US20120193604A1 - Wavelength conversion plate and light emitting device using the same - Google Patents
Wavelength conversion plate and light emitting device using the same Download PDFInfo
- Publication number
- US20120193604A1 US20120193604A1 US13/446,735 US201213446735A US2012193604A1 US 20120193604 A1 US20120193604 A1 US 20120193604A1 US 201213446735 A US201213446735 A US 201213446735A US 2012193604 A1 US2012193604 A1 US 2012193604A1
- Authority
- US
- United States
- Prior art keywords
- wavelength conversion
- conversion plate
- group
- light
- compound semiconductor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Provided is a wavelength conversion plate having excellent luminous efficiency of a wavelength-converted light. The wavelength conversion plate includes a dielectric layer with nano pattern, a metal layer formed inside the nano pattern, and a wavelength conversion layer formed on the metal layer and having quantum dot or phosphor which wavelength-converts an excitation light to generate a wavelength-converted light.
Description
- This application claims the priority of Korean Patent Application No. 2008-0086983 filed on Sep. 3, 2008, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference.
- 1. Field of the Invention
- The present invention relates to a light emitting device and a method for manufacturing the same, and more particularly, to a wavelength conversion plate having excellent luminous efficiency of a wavelength-converted light, and a light emitting device using the same.
- 2. Description of the Related Art
- Light emitting diode (LED) is characterized in that it emits light substantially identical to monochromatic light, while light from other light emitting devices such as an incandescent lamp has a wide light emission spectrum. Since LEDs have different energies according to their electron-hole recombination, they emit a red light, a green light, a blue light, a reddish yellow light, or a yellow light according to their characteristics.
- Recently, there have been developed LEDs which can emit a white light or reproduce a plurality of colors. A white LED is manufactured by combination of several color LED chips, or combination of LED chips emitting specific color light and phosphors emitting specific color fluorescence. The currently commercialized white LED generally employs the latter method.
- For example, a white LED package can be obtained by encapsulating a blue LED chip with a molding resin where a yellow phosphor is dispersed. If light having a wavelength of 460 nm is generated from the blue LED chip, the yellow phosphor absorbs the light and generates light having a wavelength of 545 nm. The two lights having the different wavelengths are mixed to output a white light. Therefore, a desired color light can be obtained by combining different kinds of phosphors.
- Although the desired color can be obtained using the phosphors, the increase of the luminous efficiency is still required in view of the emission of the LED.
- An aspect of the present invention provides a wavelength conversion plate having excellent luminous efficiency of a wavelength-converted light, and a light emitting device using the same.
- According to an aspect of the present invention, there is provided a wavelength conversion plate including: a dielectric layer with nano pattern; a metal layer formed inside the nano pattern; and a wavelength conversion layer formed on the metal layer and comprising quantum dot or phosphor which wavelength-converts an excitation light to generate a wavelength-converted light.
- The dielectric layer may include polymer resin or metal oxide. The polymer resin may include poly methyl methacrylate (PMMA), poly lauryl methacrylate (PLMA), or polystyrene. The metal oxide may include SiO2 or TiO2. The metal layer may include any one of Au, Ag, Al, Cu, Pt, Pd, and alloy thereof.
- The quantum dot may include any one of Si nanocrystal, group II-VI compound semiconductor nanocrystal, group III-V compound semiconductor nanocrystal, group IV-VI compound semiconductor nanocrystal, and compounds thereof. The group II-VI compound semiconductor nanocrystal may include any one material selected from the group consisting of CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, HgS, HgSe, HgTe, CdSeS, CdSeTe, CdSTe, ZnSeS, ZnSeTe, ZnSTe, HgSeS, HgSeTe, HgSTe, CdZnS, CdZnSe, CdZnTe, CdHgS, CdHgSe, CdHgTe, HgZnS, HgZnSe, HgZnTe, CdZnSeS, CdZnSeTe, CdZnSTe, CdHgSeS, CdHgSeTe, CdHgSTe, HgZnSeS, HgZnSeTe, and HgZnSTe. The group III-V compound semiconductor nanocrystal may include any one material selected from the group consisting of GaN, GaP, GaAs, AlN, AlP, AlAs, InN, InP, InAs, GaNP, GaNAa, GaPAs, AlNP, AlNAs, AlPAs, InNP, InNAs, InPAs, GaAlP, GaAlNAs, GaAlPAs, GaInNP, GaInAs, GaInPAs, InAlNP, InAlNAs, and InAlPAs. The group IV-VI compound semiconductor nanocrystal may include SbTe.
- According to another aspect of the present invention, there is provided a light emitting device including: a light emitting element; a groove part having a bottom surface where the light emitting element is mounted, and aside surface where a reflection part is formed; a support part supporting the groove part and having an electrode part electrically connected to the light emitting element; and a wavelength conversion plate disposed in at least one of the bottom surface and the side surface of the groove part, wherein the wavelength conversion plate includes: a dielectric layer with nano pattern; a metal layer formed inside the nano pattern; and a wavelength conversion layer formed on the metal layer and comprising quantum dot or phosphor which wavelength-converts an excitation light to generate a wavelength-converted light.
- The light emitting device may further include a wavelength conversion unit disposed on the light emitting element and having quantum dot or phosphor which wavelength-converts light from the light emitting element. The wavelength conversion unit may be implemented with a plurality of layers. In this case, the wavelength conversion unit may be formed inside the groove part where the light emitting element is mounted.
- When the wavelength conversion unit is implemented with a plurality of layers, at least two wavelength conversion units among the plurality of wavelength conversion units may include quantum dots or phosphors which convert the light emitted from the light emitting element into light having different wavelengths. Therefore, the light emitting element may emit an infrared light; the wavelength conversion plate may emit a blue light; a first wavelength conversion unit among the plurality of wavelength conversion units may emit a red light; and a second wavelength conversion unit different from the first wavelength conversion unit among the plurality of wavelength conversion units may emit a green light. In this way, the light emitting device can emit a white light.
- The above and other aspects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
-
FIG. 1 illustrates a wavelength conversion plate according to an embodiment of the present invention; -
FIG. 2 illustrates a light emitting device including the wavelength conversion plate according to an embodiment of the present invention; -
FIG. 3 illustrates a light emitting device including the wavelength conversion plate on the bottom surface of a groove part according to another embodiment of the present invention; -
FIG. 4 illustrates a light emitting device further including a wavelength conversion unit according to another embodiment of the present invention; and -
FIG. 5 illustrates a light emitting device further including a plurality of wavelength conversion units according to another embodiment of the present invention. - Exemplary embodiments of the present invention will now be described in detail with reference to the accompanying drawings. The invention may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will be thorough and complete and will fully convey the concept of the invention to those skilled in the art. In the drawings, the thicknesses of layers and regions are exaggerated for clarity.
-
FIG. 1 illustrates a wavelength conversion plate according to an embodiment of the present invention. Thewavelength conversion plate 10 according to the embodiment of the present invention includes a dielectric layer 11 withnano pattern 12, ametal layer 13 formed inside thenano pattern 12, and awavelength conversion layer 14 formed on themetal layer 13 and having quantum dot or phosphor wavelength-converting an excitation light to generate a wavelength-converted light. - Since the
wavelength conversion plate 10 according to the embodiment of the present invention includes the dielectric layer 11 with thenano pattern 12 and the film-type metal layer 13 inside thenano pattern 12, that is, thepatterned metal layer 13, incident light is amplified by surface plasmon phenomenon generated at an interface of the dielectric layer 11 and themetal layer 13. - The surface plasmon phenomenon is a collective charge density oscillation generated at the surface of the metal film, and a surface plasmon wave generated by the collective charge density oscillation is a surface electromagnetic wave which propagates along the interface of the metal and the dielectric. Such a phenomenon is generated in metals, such as gold (Au), silver (Ag), copper (Cu) or aluminum (Al), which are easily subject to emission of electrons by external stimulation and have a negative dielectric constant. Among those metals, silver (Ag) exhibiting the sharpest surface plasmon resonance (SPR) peak and gold (Au) exhibiting excellent surface stability are usually used.
- The excitation of the surface Plasmon refers to the phenomenon that, when an electric field is applied from the outside to the interface of two media (i.e., metal and dielectric) having a different dielectric constant, surface charges are induced because of the discontinuity of vertical components of the electric field at the interface of the two media, and oscillation of those surface charges is exhibited as the surface plasmon wave.
- Recently, the emission increase phenomenon derived from the surface plasmon phenomenon has been reported (Nano Letters, Vol. 5, No. 8, 1557-1561, 2005). According to this document, after patterning a polymer resin with constant sizes and intervals, an Ag layer was formed and a visible ray was irradiated thereon. In this case, the luminous efficiency was rapidly increased more than 10 times.
- In the
wavelength conversion plate 10 according to the embodiment of the present invention, if the quantum dot or phosphor included in thewavelength conversion layer 14 wavelength-converts the excitation light, the surface plasmon phenomenon is generated in themetal layer 13 and thus the wavelength-converted light is amplified. - The dielectric layer 11 may include a material having a different dielectric function from the
metal layer 13 in order to generate the surface plasmon phenomenon in themetal layer 13. For example, the dielectric layer 11 may include polymer resin or metal oxide. The polymer resin used herein may be, but is not limited to, poly methyl methacrylate (PMMA), poly lauryl methacrylate (PLMA), or polystyrene. Also, the metal oxide used herein may be, but is not limited to, SiO2 or TiO2. - The
nano pattern 12 is formed in the dielectric layer 11. Referring toFIG. 1 , thenano pattern 12 may be formed in a cylindrical shape with a curved bottom. However, there is no special limitation in the shape of thenano pattern 12 only if the pattern itself is nano-sized. - As a method of forming the
nano pattern 12 in the dielectric layer 11, an Anodic Aluminum Oxide template (AAO template) formed by oxidizing aluminum may be used. In the method using the AAO template, aluminum is used because of its unique characteristic in that aluminum forms a pore arrangement in itself in an oxidation process for forming aluminum oxide. In this case, the pore is several ten to several hundred nanometers in diameter and is several micrometers in length according to voltage and concentration of an acid solution in the aluminum oxidation process. - Therefore, if the dielectric layer is formed and its upper surface is etched using the AAO template, the
nano pattern 12 is formed in the same shape as the pore formed in the AAO template. - The
metal layer 13 patterned along the pattern inside thenano pattern 12 is formed on the dielectric layer 11. As described above, themetal layer 13 may be formed using a metal where the surface Plasmon phenomenon is easily generated, that is, a metal which is easily subject to emission of electrons by external stimulation and has a negative dielectric constant. The metal may include, but is not limited to, Au, Ag, Al, Cu, Pt, or Pd. There are many methods of forming themetal layer 13. As one method, themetal layer 13 may be formed by sputtering a metal onto the dielectric layer 11 where thenano pattern 12 is formed. - The
wavelength conversion layer 14 is formed on themetal layer 13. Thewavelength conversion layer 14 includes quantum dot or phosphor which wavelength-converts the excitation light to generate the wavelength-converted light. Thewavelength conversion layer 14 is formed while filling the inside of the pattern of themetal layer 13. - The quantum dot is a nano-sized light emitting body which has a diameter of 10 nm or less and exhibits a quantum confinement effect. The quantum dot generates stronger light than a typical phosphor in a narrow wavelength. The emission of the quantum dot is generated when excited electrons move from a conduction band to a valence band. Even the same material exhibits different wavelengths according to the particle size. As the size of the quantum dot is smaller, light having a shorter wavelength is emitted. Thus, light having a desired wavelength range can be obtained by adjusting the size of the quantum dot.
- The quantum dot emits light even at an arbitrary excitation wavelength. Thus, when several kinds of quantum dots exist, several color light can be observed at a time even though the quantum dot is excited at a single wavelength. Furthermore, since the quantum dot moves from the ground oscillation state of the conduction band to the ground oscillation state of the valence band, it is advantageous that the emission wavelength is almost the monochromatic light.
- The quantum dot may be a semiconductor nanocrystal. Examples of the quantum dot may include Si nanocrystal, group II-VI compound semiconductor nanocrystal, group III-V compound semiconductor nanocrystal, or group IV-VI compound semiconductor nanocrystal. In the current embodiment, the quantum dots may be used solely or in mixture thereof.
- The group II-VI compound semiconductor nanocrystal may include, but is not limited to, CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, HgS, HgSe, HgTe, CdSeS, CdSeTe, CdSTe, ZnSeS, ZnSeTe, ZnSTe, HgSeS, HgSeTe, HgSTe, CdZnS, CdZnSe, CdZnTe, CdHgS, CdHgSe, CdHgTe, HgZnS, HgZnSe, HgZnTe, CdZnSeS, CdZnSeTe, CdZnSTe, CdHgSeS, CdHgSeTe, CdHgSTe, HgZnSeS, HgZnSeTe, or HgZnSTe.
- Furthermore, the group III-V compound semiconductor nanocrystal may include, but is not limited to, GaN, GaP, GaAs, AlN, AlP, AlAs, InN, InP, InAs, GaNP, GaNAa, GaPAs, AlNP, AlNAs, AlPAs, InNP, InNAs, InPAs, GaAlP, GaAlNAs, GaAlPAs, GaInNP, GaInAs, GaInPAs, InAlNP, InAlNAs, or InAlPAs.
- Moreover, the group IV-VI compound semiconductor nanocrystal may include, but is not limited to, SbTe.
- As a method of synthesizing the nanocrystal as the quantum dot, the quantum dot is formed by a vapor deposition method, such as a metal organic chemical vapor deposition (MOCVD) or a molecular beam epitaxy (MBE), or a chemical wet method of growing a crystal by putting a precursor material into an organic solvent.
- The phosphor may be selected from an oxide phosphor, a sulfide phosphor, and a nitride phosphor according to the conversion wavelength. For example, the phosphor may include a yellow emission phosphor based on β-SiAlON:Eu,Re, a silicate-based green emission phosphor such as (Ba,Sr,Ca,Mg)2SiO4:Eu,Re, or a sulfide-based green emission phosphor such as (Ba,Sr,Ca,Mg) (Ga,Al,In)2(S,Se,Te)4:Eu,Re, a nitride-based red emission phosphor such as (Sr,Ca,Ba,Mg)AlSiNx:Eu,Re (1≦x≦5), or a sulfide-based red emission phosphor such as (Sr,Ca,Ba,Mg) (S,Se,Te):Eu,Re. Herein, Re may be any one of Nd, Pm, Sm, Tb, Dy, Ho, Er, Tm, Yb, F, Cl, Br, and I.
- The
wavelength conversion layer 14 may be used by dispersing the quantum dot in a dispersive medium. The dispersive medium may be a resin such as epoxy resin or silicon. Thewavelength conversion layer 14 may be formed by dispersing the quantum dot or phosphor in the dispersive medium and coating the dispersive medium on themetal layer 13. The wavelength conversion performance of thewavelength conversion layer 14 may be selected by adjusting the concentration of the quantum dot or phosphor dispersed in the dispersive medium. - In the
wavelength conversion plate 10, the quantum dot or phosphor included in thewavelength conversion layer 14 absorbs the incident light and emits the wavelength-converted light. Thus, in addition to the wavelength conversion function, thewavelength conversion plate 10 can amplify the emission of the wavelength-converted light due to the surface plasmon phenomenon generated in themetal layer 13 formed inside thenano pattern 12. - Therefore, the
wavelength conversion plate 10 can be variously used when it is necessary to receive an excitation light from a light source, wavelength-convert the received excitation light and then amplify the wavelength-converted light. For example, thewavelength conversion plate 10 may be used as a reflection plate of a light guide panel in an LED package or backlight unit, but it is not limited thereto. Hereinafter, a light emitting device using thewavelength conversion plate 10 will be described in detail with reference toFIGS. 2 to 5 . -
FIG. 2 illustrates a light emitting device including a wavelength conversion plate according to an embodiment of the present invention. Herein, duplicate description about the dielectric layer, the nano pattern, the metal layer, and the wavelength conversion layer in thelight emitting device 100 ofFIG. 2 will be omitted, except when necessary. - The
light emitting device 100 according to the embodiment of the present invention includes alight emitting element 140, a groove part, a support part 110, and awavelength conversion plate 160. The groove part has a bottom surface where thelight emitting element 140 is mounted, and a side surface where areflection part 120 is formed. The support part 110 supports the groove part and includes anelectrode part 130 electrically connected to thelight emitting element 140. Thewavelength conversion plate 160 is disposed in at least one of the bottom surface and the side surface of the groove part. Thewavelength conversion plate 160 includes a dielectric layer with nano pattern, a metal layer formed inside the nano pattern, and a wavelength conversion layer formed on the metal layer and including quantum dot or phosphor which wavelength-converts an excitation light to generate a wavelength-converted light. Theelectrode part 130 is formed with two sections which are electrically separated. - The
light emitting element 140 may be one of a light emitting diode and a laser diode. A blue LED may be used as thelight emitting element 140. The blue LED may be a GaN-based LED emitting a blue light of 420-480 nm. Theelectrode part 130 is formed on the support part 110 and is electrically connected to thelight emitting element 140 through a wire. - An
encapsulation part 150 is formed of an encapsulation material on thelight emitting element 140 in order to encapsulate thelight emitting element 140. Theencapsulation part 150 is formed by filling the groove part with an encapsulation material, such as epoxy, silicon, acryl-based polymer, glass, carbonate-based polymer, or a mixture thereof. - The
reflection part 120 formed in the side surface of the groove part reflects light generated from thelight emitting element 140 toward the outside of the groove part. InFIG. 2 , thewavelength conversion plate 160 is formed in thereflection part 120. - The
wavelength conversion plate 160 includes the dielectric layer with the nano pattern, the metal layer formed on the dielectric layer, and the wavelength conversion layer formed on the metal layer and including the quantum dot or phosphor which wavelength-converts the light generated from thelight emitting element 140 to generate the wavelength-converted light. As described above with reference toFIG. 1 , the wavelength conversion layer may be used by dispersing the quantum dot or phosphor in the dispersive medium. Since the dispersive medium may be a resin such as epoxy resin or silicon, it may be an identical or similar material to the encapsulation material. - Since the
wavelength conversion plate 160 wavelength-converts and amplifies the light from thelight emitting element 140, the quantum dot or phosphor inside thewavelength conversion plate 160 may be selected considering color and intensity of light desired to be obtained from thelight emitting device 100. For example, when thelight emitting element 140 emits a blue light, thelight emitting device 100 can emit a white color by selecting the quantum dot or phosphor inside thewavelength conversion plate 160 such that it emits a yellow color. - Although the
wavelength conversion plate 160 shown inFIG. 2 is disposed at thereflection part 120 located on the side surface of the groove part, it can also be disposed on the bottom surface of the groove part.FIG. 3 illustrates a light emitting device according to another embodiment of the present invention, in which a wavelength conversion plate is disposed on a bottom surface of a groove part. Regarding a dielectric layer, a nano pattern, a metal layer, and a wavelength conversion layer in thelight emitting device 200 ofFIG. 3 , the description of the same parts as described with reference toFIGS. 1 and 2 will be omitted, except when necessary. Also, regarding asupport part 210, areflection part 220, anelectrode part 230, alight emitting element 240, anencapsulation part 250, and awavelength conversion plate 260, the description of the same parts as described with reference toFIG. 2 will be omitted. - Unlike in
FIG. 2 , thewavelength conversion plate 260 is disposed on the bottom surface of the groove part where thelight emitting element 240 is mounted. Thewavelength conversion plate 260 is formed in a region other than the region where thelight emitting element 240 is formed. The case where thewavelength conversion plate 260 is formed on the bottom surface of the groove part is related to the shape of thelight emitting device 200. In order for thewavelength conversion plate 260 to effectively wavelength-convert and amplify the light from thelight emitting element 240, the quantity of light reaching thewavelength conversion plate 260 should be large. However, if the width of thelight emitting device 200 is wide, the case where the excitation light reaches the bottom surface may be much more than the case where the excitation light reaches thereflection part 220. Therefore, in such a case, thewavelength conversion plate 260 is formed on the bottom surface of the groove part. - According to another embodiment of the present invention, in addition to the wavelength conversion plate formed in at least one of the side surface and the bottom surface of the groove part, a light emitting device further includes a wavelength conversion unit which wavelength-converts light from the light emitting element.
FIG. 4 illustrates the light emitting device which further includes the wave conversion unit according to the embodiment of the present invention. Regarding a dielectric layer, a nano pattern, a metal layer, and a wavelength conversion layer in thelight emitting device 300 ofFIG. 4 , the description of the same parts as described with reference toFIGS. 1 to 3 will be omitted, except when necessary. Also, regarding asupport part 310, areflection part 320, anelectrode part 330, alight emitting element 340, anencapsulation part 350, and awavelength conversion plate 360, the description of the same parts as described with reference toFIGS. 2 and 3 will be omitted. - In the current embodiment, the
wavelength conversion unit 370 further included in thelight emitting device 300 includes awavelength conversion body 371 and adispersive medium 372. Thewavelength conversion body 371 may be a typical quantum dot or phosphor. Thedispersive medium 372 may be a medium which properly disperses polymer resin and thewavelength conversion body 371. Thedispersive medium 372 may be an identical or similar material to an encapsulation material of theencapsulation part 350. - After mounting the
light emitting element 340, thewavelength conversion unit 370 may be formed on thelight emitting element 340 before the groove part is filled with theencapsulation material 350. Thewavelength conversion unit 370 can include an appropriate quantum dot or phosphor according to the wavelength of light desired to be obtained from thelight emitting device 300, the color of the light emitted from thelight emitting device 300 can be controlled together with the quantum dot or phosphor included in thewavelength conversion plate 360. Although thewavelength conversion unit 370 shown inFIG. 4 is formed in a layer type, it can also be formed to cover the surface of thelight emitting device 340. Also, thewavelength conversion unit 370 may be disposed in any shape only if the light incident from thelight emitting element 340 can be wavelength-converted at thewavelength conversion unit 370. - At this point, the
light emitting device 300 can emit a white light, when thelight emitting element 340 emits a blue light, the quantum dot or phosphor of thewavelength conversion unit 370 emits a red light, and the quantum dot or phosphor of thewavelength conversion plate 360 emits a green light. Furthermore, thelight emitting element 340 can be made to emit a blue light, and the quantum dot or phosphor of thewavelength conversion unit 370 can be made to emit a yellow light. In this case, the quantum dot of thewavelength conversion plate 360 can be selected to emit a blue light or a yellow light. The color rendering of the light emitted from thelight emitting device 300 can be controlled by making the quantum dot of thewavelength conversion plate 360 emit the light having the lower intensity of the blue light and the yellow light. - According to another embodiment of the present invention, a light emitting device may further include a plurality of wavelength conversion units.
FIG. 5 illustrates the light emitting device which further includes the plurality of wave conversion units according to the embodiment of the present invention. Regarding a dielectric layer, a nano pattern, a metal layer, and a wavelength conversion layer in thelight emitting device 400 ofFIG. 5 , the description of the same parts as described with reference toFIGS. 1 to 4 will be omitted, except when necessary. Also, regarding asupport part 410, areflection part 420, anelectrode part 430, alight emitting element 440, anencapsulation part 450, and awavelength conversion plate 460, the description of the same parts as described with reference toFIGS. 2 and 4 will be omitted. - In the current embodiment, the wavelength conversion units further included in the
light emitting device 400 include a firstwavelength conversion unit 470 and a second wavelength conversion unit 480. InFIG. 5 , a wavelength conversion unit nearer to thelight emitting element 440 is referred to as the firstwavelength conversion unit 470, and another is referred to as the second wavelength conversion unit 480. The firstwavelength conversion unit 470 includes a firstwavelength conversion body 471 and a firstdispersive medium 472, and the second wavelength conversion unit 480 includes a secondwavelength conversion body 481 and asecond dispersive medium 482. The first and secondwavelength conversion bodies dispersive media wavelength conversion bodies dispersive media encapsulation part 450. - When the wavelength conversion unit is implemented with a plurality of layers, at least two wavelength conversion units may include quantum dots or phosphors which can convert the light emitted from the light emitting element into light having different wavelengths. Therefore, the
light emitting element 440 emits a blue light, any one of the wavelength conversion units emits a red light, and the second wavelength conversion unit 480 different from the first wavelength conversion unit emits a green light. In this way, the light emitting device can emit a white light. Furthermore, thewavelength conversion plate 460 can select quantum dots to emit light by appropriately selecting the wavelength of the light required to be amplified among the blue light, the red light, and the green light. - Alternatively, the light emitting device can emit a white light, when the
light emitting element 440 emits an infrared ray, and thewavelength conversion plate 460, the firstwavelength conversion unit 470 and the second wavelength conversion unit 480 emit a blue light, a green light and a red light, respectively. - The light emitting devices are shown in a package type in
FIGS. 2 to 5 , but they are not limited thereto. For example, the light emitting devices may be lamp-type light emitting devices. - The wavelength conversion plates according to the embodiments of the present invention can use the surface plasmon phenomenon by forming the metal layer on the dielectric layer with the nano pattern. Therefore, the wavelength-converted light generated by the wavelength conversion of the excitation light at the quantum dot, or the light emitted from the light emitting source can be amplified by the surface plasmon phenomenon.
- Furthermore, if the wavelength conversion plate capable of amplifying the light by using the surface plasmon phenomenon is used on the side surface of the light emitting package, the luminous efficiency of the light emitting package can be increased. In addition, if the wavelength conversion plate is used as the reflection plate or wavelength conversion plate of the light emitting source, the light of the light emitting source can be amplified. Thus, the light emitting device having excellent efficiency can be manufactured.
- While the present invention has been shown and described in connection with the exemplary embodiments, it will be apparent to those skilled in the art that modifications and variations can be made without departing from the spirit and scope of the invention as defined by the appended claims.
Claims (21)
1-15. (canceled)
16. A wavelength conversion plate comprising:
a dielectric layer having a planar upper surface and a nano pattern formed in a cylindrical shape with a curved bottom, wherein the nano pattern comprises a plurality of nano scale grooves;
a metal layer formed on an inside wall of the nano scale grooves of the nano pattern; and
a wavelength conversion layer formed on the metal layer and comprising quantum dots or phosphors which wave length-convert excited light to generate wavelength-converted light.
17. The wavelength conversion plate of claim 16 , wherein the dielectric layer comprises a polymer resin or a metal oxide.
18. The wavelength conversion plate of claim 17 , wherein the polymer resin comprises poly methyl methacrylate (PMMA), poly lauryl methacrylate (PLMA), or polystyrene.
19. The wavelength conversion plate of claim 17 , wherein the metal oxide comprises SiO2 or TiO2.
20. The wavelength conversion plate of claim 16 , wherein the metal layer comprises any one of Au, Ag, Al, Cu, Pt, Pd, and alloys thereof.
21. The wavelength conversion plate of claim 16 , wherein the quantum dot comprises any one of an Si nanocrystal, a group II-VI compound semiconductor nanocrystal, a group III-V compound semiconductor nanocrystal, a group IV-VI compound semiconductor nanocrystal, and compounds thereof.
22. The wavelength conversion plate of claim 21 , wherein the group II-VI compound semiconductor nanocrystal comprises any one material selected from the group consisting of CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, HgS, HgSe, HgTe, CdSeS, CdSeTe, CdSTe, ZnSeS, ZnSeTe, ZnSTe, HgSeS, HgSeTe, HgSTe, CdZnS, CdZnSe, CdZnTe, CdHgS, CdHgSe, CdHgTe, HgZnS, HgZnSe, HgZnTe, CdZnSeS, CdZnSeTe, CdZnSTe, CdHgSeS, CdHgSeTe, CdHgSTe, HgZnSeS, HgZnSeTe, and HgZnSTe.
23. The wavelength conversion plate of claim 21 , wherein the group III-V compound semiconductor nanocrystal comprises any one material selected from the group consisting of GaN, GaP, GaAs, AlN, AlP, AlAs, InN, InP, InAs, GaNP, GaNAa, GaPAs, AlNP, AlNAs, AlPAs, InNP, InNAs, InPAs, GaAlP, GaAlNAs, GaAIPAs, GaInNP, GaInAs, GaInPAs, InAlNP, InAlNAs, and InAlPAs.
24. The wavelength conversion plate of claim 21 , wherein the group IV-VI compound semiconductor nanocrystal comprises SbTe.
25. The wavelength conversion plate of claim 16 , wherein the dielectric layer is formed by using an Anodic Aluminum Oxide template.
26. A method of manufacturing a wavelength conversion plate comprising:
forming a nano pattern in a dielectric layer, wherein the nano pattern comprises a plurality of nano scale grooves and is formed in a cylindrical shape with a curved bottom;
forming a metal layer on an inside wall of the nano scale grooves of the nano pattern; and
forming a wavelength conversion layer comprising quantum dots or phosphors which wave length-convert excited to generate wave length-converted light, on the metal layer.
27. The method of claim 26 , wherein the dielectric layer comprises a polymer resin or a metal oxide.
28. The method of claim 27 , wherein the polymer resin comprises poly methyl methacrylate (PMMA), poly lauryl methacrylate (PLMA), or polystyrene.
29. The method of claim 27 , wherein the metal oxide comprises SiO2 or TiO2.
30. The method of claim 26 , wherein the metal layer comprises any one of Au, Ag, Al, Cu, Pt, Pd, and alloys thereof.
31. The method of claim 26 , wherein the quantum dot comprises any one of an Si nanocrystal, a group II-VI compound semiconductor nanocrystal, a group III-V compound semiconductor nanocrystal, a group IV-VI compound semiconductor nanocrystal, and compounds thereof.
32. The method of claim 31 , wherein the group II-VI compound semiconductor nanocrystal comprises any one material selected from the group consisting of CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, HgS, HgSe, HgTe, CdSeS, CdSeTe, CdSTe, ZnSeS, ZnSeTe, ZnSTe, HgSeS, HgSeTe, HgSTe, CdZnS, CdZnSe, CdZnTe, CdHgS, CdHgSe, CdHgTe, HgZnS, HgZnSe, HgZnTe, CdZnSeS, CdZnSeTe, CdZnSTe, CdHgSeS, CdHgSeTe, CdHgSTe, HgZnSeS, HgZnSeTe, and HgZnSTe.
33. The method of claim 31 , wherein the group III-V compound semiconductor nanocrystal comprises any one material selected from the group consisting of GaN, GaP, GaAs, AlN, AlP, AlAs, InN, InP, InAs, GaNP, GaNAa, GaPAs, AlNP, AlNAs, AlPAs, InNP, InNAs, InPAs, GaAlP, GaAlNAs, GaAIPAs, GaInNP, GaInAs, GaInPAs, InAlNP, InAlNAs, and InAlPAs.
34. The method of claim 31 , wherein the group IV-VI compound semiconductor nanocrystal comprises SbTe.
35. The method of claim 26 , wherein the dielectric layer is formed by using an Anodic Aluminum Oxide template.