferred embodiment, a pre-cured coating mixture for use with tile as the substrate comprises, by weight, 35.303% ethoxylated trimethylolpropane triacrylate (SR 454, available from Sartomer, Exton, PA), 41.050% polyester acrylate (Laromer PE56F, available from BASF, Charlotte, NC), 5.747% urethane acrylate (Alua 1001, available from Congoleum Corporation, Mercerville, NJ), 0.330% acylphosphine

, ₀ oxide (Luceirin TPO, available from BASF, Charlotte, NC), 8.000% 3 micron inorganic flatting agent (Acematte OK 412, available from Degussa Corp., Ridgefield Park, N.J.), 2.323% prehydrolyzed silane as an RCA coupling agent comprising 0.21% 3- methacryloxypropyltrimethoxysilane (Z-6030 available from Dow Corning, Midland, MI), 0.015%) glacial acetic acid, 0.015% deionized water, and 0.07% ethanol, prehydrolyzed as

₁ described in Example 1 below, 1.000% inorganic RCA (Nanotek Alumina #0100, available from Nanophase Technologies, Burr Ridge, IL), and 6.250% 60 micron texture-producing particle (Orgasol 2002 ES6, available from Atofina, Philadelphia, PA). As such, a preferred cured coating according to the present invention is that coating produced using the above preferred pre-cured coating mixture.

2_β In another embodiment ofthe present invention, the pre-cured coating mixture comprises a thermally-curable resin and a thermal initiator. The thermally-curable resin may be any resin capable of being cured using thermal energy. The thermally-curable resins preferably include organic monomers, oligomers, or both. U.S. Patent Nos. 4,169,167, 4,358,476, 4,522,958, 5,104,929, 5,585,415, 5,648,40, and 5,858,809, ye incorporated herein by reference, describe various resins, including crosslinkable

(thermosetting) resins, that may be used in the present invention. The thermal initiator used for thermally-curable coatings ofthe present invention is any thermal initiator known in the art. Preferably, the free radical thermal initiator is an organic peroxide, such as tertiary- butyl peroxybenzoate. o More preferably, the thermally-curable resin comprises a mixture of crosslinkable monomers and oligomers that contain on average from 1-20 reactive groups per molecule of monomer or oligomer, where the reactive group provides the functionality for polymerization upon exposure to heat. More preferably, the number of reactive groups per molecular is from 1-6. Preferred reactive groups include acrylate, vinyl, lactone, or oxirane, vinyl ether, and hydroxyl. More preferred reactive groups include acrylate, oxirane, vinyl ether, and hydroxyl. The most preferred monomers and oligomers, however, are acrylates. Acrylates have the following structure:

CH₂=CR-CO-

r where R can be hydrogen, or alkyl, including, but not limited to, methyl, ethyl, propyl, butyl, etc. These thermally-curable resins are readily available or may be synthesized by procedures well known to one of skill in the art. It is noted that the term "thermally-cured groups" refers to these reactive groups after they have been cured.

The oligomers and monomers can also have 1-100 non-thermally-curable

_{1 Λ} functional groups per molecule of ester, amide, ethylene oxide, propylene oxide, and siloxane. More preferred non-reactive groups are urethane, ethylene oxide, and propylene oxide.

As will be further described below in connection with the process for making the coating ofthe present invention, the concentration ofthe thermally-curable resin is

H r dependent upon several factors. In one preferred embodiment, the concentration ofthe thermally-curable resin is selected to provide an effective or desired viscosity ofthe pre- cured coating mixture. The effective viscosity ofthe pre-cured coating mixture is that viscosity capable of producing a macroscopic texture, described below, upon application of the pre-cured coating mixture to a substrate and subsequent curing. Preferably, the viscosity

2_Q ofthe pre-cured coating mixture is approximately 100,000-1,000,000 cPs at a shear rate of 0.150 s^"1 at the application temperature. Therefore, the thermally-cured resin may comprise approximately 50-99%, by weight ofthe pre-cured coating mixture to provide the desired viscosity. Preferably, the thermally-cured resin comprises approximately 70-99%, by weight, ofthe pre-cured coating mixture. Of course, the viscosity ofthe pre-cured coating ye mixture, and, therefore, the concentration ofthe thermally-curable resin, will be affected by the use of additional components in the pre-cured coating mixture such as rheological control agents, which will be described below. Other factors that affect the concentration of the thermally-curable resin are well known to one of skill in the art.

As with the radiation-curable coatings ofthe present invention, the on thermally-cured coatings ofthe present invention also provide a macroscopic texture. A such, the same rheological control agents, coupling agents, flatting agents, and texture- producing particles previously described may be used with the thermally-curable coatings of the present invention. The manner of use of these agents with the thermally-curable coatings ofthe present invention is the same as previously described for the radiation- or curable coatings. A preferred embodiment of a thermally pre-cured coating mixture ofthe present invention comprises, by weight, 44.83% urethane acrylate (Alua 1001, available from Congoleum Corporation, Mercerville, NJ), 6.92% ethoxylated diacrylate (SR 259 available from Sartomer, Exton, PA), 20.53% propoxylated diacrylate (SR 306 available from Sartomer, Exton, PA), 11.25% ethoxylated trimethlyolpropane triacrylate (SR 454 e available from Sartomer, Exton, PA), 1.06% tertiary-butyl peroxybenzoate (P-20 available from Norac, Azusa, CA,) 8% flatting agent comprising 5 micron nylon 12 particles (Orgasol 2001 UD available from Atofina, Philadelphia, PA), 6.25% texture-producing particles comprising 60 micron nylon 12 particles (Orgasol 2002 ES6 available from Atofina, Philadelphia, PA), 1% alumina RCA having a particle size distribution in the range of 27-56

₁ n nm, and nominally 35 nm, (Nanotek Alumina #0100 available from Nanophase

Technologies Corp. Burr Ridge, IL), and 0.16%o prehydrolyzed silane as an RCA coupling agent comprising 0.21% 3-methacryloxypropyltrimethoxysilane (Z-6030 available from Dow Corning, Midland, MI), 0.015% glacial acetic acid, 0.015% deionized water, and 0.07% ethanol, prehydrolyzed as described in Example 1 below. As such, a preferred cured ι r coating according to the present invention is that coating produced using the above preferred pre-cured coating mixture. Another preferred embodiment is the use ofthe foregoing pre-cured coating mixture and resulting cured coating with sheet flooring as the substrate.

It should be appreciated that many additional components known in the art

2_Q may be added to the coatings ofthe present invention. These additional components may include fillers, plasticizers, antioxidants, optical brighteners, defoamers, stabilizers, wetting agents, mildewcides and fungicides, surfactants, adhesion promoters, colorants, dyes, pigments, slip agents, fire and flame retardants, and release agents.

FIG. 1 illustrates a perspective view of a coated substrate 10 according to

25 one embodiment ofthe present invention, h FIG. 1 a coating 12 is adhered to a substrate 14, where the coating 12 is produced by curing the pre-cured coating mixture made according to the present invention either being a radiation-curable coating mixture or a thermally-curable coating mixture. It should be appreciated that the coating ofthe present invention may be used in conjunction with any substrate that is capable of remaining on attached to the coating after curing. Substrates that may be used include those containing plastic such as polyvinyl chloride, metal, cellulose, fiberglass, wood, and ceramic, among others. Preferably, the subsfrate is a flooring material, such as a floor tile or flexible sheet, where the surface ofthe coating having the macroscopic texture is the exposed surface of the flooring or that surface upon which one would walk. The superior scratch resistance of

^^ the coating ofthe present invention, and the ease of cleaning, make the coating particularly suitable for flooring applications. As noted, the coating ofthe present invention has an inherent macroscopic texture. The term "macroscopic texture" is intended to encompass any textural features, regular or irregular, produced on the surface of a coating that are visible to the naked eye at close range, as opposed to microscopic texture that would require the use of a microscope to view the texture. The macroscopic texture ofthe present invention may also provide a non- r smooth surface such that the texture is apparent to the touch. Additionally, the macroscopic texture when produced by the use of texture-producing particles may be visible to the naked or unaided eye at a close range. The macroscopic texture may have any design, shape, or pattern on the surface ofthe coating. This macroscopic texture (not shown in FIG. 1) is provided by the coating 12 and is visible to the naked eye when viewing the coating 12 on

, ₀ the coated substrate 10.

As described above in connection with the pre-cured coating mixture, the macroscopic texture may be provided by different components in the pre-cured coating mixture. In one embodiment ofthe invention, the macroscopic texture is provided by a pre- cured coating mixture having an effective viscosity capable of providing a macroscopic

₁ r texture. In another embodiment, the macroscopic texture is provided by a pre-cured coating mixture that comprises texture-producing particles having an effective size to produce a cured coating with the macroscopic texture. In yet another embodiment, the macroscopic texture may be provided by a pre-cured coating mixture having both an effective viscosity and texture-producing particles. Several examples of various coatings made according to

2_Q various embodiments ofthe present invention are described below, which provide examples ofthe various macroscopic textures. These examples are intended to provide examples of how a macroscopic texture may be achieved, but are not intended to be limiting as to the types, shapes, or patterns of macroscopic texture that maybe obtained.

In addition, it was surprisingly found that the coatings ofthe present rye invention with macroscopic texture have superior scratch and abrasion resistance as measured by a Taber scratch test and traffic were panels. Scratch test results for various coatings made according to the present invention are described in the examples below.

It should be appreciated that the concentrations ofthe various non-reactive groups and components in the cured coating are assumed to be the same in the pre-cured o coating mixture. As will be described below, the coating ofthe present invention is made by applying the pre-cured coating mixture to a substrate followed by either radiation-curing or thermal curing. Therefore, it is assumed that the concentrations ofthe various non- reactive groups and components in the pre-cured coating mixture will not change substantially during curing and will remain substantially the same. However, those skilled o in the art will recognize that otlier factors, such as coating application processing conditions, may induce some degree of variability in these concentrations. FIG. 2 illustrates a cross-sectional view of a coated substrate according to another embodiment ofthe present invention. FIG. 2 shows a coated substrate 20 having a coating 22 on a coated substrate layer 24 and additional substrate layers 26 attached to the coated substrate layer 22 on the side opposite the coating 22. The coating 22 illustrates the macroscopic texture provided by the coating 22. As shown in FIG. 2, it should be r appreciated that the macroscopic texture ofthe coatings made according to the present invention is inherent in, or provided by, the coating itself and is independent ofthe substrate to which the coating is adhered. Therefore, it should be appreciated that this coating is significantly different from coatings that naturally conform to a substrate having a texture or for cured coatings that are impressed with a pattern.

. „ FIG. 3 illustrates a cross-sectional view of a coated substrate according to yet another embodiment ofthe present invention. FIG. 3 shows a coated substrate 30 having a coating 32 on a coated substrate layer 34 and additional substrate layers 36 attached to the coated substrate layer 32 on the side opposite the coating 32. FIG. 3 illustrates that the coatings ofthe present invention may also be applied to substrates that already have

, r macroscopic texture themselves due to embossing or some other method. Thus, two or more textures can exist on a given coated substrate, i.e., texture from the coating and texture from the substrate. As illustrated in FIG. 3, the macroscopic texture ofthe coating 32 may be such that it conforms to the texture ofthe underlying substrate 34. Alternatively, the macroscopic texture may be applied so that it does not conform to the texture ofthe

2 underlying substrate.

FIG. 4 is a process flow diagram of a process for making a coating according to one embodiment ofthe present invention, hi the step 40, the initiator is dissolved in the radiation-curable resin. The initiator and the resin may be mixed in any manner typically used in the art such that the initiator is dissolved into the resin phase.

,ye In the step 42, any RCA, coupling agent, flatting agent, or texture-producing particles are added to the mixture produced in the step 40. It should be appreciated that for the RCA, flatting agent, and/or texture-producing particles, a coupling agent may also be used. In this case, the particles and the coupling agent may simply be added to the mixture either simultaneously or sequentially, without the need to pre-freat the particles with the o coupling agent before adding these components to the mixture. This avoids the use of a solvent that may create diffusion pathways for staining materials to diffuse through and stain the coating. In some cases, it is desirable to make a concentrated mixture of RCA, coupling agent, flatting agent, and/or texture-producing particles in a liquid medium and dilute it down into the pre-cured coating mixture. This concentrate is called a master batch o and is well known in the art. In the step 44, all ofthe components are mixed to produce the pre-cured coating mixture. The step 44 may be accomplished using a Cowles blade mixer, ultrasonic probe, or other high shear mixer. It should be appreciated that during mixing the temperature ofthe mixture should not be allowed to increase significantly. For example, increases in temperature to approximately 100°C may result in thermal reaction ofthe resin causing gelation. In cases where an organic solid is used as a RCA, the temperature during mixing should be allowed to increase to a temperature that is adequate to dissolve the organic solid, for example, 70 °C. The temperature should then be reduced to ambient temperature, thereby producing a highly viscous pre-cured coating mixture.

In one embodiment ofthe invention, the pre-cured coating mixture produced in the step 44 must have the necessary viscosity to produce a macroscopic texture upon application and subsequent curing ofthe pre-cured coating mixture on a substrate. Preferably, the viscosity ofthe pre-cured coating mixture should be approximately 100,000- 1,000,000 cPs at a shear rate of 0.150 s^"1 at the application temperature. As will be further discussed below a viscosity that is too low does not provide a macroscopic texture, and a viscosity that is too high results in poor distribution of the pre-cured coating mixture over the substrate surface.

To obtain the requisite viscosity in the pre-cured coating mixture requires the use ofthe appropriate concentration ofthe radiation-curable resin. It should be appreciated that the radiation-curable resin may alone be used to provide the requisite viscosity, but that it may be desirable to use a RCA in conjunction with the radiation-curable resin to provide the requisite viscosity. If a RCA is used, then the requisite viscosity will be determined by using the appropriate concentration of both the radiation-curable resin and the RCA. It should be appreciated that in either case, the concentration of these components will be dependent upon the intrinsic properties of each. It should also be appreciated that the addition of other components, such as coupling agents and flatting agents, may also affect the viscosity ofthe pre-cured coating mixture. Therefore, these other components may also need to be considered in determining the appropriate concentrations ofthe radiation-curable resin and the RCA, if used. hi the step 46, the pre-cured coating mixture is distributed across the surface of a substrate. The step 46 requires that the pre-cured coating mixture is initially applied to the substrate surface and then distributed across the surface. Application ofthe pre-cured coating mixture to the surface ofthe substrate may be accomplished by any means known in the art for placing a high viscosity material onto a substrate. For example, the pre-cured coating mixture may be pumped to the substrate and placed on the substrate using a slot die. It should be appreciated that it may be necessary to heat the pre-cured coating mixture to reduce the viscosity to allow for its placement on the substrate surface; however, it is

- 18 -

SUBSfΪTOTE SHEET (RULE 26) important that the pre-cured coating mixture be allowed to cool prior to actually distributing it across the substrate surface, so that it has the required viscosity necessary to generate macroscopic texture.

Distributing the pre-cured coating mixture across the substrate surface may be accomplished using any means known in the art; however, it is important that such r means are capable of moving a high viscosity material across the surface in a manner that leaves the pre-cured coating mixture in the form ofthe desired macroscopic texture that will become fixed upon curing. It should be appreciated that it is preferred to uniformly distribute the pre-cured coating across the substrate surface, but such uniform distribution should not be confused with a completely smooth distribution ofthe pre-cured coating

, r, mixture across the substrate surface. After the pre-cured coating mixture has been distributed, the macroscopic texture should be apparent, as it is this texture that will be fixed on the substrate after curing. Therefore, it should be appreciated that, in addition to the use of an effective viscosity and/or texture-producing particles, the macroscopic texture can be altered using different techniques for applying the pre-cured coating mixture to a

₁5 substrate.

Before discussing specific pre-cured coating application methods, it should be noted that the pre-cured coatings in this embodiment can have a viscosity that is dependent on both the amount of shear applied to the pre-cured coating mixture, as well as the amount of time during and after the application ofthe shear. This type of behavior is

2_Q referred to in the art as thixotropic. Thus, the production of texture is dependent on the viscosity ofthe pre-cured coating under the shear ofthe application equipment.

One method for distributing the pre-cured coating mixture uniformly across the substrate surface in a manner that produces a desired macroscopic texture is by use of an air knife. The use of an air knife requires that the pre-cured coating mixture has been r_ye properly and uniformly applied to the substrate surface to allow the air knife to uniformly distribute the pre-cured coating mixture over the substrate surface. It should be appreciated that the relatively high viscosity ofthe pre-cured coating mixture at low shear rates allows the air knife to produce a macroscopic texture and prohibits a macroscopically smooth distribution ofthe pre-cured coating mixture. Thus, the pre-cured coating in this on embodiment ofthe present invention has a high enough viscosity under the shear ofthe air knife to produce a macroscopic texture and not level into a macroscopically smooth surface. More specifically, the air knife actually generates a wave of pre-cured coating mixture that flows over the substrate surface as it passes by the air knife. This wave leaves behind a metered pre-cured coating with ripples that are the macroscopic texture.

35 It should be appreciated that the operating parameters ofthe air knife can be changed to produce varying macroscopic textures. These parameters include the line speed (dwell time under the air knife), air pressure, angle of attack, and the gap between the substrate and the air knife. Therefore, different macroscopic textures providing a variety of aesthetic looks may be produced.

It can now be appreciated that one method for determining whether the pre- cured coating mixture has the appropriate viscosity is by distributing the pre-cured coating r mixture on the desired substrate using an air knife. If the viscosity ofthe pre-cured coating under the shear ofthe air knife is too low, the coating will level and produce a macroscopically smooth surface. If the viscosity under shear is too high, the pre-cured coating mixture will be blown off the substrate resulting in an incompletely or uncoated substrate.

, r. Another method for distributing the pre-cured coating mixture uniformly across the substrate surface in a manner that produces a desired macroscopic texture is by use of a roll coater. The roll coater both applies and coats the pre-cured coating mixture to the substrate. The texture is generated by the roller being in direct contact with the coating on the subsfrate. As the substrate passes under the roller, the roller passes away from the

, r substrate pulling or splitting some ofthe pre-cured coating from the substrate. This splitting results in macroscopic texture that can be varied with the roll coater operating parameters including line speed, gap between the roller and the substrate, roller material type (roller covering), engraving pattern on the roller, roller speed relative to the line speed and roller diameter. ryn. hi the step 48 the pre-cured coating mixture that has been distributed over the substrate surface and is in the form ofthe desired macroscopic texture is cured using radiation. This curing step acts to polymerize the pre-cured coating mixture to fix the macroscopic texture in place and adhere it to the substrate surface, thereby producing a radiation-cured coating on the substrate. The step 48 may be conducted under conditions

2 e typical of radiation-curing processes depending upon the particular radiation-curable resin and initiator used. For example, the step 48 may be conducted using radiation lamps in an inert atmosphere. It should be appreciated that if a matte finish is desired, the radiation lamps can be used in an ambient atmosphere followed by an inert atmosphere. Thus, a matte finish can be superimposed on the macroscopic texture if a flatting agent is used. on It should be appreciated that process steps described in connection with FIG.

4 are equally applicable to the use of a thermally-curable coating mixture made according to the present invention. In this case, the step 40 would be directed to a thermally-curable resin and a thermal initiator, and the step 48 would be directed to thermal curing and the formation of a thermally-cured coating.

3 In another embodiment ofthe invention, the pre-cured coating mixture utilizes texture-producing particles to produce the macroscopic texture ofthe coating. These texture-producing particles may be added to the pre-cured coatmg mixture in the step 42. These are mixed in the same manner as the previous embodiment, but the effective viscosity ofthe pre-cured coatmg can be much lower, typically 50-5000 cPs at a shear rate of 0.150 s^"1 at the application temperature, as the macroscopic texture is provided by the texture-producing particles and not necessarily by the viscosity ofthe pre-cured coating r mixture. It should be appreciated, however, that these texture-producing particles can be used in combination with a pre-cured coatmg mixture that does have an effective viscosity as well. The pre-cured coating mixture containing these texture-producing particles is then processed in a similar manner using the steps 44, 46, and 48. Specifically, this pre-cured coating mixture can be mixed in a similar manner as described above in the step 44. This

, r, pre-cured coatmg mixture may be applied and coated on a substrate in the step 46 using methods known in the art, including the use of an air knife, roll coater, spray coating, curtain coating, and other coating application methods. Lastly, this pre-cured coating mixture may be cured in a similar manner as described above in the step 48.

It should be appreciated that the foregoing description ofthe methods used to

, r generate the coatings ofthe present invention in the context of a radiation-cured coating is equally applicable to the generation ofthe thermally-cured coatings ofthe present invention.

FIG. 4B illustrates a cross-sectional view of a coated substrate according to yet another embodiment ofthe present invention. In this embodiment, the coated substrate 400 is a sheet-style flooring material. This sheet flooring 400 comprises a bottom layer 401 r_yr, made of felt or cellulose paper. On top ofthe bottom layer 401 is a gel layer 403, typically comprising a polyvinyl chloride plastisol, and on top of this gel layer 403 is a print layer 405 that may or may not comprise ink to provide a decorative pattern (not shown). On top ofthe print layer 405 is a clear wear layer 407 that is typically made of a polyvinyl chloride plastisol. On top ofthe wear layer 407 is a top coat 409, which may be any ofthe coatings

2 ofthe present invention. A preferred construction of this sheet flooring comprises a felt layer of approximately 23.5 mils, a gel layer of approximately 57 mils, a print layer of nominal or relatively small thickness, a wear layer of approximately 20 mils, and a top coat of approximately 1-1.3 mils.

The basic sheet floor manufacturing process is well known in the industry. o Generally, a felt backing is coated with a gel layer, typically a plastisol. This gel layer is then gelled to solidify it. A decorative print may then be applied to the top of this gel layer. The inks used in printing may be used in cooperation with the gel layer to inhibit a blowing agent that may be used in the gel layer to subsequently enable chemical embossing ofthe gel layer to provide additional aesthetics. Additionally, another plastisol-type layer maybe

05 applied on top ofthe print layer to provide protection for the decorative print or chemically embossed effects. This layer is typically referred to as a wear layer; however, a topcoat may also be used on top ofthe wear layer to protect it from scuffing or marring. This topcoat maybe a thermal or radiation-curable coating according to any ofthe embodiments ofthe present invention. hi a preferred embodiment ofthe sheet floor manufacturing process, a 6 to 16 feet wide felt is coated with a liquid polyvinly chloride (PVC) plastisol (e.g., PVC resin e particles dispersed in plastisizers (e.g., phthalates)). Mixed into this liquid plastisol, which is called a gel layer, is a blowing agent (e.g., azodicarbonamide) and a catalyst (e.g., zinc oxide). The catalyst lowers the decomposition temperature ofthe azodicarbonamide and increases the amount of nitrogen gas produced by the azodicarbonamide decomposition. The liquid gel layer on felt is then gelled at a temperature below the decomposition

, r. temperature ofthe blowing agent (approximately 300 °F) to provide a solid non-foamed and smooth surface for printing. After the gel layer is solidified, it is printed with the desired design using water-based inks, thereby creating the print layer, hi some ofthe inks, a compound that inhibits the decomposition ofthe blowing agent is present. After the ink is printed, the PVC-coated felt is wound up and allowed to age about 24 hours. This aging

, r allows the inhibitor in the ink to diffuse into the gel layer, where it is believed that the inhibitor reduces the effectiveness ofthe catalyst.

The gel coated felt is then unwound on another production line where it is coated with another PVC plastisol that is formulated to be a clear layer when solidified. This liquid layer, called the wear layer since it protects the print from wearing, is then r_yr, solidified (referred to as fused) at 385 °F for about 1.5 minutes. At this temperature, the azodicarbonamide blowing agent is activated in the gel layer resulting in the foaming of this layer which increases its thickness by forming a cell structure due to the gas formation. The ratio ofthe gel thickness before and after foaming is called the blow ratio, which is typically 2:1 to 4:1. h the areas ofthe gel directly below the ink containing inhibitor, less foaming

₂₅ occurs giving less of an increase in gel layer thickness. This process results in an embossing effect (i.e., chemical embossing). After the warm fused sheet leaves the oven it can be mechanically embossed for additional aesthetics.

While these PVC wear layers provide protection to the underlying print, they are susceptible to scuffing and marring due to the softness ofthe thermoplastic. To reduce n the scuffing, these PVC surfaces can be either waxed or coated with a thermosettmg coating (known as a "no wax coating") such as a radiation-curable coating (e.g., urethane acrylate) or thermally-curable coating made according to the present invention. If the flooring is to have a no wax finish, a radiation-curable or thermally-curable coatmg is then applied after the wear layer is cleaned with an acetic acid solution to remove dirt and oils. Excess

35 coating is applied to the wear layer using a roller, where the roller transfers the coating from a trough to the wear layer surface. An air knife immediately meters the excess coating, where the excess is recycled back into the trough. As partially described in Example 19, the process conditions ofthe coating application and metering such as line speed (dwell time under the air knife), air knife pressure, angle of air knife relative to the web, gap between air knife and web, and the speed ofthe application roll relative to the line speed affect the coating texture. The uncured metered coating is then cured thermally or under UV lamps

5 where both air and nitrogen atmospheres may be used for UV curing depending on the gloss ofthe coating desired.

The degree of texture ofthe radiation-curable or thermally-curable coating or top coat is dependent on the ratio of wet coating thickness to particle diameter. In using an air knife, the air knife pressure and the web (line) speed are the critical parameters for

, r, achieving texture. For example, low line speed and high air knife pressure result in a very thin coating due to increased metering. When the coating contains texture-producing particles, if the coating is too thin it can not hold the particles and a smooth non-textured coating results. If the line speed is high and the air knife pressure is low, the coating will be less metered and apply thick. If the coating is thicker than the texture-producing particles,

₁5 the coating will be smooth. Thus, there is an optimum set of process conditions to get texture in production that can be determined based upon the particular pre-cured coating mixture used.

Referring back to FIG. 3 wherein the macroscopic texture may be provided by an underlying layer in the flooring material, one embodiment ofthe present invention is ryry the use of texture producing particles in the wear layer of a flooring composition, such as that described in connection with FIG. 4B. h this embodiment, the texture is provided by the wear layer which may then be coated with a top coating that conforms to the underlying texture. By conforming to the underlying texture, the flooring composition will exhibit a macroscopic texture, such as a ceramic-like texture where the inherently textured coating

₂ layer is the PVC wear layer in this case. Alternatively, the top coating may be made according to the present invention to provide additional macroscopic texture to the flooring composition.

As noted above, the wear layer is constructed by applying PVC plastisols (dispersion of PVC particles in plastisizers) that have a viscosity of approximately 500-1600 on cP to a printed surface (e.g., using knife over roll coating) at 10-30 mils in thickness. The plastisol is then gelled at high temperature (e.g., 300-400 °F) to form the solid, clear thermoplastic wear layer. In generating macroscopic texture with texture-producing particles in the wear layer, the following variables are important: (1) the type of application methods used (e.g., knife over roll coater), (2) the high viscosity ofthe plastisol (typically

05 500-1600 cP at room temperature), and (3) the thickness ofthe applied wear layer (10-30 mils). By comparison, using an air knife with the lower viscosity coating containing texture- producing particles as discussed in previous embodiments ofthe present invention allows the liquid coating to be metered around the texture-producing particles to generate the macroscopic texture, hi addition, a radiation-curable or thermally-curable top coating with a lower viscosity (e.g., 50-250 cP) facilitates this metering, while the low application gauge (1-2 mils) allows fairly small particles (30-100 μm) to be used to provide texture in the

5 coating. Therefore, to achieve texture with particles in a wear layer, specific application methods are needed to address each of these variables.

In using a knife over roll coater to apply PVC plastisols, the knife over roll coater mechanically sets the wet coating thickness, thus the texture-producing particles in the plastisol must be smaller than the wet film thickness or streaks will be generated. Thus,

, r. to use a knife over roll coater, texture-producing particles have to be added to the plastisol that are smaller than the wet film thickness, or the particles have to be added after the plastisol is coated. If the texture-producing particles are added to the plastisol before coating, these particles must either increase in size or change aspect ratio during gelation such that they protrude from the gelled wear layer to provide the macroscopic texture, or the

, 5 wear layer must shrink during gelling to expose the particles.

With regard to swelling particles, U.S. Patent No. 5,627,231 describes a process of adding particles to a wear layer that swell during gelation to give the wear layer a ceramic-like texture. The particles added to the plastisol absorb plasticizer during the gelling process and swell to give texture. However, the particles continue to absorb

2_Q plasticizer and eventually become sticky. These sticky particles then attract dirt which quickly makes the floor dirty and hard to clean. As such, an alternative would be to utilize shrinking wear layer. Example 22 provides an example of a wear layer composition that shrinks thereby allowing for greater exposure ofthe texture-producing particles and providing the macroscopic texture.

2 If the particles are to be added after knife over roll coating, the particles can simply be wet flocked on to the surface ofthe coated, wet plastisol, and then gelled. This ensures that (1) the particles are on the surface ofthe plastisol and, therefore, can be much smaller than the thickness ofthe wet plastisol, and (2) the particles do not interfere with the coating application method since they are sprinkled on the wet plastisol and then the excess on particles removed (i.e., wet flocking) after the plastisol is applied. Example 23 demonstrates the use wet flocking.

To avoid the problem of mechanically setting the wet film thickness, a coating method such as air knife application can be used. However, in the present invention it is preferred to use plastisol viscosities that are much greater (500-1600 cP) than what is

25 recommended for the air knife (<500 cP). When high viscosity plastisols containing texture-producing particles are applied by an air knife, the plastisol entraps the particles

- 24 -

SUBSTlf CJTE SHEET (RULE 26) such that they are blown off the substrate leaving a smooth coating with no particles or texture. Thus, a standard plastisol must be modified to have a lower viscosity so that it can be metered around particles. An example of a plastisol with a low viscosity (200 cP) comprises by weight, 30.8% PVC resin (75HC available from Oxychem, Dallas, TX), 30.8% PVC resin (567 available from Oxychem, Dallas, TX), 28.4% plasticizer (N-6000

₅ available from Velsicol, Rose ont, EL), 4.7% plasticizer (S-375 available from Solutia, St. Louis, MO), 2.0% plasticizer (A-150 available from Exxon, Houston, TX), and 3.3% stabilizer (2347 available from OMG, Cleveland, OH).

As described above, the coatings ofthe present invention may also be utilized in connection with floor tiles. The vinyl tile manufacturing process and tile

, . construction for high-end "no wax" residential tiles are different from those of vinyl sheet floor and require specialized process and formulation changes to achieve macroscopically textured, radiation-cured or thermally-cured surface topcoats.

In general, tiles are manufactured by calendering and/or lamination processes. For example, a tile base comprising, for example, limestone, is made into a

, 5 continuous sheet to which a printed design and a cap film, which is positioned on top ofthe printed design for protection, may be laminated. Optionally, a topcoat may then be applied to the cap film for additional wear protection. This topcoat may be a thermal or radiation- curable coating according to any ofthe embodiments ofthe present invention. It should be appreciated that the general process for constructing tiles can be used to make tiles of any r_yrx tl icktiess or size.

In a preferred tile manufacturing process, 9" by 9", 12" by 12", 14" by 14", 16" by 16", and 18" by 18" vinyl tiles are made by first mixing PVC resin, plasticizer, pigments, and a high level (-80%) of limestone (calcium carbonate) filler in a blender held at 115-135 °F. The blended powder effluent is then transferred to a continuous mixer held

2 at 320-340 °F for fusion (i.e. chain entanglement) ofthe limestone-filled resin into thermoplastic pieces of various sizes. The thermoplastic pieces are next sent to calendering roll operations for partial softening and re-fusion ofthe limestone-filled resin into the shape of a continuous sheet having an exiting temperature of 250-270°F and a thickness of 50-200 mils. The continuous sheet of tile base is then carried via conveyor belt to a nip station for o lamination of a printed design using either 2 mil thick printed PVC film or 0.5 mil thick printed transfer paper. The latter case involves transferring the ink of a printed design, originally on a paper roll, to the tile base at the lamination nip (the paper is subsequently removed with a re-wind operation immediately following the lamination nip).

Next, the continuous sheet of tile base and laminated print layer is conveyed

25 to another nip for lamination of "cap film," which is an ~3 mil thick PVC film designed to protect the print layer. Both the cap film and print layer applications rely upon the nip pressure and incoming substrate temperature for lamination; the laminating rolls themselves are not heated. For floors requiring periodic waxing, the PVC cap film forms the uppermost layer ofthe manufactured tile construction (an end-user applied, sacrificial wax layer being the uppermost layer in practice). However, for "no-wax" floors, a thermosettmg topcoat is applied to the top ofthe PVC cap film during manufacture and forms a surface with

₅ sufficient durability that the need for a sacrificial wax layer is eliminated. Nevertheless, and regardless of its final designation as a waxed or no-wax floor tile, the continuous sheet of laminated tile base, print layer, and cap film is then optionally mechanically embossed and finally punched into 9" by 9", 12" by 12", 14" by 14", 16" by 16", or 18" by 18" tiles using a metal die. The edge material not punched out ofthe continuous sheet by the die is recycled

H ₀ back into the tile base mixing process. The cut tiles themselves are conveyed to either a final processing and packaging station (for tiles requiring waxing in practice) or to the topcoat application operation (for no-wax tiles).

The traditional topcoat application process for no-wax tiles involves the deposition and metering of a liquid film of thermally-curable or radiation-curable resin onto

_{1 5} the tile, followed by subsequent curing ofthe resin to form a durable thermoset topcoat. The traditionally preferred (but not exclusive) coating application method involves the use of a curtain coater to apply and meter ~3 mil of uncured UV-curable resin to the cap film surface ofthe tile. The coated, but uncured, tiles are then sent through a series of UV- processors containing UV lamps to induce cross-linking ofthe thermosetting resin, in the

_2Q case where the coating is a radiation-curable coating. (Alternatively, the tiles would be heated to induce the cross-linking in the case where the coating is a thermally-curable coating.) Final processing of most no wax tile products involves an annealing process at 110-125 °F for up to two days to remove processing stresses and to ensure dimensional stability, as well as an edge grinding process to ensure that smooth edges are present for

25 proper field installation. A thermosetting urethane backcoat is also applied with a roll- coater to balance the curling stresses imparted on the tile by the topcoat. The physical location ofthe backcoater and backcoat UV-processor is usually just prior to the topcoat operation (i.e., the backcoat is applied and cured first).

FIG. 4C is a cross-sectional view of a vinyl tile according to one on embodiment ofthe present invention. The tile 410 generally comprises a backcoat 412, a tile base 414, a print film or alternatively a transfer print ink (not shown), a cap film 418, and a topcoat 420 having macroscopic texture (not shown), hi a preferred embodiment, the backcoat 412 comprises a urethane backcoat of approximately 0.5-2 mils in thickness. The tile base 414 is approximately 50-200 mils in thickness, and the print film 416 is

25 approximately 0.5 mils in thickness. The cap film 418 comprises a PVC cap film of approximately 2.8 mils in thickness, and the topcoat 420 comprises a urethane topcoat of approximately 1-3 mils in thickness having macroscopic texture.

The urethane topcoat 420 may alternatively be any ofthe coatings according to the present invention. As discussed generally above, the topcoat resin formulation generally contains mixtures of monomers and oligomers with acrylate functional groups to

5 serve as the cross-linking centers, a photoinitiator or photoinitiator package to activate the cross-linking process under the UV-lamps, flatting agents for low-gloss finishes, and various mixtures of polyurethane, polyester, and polyether functional groups for imparting desired end-use performance into the cured topcoat. Moreover, the precise formulation of these ingredients is tailored to maximize performance on vinyl tile, where the rigidity ofthe

, n tile substrate relative to vinyl sheet flooring makes scratch resistance more difficult to achieve and places less emphasis on flexibility. UV-coatings for the preferred tile topcoat process must also be formulated to adhere to the PVC cap film, which can require different ingredients than those used for adhesion of UV-topcoats to the PVC wearlayer in sheet floor, and the coating formulation may need to form a stable curtain in the curtain coater,

, 5 since curtain coating is commonly used to apply non-textured coatings to floor tile. Lastly, the UV-processor conditions must be adjusted to produce the desired topcoat gloss (inert nitrogen atmospheres being preferred for high gloss, while a dual air, then nitrogen, curing environment is generally required for low gloss).

A preferred UV-curable coating formulation for use with tile substrates

₂^ contains texture-generating nylon particles and alumina/silane rheological control agents. A more preferred pre-cured coatmg mixture comprises, by weight, 35.303% ethoxylated trimethylolpropane triacrylate (SR 454, available from Sartomer, Exton, PA), 41.050% polyester acrylate (Laromer PE56F, available from BASF, Charlotte, NC), 5.747% urethane acrylate (Alua 1001, available from Congoleum Corporation, Mercerville, NJ), 0.330% ₅ acylphosphine oxide (Luceirin TPO, available from BASF, Charlotte, NC), 8.000% 3 micron inorganic flatting agent (Acematte OK 412, available from Degussa Corp.), 2.323% prehydrolyzed silane as an RCA coupling agent comprising 0.21%) 3- methacryloxypropyltrimethoxysilane (Z-6030 available from Dow Corning, Midland, MI), 0.015% glacial acetic acid, 0.015% deionized water, and 0.07% ethanol, prehydrolyzed as _Q described in Example 1 below, 1.000% inorganic RCA (Nanotek Alumina #0100, available from Nanophase Technologies, Burr Ridge, IL), and 6.250% 60 micron texture-producing particle (Orgasol 2002 ES6, available from Atofina, Philadelphia, PA). As such, a preferred cured coating according to the present invention is that coating produced using the above preferred pre-cured coating mixture. FIG. 4D is a process flow diagram of a process for applying a coating ofthe present invention to a tile subsfrate according to one embodiment ofthe present invention. In this embodiment, a radiation-curable thermosetting topcoat that provides macroscopic texture is applied to a vinyl tile subsfrate using a novel application method. This application method is called the Roll-coat and Air-Station (RAS) process, and is used in a preferred embodiment for application of pre-cured coating mixture to the cap film surface of a vinyl tile. The RAS process 430 first involves the use of a roll-coater 432 for application

5 and metering ofthe uncured coating onto the tile subsfrate 431 in the form of a thin film having macroscopic, particle-generated texture. As described previously, the aggressiveness ofthe macroscopic texture is dependent upon the ratio of wet film thickness to particle diameter, and this ratio is determined primarily (although not necessarily exclusively) by this roll-coating step in the RAS process ofthe present invention. For a

, preferred three-roll coater, the horizontal metering and transfer gaps (nips) and the vertical application gap must be carefully optimized to apply the proper amount of coating for the generation of macroscopic particle-generated texture. If either or both ofthe gaps are too small, then the texture-generating particles cannot pass through the nips and are not applied to the tile substrate, which results in a smooth, non-textured coating. Conversely, if the

, 5 gaps are too large, then the coating gauge is thicker than the particle diameter and a smooth, non-textured coating is again created (i.e., the particles are buried). Macroscopically textured coatings are generated in the present invention when the gaps are optimized for deposition of coatings having about the same or slightly less film thickness than the particle diameter (e.g., -1-2 mils of wet coatings containing 60 micron texture-generating particles).

2_Q However, the roll-coat process also imparts a directional distribution to the particle-generated textural features due to film-splitting between the roller and tile (see the Examples that describe film-splitting). This directionality is generally undesirable for field installation. Thus, subsequent passage ofthe textured, but directional, coated tiles 434 under an air knife 436 is then required to remove the roll-coat directionality and generate

25 more desirable uniform aid random macroscopic texture. Unlike traditional air knife coaters, the present invention uses air knife parameters of lip gap, gap to tile, line speed (dwell time under the air knife), and air pressure that are optimized primarily for the random redistribution ofthe roll-coat directionality in the uncured coating and not for metering of the coating off of the tile. Moreover, a vacuum conveyor is required to hold the tile on the on conveyor belt during passage under the air knife. The assemblage of vacuum conveyor and air knife is hereafter termed the "air-station."

It was also found that the orientation ofthe roll-coat directionality relative to the airstream direction under the air knife greatly impacts the ability ofthe airstation to remove the roll-coat directionality. For example, if the tiles with uncured coatmg are sent

25 under the air knife with the roll-coat directionality lines 435 parallel to the conveyor line direction (i.e., normal to the air knife slit direction and parallel to the airstream), then very little texture randomization occurs. However, if the tile 430 is rotated 90° relative to its orientation upon exiting the roU-coater (i.e., the roll-coat directionality lines 435 are parallel to the air knife slit 437 and normal to both the conveyor line direction and the air knife airstream 438), then the airstation can much more easily randomize the particle-generated texture. By readjusting the airstation parameters it was also possible to randomize the

5 texture with a 45 ° tile rotation 439, which implies that simply mounting the air knife at 45 ° relative to the airstation conveyor will eliminate the need for actual rotation ofthe tiles in a continuous production process.

It should be appreciated that in the use of a roll-coating process, particularly with multiple rolls, it is desirable that the roll in contact with the substrate is a soft

, . durometer roll to meter the coating mixture into the embossed areas or regions ofthe substrate, such as an embossed tile or sheet flooring or other embossed substrate. An example of this is described in Example 25.

It should be appreciated that the roll coating process and the air knife process may also be used separately for coating tiles. In addition, it should be appreciated that

, 5 although the foregoing methods described for use in the manufacture of coated tiles, these methods may also be used in applying the pre-cured coating compositions ofthe present invention to sheet flooring as well. Specifically, the RAS process may be used for sheet flooring, other flooring substrates, and non-flooring substrates. Further, the roll coating process alone and spray coating alone may be used to coat tiles, sheet flooring, other

2_Q flooring substrates, and non-flooring substrates.

FIG. 4E shows a cross-sectional view of another embodiment ofthe present invention. The tile 440 generally comprises a backcoat 442, a tile base 444, a print film 446 or alternatively a transfer print ink (not shown), a cap film 448; an undercoat 450, and a topcoat 452 having macroscopic texture 454. It should be appreciated that the

2 diagrammatic representation of the macroscopic texture 454 should not be deemed limiting and is simply used to represent the macroscopic texture. In a preferred embodiment, the backcoat 442 comprises a urethane backcoat of approximately 0.5-2 mils in thickness. The tile base 444 is approximately 50-200 mils in thickness, and the print film 446 is approximately 0.5 mils in thickness. The cap film 448 comprises a PVC cap film of on approximately 2.8 mils in thickness, and the undercoat 450 comprises a radiation or thermally cured undercoat of approximately 1-3 mils in thickness. The topcoat 452 comprises a radiation or thermally cured topcoat of approximately 1-3 mils in thickness having macroscopic texture.

In this particular embodiment, there is a double layer of radiation-cured top

05 coats, which provides improved scratch resistance. Such double-layer topcoats require a partial cure ofthe undercoat to give the undercoat sufficient structural integrity to withstand the RAS process used in application ofthe textured upper coat. However, if the undercoat approaches a fully cured state prior to application ofthe second, textured coating, then the textured upper coat will not properly adhere to the undercoat. Careful control of cure conditions during the partial cure ofthe undercoat is, therefore, required. After the textured upper coating has been applied on top ofthe partially cured undercoat via the RAS process, 5 normal low or high gloss curing is then used to fully cure the entire double-layer topcoat system.

The invention having been described, the following examples illustrate various embodiments and features ofthe present invention. It should be appreciated that the following examples are presented to illustrate, rather than to limit, the scope ofthe invention.

10

EXAMPLE 1

This example describes a microscopic texture with good abrasion resistance, but poor cleanability. 60g of alumina (available as Nanotek® alumina 0100 from

Nanophase Technologies Corp., Burr Ridge, IL) having an average particle diameter range

, 5 of 27-56 nm, 7.92g of prehydrolyzed 3-methacryloxypropyltrimethoxysilane (available as Z-6030 from Dow Corning, Midland, MI), 240g of a UV-curable resin (see Table 1 below for the resin composition), and about 200g of 0.5 in. diameter porcelain balls were added to a porcelain media mill.

The mixture was ball milled for about 6 hours at room temperature. The pre-

2_Q cured coating mixture, after removal ofthe grinding media, was applied using a 1.5 mil draw bar to rigid polyvinyl chloride floor tile substrates at room temperature. The tile substrates were then UV-cured in a two step process. First, the tile substrates were UV- cured in air using a line speed of 100 feet per minute (fpm) under two H-bulb (mercury) lamps on high. Then the tile substrates were UV-cured in nitrogen (<500 ppm oxygen) using two H-bulbs set on low and a line speed of 20 φm. The coated tiles were subjected to this latter inert UV-curing step a second time. The resulting coatings were transparent with an extremely low gloss of 6% (at 60°). Scanning Electron Microscopy (SEM) images of this coating indicate that microscopic wrinkling was present, i.e., micro-wrinkling. A Taber scratch test consisting of scribing 5 concentric circles on the coated samples with a metal

2o stylus weighted from 300 to 500g in 50g increments yielded no visible scratches on the coating surface. A qualitative scratch rating system was used to evaluate the scratches from the test (i.e., a 0-7 scale was used, where 7 is the best in that there are no visible scratches), and this coating was rated 7. When this coating was exposed to heavy traffic areas, it picked up dirt particles quite easily and was very difficult to clean.

35 Table 1 : UV-Curable Resin Composition

As noted above, prehydrolyzed silane was used. The silane (Z-6030) was prehydrolyzed to make it more reactive with the surface ofthe nanometer-sized alumina. The prehydrolysis was conducted by first mixing at room temperature 5g of glacial acetic acid, 5g of deionized water, and 25g of ethyl alcohol. Then, 75g of Z-6030 were added to the mixture. The mixture was gently agitated for about 24 hours. The mixture was allowed to stand several days before use.

EXAMPLE 2 This example shows a coating with macroscopic texture having good cleanability and scratch resistance. 31.17g of silica (available as Nanotek® silica 2000 from Nanophase Technologies Corp., Burr Ridge, IL) having an average particle diameter range of 15-33 nm, 10.51g of prehydrolyzed 3-methacryloxypropyltrimethoxysilane (available as Z-6030 from Dow Corning, Midland, MI) prepared as described in Example 1, lOOg of a UV-curable resin (see Table 2 below for resin composition). The mixture was hand stirred with a wooden spatula and then mixed with an ultrasonic probe for about 20 minutes. The pre-cured coating mixture was applied to flexible polyvinyl chloride floor substrates at room temperature with a spatula and distributed on the substrate with an air knife. These sheet vinyl substrates were then UV-cured under nitrogen (<500 ppm oxygen) using two H-bulbs set on high and a line speed of 100 φm. Two passes under the lamps were made under these conditions. The resulting coating was transparent with a gloss value (at 60°) of about 11%. The coating also had a macroscopic wave-like texture and was found to be cleanable. A Taber scratch test consisting of scribing 5 concentric circles on the coated samples with a metal stylus weighted from 300 to 500g in 50g increments yielded no visible scratches on the coating surface. Using the qualitative scratch rating system, this coating was rated a 7. Table 2: UV-Curable Resin Composition

EXAMPLE 3 To show the benefits of using nanometer-sized alumina in a coatmg according to the present invention, a coating was made using larger alumina particles. 60g of alumina (available as A152-SG from Alcoa, Pittsburgh, PA) having an average particle diameter of 1.5 μm, 0.48 g prehydrolyzed silane (Z-6030), 240g ofthe resin used in Example 1, and about 200g of 0.5 in. porcelain balls were added to a ball mill and milled as in Example 1. This pre-cured coating mixture was applied, cured, and tested for scratch resistance as given in Example 1. The resulting coating was visually not as transparent as the coating in Example 1 and was given a scratch rating of 2 indicating visual scratches were present.

EXAMPLE 4 Tests were conducted to determine the effects of silane as a coupling agent on the dispersion of nanometer-sized alumina. 2g of Nanotek® alumina 0100 having an average particle diameter range of 27-56 nm was added to lOg of each ofthe following liquids: ethoxylated diacrylate (available as SR 259 from Sartomer, Exton, PA), propoxylated diacrylate (available as SR 306 from Sartomer, Exton, PA), ethoxylated trimethlolpropane triacrylate (available as SR 454 from Sartomer, Exton, PA), and urethane acrylate (available as Alua 1001 from Congoleum, Mercerville, NJ). The mixtures were stirred, shaken, and then placed into an ultrasonic bath for 30 minutes. To some of these mixtures 0.24g prehydrolyzed silane, as prepared in Example 1, was added, and the mixture was stirred. The consistencies of each of these mixtures are described in the Table 3 below. Table 3: Effects of Prehydrolyzed Silane

The observations show that the urethane acrylate and the Ethoxylated diacrylate disperse the nanometer-sized alumina better than the propoxylated diacrylate and the Ethoxylated trimethlolpropane triacrylate. These observations also show that the addition ofthe prehydrolyzed silane dispersing agent improves the dispersion ofthe nanometer-sized alumina.

EXAMPLE 5 This example shows the effects of alumina size and coupling agent on the clarity ofthe cured coating. The pre-cured coating mixture in Example 1 was prepared in the identical manner described with the following exception: the prehydrolyzed silane was prepared using 75g of ethanol instead of 75g of Z-6030 silane. Thus, this pre-cured coating mixture contained no coupling agent. This pre-cured coating mixture (referred to as Example 5), the pre-cured coating mixture in Example 1, and the pre-cured coating mixture in Example 3 were applied at room temperature using a 3 mil draw-down bar to glass substrates. The drawn down pre-cured coating mixtures were then cured using two curing conditions as described in Table 4.

Table 4: UV-Curing Conditions

The percent haze is defined as follows:

% haze = (100- % specular transmission)/% total transmission

and was determined for these cured coatings using a CHROMA SENSOR CS-5 from Applied Color Systems, Inc. and a method similar to ASTM D 1003-92. The thicknesses of the detached coatings were determined with a MADAKE micrometer. The haze and thickness values are given in Table 5 below.

The percent haze values show that the coating with nanometer-sized alumina was much less hazy than the coating containing micron-sized alumina regardless of cure conditions. The data also show that the silane coupling agent improves the clarity ofthe coatings containing nanometer-sized alumina.

EXAMPLE 6 This example shows the effects of inorganic particle type and loading on the cured coating texture. Six pre-cured coating mixtures were prepared where the inorganic nano-particles and the prehydrolyzed silane (as described in Example 1) were added to the UV-curable organic phase used in Example 2. Each pre-cured coating mixture was mixed with a Cowles blade and then an ultrasonic probe. The composition of these pre-cured coating mixtures is shown in Table 6.

Table 6: Pre-Cured Coating Mixture Compositions

0

These pre-cured coating mixtures were then applied to flexible vinyl flooring substrates which were cleaned with a solution of acetic acid, soap, and water. The pre- cured coating mixtures were applied at room temperature using a pipette or a spatula 5 depending on the viscosity, and then the samples were passed through an air knife to distribute the pre-cured coating mixture over the substrate and to remove any excess. The resultant films were then cured under UV lamps using different lamp intensities and atmospheres as described in Table 7 below. Scanning electron microscopy (SEM) images _Q ofthe coatings were taken along with gloss measurements at 60 °.

5

0

5

Coatings cured under both air and inert atmospheres having 30% or less nanometer-sized alumina showed micro-sized wrinkles, which looked like spaghetti in the SEM images (200x). As the concentration of alumina is increased from 0 to 20%, the length ofthe wrinkles decreases under inert (N₂) curing conditions. At 30% alumina, the wrinkle length is quite small resulting in a surface resembling a golf ball surface in the SEM images. At 40% alumina, the micro-wrinkling is not observed in the SEM (surface is smooth), but a macro wave-like texture is observed with the naked eye. Wave-like macro texture is also observed with the coatings having 16% and 22% silica. In the cases where micro-wrinkling is not observed, the macro texture observed is independent ofthe cure conditions (two zone versus one zone) used. EXAMPLE 7 This example demonstrates that wave-like macroscopic texture is generated by the coating application method. Pre-cured coating mixture 5 in Example 6 above was applied to a substrate with an air knife as in Example 6. The same pre-cured coating mixture was also applied to a second substrate with a 1.5 mil draw down bar. Both samples ₅ were cured in the inert atmosphere as described in Example 6. The sample coated with a draw bar had a visibly smooth surface and a gloss of 74% compared to a wave-like visible texture with a gloss of 20% for the sample coated with an air knife.

EXAMPLE 8

. r. This example shows the effect of shear rate and temperature on the pre-cured coating viscosity. The viscosities of pre-cured coating mixtures 3 (28.9% alumina) and 4 (40%) alumina) from Example 6 were measured using a Brookfield viscometer (model DV- π, RV) with spindles 21 and 29 as a function of spindle rotation rate (related to shear rate) and temperature. FIG. 5 shows the results of these measurements for pre-cured coating

, 5 mixture 3 and FIG. 6 shows the results for pre-cured coating mixture 4. The data show that the pre-cured coating mixture viscosity decreases with temperature and shear rate. The viscosity dependence with shear rate indicates that the actual viscosity ofthe pre-cured coating during application with an air knife is probably less than when measured at low shear (0.150 s^"1) by the Brookfield, since the shear rate under the air knife is assumed to be _j . greater than 0.150 s^"1. The viscosity dependence on temperature demonstrates the importance of keeping the pre-cured coating at the required temperature during application, since too high of a temperature may result in a coating that does not produce macroscopic texture because the viscosity is too low. The difference in the curves between FIGS. 5 and 6 show that the amount of RCA in the pre-cured coating influences the coating rheology,

₂ which could control the type and degree of texture in the cured coating.

EXAMPLE 9 This example shows the effects of pre-cured coating viscosity on cured coating texture. Using the pre-cured UV resin described in Table 2, 20%, 22.5%, 25%, on 27.5%, and 30% nanometer sized alumina (as described in Example 1) was added and mixed with a Cowles blade mixer. Additionally 45 % of nanometer-sized calcium carbonate was added to the resin described in Table 2 and mixed with a Cowles blade mixer. The viscosities of these pre-cured coatings were measured as described in Example 8 and are given in Table 8. These pre-cured coatings were then applied to flexible sheet vinyl

25 substrates and coated with an air knife at room temperature. In the case ofthe coating with 45% calcium carbonate, the pre-cured coating simply blew off the substrate when the air knife was used. The samples were cured under inert conditions and tested for scratch resistance (Taber) and the gloss was determined. These data are also given in Table 8.

Table 8: Pre-Cured Coating Viscosity Effects on Cured Coating Properties

These data indicate that for the air knife conditions presently used, the viscosity ofthe coating needs to be approximately in the range of 100,000-1,000,000 cPs measured at room temperature (at a shear rate of 0.150 s^"1) in order to generate macroscopic texture. The data also indicate that more aggressive texture yields better scratch resistance.

EXAMPLE 10

This example shows the effect of aging and prehydrolyzed silane concentration on the pre-cured coating viscosity. The viscosity of pre-cured coating mixture 4 in Example 6 (40% alumina) was determined as a function of time. These results are shown in FIG. 7. The pre-cured coating mixture viscosity was found to have an aging effect in which fresh samples change viscosity over a period of about one week before leveling at a new viscosity. Specifically, pre-cured coating mixtures prepared with the optimal prehydrolyzed silane concentration (10 μmol/m²) decrease about 25%> in viscosity after 10 days and change color from a dark gray to a lighter gray, whereas pre-cured coating mixtures with 20 μmol/m² increase in viscosity by more than 4 times (i.e., the initial value was 75% lower than final value) in the same time period. This behavior suggests that at and below the optimal prehydrolyzed silane concentration the prehydrolyzed silane is continuing to further disperse the alumina particles as the prehydrolyzed silane molecules diffuse slowly to their final equilibrium locations on the particle surfaces and react with Al-OH groups. Conversely, when excess prehydrolyzed silane is present the equilibrium favors reagglomeration and crosslinking by prehydrolyzed silane condensation but is apparently kinetically limited prior to equilibration. Both processes seem to involve rather slow kinetic and/or diffusive steps and are unlikely to be affected much by additional mechanical mixing.

EXAMPLE 11

₅ The effect on pre-cured coating viscosity of the concentration of prehydrolyzed silane coupling agent (as prepared in Example 1) was determined by measuring the viscosity as in Example 8 of a pre-cured coating mixture containing 40% nanometer-sized alumina (e.g., the pre-cured coating mixture 4 in Example 6 except the silane level was varied). The amount of prehydrolyzed silane used in all the examples was

₁ r, calculated using the following equation:

M_ps = (10-⁶ MW_ps a s_np m_Bp)/C ps

where M_pS is the mass of prehydrolyzed Z-6030 (in g), a is the number of active sites on the

, 5 nano-particle (in μmole/m²), MW_ps is the molecular weight of the prehydrolyzed Z-6030 (234 g/mol), s_np is the nanometer-sized particle surface area (in m²/g), m^ is the mass of nanometer-sized particles used in the formulation (in g), and C_ps is the weight fraction of prehydrolyzed silane in the solution (from Example 1, typically 0.6818). Based on Parker et al., Mat. Res. Symp. Proc. 249 (1992) 273, 10 μm of active sites/m² of inorganic in all of

₂n the samples was used, because it should give the lowest pre-cured coating mixture viscosity and, hence, the best dispersion ofthe nanometer-sized particles. However, it should be appreciated that by controlling the amount of prehydrolyzed silane (more or less than 10 μmole/m²) can result in different shear dependent rheology, which in turn could lead to different textures.

25 The pre-cured coating mixture viscosity was measured as a function of prehydrolyzed silane level (represented by the "a" value as described above) and the results are shown in FIG 8. These data show that at a given strain rate, the pre-cured coating mixture equilibrium viscosity was found to initially decrease as the silane concentration was increased, presumably due to enhanced dispersion ofthe nanometer-sized particles in _Q the resin phase. A viscosity minimum was reached at approximately 10 μmol silane/m² Al₂O₃ and serves as a measure of optimal dispersion for this surfactant-inorganic-resin mixture (in agreement with sedimentation results obtained by Parker et al. for the n- octyltriethoxysilane-toluene-5 μm Al₂O₃ system). The increase in viscosity observed at slightly higher silane concentrations corresponds to some reagglomeration of alumina 5 particles as the excess silane forms larger organo-phobic phase domains (domains that include both the alumina particles and the hydrophilic ends ofthe silane molecules) that minimize surface energies between phases. Finally, viscosity again decreases at much higher silane concentrations due to simple mixing-rule behavior.

EXAMPLE 12 This example demonstrates the use of an organic RCA. 20g of an organic

₅ (castor wax derivative) RCA Thixcin R (Rheox Inc., Hightstown, NJ) was added to 480g of the pre-cured UV resin described in Table 2 and mixed with a Cowles blade mixer. The mixture was then heated at 70 °C until the Thixcin R dissolved. The mixture was then allowed to cool to room temperature. The viscosity, of this mixture at a shear rate of 0.150 s^"1 at room temperature was 243,000 cPs. This mixture was then coated on flexible

_{* r}. sheet vinyl using an air knife and cured under inert conditions. The resulting cured coating was transparent and had a wave-like macroscopic texture. When scratched using the Taber scratch test, no visible scratches were observed.

EXAMPLE 13

, ₅ This example demonstrates the use of both an organic RCA and an inorganic flatting agent. 12g of Thixcin R organic RCA and 19.14g of Acematte OK 412 (Degussa Corp.) silica flatting agent were added to 288g ofthe pre-cured UV resin described in Table 2 and mixed as in Example 12. This mixture was coated on a flexible vinyl sheet floor with an air knife and cured under both atmospheric and inert conditions. The resulting coating _jr. had a matte finish and wave-like texture.

EXAMPLE 14 This example shows that wave-like macroscopic texture can be generated without the use of an RCA. 85.25g of Alua 2302 and 21.31g Alua 1001 urethane acrylate

₂₅ oligomers (Congoleum Corp., Mercerville, NJ), 66.14g of Actilane 424 and 26.64g of Actilane 430 acrylate monomers (Akcros Chemicals, New Brunswick, NJ), 0.2g DC 193 surfactant, and 0.394g of Luceirin TPO photoinitiator were added to a container at room temperature. This mixture was heated to 70 °C and mixed with a Cowles blade mixer. After cooling to room temperature, the pre-cured coating mixture was applied to flexible on vinyl substrates, coated with an air knife, and UV-cured under inert conditions. The resulting coating was transparent and had macroscopic wave-like texture.

EXAMPLE 15 This example demonstrates the use of organic texture-producing particles 25 and an inorganic flatting agent. 6.25g of Orgasol 2002 ES 6 NAT (Atofina, Philadelphia, PA) polyamide 12 texture-producing particle (60 μm in diameter) and 5.625 g of Acematte OK 412 flatting agent (3 μm diameter) were added to 88.125g ofthe pre-cured UV-resin described in Table 2 and mixed with a Cowles blade mixer. This mixture was heated to 70°C and coated on a flexible sheet vinyl floor using an air knife. The pre-cured coating was cured at a line speed of 100 φm using atmospheric and then inert conditions. The resulting coating was transparent coating with a matte finish and sandpaper-like texture.

5

EXAMPLE 16

This example shows the effects ofthe size ofthe texture-producing particles on the cured coating texture. Four pre-cured coating mixtures were prepared as in Example

15 where 6.25% of Orgasol 2002 polyamide 12 texture-producing particles was added to the

, . pre-cured UV-resin described in Table 2. The four mixtures differed in that each contained a different sized particle of Orgasol 2002: 30 μm (grade ES 3), 40 μm (grade ES A), 50 μm (grade ES 5), and 60 μm (grade ES 6). Each mixture was applied at 70°C to sheet vinyl and coated with an air knife. All coatings were UV-cured under inert conditions. The cured coating containing the 30 μm particles had a visibly fairly smooth surface with a matte

₁5 finish. The coatings with the larger particles had progressively more visible texture as the particle size increased, where the 60 μm particles gave the most visible and aggressive (largest textural features) texture. The scratch resistance ofthe coatings improved with increasing particle size, where 60 μm showed almost no visible scratches after the Taber scratch test. FIG. 9 is a photograph ofthe top of a portion ofthe coated substrate produced r_yr. using the 60 μm particles, and FIG. 10 is a photograph ofthe top of a portion ofthe coated substrate produced using the 40 μm particles. The difference in the aggressiveness ofthe texture is evident. It should be appreciated, however, that the concentration of particles used would also be expected to have an influence on textural aggressiveness.

For illustrative purposes, "traces" ofthe surface textures of these samples

25 were obtained by rubbing a soft graphite pencil over translucent tracing paper that was itself placed on top ofthe textured surfaces. The traces were then digitally scanned. FIG. 11 shows the texture ofthe coating producing using the 60 μm particles, and FIG. 12 shows the texture ofthe coating produced using the 40 μm particles. The traces clearly show the decrease in textural aggressiveness as nylon particle size is decreased from 60 μm as shown

₃₀ in FIG. 11 to 40 μm in FIG. 12.

These traces also allow for estimation of certain features ofthe texture. FIG. 13 is an illustration ofthe general type of macroscopic texture produced by the coatings in this Example 16. As shown, three parameters, a, b and c, are defined to describe certain planar features ofthe texture. These parameters are defined as follows: "a" represents the

25 distance between peaks ofthe texture, "b" represents the width of each textural feature, and "c" represents the length of each textural feature. These parameters were measured manually from the corresponding traces and, therefore, may have substantial inherent error associated with them; however, they can be used to distinguish gross differences between the textures. Regardless, these parameters should not be viewed or used as limiting the type, shape, or size ofthe macroscopic texture. The ranges for these parameters for the coatings produced in this Example 16 are as follows: for the coating made with 60 μm particles a ranges from 10-50 mils, b ranges from 5-30 mils, and c ranges from 100-350 mils, for the coating made with 40 μm particles a ranges from 5-30 mils, b ranges from 1-20 mils, and c ranges from 10-150 mils, and for the coating made with 30 μm particles a ranges from 5-20 mils, b ranges from 1-10 mils and c ranges from 1-50 mils.

The average gloss values (60°) and the textural relief values (defined as maximum coating thickness minus minimum coating thickness) were also measured for the coatings produced by this Example 16. The gloss values are 10.8, 16.9, and 35.3 for the coatings made with 60 μm, 40 μm, and 30 μm particles, respectively. The textural relief values are 1.99 mils, 0.52 mils, and 0.29 mils for the coatings made with 60 μm, 40 μm, and 30 μm particles, respectively.

EXAMPLE 17 This example describes textured coatings containing organic texture- producing particles, an inorganic RCA with a coupling agent, and both organic and inorganic flatting agents. Per-cured coating mixtures having the composition shown in Table 9 were mixed with a Cowles blade mixer.

Table 9: Pre-Cured Coating Mixture Compositions in Weight Percent

Both coatings were applied to flexible sheet vinyl at 70 °C and coated with an air knife. These coated substrates were UV-cured under atmospheric and then inert environments. The resulting cured coatings were transparent and had sandpaper-like macroscopic texture and matte finishes. EXAMPLE 18 This example demonstrates the use of a roll coater application method for generating and controlling macroscopic texture similar to that of wood-grain. Three pre- cured coating mixtures were used, including the coating of Example 9 (30% nano-alumina inorganic RCA), the coating of Example 12 (organic RCA), and the coating of Example 16

₅ (60 μm texture-generating nylon particles). These pre-cured coating mixtures were then applied to cleaned, semi-rigid vinyl tile flooring substrates using a pipette or spatula as described in Example 6. Distribution ofthe pre-cured coating mixture to a macroscopically textured state and removal of excess coating was then achieved by passing the samples under a contacting roller using the process conditions listed in Table 10. Specifically, Table

, , 10 gives the conditions for the contacting roll, which actually makes contact with and the pre-cured coating to provide macroscopic texture. More specifically, the contacting roll acts to split the pre-cured coating mixture that has been applied to the substrate between the contacting roll and the substrate and is referred to as "film-splitting," where "film" refers to the pre-cured coating mixture as applied to the substrate. This film-splitting phenomenon

.₅ acts to form the macroscopic texture ofthe coating on the substrate. The gap indicated is between the contacting roll and the uncoated substrate surface when the uncoated substrate is between the rolls (i.e., total gap minus substrate thickness). Also, in the case where the contacting roll is rotating, the rotation is away from the surface ofthe sample. In all cases, the lower roll carried the samples between the rolls at 100 φm and, upon exiting the roll coater, the pre-cured coated samples were cured under an inert (N₂) environment at 100 φm.

25

30

35

- 44 -

SUBSflTUTE SHEET (RULE 26) Table 10: Roll Coated Sample Compositions and Process Conditions

FIGS. 14-18 are photographs ofthe top of a portion of each coated substrate made using coatings 1-5 listed in Table 10. FIGS. 19-23 are fraces, made as described in Example 16, ofthe surface textures of these coated substrates having coatings 1-5 listed in Table 10. Gloss (60°) and gauge (thickness) measurements are given in Table 11, where textural relief is calculated as the maximum gauge minus the minimum gauge (in mils). Note that the gloss is reported for both the in-line direction (i.e., the direction that the sample traveled while passing through the roll coater) and for the transverse direction. Gauge measurements were made using a light microscope equipped with a microscale and involved viewing cross-sections ofthe cured samples cut in the transverse direction.

FIG. 24 illustrates the general type of macroscopic texture produced by the coatings in this Example 18, and FIG. 25 is an enlarged view of a portion of FIG. 24. As shown, the texture produced in this Example 18 can be described as "branched". FIGS. 24 and 25 show three parameters, a, b and c, that are defined to describe certain planar features ofthe texture. These parameters are defined as follows: "a" represents the distance between branches ofthe texture, "b" represents the width of each branch, and "c" represents the length of each branch. These parameters were measured manually from the traces for each ofthe coatings shown in FIGS. 19-23 and, therefore, may have substantial inherent error associated with them; however, they can be used to distinguish gross differences between the textures. Regardless, these parameters should not be viewed or used as limiting the type, shape, or size ofthe macroscopic texture. The ranges for these parameters for the coatings produced in this Example 18 are provided in Table 11. Table 11 : Gloss and Texture Measurements of Roll Coated Samples

These results show that a range of texture similar to that of wood-grain may be achieved by adjustment of process conditions during the roll coating application ofthe pre-cured coating mixtures. Key parameters appear to be the rotational speed ofthe contacting roll that directly contacts the pre-cured coating, the gap between the contacting roll and the sample, and the hardness ofthe contacting roll.

If the contacting roll is moving in the line direction, then the pre-cured coating film is split quickly as the moving roll pulls a fraction ofthe coating away from the coated substrate. This results in very short textural branches (see, for example, FIG. 18). Conversely, a stationary contacting roll does not split the film as rapidly, allowing the branches to extend to much longer lengths before a fraction ofthe branching film detaches from the substrate and ends the branch. This macroscopic texture is best described as "wood-grain" in nature. Moreover, the wood-grain texture may be further controlled by adjusting the gap. A smaller gap yields a more finely scaled wood-grain texture (e.g., compare FIGS. 19 and 21). The use of texture-producing particles in a roll-coated pre-cured coating mixture produces a hybrid macroscopic texture that contains both wood-grain and "sandpaper-like" textural elements (see, for example, FIGS. 18 and 23). The hardness of the contacting roll is also expected to affect the film splitting behavior ofthe roll-coating application method, as are intrinsic pre-cured coating properties such as viscosity and particle density.

EXAMPLE 19 This example illustrates how the manipulation of process conditions may be used to control the aggressiveness of macroscopic texture generated by an air knife coating application method. Two pre-cured coating mixtures were used, the first being the coating of Example 9 (30% nano-alumina inorganic RCA). The second pre-cured coating consisted ofthe coating composition given in Example 15, with the exception that the organic texture- generating particles were 40 μm polypropylene particles added at 5 wt.% (Propyltex 200S available from Micro Powders, Inc., Tarrytown, NY) instead ofthe 6.25 wt.% nylon particles. These pre-cured coating mixtures were applied to flexible sheet vinyl floor with an air knife using the process conditions indicated in Table 12. The pre-cured coated samples were then cured under an inert (N₂) environment at 100 φm.

Table 12. Air Knife Coater Sample Compositions and Process Conditions

FIGS. 26-28 are photographs ofthe top of a portion of each coated substrate made using coatings 1-3 listed in Table 12, respectively. FIGS. 29-31 are traces, made as described in Example 16, ofthe surface textures of these coated substrates having coatings 1-3 listed in Table 12, respectively. These figures show that the macroscopic texture produced using the inorganic RCA are wave-like. Traces ofthe particle textures for samples 4-7 in Table 12 were not made, but traces of similar particle-generated "sandpaper" macroscopic texture can be found in Example 16.

FIG. 32 is an illustration ofthe general type of wave-like macroscopic texture produced by the coatings in this Example 19. As shown, three parameters, a, b and c, are defined to describe certain planar features ofthe texture. These parameters are defined as follows: "a" represents the distance between peaks ofthe texture, "b" represents the width of each textural feature, and "c" represents the length of each textural feature. These parameters were measured manually from the corresponding fraces and, therefore, may have substantial inherent error associated with them; however, they can be used to distinguish gross differences between the textures. Regardless, these parameters should not be viewed or used as limiting the type, shape, or size ofthe macroscopic texture. The ranges for these parameters for the coatings produced in this Example 19 are provided in Table 13. Gloss (60°) and gauge (thickness) measurements are also given in Table 13 and follow the same conventions as the gloss and gauge data presented in Example 18.

Table 13: Gloss and Texture Measurements for Air Knife Coated Samples

10

15

These results show that it is possible to control the aggressiveness of macroscopic textures generated with an air knife by adjusting the process conditions. For the high viscosity coating that employs an RCA as part of its composition, the wave-like macroscopic textures progress from relatively large and broad features at fast line speeds to

20 texture with a very fine, satin finish at low line speeds. Note that even in the latter case (FIGS. 28 and 31) the fine wave-like features can still be distinguished with the unaided eye. Also note that the same pre-cured coating composition was used in samples 1-3, illustrating the appreciable textural control that may be attained from the coating application method alone. 5 Similar textural control is achieved using a coating with texture-producing particles ("sandpaper" texture), as indicated by the large variations in gloss and relief shown in Table 13 for samples 4-7 (similarly, a single pre-cured coating composition was used in samples 4-7). Ifr general, lower gloss and higher relief correspond to more aggressive textures. However, variations in the planar dimensions and in the average gauge (average of

™ the minimum and maximum gauges) are also important for the overall perceived aggressiveness ofthe textures (and may also influence gloss readings).

EXAMPLE 20 This example shows the scratch resistance properties of cured coating having

35 macroscopic texture. The pre-cured coating mixtures 4 (40% nano-alumina) and 7 (22% nano-silica) in Example 6 and the coating in Example 12 (4% wax) were coated as described in Example 6 on flexible vinyl sheet flooring and UV cured under inert conditions as described in Example 6. These cured coatings had macroscopic wave-like texture. Pieces measuring 9 in² were mounted on plywood and placed on the floor in a high traffic area (a cafeteria). After a given amount of time the floor panels were pulled up, cleaned,

5 and evaluated for scratch resistance. The scratch resistance was measured by counting the total number of scratches on a given coating and dividing by the total area in square feet. As controls, a standard high gloss (80-90%) macroscopically smooth urethane containing no inorganics and a wood laminate floor were also evaluated. The results of these tests are shown in FIG. 33. The scratch data clearly show that the textured urethane coatings have

, r, fewer scratches per square foot of exposed surface than the standard smooth urethane and the wood laminate.

EXAMPLE 21 This example demonstrates a thermally-cured top coating that provides

₁5 macroscopic texture. The pre-cured coating composition described in Table 14 was mixed using a Cowles blade mixer at room temperature. This composition is nearly identical to the radiation-curable coating mixture described in Examples 16 and 17 except that a thermally activated initiator (an organic peroxide) was used instead of a UV activated initiator to initiate the curing. This coating mixture was then applied to flexible sheet vinyl

2 at 70°C using an air knife. The resulting coated subsfrate (1-1.5 mils thick) was cured at 360 °C for 2 minutes. The resulting solid coating had a ceramic-like macro-texture, which was nearly identical in appearance to those coatings in Example 17.

5

0

5 Table 14: Thermally-Curable Coating Composition

EXAMPLE 22 This example demonstrates the use of a shrinking wear layer to provide texture from the use of texture-producing particles. A wear layer formulation was made comprising, by weight, 57.8% PVC resin (75HC available from Oxychem, Dallas, TX), 6.4% PVC resin (567 available from Oxychem, Dallas, TX), 26.6% plasticizer (N-6000 available from Velsicol, Rosemont, IL), 2.9%> plasticizer (S-375 available from Solutia, St. Louis, MO), 1.9% plasticizer (A-150 available from Exxon, Houston, TX), and 4.4% stabilizer (2347 available from OMG, Cleveland, OH). To this mixture is added 25% solid glass beads (no plasticizer absorption or melting) having a mean diameter of 203 μm (Spheriglass A- 1922 available from Potters Industries, Valley Forge, PA). The resulting wear layer mixture was coated with a draw bar at 10 mils on a flexible vinyl gel. The resulting sample was then fused at 385 °F for 1.5 minutes. As a control, this same wear layer formulation without the glass beads was coated and gelled. The control plastisol had a visibly smooth surface and a gloss value of 38%. The sample containing glass beads had macroscopic texture and a gloss of 23%, which indicates that the wear layer decreased in thickness during gelation to expose the glass beads. EXAMPLE 23 To demonstrate wet flocking, a standard PVC plastisol (Ultima Wear Layer WB4 available from Congoleum Corporation, Mercerville, NJ) was drawn down on flexible gelled PVC at 10 mils. Several types of particles, as described in Table 15, were each wet flocked on the wet plastisol. These samples were then fused at 385 °F for 1.5 minutes. The

_<- visual observations as well as the gloss values for each sample are given in Table 16. The data in Table 16 indicate that wet flocking gives ceramic-like texture as long as the plastisol is fused at a temperature lower than the melting point ofthe particle. When the fusion temperature is higher than the melting temperature ofthe particle, the particle melts to form a semi-continuous film on the surface ofthe plastisol. This phenomenon occurred when

₁ r. Nylon 12 and polypropylene particles were used.

Table 15: Particles Used in Wet Flocking

15

20

25

30

35 Table 16: Ultima Wear Layer Wet Flocked With Various Particles

EXAMPLE 24 This example illustrates the use of spray coating as a method for applying a radiation-curable coating having macroscopic texture onto a tile substrate. A pre-cured coating mixture having the composition described in Table 17 was applied to a vinyl tile substrate using an air-gun sprayer (Campbell Hausfeld Standard Duty Air-Driven Spray Gun Model DH5300). The spray gun was operated in pressure-feed mode using 45 psig of air pressure, and the nozzle configuration employed was designed for external atomization ofthe coating droplets by the high-pressure air stream. The tile substrate was sprayed by multiple passes with the handheld spray gun at a height of about 12" from the tile surface until complete coverage ofthe tile surface by the pre-cured coating mixture was achieved. The sprayed-on, pre-cured coating mixture on the tile substrate was then cured as in Example 2. Both the sprayed-on, pre-cured coating mixture on the tile substrate and the cured coating on the tile substrate exhibited macroscopic texture due to the texture-generating particles present in the pre-cured and cured topcoat.

Table 17: UV-Curable Coating Composition

EXAMPLE 25 This example shows the use of a roll-coat and air-station combination process (termed a RAS process, as described previously) for application of a radiation-curable, macroscopically textured coating onto a tile substrate. Tile substrates were coated with the pre-cured coating mixture described in Table 18 using a three-roll coater comprised of a

5 hard rubber roll as the upper metering roll (about 90 Shore A Durometer hardness), an engraved steel roll (72 tri-helical) as the transfer roll, and a soft rubber roll as the applicator roll. An especially soft durometer (35 Shore A Durometer) for the applicator roll was chosen to promote coating application in deeply embossed grout lines and in other deeply embossed substrate regions. Line speed through the roll-coater was about 70 φm (feet per

, _r. minute), and the compression ofthe applicator roll upon the tile substrate was about 115 mils. The roll-coated tiles exhibited directional lines of texture due to "film-splitting" in the machine direction. Subsequent passage ofthe roll-coated tiles through an airstation removed this roll-coater directionality. The air-station comprised a vacuum conveyor to hold down the moving tiles, as well as an airknife operating at up to 3.7 psig at angles

, 5 between +20° and -20° from vertical (vertical referring to the airknife slit pointing down directly upon the tile, and positive angles referring to the slit being angled toward the incoming tile). The airstation line speed was 40 φm with a knife-to-tile gap of 50 mils, and tiles were passed through with a planar rotation of 45 ° between the roll-coater directionality lines and the airstation machine direction. Moreover, two passes under the airknife were

2 made, with 90° planar rotation ofthe tile between passes (i.e., on the second pass there is -45 ° planar tile rotation between the roll-coater directionality lines and the airstation machine direction). Finally, the pre-cured textured coating was subjected to a low-gloss cure cycle as follows: a) two H-bulb (mercury) lamps on high at 125 φm in air, then b) six H-bulb (mercury) lamps on high in nitrogen (-3000 ppm residual O2) at 100 φm. The

25 final, UV-cured coating exhibits a low-gloss, macroscopically textured surface topcoat with textural features characteristic ofthe 60 micron texture-generating particles present in the coating composition.

0

5

-53-

I Table 18: UV-Curable Coating Composition

EXAMPLE 26

The application of a radiation-curable coating having macroscopic texture onto a tile already pre-coated with a non-textured radiation-curable coating is demonstrated in this example. Approximately 5 g of a commercial, non-textured UV-curable urethane coating (AMT-475, available from Congoleum Corp., Mercerville, NJ) was applied to a 12" square tile using a curtain coater. This undercoat was then partially cured in an air environment using four H-bulb (mercury) lamps on high with a line speed of 100 φm (feet per minute). Next, a second and final topcoat containing macroscopic texture-producing particles and having the composition of Table 17 was applied with a roll-coater and air-station (RAS) process similar to that described in Example 25 (an exception being the use of a two-roll coater instead ofthe three-roll coater described in Example 25). The double-coated tile was then subjected to the following low gloss cure cycle for curing of the two topcoat layers: a) two H-bulb (mercury) lamps on high at 100 φm in air, then b) six H-bulb (mercury) lamps on high in nitrogen (-3000 ppm residual O2) at 100 φm. The partial cure ofthe non-textured, UV-curable undercoat instills sufficient mechanical strength into the undercoat to withstand the subsequent roll-coating ofthe textured topcoat. At the same time, the partial undercoat cure also promotes adhesion ofthe textured topcoat to the undercoat via unreacted acrylate crosslinking units that remain in the undercoat after partial cure and can crosslink with similar reactive groups in the textured topcoat. The final, UV-cured coating exhibits a low-gloss, macroscopically textured surface topcoat adhered to an underlying non-textured, UV-cured basecoat. While the foregoing description and drawings represent the preferred embodiments ofthe present invention, it will be understood that various additions, modifications and substitutions may be made therein without departing from the spirit and scope ofthe present invention as defined in the accompanying claims. In particular, it will be clear to those skilled in the art that the present invention may be embodied in other specific forms, structures, arrangements, proportions, and with other elements, materials, and components, without departing from the spirit or essential characteristics thereof. The presently disclosed embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope ofthe invention being indicated by the appended claims, and not limited to the foregoing description.

Claims

What is claimed is:

1. A pre-cured coating mixture, comprising: a curable resin; and an initiator; 5 wherein said radiation-curable resin and said initiator form a pre-cured coating mixture capable of forming a macroscopic texture upon application of said mixture on a substrate.

2. The pre-cured coating mixture of claim 1 , wherein said curable resin is a

10 radiation-curable resin.

3. The pre-cured coating mixture of claim 2, wherein said pre-cured coating mixture has an effective viscosity for forming said macroscopic texture.

- 5 4. The pre-cured coating mixture of claim 1 , further comprising a rheological control agent and wherein said curable resin, said initiator, and said rheological control agent form said pre-cured coating mixture.

5. The pre-cured coating mixture of claim 4, wherein said rheological control 2_Q agent is selected from the group consisting of inorganic particles, organic solids, and mixtures thereof.

6. The pre-cured coating mixture of claim 5, wherein said inorganic particles are selected from the group consisting of alumina, silica, fumed alumina, fumed silica,

25 aluminosilicate, alumina coated on silica, metal oxides, metal, carbonates, clays, and mixtures thereof.

7. The pre-cured coating mixture of claim 6 wherein said inorganic particles have an approximate size in the range of 27-56 nanometers. 0

8. The pre-cured coating mixture of claim 5 wherein said inorganic particles are nanometer-sized alumina.

9. The pre-cured coating mixture of claim 5 wherein said inorganic particles 2 comprise approximately 1-80%, by weight, of said coating mixture.

10. The pre-cured coating mixture of claim 5, wherein said organic solids are selected from the group consisting of low molecular weight waxes, polymers of ethylene glycol, polymers of propylene glycol, natural polymers, polyamides, polypropylene, and mixtures thereof.

5 11. The pre-cured coating mixture of claim 5, wherein said organic solids comprise approximately 1-50%, by weight, of said coating mixture.

12. A coated substrate, comprising: a substrate; and

, _π a cured coating on at least a portion of said substrate, wherein said coating comprises an inherent macroscopic texture.

13. The coated substrate of claim 12 wherein said coating comprises a radiation- cured resin.

15

14. The coated substrate of claim 12, wherein said coating further comprises a rheological control agent.

15. The coated substrate of claim 14, wherein said rheological control agent is 2_Q selected from the group consisting of inorganic particles, organic solids, and mixtures thereof.

16. The coated substrate of claim 12, further comprising: a flatting agent comprising 5 micron-sized nylon particles;

2 a plurality of texture-producing particles comprising 60 micron-sized nylon 12 particles; a rheological control agent comprising a plurality of alumina particles having a particle size distribution in the range of 27-56 nanometers; a coupling agent comprising prehydrolized silane; and 2_Q wherein said resin comprises a mixture of urethane acrylate, ethoxylated diacrylate, propoxylated diacrylate, ethoxylated trimethlyolpropane triacrylate, and acylphosphine oxide.

17. The coated subsfrate of claim 12, wherein said substrate is a polyvinyl 5 chloride subsfrate, and said cured coating is a radiation-cured coating on at least a portion of said polyvinyl chloride substrate.

18. The coated substrate of claim 17, wherein said polyvinyl chloride substrate comprises polyvinyl chloride plastisol.

19. The coated substrate of claim 18, further comprising: a felt layer; a gel layer having a gel layer bottom side disposed on said felt layer; a print layer disposed on a gel layer top side of said gel layer; and wherein a bottom side of said polyvinyl chloride substrate is disposed on said print layer; and said radiation-cured coating is disposed on a top side of said polyvinly chloride substrate.

20. A process for making a coating on a substrate, comprising the steps of: distributing a pre-cured coating mixture comprising a radiation-curable resin and an initiator over at least a portion of a substrate to form a pre-cured coating having an inherent macroscopic texture; and curing said pre-cured coatmg to form a cured coating having said macroscopic texture.