WO1995009436A1 - Patterned array of uniform metal microbeads - Google Patents
Patterned array of uniform metal microbeads Download PDFInfo
- Publication number
- WO1995009436A1 WO1995009436A1 PCT/US1994/009507 US9409507W WO9509436A1 WO 1995009436 A1 WO1995009436 A1 WO 1995009436A1 US 9409507 W US9409507 W US 9409507W WO 9509436 A1 WO9509436 A1 WO 9509436A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- microspheres
- substrate
- array
- microbeads
- Prior art date
Abstract
Description
Claims