METHOD OF PROCESSING OPEN-CELLED MICROCELLULAR POLYMERIC FOAMS WITH CONTROLLED POROSITY FOR USE AS VASCULAR GRAFTS AND
STENT COVERS
BACKGROUND OF THE INVENTION
Field of the Invention:
This invention relates generally to expandable intraluminal vascular grafts and stents, and more particularly concerns grafts and stents coated or covered with an open-celled microcellular polymeric foam component capable of carrying and releasing therapeutic drugs, and a method of incorporating therapeutic drugs into the open-celled microcellular polymeric foam component of such grafts and stents.
Description of Related Art:
Vascular grafts and stents are vascular interventional devices that are typically implanted within a vessel in a contracted state and expanded when in place in the vessel in order to maintain patency of the vessel to allow fluid flow through the vessel. Ideally, implantation of such vascular interventional devices is accomplished by moving the device along a guide wire previously placed in the vessel, and expanding and locking the device in an expanded state by inflation of a balloon within the device. The graft or stent can then be left in place by deflating the balloon and removing the guide wire. However, restenosis of blood vessels, such as coronary vessels treated with percutaneous transluminal coronary angioplasty (PTCA) or stents is a current clinical challenge. To address this problem, various approaches are being developed to reduce restenosis by locally delivering drugs to the target site of possible restenosis. Stents commonly have a metallic structure to provide the strength required to function as a stent, but commonly have been unable to satisfactorily deliver localized therapeutic pharmacological agents to a blood vessel at the location being treated with the stent. While polymeric materials that can be loaded with and release drugs or other pharmacological treatments can be used for drug delivery, polymeric materials may not fulfill
the structural and mechanical requirements of a stent, especially when the polymeric materials are loaded with a drug, since drug loading of a polymeric material can significantly affect the structural and mechanical properties of the polymeric material. Since it is often useful to provide localized therapeutic pharmacological treatment of a blood vessel at the location being treated with the stent, it would be desirable to provide a polymeric component for grafts and stents to provide the capability of being loaded with therapeutic drugs, to function together with the graft or stent for placement and release of the therapeutic drugs at a specific intravascular site.
Commonly used grafts in the industry are formed from expanded polytetrafluoroethylene (ePTFE), and knitted polyesters such as Dacron. However, the use of grafts formed with such polymeric material is typically restricted to larger vessels greater than about four millimeters in diameter. When used with narrower blood vessels, these types of grafts tend to become occluded. Moreover, the compliance of such grafts commonly does not match that of natural artery. In recent years, improved polymers such as polyurethanes containing carbonate linkages, such as that available under the trade name "C ARBOTHANE" from The Carboline Company of St. Louis, Missouri, and the material available under the trade name "CHRONOFLEX" from CardioTech International, Inc. ofWoburn, Massachusetts, have been developed for use in forming small bore vascular grafts. The mechanical characteristics of these grafts are close to that of natural arteries. Such a polymeric component for use in forming vascular grafts and stent covers capable of carrying and delivering therapeutic drugs should have a microporous, open-celled structure, because the porosity not only allows the material to carry and deliver therapeutic drugs, but also permits ingrowth into the material of cells and capillaries that take part in the healing process, and can nurture the pseudointima. Currently, process techniques that have commonly been employed to make these polymers microporous include laser drilling of holes in the polymer tubing, and extrusion of the polymeric material with blowing agents, which maybe chemicals or gas, to create cells in the extruded tubing. Laser drilling of such material produces holes in the material, while extrusion with blowing agents commonly results in large non-uniform cells on the order of millimeters in diameter. However, conventional foaming techniques that use blowing agents, either using chemical blowing agents or gas assisted
blowing agents, do not typically result in an open-celled reticulated structure with an accurately controlled, uniform cell size.
Microcellular polymeric foams are also known that are characterized by cell sizes in the range of 0.1 to 100 microns, with cell densities in the range of 109 to 1015 cells per cubic cm. Typically, such microcellular polymeric foams exhibit properties comparable or superior to properties of structural foams, and, in some cases to the unfoamed polymer. Suitable microcellular foams are currently preferably produced by exposure of the thermoplastic polymer to super-critical CO2 fluid under high temperature and pressure to saturate the thermoplastic polymer with the super-critical CO2 fluid, and then cooling the thermoplastic polymer to foam the amorphous and semi-crystalline thermoplastic polymers. Such suitable microcellular foams can be produced as described in U.S. Patent Nos.4,473,665 and 5,160,674, incorporated herein by reference in their entirety. The foaming process can be carried out on extruded polymer tubing of the proper dimension. The first stage of microcellular foam processing involves dissolving an inert gas, such as nitrogen or C02, under pressure into the polymer matrix. The next phase is the rapid creation of microvoids. This is initiated by inducing large thermodynamic instability. The thermodynamic instability is induced by quickly decreasing the solubility of the gas in the polymer by changing the pressure or temperature.
There remains a need for vascular grafts and stent covers having a porosity that can be controlled to be suitable for the types of therapeutic drugs to be carried and delivered to a target site to be treated. The present invention meets this and other needs.
SUMMARY OF THE INVENTION
Briefly, and in general terms, the present invention provides for improved porous vascular grafts and stent covers formed of open-celled microcellular polymeric foams having a porosity that can be modified to be adapted for carrying and delivering different types of therapeutic drugs. The morphology of the open-celled microcellular polymeric foams, including the openness, cell size and porosity of the foams, can be controlled so that the cell sizes can be made very uniform, and can be controlled precisely by changing thermodynamic variables like pressure and temperature during formation of the open-celled microcellular
polymeric foams. The open-celled microcellular polymeric foams can be formed by a batch process that can be easily controlled and operated, in which extruded tubing can be cut to the desired lengths and then foamed in separate pressure chamber.
The invention accordingly provides for a stent cover that can be used to carry and deliver therapeutic drugs or as an overcoat barrier layer to control drug release by a drug- coated stent. In one presently preferred embodiment, such a stent cover comprises a tubular member for use with a stent, the stent cover including at least one layer of a porous, microcellular foam formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. The layer of porous, microcellular foam can range in thickness from about a few nanometers to a millimeter, and the diameter of the pores and the amount of porosity in the foam can be adjusted according to the molecular weight of the drug compound. The diameter of the pores or cells of the microcellular foam can, for example, be made as small as about a few nanometers to accommodate low molecular weight compounds with molecular weights in the range of 10- 1 ,000 daltons up to large molecular weight compounds with molecular weight in the range of 1,000 to 100,000 daltons, as well as supra molecular structures with molecular weights greater than 100,000 daltons. The polymeric material from which the microcellular foam can be formed include polyurethanes containing carbonate linkages, and biodegradable polymers such as poly-L-lactic acid (PLLA), poly-DL-lactic acid (DL-PLA), polyglycolic acid (PGA), p-dioxanone, and trimethylene carbonate/glycolic acid copolymers (TMC/PGA), for example, although other similar materials may also be suitable. Examples of supra molecular structures include viral particles used for gene therapy, liposomes, ribozymes, and the like.
In another aspect, the invention also provides for a composite metal and polymer vascular graft or coated stent, comprising an interior structural stent member, and an outer layer or coating of a porous, microcellular foam formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. In a currently preferred embodiment, the stent can be formed of a metal such as stainless steel, tantalum, a composite of tantalum and silicon carbide, gold, or can be formed of a polymer, or of a composite. Other metals that may also be suitable for forming the stent include nickel-titanium alloy, platinum-
iridium alloy, molybdenum-rhenium alloy, gold, magnesium, and combinations thereof. The porous, microcellular foam can range in thickness from about a few nanometers to a millimeter, and the diameter of the pores and the amount of porosity in the foam can be adjusted according to the molecular weight of the drug compound. The diameter of the pores or cells of the microcellular foam can, for example, be made as small as about a few nanometers to accommodate low molecular weight compounds with molecular weights in the range of 10-1,000 daltons up to large molecular weight compounds with molecular weight in the range of 1,000 to 100,000 daltons and supramolecular structures with molecular weights greater than 100,000 daltons. The polymeric material from which the microcellular foam can be formed include polyurethanes containing carbonate linkages, and biodegradable polymers such as poly-L-lactic acid (PLLA), poly-DL-lactic acid (DL-PLA), polyglycolic acid (PGA), p-dioxanone, and trimethylene carbonate/glycolic acid copolymers (TMC/PGA), for example, although other similar materials may also be suitable. Examples of supra molecular structures include viral particles used for gene therapy, liposomes, ribozymes, and the like. In another aspect, the present invention also provides for a method of making a composite metal and polymer vascular graft or coated stent, including an interior structural stent member and an outer layer or coating of a porous, microcellular foam formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel, comprising the steps of providing a stent, and coating the stent with an outer layer or coating of a porous, microcellular foam formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. In another aspect, the method can further comprise the step of loading a therapeutic drug into the outer layer or coating of a porous, microcellular foam for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. The porous, microcellular foam can be formed with different thicknesses, pore sizes, pore distributions, and pore-size gradients to control drug release or pharmacokinetics, as desired.
Preferred examples of therapeutic drugs or pharmacologic compounds that may be loaded into the outer layer of the composite metal and polymer vascular graft or coated stent or into the stent cover and delivered to the target site in the vasculature, or loaded onto the stent over which the stent cover is to be disposed for controlling the drug release of the drug
coated stent include taxol, aspirin, prostaglandins, and the like. Therapeutic agents that may also be suitable for loading into the stent cover or for moderation of drug release from the covered stent may also include, for example, antiplatelets, antithrombins, cytostatic or antiproliferative agents, sodium heparin, low molecular weight heparin, hirudin, argatroban, forskolin, vapiprost, prostacyclin and prostacyclin analogues, dextran, D-phe-pro-arg- chloromethylketone, dipyridamole, glycoprotein Ilb/Iϋa platelet membrane receptor antibody, recombinant hirudin, thrombin inhibitor, angiopeptin, angiotensin converting enzyme inhibitors, Lisinopril, and cisplatin; anti-inflammatories such as steroids; anti-cancer compounds such as taxon and actinomycin; macromolecules such as peptides, proteins, genes and antisense compounds; calcium channel blockers, colchicine, fibroblast growth factor antagonists, fish oil, omega 3-fatty acid, histamine antagonists, HMG-CoA reductase inhibitor, methotrexate, monoclonal antibodies, nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitor, serotonin blockers, thioprotease inhibitors, triazolopyrimidine and other PDGF antagonists, alpha-interferon and genetically engineered epithelial cells, supramolecular weight structures with molecular weights greater than 100,000 daltons, and up to about 1 ,000,000 daltons, including viral particles used for gene therapy, ribozymes and liposomes, and combinations thereof.
These and other aspects and advantages of the invention will become apparent from the following detailed description and the accompanying drawings, which illustrate by way of example the features of the invention.
BRIEF DESCRIPTION OF THE DRAWINGS
Figure 1 is a perspective view of a combination of a stent and stent cover according to the present invention;
Fig. 2 is a cross-sectional view taken along line 2-2 of Fig. 1;
Fig. 3 is a perspective view of a composite metal and polymer vascular graft or coated stent according to the present invention; and
Fig. 4 is a cross-sectional view of an element of the composite metal and polymer vascular graft or coated stent taken along line 4-4 of Fig. 3.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
Stents commonly have a metallic structure to provide the strength required to function as a stent, while polymeric materials are typically used for loading and release of drugs or other pharmacological treatments for drug delivery. Vascular grafts can be made of polymers such as polyurethanes containing carbonate linkages, but such polymeric components used in forming components of stents or vascular grafts capable of carrying and delivering therapeutic drugs typically do not have a microporous, open-celled structure, and conventional techniques for forming foamed polymeric materials typically do not result in an open-celled reticulated structure with an accurately controlled, uniform cell size.
As is illustrated in the drawings, the invention is embodied in improved porous vascular grafts and stent covers formed of open-celled microcellular polymeric foams having a porosity adapted for carrying and delivering different types of therapeutic drugs. Referring to Figs. 1 and 2, in a currently preferred embodiment, the invention provides for a stent cover that can be used to carry and deliver therapeutic drugs or as an overcoat barrier layer to control drug release by a drug-coated stent such as stent 10. The stent can be of the type that is expanded by a balloon member or other similar device, or of the type that is self-expanding, and can have virtually any pattern known from prior art stents. In a currently preferred embodiment, the stent can be formed of a metal such as stainless steel, tantalum, a composite of tantalum and silicon carbide, gold, or can be formed of a polymer, or of a composite. Other metals that may also be suitable for forming the stent include nickel-titanium alloy, platinum- iridium alloy, molybdenum-rhenium alloy, gold, magnesium, and combinations thereof.
In a currently preferred embodiment, the stent cover 12 comprises a tubular member adapted to be mounted over the stent. As shown in Figs. 1 and 2, the stent cover includes at least one layer 14 of a porous, microcellular foam formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. The layer of porous, microcellular foam can range in thickness from about a few nanometers to a millimeter, and the diameter of the pores and the amount of porosity in the foam can be adjusted according to the molecular weight of the drug compound.
Microcellular foams are typically characterized by cell sizes or diameters in the range of 0. 1 to 100 microns, and cell densities in the range of 109 to 1015 cells per cubic cm. Typically, microcellular plastics exhibit comparable or superior properties to structural foams, and, in some cases to the unfoamed polymer. Microcellular foams can be formed based upon the process developed at MIT and Clarkson Univ., as outlined in V. Kumar and N. P. Suh, Polym. Eng. Sci., 30, pp. 1323-1329, (1990), and C. Wang, K. Cox and G. Campbell, J. Vinyl Additives Tech., 2(2), pp. 167-169 (1996).
The foaming process can be carried out on polymer preforms such as extruded polymer tubing of the desired dimension. The first stage of microcellular foam processing involves dissolving an inert gas, such as nitrogen or C02, under pressure into the polymer matrix. The next phase is the rapid creation of microvoids. This is initiated by inducing large thermodynamic instability. The thermodynamic instability is induced by quickly decreasing the solubility of the gas in the polymer by changing the pressure or temperature.
The diameter of the pores or cells of the microcellular foam can, for example, be made as small as about a few nanometers to accommodate low molecular weight compounds with molecular weights in the range of 10-1,000 daltons up to large molecular weight compounds with molecular weight in the range of 1,000 to 100,000 daltons. The polymeric material from which the microcellular foam can be formed include polyurethanes containing carbonate linkages, and biodegradable polymers such as poly-L-lactic acid (PLLA), poly-DL-lactic acid (DL-PLA), polyglycolic acid (PGA), p-dioxanone, and trimethylene carbonate/glycolic acid copolymers (TMC/PGA), for example, although other similar materials may also be suitable.
The morphology of the open-celled microcellular polymeric foams, including the openness, cell size and porosity of the foams, can be controlled so that the cell sizes can be made very uniform, and can be controlled precisely by changing thermodynamic variables like pressure and temperature during formation of the open-celled microcellular polymeric foams. The open-celled microcellular polymeric foams can be formed by a batch process that can be easily controlled and operated, in which extruded tubing can be cut to the desired lengths and then foamed in separate pressure chamber. In another presently preferred embodiment illustrated in Figs. 3 and 4, the invention provides for a composite metal and polymer vascular graft or coated stent,
comprising an interior structural stent member 10, and an outer layer or coating of a porous, microcellular foam 16 formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. The composite metal and polymer vascular graft or coated stent, can be formed by providing a stent member 10, and coating the stent with an outer layer or coating of a porous, microcellular foam formed from a polymeric material capable of absorbing and releasing therapeutic drugs at predictable rates for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. This can be accomplished by coating the stent member with a polymer matrix in which an inert gas, such as nitrogen or C02, is dissolved under pressure. The creation of microvoids to form the microcellular foam can be accomplished by quickly decreasing the solubility of the gas in the polymer matrix coated on the stent member by changing the pressure or temperature. As noted above, the porous, microcellular foam can range in thickness from about a few nanometers to a millimeter, and the diameter of the pores and the amount of porosity in the foam can be adjusted according to the molecular weight of the drug compound. The diameter of the pores or cells of the microcellular foam can, for example, be made as small as about a few nanometers to accommodate low molecular weight compounds with molecular weights in the range of 10-1,000 daltons up to large molecular weight compounds with molecular weight in the range of 1,000 to 100,000 daltons. The polymeric material from which the microcellular foam can be formed include polyurethanes containing carbonate linkages, and biodegradable polymers such as poly-L-lactic acid (PLLA), poly-DL-lactic acid (DL-PLA), polyglycolic acid (PGA), p-dioxanone, and trimethylene carbonate/glycolic acid copolymers (TMC/PGA), for example, although other similar materials may also be suitable.
In another currently preferred embodiment, a therapeutic drug can be loaded into the outer layer or coating 16 of porous, microcellular foam for delivery of the therapeutic drugs in localized drug therapy in a blood vessel. The porous, microcellular foam can be formed with different thicknesses, pore sizes, pore distributions, and pore-size gradients to control drug release or pharmacokinetics, as desired. The stent cover may also be loaded with such therapeutic drugs for a similar purpose in use in combination with a stent. Alternatively, or in addition, particularly when the stent is formed of a suitable material, the stent may also be drug loaded. Preferred examples of therapeutic drugs or pharmacologic compounds that
may be loaded, for controlling the release of the drug include taxol, aspirin, prostaglandins, and the like. Therapeutic agents that may also be suitable for loading into the stent cover or for moderation of drug release from the covered stent may also include, for example, antiplatelets, antithrombins, cytostatic or antiproliferative agents, sodium heparin, low molecular weight heparin, hirudin, argatroban, forskolin, vapiprost, prostacyclin and prostacyclin analogues, dextran, D-phe-pro-arg-chloromethylketone, dipyridamole, glycoprotein πb/Iϋa platelet membrane receptor antibody, recombinant hirudin, thrombin inhibitor, angiopeptin, angiotensin converting enzyme inhibitors, Lisinopril, and cisplatin; anti-inflammatories such as steroids; anti-cancer compounds such as taxon and actinomycin; macromolecules such as peptides, proteins, genes and antisense compounds; calcium channel blockers, colchicine, fibroblast growth factor antagonists, fish oil, omega 3-fatty acid, histamine antagonists, HMG-CoA reductase inhibitor, methotrexate, monoclonal antibodies, nitroprusside, phosphodiesterase inhibitors, prostaglandin inhibitor, serotonin blockers, thioprotease inhibitors, triazolopyrimidine and other PDGF antagonists, alpha-interferon and genetically engineered epithelial cells, supramolecular weight structures with molecular weights greater than 100,000 daltons, and up to about 1,000,000 daltons, including viral particles used for gene therapy, ribozymes and liposomes, and combinations thereof.
It will be apparent from the foregoing that while particular forms of the invention have been illustrated and described, various modifications can be made without departing from the spirit and scope of the invention. Accordingly, it is not intended that the invention be limited, except as by the appended claims.