WO1992019241A1 - A controlled, sustained release delivery system for smoking cessation - Google Patents
A controlled, sustained release delivery system for smoking cessation Download PDFInfo
- Publication number
- WO1992019241A1 WO1992019241A1 PCT/US1992/003860 US9203860W WO9219241A1 WO 1992019241 A1 WO1992019241 A1 WO 1992019241A1 US 9203860 W US9203860 W US 9203860W WO 9219241 A1 WO9219241 A1 WO 9219241A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lobeline
- delivery system
- kit
- drug delivery
- biodegradable polymer
- Prior art date
Abstract
Description
Claims