US20110210441A1 - Chip package - Google Patents
Chip package Download PDFInfo
- Publication number
- US20110210441A1 US20110210441A1 US13/105,866 US201113105866A US2011210441A1 US 20110210441 A1 US20110210441 A1 US 20110210441A1 US 201113105866 A US201113105866 A US 201113105866A US 2011210441 A1 US2011210441 A1 US 2011210441A1
- Authority
- US
- United States
- Prior art keywords
- layer
- metal
- substrate
- tin
- micrometers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims priority to U.S. provisional application No. 60/911,512, filed on Apr. 13, 2007, and to U.S. provisional application No. 60/914,771, filed on Apr. 30, 2007, which are herein incorporated by reference in their entirety.
- 1. Field of the Invention
- The invention relates to a chip package, and, more specifically, to a chip package having fine-pitched metal bumps connected to an external circuit through a flexible circuit film.
- 2. Brief Description of the Related Art
- In the recent years, the development of advanced technology is on the cutting edge. As a result, high-technology electronics manufacturing industries launch more feature-packed and humanized electronic products. These new products that hit the showroom are lighter, thinner, and smaller in design. In the manufacturing of these electronic products, the key component has to be the integrated circuit (IC) chip inside any electronic product.
- It is the objective of the invention to provide a chip package with a semiconductor chip having fine-pitched metal bumps connected to an external circuit through a flexible circuit film.
- In order to reach the above objective, the present invention provides a chip package including a substrate, a flexible circuit film, a first tin-containing joint, a second tin-containing joint, a semiconductor chip, a first metal bump and a second metal bump. The substrate includes multiple insulating layers and multiple metal circuit layers between the insulating layers. The flexible circuit film is over a top surface of the substrate, and the flexible circuit film includes a first polymer layer over the top surface, a first metal trace on the first polymer layer, a second metal trace on the first polymer layer and a second polymer layer on the first and second metal traces. The first tin-containing joint is between the first metal trace and a first pad of the top surface, and the first metal trace is connected to the first pad through the first tin-containing joint. The second tin-containing joint is between the second metal trace and a second pad of the top surface, and the second metal trace is connected to the second pad through the second tin-containing joint. The semiconductor chip is over the flexible circuit film and directly over the top surface. The first metal bump is between the semiconductor chip and the first metal trace, and the second metal bump is between the semiconductor chip and the second metal trace, wherein a pitch between the first and second metal bumps is less than 35 micrometers, such as between 5 and 25 micrometers.
- In order to reach the above objective, the present invention provides a chip package including a substrate, a flexible circuit film, an anisotropic conductive film (ACF), a semiconductor chip, a first metal bump and a second metal bump. The substrate includes a circuit structure in the substrate. The flexible circuit film is over a top surface of the substrate, and the flexible circuit film comprises a first polymer layer over the top surface, a first metal trace on the first polymer layer, a second metal trace on the first polymer layer and a second polymer layer on the first and second metal traces. The anisotropic conductive film is between the first metal trace and a first pad of the top surface, and between the second metal trace and a second pad of the top surface, wherein the first metal trace is connected to the first pad through multiple metal particles in the anisotropic conductive film, and the second metal trace is connected to the second pad through multiple metal particles in the anisotropic conductive film. The semiconductor chip is over the flexible circuit film and directly over the top surface. The first metal bump is between the semiconductor chip and the first metal trace, and the second metal bump is between the semiconductor chip and the second metal trace, wherein a pitch is between the first and second metal bumps is less than 35 micrometers, such as between 5 and 25 micrometers.
- In order to reach the above objective, the present invention provides a chip package including a substrate, a flexible circuit film, a first wireboning wire, a second wireboning wire, a semiconductor chip, a first metal bump and a second metal bump. The substrate includes a circuit structure in the substrate. The flexible circuit film is over a top surface of the substrate, and the flexible circuit film includes a first polymer layer over the top surface, a first metal trace on the first polymer layer, a second metal trace on the first polymer layer and a second polymer layer on the first and second metal traces. The first wireboning wire is connected to a first pad of the top surface and to the first metal trace, and the second wireboning wire is connected to a second pad of the top surface and to the second metal trace. The semiconductor chip is over the flexible circuit film and directly over the top surface. The first metal bump is between the semiconductor chip and the first metal trace, and the second metal bump is between the semiconductor chip and the second metal trace, wherein a pitch between the first and second metal bumps is less than 35 micrometers, such as between 5 and 25 micrometers.
- To enable the objectives, technical contents, characteristics and accomplishments of the present invention, the embodiments of the present invention are to be described in detail in cooperation with the attached drawings below.
-
FIGS. 1 and 2 are cross-sectional views schematically showing semiconductor chips according to the present invention. -
FIGS. 1 a-1 e are cross-sectional views showing a process for forming a semiconductor chip with metal bumps according to the present invention. -
FIGS. 3A-3K are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and joining the flexible circuit film with a rigid substrate according to one embodiment of the present invention. -
FIGS. 3L and 3M are perspective views showing two chip packages each including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 3N-3Q are cross-sectional views showing various chip packages each including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 3R-3X are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a tape-automated-bonding (TAB) technology and joining the flexible circuit film with a rigid substrate according to another embodiment of the present invention. -
FIG. 3Y is a cross-sectional view showing a chip package including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 4A-4C are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and bonding solder balls with the flexible circuit film according to another embodiment of the present invention. -
FIG. 4D is a perspective view showing a chip package including a flexible circuit film bonded with solder balls and a semiconductor chip joined with the flexible circuit film. -
FIGS. 5A-5E are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and bonding solder balls with the flexible circuit film according to another embodiment of the present invention. -
FIGS. 6A-6G are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and joining the flexible circuit film with a rigid substrate according to another embodiment of the present invention. -
FIGS. 6H and 6I are perspective views showing two chip packages each including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 6J-6M are cross-sectional views showing various chip packages each including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 6N-6S are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a tape-automated-bonding (TAB) technology and joining the flexible circuit film with a rigid substrate according to another embodiment of the present invention. -
FIG. 6T is a cross-sectional view showing a chip package including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 7A-7F are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and connecting the flexible circuit film to a rigid substrate using a wirebinding process according to another embodiment of the present invention. -
FIG. 7G is perspective view showing a chip package including a rigid substrate, a flexible circuit film mounted on the rigid substrate and a semiconductor chip joined with the flexible circuit film. -
FIGS. 7H-7M are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a tape-automated-bonding (TAB) technology and connecting the flexible circuit film to a rigid substrate using a wirebinding process according to another embodiment of the present invention. -
FIGS. 8A-8K are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology, bonding an electronic device with the flexible circuit film using a chip-on-film (COF) technology and joining the flexible circuit film with a rigid substrate according to another embodiment of the present invention. -
FIGS. 8I and 8J are perspective views showing two chip packages each including a rigid substrate, a flexible circuit film mounted on the rigid substrate, a semiconductor chip joined with the flexible circuit film and an electronic device joined with the flexible circuit film. -
FIGS. 8K-8T are cross-sectional views showing various chip packages each including a rigid substrate, a flexible circuit film mounted on the rigid substrate, a semiconductor chip joined with the flexible circuit film and an electronic device joined with the flexible circuit film. -
FIGS. 9A-9F are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and joining the flexible circuit film with a lead frame according to another embodiment of the present invention. -
FIGS. 9G and 9J are perspective views showing two chip packages each including a lead frame, a flexible circuit film mounted on the lead frame and a semiconductor chip joined with the flexible circuit film. -
FIGS. 9H-9I and 9K-9M are cross-sectional views showing various chip packages each including a lead frame, a flexible circuit film mounted on the lead frame and a semiconductor chip joined with the flexible circuit film. -
FIGS. 10A-10B are cross-sectional views showing a process for bonding a semiconductor chip with a flexible circuit film using a chip-on-film (COF) technology and joining the flexible circuit film with a lead frame according to another embodiment of the present invention. -
FIG. 10C is a perspective view showing a chip package including a lead frame, a flexible circuit film mounted on the lead frame and a semiconductor chip joined with the flexible circuit film. -
FIGS. 10D-10H are cross-sectional views showing various chip packages each including a lead frame, a flexible circuit film mounted on the lead frame and a semiconductor chip joined with the flexible circuit film. - Referring to
FIG. 1 , asemiconductor chip 2 includes asemiconductor substrate 4,multiple semiconductor devices 6, a metallization structure, multipledielectric layers 8, apassivation layer 10 and multiple metal bumps 12. Thesemiconductor substrate 4 may be a silicon substrate, a GaAs substrate or a SiGe substrate. - The
semiconductor devices 6 are formed in or over thesemiconductor substrate 4. Thesemiconductor devices 6 may comprise a memory cell, a logic circuit, a passive device, such as resistor, capacitor, inductor or filter, or an active device, such as p-channel MOS device, n-channel MOS device, CMOS (Complementary Metal Oxide Semiconductor) device, BJT (Bipolar Junction Transistor) device or BiCMOS (Bipolar CMOS) device. - The metallization structure is formed over the
semiconductor substrate 4, connected to thesemiconductor devices 6. The metallization structure comprises multiple patternedmetal layers 14 having a thickness t1 of less than 3 micrometers (such as between 0.2 and 2 μm) and multiple metal plugs 16. For example, the patternedmetal layers 14 and the metal plugs 16 are principally made of copper, wherein each of the patterned metal layers 14 has a copper-containing layer having a thickness of less than 3 micrometers (such as between 0.2 and 2 μm). Alternatively, the patternedmetal layers 14 are principally made of aluminum or aluminum-alloy, and the metal plugs 16 are principally made of tungsten, wherein each of the patterned metal layers 14 has an aluminum-containing layer having a thickness of less than 3 micrometers (such as between 0.2 and 2 μm). The patternedmetal layers 14 may include multiple metal lines each having a copper layer and an adhesion/barrier layer on the bottom surface and sidewalls of the copper layer, wherein the adhesion/barrier layer may be a tantalum-containing layer, such as tantalum layer or tantalum nitride layer. The patternedmetal layers 14 can be formed by a damascene process including sputtering an adhesion/barrier layer on the bottom of an opening in one of thedielectric layer 8, on the sidewall of the opening and on one of thedielectric layer 8, sputtering a copper seed layer on the adhesion/barrier layer, electroplating a copper bulk layer on the copper seed layer, then removing the copper bulk layer, the copper seed layer and the adhesion/barrier layer outside the opening using a chemical mechanical polishing (CMP) process. - The
dielectric layers 8 are located over thesemiconductor substrate 4 and interposed respectively between the neighboring patternedmetal layers 14, and the neighboring patternedmetal layers 14 are interconnected through the metal plugs 16 inside thedielectric layer 8. Thedielectric layers 8 are commonly formed by a chemical vapor deposition (CVD) process. The material of thedielectric layers 8 may include silicon oxide, silicon oxynitride, TEOS (Tetraethoxysilane), a compound containing silicon, carbon, oxygen and hydrogen (such as SiwCxOyHz), silicon nitride (such as Si3N4), FSG (Fluorinated Silicate Glass), Black Diamond, SiLK, a porous silicon oxide, a porous compound containing nitrogen, silicon carbon nitride (such as SiCN), oxygen and silicon, SOG (Spin-On Glass), BPSG (borophosphosilicate glass), a polyarylene ether, polybenzoxazole (PBO), or a material having a low dielectric constant (K) of between 1.5 and 3, for example. Thedielectric layer 8 between the neighboring patterned metal layers 14 has a thickness t2 of less than 3 micrometers, such as between 0.3 and 3 μm or between 0.3 and 2.5 μm. - The
passivation layer 10 is formed over thesemiconductor devices 6, over the metallization structure (including the metal layers 14 and the metal plugs 16) and over the dielectric layers 8. Thepassivation layer 10 can protect thesemiconductor devices 6 and the metallization structure from being damaged by moisture and foreign ion contamination. In other words, mobile ions (such as sodium ion), transition metals (such as gold, silver and copper) and impurities can be prevented from penetrating through thepassivation layer 10 to thesemiconductor devices 6, such as transistors, polysilicon resistor elements and polysilicon-polysilicon capacitor elements, and to the metallization structure. - The
passivation layer 10 is commonly made of silicon oxide (such as SiO2), PSG (phosphosilicate glass), silicon oxynitride, silicon nitride (such as Si3N4) or silicon carbon nitride (such as SiCN). Thepassivation layer 10 onpads 18 of the metallization structure and on the topmost metal layers 14 of the metallization structure typically has a thickness t3 of more than 0.3 μm, such as between 0.3 and 2 μm or between 0.8 and 1.5 μm. In a preferred case, thepassivation layer 10 includes a topmost silicon nitride layer of thesemiconductor chip 2, wherein the topmost silicon nitride layer in thepassivation layer 10 has a thickness of more than 0.2 μm, such as between 0.3 and 1.2 μm, wherein the passivation layer has first and second portions, and each of the metal bumps 12 shown inFIG. 1 has a metal portion between the first and second portions of thepassivation layer 10 and on thepad 18. Fifteen methods for depositing thepassivation layer 10 are described as below. - In a first method, the
passivation layer 10 is formed by depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm using a CVD method and then depositing a silicon nitride layer with a thickness of 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a second method, the
passivation layer 10 is formed by depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm using a CVD method, next depositing a silicon oxynitride layer with a thickness of between 0.05 and 0.15 μm on the silicon oxide layer using a Plasma Enhanced CVD (PECVD) method, and then depositing a silicon nitride layer with a thickness of between 0.2 and 1.2 μm on the silicon oxynitride layer using a CVD method. - In a third method, the
passivation layer 10 is formed by depositing a silicon oxynitride layer with a thickness of between 0.05 and 0.15 μm using a CVD method, next depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the silicon oxynitride layer using a CVD method, and then depositing a silicon nitride layer with a thickness of between 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a fourth method, the
passivation layer 10 is formed by depositing a first silicon oxide layer with a thickness of between 0.2 and 0.5 μm using a CVD method, next depositing a second silicon oxide layer with a thickness of between 0.5 and 1 μm on the first silicon oxide layer using a spin-coating method, next depositing a third silicon oxide layer with a thickness of between 0.2 and 0.5 μm on the second silicon oxide layer using a CVD method, and then depositing a silicon nitride layer with a thickness of 0.2 and 1.2 μm on the third silicon oxide using a CVD method. - In a fifth method, the
passivation layer 10 is formed by depositing a silicon oxide layer with a thickness of between 0.5 and 2 μm using a High Density Plasma CVD (HDP-CVD) method and then depositing a silicon nitride layer with a thickness of 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a sixth method, the
passivation layer 10 is formed by depositing an Undoped Silicate Glass (USG) layer with a thickness of between 0.2 and 3 μm, next depositing an insulating layer of TEOS, PSG or BPSG (borophosphosilicate glass) with a thickness of between 0.5 and 3 μm on the USG layer, and then depositing a silicon nitride layer with a thickness of 0.2 and 1.2 μm on the insulating layer using a CVD method. - In a seventh method, the
passivation layer 10 is formed by optionally depositing a first silicon oxynitride layer with a thickness of between 0.05 and 0.15 μm using a CVD method, next depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the first silicon oxynitride layer using a CVD method, next optionally depositing a second silicon oxynitride layer with a thickness of between 0.05 and 0.15 μm on the silicon oxide layer using a CVD method, next depositing a silicon nitride layer with a thickness of between 0.2 and 1.2 μm on the second silicon oxynitride layer or on the silicon oxide using a CVD method, next optionally depositing a third silicon oxynitride layer with a thickness of between 0.05 and 0.15 μm on the silicon nitride layer using a CVD method, and then depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the third silicon oxynitride layer or on the silicon nitride layer using a CVD method. - In a eighth method, the
passivation layer 10 is formed by depositing a first silicon oxide layer with a thickness of between 0.2 and 1.2 μm using a CVD method, next depositing a second silicon oxide layer with a thickness of between 0.5 and 1 μm on the first silicon oxide layer using a spin-coating method, next depositing a third silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the second silicon oxide layer using a CVD method, next depositing a silicon nitride layer with a thickness of between 0.2 and 1.2 μm on the third silicon oxide layer using a CVD method, and then depositing a fourth silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the silicon nitride layer using a CVD method. - In a ninth method, the
passivation layer 10 is formed by depositing a first silicon oxide layer with a thickness of between 0.5 and 2 μm using a HDP-CVD method, next depositing a silicon nitride layer with a thickness of between 0.2 and 1.2 μm on the first silicon oxide layer using a CVD method, and then depositing a second silicon oxide layer with a thickness of between 0.5 and 2 μm on the silicon nitride using a HDP-CVD method. - In a tenth method, the
passivation layer 10 is formed by depositing a first silicon nitride layer with a thickness of between 0.2 and 1.2 μm using a CVD method, next depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the first silicon nitride layer using a CVD method, and then depositing a second silicon nitride layer with a thickness of between 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a eleventh method, the
passivation layer 10 is formed by depositing a single layer of silicon nitride with a thickness of between 0.2 and 1.5 μm, and preferably of between 0.3 and 1.2 μm, using a CVD method, by depositing a single layer of silicon oxynitride with a thickness of between 0.2 and 1.5 μm, and preferably of between 0.3 and 1.2 μm, using a CVD method, or by depositing a single layer of silicon carbon nitride with a thickness of between 0.2 and 1.5 μm, and preferably of between 0.3 and 1.2 μm, using a CVD method. - In a twelfth method, the
passivation layer 10 is formed by depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm using a CVD method and then depositing a silicon carbon nitride layer with a thickness of 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a thirteenth method, the
passivation layer 10 is formed by depositing a first silicon carbon nitride layer with a thickness of between 0.2 and 1.2 μm using a CVD method, next depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the first silicon carbon nitride layer using a CVD method, and then depositing a second silicon carbon nitride layer with a thickness of 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a fourteenth method, the
passivation layer 10 is formed by depositing a silicon carbon nitride layer with a thickness of between 0.2 and 1.2 μm using a CVD method, next depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the silicon carbon nitride layer using a CVD method, and then depositing a silicon nitride layer with a thickness of 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. - In a fifteenth method, the
passivation layer 10 is formed by depositing a silicon nitride layer with a thickness of between 0.2 and 1.2 μm using a CVD method, next depositing a silicon oxide layer with a thickness of between 0.2 and 1.2 μm on the silicon nitride layer using a CVD method, and then depositing a silicon carbon nitride layer with a thickness of 0.2 and 1.2 μm on the silicon oxide layer using a CVD method. -
Openings 10 a in thepassivation layer 10 expose thepads 18 of the metallization structure used to input or output signals or to be connected to a power source or a ground reference. The neighboringpads 18 are separated from each other by an insulating material. Thepads 18 are provided by a topmost metal layer under thepassivation layer 10. Each of thepads 18 has a thickness t4 of between 0.5 and 3 μm, and thepads 18 can be connected to thesemiconductor devices 6 through the metal layers 14 and the metal plugs 16. Thepads 18 may be composed of a sputtered aluminum layer or a sputtered aluminum-copper-alloy layer with a thickness of between 0.5 and 3 μm. Alternatively, thepads 18 may include a copper layer with a thickness of between 0.5 and 3 μm, and a barrier layer, such as tantalum or tantalum nitride, on a bottom surface and sidewalls of the copper layer, wherein the copper layer may include electroplated copper. - Therefore, the
pads 18 can be aluminum pads, principally made of sputtered aluminum with a thickness of between 0.5 and 3 μm. Alternatively, thepads 18 can be copper pads, principally made of electroplated copper with a thickness of between 0.5 and 3 μm. - The
openings 10 a may have a transverse dimension, from a top view, of between 0.5 and 20 μm or between 20 and 200 μm. The shape of theopenings 10 a from a top view may be a circle, and the diameter of the circle-shapedopenings 10 a may be between 0.5 and 20 μm or between 20 and 200 μm. Alternatively, the shape of theopenings 10 a from a top view may be a square, and the width of the square-shapedopenings 10 a may be between 0.5 and 20 μm or between 20 and 200 μm. Alternatively, the shape of theopenings 10 a from a top view may be a polygon, such as hexagon or octagon, and the polygon-shapedopenings 10 a may have a width of between 0.5 and 20 μm or between 20 and 200 μm. Alternatively, the shape of theopenings 10 a from a top view may be a rectangle, and the rectangle-shapedopenings 10 a may have a shorter width of between 0.5 and 20 μm or between 20 and 200 μm. - Metal caps (not shown) having a thickness of between 0.4 and 5 μm, and preferably of between 0.4 and 2 μm, can be optionally formed on the
pads 18 exposed by theopenings 10 a in thepassivation layer 10 to prevent thepads 18 from being oxidized or contaminated. The material of the metal caps may include aluminum, an aluminum-copper alloy or an Al—Si—Cu alloy. For example, when thepads 18 are copper pads, the metal caps including aluminum are used to protect thecopper pads 18 from being oxidized. The metal caps may comprise a barrier layer having a thickness of between 0.01 and 0.5 μm on thepads 18. The barrier layer may be made of titanium, titanium nitride, titanium-tungsten alloy, tantalum, tantalum nitride, chromium or nickel. - For example, the metal caps may include a tantalum-containing layer, such as tantalum layer or tantalum-nitride layer, having a thickness of between 0.01 and 0.5 μm on the
pads 18, principally made of electroplated copper, exposed by the opening 10 a, and an aluminum-containing layer, such as aluminum layer or aluminum-copper-alloy layer, having a thickness of between 0.4 and 3 μm on the tantalum-containing layer. - The metal bumps 12 can be formed, respectively, on the
pads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a, and a pitch P1 between the neighboring metal bumps 12 is greater than 5 micrometers or less than 35 micrometers, such as between 15 and 35 micrometers, between 10 and 30 micrometers or between 5 and 20 micrometers. The metal bumps 12 can be formed of an adhesion/barrier layer having a thickness of between 0.03 and 0.7 μm, and preferably of between 0.25 and 0.35 μm, on thepads 18 exposed by theopenings 10 a and a metal layer having a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, on the adhesion/barrier layer. The adhesion/barrier layer may be titanium, a titanium-tungsten alloy, titanium nitride, chromium, tantalum, tantalum nitride or a composite of the above-mentioned materials, and the adhesion/barrier layer can be formed by a physical vapor deposition (PVD) process, such as a sputtering process or an evaporation process. The metal layer may be gold, copper, silver, nickel, palladium, tin or a composite of the above-mentioned materials, and the metal layer may be formed by a process including a sputtering process, an electroplating process or an electroless plating process. Below, the process of forming the metal bumps 12 is exemplified with the case of forming the metal bumps 12 on thepads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a. Alternatively, the metal bumps 12 can be formed on the metal caps, such as aluminum caps, wherein the metal caps are formed on thepads 18, such as copper pads, exposed by theopenings 10 a. -
FIGS. 1 a-1 e are schematically cross-sectional figures showing a process of forming the metal bumps 12 on asemiconductor wafer 20. The above-mentionedsemiconductor chip 2 is cut from thesemiconductor wafer 20. Before cutting thesemiconductor wafer 20, the metal bumps 12 are formed on thesemiconductor wafer 20. - Referring to
FIG. 1 a, an adhesion/barrier layer 22 having a thickness t5 of between 0.01 and 0.7 μm, and preferably of between 0.03 and 0.7 μm, can be formed on thepassivation layer 10 and on thepads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a. The adhesion/barrier layer 22 can be formed by a physical vapor deposition (PVD) process, such as a sputtering process or an evaporation process. The material of the adhesion/barrier layer 22 may be titanium, a titanium-tungsten alloy, titanium nitride, chromium, tantalum, tantalum nitride or a composite of the above-mentioned materials. In a case, the adhesion/barrier layer 22 can be formed by sputtering a titanium-tungsten-alloy layer with a thickness of between 0.03 and 0.7 μm, and preferably of between 0.15 and 0.4 μm, on thepassivation layer 10 and on thepads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a. In another case, the adhesion/barrier layer 22 can be formed by sputtering a titanium layer with a thickness of between 0.01 and 0.7 μm, and preferably of between 0.01 and 0.15 μm, on thepassivation layer 10 and on thepads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a. In another case, the adhesion/barrier layer 22 can be formed by sputtering a titanium-nitride layer with a thickness of between 0.01 and 0.1 μm, and preferably of between 0.01 and 0.02 μm, on thepassivation layer 10 and on thepads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a. In another case, the adhesion/barrier layer 22 can be formed by sputtering a titanium layer with a thickness of between 0.01 and 0.15 μm on thepassivation layer 10 and on thepads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a, and then sputtering a titanium-tungsten-alloy layer with a thickness of between 0.1 and 0.35 μm on the titanium layer. The adhesion/barrier layer 22 is used to prevent the occurrence of interdiffusion between metal layers and to provide good adhesion between the metal layers. - Next, a
seed layer 24 having a thickness t6 of between 0.03 and 1 μm, and preferably of between 0.05 and 0.2 μm, can be formed on the adhesion/barrier layer 22. Theseed layer 24 can be formed by a physical vapor deposition (PVD) process, such as a sputtering process or an evaporation process. Theseed layer 24 is beneficial to electroplating a metal layer thereon. - For example, when the adhesion/
barrier layer 22 is formed by sputtering a titanium-containing layer, theseed layer 24 can be formed by sputtering a gold layer with a thickness of between 0.03 and 1 μm, and preferably of between 0.05 and 0.2 μm, on the titanium-containing layer. When the adhesion/barrier layer 22 is formed by sputtering a titanium-containing layer, theseed layer 24 can be formed by sputtering a copper layer with a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer. The above-mentioned titanium-containing layer can be a single titanium-tungsten-alloy layer having a thickness of between 0.03 and 0.7 μm, and preferably of between 0.15 and 0.4 μm, a single titanium layer having a thickness of between 0.01 and 0.7 μm, and preferably of between 0.01 and 0.15 μm, a single titanium-nitride layer having a thickness of between 0.01 and 0.1 μm, and preferably of between 0.01 and 0.02 μm, or a composite layer comprising a titanium layer having a thickness of between 0.01 and 0.15 μm, and a titanium-tungsten-alloy layer, having a thickness of between 0.1 and 0.35 μm, on the titanium layer. - Referring to
FIG. 1 b, aphotoresist layer 26, such as positive-type photoresist layer or negative-type photoresist layer, having a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, is spin-on coated on theseed layer 24. Next, thephotoresist layer 26 is patterned with the processes of exposure and development to formopenings 26 a in thephotoresist layer 26 exposing theseed layer 24. A 1X stepper or 1X contact aligner can be used to expose thephotoresist layer 26 during the process of exposure. - For example, the
photoresist layer 26 can be formed by spin-on coating a positive-type photosensitive polymer layer having a thickness of between 5 and 50 μm, and preferably of between 15 and 20 μm, on theseed layer 24, then exposing the photosensitive polymer layer using a 1X stepper or contact aligner with at least two of G-line, H-line and I-line, wherein G-line has a wavelength ranging from 434 to 438 nm, H-line has a wavelength ranging from 403 to 407 nm, and I-line has a wavelength ranging from 363 to 367 nm, then developing the exposed polymer layer by spraying and puddling a developer on a wafer or by immersing a wafer into a developer, and then cleaning the wafer using deionized wafer and drying the wafer by sprining the wafer. After development, a scum removal process of removing the residual polymeric material or other contaminants from theseed layer 24 may be conducted by using an O2 plasma or a plasma containing fluorine of below 200 PPM and oxygen. By these processes, thephotoresist layer 26 can be patterned with theopenings 26 a in thephotoresist layer 26 exposing theseed layer 24. - Referring to
FIG. 1 c, ametal layer 28 having a thickness t7 of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, can be electroplated and/or electroless plated on theseed layer 24 exposed by theopenings 26 a. The material of themetal layer 28 may be gold, copper, nickel, silver, tin, palladium or a composite of the above-mentioned materials. - For example, the
metal layer 28 may be formed by electroplating a gold layer with a thickness of between 5 and 50 μm, and preferably of between 10 and 25 micrometers, on theseed layer 24, made of gold, exposed by the opening 26 a with a non-cyanide electroplating solution, such as a solution containing gold sodium sulfite (Na3Au(SO3)2) or a solution containing gold ammonium sulfite ((NH4)3[Au(SO3)2]), or with an electroplating solution containing cyanide. Alternatively, themetal layer 28 may be formed by electroplating a copper layer having a thickness of between 0.5 and 45 μm, and preferably of between 5 and 35 micrometers, on theseed layer 24, made of copper, exposed by the opening 26 a, then electroplating a nickel layer having a thickness of between 0.5 and 5 μm, and preferably of between 1 and 3 micrometers, on the copper layer in theopening 26 a, and then electroplating a gold layer having a thickness of between 0.5 and 5 μm, and preferably of between 1 and 3 micrometers, on the nickel layer in theopening 26 a with a non-cyanide electroplating solution, such as a solution containing gold sodium sulfite (Na3Au(SO3)2) or a solution containing gold ammonium sulfite ((NH4)3[Au(SO3)2]), or with an electroplating solution containing cyanide. Alternatively, themetal layer 28 may be formed by electroplating a copper layer having a thickness of between 0.5 and 45 μm, and preferably of between 5 and 35 micrometers, on theseed layer 24, made of copper, exposed by the opening 26 a, and then electroplating a gold layer having a thickness of between 0.5 and 5 μm, and preferably of between 1 and 3 micrometers, on the copper layer in theopening 26 a with a non-cyanide electroplating solution, such as a solution containing gold sodium sulfite (Na3Au(SO3)2) or a solution containing gold ammonium sulfite ((NH4)3[Au(SO3)2]), or with an electroplating solution containing cyanide. Alternatively, themetal layer 28 may be formed by electroplating a nickel layer having a thickness of between 0.5 and 45 μm, and preferably of between 5 and 35 micrometers, on theseed layer 24, made of copper, exposed by the opening 26 a, and then electroplating a gold layer having a thickness of between 0.5 and 5 μm, and preferably of between 1 and 3 micrometers, on the nickel layer in theopening 26 a with a non-cyanide electroplating solution, such as a solution containing gold sodium sulfite (Na3Au(SO3)2) or a solution containing gold ammonium sulfite ((NH4)3[Au(SO3)2]), or with an electroplating solution containing cyanide. - Referring to
FIG. 1 d, after themetal layer 28 is formed, most of thephotoresist layer 26 can be removed using an organic solution with amide or a solution containing H2SO4 and H2O2. However, some residuals from thephotoresist layer 26 could remain on themetal layer 28 and on theseed layer 24. Thereafter, the residuals can be removed from themetal layer 28 and from theseed layer 24 with a plasma, such as O2 plasma or plasma containing fluorine of below 200 PPM and oxygen. - Referring to
FIG. 1 e, theseed layer 24 and the adhesion/barrier layer 22 not under themetal layer 28 are subsequently removed with a wet etching method or a dry etching method. The dry etching method may be an Ar sputtering etching process or a reactive ion etching (RIE) process. As to the wet etching method, when theseed layer 24 is a gold layer, it can be etched with an iodine-containing solution, such as solution containing potassium iodide; when the seed layer 24 a copper layer, it can be etched with a solution containing NH4OH or with a solution containing H2SO4; when the adhesion/barrier layer 22 is a titanium-tungsten-alloy layer, it can be etched with a solution containing hydrogen peroxide or with a solution containing NH4OH and hydrogen peroxide; when the adhesion/barrier layer 22 is a titanium layer, it can be etched with a solution containing hydrogen fluoride or with a solution containing NH4OH and hydrogen peroxide; when the adhesion/barrier layer 22 is a chromium layer, it can be etched with a solution containing potassium ferricyanide. - Thereby, in the present invention, the metal bumps 12 can be formed, respectively, on the
pads 18, such as aluminum pads or copper pads, exposed by theopenings 10 a, and the pitch P1 between the neighboring metal bumps 12 is greater than 5 micrometers or less than 35 micrometers, such as between 15 and 35 micrometers, between 10 and 30 micrometers or between 5 and 20 micrometers. The metal bumps 12 can be formed of the adhesion/barrier layer 22 on thepads 18 and a bump metal layer (including theseed layer 24 and themetal layer 28 on the seed layer 24), having a thickness of between 5 and 30 micrometers, and preferably of between 10 and 25 micrometers, on the adhesion/barrier layer 22. - In a case, the metal bumps 12 may include a titanium-containing layer on the
pads 18 exposed by theopenings 10 a, and a gold layer having a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, on the titanium-containing layer. In another case, the metal bumps 12 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the titanium-containing layer, a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer. In another case, the metal bumps 12 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the titanium-containing layer, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer. In another case, the metal bumps 12 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer, formed by a sputtering process, having a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer, a nickel layer, formed by an electroplating process, having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the copper layer, and a gold layer, formed by an electroplating process, having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer. The above-mentioned titanium-containing layer can be a single titanium-tungsten-alloy layer having a thickness of between 0.03 and 0.7 μm, and preferably of between 0.15 and 0.4 μm, a single titanium layer having a thickness of between 0.01 and 0.7 μm, and preferably of between 0.01 and 0.15 μm, a single titanium-nitride layer having a thickness of between 0.01 and 0.1 μm, and preferably of between 0.01 and 0.02 μm, or a composite layer comprising a titanium layer having a thickness of between 0.01 and 0.15 μm on thepads 18 exposed by theopenings 10 a, and a titanium-tungsten-alloy layer having a thickness of between 0.1 and 0.35 μm on the titanium layer. - Multiple undercuts 29 may be formed under the
seed layer 24 and under themetal layer 28 when the adhesion/barrier layer 22 not under themetal layer 28 is removed using a wet etching method. The adhesion/barrier layer 22 under themetal layer 28 has a first sidewall recessed from a second sidewall of theseed layer 24, wherein a distance D between the first sidewall and the second sidewall is between 0.3 and 2 micrometers. - However, the
undercuts 29 could result in the dramatical drop of the contact area between themetal bump 12, especially fine pitch metal bump, and thepassivation layer 10. For avoiding theundesired undercuts 29, the adhesion/barrier layer 22 not under themetal layer 28 can be alternatively removed using the above-mentioned dry etching method. - After the metal bumps 12 are formed, the
semiconductor wafer 20 can be cut into thesemiconductor chips 2 by a mechanical cutting process. The fine-pitchedmetal bumps 12 are formed on thepads 18, of each semiconductor chips 2, exposed by theopenings 10 a. - Referring to
FIG. 2 , alternatively, thesemiconductor chip 2 cut from the semiconductor wafer includes thesemiconductor substrate 4, thesemiconductor devices 6, the metallization structure (including the patternedmetal layers 14 and the metal plugs 16), thedielectric layers 8, thepassivation layer 10, apolymer layer 30, multiple metal traces 32, the metal bumps 12 and apolymer layer 34. The specification of thesemiconductor substrate 4, thesemiconductor devices 6, the metallization structure (including the patternedmetal layers 14 and the metal plugs 16), thedielectric layers 8 and thepassivation layer 10 shown inFIG. 2 can be referred to as the specification of thesemiconductor substrate 4, thesemiconductor devices 6, the metallization structure (including the patternedmetal layers 14 and the metal plugs 16), thedielectric layers 8 and thepassivation layer 10 illustrated inFIG. 1 . The process, of forming the metallization structure (including the patternedmetal layers 14 and the metal plugs 16), thedielectric layers 8 and thepassivation layer 10, as shown inFIG. 2 can be referred to as the process, of forming the metallization structure (including the patternedmetal layers 14 and the metal plugs 16), thedielectric layers 8 and thepassivation layer 10, as illustrated inFIG. 1 . - The
polymer layer 30 having a thickness t8 of between 3 and 25 μm can be formed on thepassivation layer 10 by a process including a spin-on coating process, a lamination process or a screen-printing process. The material of thepolymer layer 30 may include benzocyclobutane (BCB), polyimide (PT), polybenzoxazole (PBO) or epoxy resin. - For example, the polymer layer 30 can be formed by spin-on coating a negative-type photosensitive polyimide layer having a thickness of between 6 and 50 μm on the passivation layer 10 and on the pads 18 exposed by the openings 10 a, then baking the spin-on coated polyimide layer, then exposing the baked polyimide layer using a 1X stepper or 1X contact aligner with at least two of G-line having a wavelength ranging from 434 to 438 nm, H-line having a wavelength ranging from 403 to 407 nm, and I-line having a wavelength ranging from 363 to 367 nm, illuminating the baked polyimide layer, that is, G-line and H-line, G-line and I-line, H-line and I-line, or G-line, H-line and I-line illuminate the baked polyimide layer, then developing the exposed polyimide layer to form a patterned polyimide layer on the passivation layer 10, then curing or heating the patterned polyimide layer at a peak temperature of between 180 and 400° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient, the cured polyimide layer having a thickness of between 3 and 25 μm, and then removing the residual polymeric material or other contaminants from the upper surface of the pads 18 with an O2 plasma or a plasma containing fluorine of below 200 PPM and oxygen, such that the polymer layer 30 can be formed on the passivation layer 10. For example, the patterned polyimide layer can be cured or heated at a temperature between 180 and 250° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient. Alternatively, the patterned polyimide layer can be cured or heated at a temperature between 250 and 290° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient. Alternatively, the patterned polyimide layer can be cured or heated at a temperature between 290 and 400° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient. Alternatively, the patterned polyimide layer can be cured or heated at a temperature between 250 and 400° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient.
- Alternatively, the polymer layer 30 can be formed by spin-on coating a positive-type photosensitive polybenzoxazole layer having a thickness of between 3 and 25 μm on the passivation layer 10 and on the pads 18 exposed by the openings 10 a, then baking the spin-on coated polybenzoxazole layer, then exposing the baked polybenzoxazole layer using a 1X stepper or 1X contact aligner with at least two of G-line having a wavelength ranging from 434 to 438 nm, H-line having a wavelength ranging from 403 to 407 nm, and I-line having a wavelength ranging from 363 to 367 nm, illuminating the baked polyimide layer, that is, G-line and H-line, G-line and I-line, H-line and I-line, or G-line, H-line and I-line illuminate the baked polybenzoxazole layer, then developing the exposed polybenzoxazole layer to form a patterned polybenzoxazole layer on the passivation layer 10, then curing or heating the patterned polybenzoxazole layer at a peak temperature of between 150 and 250° C., and preferably of between 180 and 250° C., for a time of between 5 and 180 minutes, and preferably of between 30 and 120 minutes, in a nitrogen ambient or in an oxygen-free ambient, the cured polybenzoxazole layer having a thickness of between 3 and 25 μm, and then removing the residual polymeric material or other contaminants from the upper surface of the pads 18 with an O2 plasma or a plasma containing fluorine of below 200 PPM and oxygen, such that the polymer layer 30 can be formed on the passivation layer 10. Alternatively, the patterned polybenzoxazole layer can be cured or heated at a temperature between 200 and 400° C., and preferably of between 250 and 350° C., for a time of between 5 and 180 minutes, and preferably of between 30 and 120 minutes, in a nitrogen ambient or in an oxygen-free ambient.
- Each of the metal traces 32 having a thickness t9 of between 1 and 30 micrometers, and preferably of between 5 and 20 micrometers, can be formed on the
passivation layer 10, on thepolymer layer 30 and on thepads 18 exposed by theopenings 10 a, wherein themetal trace 32 may connect one of thepads 18 to another one of thepads 18. The metal traces 32 may include titanium, a titanium-tungsten alloy, titanium nitride, chromium, tantalum, tantalum nitride, gold, copper, nickel or a composite of the above-mentioned materials, and the metal traces 32 may be formed by a process including a sputtering process, an electroplating process or an electroless plating process. - In a case, the metal traces 32 may include a titanium-containing layer on the
pads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, and a gold layer having a thickness of between 1 and 30 micrometers, and preferably of between 5 and 20 micrometers, on the titanium-containing layer. In another case, the metal traces 32 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, and a copper layer having a thickness of between 1 and 30 micrometers, and preferably of between 5 and 20 micrometers, on the titanium-containing layer. In another case, the metal traces 32 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, and a nickel layer having a thickness of between 1 and 30 micrometers, and preferably of between 5 and 20 micrometers, on the titanium-containing layer. In another case, the metal traces 32 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, a copper layer having a thickness of between 1 and 25 micrometers, and preferably of between 3 and 15 micrometers, on the titanium-tungsten-alloy layer, a nickel layer having a thickness of between 0.5 and 2.5 micrometers, and preferably of between 1 and 2.5 micrometers, on the copper layer, and a gold layer having a thickness of between 0.5 and 2.5 micrometers, and preferably of between 1 and 2.5 micrometers, on the nickel layer. In another case, the metal traces 32 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, a copper layer having a thickness of between 1 and 25 μm, and preferably of between 3 and 15 micrometers, on the titanium-containing layer, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 2 and 5 micrometers, on the copper layer. In another case, the metal traces 32 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, a copper layer, formed by a sputtering process, having a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer, a nickel layer, formed by an electroplating process, having a thickness of between 0.5 and 25 micrometers, and preferably of between 3 and 15 micrometers, on the sputtered copper layer, and a gold layer, formed by an electroplating process, having a thickness of between 0.5 and 5 micrometers, and preferably of between 2 and 5 micrometers, on the nickel layer. In another case, the metal traces 32 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, on thepassivation layer 10 and on thepolymer layer 30, a copper layer, formed by a sputtering process, having a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer, and a nickel layer, formed by an electroplating process, having a thickness of between 0.5 and 25 micrometers, and preferably of between 3 and 15 micrometers, on the sputtered copper layer. The above-mentioned titanium-containing layer can be a single titanium-tungsten-alloy layer having a thickness of between 0.03 and 0.7 μm, and preferably of between 0.15 and 0.4 μm, a single titanium layer having a thickness of between 0.01 and 0.7 μm, and preferably of between 0.01 and 0.15 μm, a single titanium-nitride layer having a thickness of between 0.01 and 0.1 μm, and preferably of between 0.01 and 0.02 μm, or a composite layer comprising a titanium layer having a thickness of between 0.01 and 0.15 μm, and a titanium-tungsten-alloy layer, having a thickness of between 0.1 and 0.35 μm, on the titanium layer. - The
polymer layer 34 having a thickness t10 of between 1 and 25 μm can be formed on thepassivation layer 10, on the metal traces 32 and on thepolymer layer 30 by a process including a spin-on coating process, a lamination process or a screen-printing process. Thepolymer layer 34 uncovers the metal bumps 12 on the metal traces 32, withopenings 34 a in thepolymer layer 34 being over the metal traces 32 having the metal bumps 12 formed thereon. The material of thepolymer layer 34 may include benzocyclobutane (BCB), polyimide (PI), polybenzoxazole (PBO) or epoxy resin. - For example, the polymer layer 34 can be formed by spin-on coating a negative-type photosensitive polyimide layer having a thickness of between 2 and 50 μm on the passivation layer 10, on the metal traces 32, on the metal bumps 12 and on the polymer layer 30, then baking the spin-on coated polyimide layer, then exposing the baked polyimide layer using a 1X stepper or 1X contact aligner with at least two of G-line having a wavelength ranging from 434 to 438 nm, H-line having a wavelength ranging from 403 to 407 nm, and I-line having a wavelength ranging from 363 to 367 nm, illuminating the baked polyimide layer, that is, G-line and H-line, G-line and I-line, H-line and I-line, or G-line, H-line and I-line illuminate the baked polyimide layer, then developing the exposed polyimide layer to uncover the metal bumps 12, then curing or heating the developed polyimide layer at a peak temperature of between 180 and 400° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient, the cured polyimide layer having a thickness of between 3 and 25 μm, and then removing the residual polymeric material or other contaminants from the upper surface of the metal bumps 12 and from the upper surface of the metal traces 32 with an O2 plasma or a plasma containing fluorine of below 200 PPM and oxygen, such that the polymer layer 34 can be formed on the passivation layer 10, on the metal traces 32 and on the polymer layer 30, uncovering the metal bumps 12. For example, the developed polyimide layer can be cured or heated at a temperature between 180 and 250° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient. Alternatively, the developed polyimide layer can be cured or heated at a temperature between 250 and 290° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient. Alternatively, the developed polyimide layer can be cured or heated at a temperature between 290 and 400° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient. Alternatively, the developed polyimide layer can be cured or heated at a temperature between 250 and 400° C. for a time of between 20 and 150 minutes in a nitrogen ambient or in an oxygen-free ambient.
- Alternatively, the polymer layer 34 can be formed by spin-on coating a positive-type photosensitive polybenzoxazole layer having a thickness of between 3 and 25 μm on the passivation layer 10, on the metal traces 32 and on the polymer layer 30, then baking the spin-on coated polybenzoxazole layer, then exposing the baked polybenzoxazole layer using a 1X stepper or 1X contact aligner with at least two of G-line having a wavelength ranging from 434 to 438 nm, H-line having a wavelength ranging from 403 to 407 nm, and I-line having a wavelength ranging from 363 to 367 nm, illuminating the baked polyimide layer, that is, G-line and H-line, G-line and I-line, H-line and I-line, or G-line, H-line and I-line illuminate the baked polybenzoxazole layer, then developing the exposed polybenzoxazole layer to uncover the metal bumps 12, then curing or heating the developed polybenzoxazole layer at a peak temperature of between 200 and 400° C., and preferably of between 250 and 350° C., for a time of between 5 and 180 minutes, and preferably of between 30 and 120 minutes, in a nitrogen ambient or in an oxygen-free ambient, the cured polybenzoxazole layer having a thickness of between 3 and 25 μm, and then removing the residual polymeric material or other contaminants from the upper surface of the metal bumps 12 and from the upper surface of the metal traces 32 with an O2 plasma or a plasma containing fluorine of below 200 PPM and oxygen, such that the polymer layer 34 can be formed on the passivation layer 10, on the metal traces 32 and on the polymer layer 30, uncovering the metal bumps 12.
- The metal bumps 12 are on the metal traces 32 exposed by the
openings 34 a, and the pitch P2 between the neighboring metal bumps 12 is greater than 5 micrometers or less than 35 micrometers, such as between 15 and 35 micrometers, between 10 and 30 micrometers or between 5 and 20 micrometers. The metal bumps 12 may include titanium, a titanium-tungsten alloy, titanium nitride, chromium, tantalum, tantalum nitride, gold, copper, silver, nickel, palladium, tin or a composite of the above-mentioned materials, and the metal bumps 12 may be formed by a process including a sputtering process, an electroplating process or an electroless plating process. - For example, the specification of the metal bumps 12 shown in
FIG. 2 can be referred to as the specification of the metal bumps 12 illustrated inFIG. 1 andFIGS. 1 a-1 e. Alternatively, the metal bumps 12 can be formed by electroplating a gold layer with a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, directly on the gold layer of the metal traces 32, directly on the copper layer of the metal traces 32 or directly on the nickel layer of metal traces 32. Alternatively, the metal bumps 12 can be formed by electroplating a copper layer with a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, directly on the gold layer of the metal traces 32, directly on the copper layer of the metal traces 32 or directly on the nickel layer of metal traces 32. Alternatively, the metal bumps 12 can be formed by electroplating a copper layer with a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, directly on the gold layer of the metal traces 32, directly on the copper layer of the metal traces 32 or directly on the nickel layer of metal traces 32, and then electroplating a gold layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the electroplated copper layer. Alternatively, the metal bumps 12 can be formed by electroplating a copper layer with a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, directly on the gold layer of the metal traces 32, directly on the copper layer of the metal traces 32 or directly on the nickel layer of metal traces 32, then electroplating a nickel layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the electroplated copper layer, and then electroplating a gold layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the electroplated nickel layer. - The above-mentioned
metal bumps 12 of thesemiconductor chip 2 can be joined with any one of variousflexible circuit films -
FIG. 3A is a schematically cross-sectional figure showing a chip-on-film (COF) package. Aflexible circuit film 36 includes apolymer layer 200, apolymer layer 220 and multiple copper traces 210 between the polymer layers 200 and 220, whereinopenings 200 a in thepolymer layer 200 expose first contact points of the copper traces 210 andopenings 220 a in thepolymer layer 220 expose second contact points of the copper traces 210. Each of the copper traces 210 has a thickness t11 of between 3 and 30 micrometers, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The
polymer layer 200 has a thickness t13 of between 10 and 100 micrometers, of between 15 and 30 micrometers or of between 20 and 80 micrometers, and the material of thepolymer layer 200 may be polybenzoxazole, expoxy, polyester or polyimide. Thepolymer layer 220 has a thickness t14 of between 5 and 30 micrometers, and preferably of between 5 and 15 micrometers, and the material of thepolymer layer 220 may be polybenzoxazole, expoxy, polyester or polyimide. - The
flexible circuit film 36 further comprises awetting layer 240 a on the first contact points of the copper traces 210 exposed by theopenings 200 a, and awetting layer 240 b on the second contact points of the copper traces 210 exposed by theopenings 220 a to be joined with the metal bumps 12 preformed on themetal pads 18 or on the metal traces 32 of thesemiconductor chip 2 shown inFIG. 1 or 2. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210 of theflexible circuit film 36 exposed by theopenings 220 a through aninterface bonding layer 250. Two methods for bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 36 are described as shown inFIG. 3B andFIG. 3C . - Referring to
FIGS. 3B and 3C , theflexible circuit film 36 can be connected to thesemiconductor chip 2. Theflexible circuit film 36 has thewetting layer 240 a to be joined with asubstrate 300 shown inFIG. 3E , and thewetting layer 240 b to be joined with the metal bumps 12 preformed on themetal pads 18 or on the metal traces 32 of thesemiconductor chip 2 shown inFIG. 1 or 2. Thewetting layer 240 a having a thickness of between 0.05 and 5 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, nickel, silver, palladium, tin or a composite of the above-mentioned materials. For example, thewetting layer 240 a may be a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, having a thickness of between 0.05 and 5 micrometers, and preferably of between 0.1 and 1 micrometer, directly on the first contact points of the copper traces 210. Alternatively, thewetting layer 240 a may be a gold layer having a thickness of between 0.05 and 5 micrometers, and preferably of between 0.1 and 1 micrometer, directly on the first contact points of the copper traces 210; optionally, a nickel layer having a thickness between 0.05 and 1 micrometer may be between the copper traces 210 and the gold layer. Thewetting layer 240 b having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, nickel, silver, palladium, tin or a composite of the above-mentioned materials. For example, thewetting layer 240 b may be a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, directly on the second contact points of the copper traces 210. Alternatively, thewetting layer 240 b may be a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, directly on the second contact points of the copper traces 210; optionally, a nickel layer having a thickness between 0.05 and 1 micrometer may be between the copper traces 210 and the gold layer. - In a first case, referring to
FIG. 3B , the metal bumps 12 have the above-mentioned gold layer, at the tips of the metal bumps 12, capable of being used to be joined with thewetting layer 240 b of pure tin or an above-mentioned tin alloy using gang bonding, which process is described as below. First, thesemiconductor chip 2 is held by vacuum adsorption on astage 600 kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C. Next, theflexible circuit film 36 is thermally pressed on the metal bumps 12 of thesemiconductor chip 2 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by atool head 610 kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 36, to join thewetting layer 240 b with the metal bumps 12. Referring toFIGS. 3A and 3B , in the step of joining thewetting layer 240 b with the metal bumps 12, theinterface bonding layer 250, such as a metal alloy, may be formed between the metal bumps 12 and the copper traces 210. Theinterface bonding layer 250 has a thickness t12 of between 0.2 and 10 micrometers, and preferably of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is pure tin, theinterface bonding layer 250 is a tin-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers, wherein an atomic ratio of tin to gold in the tin-gold alloy is between 0.2 and 0.3. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-silver-copper alloy, theinterface bonding layer 250 is a tin-silver-gold-copper alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-silver alloy, theinterface bonding layer 250 is a tin-silver-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-lead alloy, theinterface bonding layer 250 is a tin-lead-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. Next, thetool head 610 is removed from theflexible circuit film 36. Next, thesemiconductor chip 2 bonded with theflexible circuit film 36 is removed from thestage 600. - The metal bumps 12 bonded with the copper traces 210 of the
flexible circuit film 36 have a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers. For example, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, and a gold layer having a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, and a copper layer having a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250, a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and theinterface bonding layer 250, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer and between the nickel layer and theinterface bonding layer 250. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250, and a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and theinterface bonding layer 250. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and theinterface bonding layer 250. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer, formed by a sputtering process, having a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250, a nickel layer, formed by an electroplating process, having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the sputtered copper layer and between the sputtered copper layer and theinterface bonding layer 250, and a gold layer, formed by an electroplating process, having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer and between the nickel layer and theinterface bonding layer 250. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer, formed by a sputtering process, having a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer and between the titanium-containing layer and theinterface bonding layer 250, and a nickel layer, formed by an electroplating process, having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the sputtered copper layer and between the sputtered copper layer and theinterface bonding layer 250. The above-mentioned titanium-containing layer can be a single titanium-tungsten-alloy layer having a thickness of between 0.03 and 0.7 μm, and preferably of between 0.15 and 0.4 μm, a single titanium layer having a thickness of between 0.01 and 0.7 μm, and preferably of between 0.01 and 0.15 μm, a single titanium-nitride layer having a thickness of between 0.01 and 0.1 μm, and preferably of between 0.01 and 0.02 μm, or a composite layer comprising a titanium layer having a thickness of between 0.01 and 0.15 μm, and a titanium-tungsten-alloy layer, having a thickness of between 0.1 and 0.35 μm, on the titanium layer. - In a second case, referring to
FIG. 3B , the metal bumps 12 have the above-mentioned gold layer, at the tips of the metal bumps 12, capable of being used to be joined with a gold layer of thewetting layer 240 b using gang bonding, which process is described as below. First, thesemiconductor chip 2 is held by vacuum adsorption on thestage 600 kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C. Next, theflexible circuit film 36 is thermally pressed on the metal bumps 12 of thesemiconductor chip 2 at a force of between 20 and 150N, and preferably of between 70 and 120N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 36, to join the gold layer of thewetting layer 240 b with the above-mentioned gold layer of the metal bumps 12. Next, thetool head 610 is removed from theflexible circuit film 36. Next, thesemiconductor chip 2 bonded with theflexible circuit film 36 is removed from thestage 600. - Thereby, the
pads 18 of thesemiconductor chip 2 can be connected to the copper traces 210 of theflexible circuit film 36 through gold joints formed by joining the gold layer of thewetting layer 240 b with the above-mentioned gold layer of the metal bumps 12. For example, the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, and a gold joint having a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers on the titanium-containing layer and between the titanium-containing layer and the copper traces 210. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the titanium-containing layer and between the titanium-containing layer and the copper traces 210, a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and the copper traces 210, and a gold joint having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer and between the nickel layer and the copper traces 210. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 μm, on the titanium-containing layer and between the titanium-containing layer and the copper traces 210, and a gold joint having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and the copper traces 210. Alternatively, the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 may include a titanium-containing layer on thepads 18 exposed by theopenings 10 a, a copper layer, formed by a sputtering process, having a thickness of between 0.03 and 1 μm, and preferably of between 0.1 and 0.5 μm, on the titanium-containing layer and between the titanium-containing layer and the copper traces 210, a nickel layer, formed by an electroplating process, having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, on the sputtered copper layer and between the sputtered copper layer and the copper traces 210, and a gold joint having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer and between the nickel layer and the copper traces 210. The above-mentioned titanium-containing layer can be a single titanium-tungsten-alloy layer having a thickness of between 0.03 and 0.7 μm, and preferably of between 0.15 and 0.4 μm, a single titanium layer having a thickness of between 0.01 and 0.7 μm, and preferably of between 0.01 and 0.15 μm, a single titanium-nitride layer having a thickness of between 0.01 and 0.1 μm, and preferably of between 0.01 and 0.02 μm, or a composite layer comprising a titanium layer having a thickness of between 0.01 and 0.15 μm, and a titanium-tungsten-alloy layer, having a thickness of between 0.1 and 0.35 μm, on the titanium layer. - In a first case, referring to
FIG. 3C , the metal bumps 12 have the above-mentioned gold layer, at the tips of the metal bumps 12, capable of being used to be joined with thewetting layer 240 b of pure tin or an above-mentioned tin alloy using flip-chip bonding, which process is described as below. First, theflexible circuit film 36 is placed on astage 600 a kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., and thesemiconductor chip 2 is held by vacuum adsorption on atool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C. Next, thesemiconductor chip 2 is thermally pressed on thewetting layer 240 b of theflexible circuit film 36 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 36, to join the metal bumps 12 with thewetting layer 240 b. Referring toFIGS. 3A and 3C , in the step of joining the metal bumps 12 with thewetting layer 240 b, theinterface bonding layer 250, such as a metal alloy, may be formed between the metal bumps 12 and the copper traces 210. The specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIG. 3C can be referred to as the specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Next, thetool head 610 a is removed from thesemiconductor chip 2. Next, theflexible circuit film 36 bonded with thesemiconductor chip 2 is removed from thestage 600 a. The specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIG. 3C can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . - In a second case, referring to
FIG. 3C , the metal bumps 12 have the above-mentioned gold layer, at the tips of the metal bumps 12, capable of being used to be joined with a gold layer of thewetting layer 240 b using flip-chip bonding, which process is described as below. First, theflexible circuit film 36 is placed on thestage 600 a kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., and thesemiconductor chip 2 is held by vacuum adsorption on thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C. Next, thesemiconductor chip 2 is thermally pressed on thewetting layer 240 b of theflexible circuit film 36 at a force of between 20 and 150N, and preferably of between 70 and 120N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 36, to join the above-mentioned gold layer of the metal bumps 12 with the gold layer of thewetting layer 240 b. Next, thetool head 610 a is removed from thesemiconductor chip 2. Next, theflexible circuit film 36 bonded with thesemiconductor chip 2 is removed from thestage 600 a. Thereby, thepads 18 of thesemiconductor chip 2 can be connected to the copper traces 210 of theflexible circuit film 36 through gold joints formed by joining the above-mentioned gold layer of the metal bumps 12 with the gold layer of thewetting layer 240 b. The specification of the metal bumps 12, between thesemiconductor chip 2 and theflexible circuit film 36, formed in the process as illustrated in the second case shown inFIG. 3C can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIG. 3D , apolymer layer 260 is filled into the gap between thesemiconductor chip 2 and theflexible circuit film 36, enclosing the metal bumps 12, by dispensing a polymer on theflexible circuit film 36 close to thesemiconductor chip 2, with the polymer flowing into the gap between thesemiconductor chip 2 and theflexible circuit film 36, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester, polybenzoxazole or polyimide. - Referring to
FIG. 3E , asubstrate 300 comprises a circuit structure in thesubstrate 300, an insulatinglayer 320, an insulatinglayer 330,metal pads 310 a andmetal pads 310 b. The circuit structure comprises copper traces (including 340 a and 340 b) each having a thickness between 5 and 30 micrometers.Openings 320 a in the insulatinglayer 320 expose the topmost copper traces 340 a andopenings 330 a in the insulatinglayer 330 expose the bottommost copper traces 340 b. Themetal pads 310 a are on the topmost copper traces 340 a exposed by theopenings 320 a, and themetal pads 310 b are on the bottommost copper traces 340 b exposed by theopenings 330 a. Themetal pads 310 a are connected to themetal pads 310 b through the copper traces (comprising the copper traces 340 a and 340 b) in thesubstrate 300. - Each of the insulating
layers metal pads metal pads 310 a can be formed by electroless plating a nickel layer having a thickness of between 0.05 and 1 μm on the topmost copper traces 340 a exposed by theopenings 320 a, and electroless plating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the nickel layer in theopenings 320 a. Alternatively, themetal pads 310 a can be formed by electroless plating a nickel layer having a thickness of between 0.05 and 1 μm on the topmost copper traces 340 a exposed by theopenings 320 a, and electroless plating a tin layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the nickel layer in theopenings 320 a. Alternatively, themetal pads 310 a can be formed by electroless plating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the topmost copper traces 340 a exposed by theopenings 320 a. For example, themetal pads 310 b can be formed by electroless plating a nickel layer having a thickness of between 0.05 and 1 μm on the bottommost copper traces 340 b exposed by theopenings 330 a, and electroless plating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the nickel layer in theopenings 330 a. Alternatively, themetal pads 310 b can be formed by electroless plating a nickel layer having a thickness of between 0.05 and 1 μm on the bottommost copper traces 340 b exposed by theopenings 330 a, and electroless plating a tin layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the nickel layer in theopenings 330 a. Alternatively, themetal pads 310 b can be formed by electroless plating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottommost copper traces 340 b exposed by theopenings 330 a. - In a case, the
substrate 300 may comprise a core layer, such as a glass fiber reinforced epoxy with a thickness of between 200 and 2,000 μm, multiple copper circuit layers respectively over and under the core layer, and multiple polymer layers between the neighboring copper circuit layers. The copper circuit layers provide the circuit structure in thesubstrate 300. Themetal pads - In another case, the
substrate 300 may comprise multiple copper circuit layers and multiple ceramic layers between the neighboring copper circuit layers. The copper circuit layers provide the circuit structure in thesubstrate 300. Themetal pads - The
substrate 300 may be a ball grid array (BGA) substrate with a thickness t15 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 may be a glass fiber reinforced epoxy based substrate with a thickness t15 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 may be a silicon substrate with a thickness t15 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 may be a ceramic substrate with a thickness t15 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 may be an organic substrate with a thickness t15 of between 200 and 2,000 μm. - Referring to
FIG. 3F ,metal joints 410 a, such as tin-containing joints, are formed on themetal pads 310 a by screen printing a solder paste containing flux and solder, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, on themetal pads 310 a and then reflowing the solder paste. The metal joints 410 a may be formed of pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. Two methods of bonding theflexible circuit film 36 with thesubstrate 300 are described as follow. - In a first case, referring to
FIGS. 3F and 3G , when themetal joints 410 a are tin-containing joints, themetal joints 410 a can be used to be joined with thewetting layer 240 a of pure tin or an above-mentioned tin alloy using a heat press process, which method is described as below. First, thesubstrate 300 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, theflexible circuit film 36 is thermally pressed on themetal joints 410 a on themetal pads 310 a of thesubstrate 300 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 a with themetal joints 410 a. In the step of joining thewetting layer 240 a with themetal joints 410 a,metal joints 410 b can be formed between the first contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300. The metal joints 410 b can be tin-containing joints having a thickness t16 of between 20 and 150 micrometers or of between 15 and 50 micrometers, wherein the tin-containing joints may include pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. The tin-containing joints may include a tin-gold alloy, a tin-silver-gold alloy, a tin-silver-gold-copper alloy or a tin-lead-gold alloy at the bottom side of the tin-containing joints due to the reaction between tin in themetal joints 410 a and gold at the top of themetal pads 310 a. Next, the tool head is removed from theflexible circuit film 36. Next, thesubstrate 300 bonded with theflexible circuit film 36 is removed from the stage. - In a second case, referring to
FIGS. 3F and 3G , when themetal joints 410 a are tin-containing joints, themetal joints 410 a can be used to be joined with a gold layer of thewetting layer 240 a using a heat press process, which method is described as below. First, thesubstrate 300 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, theflexible circuit film 36 is thermally pressed on themetal joints 410 a on themetal pads 310 a of thesubstrate 300 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 a with themetal joints 410 a. In the step of joining thewetting layer 240 a with themetal joints 410 a, themetal joints 410 b can be formed between the first contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300. The metal joints 410 b can be tin-containing joints having a thickness t16 of between 20 and 150 micrometers or of between 15 and 50 micrometers. The tin-containing joints may include a tin-silver-gold-copper alloy, a tin-silver-gold alloy or a tin-gold alloy at the top side of the tin-containing joints due to the reaction between tin in themetal joints 410 a and gold at the top of thewetting layer 240 a. The tin-containing joints may include a tin-gold alloy, a tin-silver-gold alloy or a tin-silver-gold-copper alloy at the bottom side of the tin-containing joints due to the reaction between tin in themetal joints 410 a and gold at the top of themetal pads 310 a. Next, the tool head is removed from theflexible circuit film 36. Next, thesubstrate 300 bonded with theflexible circuit film 36 is removed from the stage. - Referring to
FIG. 3H , after theflexible circuit film 36 is bonded with thesubstrate 300, apolymer layer 350 can be filled into the gap between theflexible circuit film 36 and thesubstrate 300, enclosing themetal joints 410 b, by dispensing a polymer on thesubstrate 300 close to theflexible circuit film 36, with the polymer flowing into the gap between theflexible circuit film 36 and thesubstrate 300, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 350 may be expoxy, polyester or polyimide, and thepolymer layer 350 has a thickness t17 of between 1 and 30 micrometers. - Referring to
FIG. 3I , apolymer compound 360 is formed on thesemiconductor chip 2, on theflexible circuit film 36 and on a peripheral region of thesubstrate 300 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theflexible circuit film 36 and on the peripheral region of thesubstrate 300 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide, polybenzoxazole (PBO) or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIGS. 3J and 3K ,solder balls 501 shown inFIG. 3J may be being placed, in a ball-grid-array arrangement, on a flux orsolder paste 505 preformed on themetal pads 310 b of thesubstrate 300 using a ball placement process to formsolder balls 502 shown inFIG. 3K on thesubstrate 300. Thesolder balls 502 can be formed by printing the flux orsolder paste 505 on themetal pads 310 b, next placing thesolder balls 501, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a diameter of between 0.25 and 1.2 millimeters on the flux orsolder paste 505, next reflowing thesolder balls 501 at a peak temperature of between 230 and 270° C., and then cleaning the remaining flux from thesubstrate 300. Thesolder balls 502 have a diameter of between 0.2 and 1.2 millimeters, and thesolder balls 502 may include pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. - For example, during the step of reflowing the
solder balls 501, when themetal pads 310 b have a bottommost metal layer of gold, the gold layer of themetal pads 310 b is solved in thesolder balls 502. Preferably, themetal pads 310 b have a nickel layer between the gold layer and the copper traces 340 b. The nickel layer serves as a barrier layer preventing copper in the copper traces 340 b from being solved in thesolder balls 502 after thesolder balls 502 are formed on thesubstrate 300. In the case of gold serving as a bottommost metal layer of themetal pads 310 b, thesolder balls 502, after being joined with thesubstrate 300, may include a portion, of a tin-silver-gold-copper alloy, a tin-silver-gold alloy, a tin-gold alloy or a tin-lead-gold alloy, on the nickel layer of themetal pads 310 b and under the copper traces 340 b of thesubstrate 300 due to the reaction between gold in themetal pads 310 b and tin in thesolder balls 501 during reflowing thesolder balls 501. - After the
solder balls 502 are formed on thesubstrate 300, thesubstrate 300 and thepolymer compound 360 can be optionally cut into multiple units. -
FIG. 3L is a perspective view showingFIG. 3K . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 36 by bonding thesemiconductor chip 2 with theflexible circuit film 36. Theflexible circuit film 36 is also bonded with thesubstrate 300 to connect the fine-pitchedmetal bumps 12 of thesemiconductor chip 2 with the circuit structure of thesubstrate 300. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 36 and the circuit structure of thesubstrate 300. - Alternatively, referring to
FIGS. 3M and 3N , the step of forming thepolymer compound 360, as shown inFIG. 3I , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 36 are uncovered by any polymer compound. Alternatively, referring toFIG. 30 , the step of forming thepolymer layer 350, as shown inFIG. 3H , can be omitted. Alternatively, referring toFIG. 3P , the steps of forming thepolymer layer 350, as shown inFIG. 3H , and of forming thepolymer compound 360, as shown inFIG. 3I , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 36 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 3I . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 3H . Thesemiconductor chip 2 and theflexible circuit film 36 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 and thesolder balls 502 can be omitted, as shown inFIG. 3Q . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350, thepolymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 3G . Thesemiconductor chip 2 and theflexible circuit film 36 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. -
FIG. 3R is a schematically cross-sectional figure showing a chip package including thesemiconductor chip 2 joined with aflexible circuit substrate 38 using a tape-automated-bonding (TAB) technology. The above-mentionedflexible circuit film 36 can be replaced by theflexible circuit film 38. Theflexible circuit film 38 includes thepolymer layer 200, thepolymer layer 220, thewetting layer 240 a, thewetting layer 240 b and the copper traces 210 between the polymer layers 200 and 220, wherein theopenings 200 a in thepolymer layer 200 expose contact points of the copper traces 210, and the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the center portion of theflexible circuit film 38. Thewetting layer 240 a is on the contact points of the copper traces 210 exposed by theopenings 200 a in thepolymer layer 200, and thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 38. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 3R can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewetting layer 240 a shown inFIG. 3R can be referred to as the specification of thewetting layer 240 a illustrated inFIGS. 3B and 3C . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 38 through theinterface bonding layer 250. A method for bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 at the center portion of theflexible circuit film 38 is described as shown inFIG. 3S . - Referring to
FIG. 3S , theflexible circuit film 38 can be connected to thesemiconductor chip 2. Theflexible circuit film 38 has thewetting layer 240 a to be joined with thesubstrate 300 shown inFIG. 3E , and thewetting layer 240 b to be joined with the metal bumps 12 on thesemiconductor chip 2. Thewetting layer 240 b is formed on the top and bottom sides of the copper traces 210, uncovered by the polymer layers 200 and 220, at the center portion of theflexible circuit film 38, and thewetting layer 240 b having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, nickel, silver, palladium, tin or a composite of the above-mentioned materials. For example, thewetting layer 240 b may be a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the top and bottom sides of the copper traces 210, uncovered by the polymer layers 200 and 220, at the center portion of theflexible circuit film 38. Alternatively, thewetting layer 240 b may be a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the top and bottom sides of the copper traces 210, uncovered by the polymer layers 200 and 220, at the center portion of theflexible circuit film 38. - In a first case, referring to
FIG. 3S , the metal bumps 12 have the above-mentioned gold layer, at the tips of the metal bumps 12, capable of being used to be joined with thewetting layer 240 b of pure tin or an above-mentioned tin alloy, which method is described as below. First, thesemiconductor chip 2 is held by vacuum adsorption on astage 600 b kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C. Next, theflexible circuit film 38 is thermally pressed on the metal bumps 12 of thesemiconductor chip 2 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by atool head 610 b kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 38, to join thewetting layer 240 b with the metal bumps 12. Referring toFIGS. 3R and 3S , in the step of joining thewetting layer 240 b with the metal bumps 12, theinterface bonding layer 250, such as a metal alloy, may be formed between the metal bumps 12 and the copper traces 210. Theinterface bonding layer 250 has a thickness t12 of between 0.2 and 10 micrometers, and preferably of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is pure tin, theinterface bonding layer 250 is a tin-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers, wherein an atomic ratio of tin to gold in the tin-gold alloy is between 0.2 and 0.3. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-silver alloy, theinterface bonding layer 250 is a tin-silver-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-silver-copper alloy, theinterface bonding layer 250 is a tin-silver-gold-copper alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. Next, thetool head 610 b is removed from theflexible circuit film 38. Next, thesemiconductor chip 2 bonded with theflexible circuit film 38 is removed from thestage 600 b. The metal bumps 12 bonded with the copper traces 210 of theflexible circuit film 38 have a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers, and the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3R and 3S can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . - In a second case, referring to
FIG. 3S , the metal bumps 12 have the above-mentioned gold layer, at the tips of the metal bumps 12, capable of being used to be joined with a gold layer of thewetting layer 240 b, which method is described as below. First, thesemiconductor chip 2 is held by vacuum adsorption on thestage 600 b kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C. Next, theflexible circuit film 38 is thermally pressed on the metal bumps 12 of thesemiconductor chip 2 at a force of between 20 and 150N, and preferably of between 70 and 120N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 b kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 38, to join the gold layer of thewetting layer 240 b with the above-mentioned gold layer of the metal bumps 12. Next, thetool head 610 b is removed from theflexible circuit film 38. Next, thesemiconductor chip 2 bonded with theflexible circuit film 38 is removed from thestage 600 b. Thereby, thepads 18 of thesemiconductor chip 2 can be connected to the copper traces 210 of theflexible circuit film 38 through gold joints formed by joining the gold layer of thewetting layer 240 b with the above-mentioned gold layer of the metal bumps 12. The metal bumps 12 bonded with the copper traces 210 of theflexible circuit film 38 have a thickness of between 5 and 50 micrometers, and preferably of between 10 and 25 micrometers. The specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3S can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIG. 3T , thepolymer layer 260 can be formed by dispensing a polymer on thesemiconductor chip 2 with the polymer enclosing the metal bumps 12 and the copper traces 210 at the center portion of theflexible circuit film 38, and then curing the polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester or polyimide. - The metal joints 410 a, such as tin-containing joints, are formed on the
metal pads 310 a of thesubstrate 300 shown inFIG. 3E by screen printing a solder paste containing flux and solder, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, on themetal pads 310 a and then reflowing the solder paste. The metal joints 410 a may be formed of pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. The specification of thesubstrate 300 shown inFIG. 3T can be referred to as the specification of thesubstrate 300 illustrated inFIG. 3E . Two methods of bonding theflexible circuit film 38 with thesubstrate 300 are described as follow. - In a first case, referring to
FIGS. 3T and 3U , when themetal joints 410 a are tin-containing joints, themetal joints 410 a can be used to be joined with thewetting layer 240 a of pure tin or an above-mentioned tin alloy using a heat press process, which method which process is described as below. First, thesubstrate 300 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, theflexible circuit film 38 is thermally pressed on themetal joints 410 a on themetal pads 310 a of thesubstrate 300 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 a with themetal joints 410 a. In the step of joining thewetting layer 240 a with themetal joints 410 a, themetal joints 410 b can be formed between the contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300. Next, the tool head is removed from theflexible circuit film 38. Next, thesubstrate 300 bonded with theflexible circuit film 38 is removed from the stage. The specification of themetal joints 410 b, between the contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300, formed in the process as illustrated in the first case shown inFIGS. 3T and 3U can be referred to as the specification of themetal joints 410 b, between the first contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300, formed in the process as illustrated in the first case shown inFIGS. 3F and 3G . - In a second case, referring to
FIGS. 3T and 3U , when themetal joints 410 a are tin-containing joints, themetal joints 410 a can be used to be joined with a gold layer of thewetting layer 240 a using a heat press process, which method is described as below. First, thesubstrate 300 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, theflexible circuit film 38 is thermally pressed on themetal joints 410 a on themetal pads 310 a of thesubstrate 300 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 a with themetal joints 410 a. In the step of joining thewetting layer 240 a with themetal joints 410 a, themetal joints 410 b can be formed between the contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300. Next, the tool head is removed from theflexible circuit film 38. Next, thesubstrate 300 is removed from the stage. The specification of themetal joints 410 b, between the contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300, formed in the process as illustrated in the second case shown inFIGS. 3T and 3U can be referred to as the specification of themetal joints 410 b, between the first contact points of the copper traces 210 and the topmost copper traces 340 a of thesubstrate 300, formed in the process as illustrated in the second case shown inFIGS. 3F and 3G . - Referring to
FIG. 3V , after theflexible circuit film 38 is bonded with thesubstrate 300, thepolymer layer 350 can be optionally filled into the gap between theflexible circuit film 38 and thesubstrate 300, enclosing themetal joints 410 b, by dispensing a polymer on thesubstrate 300 close to theflexible circuit film 38, with the polymer flowing into the gap between theflexible circuit film 38 and thesubstrate 300, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 350 may be expoxy, polyester or polyimide, and thepolymer layer 350 has a thickness t17 of between 1 and 30 micrometers. - Referring to
FIG. 3W , thepolymer compound 360 can be optionally formed on thesemiconductor chip 2, on theflexible circuit film 38 and on thesubstrate 300 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theflexible circuit film 38 and the peripheral region of thesubstrate 300 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 3X , after thepolymer compound 360 is formed, thesolder balls 502 may be formed, in a ball-grid-array arrangement, on themetal pads 310 b of thesubstrate 300 using a ball placement process. The process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as shown inFIG. 3X can be referred to as the process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as illustrated inFIGS. 3J and 3K . The specification of thesolder balls 502 shown inFIG. 3X can be referred to as the specification of thesolder balls 502 illustrated inFIGS. 3J and 3K . Optionally, thesubstrate 300 can be sawed after thesolder balls 502 are formed on themetal pads 310 b of thesubstrate 300. - Thereby, the fine-pitched
metal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 38 by bonding thesemiconductor chip 2 with theflexible circuit film 38. Theflexible circuit film 38 is also bonded with thesubstrate 300 to connect the fine-pitchedmetal bumps 12 of thesemiconductor chip 2 with the circuit structure of thesubstrate 300. Thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 38 and the circuit structure of thesubstrate 300. - Alternatively, the step of forming the
polymer compound 360, as shown inFIG. 3W , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 38 are uncovered by any polymer compound. Alternatively, the step of forming thepolymer layer 350, as shown inFIG. 3V , can be omitted. Alternatively, the steps of forming thepolymer layer 350, as shown inFIG. 3V , and of forming thepolymer compound 360, as shown inFIG. 3W , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 38 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 3W . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 3V . Thesemiconductor chip 2 and theflexible circuit film 38 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 and thesolder balls 502 can be omitted, as shown inFIG. 3Y . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350, thepolymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 3U . Thesemiconductor chip 2 and theflexible circuit film 38 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIG. 4A , after the step shown inFIG. 3D , apolymer compound 360 is formed on thesemiconductor chip 2 and on theflexible circuit film 36 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2 and on theflexible circuit film 36 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIGS. 4B and 4C , after thepolymer compound 360 is formed,solder balls 501 shown inFIG. 4B are placed, in a ball-grid-array arrangement, on a flux orsolder paste 505 preformed on thewetting layer 240 a of theflexible circuit film 36 using a ball placement process to formsolder balls 502 shown inFIG. 4C on theflexible circuit film 36. Thesolder balls 502 can be formed by printing the flux orsolder paste 505 on thewetting layer 240 a, next placing thesolder balls 501, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a diameter of between 0.25 and 1.2 millimeters on the flux orsolder paste 505, next reflowing thesolder balls 501 at a peak temperature of between 230 and 270° C., and then cleaning the remaining flux from theflexible circuit film 36. Thesolder balls 502 have a diameter of between 0.2 and 1.2 millimeters, and thesolder balls 502 may include pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. - For example, during the step of reflowing the
solder balls 501, when thewetting layer 240 a is a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, the tin-containing layer is solved in thesolder balls 502. - Alternatively, during the step of reflowing the
solder balls 501, when thewetting layer 240 a is a gold layer, the gold layer is solved in thesolder balls 502. Thesolder balls 502, after being joined with theflexible circuit film 36, include a portion, of a tin-silver-gold-copper alloy, a tin-silver-gold alloy, a tin-gold alloy or a tin-lead-gold alloy, on the copper traces 210 of theflexible circuit film 36 due to the reaction between gold in thewetting layer 240 a and tin in thesolder balls 501 during reflowing thesolder balls 501. - After the
solder balls 502 are formed on theflexible circuit film 36, theflexible circuit film 36 and thepolymer compound 360 can be cut into multiple units. -
FIG. 4D is a perspective view showingFIG. 4C . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 36 by bonding thesemiconductor chip 2 with theflexible circuit film 36. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 36 and thesolder balls 502. -
FIG. 5A is a schematically cross-sectional figure showing a chip-on-film package. The above-mentionedflexible circuit film 36 can be replaced by aflexible circuit film 40. Theflexible circuit film 40 includes thepolymer layer 200, thepolymer layer 220, thewetting layer 240 b,metal pads 245 and the copper traces 210 between the polymer layers 200 and 220. Themetal pads 245 are formed on first contact points of the copper traces 210 exposed by openings in thepolymer layer 200, and the openings are filled up with themetal pads 245. Thewetting layer 240 b are formed on second contact points of the copper traces 210 exposed by theopenings 220 a in thepolymer layer 220. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 5A can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewetting layer 240 b shown inFIG. 5A can be referred to as the specification of thewetting layer 240 b illustrated inFIGS. 3B and 3C . The specification of theinterface bonding layer 250 shown inFIG. 5A can be referred to as the specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The material of the
metal pads 245 may be gold, copper, nickel, silver, tin, palladium or a composite of the above-mentioned materials, and themetal pads 245 have a thickness t18 of between 4 and 10 micrometers, of between 15 and 30 micrometers or of between 10 and 100 micrometers. In a case, themetal pads 245 may be formed by electroplating or electroless plating a gold layer with a thickness of between 4 and 10 micrometers, of between 15 and 30 micrometers or of between 10 and 100 micrometers on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and the openings in thepolymer layer 200 are filled up with the gold layer. In another case, themetal pads 245 may be formed by electroplating or electroless plating a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, with a thickness of between 4 and 10 micrometers, of between 15 and 30 micrometers or of between 10 and 100 micrometers on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and the openings are filled up with the tin-containing layer. In another case, themetal pads 245 may be formed by electroplating or electroless plating a copper layer with a thickness of between 4 and 10 micrometers, of between 15 and 30 micrometers or of between 10 and 100 micrometers on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and the openings are filled up with the copper layer. In another case, themetal pads 245 may be formed by electroplating a nickel layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and then electroplating a gold layer with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.5 micrometers, on the nickel layer in the openings in thepolymer layer 200, wherein the openings in thepolymer layer 200 are filled up with the nickel layer and the gold layer. In another case, themetal pads 245 may be formed by electroless plating a nickel layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and then electroless plating a gold layer with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.5 micrometers, on the nickel layer in the openings in thepolymer layer 200, wherein the openings in thepolymer layer 200 are filled up with the nickel layer and the gold layer. In another case, themetal pads 245 may be formed by electroplating a nickel layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and then electroplating a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.5 micrometers, on the nickel layer in the openings in thepolymer layer 200, wherein the openings in thepolymer layer 200 are filled up with the nickel layer and the tin-containing layer. In another case, themetal pads 245 may be formed by electroless plating a nickel layer with a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the first contact points of the copper traces 210 exposed by the openings in thepolymer layer 200, and then electroless plating a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.5 micrometers, on the nickel layer in the openings in thepolymer layer 200, wherein the openings in thepolymer layer 200 are filled up with the nickel layer and the tin-containing layer. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210, exposed by theopenings 220 a, of theflexible circuit film 40 through theinterface bonding layer 250. The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 40, as shown inFIG. 5A can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 36, as illustrated in the first and second cases shown inFIGS. 3B and 3C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 5A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 5A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIG. 5B , after thesemiconductor chip 2 is bonded with theflexible circuit film 40, thepolymer layer 260 is filled into the gap between thesemiconductor chip 2 and theflexible circuit film 40, enclosing the metal bumps 12, by dispensing a polymer on theflexible circuit film 40 close to thesemiconductor chip 2, with the polymer flowing into the gap between thesemiconductor chip 2 and theflexible circuit film 40, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester, polybenzoxazole or polyimide. - Referring to
FIG. 5C , after thepolymer layer 260 is formed, thepolymer compound 360 is formed on thesemiconductor chip 2 and on theflexible circuit film 40 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2 and on theflexible circuit film 40 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIGS. 5D and 5E , after thepolymer compound 360 is formed, thesolder balls 501 shown inFIG. 5D are placed, in a ball-grid-array arrangement, on the flux orsolder paste 505 preformed on themetal pads 245 of theflexible circuit film 40 using a ball placement process to form thesolder balls 502 shown inFIG. 5E on theflexible circuit film 40. Thesolder balls 502 can be formed by printing the flux orsolder paste 505 on themetal pads 245, next placing thesolder balls 501, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, having a diameter of between 0.25 and 1.2 millimeters on the flux orsolder paste 505, next reflowing thesolder balls 501 at a peak temperature of between 230 and 270° C., and then cleaning the remaining flux from theflexible circuit film 40. Thesolder balls 502 have a diameter of between 0.2 and 1.2 millimeters, and thesolder balls 502 may include pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. - For example, during the step of reflowing the
solder balls 501, when themetal pads 245 have a bottommost metal layer of gold, the gold layer of themetal pads 245 is solved in thesolder balls 502. Preferably, themetal pads 245 have a nickel layer between the gold layer and the copper traces 210. The nickel layer serves as a barrier layer preventing copper in the copper traces 210 from being solved in thesolder balls 502 after thesolder balls 502 are formed on theflexible circuit film 40. In the case of gold serving as a bottommost metal layer of themetal pads 245, thesolder balls 502, after being joined with theflexible circuit film 40, may include a portion, of a tin-gold alloy, a tin-silver-gold-copper alloy, a tin-silver-gold alloy or a tin-lead-gold alloy, on the nickel layer of themetal pads 245 and under the first contact points of the copper traces 210 due to the reaction between gold in themetal pads 245 and tin in thesolder balls 501 during reflowing thesolder balls 501. - Alternatively, during the step of reflowing the
solder balls 501, when themetal pads 245 have a bottommost metal layer of copper, all or a part of the copper layer of themetal pads 245 may be solved in thesolder balls 502. In the case of copper serving as a bottommost metal layer of themetal pads 245, thesolder balls 502, after being joined with theflexible circuit film 40, may include a portion, of a tin-silver-copper alloy, a tin-lead-copper alloy or a tin-copper alloy, under the first contact points of the copper traces 210 due to the reaction between copper in themetal pads 245 and tin in thesolder balls 501 during reflowing thesolder balls 501. - After the
solder balls 502 are formed on theflexible circuit film 40, theflexible circuit film 40 and thepolymer compound 360 can be cut into multiple units. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 5C . Theflexible circuit film 40 is sawed into multiple units. After sawing theflexible circuit film 40, themetal pads 245 of theflexible circuit film 40 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Thereby, the fine-pitched
metal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 40 by bonding thesemiconductor chip 2 with theflexible circuit film 40. Thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 40. -
FIG. 6A is a schematically cross-sectional figure showing a chip-on-film package. Aflexible circuit film 42 includes apolymer layer 200, apolymer layer 220, awetting layer 240 b, awetting layer 240 c and copper traces 210 between the polymer layers 200 and 220, wherein the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the outer portion of theflexible circuit film 42. Thewetting layer 240 b is on contact points, exposed byopenings 220 a, of the copper traces 210 in thepolymer layer 220. Thewetting layer 240 c is on the copper traces 210 at the outer portion of theflexible circuit film 42. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 6A can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewetting layer 240 b shown inFIG. 6A can be referred to as the specification of thewetting layer 240 b illustrated inFIGS. 3B and 3C . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The
wetting layer 240 c having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, nickel, silver, tin or a composite of the above-mentioned materials. For example, thewetting layer 240 c may be a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the copper traces 210 at the outer portion of theflexible circuit film 42. Alternatively, thewetting layer 240 c may be a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the copper traces 210 at the outer portion of theflexible circuit film 42. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210, exposed by theopenings 220 a, of theflexible circuit film 42 through aninterface bonding layer 250. The specification of theinterface bonding layer 250 shown inFIG. 6A can be referred to as the specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 42, as shown inFIG. 6A can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 36, as illustrated in the first and second cases shown inFIGS. 3B and 3C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 6A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 6A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIG. 6B , apolymer layer 260 is filled into the gap between thesemiconductor chip 2 and theflexible circuit film 42, enclosing the metal bumps 12, by dispensing a polymer on theflexible circuit film 42 close to thesemiconductor chip 2, with the polymer flowing into the gap between thesemiconductor chip 2 and theflexible circuit film 42, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester, polybenzoxazole or polyimide. - Metal joints 410 c, such as tin-containing joints, are formed on the
metal pads 310 a of thesubstrate 300 shown inFIG. 3E by screen printing a solder paste containing flux and solder, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, on themetal pads 310 a and then reflowing the solder paste. The metal joints 410 a may be formed of pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. The specification of thesubstrate 300 shown inFIG. 6B can be referred to as the specification of thesubstrate 300 illustrated inFIG. 3E . Two methods of bonding theflexible circuit film 42 with thesubstrate 300 are described as follow. - In a first case, referring to
FIGS. 6B and 6C , when themetal joints 410 c are tin-containing joints, themetal joints 410 c can be used to be joined with thewetting layer 240 c of pure tin or an above-mentioned tin alloy using a heat press process, which method is described as below. First, thesubstrate 300 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, theflexible circuit film 42 is thermally pressed on themetal joints 410 c on themetal pads 310 a of thesubstrate 300 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 c with themetal joints 410 c. In the step of joining thewetting layer 240 c with themetal joints 410 c,metal joints 410 d can be formed between the topmost copper traces 340 a of thesubstrate 300 and the copper traces 210 at the outer portion of theflexible circuit film 42. The metal joints 410 d can be tin-containing joints having a thickness t19 of between 0.5 and 100 micrometers, and preferably of between 1 and 10 micrometers, wherein the tin-containing joints may include pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy. The tin-containing joints may include a tin-gold alloy, a tin-silver-gold alloy, a tin-silver-gold-copper alloy or a tin-lead-gold alloy at the bottom side of the tin-containing joints due to the reaction between tin in themetal joints 410 c and gold at the top of themetal pads 310 a. Preferably, themetal pads 310 a have a nickel layer between themetal joints 410 d and the copper traces 340 a. The nickel layer serves as a barrier layer preventing copper in the copper traces 340 a from being solved in themetal joints 410 d after themetal joints 410 d are formed between theflexible circuit film 42 and thesubstrate 300. Next, the tool head is removed from theflexible circuit film 42. Next, thesubstrate 300 bonded withflexible circuit film 42 is removed from the stage. - In a second case, referring to
FIGS. 6B and 6C , when themetal joints 410 c are tin-containing joints, themetal joints 410 c can be used to be joined with a gold layer of thewetting layer 240 c using a heat press process, which method is described as below. First, thesubstrate 300 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, theflexible circuit film 42 is thermally pressed on themetal joints 410 c on themetal pads 310 a of thesubstrate 300 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 c with themetal joints 410 c. In the step of joining thewetting layer 240 c with themetal joints 410 c, themetal joints 410 d can be formed between the topmost copper traces 340 a of thesubstrate 300 and the copper traces 210 at the outer portion of theflexible circuit film 42. The metal joints 410 d can be tin-containing joints having a thickness t19 of between 0.5 and 100 micrometers, and preferably of between 1 and 10 micrometers. The tin-containing joints may include a tin-silver-gold-copper alloy, a tin-silver-gold alloy, a tin-gold alloy or a tin-lead-gold alloy at the top side of the tin-containing joints due to the reaction between tin in themetal joints 410 c and gold at the top of thewetting layer 240 c. The tin-containing joints may include a tin-gold alloy, a tin-silver-gold alloy, a tin-silver-gold-copper alloy or a tin-lead-gold alloy at the bottom side of the tin-containing joints due to the reaction between tin in themetal joints 410 c and gold at the top of themetal pads 310 a. Preferably, themetal pads 310 a have a nickel layer between themetal joints 410 d and the copper traces 340 a. The nickel layer serves as a barrier layer preventing copper in the copper traces 340 a from being solved in themetal joints 410 d after themetal joints 410 d are formed between theflexible circuit film 42 and thesubstrate 300. Next, the tool head is removed from theflexible circuit film 42. Next, thesubstrate 300 bonded with theflexible circuit film 42 is removed from the stage. - Referring to
FIG. 6C , there is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300. Alternatively, themetal joints 410 d can be replaced by an anisotropic conductive film (ACF). The anisotropic conductive film can be preformed on themetal pads 310 a of thesubstrate 300 shown inFIG. 3E , and then thewetting layer 240 c on the copper traces 210 at the outer portion of theflexible circuit film 42 can be pressed on the anisotropic conductive film, such that metal particles in the anisotropic conductive film connects thewetting layer 240 c of theflexible circuit film 42 to themetal pads 310 a of thesubstrate 300. - Referring to
FIG. 6D , after theflexible circuit film 42 is bonded with thesubstrate 300, apolymer layer 350 a can be filled into the gap between theflexible circuit film 42 and thesubstrate 300, enclosing themetal joints 410 d and thewetting layer 240 c, by dispensing a polymer on thesubstrate 300 close to theflexible circuit film 42, with the polymer flowing into the gap between theflexible circuit film 42 and thesubstrate 300, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 350 a may be expoxy, polyester or polyimide, and thepolymer layer 350 a between theflexible circuit film 42 and thesubstrate 300 has a thickness t20 of between 1 and 30 micrometers. - Referring to
FIG. 6E , apolymer compound 360 is formed on thesemiconductor chip 2, on theflexible circuit film 42 and on a peripheral region of thesubstrate 300 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theflexible circuit film 42 and on the peripheral region of thesubstrate 300 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIGS. 6F and 6G ,solder balls 501 shown inFIG. 6F may be being placed, in a ball-grid-array arrangement, on a flux orsolder paste 505 preformed on themetal pads 310 b of thesubstrate 300 using a ball placement process to formsolder balls 502 shown inFIG. 6G on thesubstrate 300. Thesolder balls 502 can be formed by printing the flux orsolder paste 505 on themetal pads 310 b, next placing thesolder balls 501, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a diameter of between 0.25 and 1.2 millimeters on the flux orsolder paste 505, next reflowing thesolder balls 501 at a peak temperature of between 230 and 270° C., and then cleaning the remaining flux from thesubstrate 300. Thesolder balls 502 have a diameter of between 0.2 and 1.2 millimeters, and thesolder balls 502 may include pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. - For example, during the step of reflowing the
solder balls 501, when themetal pads 310 b have a bottommost metal layer of gold, the gold layer of themetal pads 310 b is solved in thesolder balls 502. Preferably, themetal pads 310 b have a nickel layer between the gold layer and the copper traces 340 b. The nickel layer serves as a barrier layer preventing copper in the copper traces 340 b from being solved in thesolder balls 502 after thesolder balls 502 are formed on thesubstrate 300. In the case of gold serving as a bottommost metal layer of themetal pads 310 b, thesolder balls 502, after being joined with thesubstrate 300, may include a portion, of a tin-silver-gold-copper alloy, a tin-silver-gold alloy, a tin-gold alloy or a tin-lead-gold alloy, on the nickel layer of themetal pads 310 b and under the copper traces 340 b of thesubstrate 300 due to the reaction between gold in themetal pads 310 b and tin in thesolder balls 501 during reflowing thesolder balls 501. - After the
solder balls 502 are formed on thesubstrate 300, thesubstrate 300 and thepolymer compound 360 can be optionally cut into multiple units. -
FIG. 6H is a perspective view showingFIG. 6G . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 42 by bonding thesemiconductor chip 2 with theflexible circuit film 42. Theflexible circuit film 42 is also bonded with thesubstrate 300 to connect the fine-pitchedmetal bumps 12 of thesemiconductor chip 2 with the circuit structure of thesubstrate 300. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 42 and the circuit structure of thesubstrate 300. - Alternatively, referring to
FIGS. 6I and 6J , the step of forming thepolymer compound 360, as shown inFIG. 6E , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 42 are uncovered by any polymer compound. Alternatively, referring toFIG. 6K , the step of forming thepolymer layer 350 a, as shown inFIG. 6D , can be omitted. Alternatively, referring toFIG. 6L , the steps of forming thepolymer layer 350 a, as shown inFIG. 6D , and of forming thepolymer compound 360, as shown inFIG. 6E , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 42 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 6E . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 6D . Thesemiconductor chip 2 and theflexible circuit film 42 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a and thesolder balls 502 can be omitted, as shown inFIG. 6M . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a, thepolymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 6C . Thesemiconductor chip 2 and theflexible circuit film 42 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. -
FIG. 6N is a schematically cross-sectional figure showing a chip package including thesemiconductor chip 2 joined with aflexible circuit substrate 44 using a tape-automated-bonding (TAB) technology. The above-mentionedflexible circuit film 42 can be replaced by theflexible circuit film 44. Theflexible circuit film 44 includes thepolymer layer 200, thepolymer layer 220, thewetting layer 240 b, thewetting layer 240 c and the copper traces 210 between the polymer layers 200 and 220, wherein the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the center portion and the outer portion of theflexible circuit film 44. Thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 44, and thewetting layer 240 c is on the copper traces 210 at the outer portion of theflexible circuit film 44. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 6N can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewetting layer 240 b shown inFIG. 6N can be referred to as the specification of thewetting layer 240 b illustrated inFIG. 3S . The specification of thewetting layer 240 c shown inFIG. 6N can be referred to as the specification of thewetting layer 240 c illustrated inFIG. 6A . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 44 through theinterface bonding layer 250. The specification of theinterface bonding layer 250 shown inFIG. 6N can be referred to as the specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIGS. 3R and 3S . The method, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 44, as shown inFIG. 6N can be referred to as the method, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 38, as illustrated in the first and second cases shown inFIG. 3R . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 6N can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 6N can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIG. 6O , thepolymer layer 260 can be formed by dispensing a polymer on thesemiconductor chip 2 with the polymer enclosing the metal bumps 12 and the copper traces 210 at the center portion of theflexible circuit film 44, and then curing the polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester or polyimide. - The metal joints 410 c, such as tin-containing joints, are formed on the
metal pads 310 a of thesubstrate 300 shown inFIG. 3E by screen printing a solder paste containing flux and solder, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, on themetal pads 310 a and then reflowing the solder paste. The metal joints 410 a may be formed of pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. The specification of thesubstrate 300 shown inFIG. 6O can be referred to as the specification of thesubstrate 300 illustrated inFIG. 3E . - Referring to
FIG. 6P , after thepolymer layer 260 is formed, theflexible circuit film 44 is bonded with thesubstrate 300. There is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300. The methods of bonding theflexible circuit film 44 with thesubstrate 300, as shown inFIG. 6P , can be referred to as the methods of bonding theflexible circuit film 42 with thesubstrate 300, as illustrated in the first and second cases shown inFIGS. 6B and 6C . - Alternatively, the
metal joints 410 d can be replaced by an anisotropic conductive film (ACF). The anisotropic conductive film can be preformed on themetal pads 310 a of thesubstrate 300 shown inFIG. 3E , and then thewetting layer 240 c on the copper traces 210 at the outer portion of theflexible circuit film 44 can be pressed on the anisotropic conductive film, such that metal particles in the anisotropic conductive film connects thewetting layer 240 c of theflexible circuit film 44 to themetal pads 310 a of thesubstrate 300. - Referring to
FIG. 6Q , after theflexible circuit film 44 is bonded with thesubstrate 300, thepolymer layer 350 a can be optionally filled into the gap between theflexible circuit film 44 and thesubstrate 300, enclosing themetal joints 410 d and thewetting layer 240 c, by dispensing a polymer on thesubstrate 300 close to theflexible circuit film 44, with the polymer flowing into the gap between theflexible circuit film 44 and thesubstrate 300, and then curing the flowing polymer at a temperature of between 100 and 250° C. The specification of thepolymer layer 350 a shown inFIG. 6Q can be referred to as the specification of thepolymer layer 350 a illustrated inFIG. 6D . - Referring to
FIG. 6R , thepolymer compound 360 can be optionally formed on thesemiconductor chip 2, on theflexible circuit film 44 and on a peripheral region of thesubstrate 300 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theflexible circuit film 44 and the peripheral region of thesubstrate 300 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 6S , after thepolymer compound 360 is formed, thesolder balls 502 may be formed, in a ball-grid-array arrangement, on themetal pads 310 b of thesubstrate 300 using a ball placement process. The process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as shown inFIG. 6S can be referred to as the process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as illustrated inFIGS. 6F and 6G . The specification of thesolder balls 502 shown inFIG. 6S can be referred to as the specification of thesolder balls 502 illustrated inFIGS. 6F and 6G . - Thereby, the fine-pitched
metal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 44 by bonding thesemiconductor chip 2 with theflexible circuit film 44. Theflexible circuit film 44 is also bonded with thesubstrate 300 to connect the fine-pitchedmetal bumps 12 of thesemiconductor chip 2 with the circuit structure of thesubstrate 300. Thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 44 and the circuit structure of thesubstrate 300. - Alternatively, the step of forming the
polymer compound 360, as shown inFIG. 6R , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 44 are uncovered by any polymer compound. Alternatively, the step of forming thepolymer layer 350 a, as shown inFIG. 6Q , can be omitted. Alternatively, the steps of forming thepolymer layer 350 a, as shown inFIG. 6Q , and of forming thepolymer compound 360, as shown inFIG. 6R , can be omitted, that is, thesemiconductor chip 2 and theflexible circuit film 44 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 6R . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 6Q . Thesemiconductor chip 2 and theflexible circuit film 44 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a and thesolder balls 502 can be omitted, as shown inFIG. 6T . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a, thepolymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 6P . Thesemiconductor chip 2 and theflexible circuit film 44 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. -
FIG. 7A is a schematically cross-sectional figure showing a chip-on-film package. Aflexible circuit film 46 includes apolymer layer 200, apolymer layer 220, awirebondable layer 230, awetting layer 240 b and copper traces 210 between the polymer layers 200 and 220. Thewirebondable layer 230 is on first contact points, exposed byopenings 220 b, of the copper traces 210 in thepolymer layer 220, and thewetting layer 240 b is on second contact points, exposed byopenings 220 a, of the copper traces 210 in thepolymer layer 220. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 7A can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewetting layer 240 b shown inFIG. 7A can be referred to as the specification of thewetting layer 240 b illustrated inFIGS. 3B and 3C . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The
wirebondable layer 230 having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, aluminum, nickel, silver, palladium or a composite of the above-mentioned materials. For example, thewirebondable layer 230 may be a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 1 micrometer, on the first contact points, exposed by theopenings 220 b, of the copper traces 210 in thepolymer layer 220. Alternatively, thewirebondable layer 230 may be a palladium layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 1 micrometer, on the first contact points, exposed by theopenings 220 b, of the copper traces 210 in thepolymer layer 220. Alternatively, thewirebondable layer 230 may be a silver layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the first contact points, exposed by theopenings 220 b, of the copper traces 210 in thepolymer layer 220. Alternatively, thewirebondable layer 230 may be an aluminum layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the first contact points, exposed by theopenings 220 b, of the copper traces 210 in thepolymer layer 220. Alternatively, thewirebondable layer 230 comprises a nickel layer having a thickness of between 0.05 and 1 micrometer on the first contact points, exposed by theopenings 220 b, of the copper traces 210 in thepolymer layer 220, and a gold layer having a thickness of between 0.05 and 1 micrometer on the nickel layer. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210, exposed by theopenings 220 a, of theflexible circuit film 46 through aninterface bonding layer 250. The specification of theinterface bonding layer 250 shown inFIG. 7A can be referred to as the specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 46, as shown inFIG. 7A can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 36, as illustrated in the first and second cases shown inFIGS. 3B and 3C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 7A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 7A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIG. 7B , apolymer layer 260 is filled into the gap between thesemiconductor chip 2 and theflexible circuit film 46, enclosing the metal bumps 12, by dispensing a polymer on theflexible circuit film 46 close to thesemiconductor chip 2, with the polymer flowing into the gap between thesemiconductor chip 2 and theflexible circuit film 46, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester, polybenzoxazole or polyimide. - A
substrate 300 a comprises a circuit structure in thesubstrate 300 a, an insulatinglayer 320, an insulatinglayer 330,wirebonding pads 310 c andmetal pads 310 b. The circuit structure comprises copper traces (including 340 a and 340 b) each having a thickness between 5 and 30 micrometers. Thewirebonding pads 310 c are formed on the topmost copper traces 340 a exposed by openings in the insulatinglayer 320, and the openings may be filled up with thewirebonding pads 310 c. Themetal pads 310 b are formed on the bottommost copper traces 340 b exposed byopenings 330 a in the insulatinglayer 330. Thewirebonding pads 310 c are connected to themetal pads 310 b through the copper traces (comprising the copper traces 340 a and 340 b) in thesubstrate 300 a. The specification of themetal pads 310 b, the insulatinglayer 320 and the insulatinglayer 330 shown inFIG. 7B can be referred to as the specification of themetal pads 310 b, the insulatinglayer 320 and the insulatinglayer 330 illustrated inFIG. 3E . - The material of the
wirebonding pads 310 c may be gold, copper, nickel, aluminum, palladium, silver or a composite of the above-mentioned materials, and thewirebonding pads 310 c have a thickness t21 of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer. For example, thewirebonding pads 310 c may be formed by electroplating or electroless plating a gold layer with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 1 micrometer, on the topmost copper traces 340 a exposed by openings in the insulatinglayer 320, and the openings in the insulatinglayer 320 may be filled up with the gold layer. Alternatively, thewirebonding pads 310 c may be formed by electroplating or electroless plating a palladium layer with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 1 micrometer, on the topmost copper traces 340 a exposed by openings in the insulatinglayer 320, and the openings in the insulatinglayer 320 may be filled up with the palladium layer. Alternatively, thewirebonding pads 310 c may be formed by electroplating or electroless plating a silver layer with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the topmost copper traces 340 a exposed by openings in the insulatinglayer 320, and the openings in the insulatinglayer 320 may be filled up with the silver layer. Alternatively, thewirebonding pads 310 c may be formed by electroplating or electroless plating an aluminum layer with a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the topmost copper traces 340 a exposed by openings in the insulatinglayer 320, and the openings in the insulatinglayer 320 may be filled up with the aluminum layer. Alternatively, thewirebonding pads 310 c may be formed by electroless plating a nickel layer with a thickness of between 0.05 and 1 micrometer on the topmost copper traces 340 a exposed by openings in the insulatinglayer 320, and electroless plating a gold layer with a thickness of between 0.05 and 1 micrometer on the nickel layer in the openings in the insulatinglayer 320, and the openings in the insulatinglayer 320 may be filled up with the nickel layer and the gold layer. - In a case, the
substrate 300 a may comprise a core layer, such as a glass fiber reinforced epoxy with a thickness of between 200 and 2,000 μm, multiple copper circuit layers respectively over and under the core layer, and multiple polymer layers between the neighboring copper circuit layers. The copper circuit layers provide the circuit structure in thesubstrate 300 a. Thewirebonding pads 310 c are on the copper traces 340 a of the topmost copper circuit layer, and themetal pads 310 b are on the copper traces 340 b of the bottommost copper circuit layer. - In another case, the
substrate 300 a may comprise multiple copper circuit layers and multiple ceramic layers between the neighboring copper circuit layers. The copper circuit layers provide the circuit structure in thesubstrate 300 a. Thewirebonding pads 310 c are on the copper traces 340 a of the topmost copper circuit layer, and themetal pads 310 b are on the copper traces 340 b of the bottommost copper circuit layer. - The
substrate 300 a may be a ball grid array (BGA) substrate with a thickness t22 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 a may be a glass fiber reinforced epoxy based substrate with a thickness t22 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 a may be a silicon substrate with a thickness t22 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 a may be a ceramic substrate with a thickness t22 of between 200 and 2,000 μm. Alternatively, thesubstrate 300 a may be an organic substrate with a thickness t22 of between 200 and 2,000 μm. - Referring to
FIGS. 7B and 7C , aglue material 650 is first formed on the insulatinglayer 320 of thesubstrate 300 a by a dispensing process after thesemiconductor chip 2 is bonded with theflexible circuit film 46. Next, thepolymer layer 200 of theflexible circuit film 46 adheres onto theglue material 650, and then theglue material 650 is baked at a temperature of between 100 and 200° C. and to a thickness t23 between 5 and 30 micrometers if theglue material 650 is an epoxy. Alternatively, theglue material 650 can be polyimide, silver-filed epoxy or polyester. Thereby, theflexible circuit film 46 can be joined with thesubstrate 300 a. In another word, theflexible circuit film 46 bonded with thesemiconductor chip 2 can be joined with thesubstrate 300 a using theglue material 650. - Referring to
FIG. 7C , there is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300 a. - Referring to
FIG. 7D , after theflexible circuit film 46 is joined with thesubstrate 300 a,wireboning wires 400 having a diameter of between 12 and 40 micrometers are bonded with thewirebondable layer 230 and with thewirebonding pads 310 c via a wire-bonding process. Thewireboning wires 400 may be gold wires with a diameter of between 12 and 40 micrometers. Thereby, thewirebondable layer 230 of theflexible circuit film 46 can be electrically connected to thewirebonding pads 310 c of thesubstrate 300 a through thewireboning wires 400. - Referring to
FIG. 7E , apolymer compound 360 is formed on thesemiconductor chip 2, on theflexible circuit film 46 and on a peripheral region of thesubstrate 300 a by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theflexible circuit film 46 and on the peripheral region of thesubstrate 300 a at a temperature of between 130 and 250° C. Thepolymer compound 360 encloses thewireboning wires 400, to protect thewireboning wires 400. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 7F , after thepolymer compound 360 is formed, thesolder balls 502 may be formed, in a ball-grid-array arrangement, on themetal pads 310 b of thesubstrate 300 a using a ball placement process. The process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300 a, as shown inFIG. 7F can be referred to as the process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as illustrated inFIGS. 3J and 3K . The specification of thesolder balls 502 shown inFIG. 7F can be referred to as the specification of thesolder balls 502 illustrated inFIGS. 3J and 3K . After thesolder balls 502 are formed on thesubstrate 300 a, thesubstrate 300 a and thepolymer compound 360 can be optionally cut into multiple units. -
FIG. 7G is a perspective view showingFIG. 7F . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 46 by bonding thesemiconductor chip 2 with theflexible circuit film 46. Theflexible circuit film 46 is also joined with thesubstrate 300 a, and thewireboning wires 400 connect theflexible circuit film 46 to thesubstrate 300 a. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 46, thewirebonding wires 400 and the circuit structure of thesubstrate 300 a. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 7E . Thesubstrate 300 a can be optionally sawed into multiple units. After sawing thesubstrate 300 a, themetal pads 310 b of thesubstrate 300 a can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. -
FIG. 7H is a schematically cross-sectional figure showing a chip package including thesemiconductor chip 2 joined with aflexible circuit substrate 48 using a tape-automated-bonding (TAB) technology. The above-mentionedflexible circuit film 46 can be replaced by theflexible circuit film 48. Theflexible circuit film 48 includes thepolymer layer 200, thepolymer layer 220, thewirebondable layer 230, thewetting layer 240 b and the copper traces 210 between the polymer layers 200 and 220, wherein theopenings 220 b in thepolymer layer 220 expose contact points of the copper traces 210, and the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the center portion of theflexible circuit film 48. Thewirebondable layer 230 is on the contact points, exposed byopenings 220 b, of the copper traces 210 in thepolymer layer 220, and thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 48. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 7H can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewirebondable layer 230 shown inFIG. 7H can be referred to as the specification of thewirebondable layer 230 illustrated inFIG. 7A . The specification of thewetting layer 240 b shown inFIG. 7H can be referred to as the specification of thewetting layer 240 b illustrated inFIG. 3S . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 48 through theinterface bonding layer 250. The specification of theinterface bonding layer 250 shown inFIG. 7H can be referred to as the specification of theinterface bonding layer 250 formed in the process as illustrated in the first case shown inFIGS. 3R and 3S . The method, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 48, as shown inFIG. 7H can be referred to as the method, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 38, as illustrated in the first and second cases shown inFIGS. 3R and 3S . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 7H can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3R and 3S . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 7H can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the as illustrated in the second case shown inFIG. 3S . - Referring to
FIG. 7I , thepolymer layer 260 can be formed by dispensing a polymer on thesemiconductor chip 2 with the polymer enclosing the metal bumps 12 and the copper traces 210 at the center portion of theflexible circuit film 48, and then curing the polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester or polyimide. The specification of thesubstrate 300 a shown inFIG. 7I can be referred to as the specification of thesubstrate 300 a illustrated inFIG. 7B . - Referring to
FIGS. 7I and 7J , theglue material 650 is first formed on the insulatinglayer 320 of thesubstrate 300 a by a dispensing process after thesemiconductor chip 2 is bonded with theflexible circuit film 48. Next, thepolymer layer 200 of theflexible circuit film 48 adheres onto theglue material 650, and then theglue material 650 is baked at a temperature of between 100 and 200° C. and to a thickness t23 between 5 and 30 micrometers if theglue material 650 is an epoxy. Alternatively, theglue material 650 can be polyimide or polyester. Thereby, theflexible circuit film 48 can be joined with thesubstrate 300 a. In another word, theflexible circuit film 48 bonded with thesemiconductor chip 2 can be joined with thesubstrate 300 a using theglue material 650. - Referring to
FIG. 7J , there is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300 a. - Referring to
FIG. 7K , after theflexible circuit film 48 is joined with thesubstrate 300 a, thewireboning wires 400 having a diameter of between 12 and 40 micrometers are bonded with thewirebondable layer 230 and with thewirebonding pads 310 c via a wire-bonding process. Thewireboning wires 400 may be gold wires with a diameter of between 12 and 40 micrometers. Thereby, thewirebondable layer 230 of theflexible circuit film 48 can be electrically connected to thewirebonding pads 310 c of thesubstrate 300 a through thewireboning wires 400. - Referring to
FIG. 7L , thepolymer compound 360 is formed on thesemiconductor chip 2, on theflexible circuit film 48 and on a peripheral region of thesubstrate 300 a by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theflexible circuit film 48 and on the peripheral region of thesubstrate 300 a at a temperature of between 130 and 250° C. Thepolymer compound 360 encloses thewireboning wires 400, to protect thewireboning wires 400. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 7M , after thepolymer compound 360 is formed, thesolder balls 502 may be formed, in a ball-grid-array arrangement, on themetal pads 310 b of thesubstrate 300 a using a ball placement process. The process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300 a, as shown inFIG. 7M can be referred to as the process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as illustrated inFIGS. 3J and 3K . The specification of thesolder balls 502 shown inFIG. 7M can be referred to as the specification of thesolder balls 502 illustrated inFIGS. 3J and 3K . After thesolder balls 502 are formed on thesubstrate 300 a, thesubstrate 300 a and thepolymer compound 360 can be optionally cut into multiple units. - The fine-pitched
metal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 48 by bonding thesemiconductor chip 2 with theflexible circuit film 48. Theflexible circuit film 48 is also joined with thesubstrate 300 a, and thewireboning wires 400 connect theflexible circuit film 48 to thesubstrate 300 a. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 48, thewirebonding wires 400 and the circuit structure of thesubstrate 300 a. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 7L . Thesubstrate 300 a can be optionally sawed into multiple units. After sawing thesubstrate 300 a, themetal pads 310 b of thesubstrate 300 a can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. -
FIG. 8A is a schematically cross-sectional figure showing a chip-on-film package. Aflexible circuit film 42 includes apolymer layer 200, apolymer layer 220, awetting layer 240 b, awetting layer 240 c and copper traces 210 between the polymer layers 200 and 220, wherein the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the outer portion of theflexible circuit film 42, andopenings 220 a in thepolymer layer 220expose contact points wetting layer 240 b is on the contact points 71, 72, 73 and 74 of the copper traces 210 exposed by theopenings 220 a in thepolymer layer 220. Thewetting layer 240 c is on the copper traces 210 at the outer portion of theflexible circuit film 42. The specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 shown inFIG. 8A can be referred to as the specification of thepolymer layer 200, thepolymer layer 220 and the copper traces 210 illustrated inFIG. 3A . The specification of thewetting layer 240 b shown inFIG. 8A can be referred to as the specification of thewetting layer 240 b illustrated inFIGS. 3B and 3C . The specification of thewetting layer 240 c shown inFIG. 8A can be referred to as the specification of thewetting layer 240 c illustrated inFIG. 6A . Alternatively, the copper traces 210 can be replaced by gold traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. Alternatively, the copper traces 210 can be replaced by silver traces having a thickness of between 3 and 30 μm, of between 5 and 20 micrometers or of between 4 and 10 micrometers. - The metal bumps 12 of the
semiconductor chip 2 are bonded with the contact points 71 and 72, exposed by theopenings 220 a, of the copper traces 210 of theflexible circuit film 42 through aninterface bonding layer 250, andmultiple metal bumps 62 of anelectronic device 60 are bonded with the contact points 73 and 74, exposed by theopenings 220 a, of the copper traces 210 of theflexible circuit film 42 through aninterface bonding layer 255. Theelectronic device 60 can be a passive device, such as resistor, capacitor or inductor, or another semiconductor chip. Thesemiconductor chip 2 is connected to theelectronic device 60 through thecopper trace 210 at the center portion of theflexible circuit film 42. A method for bonding the metal bumps 12 of thesemiconductor chip 2 with the contact points 71 and 72 of the copper traces 210 of theflexible circuit film 42, and for bonding the metal bumps 62 of theelectronic device 60 with the contact points 73 and 74 of the copper traces 210 of theflexible circuit film 42 are described as shown inFIG. 8B andFIG. 8C . - Referring to
FIGS. 8B and 8C , theflexible circuit film 42 can be connected to thesemiconductor chip 2 and to theelectronic device 60. Theflexible circuit film 42 has thewetting layer 240 c to be joined with thesubstrate 300 shown inFIG. 3E , and thewetting layer 240 b to be joined with the metal bumps 12 of thesemiconductor chip 2 and with the metal bumps 62 of theelectronic device 60. The metal bumps 62 of theelectronic device 60 having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers, may comprise gold, copper, nickel, silver, tin, palladium or a composite of the above-mentioned materials. A pitch between the neighboring metal bumps 62 is greater than 1 micrometer, greater than 5 micrometers, less than 35 micrometers, less than 30 micrometers, less than 25 micrometers or less than 20 micrometers, such as between 1 and 30 micrometers or between 2 and 20 micrometers. For example, the metal bumps 62 may be gold bumps having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers. Alternatively, the metal bumps 62 may be copper bumps having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers. Alternatively, the metal bumps 62 may be tin-containing bumps having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers, wherein the tin-containing bumps may be made of a lead-free solder, such as a tin-silver alloy or a tin-silver-copper alloy, of an eutectic solder, such as a tin-lead alloy, or of a high-lead solder containing more than 90 weight percent of lead. Alternatively, the metal bumps 62 may comprise a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer. - In a first case, referring to
FIGS. 8B and 8C , the metal bumps 12 and 62 have the above-mentioned gold layer, at the tips of the metal bumps 12 and 62, capable of being used to be joined with thewetting layer 240 b of pure tin or an above-mentioned tin alloy using flip-chip bonding, which method is described as below. First, theflexible circuit film 42 is placed on astage 600 a kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., and thesemiconductor chip 2 is held by vacuum adsorption on atool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C. Next, thesemiconductor chip 2 is thermally pressed on thewetting layer 240 b of theflexible circuit film 42 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 42, to join the metal bumps 12 with thewetting layer 240 b. In the step of joining the metal bumps 12 with thewetting layer 240 b, theinterface bonding layer 250, such as a metal alloy, may be formed between the metal bumps 12 and the contact points 71 and 72 of the copper traces 210. Theinterface bonding layer 250 between the metal bumps 12 and the contact points 71 and 72 of the copper traces 210 has a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is pure tin, theinterface bonding layer 250 is a tin-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers, wherein an atomic ratio of tin to gold in the tin-gold alloy is between 0.2 and 0.3. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-silver-copper alloy, theinterface bonding layer 250 is a tin-silver-gold-copper alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 12 is a tin-silver alloy, theinterface bonding layer 250 is a tin-silver-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. Next, thetool head 610 a is removed from thesemiconductor chip 2. Next, theelectronic device 60 is held by vacuum adsorption on thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C. Next, theelectronic device 60 is thermally pressed on thewetting layer 240 b of theflexible circuit film 42 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C., optionally applying ultrasonic waves to the metal bumps 62 and to thewetting layer 240 b of theflexible circuit film 42, to join the metal bumps 62 with thewetting layer 240 b. Referring toFIGS. 8A and 8C , in the step of joining the metal bumps 62 with thewetting layer 240 b, theinterface bonding layer 255, such as a metal alloy, may be formed between the metal bumps 62 and the contact points 73 and 74 of the copper traces 210. Theinterface bonding layer 255 between the metal bumps 62 and the contact points 73 and 74 of the copper traces 210 has a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 62 is pure tin, theinterface bonding layer 255 is a tin-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers, wherein an atomic ratio of tin to gold in the tin-gold alloy is between 0.2 and 0.3. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 62 is a tin-silver-copper alloy, theinterface bonding layer 255 is a tin-silver-gold-copper alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. When thewetting layer 240 b before bonded with the gold layer of the metal bumps 62 is a tin-silver alloy, theinterface bonding layer 255 is a tin-silver-gold alloy having a thickness of between 0.2 and 10 micrometers or of between 0.4 and 5 micrometers. Next, thetool head 610 a is removed from theelectronic device 60. Next, theflexible circuit film 42 bonded with thesemiconductor chip 2 and with theelectronic device 60 is removed from thestage 600 a. - The specification of the metal bumps 12 between the
semiconductor chip 2 and theinterface bonding layer 250 shown inFIGS. 8A and 8C can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . - The metal bumps 62 bonded with the contact points 73 and 74 of the copper traces 210 of the
flexible circuit film 42 have a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers. For example, the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 may include a gold layer having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers, between theelectronic device 60 and theinterface bonding layer 255. Alternatively, the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 may include a copper layer having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers, between theelectronic device 60 and theinterface bonding layer 255. Alternatively, the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 may include a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, between theelectronic device 60 and theinterface bonding layer 255, a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and theinterface bonding layer 255, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer and between the nickel layer and theinterface bonding layer 255. Alternatively, the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 may include a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, between theelectronic device 60 and theinterface bonding layer 255, and a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and theinterface bonding layer 255. Alternatively, the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 may include a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, between theelectronic device 60 and theinterface bonding layer 255, and a gold layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and theinterface bonding layer 255. - In a second case, referring to
FIGS. 8B and 8C , the metal bumps 12 and 62 have the above-mentioned gold layer, at the tips of the metal bumps 12 and 62, capable of being used to be joined with a gold layer of thewetting layer 240 b using flip-chip bonding, which method is described as below. First, theflexible circuit film 42 is placed on thestage 600 a kept at a temperature of between 150 and 450° C., and preferably of between 250 and 400° C., and thesemiconductor chip 2 is held by vacuum adsorption on thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C. Next, thesemiconductor chip 2 is thermally pressed on thewetting layer 240 b of theflexible circuit film 42 at a force of between 20 and 150N, and preferably of between 70 and 120N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C., optionally applying ultrasonic waves to the metal bumps 12 and to thewetting layer 240 b of theflexible circuit film 42, to join the above-mentioned gold layer of the metal bumps 12 with the gold layer of thewetting layer 240 b. Next, thetool head 610 a is removed from thesemiconductor chip 2. Next, theelectronic device 60 is held by vacuum adsorption on thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C. Next, theelectronic device 60 is thermally pressed on thewetting layer 240 b of theflexible circuit film 42 at a force of between 20 and 150N, and preferably of between 70 and 120N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by thetool head 610 a kept at a temperature of between 250 and 500° C., of between 350 and 450° C. or of between 100 and 500° C., optionally applying ultrasonic waves to the metal bumps 62 and to thewetting layer 240 b of theflexible circuit film 42, to join the above-mentioned gold layer of the metal bumps 62 with the gold layer of thewetting layer 240 b. Next, thetool head 610 a is removed from theelectronic device 60. Next, theflexible circuit film 42 bonded with thesemiconductor chip 2 and with theelectronic device 60 is removed from thestage 600 a. - Thereby, the
pads 18 of thesemiconductor chip 2 can be connected to the contact points 71 and 72 of the copper traces 210 of theflexible circuit film 42 through gold joints formed by joining the above-mentioned gold layer of the metal bumps 12 with the gold layer of thewetting layer 240 b. The specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIGS. 8B and 8C can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - The
electronic device 60 can be connected to the contact points 73 and 74 of the copper traces 210 of theflexible circuit film 42 through gold joints formed by joining the above-mentioned gold layer of the metal bumps 62 with the gold layer of thewetting layer 240 b. For example, the metal bumps 62 between theelectronic device 60 and the contact points 73 and 74 of the copper traces 210 may include a gold joint having a thickness of between 5 and 200 micrometers, and preferably of between 10 and 50 micrometers, between theelectronic device 60 and the contact points 73 and 74 of the copper traces 210. Alternatively, the metal bumps 62 between theelectronic device 60 and the contact points 73 and 74 of the copper traces 210 may include a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 micrometers, between theelectronic device 60 and the contact points 73 and 74 of the copper traces 210, a nickel layer having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and the contact points 73 and 74 of the copper traces 210, and a gold joint having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the nickel layer and between the nickel layer and the contact points 73 and 74 of the copper traces 210. Alternatively, the metal bumps 62 between between theelectronic device 60 and the contact points 73 and 74 of the copper traces 210 may include a copper layer having a thickness of between 0.5 and 45 micrometers, and preferably of between 5 and 35 μm, between theelectronic device 60 and the contact points 73 and 74 of the copper traces 210, and a gold joint having a thickness of between 0.5 and 5 micrometers, and preferably of between 1 and 3 micrometers, on the copper layer and between the copper layer and the contact points 73 and 74 of the copper traces 210. - Referring to
FIG. 8D , apolymer layer 260 is filled into the gap between thesemiconductor chip 2 and theflexible circuit film 42 and into the gap between theelectronic device 60 and theflexible circuit film 42, enclosing the metal bumps 12 and 62, by dispensing a polymer on theflexible circuit film 42 close to thesemiconductor chip 2 and close to theelectronic device 60, with the polymer flowing into the gap between thesemiconductor chip 2 and theflexible circuit film 42 and into the gap between theelectronic device 60 and theflexible circuit film 42, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 260 may be expoxy, polyester, polybenzoxazole or polyimide. - Referring to
FIG. 8E , theflexible circuit film 42 is joined with thesubstrate 300 shown inFIG. 6B by joining thewetting layer 240 c of theflexible circuit film 42 with themetal joints 410 c, shown inFIG. 6B , screen printed on themetal pads 310 a of thesubstrate 300 in advance, wherein themetal joints 410 c may be pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. There is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300. The methods of bonding theflexible circuit film 42 with thesubstrate 300, as shown inFIG. 8E , can be referred to as the methods of bonding theflexible circuit film 42 with thesubstrate 300, as illustrated in the first and second cases shown inFIGS. 6B and 6C . - Alternatively, the
metal joints 410 d can be replaced by an anisotropic conductive film (ACF). The anisotropic conductive film can be preformed on themetal pads 310 a of thesubstrate 300 shown inFIG. 3E , and then thewetting layer 240 c on the copper traces 210 at the outer portion of theflexible circuit film 42 can be pressed on the anisotropic conductive film, such that metal particles in the anisotropic conductive film connects thewetting layer 240 c of theflexible circuit film 42 to themetal pads 310 a of thesubstrate 300. - Referring to
FIG. 8F , after theflexible circuit film 42 is bonded with thesubstrate 300, apolymer layer 350 a can be filled into the gap between theflexible circuit film 42 and thesubstrate 300, enclosing themetal joints 410 d and thewetting layer 240 c, by dispensing a polymer on thesubstrate 300 close to theflexible circuit film 42, with the polymer flowing into the gap between theflexible circuit film 42 and thesubstrate 300, and then curing the flowing polymer at a temperature of between 100 and 250° C. The material of thepolymer layer 350 a may be expoxy, polyester or polyimide, and thepolymer layer 350 a between theflexible circuit film 42 and thesubstrate 300 has a thickness t20 of between 1 and 30 micrometers. - Referring to
FIG. 8G , apolymer compound 360 is formed on thesemiconductor chip 2, on theelectronic device 60, on theflexible circuit film 42 and on a peripheral region of thesubstrate 300 by molding an epoxy-based polymer with carbon fillers therein on thesemiconductor chip 2, on theelectronic device 60, on theflexible circuit film 42 and on the peripheral region of thesubstrate 300 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 360 can be polyimide or polyester. Preferably, thepolymer compound 360 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 8H , after thepolymer compound 360 is formed,solder balls 502 may be formed, in a ball-grid-array arrangement, on themetal pads 310 b of thesubstrate 300 using a ball placement process. The process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as shown inFIG. 8H can be referred to as the process, of forming thesolder balls 502 on themetal pads 310 b of thesubstrate 300, as illustrated inFIGS. 6F and 6G . The specification of thesolder balls 502 shown inFIG. 8H can be referred to as the specification of thesolder balls 502 illustrated inFIGS. 6F and 6G . After thesolder balls 502 are formed on thesubstrate 300, thesubstrate 300 and thepolymer compound 360 can be optionally cut into multiple units. -
FIG. 8I is a perspective view showingFIG. 8H . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 42 by bonding thesemiconductor chip 2 with theflexible circuit film 42. Theelectronic device 60 is also can be fanned out through the copper traces 210 of theflexible circuit film 42 by bonding theelectronic device 60 with theflexible circuit film 42, and theelectronic device 60 is connected to thesemiconductor chip 2 through the copper traces 210 of theflexible circuit film 42. Theflexible circuit film 42 is bonded with thesubstrate 300 to connect the fine-pitchedmetal bumps 12 of thesemiconductor chip 2 with the circuit structure of thesubstrate 300, and to connect theelectronic device 60 with the circuit structure of thesubstrate 300. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 42 and the circuit structure of thesubstrate 300, and to theelectronic device 60 through the copper traces 210 of theflexible circuit film 42. - Alternatively, referring to
FIGS. 8J and 8K , the step of forming thepolymer compound 360, as shown inFIG. 8G , can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 42 are uncovered by any polymer compound. Alternatively, referring toFIG. 8L , the step of forming thepolymer layer 350 a, as shown inFIG. 8F , can be omitted. Alternatively, referring toFIG. 8M , the steps of forming thepolymer layer 350 a, as shown inFIG. 8F , and of forming thepolymer compound 360, as shown inFIG. 8G , can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 42 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 can be omitted, as shown inFIG. 8G . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 8F . Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 42 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a and thesolder balls 502 can be omitted, as shown inFIG. 8N . Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a, thepolymer compound 360 and thesolder balls 502 can be omitted, as shown inFIG. 8E . Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 42 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIG. 8O , the above-mentionedflexible circuit film 42 shown inFIG. 8H can be replaced by aflexible circuit film 44, that is, thesemiconductor chip 2 and theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 44, followed by forming thepolymer layer 260 on thesemiconductor chip 2 and on theelectronic device 60, enclosing the metal bumps 12, the metal bumps 62 and thewetting layer 240 b, followed by performing the above-mentioned steps as shown inFIGS. 8E-8H . Theflexible circuit film 44 includes thepolymer layer 200, thepolymer layer 220, thewetting layer 240 b, thewetting layer 240 c and the copper traces 210 between the polymer layers 200 and 220, wherein the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the center portion and the outer portion of theflexible circuit film 44. Thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 44, and thewetting layer 240 c is on the copper traces 210 at the outer portion of theflexible circuit film 44. There is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300. The metal bumps 12 of thesemiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 44 through theinterface bonding layer 250, and the metal bumps 62 of theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 44 through theinterface bonding layer 255. - The specification of the
interface bonding layer 250 shown inFIG. 8O can be referred to as the specification of theinterface bonding layer 250 between the metal bumps 12 and the copper traces 210 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The specification of theinterface bonding layer 255 shown inFIG. 8O can be referred to as the specification of theinterface bonding layer 255 formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 44, as shown inFIG. 8O can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 42, as illustrated in the first and second cases shown inFIGS. 8B and 8C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 8O can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 8O can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . When the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 shown inFIG. 8O can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and theinterface bonding layer 255, formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. Alternatively, when the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and the copper traces 210 shown inFIG. 8O can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and the copper traces 210, formed in the process as illustrated in the second case shown inFIGS. 8B and 8C . - Alternatively, the
metal joints 410 d shown inFIG. 8O can be replaced by an anisotropic conductive film (ACF). The anisotropic conductive film can be preformed on themetal pads 310 a of thesubstrate 300 shown inFIG. 3E , and then thewetting layer 240 c on the copper traces 210 at the outer portion of theflexible circuit film 44 can be pressed on the anisotropic conductive film, such that metal particles in the anisotropic conductive film connects thewetting layer 240 c of theflexible circuit film 44 to themetal pads 310 a of thesubstrate 300. - Alternatively, the
polymer compound 360 shown inFIG. 8O can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 44 are uncovered by any polymer compound. Alternatively, thepolymer layer 350 a shown inFIG. 8O can be omitted. Alternatively, thepolymer layer 350 a and thepolymer compound 360 shown inFIG. 8O can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 44 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 shown inFIG. 8O can be omitted. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 shown inFIG. 8O can be omitted. Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 44 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a and thesolder balls 502 shown inFIG. 8O can be omitted. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 a, thepolymer compound 360 and thesolder balls 502 shown inFIG. 8O can be omitted. Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 44 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIGS. 8P and 8Q , the above-mentionedflexible circuit film 42 shown inFIG. 8H can be replaced by aflexible circuit film 46, and thesubstrate 300 shown inFIG. 8H can be replaced by thesubstrate 300 a shown inFIG. 7B , that is, thesemiconductor chip 2 and theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 46, followed by performing the above-mentioned step as shown inFIG. 8D , followed by joining theflexible circuit film 46, bonded with thesemiconductor chip 2 and with theelectronic device 60, with thesubstrate 300 a using aglue material 650, followed bybonding wireboning wires 400, such as gold wires, having a diameter of between 12 and 40 micrometers with awirebondable layer 230 of theflexible circuit film 46 and with thewirebonding pads 310 c of thesubstrate 300 a via a wire-bonding process, followed by performing the above-mentioned steps as shown inFIGS. 8G-8H . - The
flexible circuit film 46 includes thepolymer layer 200, thepolymer layer 220, thewirebondable layer 230, thewetting layer 240 b and the copper traces 210 between the polymer layers 200 and 220. Thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 46, and thewirebondable layer 230 is on the copper traces 210 at the outer portion of theflexible circuit film 46. Thewirebondable layer 230 having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, aluminum, nickel, silver, palladium or a composite of the above-mentioned materials. For example, thewirebondable layer 230 may be a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 1 micrometer, on the copper traces 210 at the outer portion of theflexible circuit film 46. Alternatively, thewirebondable layer 230 may be a palladium layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 1 micrometer, on the copper traces 210 at the outer portion of theflexible circuit film 46. Alternatively, thewirebondable layer 230 may be a silver layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the copper traces 210 at the outer portion of theflexible circuit film 46. Alternatively, thewirebondable layer 230 may be an aluminum layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.1 and 1 micrometer, on the copper traces 210 at the outer portion of theflexible circuit film 46. Alternatively, thewirebondable layer 230 comprises a nickel layer having a thickness of between 0.05 and 1 micrometer on the copper traces 210 at the outer portion of theflexible circuit film 46, and a gold layer having a thickness of between 0.05 and 1 micrometer on the nickel layer. There is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300 a. The metal bumps 12 of thesemiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 46 through theinterface bonding layer 250, and the metal bumps 62 of theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 46 through theinterface bonding layer 255. - The specification of the
substrate 300 a shown inFIG. 8P can be referred to as the specification of thesubstrate 300 a illustrated inFIG. 7B . The specification of theinterface bonding layer 250 shown inFIG. 8P can be referred to as the specification of theinterface bonding layer 250 between the metal bumps 12 and the copper traces 210 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The specification of theinterface bonding layer 255 shown inFIG. 8P can be referred to as the specification of theinterface bonding layer 255 formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. The specification of theglue material 650 shown inFIG. 8P can be referred to as the specification of theglue material 650 illustrated inFIGS. 7B and 7C . The process, of forming theglue material 650, as shown inFIG. 8P can be referred to as the process, of forming theglue material 650, as illustrated inFIGS. 7B and 7C . The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 46, as shown inFIG. 8P can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 42, as illustrated in the first and second cases shown inFIGS. 8B and 8C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 8P can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 8P can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . When the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 shown inFIG. 8P can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and theinterface bonding layer 255, formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. Alternatively, when the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and the copper traces 210 shown inFIG. 8P can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and the copper traces 210, formed in the process as illustrated in the second case shown inFIGS. 8B and 8C . - Alternatively, the
solder balls 502 shown inFIGS. 8P and 8Q can be omitted. Thesubstrate 300 a can be optionally sawed into multiple units. After sawing thesubstrate 300 a, themetal pads 310 b of thesubstrate 300 a can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIG. 8R , the above-mentionedflexible circuit film 42 shown inFIG. 8H can be replaced by aflexible circuit film 48, and thesubstrate 300 shown inFIG. 8H can be replaced by thesubstrate 300 a shown inFIG. 7B , that is, thesemiconductor chip 2 and theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 48, followed by forming thepolymer layer 260 on thesemiconductor chip 2 and on theelectronic device 60, enclosing the metal bumps 12, the metal bumps 62 and thewetting layer 240 b, followed by joining theflexible circuit film 48, bonded with thesemiconductor chip 2 and with theelectronic device 60, with thesubstrate 300 a using theglue material 650, followed by bonding thewireboning wires 400, such as gold wires, having a diameter of between 12 and 40 micrometers with thewirebondable layer 230 of theflexible circuit film 48 and with thewirebonding pads 310 c of thesubstrate 300 a via a wire-bonding process, followed by performing the above-mentioned steps as shown inFIGS. 8G-8H . - The
flexible circuit film 48 includes thepolymer layer 200, thepolymer layer 220, thewirebondable layer 230, thewetting layer 240 b and the copper traces 210 between the polymer layers 200 and 220, wherein the polymer layers 200 and 220 uncover top and bottom sides of the copper traces 210 at the center portion of theflexible circuit film 48. Thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 48, and thewirebondable layer 230 is on the copper traces 210 at the outer portion of theflexible circuit film 48. There is no opening in thepolymer layer 200 exposing the copper traces 210 to lead the copper traces 210 to be connected to thesubstrate 300 a. The metal bumps 12 of thesemiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 48 through theinterface bonding layer 250, and the metal bumps 62 of theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 48 through theinterface bonding layer 255. - The specification of the
substrate 300 a shown inFIG. 8R can be referred to as the specification of thesubstrate 300 a illustrated inFIG. 7B . The specification of thewirebondable layer 230 shown inFIG. 8R can be referred to as the specification of thewirebondable layer 230 illustrated inFIGS. 8P and 8Q . The specification of theinterface bonding layer 250 shown inFIG. 8R can be referred to as the specification of theinterface bonding layer 250 between the metal bumps 12 and the copper traces 210 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The specification of theinterface bonding layer 255 shown inFIG. 8R can be referred to as the specification of theinterface bonding layer 255 formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. The specification of theglue material 650 shown inFIG. 8R can be referred to as the specification of theglue material 650 illustrated inFIGS. 7B and 7C . The process, of forming theglue material 650, as shown inFIG. 8R can be referred to as the process, of forming theglue material 650, as illustrated inFIGS. 7B and 7C . The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 48, as shown inFIG. 8R can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 42, as illustrated in the first and second cases shown inFIGS. 8B and 8C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 8R can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 8R can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . When the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 shown inFIG. 8R can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and theinterface bonding layer 255, formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. Alternatively, when the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and the copper traces 210 shown inFIG. 8R can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and the copper traces 210, formed in the process as illustrated in the second case shown inFIGS. 8B and 8C . - Alternatively, the
solder balls 502 shown inFIG. 8R can be omitted. Thesubstrate 300 a can be optionally sawed into multiple units. After sawing thesubstrate 300 a, themetal pads 310 b of thesubstrate 300 a can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIG. 8S , the above-mentionedflexible circuit film 42 shown inFIG. 8H can be replaced by aflexible circuit film 36, that is, thesemiconductor chip 2 and theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 36, followed by performing the above-mentioned step as shown inFIG. 8D , followed by joining the copper traces 210 with tin-containing joints preformed on themetal pads 310 a of thesubstrate 300 to providemetal joints 410 b, such as tin-containing joints, between the copper traces 210 of theflexible circuit film 36 and the topmost copper traces 340 a of thesubstrate 300, followed by filling apolymer layer 350 into the gap between theflexible circuit film 36 and thesubstrate 300, enclosing themetal joints 410 b, followed by performing the above-mentioned steps as shown inFIGS. 8G-8H . - The
flexible circuit film 36 includes thepolymer layer 200, thepolymer layer 220, thewetting layer 240 a, thewetting layer 240 b and the copper traces 210 between the polymer layers 200 and 220. Thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 36, and thewetting layer 240 a is on the copper traces 210 at the outer portion of theflexible circuit film 36. Thewetting layer 240 a having a thickness of between 0.05 and 5 micrometers, and preferably of between 0.1 and 1 micrometer, may be gold, copper, nickel, silver, tin or a composite of the above-mentioned materials. For example, thewetting layer 240 a may be a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, having a thickness of between 0.05 and 5 micrometers, and preferably of between 0.1 and 1 micrometer, directly on the copper traces 210 at the outer portion of theflexible circuit film 36. Alternatively, thewetting layer 240 a may be a gold layer having a thickness of between 0.05 and 5 micrometers, and preferably of between 0.1 and 1 micrometer, directly on the copper traces 210 at the outer portion of theflexible circuit film 36; optionally, a nickel layer having a thickness between 0.05 and 1 micrometer may be between the copper traces 210 and the gold layer. The metal bumps 12 of thesemiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 36 through theinterface bonding layer 250, and the metal bumps 62 of theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 36 through theinterface bonding layer 255. - The specification of the
interface bonding layer 250 shown inFIG. 8S can be referred to as the specification of theinterface bonding layer 250 between the metal bumps 12 and the copper traces 210 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The specification of theinterface bonding layer 255 shown inFIG. 8S can be referred to as the specification of theinterface bonding layer 255 formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. The specification of themetal joints 410 b shown inFIG. 8S can be referred to as the specification of themetal joints 410 b formed in the process as illustrated in the first and second cases shown inFIGS. 3F and 3G . The specification of thepolymer layer 350 shown inFIG. 8S can be referred to as the specification of thepolymer layer 350 illustrated inFIG. 3H . The process, of forming thepolymer layer 350, as shown inFIG. 8S can be referred to as the process, of forming thepolymer layer 350, as illustrated inFIG. 3H . The methods, of joining theflexible circuit film 36 with the tin-containing joints preformed on themetal pads 310 a of thesubstrate 300, as shown inFIG. 8S can be referred to as the methods, of joining theflexible circuit film 36 with the tin-containingjoints 410 a preformed on themetal pads 310 a of thesubstrate 300, as illustrated in the first and second cases shown inFIGS. 3F and 3G . The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 36, as shown inFIG. 8S can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 42, as illustrated in the first and second cases shown inFIGS. 8B and 8C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 8S can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 8S can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . When the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 shown inFIG. 8S can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and theinterface bonding layer 255, formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. Alternatively, when the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and the copper traces 210 shown inFIG. 8S can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and the copper traces 210, formed in the process as illustrated in the second case shown inFIGS. 8B and 8C . - Alternatively, the
polymer compound 360 shown inFIG. 8S can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 36 are uncovered by any polymer compound. Alternatively, thepolymer layer 350 shown inFIG. 8S can be omitted. Alternatively, thepolymer layer 350 and thepolymer compound 360 shown inFIG. 8S can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 36 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 shown inFIG. 8S can be omitted. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 shown inFIG. 8S can be omitted. Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 36 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 and thesolder balls 502 shown inFIG. 8S can be omitted. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350, thepolymer compound 360 and thesolder balls 502 shown inFIG. 8S can be omitted. Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 36 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIG. 8T , the above-mentionedflexible circuit film 42 shown inFIG. 8H can be replaced by aflexible circuit film 38, that is, thesemiconductor chip 2 and theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 38, followed by forming thepolymer layer 260 on thesemiconductor chip 2 and on theelectronic device 60, enclosing the metal bumps 12, the metal bumps 62 and thewetting layer 240 b, followed by joining the copper traces 210 with tin-containing joints preformed on themetal pads 310 a of thesubstrate 300 to provide themetal joints 410 b, such as tin-containing joints, between the copper traces 210 of theflexible circuit film 38 and the topmost copper traces 340 a of thesubstrate 300, followed by filling thepolymer layer 350 into the gap between theflexible circuit film 38 and thesubstrate 300, enclosing themetal joints 410 b, followed by performing the above-mentioned steps as shown inFIGS. 8G-8H . - The
flexible circuit film 38 includes thepolymer layer 200, thepolymer layer 220, thewetting layer 240 a, thewetting layer 240 b and the copper traces 210 between the polymer layers 200 and 220. Thewetting layer 240 b is on the copper traces 210 at the center portion of theflexible circuit film 38, and thewetting layer 240 a is on the copper traces 210 at the outer portion of theflexible circuit film 38. The metal bumps 12 of thesemiconductor chip 2 are bonded with the copper traces 210 at the center portion of theflexible circuit film 38 through theinterface bonding layer 250, and the metal bumps 62 of theelectronic device 60 are bonded with the copper traces 210 at the center portion of theflexible circuit film 38 through theinterface bonding layer 255. The specification of thewetting layer 240 a shown inFIG. 8T can be referred to as the specification of thewetting layer 240 a illustrated inFIG. 8S . - The specification of the
interface bonding layer 250 shown inFIG. 8T can be referred to as the specification of theinterface bonding layer 250 between the metal bumps 12 and the copper traces 210 formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . The specification of theinterface bonding layer 255 shown inFIG. 8T can be referred to as the specification of theinterface bonding layer 255 formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. The specification of themetal joints 410 b shown inFIG. 8T can be referred to as the specification of themetal joints 410 b formed in the process as illustrated in the first and second cases shown inFIGS. 3F and 3G . The specification of thepolymer layer 350 shown inFIG. 8T can be referred to as the specification of thepolymer layer 350 illustrated inFIG. 3H . The process, of forming thepolymer layer 350, as shown inFIG. 8T can be referred to as the process, of forming thepolymer layer 350, as illustrated inFIG. 3H . The methods, of joining theflexible circuit film 38 with the tin-containing joints preformed on themetal pads 310 a of thesubstrate 300, as shown inFIG. 8S can be referred to as the methods, of joining theflexible circuit film 38 with the tin-containingjoints 410 a preformed on themetal pads 310 a of thesubstrate 300, as illustrated in the first and second cases shown inFIGS. 3F and 3G . The methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 38, as shown inFIG. 8T can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 and the metal bumps 62 of theelectronic device 60 with the copper traces 210 of theflexible circuit film 42, as illustrated in the first and second cases shown inFIGS. 8B and 8C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 8T can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 8T can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . When the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and theinterface bonding layer 255 shown inFIG. 8T can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and theinterface bonding layer 255, formed in the process as illustrated in the first case shown inFIGS. 8A , 8B and 8C. Alternatively, when the step of bonding a gold layer of the metal bumps 62 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 62 between theelectronic device 60 and the copper traces 210 shown inFIG. 8T can be referred to as the specification of the metal bumps 62, between theelectronic device 60 and the copper traces 210, formed in the process as illustrated in the second case shown inFIGS. 8B and 8C . - Alternatively, the
polymer compound 360 shown inFIG. 8T can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 38 are uncovered by any polymer compound. Alternatively, thepolymer layer 350 shown inFIG. 8T can be omitted. Alternatively, thepolymer layer 350 and thepolymer compound 360 shown inFIG. 8T can be omitted, that is, thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 38 are uncovered by any polymer compound. - Alternatively, the
solder balls 502 shown inFIG. 8T can be omitted. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer compound 360 and thesolder balls 502 shown inFIG. 8T can be omitted. Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 38 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350 and thesolder balls 502 shown inFIG. 8T can be omitted. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Alternatively, the
polymer layer 350, thepolymer compound 360 and thesolder balls 502 shown inFIG. 8T can be omitted. Thesemiconductor chip 2, theelectronic device 60 and theflexible circuit film 38 are uncovered by any polymer compound. Thesubstrate 300 can be optionally sawed into multiple units. After sawing thesubstrate 300, themetal pads 310 b of thesubstrate 300 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. - Referring to
FIG. 9A , alead frame 700 comprisesmultiple leads 701 and adie pad 702 surrounded by theleads 701. Both theleads 701 and thedie pad 702 are made of copper or a copper alloy. Awetting layer 510 is formed on theleads 701, and thewetting layer 510 may be a gold layer or a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. - The methods, of bonding the metal bumps 12 of the
semiconductor chip 2 with the copper traces 210 of theflexible circuit film 42, as shown inFIG. 9A can be referred to as the methods, of bonding the metal bumps 12 of thesemiconductor chip 2 with the copper traces 210 of theflexible circuit film 36, as illustrated in the first and second cases shown inFIGS. 3B and 3C . When the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a tin-containing layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and theinterface bonding layer 250 shown inFIG. 9A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and theinterface bonding layer 250, formed in the process as illustrated in the first case shown inFIGS. 3A and 3B . Alternatively, when the step of bonding a gold layer of the metal bumps 12 with thewetting layer 240 b of a gold layer is performed, the specification of the metal bumps 12 between thesemiconductor chip 2 and the copper traces 210 shown inFIG. 9A can be referred to as the specification of the metal bumps 12, between thesemiconductor chip 2 and the copper traces 210, formed in the process as illustrated in the second case shown inFIG. 3B . - Referring to
FIGS. 9A and 9B , aglue material 650 is first formed on thedie pad 702 of thelead frame 700 by a dispensing process after thesemiconductor chip 2 is bonded with the above-mentionedflexible circuit film 42 shown inFIG. 6B . Next, thepolymer layer 200 of theflexible circuit film 42 adheres onto theglue material 650, and then theglue material 650 is baked at a temperature of between 100 and 200° C. and to a thickness t23 between 5 and 30 micrometers if theglue material 650 is an epoxy. Alternatively, theglue material 650 can be polyimide or polyester. Thereby, theflexible circuit film 42 can be joined with thedie pad 702. In another word, theflexible circuit film 42 bonded with thesemiconductor chip 2 can be joined with thedie pad 702 using theglue material 650. - Referring to
FIG. 9C , after theflexible circuit film 42 is joined with thedie pad 702, the copper traces 210 at the outer portion of theflexible circuit film 42 are bonded with theleads 701 of thelead frame 700. Four methods of bonding the copper traces 210 at the outer portion of theflexible circuit film 42 with theleads 701 of thelead frame 700 are described as follow. - In a first case, referring to
FIGS. 9B and 9C , when thewetting layer 510 is a gold layer, thewetting layer 510 can be used to be joined with thewetting layer 240 c of pure tin or an above-mentioned tin alloy using a heat press process, which method is described as below. First, thelead frame 700 joined with theflexible circuit film 42 using theglue material 650 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, thewetting layer 240 c of theflexible circuit film 42 is thermally pressed on thewetting layer 510 on theleads 701 of thelead frame 700 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 c with thewetting layer 510. In the step of joining thewetting layer 240 c with thewetting layer 510,metal joints 512 can be formed between theleads 701 of thelead frame 700 and the copper traces 210 at the outer portion of theflexible circuit film 42. The metal joints 512 can be tin-containing joints having a thickness t24 of between 0.1 and 10 micrometers, and preferably of between 0.2 and 2 micrometers, wherein the tin-containing joints may include a tin-gold alloy, a tin-silver-gold alloy, a tin-silver-gold-copper alloy or a tin-lead-gold alloy due to the reaction between tin in thewetting layer 240 c and gold in thewetting layer 510. Next, the tool head is removed from theflexible circuit film 42. Next, thelead frame 700 bonded with theflexible circuit film 42 is removed from the stage. - In a second case, referring to
FIGS. 9B and 9C , when thewetting layer 510 is a tin-containing layer, thewetting layer 510 can be used to be joined with a gold layer of thewetting layer 240 c using a heat press process, which method is described as below. First, thelead frame 700 joined with theflexible circuit film 42 using theglue material 650 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, thewetting layer 240 c of theflexible circuit film 42 is thermally pressed on thewetting layer 510 on theleads 701 of thelead frame 700 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 c with thewetting layer 510. In the step of joining thewetting layer 240 c with thewetting layer 510, themetal joints 512 can be formed between theleads 701 of thelead frame 700 and the copper traces 210 at the outer portion of theflexible circuit film 42. The metal joints 512 can be tin-containing joints having a thickness t24 of between 0.1 and 10 micrometers, and preferably of between 0.2 and 2 micrometers, wherein the tin-containing joints may include a tin-gold alloy, a tin-silver-gold alloy, a tin-silver-gold-copper alloy or a tin-lead-gold alloy due to the reaction between gold in thewetting layer 240 c and tin in thewetting layer 510. Next, the tool head is removed from theflexible circuit film 42. Next, thelead frame 700 bonded with theflexible circuit film 42 is removed from the stage. - In a third case, referring to
FIGS. 9B and 9C , when thewetting layer 510 is a tin-containing layer, thewetting layer 510 can be used to be joined with thewetting layer 240 c of pure tin or an above-mentioned tin alloy using a heat press process, which method is described as below. First, thelead frame 700 joined with theflexible circuit film 42 using theglue material 650 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, thewetting layer 240 c of theflexible circuit film 42 is thermally pressed on thewetting layer 510 on theleads 701 of thelead frame 700 at a force of between 20 and 150N, and preferably of between 50 and 90N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 c with thewetting layer 510. Next, the tool head is removed from theflexible circuit film 42. Next, thelead frame 700 bonded with theflexible circuit film 42 is removed from the stage. Thereby, theleads 701 of thelead frame 700 can be connected to the copper traces 210 of theflexible circuit film 42 through tin-containing joints formed by joining the tin-containing layer of thewetting layer 240 b with the tin-containing layer of thewetting layer 510, wherein the tin-containing joints may include pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy. - In a fourth case, referring to
FIGS. 9B and 9C , when thewetting layer 510 is a gold layer, themetal joints 510 can be used to be joined with a gold layer of thewetting layer 240 c using a heat press process, which method is described as below. First, thelead frame 700 joined with theflexible circuit film 42 using theglue material 650 is placed on a stage kept at a temperature of between 150 and 350° C., and preferably of between 200 and 300° C. Next, thewetting layer 240 c of theflexible circuit film 42 is thermally pressed on thewetting layer 510 on theleads 701 of thelead frame 700 at a force of between 20 and 150N, and preferably of between 70 and 120N, for a time of between 0.1 and 10 seconds, and preferably of between 0.5 and 3 seconds, by a tool head kept at a temperature of between 250 and 500° C., and preferably of between 350 and 450° C., to join thewetting layer 240 c with thewetting layer 510. Next, the tool head is removed from theflexible circuit film 42. Next, thelead frame 700 bonded with theflexible circuit film 42 is removed from the stage. Thereby, theleads 701 of thelead frame 700 can be connected to the copper traces 210 of theflexible circuit film 42 through gold joints formed by joining the gold layer of thewetting layer 240 b with the gold layer of thewetting layer 510. - Referring to
FIG. 9D , after the step shown inFIG. 9C , apolymer compound 370 is formed using a molding process, enclosing thedie pad 702, an inner portion of theleads 701 close to thedie pad 702, thesemiconductor chip 2 and theflexible circuit film 42. For example, thepolymer compound 370 can be formed by molding an epoxy-based polymer with carbon fillers therein enclosing thedie pad 702, the inner portion of theleads 701, thesemiconductor chip 2 and theflexible circuit film 42 at a temperature of between 130 and 250° C. Alternatively, thepolymer compound 370 can be polyimide or polyester. Preferably, thepolymer compound 370 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 9E , after thepolymer compound 370 is formed, awetting layer 515, such as gold, pure tin, a tin-silver alloy, a tin-silver-copper alloy or a tin-lead alloy, can be electroplated or electroless plated on an outer portion of theleads 701 unenclosed by thepolymer compound 370. - Referring to
FIG. 9F , after thewetting layer 515 is formed, the steps of dejunking the residual of thepolymer compound 370, trimming dam bars and cutting and punching theleads 701 can be performed, such that theleads 701 have a predetermined shape and multiple chip packages are singularized. -
FIG. 9G is a perspective view showingFIG. 9F . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 42 by bonding thesemiconductor chip 2 with theflexible circuit film 42. Theflexible circuit film 42 is also joined with thelead frame 700, and theflexible circuit film 42 can be connected to thelead frame 700. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 42 and through theleads 701 of thelead frame 700. Alternatively, theglue material 650 shown inFIGS. 9A-9F can be omitted. - Referring to
FIG. 9H , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 9A-9G can be replaced by the above-mentionedflexible circuit film 44, bonded with thesemiconductor chip 2, shown inFIG. 6O , that is, theflexible circuit film 44 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by performing the above-mentioned steps as shown inFIGS. 9C-9F . The method, of joining theflexible circuit film 44 bonded with thesemiconductor chip 2 with thelead frame 700 using theglue material 650, as shown inFIG. 9H can be referred to as the method, of joining theflexible circuit film 42 bonded with thesemiconductor chip 2 with thelead frame 700 using theglue material 650, as illustrated inFIGS. 9A and 9B . - Referring to
FIGS. 9I and 9J , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 9A-9G can be replaced by the above-mentionedflexible circuit film 46, bonded with thesemiconductor chip 2, shown inFIG. 7B , that is, theflexible circuit film 46 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed bybonding wireboning wires 400, such as gold wires, having a diameter of between 12 and 40 micrometers with thewirebondable layer 230 and with theleads 701 via a wire-bonding process, followed by performing the above-mentioned steps as shown inFIGS. 9D-9F . Thereby, thewirebondable layer 230 of theflexible circuit film 46 can be electrically connected to theleads 701 of thelead frame 700 through thewireboning wires 400. - Referring to
FIG. 9K , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 9A-9G can be replaced by the above-mentionedflexible circuit film 48, bonded with thesemiconductor chip 2, shown inFIG. 7I , that is, theflexible circuit film 48 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by bonding thewireboning wires 400, such as gold wires, having a diameter of between 12 and 40 micrometers with thewirebondable layer 230 and with theleads 701 via a wire-bonding process, followed by performing the above-mentioned steps as shown inFIGS. 9D-9F . Thereby, thewirebondable layer 230 of theflexible circuit film 48 can be electrically connected to theleads 701 of thelead frame 700 through thewireboning wires 400. - Referring to
FIG. 9L , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 9A-9G can be replaced by the above-mentionedflexible circuit film 36, bonded with thesemiconductor chip 2, shown inFIG. 3D , that is, theflexible circuit film 36 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by joining the copper traces 210 with tin-containing solder preformed on theleads 701 to providemetal joints 513, such as tin-containing joints, between the copper traces 210 and theleads 701, followed by performing the above-mentioned steps as shown inFIGS. 9D-9F . - Referring to
FIG. 9M , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 9A-9G can be replaced by the above-mentionedflexible circuit film 38, bonded with thesemiconductor chip 2, shown inFIG. 3T , that is, theflexible circuit film 38 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by joining the copper traces 210 with a tin-containing solder preformed on theleads 701 to provide themetal joints 513, such as tin-containing joints, between the copper traces 210 and theleads 701, followed by performing the above-mentioned steps as shown inFIGS. 9D-9F . - Referring to
FIG. 10A , after the step shown inFIG. 9C , apolymer compound 380 is formed using a molding process, enclosing thedie pad 702, an inner portion of theleads 701 close to thedie pad 702, an outer portion of theleads 701, thesemiconductor chip 2 and theflexible circuit film 42, andopenings 380 a in thepolymer compound 380 expose the bottom surface of the outer portion of theleads 701. For example, thepolymer compound 380 can be formed by molding an epoxy-based polymer with carbon fillers therein enclosing thedie pad 702, the inner portion of theleads 701, the outer portion of theleads 701, thesemiconductor chip 2 and theflexible circuit film 42 at a temperature of between 130 and 250° C., and theopenings 380 a in thepolymer compound 380 expose the bottom surface of the outer portion of theleads 701. Alternatively, thepolymer compound 380 can be polyimide or polyester. Preferably, thepolymer compound 380 has a value of Young's modulus less than 0.5 GPa. - Referring to
FIG. 10B , after thepolymer compound 380 is formed, awetting layer 514 can be electroplated or electroless plated on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. Thewetting layer 514 has a thickness of between 0.1 and 3 micrometers, and may be gold, copper, silver, nickel, tin, aluminum, palladium or a composite of the above-mentioned materials. For example, thewetting layer 514 can be formed by electroless plating a nickel layer having a thickness of between 0.05 and 1 μm on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380, and electroless plating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the nickel layer in theopenings 380 a. Alternatively, thewetting layer 514 can be formed by electroplating a nickel layer having a thickness of between 0.05 and 1 μm on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380, and electroplating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the nickel layer in theopenings 380 a. Alternatively, thewetting layer 514 can be formed by electroless plating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. Alternatively, thewetting layer 514 can be formed by electroplating a gold layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. Alternatively, thewetting layer 514 can be formed by electroless plating a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. Alternatively, thewetting layer 514 can be formed by electroplating a tin-containing layer, such as pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. Alternatively, thewetting layer 514 can be formed by electroless plating an aluminum layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. Alternatively, thewetting layer 514 can be formed by electroplating an aluminum layer having a thickness of between 0.05 and 2 micrometers, and preferably of between 0.05 and 0.3 micrometers, on the bottom surface of the outer portion of theleads 701 exposed by theopenings 380 a in thepolymer compound 380. - Next, the steps of dejunking the residual of the
polymer compound 380, trimming dam bars and cutting and punching theleads 701 can be performed, such that multiple chip packages are singularized. After singularizing the chip packages, thewetting layer 514 can be joined with a solder, containing pure tin, a tin-silver alloy, a tin-lead alloy or a tin-silver-copper alloy, preformed on an external circuit or can contact with contact points of a socket. -
FIG. 10C is a perspective view showingFIG. 10B . The fine-pitchedmetal bumps 12 of thesemiconductor chip 2 can be fanned out through the copper traces 210 of theflexible circuit film 42 by bonding thesemiconductor chip 2 with theflexible circuit film 42. Theflexible circuit film 42 is also joined with thelead frame 700, and theflexible circuit film 42 can be connected to thelead frame 700. Thereby, thesemiconductor chip 2 has the fine-pitchedmetal bumps 12 connected to an external circuit, such as a printed circuit board (PCB) comprising a glass fiber as a core, through the copper traces 210 of theflexible circuit film 42 and through theleads 701 of thelead frame 700. - Referring to
FIG. 10D , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 10A-10B can be replaced by the above-mentionedflexible circuit film 44, bonded with thesemiconductor chip 2, shown inFIG. 6O , that is, theflexible circuit film 44 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by performing the above-mentioned steps as shown inFIG. 9C , followed by performing the above-mentioned steps as shown inFIG. 10A-10B . The methods, of joining theflexible circuit film 44 bonded with thesemiconductor chip 2 with thelead frame 700 using theglue material 650, as shown inFIG. 10D can be referred to as the methods, of joining theflexible circuit film 42 bonded with thesemiconductor chip 2 with thelead frame 700 using theglue material 650, as illustrated in the first, second, third and fourth cases shown inFIGS. 9A and 9B . - Referring to
FIG. 10E , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 10A-10B can be replaced by the above-mentionedflexible circuit film 46, bonded with thesemiconductor chip 2, shown inFIG. 7B , that is, theflexible circuit film 46 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by bonding thewireboning wires 400, such as gold wires, having a diameter of between 12 and 40 micrometers with thewirebondable layer 230 and with the inner portion of theleads 701 via a wire-bonding process, followed by performing the above-mentioned steps as shown inFIG. 10A-10B . Thereby, thewirebondable layer 230 of theflexible circuit film 46 can be electrically connected to theleads 701 of thelead frame 700 through thewireboning wires 400. - Referring to
FIG. 10F , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 10A-10B can be replaced by the above-mentionedflexible circuit film 48, bonded with thesemiconductor chip 2, shown inFIG. 7I , that is, theflexible circuit film 48 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by bonding thewireboning wires 400, such as gold wires, having a diameter of between 12 and 40 micrometers with thewirebondable layer 230 and with the inner portion of theleads 701 via a wire-bonding process, followed by performing the above-mentioned steps as shown inFIG. 10A-10B . Thereby, thewirebondable layer 230 of theflexible circuit film 48 can be electrically connected to theleads 701 of thelead frame 700 through thewireboning wires 400. - Referring to
FIG. 10G , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 10A-10B can be replaced by the above-mentionedflexible circuit film 36, bonded with thesemiconductor chip 2, shown inFIG. 3D , that is, theflexible circuit film 36 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by joining the copper traces 210 with a tin-containing solder preformed on theleads 701 to provide themetal joints 513, such as tin-containing joints, between the copper traces 210 and theleads 701, followed by performing the above-mentioned steps as shown inFIGS. 10A-10B . - Referring to
FIG. 10H , the above-mentionedflexible circuit film 42, bonded with thesemiconductor chip 2, shown inFIGS. 10A-10B can be replaced by the above-mentionedflexible circuit film 38, bonded with thesemiconductor chip 2, shown inFIG. 3T , that is, theflexible circuit film 38 bonded with thesemiconductor chip 2 is joined with thelead frame 700 using theglue material 650, followed by joining the copper traces 210 with a tin-containing solder preformed on theleads 701 to provide themetal joints 513, such as tin-containing joints, between the copper traces 210 and theleads 701, followed by performing the above-mentioned steps as shown inFIGS. 10A-10B . - Those described above are the embodiments to exemplify the present invention to enable the person skilled in the art to understand, make and use the present invention. However, it is not intended to limit the scope of the present invention. Any equivalent modification and variation according to the spirit of the present invention is to be also included within the scope of the claims stated below.
Claims (37)