WO1994017116A1 - Process for improving impact resistance of coated plastic substrates - Google Patents
Process for improving impact resistance of coated plastic substrates Download PDFInfo
- Publication number
- WO1994017116A1 WO1994017116A1 PCT/US1994/000249 US9400249W WO9417116A1 WO 1994017116 A1 WO1994017116 A1 WO 1994017116A1 US 9400249 W US9400249 W US 9400249W WO 9417116 A1 WO9417116 A1 WO 9417116A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- abrasion resistant
- primer layer
- plastic
- poiyurethane
- coating composition
- Prior art date
Abstract
Description
Claims