US20140349422A1 - Method for hybrid encapsulation of an organic light emitting diode - Google Patents
Method for hybrid encapsulation of an organic light emitting diode Download PDFInfo
- Publication number
- US20140349422A1 US20140349422A1 US14/455,208 US201414455208A US2014349422A1 US 20140349422 A1 US20140349422 A1 US 20140349422A1 US 201414455208 A US201414455208 A US 201414455208A US 2014349422 A1 US2014349422 A1 US 2014349422A1
- Authority
- US
- United States
- Prior art keywords
- layer
- inorganic
- sublayer
- hmdso
- hybrid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Methods and apparatus for encapsulating organic light emitting diode (OLED) structures disposed on a substrate using a hybrid layer of material are provided. The processing parameters used during deposition of the hybrid layer of material allow control of the characteristics of the deposited hybrid layer. The hybrid layer may be deposited such that the layer has characteristics of an inorganic material in some sublayers of the hybrid layer and characteristics of an organic material in other sublayers of the hybrid layer. Use of the hybrid material allows OLED encapsulation using a single hard mask for the complete encapsulating process with low cost and without alignment issues present in conventional processes.
Description
- This is a continuation application of U.S. patent application Ser. No. 14/296,263, filed Jun. 4, 2014, which is a continuation application of U.S. patent application Ser. No. 13/361,637, now U.S. Pat. No. 8,772,066, filed Jan. 30, 2012, which claims benefit of U.S. Provisional Patent Application Ser. No. 61/482,869, filed May 5, 2011 and U.S. Provisional Patent Application Ser. No. 61/440,701, filed Feb. 8, 2011, each of which is herein incorporated by reference.
- 1. Field
- Embodiments of the invention generally relate to a method and apparatus for encapsulating an organic light emitting diode.
- 2. Description of the Related Art
- Organic light emitting diode (OLED) displays have gained significant interest recently in display applications due to their faster response time, larger viewing angles, higher contrast, lighter weight, low power and amenability to flexible substrates such as compared to liquid crystal displays (LCD). However, OLED structures may have a limited lifetime, characterized by a decrease in electroluminescence efficiency and an increase in drive voltage. A main reason for the degradation of OLED structures is the formation of non-emissive dark spots due to moisture or oxygen ingress. For this reason, OLED structures are typically encapsulated by an organic layer sandwiched between inorganic layers. The organic layer is utilized to fill any voids or defects in the first inorganic layer such that the second inorganic layer has a substantially uniform surface or deposition.
-
FIGS. 1A-C illustrate a conventional process for depositing the encapsulating layers, typically including a first inorganic layer 106 (shown as 106 a and 106 b), an organic layer 108 (shown as 108 a and 108 b) and a second inorganic layer 116 (shown as 116 a and 116 b). The process begins by aligning afirst mask 109 over asubstrate 100 such that anOLED structure 104 is exposed through anopening 107 unprotected by themask 109, as shown inFIG. 1A . Thefirst mask 109 defines the opening 107 having adistance 110 from theOLED structure 104 to the edge of thefirst mask 109. Thefirst mask 109 is typically made from a metal material, such as INVAR®. As illustrated inFIG. 1A , thefirst mask 109 is utilized to pattern the first inorganic layer 106 (shown as 106 a, 106 b), such as silicon nitride or aluminum oxide, over theOLED structure 104. Thefirst mask 109 is positioned such that aportion 105 of acontact layer 102 adjacent to theOLED structure 104 is covered by thefirst mask 109 so that theinorganic layer 106 does not deposit on thatportion 105. As illustrated inFIG. 1B , thefirst mask 109 is removed and replaced by asecond mask 114 having anopening 111 smaller than the opening 107 of thefirst mask 109. Thesecond mask 114 defines the opening 111 having adistance 112, which is shorter than thedistance 110 as defined by thefirst mask 109, from theOLED structure 104 to the edge of thesecond mask 114. By utilizing thesecond mask 114, an organic layer 108 (shown as 108 a, 108 b) is deposited over the firstinorganic layer 106. As thesecond mask 114 has theopening 111 smaller than thefirst mask 109, theorganic layer 108 does not completely cover the underlyinginorganic layer 106. The encapsulation of theOLED structure 104 is finished by depositing at least a second inorganic layer 116 (shown as 116 a and 116 b) over the top of the exposed portion of the firstinorganic layer 106 and theorganic layer 108 utilizing thefirst mask 109 as illustrated inFIG. 1C . The secondinorganic layer 116 fully encapsulates theorganic layer 108 with the firstinorganic layer 106, thereby encapsulating theOLED structure 104 while leaving theportion 105 of thecontact layer 102 exposed. - The conventional process flow described above has significant challenges preventing commercially viable scaling for use with larger area substrates, such as substrates having a top plan area greater than about 1,500 centimeters square. For example, the two
metal masks metal mask OLED structure 104 is required, generally within 100 μm. As thesemasks masks openings masks OLED structure 104. Loss of alignment may result in incomplete encapsulation of theOLED structure 104, which in turn leads to shortened life and diminished performance of theOLED device 104. - Therefore, an improved method and apparatus for encapsulating an OLED structure is needed.
- In one embodiment of the present invention, a method for forming an encapsulating layer on an organic light emitting diode (OLED) substrate comprises forming a first inorganic layer on a region of a substrate having an OLED structure disposed thereon, forming a hybrid inorganic/organic layer on the first inorganic layer, and forming a second inorganic layer on the hybrid inorganic/organic layer.
- In another embodiment, a method for forming an encapsulating layer on an organic light emitting diode (OLED) substrate comprises forming a first inorganic sublayer of a hybrid layer on a region of a substrate having an OLED structure disposed thereon, forming an organic sublayer of the hybrid layer on the first inorganic sublayer, and forming a second inorganic sublayer of the hybrid layer on the organic sublayer.
- In yet another embodiment, an encapsulating layer on an organic light emitting diode (OLED) substrate comprises a first inorganic sublayer of a hybrid layer formed on a region of a substrate having an OLED structure disposed thereon, an organic sublayer of the hybrid layer formed on the first inorganic sublayer, and a second inorganic sublayer of the hybrid layer formed on the organic sublayer.
- So that the manner in which the above recited features of the present disclosure can be understood in detail, a more particular description of the disclosure, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this disclosure and are therefore not to be considered limiting of its scope, for the disclosure may admit to other equally effective embodiments.
-
FIGS. 1A-1C illustrate schematic cross-sectional views of an OLED structure during different stages of a conventional encapsulation sequence known in the art. -
FIG. 2 is a flow diagram of a method for encapsulating an OLED structure in accordance with one embodiment of the present invention. -
FIGS. 3A-3C illustrate schematic cross-sectional views of an OLED structure during different stages of the method ofFIG. 2 . -
FIG. 4 is a flow diagram of a method for encapsulating an OLED structure in accordance with another embodiment of the present invention. -
FIGS. 5A-5C illustrate schematic cross-sectional views of an OLED structure during different stages of the method ofFIG. 4 . - To facilitate understanding, identical reference numerals have been used, where possible, to designate identical elements that are common to the figures. It is contemplated that elements and features of one embodiment may be beneficially incorporated in other embodiments without further recitation.
- The present disclosure provides methods and apparatus for encapsulating OLED structures disposed on a substrate using a hybrid layer of material. The processing parameters used during deposition of the hybrid layer of material allow control of the characteristics of the deposited hybrid layer. The hybrid layer may be deposited such that the layer has characteristics of an inorganic material in some sublayers of the hybrid layer and characteristics of an organic material in other sublayers of the hybrid layer. Use of the hybrid material allows OLED encapsulation using a single hard mask for the complete encapsulating process with low cost and without alignment issues present in conventional processes.
-
FIG. 2 is a flow diagram of amethod 200 for encapsulating an OLED structure disposed on a substrate.FIGS. 3A-3C illustrate schematic cross-sectional views of an OLED structure during different stages of theencapsulation method 200 ofFIG. 2 . Themethod 200 starts atprocess 202 by providing asubstrate 100 having a preformedOLED structure 104 disposed thereon. Similar to that discussed above, thesubstrate 100 may have acontact layer 102 disposed thereon, with anOLED structure 104 disposed on thecontact layer 102, as shown inFIG. 3A . - At
process 204, amask 309 is aligned over thesubstrate 100 such that theOLED structure 104 is exposed through anopening 307 unprotected by themask 309, as shown inFIG. 3A . Themask 309 is positioned such that aportion 305 of thecontact layer 102 adjacent theOLED structure 104 is covered by themask 309 so that the any subsequently deposited material does not deposit on theportion 305. Themask 309 may be made from a metal material, such as INVAR®. - At
process 206, a firstinorganic layer 308 is deposited on thesubstrate 100, as shown inFIG. 3A . The firstinorganic layer 308 has afirst portion 308 a and asecond portion 308 b. Thefirst portion 308 a of the firstinorganic layer 308 is deposited through theopening 307 onto a region of thesubstrate 100 exposed by themask 309, which includes theOLED structure 104 and a portion of thecontact layer 102. Thesecond portion 308 b of the firstinorganic layer 308 is deposited on themask 309 covering a second region of thesubstrate 100, which includes theportion 305 of thecontact layer 102. The firstinorganic layer 308 is a dielectric layer, such as SiN, SiON, SiO2, Al2O3, AlN, or other suitable dielectric layers. The firstinorganic layer 308 may be deposited by a suitable deposition technique, such as CVD, PVD, spin-coating, or other suitable technique. - At
process 208, after the firstinorganic layer 308 is formed on thesubstrate 100, ahybrid layer 312 is then formed on the firstinorganic layer 308 on thesubstrate 100, as shown inFIG. 3B . Afirst portion 312 a of thehybrid layer 312 may be deposited on thesubstrate 100 through theopening 307 of themask 309 on the region of thesubstrate 100 exposed by themask 309, covering thefirst portion 308 a of first theinorganic layer 308. Asecond portion 312 b of thehybrid layer 312 is deposited on thesecond portion 308 b of the firstinorganic layer 308 disposed on themask 309, which covers theportion 305 of thecontact layer 102. - The
hybrid layer 312 is a layer of material that is controlled through the deposition process, such as the flow ratio of gases, to be organic and have properties of organic materials, such as acrylate, methacrylate, acrylic acid, or the like, or be inorganic and have properties of inorganic materials, such as those used for the firstinorganic layer 308 described above. When the hybrid material is in the inorganic state, it has inorganic material properties, such as density and porosity approximately the same as those of the listed inorganic materials. When the hybrid material is in the organic state, it has organic properties that may include characteristics of organic materials including stress relief, particle conformality, and flexibility approximately the same as those of the listed organic materials. Generally, a hybrid material in its “organic” state is more flexible and less dense than the hybrid material in its “inorganic” state. - An example of a material used in the
hybrid layer 312 is plasma-polymerized hexamethyldisiloxane (pp-HMDSO). Deposition of the pp-HMDSO material layer is achieved by flowing an oxygen-containing gas and HMDSO gas. During deposition of the pp-HMDSO layer, the ratio of the flow of oxygen-containing gas to the flow of HMDSO gas is controlled to control the organic/inorganic state and properties of the resulting pp-HMDSO layer. - In one example, the oxygen-containing gas is oxygen gas (O2). A high O2/HMDSO flow ratio (e.g., greater than 10) may be maintained during processing to deposit an inorganic pp-HMDSO layer having characteristics, such as the high density and low porosity barrier properties associated with inorganic films. A low O2/HMDSO flow ratio (e.g, less than 2) may be maintained during processing to deposit an organic pp-HMDSO layer having properties, such as the low stress properties associated with organic films.
- Control of the oxygen gas used during deposition of the pp-HMDSO layer can minimize potential reaction with residual silane if present in the gas line or inlet of the deposition chamber. The reaction between the oxygen gas and residual silane can result in undesirable particle formation in the pp-HMDSO layer, which has the potential for contaminating the final OLED device. One method of minimizing the potential for reaction with silane is to perform a gas-line purge between deposition processes. Alternatively, other gases such as nitrous oxide, which are less reactive with silane relative to oxygen gas, may be used. It has been found that the use of nitrous oxide gas (N2O) as the oxygen-containing gas results in minimal reaction with residual silane, thereby reducing, if not eliminating, the need to thoroughly purge the gas lines and chamber after use of silane within the chamber. Thus, a high-quality pp-HMDSO layer can be deposited without any intervening purge process between the inorganic
layer deposition process 206 and the hybridlayer deposition process 208. - Therefore, in one example the oxygen-containing gas is nitrous oxide gas. A high N2O/HMDSO flow ratio (e.g., greater than 10) may be maintained during processing to deposit a relatively inorganic pp-HMDSO layer having characteristics, such as the high density and low porosity barrier properties associated with inorganic films. A low N2O/HMDSO flow ratio (e.g, less than 2) may be maintained during processing to deposit an organic pp-HMDSO layer having properties, such as the low stress properties associated with organic films.
- It has been found that inorganic pp-HMDSO provides an excellent moisture barrier due to its high density and low porosity, even though its water contact angle is low (e.g., below 50 degrees, such as 10 to 30 degrees). It has further been found that although such organic pp-HMDSO exhibits excellent flexibility and stress relieving characteristics like the organic materials listed above, the organic pp-HMDSO also has good moisture resistance due to its high water contact angle (e.g., greater than 50 degrees, such as 60 to 99 degrees). In one example, the organic pp-HMDSO has an FTIR of less than 20% of pp-HMDSO in a silicon dioxide network.
- In an exemplary embodiment, the processing parameters of the pp-HMDSO layer may include an HMDSO flow rate between about 100 sccm and about 800 sccm, the power density may be between about 0.15 W/cm2 and about 0.75 W/cm2, the pressure may be between about 500 mTorr and about 2000 mTorr, and the spacing may be between about 500 to 1200 mils.
- At
process 210, a secondinorganic layer 314 is formed on thesubstrate 100, covering thehybrid layer 312 and the firstorganic layer 308 formed on theOLED structure 104, as shown inFIG. 3C . The secondinorganic layer 314 includes afirst portion 314 a deposited over thefirst portion 312 a of thehybrid layer 312 and asecond portion 314 b deposited over thesecond portion 312 b of thehybrid layer 312. - The second
inorganic layer 314 may be a dielectric layer similar to the firstinorganic layer 308. The secondinorganic layer 314 is a dielectric layer such as SiN, SiON, SiO2, or other suitable dielectric layers. The secondinorganic layer 314 may be deposited by a suitable deposition technique, such as CVD, PVD, spin-coating, or other suitable technique. - The second
inorganic layer 314 may be deposited on thesubstrate 100 using thesame mask 309 utilized to deposit the firstinorganic layer 308 and thehybrid layer 312. This is possible due to the ability to control the properties, such as hydrophobicity of thehybrid layer 312 to have both good barrier properties (i.e., inorganic state) and good stress relief properties (i.e., organic state). At the same time, thehybrid layer 312, in all regions may be maintained to have adequate hydrophobic properties to ensure good encapsulation of the OLED structure 104 (i.e., density/porosity or water contact angle). Thus, themask 309 does not have to be changed or removed during the encapsulation sequence. - In one embodiment, the deposition of the
hybrid layer 312 is controlled such that deposition of a sublayer adjacent the firstinorganic layer 308 and another sublayer adjacent the secondinorganic layer 314 is controlled such that the hybrid material in those respective sublayers is inorganic, which enables good adhesion to the first and secondinorganic layers hybrid layer 312 is controlled to have a central sublayer that is organic to provide good stress relief between the inorganic sublayers. For example, the deposition of thehybrid layer 312 onto the firstinorganic layer 308 is controlled to be inorganic having properties closely matching that of the first inorganic layer (e.g., O2/HMDSO or N2O/HMDSO flow ratio greater than 10). Proceeding upward, the deposition is controlled to have a gradual gradient, wherein the material is increasingly organic (e.g, decreasing O2/HMDSO or N2O/HMDSO flow ratio to less than 2). Continuing upward, the deposition is controlled to have a gradual gradient, wherein the material is increasingly inorganic (e.g., increasing O2/HMDSO or N2O/HMDSO flow ratio) until the material is inorganic having properties closely matching that of the second inorganic layer (e.g., O2/HMDSO or N2O/HMDSO flow ratio greater than 10) are achieved. The deposition gradient may be controlled by analog mode (i.e., continuous modulation), digital mode (i.e., stepwise modulation), or alternating modulation. -
FIG. 4 is a flow diagram of amethod 400 for encapsulating an OLED structure disposed on a substrate.FIGS. 5A-C illustrate schematic cross-sectional views of an OLED structure using theencapsulation method 400 ofFIG. 4 . Themethod 400 starts atprocess 402 by providing a substrate having a preformedOLED structure 104 disposed on asubstrate 100. Similar to that discussed above, thesubstrate 100 may have acontact layer 102 disposed thereon, with anOLED structure 104 disposed on thecontact layer 102, as shown inFIG. 5A . - At
process 404, amask 509 is aligned over thesubstrate 100 such that theOLED structure 104 is exposed through anopening 507 unprotected by themask 509, as shown inFIG. 5A . Themask 509 is positioned such that aportion 505 of thecontact layer 102 adjacent to theOLED structure 104 is covered by themask 509 such that the any subsequently deposited material does not deposit on theportion 505. Themask 509 may be made from a metal material, such as INVAR®. - At processes 406-410, a
hybrid layer 512 is deposited on thesubstrate 100, as shown inFIG. 5C . Thehybrid layer 512 is deposited insublayers 512 a-c through theopening 507 onto a region of thesubstrate 100 exposed by themask 509, which includes theOLED structure 104 and a portion of thecontact layer 102. Thehybrid layer 512 is also deposited on themask 509 covering a second region of thesubstrate 100, which includes theportion 505 of thecontact layer 102. - As previously described with respect to the
hybrid layer 312, thehybrid layer 512 is a layer of material that is controlled through the deposition process, such as the flow ratio of gases, to be organic and have properties of organic materials, such as acrylate, methacrylate, acrylic acid, or the like, or inorganic and have properties of inorganic materials, such as those used for the firstinorganic layer 308 described above. An example of a material used in thehybrid layer 512 is plasma-polymerized hexamethyldisiloxane (pp-HMDSO). During deposition of the pp-HMDSO film, the ratio of oxygen-containing gas (e.g., O2 or N2O) flow to HMDSO flow may be controlled to control the organic/inorganic properties of the resulting pp-HMDSO film sublayers. - In
process 406, afirst sublayer 512 a of thehybrid layer 512 is deposited as shown inFIG. 5A . During deposition of thefirst sublayer 512 a, the process parameters are controlled such that deposition of thefirst sublayer 512 a is relatively inorganic having material properties matching those of the inorganic materials described above to provide good barrier properties to thehybrid layer 512. For example, thefirst sublayer 512 a of thehybrid layer 512 may be deposited with a high O2/HMDSO or N2O/HMDSO flow ratio (e.g., greater than 10) to provide a pp-HMDSO layer with good barrier properties (e.g., high density, low porosity). - In
process 408, asecond sublayer 512 b of thehybrid layer 512 is deposited as shown inFIG. 5B . During deposition of thesecond sublayer 512 b, the process parameters are controlled such that deposition of thesecond sublayer 512 b is organic having properties matching those of the organic materials described above to provide good stress relief betweensublayers second sublayer 512 b of thehybrid layer 512 may be deposited with a low O2/HMDSO or N2O/HMDSO flow ratio (e.g., less than 2) to provide a pp-HMDSO layer that is organic with organic properties and high water contact angle (e.g., greater than 50 degrees). - In
process 410, athird sublayer 512 c of thehybrid layer 512 is deposited as shown inFIG. 5C . During deposition of thethird sublayer 512 c, the process parameters are controlled such that deposition of thethird sublayer 512 c is inorganic and has properties matching those of the inorganic materials described above to provide good barrier properties to thehybrid layer 512. For example, thethird sublayer 512 c of thehybrid layer 512 may be deposited with a high O2/HMDSO or N2O/HMDSO flow ratio (e.g., greater than 10) to provide a relatively inorganic pp-HMDSO layer with good barrier properties and with a low contact angle (less than 50 degrees). - Although deposition of the
hybrid layer 512 is depicted and described above in three distinct sublayers, the deposition of the hybrid layer may be controlled more smoothly to deposit thehybrid layer 512 in a single layer with a gradient starting as inorganic at thefirst sublayer 512 a. The deposition parameters may then be gradually changed to provide a smooth (continuous or stepwise) gradient of material with increasingly organic properties (e.g., by decreasing the O2/HMDSO or N2O/HMDSO flow ratio) until thesublayer 512 b is organic. Then, the deposition parameters may be gradually changed to provide a smooth (continuous or stepwise) gradient of material with increasingly that is increasing inorganic (e.g., by increasing the O2/HMDSO or N2O/HMDSO flow ratio) until thesublayer 512 c is inorganic. - In an exemplary embodiment, the processing parameters of the pp-HMDSO layer may include an HMDSO flow rate between about 100 sccm and about 800 sccm, the power density may be between 0.15 W/cm2 and about 0.75 W/cm2, the pressure may be between about 500 mTorr and about 2000 mTorr, and the spacing may be between about 500 to 1200 mils.
- Thus, methods and apparatus for forming encapsulation layers on an OLED structure are provided. By utilizing a hybrid layer during the encapsulation formation process, a single mask may be used, thereby advantageously lowering the manufacture cost as compared to the conventional two hard mask deposition processes while increasing the manufacture throughput. It should be noted that although the embodiments described herein depict a single stack of encapsulation layers/sublayers, multiple stacks of encapsulation layers/sublayers may be used without deviating from the scope of the invention.
- While the foregoing is directed to embodiments of the present disclosure, other and further embodiments of the disclosure may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.
Claims (20)
1. A method for forming an encapsulating structure on an organic light emitting diode (OLED) substrate, comprising:
forming a first layer on a region of a substrate having an OLED structure disposed thereon, the region being defined by a mask;
forming a second layer on the first layer in the region defined by the mask, wherein the second layer is formed by supplying a processing gas comprising a HMDSO (hexamethyldisiloxane) gas throughout the formation of the second layer; and
forming a third layer on the second layer in the region defined by the mask.
2. The method of claim 1 , wherein the first layer, the second layer and the third layer are formed in the same chamber.
3. The method of claim 1 , wherein the second layer comprises:
a first sublayer having a majority of inorganic materials and a minority of organic materials;
a second sublayer having a majority of organic materials and a minority of inorganic materials; and
a third sublayer having a majority of inorganic materials and a minority of organic materials.
4. The method of claim 3 , wherein the first sublayer is formed by providing an oxygen-containing gas to the HMDSO gas at a flow ratio of about 10 or greater.
5. The method of claim 3 , wherein the second sublayer is formed by providing the oxygen-containing gas to the HMDSO gas at a flow ratio of less than about 2.
6. The method of claim 3 , wherein the third sublayer is formed by providing the oxygen-containing gas to the HMDSO gas at a flow ratio of about 10 or greater.
7. The method of claim 1 , wherein the first layer is an inorganic layer.
8. The method of claim 1 , wherein the third layer is an inorganic layer.
9. A method for forming an encapsulating structure on an organic light emitting diode (OLED) substrate, comprising:
forming a hybrid layer over a region of a substrate having an OLED structure disposed thereon, the region being defined by a mask, wherein the hybrid layer is formed by supplying a processing gas comprising a HMDSO (hexamethyldisiloxane) gas throughout the formation of the hybrid layer, and the hybrid layer comprises:
a first sublayer having a majority of inorganic materials and a minority of organic materials;
a second sublayer having a majority of organic materials and a minority of inorganic materials; and
a third sublayer having a majority of inorganic materials and a minority of organic materials.
10. The method of claim 9 , further comprising:
before forming the hybrid layer, forming a first layer on the region defined by the mask.
11. The method of claim 10 , further comprising:
forming a second layer on the hybrid layer on the region defined by the mask.
12. The method of claim 10 , wherein the first layer is an inorganic layer.
13. The method of claim 11 , wherein the second layer is an inorganic layer.
14. The method of claim 11 , wherein the first layer, the hybrid layer and the second layer are formed in the same chamber.
15. The method of claim 9 , wherein the first sublayer is formed by providing an oxygen-containing gas to the HMDSO gas at a flow ratio of about 10 or greater.
16. The method of claim 9 , wherein the second sublayer is formed by providing the oxygen-containing gas to the HMDSO gas at a flow ratio of less than about 2.
17. The method of claim 9 , wherein the third sublayer is formed by providing the oxygen-containing gas to the HMDSO gas at a flow ratio of about 10 or greater.
18. A method for forming an encapsulating structure on an organic light emitting diode (OLED) substrate, comprising:
forming a first layer on a region of a substrate having an OLED structure disposed thereon in a processing chamber, the region being defined by a mask;
forming a second layer on the first layer in the region defined by the mask in the processing chamber; and
forming a third layer on the second layer in the region defined by the mask in the processing chamber.
19. The method of claim 18 , wherein the second layer is formed by supplying a processing gas comprising a HMDSO (hexamethyldisiloxane).
20. The method of claim 18 , wherein the second layer comprises:
a first sublayer having a majority of inorganic materials and a minority of organic materials;
a second sublayer having a majority of organic materials and a minority of inorganic materials; and
a third sublayer having a majority of inorganic materials and a minority of organic materials.