US20140287551A1 - Thermal pre-treatment process for soda lime glass substrate for thin film photovoltaic materials - Google Patents

Thermal pre-treatment process for soda lime glass substrate for thin film photovoltaic materials Download PDF

Info

Publication number
US20140287551A1
US20140287551A1 US14/295,107 US201414295107A US2014287551A1 US 20140287551 A1 US20140287551 A1 US 20140287551A1 US 201414295107 A US201414295107 A US 201414295107A US 2014287551 A1 US2014287551 A1 US 2014287551A1
Authority
US
United States
Prior art keywords
treatment process
layer
thermal treatment
lime glass
soda lime
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/295,107
Inventor
Robert D. Wieting
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CM Manufacturing Inc
Original Assignee
CM Manufacturing Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CM Manufacturing Inc filed Critical CM Manufacturing Inc
Priority to US14/295,107 priority Critical patent/US20140287551A1/en
Publication of US20140287551A1 publication Critical patent/US20140287551A1/en
Abandoned legal-status Critical Current

Abstract

A method for fabricating a thin film solar cell includes providing a soda lime glass substrate comprising a surface region, treating the surface region with one or more cleaning process including an aqueous solution to remove one or more contaminants and/or particulates, and forming a lower electrode layer overlying the surface region. The method also includes performing a thermal treatment process to remove any residual water species to substantially less than a monolayer of water species from the lower electrode layer and soda lime glass substrate. The thermal treatment process changes a temperature of the soda lime glass substrate from a first temperature to a second temperature to pre-heat the soda lime glass substrate. Additionally, the method includes transferring the soda lime glass substrate, which has been preheated, to a deposition chamber and forming a layer of photovoltaic material overlying the lower electrode layer within the deposition chamber.

Description

    CROSS-REFERENCES TO RELATED APPLICATIONS
  • This application is a continuation of and claims priority to application Ser. No. 12/569,368, filed Sep. 29, 2009, and U.S. Provisional Patent Application No. 61/101,989 filed Oct. 1, 2008, commonly assigned, both of which are herein incorporated by reference in their entirety for all purposes.
  • BACKGROUND OF THE INVENTION
  • The present invention relates generally to photovoltaic materials and manufacturing method. More particularly, the present invention provides a method and structure for fabricating a thin film solar cells on soda lime glass substrate. Merely by way of example, the present method includes a thermal treatment process of the soda lime glass substrate for manufacture of thin film photovoltaic devices, but it would be recognized that the invention may have other configurations.
  • From the beginning of time, mankind has been challenged to find way of harnessing energy. Energy comes in the forms such as petrochemical, hydroelectric, nuclear, wind, biomass, solar, and more primitive forms such as wood and coal. Over the past century, modern civilization has relied upon petrochemical energy as an important energy source. Petrochemical energy includes gas and oil. Gas includes lighter forms such as butane and propane, commonly used to heat homes and serve as fuel for cooking Gas also includes gasoline, diesel, and jet fuel, commonly used for transportation purposes. Heavier forms of petrochemicals can also be used to heat homes in some places. Unfortunately, the supply of petrochemical fuel is limited and essentially fixed based upon the amount available on the planet Earth. Additionally, as more people use petroleum products in growing amounts, it is rapidly becoming a scarce resource, which will eventually become depleted over time.
  • More recently, environmentally clean and renewable sources of energy have been desired. An example of a clean source of energy is hydroelectric power. Hydroelectric power is derived from electric generators driven by the flow of water produced by dams such as the Hoover Dam in Nevada. The electric power generated is used to power a large portion of the city of Los Angeles in California. Clean and renewable sources of energy also include wind, waves, biomass, and the like. That is, windmills convert wind energy into more useful forms of energy such as electricity. Still other types of clean energy include solar energy. Specific details of solar energy can be found throughout the present background and more particularly below.
  • Solar energy technology generally converts electromagnetic radiation from the sun to other useful forms of energy. These other forms of energy include thermal energy and electrical power. For electrical power applications, solar cells are often used. Although solar energy is environmentally clean and has been successful to a point, many limitations remain to be resolved before it becomes widely used throughout the world. As an example, one type of solar cell uses crystalline materials, which are derived from semiconductor material ingots. These crystalline materials can be used to fabricate optoelectronic devices that include photovoltaic and photodiode devices that convert electromagnetic radiation into electrical power. However, crystalline materials are often costly and difficult to make on a large scale. Additionally, devices made from such crystalline materials often have low energy conversion efficiencies. Other types of solar cells use “thin film” technology to form a thin film of photosensitive material to be used to convert electromagnetic radiation into electrical power. Similar limitations exist with the use of thin film technology in making solar cells. That is, efficiencies are often poor. Additionally, film reliability is often poor and cannot be used for extensive periods of time in conventional environmental applications. Often, thin films are difficult to mechanically integrate with each other. Furthermore, processing to integrate sodium containing glass substrates including overlying electrode layers with the subsequently formed photovoltaic layer is problematic, especially for large scale manufacture. These and other limitations of these conventional technologies can be found throughout the present specification and more particularly below.
  • BRIEF SUMMARY OF THE INVENTION
  • The present invention relates generally to photovoltaic materials and manufacturing method. More particularly, the present invention provides a method and structure for fabricating a thin film solar cells on soda lime glass substrate. Merely by way of example, the present method includes a thermal treatment process of the soda lime glass substrate for manufacture of thin film photovoltaic devices, but it would be recognized that the invention may have other configurations.
  • In a specific embodiment, the present invention provides a method for fabricating a thin film solar cell. The method includes providing a soda lime glass substrate comprising a surface region and treating the surface region with one or more cleaning process including an aqueous solution to remove one or more contaminants and/or particulates. The method further includes forming a lower electrode layer comprising molybdenum overlying the surface region. Additionally, the method includes performing a thermal treatment process on the soda lime glass substrate comprising the lower electrode layer to remove any residual water species such that there is substantially less than a monolayer of water species on the soda lime glass substrate and the overlying lower electrode layer. The thermal treatment process changes a temperature of the soda lime glass substrate from a first temperature to a second temperature to pre-heat the soda lime glass substrate comprising the lower electrode layer and maintains the second temperature less than about 90 Degrees Celsius. The method further includes transferring the soda lime glass substrate, which has been preheated, to a deposition chamber. Furthermore, the method includes forming a layer of photovoltaic material overlying the lower electrode layer within the deposition chamber. Moreover, the method includes forming a first zinc oxide layer overlying the layer of photovoltaic material.
  • In another specific embodiment, the present invention provides a method for fabricating a thin film solar cell. The method includes providing a soda lime glass substrate comprising a surface region and treating the surface region with one or more cleaning process including an aqueous solution to remove one or more contaminants and/or particulates. The method further includes forming a lower electrode layer comprising molybdenum overlying the surface region. Additionally, the method includes performing a thermal treatment process to reduce any residual water species to substantially less than a monolayer of water species overlying the lower electrode layer after the thermal treatment process. The thermal treatment process changes a temperature of the soda lime glass substrate from a first temperature to a second temperature to pre-heat the soda lime glass substrate comprising the lower electrode layer. Furthermore, the method includes transferring the soda lime glass substrate, which has been preheated, to a deposition chamber. Moreover, the method includes forming a layer of photovoltaic material overlying the lower electrode layer within the deposition chamber.
  • Many benefits can be achieved by applying the embodiments of the present invention. Particularly, a thermal treatment process serves an important step for preparing a soda lime glass substrate for growing copper based chalcopyrite structured high efficiency photovoltaic absorber layer. The present invention provides an efficient way using a plurality of in-chamber disposed infrared heaters to directly heat the work piece including the soda lime glass substrate and an overlying patterned lower electrode layer. The method simplifies the system design can be easily implemented into a batch system for large scale manufacture with reduced cost. Of course, there can be other variations, modifications, and alternatives.
  • These and other benefits may be described throughout the present specification and more particularly below.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1 is a simplified flowchart illustrating a method of fabricating a thin film solar cell according to an embodiment of the present invention;
  • FIGS. 2-10 are schematic diagrams illustrating a method comprising a series of processes and structures for fabricating a thin film solar cell according to certain embodiments of the present invention.
  • DETAILED DESCRIPTION OF THE INVENTION
  • The present invention relates generally to photovoltaic materials and manufacturing method. More particularly, the present invention provides a method and structure for fabricating a thin film solar cells on soda lime glass substrate. Merely by way of example, the present method includes a thermal treatment process of the soda lime glass substrate for manufacture of thin film photovoltaic devices, but it would be recognized that the invention may have other configurations.
  • FIG. 1 is a simplified flowchart illustrating a method of fabricating a thin film solar cell according to an embodiment of the present invention. This diagram is merely an example, which should not unduly limit the scope of the claims herein. The method 1000 includes the following processes:
  • 1. Process 1010 for providing a soda lime glass substrate with a surface region;
  • 2. Process 1020 for treating the surface region;
  • 3. Process 1030 for forming a lower electrode layer overlying the surface region;
  • 4. Process 1040 for performing a thermal treatment process on the soda lime glass substrate comprising the lower electrode layer;
  • 5. Process 1050 for forming a layer of photovoltaic material overlying the lower electrode layer;
  • 6. Process 1060 for forming a first zinc oxide layer overlying the layer of photovoltaic material;
  • 7. Process 1070 for performing other steps.
  • The above sequence of processes provides a method of treating the soda lime glass substrate for manufacture of thin film solar cells according to an embodiment of the present invention. In a specific embodiment, the method includes performing a surface treatment and one or more thermal treatment processes on the soda lime glass substrate. Other alternatives can also be provided where processes are added, one or more processes are removed, or one or more processes are provided in a different sequence without departing from the scope of the claims herein. For example, a barrier layer may be formed before the lower electrode layer is formed. More functional layers with different material compositions can be inserted between the layer of photovoltaic material and first zinc oxide layer, and so on. Further details of the method can be found throughout the present specification and more particularly below.
  • At Process 1010, a soda lime glass substrate is provided. This process can be visually illustrated by FIG. 2. FIG. 2 is a simplified diagram illustrating a soda lime glass substrate provided for fabricating a thin film photovoltaic cell according to an embodiment of the present invention. This diagram is merely an example, which should not unduly limit the scope of the claims herein. One of ordinary skill in the art would recognize many variations, alternatives, and modifications. As shown, the soda lime glass substrate 100 including a surface region 101 is provided. The soda lime glass has been widely used as window glass. One important reason for choosing the soda lime glass as substrate for forming thin film photovoltaic cells other than simple economical concern is a positive influence from alkaline ions (e.g., Na+) contained therein on the grain growth of high efficiency thin film photovoltaic materials. For example, polycrystalline chalcopyrite semiconductor films of CuIn(Ga)Se2 or CuInSe2 materials can be formed on soda lime glass substrates with coarse grain sizes of 1 microns or larger so that high photovoltaic current can be collected to achieve high efficiencies of near 17% or above with these chalcopyrite films.
  • At Process 1020, the method 1000 includes a surface treatment process for treating the surface region of the soda lime glass substrate. As shown in FIG. 3, the surface region 101 of the soda lime glass substrate 100 is subjected to the treatment process 150. In one embodiment, the treatment process 150 is a washing process carried out by rinsing with an aqueous solution or directly soaking into it. For example, the aqueous solution can be a water based solution of about 0.15% of acid containing potassium dichromate, sulfuric acid, or even less amount of hydrochloric acid with controlled PH-value. The soda lime glass substrates were left then for 20 minutes under ultrasonic duty in isopropyl alcohol, then washed in deionized water, and finally dried by blowing with dry air or dry nitrogen. The surface treatment process substantially cleans the surface region 101 by removing one or more surface contaminants, greases, dirts, or particulates, and others.
  • At Process 1030, a lower electrode layer is formed overlying the surface region of the soda lime glass substrate. This process can be visually illustrated by FIG. 4, as shown, the lower electrode layer 200 is formed overlying the surface region 101 of the soda lime glass substrate 100. The lower electrode layer 200 is used to serve a back electrode for a thin film photovoltaic cell to be formed in subsequent processes. Here “lower” is merely a word for current example of forming a thin film on substrate, the thin film is to become a bottom solar cell. “Lower” electrode may correspond to an “upper” or “front” electrode that is located on top of a window layer. As shown in FIG. 4, the lower electrode layer 200 is formed on the surface region 101 which is displayed as an front side of the soda lime glass substrate 100 while the backside 102 is still an blank surface. When the soda lime glass substrate 100 is used as “superstrate” in an application of forming a top solar cell, the lower or upper electrodes can be disposed in opposite way. In certain cases when no confusion, only electrode layer is mentioned. In particular, either the lower or upper electrode layer can be optically transparent. For example, the lower electrode layer is made of molybdenum material with thickness ranging from 0.5 to 1 microns. In other examples, transparent conductive oxide can be used as the material for upper electrode layer.
  • In an implementation, the formation of the lower electrode layer can be achieved using a series of processes within a large scale batch system. The series of processes at least include one or more deposition processes, such as sputtering, plating, evaporation, plasma deposition, and the like. For example, an AC sputtering technique is used to deposit a bi-layer molybdenum materials respectively with different stress characteristics formed at different chamber pressures. More details can be found in U.S. Patent Application No. 61/101,646, commonly assigned to Stion Corporation and fully incorporated by reference herein. Additionally, the series of processes also include a patterning process. One option is to use laser patterning in which a laser beam with well controlled beam energy, pulse rate, and beam profile is utilized to ablate molybdenum layer to make one or more patterns. Shown as an example, the lower electrode layer 200 includes a pattern 205 is formed overlying the soda lime glass substrate 100. As a result, an work piece 210 including the patterned lower electrode layer 200 overlying the soda lime glass substrate 100 is formed. Furthermore, the series of processes may include a cleaning process to remove certain berm structures or other particulates generated during the patterning process. The cleaning process may involve a use of one or more mechanical brush devices and use DI water to rinse the whole soda lime glass substrate 100 including the patterned lower electrode layer 200, followed by air knife blowing. More details about the patterning process and subsequent cleaning process can be found in U.S. Patent Application No. 61/101,650, commonly assigned to Stion Corporation and fully incorporated by reference herein.
  • In the next process (referring FIG. 1), the method 1000 includes performing a thermal treatment process 1040 on the work piece, e.g., the soda lime glass substrate comprising the lower electrode layer. This process is intended for preparing the work piece for subsequent thin film growth processes on the soda lime glass substrate. This process can be visually illustrated by FIG. 5. FIG. 5 is a simplified diagram illustrating a thermal treatment process according to an embodiment of the present invention. This diagram is merely an example, which should not unduly limit the scope of the claims herein. One of ordinary skill in the art would recognize many variations, alternatives, and modifications. As shown, a work piece 210 is transferred out of cleaning station 2010 and into a thermal treatment station 2020. In an example, the work piece 210 with its backside 102 seating over a plurality of rollers 230 is rolled into the thermal treatment station 2020. The rollers 230 are configured to move the work piece back and forth as desired during the thermal treatment process 1040. Additionally, a plurality of heaters 240 can be disposed near the work piece 210 seated over the rollers 230. In one example shown in FIG. 5, the plurality of heaters 240 are positioned to provide heat to the work piece 210 from the backside 102. Of course, there can be many variations, alternatives, and modifications.
  • In an implementation, each of the plurality of heaters 240 is an infrared heater that is easy to control and adjust power through an electric supply. For example, each infrared heater can heat nearby air to about 170 degrees Celsius, causing a temperature of the soda lime glass substrate above to change from a first temperature (initially near room temperature) to a second temperature. As one main reason of the thermal treatment process 1040 is to remove any water species sticking on the work piece 210, the soda lime glass substrate is pre-heated or sequentially heated to a temperature that is controlled to be less than 90 degrees Celsius. Depending on applications, in particular, with different placement of the heaters 240 relative to the work piece 210, the electric supply can be adjust to produce suitable heat supply towards to soda lime glass substrate for a proper time period. In one example, the plurality of infrared heaters 240 are adjusted to maintain a desired temperature (less than 90 degree Celsius) of the soda lime glass substrate for 250 seconds. In another example, the plurality of infrared heaters 240 are adjusted to maintain a desired temperature (less than 90 degree Celsius) of the soda lime glass substrate for 200 seconds. In yet another example, the plurality of infrared heaters 240 are adjusted to maintain a desired temperature (less than 90 degree Celsius) of the soda lime glass substrate for 60 seconds.
  • In particular for the configuration shown in FIG. 5, the thermal treatment process 1040 is aimed to substantially remove water species overlying both the surface 201 of the lower electrode layer 200 and the backside 102 of the soda lime glass substrate 100. For example, the work piece 210 should be first preheated for a period of time to allow the temperature being raised to about a desired value (less than 90 degrees Celsius) and then the heating is continued for another period of time, as described in previous paragraph. In another example, during the preheating and/or continuous heating period, the work piece 210 can be moved back and forth by controlling the rollers 230, allowing more uniform heating through the whole area of the work piece 210. In an embodiment, the thermal treatment process 1040 as described results in dissolving water species from any exposed surface of the work piece 210. In particular within a proper heating period, any water species should be removed from the surface 201 of the lower electrode layer 200 and the backside 102 of the soda lime glass substrate. Embodiments of the invention show that the thermal treatment process results in a substantially less than a monolayer of water species overlying the lower electrode layer. Furthermore, the mentioned any exposed surface of the work piece 210 should include region of pattern 205 or regions of glass side edges. Followed by the thermal treatment process, the prepared work piece 210, characterized by substantially less than a monolayer of water species overlying a patterned lower electrode layer on soda lime glass substrate, can be further transferred to a deposition chamber 2030 (as shown in FIG. 5).
  • Referring to FIG. 1, the method 1000 includes a next process 1050 of forming a layer of photovoltaic material overlying the lower electrode layer. This process can be visually illustrated by FIG. 6, which is a schematic diagram showing a layer of photovoltaic material formed overlying the lower electrode layer according to an embodiment of the present invention. This diagram is merely an example, which should not unduly limit the scope of the claims herein. One of ordinary skill in the art would recognize many variations, alternatives, and modifications. As shown, a layer of photovoltaic material 300 is formed overlying the lower electrode layer 200. In a specific embodiment, the process 1050 includes at least one or more deposition processes and one or more additional thermal treatment processes. In an example, the one or more depositing processes include forming one or more precursor layers using one or more sputtering processes. For example, the one or more precursor layers include copper, indium, gallium species and may further include sodium species. In an implementation, the one or more sputtering processes are performed within the deposition chamber 2030. In another implementation, the one or more sputtering processes are carried out in different compartments of the chamber 2030. Furthermore, process 1050 would include performing one or more additional thermal treatment processes to transform the precursor layers into the layer of photovoltaic material 300. These additional thermal treatment processes may include a selenization process or sulfidazation process involving one or more chemical reactions, annealing, and/or diffusions. More details about the formation of one or more copper species based precursor layers and subsequently transformation into a polycrystalline coarse grained CIGS chalcopyrite photovoltaic absorber can be found in U.S. Patent Application No. 61/101,638, commonly assigned to Stion Corporation and fully incorporated by reference herein.
  • In an example shown in FIG. 6, the layer of photovoltaic material 300 has formed overlying the surface 201 of the lower electrode layer 200 with an embedded interconnect structure 206 located at the pattern 205 formed previously. In another specific embodiment, the layer of photovoltaic material 300 comprises a copper indium gallium diselenide material, or copper indium (gallium) disulfide material with coarse grain chalcopyrite structure including a certain amount of sodium doping concentration. Large grain sizes as large as a few microns are obtained with CIGS chalcopyrite structure accord to embodiments of the present invention to form the layer of photovoltaic. Therefore, high photo current can be expected and subsequently high efficiency is expected for the CIGS based thin film solar cells formed thereafter. Although the above has been generally described in terms of a specific structure for CIS and/or CIGS thin film solar cells, other specific CIS and/or CIGS configurations can also be used, such as those noted in U.S. Pat. No. 4,612,411 and U.S. Pat. No. 4,611,091, which are hereby incorporated by reference herein, without departing from the invention described by the claims herein.
  • Referring to FIG. 1 again, the method 1000 further includes a process (1060) of forming an upper electrode layer over the layer of photovoltaic material. This process can be visually illustrated by FIG. 7, which is a schematic diagram showing a process of for fabricating a thin film solar cell according to an embodiment of the present invention. This diagram is merely an example, which should not unduly limit the scope of the claims herein. One of ordinary skill in the art would recognize many variations, alternatives, and modifications. As shown, the upper electrode layer 400 is a first zinc oxide layer which is a kind of transparent conductive oxide or TCO. In a specific embodiment, the upper electrode layer 400 can be a zinc oxide layer formed using a metalorganic chemical vapor deposition (MOCVD) technique within a batch system. The formed first zinc oxide layer by MOCVD is a rough layer, which can diffuse the incoming light by scattering, increasing the efficiency of solar cells.
  • The method 1000 then can include a process 1070 for any additional step of fabricating a thin film photovoltaic device. For example, the process 1070 can be a process of inserting one more layers with various suitable materials between those layers formed in above processes. The process 1070 can also be a laser or mechanical patterning process for making one or more patterns within the lower or upper electrode layers. The one or more patterns can be filled with materials that have suitable optical and electrical properties for making interconnect structures of the thin film solar cells thereof. Of course, there can be many variations, alternatives, and modifications.
  • In an alternative embodiment, the method 1000 may include a process of forming a barrier layer directly onto the surface region after a treatment process 1020 of the soda lime glass substrate and before the process 1030 for forming a lower electrode layer. FIG. 8 shows such a process of fabricating a thin film photovoltaic cell on soda lime glass substrate according to an alternative embodiment of the present invention. This diagram is merely an example, which should not unduly limit the scope of the claims herein. One of ordinary skill in the art would recognize many variations, alternatives, and modifications. As shown, a barrier layer 120 is inserted between the lower electrode layer 200 and the surface region 101 of the soda lime glass substrate 100. Because excessive, uncontrolled amount of sodium may reduce the grain sizes of the photovoltaic thin film grown on the soda lime glass substrate, the barrier layer 120 is applied for preventing sodium element from diffusing into the upper layers especially the layer of photovoltaic material. In one embodiment, the barrier layer 120 is a layer of silicon dioxide formed by a sputtering process, which serves as an effective sodium diffusion barrier with a thickness of only about 500 Angstroms or less. Other materials including aluminum oxide, silicon nitride, titanium nitride, titanium oxide, or zirconium oxide also can be used depending on applications.
  • In another alternative embodiment, the method 1000 can include a process of forming a cadmium sulfide layer overlying the layer of photovoltaic material before forming the first zinc oxide layer. In particular, as shown in FIG. 9 the layer of photovoltaic material 300 is a layer of copper indium diselenide material overlying the lower electrode molybdenum layer 200. The cadmium sulfide layer 305, characterized as a wide bandgap semiconductor, is formed over the layer of copper indium diselenide material 300 to serve as a window layer for the thin film solar cell while the layer of copper indium diselenide material 300 acting as an absorber layer. In certain embodiments, the cadmium sulfide layer 305 is considered as one part of the layer of photovoltaic material which is formed using a multilayer deposition and treatment process. In one example, the cadmium sulfide layer 305 can be formed using sputtering, vacuum evaporation, or chemical bath deposition (CBD) techniques and doped with n+-type impurities for conductivity. Depending on embodiments, the window layer 305 can be selected from a group materials consisting of a cadmium sulfide (CdS), a zinc sulfide (ZnS), zinc selenium (ZnSe), zinc oxide (ZnO), zinc magnesium oxide (ZnMgO), or others.
  • In yet another alternative embodiment, the method 1000 can include a process of forming a second zinc oxide layer before forming the first zinc oxide layer. As shown in FIG. 10 the second zinc oxide layer 405 is first formed over the layer of photovoltaic material, or in particular over the cadmium sulfide layer 305, and the first zinc oxide layer 400 is formed over the second oxide layer 405. The layer of photovoltaic material 300 is a layer of copper indium diselenide material overlying the lower electrode molybdenum layer 200. In a specific embodiment, the second zinc oxide layer 405 has a higher resistivity than the first zinc oxide layer 400. Functionally, the second zinc oxide layer 405 plays more a role of barrier/protection layer while the first zinc oxide layer 400 with lower resisitivity plays more a role of conductive electrode layer. In certain embodiment, the second zinc oxide layer 405 is also formed using a metalorganic chemical vapor deposition (MOCVD) technique within a batch system.
  • Although the above has been illustrated according to specific embodiments, there can be other modifications, alternatives, and variations. It is understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims.

Claims (20)

What is claimed is:
1. A method for fabricating a thin film solar cell, the method comprising:
treating a surface region of a substrate with an aqueous;
subsequently forming a lower electrode layer including a conductive metal over the surface region;
performing a thermal treatment process on the substrate and the lower electrode layer to remove residual water species; and
forming a layer of photovoltaic material overlying the lower electrode layer.
2. The method of claim 1 wherein performing the thermal treatment process comprises thermally desorbing residual water species.
3. The method of claim 1 wherein performing the thermal treatment process comprises subjecting a plurality of infrared heaters from a backside of the substrate.
4. The method of claim 3 wherein the thermal treatment process comprises heating the substrate with the infrared heaters for less than about 250 seconds.
5. The method of claim 3 wherein the thermal treatment process comprises heating the substrate with the infrared heaters for less than about 60 seconds.
6. The method of claim 3 wherein the thermal treatment process comprises rolling the soda lime glass substrate back and forth over the plurality of infrared heaters.
7. The method of claim 1 wherein the thermal treatment process heats the substrate from a first temperature to a second temperature less than or about 170 degrees Celsius.
8. The method of claim 1 wherein the layer of photovoltaic material comprises one or more precursor layers of an absorber material.
9. The method of claim 8 wherein the one or more precursor layers comprises at least a copper layer and/or an indium layer.
10. The method of claim 1 further comprising forming a barrier layer overlying the surface region before forming the lower electrode layer.
11. The method of claim 10 wherein the barrier layer comprises a silicon dioxide layer of about 500 Angstroms or less for keeping sodium species within the soda lime glass substrate during the thermal treatment process.
12. A method for fabricating a thin film solar cell, the method comprising:
treating a surface of a substrate with an acidic solution;
forming a layer of a conductive metal directly over the surface region;
performing a thermal treatment process on the substrate having the layer of conductive material, the thermal treatment process changing a temperature of the soda lime glass substrate from a first temperature to a second temperature;
transferring the preheated substrate to a deposition chamber; and
forming a layer of photovoltaic material overlying the lower electrode layer within the deposition chamber.
13. The method of claim 12 wherein performing the thermal treatment process comprises thermally desorbing residual water species.
14. The method of claim 12 wherein performing the thermal treatment process comprises subjecting a plurality of infrared heaters from a backside of the substrate.
15. The method of claim 14 wherein the thermal treatment process comprises rolling the soda lime glass substrate back and forth over the plurality of infrared heaters.
16. The method of claim 14 wherein the thermal treatment process comprises heating the substrate with the infrared heaters for less than about 250 seconds.
17. The method of claim 14 wherein the thermal treatment process comprises heating the substrate with the infrared heaters for less than about 60 seconds.
18. The method of claim 12 wherein the thermal treatment process heats the substrate from a first temperature to a second temperature less than or about 170 degrees Celsius.
19. The method of claim 12 wherein the layer of photovoltaic material comprises one or more precursor layers of an absorber material.
20. The method of claim 19 wherein the one or more precursor layers comprises at least a copper layer and/or an indium layer.
US14/295,107 2008-10-01 2014-06-03 Thermal pre-treatment process for soda lime glass substrate for thin film photovoltaic materials Abandoned US20140287551A1 (en)