US20140111924A1 - Sol-gel and mask patterning for thin-film capacitor fabrication, thin-film capacitors fabricated thereby, and systems containing same - Google Patents
Sol-gel and mask patterning for thin-film capacitor fabrication, thin-film capacitors fabricated thereby, and systems containing same Download PDFInfo
- Publication number
- US20140111924A1 US20140111924A1 US14/142,709 US201314142709A US2014111924A1 US 20140111924 A1 US20140111924 A1 US 20140111924A1 US 201314142709 A US201314142709 A US 201314142709A US 2014111924 A1 US2014111924 A1 US 2014111924A1
- Authority
- US
- United States
- Prior art keywords
- tfc
- thin
- electrode
- dielectric
- film capacitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A process of forming a thin-film capacitor that includes sol-gel patterning of a dielectric thin film on a first electrode, lift-off removal of unwanted dielectric thin film, and mating the dielectric thin film with a second electrode. The thin-film capacitor exhibits a substantially uniform heat-altered morphology along a line defined by a characteristic dimension thereof. A computing system is also disclosed that includes the thin-film capacitor.
Description
- Disclosed embodiments relate to a plate capacitor assembly.
- A processor die often requires capacitative power sources to respond to transient loads generated during operation. Capacitors are provided to answer the transient load requirements of the die. A thin-film capacitor (TFC) is typically a dielectric disposed between two electrodes, and which was manufactured by laser drilling. Laser drilling is costly, time consuming, and subjects the structures of the TFC to significant uneven heat transients. High dielectric-constant (high-k) thin-film capacitors (TFCs) must be laser drilled or chemically etched after sintering to provide electrical contacts. These processes can affect the chemistry of the sintered high-k dielectrics. The laser drilling can create a non-uniform laser heat zone, or the etching chemistry can alter the high-k dielectric at and near the etch edge.
- During conventional laser-drill processing through a sintered thin-film capacitor (TFC) dielectric layer to form a contact corridor, the extreme heat transient of the laser beam causes a heat-altered region at the cutting edge of the laser drill. The laser-drilled edge is subjected to an extreme heat transient because of the laser-drilling process, but opposite from the cut edge, the sintered TFC dielectric can remain unchanged from the sintering process. The conventional laser-drill process can cause the laser-drilled edge to change physically or chemically compared to the region that is distant from the laser-drilled edge. For example the laser-drilled edge can embrittle in comparison to the region that is distant from the laser-drilled edge. Thus, the heat-altered morphology of the laser-drilled edge can exhibit embrittlement signs caused in a sintered dielectric. The embrittlement can be determined by physical probing among other techniques. The laser-drilled edge can also have changed chemical qualities due to lost or altered materials caused by the extreme heat transient. Thus, the heat-altered morphology of the laser-drilled edge can exhibit chemical depletion signs in a sintered dielectric. The changed chemical qualities can be determined by microscopic techniques such as by scanning electron microscopy (SEM) or ionic-coupled plasma (ICP) analysis. And due to the extreme heat transient of the laser-drilling process, the laser-drilled edge can even have incorporated volatilized stray materials into the matrix of the TFC dielectric in comparison to the distant region. Thus, the heat-altered morphology of the laser-drilled edge can exhibit chemical addition signs in a sintered dielectric. The changed chemical qualities can be determined by microscopic techniques such as by SEM or ICP analysis.
- In order to understand the manner in which embodiments are obtained, a more particular description of various embodiments briefly described above will be rendered by reference to the appended drawings. Understanding that these drawings depict only typical embodiments that are not necessarily drawn to scale and are not therefore to be considered to be limiting of its scope, some embodiments will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:
-
FIG. 1A is a cross-section elevation of a thin-film capacitor assembly during processing according to an embodiment; -
FIG. 1B is a cross-section elevation of the thin-film capacitor assembly depicted inFIG. 1A during processing according to an embodiment; -
FIG. 1C is a cross-section elevation of the thin-film capacitor assembly depicted inFIG. 1B during processing according to an embodiment; -
FIG. 1D is a cross-section elevation of the thin-film capacitor assembly depicted inFIG. 1C during processing according to an embodiment; -
FIG. 2 is a top plan with a cut section of a thin-film capacitor assembly that has been processed according to an embodiment; -
FIG. 3 is an cross-section elevation of a package that includes a thin-film capacitor assembly that was formed according to an embodiment; -
FIG. 4 is a process flow diagram according to various embodiments; -
FIG. 5 is a cut-away perspective that depicts a computing system according to an embodiment; and -
FIG. 6 is a schematic of an electronic system according to an embodiment. - The following description includes terms, such as upper, lower, first, second, etc., that are used for descriptive purposes only and are not to be construed as limiting. The embodiments of a device or article described herein can be manufactured, used, or shipped in a number of positions and orientations. The terms “die” and “chip” generally refer to the physical object that is the basic workpiece that is transformed by various process operations into the desired integrated circuit device. A die is usually singulated from a wafer, and wafers may be made of semiconducting, non-semiconducting, or combinations of semiconducting and non-semiconducting materials. A board is typically a resin-impregnated fiberglass structure that acts as a mounting substrate for the die.
- Reference will now be made to the drawings wherein like structures will be provided with like reference designations. In order to show the structure and process embodiments most clearly, the drawings included herein are diagrammatic representations of embodiments. Thus, the actual appearance of the fabricated structures, for example in a photomicrograph, may appear different while still incorporating the essential structures of embodiments. Moreover, the drawings show only the structures necessary to understand the embodiments. Additional structures known in the art have not been included to maintain the clarity of the drawings.
-
FIG. 1A is a cross-section elevation of a thin-film capacitor (TFC)assembly 100 during processing according to an embodiment. TheTFC assembly 100 at this processing instant includes afirst electrode 110 with anupper surface 112 and alower surface 114. Amask 116 is patterned above thefirst electrode 110 upon theupper surface 112. In an embodiment, themask 116 is susceptible to swelling and peeling during processing. In an embodiment, themask 116 is liquid soluble such that a lift-off process is useful to remove it. In an embodiment, themask 116 is vapor swellable such that a lift-off process is useful to remove it. -
FIG. 1B is a cross-section elevation of the thin-film capacitor assembly depicted inFIG. 1A after further processing according to an embodiment. The TFCassembly 101 exhibits a greendielectric film 118 that is disposed upon theupper surface 112 of thefirst electrode 110 as well as upon themask 116. In an embodiment, the greendielectric film 118 is a ceramicpowder suspension film 116 that is resting upon theupper surface 112. - In an embodiment, the
mask 116 includes afirst thickness 120 and the greendielectric film 118 includes asecond thickness 122. In an embodiment, thefirst thickness 120 is greater than thesecond thickness 122. In this embodiment because the maskfirst thickness 120 is greater than the green dielectric filmsecond thickness 122, themask 116 shows an exposedflank 124 that is susceptible to liquid or vapor insurgency for lift-off processing. In an embodiment, thefirst thickness 120 is about the same as thesecond thickness 122. - In an embodiment, the
green dielectric film 118 includes a sol-gel solution of a titanate compound. In an embodiment, thegreen dielectric film 118 includes a sol-gel solution of a barium titanate compound. In an embodiment, thegreen dielectric film 118 includes a sol-gel solution of a strontium titanate compound. In an embodiment, thegreen dielectric film 118 includes a sol-gel solution of a barium-strontium titanate (BST) compound as a principal presence. “Principal presence” may mean thegreen dielectric film 118 will include about 100% of the titanate ceramic after sintering. It may also mean thegreen dielectric film 118 in a majority of BST. It may also mean thegreen dielectric film 118 is the dielectric material is less than 50%, but is the most prevalent dielectric material, from about 34% BST to about 49% BST if at least two other dielectrics are present for example. In an embodiment, any other ceramic dielectric is used as thegreen dielectric film 118, which is suitable for use as a TFC dielectric. In an embodiment, the second heating process is properly called annealing instead of sintering. In this embodiment, the first-cureddielectric film 118 is heated such that only fluid loss occurs, and the chemical nature thereof is not materially changed. Because specific applications may use sintering as defined or annealing as defined, for the purposes of disclosed and claimed embodiments, the terms sintering and annealing will be used synonymously. - Preparation of a sol-
gel film 118 according to an embodiment includes blending titanium alkoxide and a strontium inorganic salt with methoxyelthanol and ethylene glycol. In an embodiment, preparation of a sol-gel film 118 according to an embodiment includes blending titanium alkoxide and a barium inorganic salt with methoxyelthanol and ethylene glycol. In an embodiment, preparation of a sol-gel film 118 according to an embodiment includes blending titanium alkoxide with a barium inorganic salt and a strontium inorganic salt, and with methoxyelthanol and ethylene glycol. - In an embodiment, application of the
green dielectric film 118 to thefirst electrode 110 and themask 116 is carried out by orthogonally spraying onto the exposed surfaces. In an embodiment, application thereof is carried out by spinning on a sol-gel liquid. In an embodiment, application thereof is carried out by dipping thefirst electrode 110 into a solution of a dielectric precursor liquid. - In an embodiment, a two-heating process is carried out. It is referred to as first curing, followed by second sintering. More generally, the process embodiment is referred to as first heating, followed by second heating. After application of the
green dielectric film 118 to thefirst electrode 110 and themask 116, a first curing process is carried out to partially stabilize thegreen dielectric film 118. In an embodiment, curing is carried out by heating thegreen dielectric film 118 sufficient to cause it to become non-flowable at room temperature. In an embodiment, thegreen dielectric film 118 has a thickness in a range from about 0.5 micrometer (μm) to about 30 μm. Thus, the non-flowable characteristic of thegreen dielectric film 118 is related to the thickness thereof and the resultant viscosity thereof after the first curing process. - In an embodiment, the first curing is carried out in a temperature range from abut 50° C. to about 150° C. and for sufficient time to cause the
green dielectric film 118 to become non-flowable at room temperature. First curing also allows thegreen dielectric film 118 to become non-flowable at room temperature, but it also retains significant porosity in the first cured stage to allow for easier removal from selected areas. -
FIG. 1C is a cross-section elevation of the thin-film capacitor assembly depicted inFIG. 1B after further processing according to an embodiment. InFIG. 1C , theTFC assembly 102 is illustrated during a lift-off process that is under way. The lift-off process causes the mask 117 (116 inFIG. 1B ) to swell and/or lift. Thegreen dielectric film 118, where it was patterned upon thefirst electrode 110 and not upon themask 117, remains adherent to thefirst electrode 110. Thegreen dielectric film 119 that was patterned upon themask 117 also is in the process of being lifted off by virtue of the peeling and/or swellingmask 117. - After removal of the
green dielectric film 119 that was in contact with themask 117, theTFC assembly 102 is further processed by heating thegreen dielectric film 118 that remains to achieve a sintering thereof. In an embodiment, curing of thegreen dielectric film 118 includes at least some oxidation such that it is referred to as a calcining process. In an embodiment, sintering is carried out in a temperature range from about 700° C. to about 900° C. In order to protect thefirst electrode 110 from oxidation, a non-reactive atmosphere is provided during sintering. In an embodiment, a non-reactive atmosphere includes a non-reactive gas such as argon. In an embodiment, a non-reactive atmosphere includes a non-oxidizing gas such as nitrogen. In an embodiment, a non-reactive atmosphere includes a vacuum. In an embodiment, a non-reactive atmosphere includes a reduced atmospheric pressure such as in the 0.1 atmospheres (atm) range and lower, and a non-reactive gas such as argon. In an embodiment, a non-reactive atmosphere includes a reduced atmospheric pressure such as in the 0.01 atm range and lower, and a non-reactive gas such as argon. - In an embodiment, because of the dimensions of the structures in the TFC assemblies of this disclosure, sintering of the
green dielectric film 118 achieves a substantially uniform heat-altered morphology of what has become a TFC dielectric layer 126 (FIG. 1D ). - One parameter to monitor during sintering is the ratio of internal resistance to heat transfer of the
green dielectric film 118, to the external resistance to heat transfer. The Biot modulus, known in heat-transfer technology, is a measure of the ratio of the internal resistance to the external resistance. In an embodiment, the internal resistance to heat transfer is minimized by evaluation of the Biot modulus in the Z-direction. Heat curing such as sintering therefore imposes a substantially uniform heat load upon thegreen dielectric film 118, such that as the first-cureddielectric film 118 is fully sintered, there exists a substantially uniform heat-altered morphology along any characteristic dimension in any direction, particularly in the X- and Y-directions. The Y-direction is into and out of the plane of the FIG. -
FIG. 1D is a cross-section elevation of the thin-film capacitor assembly depicted inFIG. 1C after further processing according to an embodiment. InFIG. 1D , theTFC assembly 103 is depicted schematically. Asecond electrode 126 has been assembled to theTFC dielectric film 118 and to thefirst electrode 110. TheTFC assembly 103 also includes a lowerdielectric layer 128 and anupper dielectric layer 130, which protect thefirst electrode 110 and thesecond electrode 126, respectively. Further to the structure of theTFC assembly 103 are afirst electrode contact 132 that contacts thefirst electrode 110, and asecond electrode contact 134 that contacts thesecond electrode 126. Thefirst electrode contact 132 and thesecond electrode contact 134 are formed in respective contact corridors that can be formed without extreme heat transients, such as laser drilling because of the process embodiments. The operative capacitor subsection of theTFC assembly 103 can also be referred to as aTFC assembly 136, which includes at least thefirst electrode 110, theTFC dielectric film 118, and thesecond electrode 126. TheTFC assembly 136 is disposed upon asubstrate 138. The respectivefirst electrode contact 132 and thesecond electrode contact 134 are “pinned out” at a respectivefirst bond pad 140 andsecond bond pad 142. In an embodiment, theTFC assembly 136 is provided without thesubstrate 138, and the respectivefirst bond pad 138 andsecond bond pad 142 are integral to the respectivefirst electrode contact 132 and thesecond electrode contact 134. -
FIG. 2 is a top plan with acut section 202, of a thin-film capacitor assembly 200 that has been processed according to an embodiment. The TFC assembly 200 is depicted as being “peeled” to lay open a plan view, and “cut” to expose part of a TFC dielectric layer. The TFC assembly 200 includes afirst electrode 210 and two occurrences of aTFC dielectric film 222. Thefirst electrode 210 also shows a contact-corridor footprint 242 that amounts to aspacing dimension 244 that is depicted between the two occurrences of theTFC dielectric film 222. - A
characteristic dimension 246 of theTFC dielectric film 222 is depicted. Thecharacteristic dimension 246 is selected to be any measuring line that can be laid across theTFC dielectric film 222 at a longest orthogonal configuration. Thecharacteristic dimension 246 inFIG. 2 is depicted as traversing theTFC dielectric film 222 along the X-axis. Because of the thin nature of theTFC dielectric film 222, which thickness is defined along the minor axis, the characteristic dimension is not selected to be in the minor axis. For example inFIG. 2 , the minor axis of theTFC dielectric film 222 is in the Z-direction, which is into and out of the plane of the FIG. - In an embodiment for chip-scale packaging of microelectronic dice, the
characteristic dimension 246 for theTFC dielectric film 222 is in a range from about 100 micrometer (gm) to about 350 μm, and it can be along either of the X- or Y-axes. In an embodiment, thecharacteristic dimension 246 is about 200 μm. - During conventional laser-drill processing through a sintered TFC dielectric layer to form a contact corridor, an
edge region 248 is heat altered in comparison to arear region 250 of theTFC dielectric film 222. Theedge region 248 is subjected to an extreme heat transient because of the laser-drilling process, but therear region 250 has the benefit of both theedge region 248 and thefirst electrode 210 as heat sinks to resist the extreme heat transient. The conventional laser-drill process can cause theedge region 248 morphology to change compared to therear region 250. For example theedge region 248 morphology can embrittle in comparison to therear region 250. Theedge region 248 morphology can also have changed chemical qualities due to lost or altered materials caused by the heat transient. And due to the extreme heat transient of the laser-drilling process, theedge region 248 morphology can even have incorporated volatilized stray materials into the matrix of theedge region 248 in comparison to therear region 250. - According to an embodiment, because of sintering a completed positive pattern, the
TFC dielectric film 222 occurs, and the heat-altered morphology of theTFC dielectric film 222 is substantially uniform along the direction defined by thecharacteristic dimension 246. This substantially uniform heat-altered morphology exhibits a known quality of theTFC dielectric film 222 at any location. Whether it is anedge region 248 or arear region 248 of theTFC dielectric film 222, the heat-altered morphology is substantially uniform. In an embodiment, theTFC dielectric film 222 includes BST as a principal presence. -
FIG. 3 is a cross-section elevation of apackage 300 that includes a thin-film capacitor assembly that was formed according to an embodiment. Thepackage 300 includes adie 352 and a mountingsubstrate 354. Two occurrences of aTFC assembly TFC assembly 334 is disposed laterally to the die 352 and upon the mountingsubstrate 354. In an embodiment, aTFC assembly 335 is disposed below thedie 352 and integral to the mountingsubstrate 354. In an embodiment, thedie 352 is not present, but a die site occupies the same space on the mountingsubstrate 354 that a die can eventually occupy such asdie 352, and theTFC assembly 335 is disposed below the die site and is integral to the mountingsubstrate 354. - The
TFC assembly 334 that is disposed laterally to the die 352 is illustrated in greater detail. TheTFC assembly 334 includes afirst electrode 310 and asecond electrode 324, which enclose aTFC dielectric film 322. In an embodiment, theTFC dielectric film 322 includes a BST powder as a principal presence. TheTFC assembly 334 also includes a lowerdielectric layer 326 and anupper dielectric layer 328, which protect thefirst electrode 310 and thesecond electrode 324, respectively. Further to the structure of theTFC assembly 334 is afirst electrode contact 330 that contacts thefirst electrode 310, and asecond electrode contact 332 that contacts thesecond electrode 324. Thefirst electrode contact 330 and thesecond electrode contact 332 are formed in respective contact corridors that can be formed without extreme heat transients, such as laser drilling because the selected regions were removed before sintering. - The mounting
substrate 354 is coupled to theTFC assembly 334 at a lowerelectrode bond pad 338 and to an upperelectrode bond pad 340. TheTFC assembly 335 that is disposed below thedie 352, and that is also integral to the mountingsubstrate 354, includes a lowerelectrode bond pad 339 and an upperelectrode bond pad 341 that emerge below the mountingsubstrate 354. -
FIG. 4 is a process flow diagram 400 according to various embodiments. - At 410, the process includes patterning a mask upon a first electrode. By way of non-limiting example, the
mask 116 inFIG. 1A is patterned upon thefirst electrode 110. Patterning can be done by spinning on a resist material and exposing the resist in preparation for a removing rinse. - At 420, the process includes forming a green dielectric film over the mask and the first electrode. By way of non-limiting example, the
green dielectric film 118 is sprayed onto themask 116 and onto the exposed portions of thefirst electrode 110 as depicted inFIG. 1B . Thegreen dielectric film 118 is a sol-gel composition that is made from titanium alkoxide, a barium inorganic salt, a strontium inorganic salt, methoxyelthanol, and ethylene glycol. - At 430, the process includes first curing the green dielectric film under conditions to resist flow thereof. By way of non-limiting example, the
green dielectric film 118 is cured at about 130° C. for about three hours. This temperature and time cause thegreen dielectric film 118 to become non-flowable at room temperature. - At 440, the process includes lifting off portions of the cured dielectric film. In an embodiment, the entire structure is immersed in a peeling liquid that swells the mask and causes the mask-mated cured dielectric film to be removed.
- At 450, the process includes second sintering the cured dielectric film to obtain a thin-film dielectric. In a non-limiting example, an 800° C. environment is provided and the atmosphere is below about 0.1 atm and in argon. The second sintering is carried out for about one hour. After the sintering, the TFC dielectric exhibits a substantially uniform morphology as set forth in this disclosure.
- At 460, the process includes mating a second electrode to the TFC dielectric. The second electrode and the first electrode thus sandwich the TFC dielectric therebetween.
-
FIG. 5 is a cut-away elevation that depicts acomputing system 500 according to an embodiment. One or more of the foregoing embodiments of the thin-film capacitors may be utilized in a computing system, such as acomputing system 500 ofFIG. 5 . Hereinafter any TFC embodiment alone or in combination with any other embodiment may be referred to as an embodiment(s) configuration. - The
computing system 500 includes at least one processor (not pictured), which is enclosed in anIC chip package 510. ATFC 511 is depicted mounted next to thechip package 510 upon aboard 520. In an embodiment, aTFC 511 is integral to thechip package 510. In an embodiment, thesystem 500 also includes adata storage system 512, at least one input device such as akeyboard 514, and at least one output device such as amonitor 516, for example. Thecomputing system 500 includes a processor that processes data signals, and may include, for example, a microprocessor, available from Intel Corporation. In addition to thekeyboard 514, thecomputing system 500 can include another user input device such as amouse 518, for example. Thecomputing system 500 can include a structure after processing as depicted inFIGS. 1A-1D and 3 of a TFC dielectric embodiment. In an embodiment, thecomputing system 500 includes ahousing 522 such as the box for a desktop computer. - For purposes of this disclosure, a
computing system 500 embodying components in accordance with the claimed subject matter may include any system that utilizes a microelectronic device system, which may include, for example, at least one of the TFC dielectric embodiments that is coupled to data storage such as dynamic random access memory (DRAM), polymer memory, flash memory, and phase-change memory. In this embodiment, the embodiment(s) is coupled to any combination of these functionalities by being coupled to a processor. In an embodiment, however, the embodiment(s) configuration set forth in this disclosure is coupled to any of these functionalities. In an example embodiment, thedata storage system 512 includes an embedded DRAM cache on a die. Additionally in an embodiment, the embodiment(s) configuration that is coupled to the processor (not pictured) is part of the system with an embodiment(s) configuration that is coupled to the data storage of the DRAM cache. Additionally in an embodiment, an embodiment(s) configuration is coupled to thedata storage system 512. - In an embodiment, the
computing system 500 can also include a die that contains a digital signal processor (DSP), a micro controller, an application specific integrated circuit (ASIC), or a microprocessor. In this embodiment, the embodiment(s) configuration is coupled to any combination of these functionalities by being coupled to a processor. For an example embodiment, a DSP is part of a chipset that may include a stand-alone processor and the DSP as separate parts of the chipset on theboard 520, which is a TFC dielectric embodiment. In this embodiment, an embodiment(s) configuration is coupled to the DSP, and a separate embodiment(s) configuration may be present that is coupled to the processor in theIC chip package 510. Additionally in an embodiment, an embodiment(s) configuration is coupled to a DSP that is mounted on thesame board 520 as theIC chip package 510. It can now be appreciated that the embodiment(s) configuration can be combined as set forth with respect to thecomputing system 500, in combination with an embodiment(s) configuration as set forth by the various embodiments of the TFC dielectric within this disclosure and their equivalents. - It can now be appreciated that embodiments set forth in this disclosure can be applied to devices and apparatus other than a traditional computer. For example, a die can be packaged with an embodiment(s) configuration, and placed in a portable device such as a wireless communicator or a hand-held device such as a personal data assistant and the like. In this embodiment, the system housing can be a shell for a wireless telephone or the like. Another example is a die that can be packaged with an embodiment(s) configuration and placed in a vehicle such as an automobile, a locomotive, a watercraft, an aircraft, or a spacecraft.
-
FIG. 6 is a schematic of anelectronic system 600 according to an embodiment. Theelectronic system 600 as depicted can embody thecomputing system 500 depicted inFIG. 5 , but the electronic system is depicted more generically. Theelectronic system 600 incorporates at least one mounting substrate, for example theboard 520 depicted inFIG. 5 , with anelectronic assembly 610, such as an integrated circuit die. In an embodiment, theelectronic system 600 is a computer system that includes asystem bus 620 to electrically couple the various components of theelectronic system 600. Thesystem bus 620 is a single bus or any combination of busses according to various embodiments. Theelectronic system 600 includes avoltage source 630 that provides power to theintegrated circuit 610. In some embodiments, thevoltage source 630 supplies current to theintegrated circuit 610 through thesystem bus 620. In an embodiment, aTFC assembly 680 is electrically located between thevoltage source 630 and theintegrated circuit 610. Such location in an embodiment is in a mounting substrate and theTFC assembly 680 is integral to the mounting substrate. Such location of theTFC assembly 680 in an embodiment is upon a mounting substrate that provides a seat for theintegrated circuit 610 and theTFC assembly 680, such as a processor and a TFC component, each mounted laterally and adjacent to the other on a board. - The
integrated circuit 610 is electrically coupled to thesystem bus 620 and includes any circuit, or combination of circuits, according to an embodiment. In an embodiment, theintegrated circuit 610 includes aprocessor 612 that can be of any type. As used herein, theprocessor 612 means any type of circuit such as, but not limited to, a microprocessor, a microcontroller, a graphics processor, a digital signal processor, or another processor. Other types of circuits that can be included in theintegrated circuit 610 are a custom circuit or an ASIC, such as acommunications circuit 614 for use in wireless devices such as cellular telephones, pagers, portable computers, two-way radios, and similar electronic systems. In an embodiment, theprocessor 610 includes on-die memory 616 such as SRAM. In an embodiment, theprocessor 610 includes on-die memory 616 such as eDRAM. - In an embodiment, the
electronic system 600 also includes anexternal memory 640 that in turn may include one or more memory elements suitable to the particular application, such as amain memory 642 in the form of RAM, one or morehard drives 644, and/or one or more drives that handleremovable media 646, such as diskettes, compact disks (CDs), digital video disks (DVDs), flash memory keys, and other removable media known in the art. - In an embodiment, the
electronic system 600 also includes adisplay device 650 or anaudio output 660. In an embodiment, theelectronic system 600 includes aninput device 670, such as a keyboard, mouse, trackball, game controller, microphone, voice-recognition device, or any other device that inputs information into theelectronic system 600. - As shown herein, the
integrated circuit 610 can be implemented in a number of different embodiments, including an electronic package, an electronic system, a computer system, one or more methods of fabricating an integrated circuit, and one or more methods of fabricating an electronic assembly that includes the integrated circuit mounted on a board and the TFC assembly embodiments as set forth herein in the various embodiments and their art-recognized equivalents. The elements, materials, geometries, dimensions, and sequence of operations can all be varied to suit particular packaging requirements. - In the foregoing Detailed Description, various features may be grouped together in a single embodiment for the purpose of simplifying the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed embodiments of the disclosure require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter may lie in less than all features of a single disclosed embodiment. Thus the following claims are hereby incorporated into the Detailed Description, with each claim standing on its own as a separate preferred embodiment.
- It will be readily understood to those skilled in the art that various other changes in the details, material, and arrangements of the parts and method stages which have been described and illustrated in order to explain the nature of embodiments may be made without departing from the principles and scope of the disclosure as expressed in the subjoined claims.
- The Abstract is provided to comply with 37 C.F.R. §1.72(b) requiring an abstract that will allow the reader to quickly ascertain the nature and gist of the technical disclosure. It is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims.
Claims (10)
1-17. (canceled)
18. A thin-film capacitor article comprising:
a first electrode;
a dielectric disposed upon the first electrode, wherein the dielectric exhibits a substantially uniform heat-altered morphology along a line defined by a characteristic dimension thereof; and
a second electrode disposed upon the dielectric.
19. The thin-film capacitor of claim 18 , wherein the characteristic dimension is in a range from about 0.1 micrometer to about 1 micrometer.
20. The thin-film capacitor of claim 18 , wherein the TFC includes BST.
21. The thin-film capacitor of claim 18 , further including a socket coupled to the TFC.
22. The thin-film capacitor of claim 21 , further including:
a die coupled to the TFC, wherein the die is disposed on the socket at a die side.
23. The thin-film capacitor of claim 21 , further including:
a die coupled to the TFC; and
a board coupled to the socket, wherein the TFC is disposed between the board and the socket.
24. A computing system comprising:
a microelectronic die;
a TFC including:
a first electrode;
a dielectric disposed upon the first electrode, wherein the dielectric exhibits a substantially uniform heat-altered morphology along a line defined by a characteristic dimension thereof; and
a second electrode disposed upon the dielectric; and
a dynamic random access memory coupled to the TFC.
25. The computing system of claim 24 , wherein the system is disposed in one of a computer, a wireless communicator, a hand-held device, an automobile, a locomotive, an aircraft, a watercraft, and a spacecraft.
26. The computing system of claim 24 , wherein the microelectronic die is selected from a data storage device, a digital signal processor, a micro controller, an application specific integrated circuit, and a microprocessor.