US20120190276A1 - Polishing pad and methods for manufacturing and using the same - Google Patents

Polishing pad and methods for manufacturing and using the same Download PDF

Info

Publication number
US20120190276A1
US20120190276A1 US13/274,831 US201113274831A US2012190276A1 US 20120190276 A1 US20120190276 A1 US 20120190276A1 US 201113274831 A US201113274831 A US 201113274831A US 2012190276 A1 US2012190276 A1 US 2012190276A1
Authority
US
United States
Prior art keywords
abrasive
polishing
polishing pad
abrasive blocks
blocks
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/274,831
Inventor
Qun Shao
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Semiconductor Manufacturing International Shanghai Corp
Original Assignee
Semiconductor Manufacturing International Shanghai Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Semiconductor Manufacturing International Shanghai Corp filed Critical Semiconductor Manufacturing International Shanghai Corp
Assigned to SEMICONDUCTOR MANUFACTURING INTERNATIONAL (SHANGHAI) CORPORATION reassignment SEMICONDUCTOR MANUFACTURING INTERNATIONAL (SHANGHAI) CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: SHAO, Qun
Publication of US20120190276A1 publication Critical patent/US20120190276A1/en
Abandoned legal-status Critical Current

Abstract

This invention provides a polishing pad, which includes a substrate and a plurality of discrete abrasive blocks fixed on the substrate, wherein the abrasive blocks are of at least two kinds of heights. This invention would not reduce the polishing rate dramatically during the process for polishing a wafer by using the polishing pad in the long run. Therefore a thickness of the wafer to be polished is able to be controlled accurately, thereby improving the effect and yield of polishing the wafer. The present invention further provides a method for manufacturing the polishing pad. The polishing pad according to this invention is manufactured conveniently by using this method. Correspondingly, a method for using the polishing pad is also provided in this invention.

Description

    CROSS REFERENCE TO RELATED APPLICATIONS
  • The present application claims the priority of Chinese Patent Application No. 201110023424.6, entitled “Polishing Pad and Methods for Manufacturing and Using the same”, and filed on Jan. 20, 2011, the entire disclosure of which is incorporated herein by reference.
  • FIELD OF THE INVENTION
  • The present invention relates generally to semiconductor manufacturing process, and more particularly to a polishing pad and methods for manufacturing and using the same.
  • BACKGROUND OF THE INVENTION
  • In semiconductor manufacturing process, it is quite important for a device capable of being miniaturized and highly integrated to have a smooth wafer surface. Generally speaking, chemical mechanical polishing (CMP) is used as a conventional process for planarizing a wafer surface. A polishing slurry is added between the wafer surface and a polishing pad. By the effects of mechanical force and the chemical reaction generated between the wafer surface and the polishing slurry, the wafer surface is planarized. In the conventional CMP process, the polishing slurry distributes randomly on the polishing pad, which induces lots of negative problems such as an uneven density, a poor polishing result, a low utilization ratio of the slurry, and environmental pollution caused by wasted polishing slurry. Therefore, the conventional CMP process tends to be replaced with a fixed abrasive polishing process.
  • In the fixed abrasive polishing process, abrasives are fixed on a polishing pad so as to form a fixed abrasive polishing pad having a surface with a regular concave-convex shape, which is disclosed in US patent Publication NO. 20020049027.
  • Afterwards, the polishing pad is mounted on a polishing platen, and a wafer which is going to be polished is mounted on a polishing face of the polishing pad. FIG. 1 is a cross-sectional view of an apparatus used in a fixed abrasive polishing process according to the prior art. Referring to FIG. 1, an inputting roller 1051 together with an outputting roller 1052 transports a polishing pad 102 to a polishing platen 101, and a surface of the polishing pad 102 is moistened by abrasives. A wafer 103 is fixed to a polishing head 104, and a surface of the wafer is contacted with the surface of the polishing pad 102. After starting a driving power, the polishing platen 101 is driven to rotate by the rotation of a bearing 100. The wafer 103 is driven to rotate by the rotating of the polishing head 104 and moves relative to the polishing pad 102, which makes the surface of the wafer 103 rub against the surface of the polishing pad 102 and polished.
  • However, the polishing rate is continuously becoming slower as the polishing process is going on. Thus the polishing rate varies greatly in the process of fixed abrasive polishing. Referring to FIG. 2, the polishing rate descends rapidly from about 1050 Å/min within the first 60 s to about 190 Å/min within a time period from 180 s to 240 s. A thickness of the wafer to be polished is difficult to be controlled accurately because the polishing rate drops rapidly, which causes over-polishing or insufficient polishing leading to wafer damaged.
  • SUMMARY OF THE INVENTION
  • Embodiments of the present invention provide a polishing pad and methods for manufacturing and using the same, to obviate the disadvantage associated with a prior art that a polishing rate can not be kept stable, which causes over or insufficient polishing leading to wafer damaged.
  • One embodiment of the present invention provides a polishing pad, including: a substrate; and
  • a plurality of discrete abrasive blocks fixed on the substrate, wherein the abrasive blocks are of at least two kinds of heights.
  • Optionally, the heights of the abrasive blocks are ranging from about 10 μm to about 50 μm.
  • Optionally, a height difference between any two kinds of the abrasive blocks is at least from about 3 μm to about 5 μm.
  • Optionally, the abrasive blocks have 2 to 20 kinds of heights.
  • Optionally, a width of the abrasive blocks is from about 50 μm to about 200 μm.
  • Another embodiment of the present invention provides a method for manufacturing a polishing pad, including:
  • forming a mixture by mixing a plurality of abrasive particles and organic polymers;
  • coating a substrate with the mixture;
  • compressing the mixture with a mould so as to form abrasive blocks which are of at least two kinds of heights, the mould has a pattern comprising a plurality of gravures which are of at least two kinds of depths and matched with the abrasive blocks; and
  • fixing the abrasive blocks on the substrate.
  • Optionally, the abrasive particles may include one or more materials selected from cerium dioxide, silicon dioxide, adamas, zirconium oxide, aluminum oxide, and silicon nitride.
  • Optionally, the abrasive blocks have 2 to 20 kinds of heights.
  • Optionally, the heights of the abrasive blocks are ranging from about 10 μm to about 50 μm.
  • Optionally, the abrasive blocks are arranged from highest to lowest height, from lowest to highest height, or alternating high and low height on the substrate.
  • Optionally, a height difference between any two kinds of the abrasive blocks is at least from about 3 μm to about 5 μm.
  • Still another embodiment of the present invention provides a method for using the polishing pad, including:
  • providing a polishing pad having a plurality of abrasive blocks which are of at least two kinds of heights; and
  • mounting a wafer on the polishing pad, and adding a polishing slurry to perform polishing.
  • Compared with the prior art, this invention has the following advantages:
  • The polishing pad according to the embodiments of the present invention has a plurality of abrasive blocks fixed thereon which are of at least two kinds of heights. When polishing a wafer, the height of the abrasive blocks having the biggest height is lowered by polishing exhaustion, which degrades the polishing rate. Afterwards, the abrasive blocks having the second biggest height can complement the polishing efficacy, thereby stabilizing the polishing rate, which facilitates to control a thickness of the wafer to be polished accurately and to improve the effect and yield of polishing.
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • FIG. 1 is a cross-sectional view of an apparatus used in a fixed abrasive polishing process according to the prior art;
  • FIG. 2 is a schematic diagram illustrating a relationship between the polishing rate and the polishing time of the fixed abrasive polishing process according to the prior art;
  • FIG. 3 and FIG. 4 are schematic diagrams illustrating a reason for the variation of the polishing rate according to the prior art;
  • FIG. 5 and FIG. 6 are cross-sectional views of a polishing pad according to a first and second embodiments of the present invention;
  • FIG. 7 to FIG. 10 are schematic diagrams illustrating a method for manufacturing a polishing pad according to a third embodiment of the present invention;
  • FIG. 11 is a flow chart of a method for using the polishing pad to perform polishing according to a fourth embodiment of the present invention; and
  • FIG. 12 is a schematic diagram illustrating a method for using the polishing pad to perform polishing according to the fourth embodiment of the present invention.
  • DETAILED DESCRIPTION OF THE EMBODIMENTS
  • In a fixed abrasive polishing process of a prior art, as shown in FIG. 3, a polishing pad includes a substrate and an abrasive layer. The abrasive layer is fixed on the substrate 201, which includes a plurality of three-dimensional abrasive blocks 202 which may be a mixture of compressed abrasive particles and resin adhesives and have a specific shape. The abrasive particles are surrounded within the resin adhesives. All of the abrasive blocks 202 are of the same height. In other words, the abrasive blocks 202 have one height. As shown in FIG. 4, during the polishing process, resin adhesives 2021 are dissolved in a polishing slurry. Therefore, abrasive particles 2022 at the uppermost layer are exposed and contact with the surface of a wafer 203, which participate in polishing the wafer 203. With the polishing process going on, the resin adhesives 2021 further continue dissolving, and the abrasive particles 2022 at the uppermost layer are gradually dissociated from the resin adhesives 2021 by the polishing force, which lowers the height of the abrasive blocks 202. Meanwhile, due to lack of soak time, the resin adhesives 2021 surrounding the abrasive particles 2022 in a next layer fail to be dissolved timely in the polishing slurry, which causes the abrasive particles 2022 in the next layer are not exposed completely. Therefore, a portion of the abrasive particles 2022 in the next layer fail to participate in the polishing process, which reduces the polishing rate of the wafer. Because of the variation of the polishing rate, a thickness of the wafer to be polished is difficult to be controlled accurately, which causes over-polishing or insufficient polishing, resulting in a decreased yield.
  • In order to resolve the problems described above, an embodiment of the present invention provides a polishing pad, which includes a substrate and a plurality of abrasive block arrays fixed on the substrate, wherein the abrasive block arrays are of at least two kinds of heights.
  • The polishing pad according to the embodiment of the present invention has a plurality of abrasive blocks fixed thereon which are of at least two kinds of heights. At the beginning of the polishing process, the abrasive blocks having the first height participate in polishing. With the polishing process going on, the height of the abrasive blocks having the first height which participate in polishing is lowered. The resin adhesives in a next layer are not dissolved timely in the polishing slurry, which causes the abrasive particles surrounded by the resin adhesives fail to participate in polishing, resulting in degrading the polishing efficacy of the abrasive blocks having the first height gradually. Meanwhile, the abrasive blocks having the second height are soaked in the polishing slurry for some time, so that the abrasive particles may be exposed to participate in polishing. Therefore, the polishing rate may not be reduced, but be kept at a stable level substantially, whereby a thickness of the wafer to be polished is controlled accurately, the quality for polishing the wafer is ensured, and the yield of the wafer is improved.
  • Hereunder, the present invention will be described in detail with reference to embodiments, in conjunction with the accompanying drawings.
  • FIG. 5 is a cross-sectional view of a polishing pad according to a first embodiment of the present invention. Referring to FIG. 5, the polishing pad includes a substrate 301 and a plurality of abrasive blocks 302 fixed on the substrate 301. The abrasive blocks 302 are of two kinds of heights, which include abrasive blocks 3021 having a first height h1 and abrasive blocks 3022 having a second height h2. The first height h1 is from about 3 μm to about 5 μm greater than the second height h2. The first height h1 and the second height h2 may be ranging from about 10 μm to about 50 μm, preferably, the first height h1 may be about 30 μm. A width of the abrasive blocks 302 having the first height h1 and the second height h2 may be from about 50 μm to about 200 μm, preferably, the width may be about 100 μm
  • In this embodiment, the abrasive blocks 302 having different heights may be arranged from highest to lowest height, from lowest to highest height, or alternating high and low height on the substrate 301, or arranged according to actual requirements.
  • In this embodiment, the width W of the abrasive block indicates an average width of a cross-sectional profile of the abrasive block. For example, as for a cylindrical abrasive block, the width W is a diameter of section of the cylinder. As for a trapeziform abrasive block, the width W is a length connecting midpoints at both sides of the trapezium formed by a cross-sectional profile of the trapezoid abrasive block. Similarly, as for a pyramidal abrasive block, the width W is a length connecting midpoints at both sides of the pyramid formed by a cross-sectional profile of the pyramidal abrasive block. The width W of the abrasive blocks aims to ensure a sufficient polishing rate which ranges from about 50 μm to about 200 μm. Preferably, the width may be about 100 μm.
  • In this embodiment, an interval between the abrasive blocks may be from about 50 μm to about 400 μm, preferably, the interval may be about 200 μm, which aims to ensure a chemical solution to flow sufficiently within the abrasive blocks.
  • In this embodiment, the substrate 301 may be a rigid substrate, such as a substrate including organic glass (PMMA), polyvinyl chloride (PVC), polycarbonate (PC), or polyethylene terephathalate (PET). Optionally, the substrate 301 may be of a certain resilience, which includes polyurethane, polyolefin, phenylethylene, polyester, polyamide, or black damping cloth. Optionally, the substrate 301 may be a multilayer substrate which is formed by combining a rigid substrate with a resilient substrate.
  • In this embodiment, the abrasive blocks 302 include a mixture of abrasive particles and resin adhesives which are compressed to form a three-dimensional structure having a specific shape. The abrasive particles may include one or more materials selected from silicon dioxide, cerium dioxide, aluminium oxide, silicon carbide, boron carbide, zirconium oxide, adamas, and the like. Preferably, the abrasive particles include cerium dioxide. A particle size of the abrasive particles ranges from about 50 nm to about 1000 nm. The resin adhesives may include one or more organic resins selected from phenolic resin, urea formaldehyde resin, melamine—formaldehyde resin, acrylic polyurethane, acrylic epoxy resin, ethyleneunion unsaturated compound, vinyl ether, epoxy resin, and the like. The shape of the abrasive blocks 302 may be cylinder, hemisphere, pyramid, trapezium, and the like. Preferably, the abrasive blocks 302 are trapezium-shaped, a cross sectional area of which decreases gradually along the height from the substrate. The abrasive blocks 302 are regularly fixed on the substrate 301 so as to form a regular topography of abrasive block arrays.
  • The aforementioned abrasive particles and resin adhesives are mixed according to a certain proportion to form a mixture, which coats the substrate 301 uniformly. The mixture is compressed by a mould which has a corresponding pattern so as to form an array of abrasive blocks 302 having a specific shape, then the abrasive blocks 302 are solidified by thermal energy or radiant energy. The proportion for mixing the abrasive particles and resin adhesives may be configured in accordance with practical use. Optionally, a percentage by weight of the abrasive particles and resin adhesives may be 1:2. As a matter of fact, a curing agent, an initiating agent, or a catalytic agent may be added into the mixture of the abrasive particles and the resin adhesives so as to speed up the solidification effect of the mixture of the abrasive particles and the resin adhesives.
  • In order to improve the mixture effect of the abrasive particles and the resin adhesives, a surface modification process may be performed to the abrasive particles. The abrasive particles include inorganic materials, most of which have hydrophilic surface, and are incompatible with organic polymer. As a result, the abrasive particles are distributed nonuniformly in the resin adhesives and the adhesive force between the abrasive particles and the resin adhesives is weak. The surface modification process for the abrasive particles may be mechanical—chemical modification, such as, high energy ball-milling, stirring-milling, high speed cutting, high frequency ultrasound. The abrasive particles with fresh surfaces after the surface modification process are exposed. Because of a large amount of dangling bond contained in the fresh surface, plus local high temperature during the surface modification process, the abrasive particles react chemically with surface modification agent, thereby achieving surface modification for the abrasive particles.
  • FIG. 6 is a cross-sectional view of a polishing pad according to a second embodiment of the present invention. Referring to FIG. 6, a polishing pad includes a substrate 301 and a plurality of abrasive blocks 302 fixed on the substrate 301. The abrasive blocks 302 are of more than two kinds of heights, which include a first height h1, a second height h2, . . . , a nth height hn (n is a natural number from 3 to 20). The height hn of the abrasive blocks 302 may be ranging from about 10 μm to about 50 μm. A height difference between any two kinds of the abrasive blocks 302 is at least from about 3 μm to about 5 μm. In other words, the absolute value of the difference between the height hn and the height hi (i is not equal to n, and i is a natural number from 3 to 20) is from about 3 μm to about 5 μm. A width W of the abrasive blocks 302 may be from about 50 μm to about 200 μm.
  • In this embodiment, the substrate 301 includes materials as described in the first embodiment. The materials and shapes of the abrasive blocks 302, and the proportion of abrasive particles and resin adhesives are still as described in the first embodiment, which are not described herein.
  • In this embodiment, the abrasive blocks 302 are of more than two kinds of heights. In other words, the heights of the abrasive blocks 302 include a first height h1, a second height h2, . . . , a nth height hn (n is a natural number from 3 to 20). The height of the abrasive blocks 302 may be ranging from about 10 μm to about 50 μm. A height difference between two of the abrasive blocks 302 having different heights is at least from about 3 μm to about 5 μm. The abrasive blocks 302 may be arranged from highest to lowest height, from lowest to highest height, or alternating high and low height on the substrate 301 so as to form a regular topography of abrasive block arrays.
  • In this embodiment, a width W of the abrasive block 302 may be from about 50 μm to about 200 μm. The width W of the abrasive block indicates an average width of a cross-sectional profile of the abrasive block. For example, as for a cylindrical abrasive block, the width W is a diameter of section of the cylinder. As for a trapeziform abrasive block, the width W is a length connecting midpoints at both sides of the trapezium formed by a cross-sectional profile of the trapezoid abrasive block. Similarly, as for a pyramidal abrasive block, the width W is a length connecting midpoints at both sides of the pyramid formed by a cross-sectional profile of the pyramidal abrasive block. The width W of the abrasive blocks aims to ensure a sufficient polishing rate which ranges from about 50 μm to about 200 μm. Preferably, the width may be about 100 μm.
  • In this embodiment, an interval between the abrasive blocks may be from about 50 μm to about 400 μm, preferably, the interval may be about 200 μm, which aims to ensure a chemical solution to flow sufficiently within the abrasive blocks.
  • The polishing pad according to the embodiment of the present invention has a plurality of abrasive block arrays which are of at least two kinds of heights. At the beginning of polishing a wafer, the abrasive block arrays having the first height participate in polishing. With the polishing process going on, the height of the abrasive block arrays which participate in polishing earlier is lowered. The resin adhesives in a next layer of the abrasive blocks having the first height are not dissolved in the polishing slurry, which causes the abrasive particles surrounded by the resin adhesives fail to participate in polishing. Meanwhile, the abrasive block arrays having the second height are soaked in the polishing slurry for some time, so that the abrasive particles may be exposed to participate in polishing. Therefore, the polishing rate may not be reduced, but be kept at a stable level substantially, whereby a thickness of the wafer to be polished is controlled accurately, the quality for polishing the wafer is ensured, and the yield of the wafer is improved.
  • FIG. 7 to FIG. 10 schematic diagrams illustrating a method for manufacturing a polishing pad according to a third embodiment of the present invention. Referring to FIG. 7, a substrate 301 is provided, and coated uniformly with a mixture 3021 comprising a plurality of abrasive particles and resin adhesives.
  • In this embodiment, the substrate 301 may be a rigid substrate, such as a substrate comprising organic glass (PMMA), polyvinyl chloride (PVC), polycarbonate (PC), polyethylene terephathalate (PET), and the like. Optionally, the substrate 301 may be a resilient substrate, which includes polyurethane, polyolefin, phenylethylene, polyester, polyamide, black damping cloth, and the like. Optionally, the substrate 301 may be a multilayer substrate which is formed by combining the rigid substrate with the resilient substrate.
  • In this embodiment, the abrasive particles may include one or more materials selected from silicon dioxide, cerium dioxide, aluminium oxide, silicon carbide, boron carbide, zirconium oxide, adamas, and the like. Preferably, the abrasive particles include cerium dioxide. A particle size of the abrasive particles ranges from about 50 nm to about 1000 nm. Preferably, the particle size is 500 nm. In order to mix the abrasive particles adequately with the resin adhesives, a mechanical—chemical modification process may be performed to the abrasive particles so that the surface of the abrasive particles is of lipophilic property. The mechanical—chemical modification process performed to the abrasive particles may be high energy ball-milling, stirring-milling, high speed cutting, high frequency ultrasound, and the like. The abrasive particles with fresh surface after the surface modification process are exposed. Because of a large amount of dangling bond contained in the fresh surface, and local high temperature during the surface modification process, the abrasive particles react chemically with surface modification agents, thereby achieving surface modification for the abrasive particles which are likely to mix with the resin adhesives.
  • The resin adhesives may include one or more organic resins selected from phenolic resin, urea formaldehyde resin, melamine—formaldehyde resin, acrylic polyurethane, acrylic epoxy resin, ethyleneunion unsaturated compound, vinyl ether, epoxy resin, and the like. The proportion for mixing the abrasive particles and resin adhesives may be configured in accordance with practical use. Optionally, a percentage by weight of the abrasive particles and resin adhesives may be 1:2. As a matter of fact, a curing agent, an initiating agent, or a catalytic agent may be added into the mixture 3021 so as to enhance a molding effect of the abrasive block arrays.
  • Referring to FIG. 8, a molding roller 400 having a pattern 401 of abrasive blocks formed thereon is rolled in a clockwise direction, and compress the mixture 3021 comprising the abrasive particles and resin adhesives fixed on the polishing pad, so as to form an array of regular abrasive blocks 302. The pattern 401 includes a plurality of gravures which may be cylindrical, hemispherical, pyramidal, trapezoidal, and the like, preferably, is trapezoidal. A cross sectional area of the trapezoidal gravure decreases along the depth gradually, whereby the molding roller 400 is easy to be demolded after compression. The topography of the abrasive blocks 302 is determined by the pattern 401.
  • Referring to FIG. 9, the pattern 401 formed on the surface of the molding roller 400 includes a plurality of regular gravures which are of at least two kinds of depths. After the molding roller 400 is rolled, the mixture 3021 comprising the abrasive particles and resin adhesives is compressed to form the abrasive blocks 302 having two kinds of heights corresponding to the two kinds of depths of the pattern 401.
  • In this embodiment, a surface of the molding roller 400 may be coated with a demolding coating, which facilitates the mixture 3021 to peel off the molding roller 400 after compression. In terms of the material of the molding roller 400, the demolding coating may include hard carbide, nitride, boride, silicon resin, fluorochemicals, and the like.
  • Referring to FIG. 10, the abrasive blocks 302 after compression are treated with energy source, so that the abrasive blocks 302 are solidified and fixed on the substrate 301. The energy source includes thermal energy and radiant energy, such as electron beam, ultraviolet light, and the like. Chemical reaction occurs in the resin adhesives in the mixture 3021 by the treatment of the thermal energy or the irradiation of the radiant energy, whereby the abrasive blocks 302 are solidified and fixed on the substrate 301. The molding abrasive blocks 302 are of at least two kinds of heights, which include a first height h1, a second height h2, . . . , a nth height hn (n is a natural number from 2 to 20).
  • In this embodiment, a bottom of each of the abrasive blocks 302 may be connected with each other, or fixed on the substrate 301 separately. Preferably, the bottoms of the abrasive blocks 302 are connected with each other to form the abrasive block arrays. The adhesive force of the abrasive blocks 302 to the substrate 301 is enhanced due to the interconnected bottoms. Therefore, the abrasive blocks are difficult to peel off during the polishing process, which improves the polishing effect.
  • Still a fourth embodiment of the present invention provides a method for using the polishing pad, which includes: step S11, providing a polishing pad which is provided in the above embodiments of the present invention and mounted on a polishing platen; step S12, mounting a wafer on the polishing pad, and adding a polishing slurry to perform polishing.
  • Hereunder, the present invention will be described in detail with reference to the fourth embodiment, in conjunction with the accompanying drawings.
  • In the step S11, a polishing pad having a plurality of abrasive blocks is provided, wherein the abrasive blocks are of at least two kinds of heights.
  • In this embodiment, the abrasive blocks 302 are of at least two kinds of heights. As shown in FIG. 6, the heights of the abrasive blocks 302 include a first height h1, a second height h2, . . . , a nth height hn (n is a natural number from 2 to 20).
  • The height of the abrasive blocks 302 may be ranging from about 10 μm to about 50 μm. A height difference between any two kinds of the abrasive blocks 302 is at least from about 3 μm to about 5 μm. The abrasive blocks 302 may be arranged from highest to lowest height, from lowest to highest height, or alternating high and low height on the substrate 301 so as to form a regular topography of abrasive blocks having different heights.
  • In this embodiment, a polishing pad 102 is transported to a polishing platen 101 by an inputting roller 1051 together with an outputting roller 1052, as shown in FIG. 1.
  • In the step S12, a wafer is mounted on the polishing pad with a polishing slurry added to perform polishing.
  • In this embodiment, because the abrasive blocks 302 fixed on the substrate are of at least two kinds of heights, the polishing rate of the wafer is able to be kept stable during the polishing process. As shown in FIG. 12, a process for polishing the wafer by using the polishing pad having a plurality of abrasive blocks which are of two kinds of heights is described. The polishing pad has a plurality of abrasive blocks (marked with A in FIG. 12) which are of a first height h1, and a plurality of abrasive blocks (marked with B in FIG. 12) which are of a second height h2. The first height h1 is the biggest height. When polishing a wafer 203 by using the polishing pad, the abrasive blocks A which are of the first height h1 contact with a surface of the wafer 203. Because the resin adhesives 2021 at the uppermost layer of the abrasive blocks A are dissolved in the polishing slurry. The abrasive particles 2022 at the uppermost layer are exposed and participate in polishing the wafer 203. With the polishing process going on, the abrasive particles 2022 of the abrasive blocks A having the first height h1 are gradually dissociated from the resin adhesives 2021 by the polishing force, which reduces the height of the abrasive blocks A. When the height is reduced to a certain degree, the resin adhesives 2021 at the next layer have no enough time to dissolve, which causes the abrasive particles 2022 fail to be exposed completely. The polishing efficacy of the abrasive blocks A having the first height h1 is degraded greatly.
  • When the polishing efficacy of the abrasive blocks A having the first height h1 is degraded, the abrasive blocks B having the second height h2 are soaked in the polishing slurry for some time, so that the resin adhesives 2021 at the uppermost layer of the abrasive blocks B are dissolved and the abrasive particles 2022 are exposed. Therefore the abrasive blocks B having the second height h2 are able to participate in polishing the surface of the wafer 203, which keeps the polishing rate stable.
  • The polishing pad according to the present invention ensures a stable polishing efficacy of the abrasive block arrays during a polishing process. Therefore, the polishing rate of the wafer may not be reduced as the polishing process is going on, but be kept at a stable level substantially, whereby a thickness of the wafer to be polished is controlled accurately, the polishing quality of the wafer is ensured, and the yield of the wafer is improved.
  • Although the present invention has been disclosed above with reference to preferred embodiments thereof, it should be understood that the invention is presented by way of example only, and not limitation. Those skilled in the art can modify and vary the embodiments without departing from the spirit and scope of the present invention.

Claims (12)

1. A polishing pad, comprising:
a substrate; and
a plurality of discrete abrasive blocks fixed on the substrate, wherein the plurality of abrasive blocks comprises abrasive blocks of at least two different heights.
2. The polishing pad according to claim 1, wherein each of the different heights of the abrasive blocks is in a range from about 10 μm to about 50 μm.
3. The polishing pad according to claim 1, wherein a height difference between any two different heights of the abrasive blocks is at least from about 3 μm to about 5 μm.
4. The polishing pad according to claim 1, wherein the plurality of abrasive blocks comprise 2 to 20 different heights.
5. The polishing pad according to claim 1, wherein a width of the abrasive blocks is from about 50 μm to about 200 μm.
6. A method for manufacturing a polishing pad, comprising:
preparing a mixture by mixing a plurality of abrasive particles and organic polymers;
coating a substrate with the mixture;
compressing the mixture with a mold so as to form a plurality of discrete abrasive blocks on the substrate, wherein the plurality of abrasive blocks comprise abrasive blocks of at least two different heights, and the mold has a corresponding pattern so as to form the abrasive blocks; and
fixing the discrete abrasive blocks on the substrate.
7. The method according to claim 6, wherein the abrasive particles comprise one or more materials selected from the group consisting of cerium dioxide, silicon dioxide, adamas, zirconium oxide, aluminum oxide, and silicon nitride.
8. The method according to claim 6, wherein the abrasive blocks have 2 to 20 different heights.
9. The method according to claim 6, wherein each of the different heights of the abrasive blocks is in a range from about 10 μm to about 50 μm.
10. The method according to claim 6, wherein the abrasive blocks are arranged in order of height from highest to lowest height or from lowest to highest height, or are arranged alternating high and low height on the substrate.
11. The method according to claim 6, wherein a height difference between any two different heights of the abrasive blocks is at least from about 3 μm to about 5 μm.
12. A method for polishing a wafer with the polishing pad of claim 1, comprising:
providing the polishing pad having a plurality of different heights of abrasive blocks fixed thereon; and
bringing a wafer into contact with the polishing pad; and
adding a polishing slurry to perform polishing.
US13/274,831 2011-01-20 2011-10-17 Polishing pad and methods for manufacturing and using the same Abandoned US20120190276A1 (en)