WO1996006881A2 - Sinterable semi-crystalline powder and article formed therewith - Google Patents
Sinterable semi-crystalline powder and article formed therewith Download PDFInfo
- Publication number
- WO1996006881A2 WO1996006881A2 PCT/US1995/011006 US9511006W WO9606881A2 WO 1996006881 A2 WO1996006881 A2 WO 1996006881A2 US 9511006 W US9511006 W US 9511006W WO 9606881 A2 WO9606881 A2 WO 9606881A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- powder
- bed
- sintered
- polymer
- temperature
- Prior art date
Abstract
Description
Claims