US20100242375A1 - Double Sintered Thermally Stable Polycrystalline Diamond Cutting Elements - Google Patents
Double Sintered Thermally Stable Polycrystalline Diamond Cutting Elements Download PDFInfo
- Publication number
- US20100242375A1 US20100242375A1 US12/750,526 US75052610A US2010242375A1 US 20100242375 A1 US20100242375 A1 US 20100242375A1 US 75052610 A US75052610 A US 75052610A US 2010242375 A1 US2010242375 A1 US 2010242375A1
- Authority
- US
- United States
- Prior art keywords
- polycrystalline diamond
- pcd
- segments
- compact
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims the benefit of and priority from U.S. Provisional Patent Application No. 61/164,770 filed on Mar. 30, 2009, which is incorporated herein in its entirety for all purposes by this reference.
- Embodiments of the present invention relate generally to the field of earth boring tools and in particular relates to polycrystalline diamond cutting elements used on drill bits for earth boring.
- Specialized drill bits are used to drill well-bores, boreholes, or wells in the earth for a variety of purposes, including water wells; oil and gas wells; injection wells; geothermal wells; monitoring wells, mining; and, other similar operations. These drill bits come in two common types, roller cone drill bits and fixed cutter drill bits.
- Wells and other holes in the earth are drilled by attaching or connecting a drill bit to some means of turning the drill bit. In some instances, such as in some mining applications, the drill bit is attached directly to a shaft that is turned by a motor, engine, drive, or other means of providing torque to rotate the drill bit.
- In other applications, such as oil and gas drilling, the well may be several thousand feet or more in total depth. In these circumstances, the drill bit is connected to the surface of the earth by what is referred to as a drill string and a motor or drive that rotates the drill bit. The drill string typically comprises several elements that may include a special down-hole motor configured to provide additional or, if a surfaces motor or drive is not provided, the only means of turning the drill bit. Special logging and directional tools to measure various physical characteristics of the geological formation being drilled and to measure the location of the drill bit and drill string may be employed. Additional drill collars, heavy, thick-walled pipe, typically provide weight that is used to push the drill bit into the formation. Finally, drill pipe connects these elements, the drill bit, down-hole motor, logging tools, and drill collars, to the surface where a motor or drive mechanism turns the entire drill string and, consequently, the drill bit, to engage the drill bit with the geological formation to drill the well-bore deeper.
- As a well is drilled, fluid, typically a water or oil based fluid referred to as drilling mud is pumped down the drill string through the drill pipe and any other elements present and through the drill bit. Other types of drilling fluids are sometimes used, including air, nitrogen, foams, mists, and other combinations of gases, but for purposes of this application drilling fluid and/or drilling mud refers to any type of drilling fluid, including gases. In other words, drill bits typically have a fluid channel within the drill bit to allow the drilling mud to pass through the bit and out one or more jets, ports, or nozzles. The purpose of the drilling fluid is to cool and lubricate the drill bit, stabilize the well-bore from collapsing or allowing fluids present in the geological formation from entering the well-bore, and to carry fragments or cuttings removed by the drill bit up the annulus and out of the well-bore. While the drilling fluid typically is pumped through the inner annulus of the drill string and out of the drill bit, drilling fluid can be reverse-circulated. That is, the drilling fluid can be pumped down the annulus (the space between the exterior of the drill pipe and the wall of the well-bore) of the well-bore, across the face of the drill bit, and into the inner fluid channels of the drill bit through the jets or nozzles and up into the drill string.
- Roller cone drill bits were the most common type of bit used historically and featured two or more rotating cones with cutting elements, or teeth, on each cone. Roller cone drill bits typically have a relatively short period of use as the cutting elements and support bearings for the roller cones typically wear out and fail after only 50 hours of drilling use.
- Because of the relatively short life of roller cone bits, fixed cutter drill bits that employ very durable polycrystalline diamond (PCD) compact cutters, tungsten carbide cutters, natural or synthetic diamond, other hard materials, or combinations thereof, have been developed. These bits are referred to as fixed cutter bits because they employ cutting elements positioned on one or more fixed blades in selected locations or randomly distributed. Unlike roller cone bits that have cutting elements on a cone that rotates, in addition to the rotation imparted by a motor or drive, fixed cutter bits do not rotate independently of the rotation imparted by the motor or drive mechanism. Through varying improvements, the durability of fixed cutter bits has improved sufficiently to make them cost effective in terms of time saved during the drilling process when compared to the higher, up-front cost to manufacture the fixed cutter bits.
- Typically, a diamond cutter for use in a drill bit having a geometric size and shape normally characterized by unleached diamond cutting elements fabricated by assembling a plurality of polycrystalline diamond compact cutting elements in an array in a cutting slug that supports the cutting element. A challenge occurs, however, in bonding the PCD cutting elements to the cutting slug because the cutting slug—typically a cemented carbide substrate—has a different material than the PCD cutting elements and, therefore, has different material properties, such as a different rate of thermal expansion than the PCD cutting element. The differences in material properties can cause thermal stresses that lead the PCD cutting element to crack, delaminate, or otherwise become weakened and/or damaged at the interface between the cutting slug and the PCD cutting element.
- Thus, there exists a need for a PCD cutting element that is, at least in part, has improved thermal compatibility with the underlying cutting slug.
- Further, there is a need for a PCD cutting element that has improved bonding to a cutting slug as compared to the prior art.
- In addition, there is a need for a PCD manufacturing process that improves the yield of usable PCD cutting elements coupled to cutting slugs that reduces the probability that the PCD cutting elements break and/or crack during a double sintering process.
- Various features and embodiments of the invention disclosed herein provide robust and durable PCD cutting elements coupled to a cutting slug. In addition, methods of coupling a PCD cutting elements to a cutting slug are also disclosed.
- Embodiments of the invention include a first layer comprising at least one polycrystalline diamond segment positioned upon a second layer or transition layer. In those embodiments that include a plurality of PCD segments, a first PCD segment is positioned proximate a second PCD segment and separated therefrom by an interfacial boundary. The interfacial boundary optionally is non-planar relative to the first and/or the second PCD segment. Optionally, the interfacial boundary includes an abrasive material. Optionally, the interfacial boundary is contiguous with and formed of the same material as the second layer. In some embodiments, the first layer remains thermally stable at a higher temperature than the temperature below which the second table remains thermally stable. In some embodiments, the second layer is coupled to a substrate or cutting slug.
- Embodiments of the PCD segments include those that have been processed to provide a granular structure comprising interstices with a reduced number of metallic catalysts. Other embodiments of the PCD segments include those that have been processed to provide a granular structure that include interstices infiltrated with a material that remains thermally stable at a higher temperature than the temperature below which the metallic catalysts remain thermally stable. Other embodiments of the granular structure of the PCD segments comprise interstices that include one or more non-metallic catalysts. Yet other embodiments of the granular structure of the PCD segments comprise substantially fully dense diamond, i.e., a granular structure being substantially free of voids and/or interstices with or without other materials within any remaining interstices.
- Other embodiments of the invention include a body of abrasive material coupled to a substrate. The body includes a substantially pointed or conical shaped cutting surface. The body optionally includes one or more PCD segments coupled to and exposed in the conical cutting surface.
- A method of forming a PCD cutting elements coupled to a cutting slug includes providing a canister or other container configured to receive a plurality of thermally stable pre-sintered polycrystalline diamond segments. The canister is filled with grains of polycrystalline diamond and, optionally, a catalytic material. The polycrystalline diamond segments are positioned upon the grains of polycrystalline diamond such that an interfacial boundary is formed from the grains of polycrystalline diamond to separate each of the plurality of polycrystalline diamond segments. A press than applies a temperature and a pressure to the container to sinter the grains of polycrystalline diamond and bond the polycrystalline diamond segments to the sintered grains of polycrystalline diamond.
- As used herein, “at least one,” “one or more,” and “and/or” are open-ended expressions that are both conjunctive and disjunctive in operation. For example, each of the expressions “at least one of A, B and C,” “at least one of A, B, or C,” “one or more of A, B, and C,” “one or more of A, B, or C” and “A, B, and/or C” means A alone, B alone, C alone, A and B together, A and C together, B and C together, or A, B and C together.
- Various embodiments of the present inventions are set forth in the attached figures and in the Detailed Description as provided herein and as embodied by the claims. It should be understood, however, that this Summary does not contain all of the aspects and embodiments of the one or more present inventions, is not meant to be limiting or restrictive in any manner, and that the invention(s) as disclosed herein is/are and will be understood by those of ordinary skill in the art to encompass obvious improvements and modifications thereto.
- Additional advantages of the present invention will become readily apparent from the following discussion, particularly when taken together with the accompanying drawings.
- To further clarify the above and other advantages and features of the one or more present inventions, reference to specific embodiments thereof are illustrated in the appended drawings. The drawings depict only exemplary embodiments and are therefore not to be considered limiting. One or more embodiments will be described and explained with additional specificity and detail through the use of the accompanying drawings in which:
-
FIG. 1 is an isometric view of an embodiment of a PCD compact cutting element; -
FIG. 2 is a microscopic level view of an embodiment of a granular structure of a PCD segment; -
FIG. 3 is a microscopic level view of another embodiment of a granular structure of a PCD segment; -
FIG. 4 is an isometric view of an embodiment of a metallic carbide disc for use in embodiments of methods of making a PCD segment; -
FIG. 5 is an isometric view of another embodiment of a metallic carbide disc for use in embodiments of methods of making a PCD segment; -
FIG. 6A is a cross-sectional view of an embodiment of a canister for use in embodiments of methods of making a PCD segment; -
FIG. 6B is a cross-sectional view of an embodiment of a canister for use in embodiments of methods of making a PCD compact; -
FIG. 7 is an orthogonal view of an embodiment of a PCD cutting element; -
FIG. 8 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 9 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 10 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 11 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 12 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 13 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 14 is an orthogonal diagram of another embodiment of a PCD cutting element; -
FIG. 15 is a cross-sectional view of an embodiment of a PCD cutting element; -
FIG. 16 is a cross-sectional view of another embodiment of a PCD cutting element; -
FIG. 17 is a cross-sectional view of another embodiment of a PCD cutting element; -
FIG. 18 is a cross-sectional view of another embodiment of a PCD cutting element; -
FIG. 19 is a cross-sectional view of another embodiment of a PCD cutting element; -
FIG. 20 is a cross-sectional view of another embodiment of a PCD cutting element; -
FIG. 21 is an isometric view of an embodiment of a rotary drag bit that includes an embodiment of a PCD compact cutting element in a close-up view; -
FIG. 22 is an isometric view of an embodiment of a PCD compact cutting element that includes a transition layer with a conical surface; -
FIG. 23 is an isometric view of another embodiment of a rotary drag bit that includes an embodiment of a PCD compact cutting element that includes a conical surface in a close-up view; -
FIG. 24 is an orthogonal view of another embodiment of a PCD cutting element; -
FIG. 25 is an orthogonal view of another embodiment of a PCD cutting element; and, -
FIG. 26 is an orthogonal view of another embodiment of a PCD cutting element; - The drawings are not necessarily to scale.
-
FIG. 1 shows an isometric view of an embodiment of a polycrystalline diamond (PCD) compact 101. The PCD compact 101 includes a first table orlayer 105 formed of a plurality ofPCD segments 110 that, optionally, are sintered and/or preformed, as will be described in further detail below. ThePCD segments 110 optionally are leached diamond, natural diamond, synthetic diamond, highly pressurized diamond, calcium carbonate sintered diamond, combinations thereof, and similar materials and for purposes of the claims a PCD segment and/or polycrystalline diamond encompasses all these materials and those that fall within the scope of this disclosure. In addition, thePCD segments 110 optionally are thermally stable as will be described in further detail below. In the embodiment of the PCD compact 101 illustrated inFIG. 1 , thefirst layer 105 has a diameter of 130. Of course, one of skill in the art will appreciate that thefirst layer 105 can optionally have different dimensions and different shapes, including ovoid, half-circle, square, and other such shapes, and that all of these embodiments fall within the scope of the disclosure. - The plurality of
PCD segments 110 are separated by aninterfacial boundary 150 between each of the plurality ofPCD segments 110. Optionally, theinterfacial boundaries 150 comprises an abrasive material selected from a group that includes, but is not limited to, tungsten carbide, cubic boron nitride, thermally stable polycrystalline diamond, polycrystalline diamond, and the like. Theinterfacial boundaries 150 optionally are non-linear and/or non-planar relative toadjacent PCD segments 110. Optionally, the non-linear and/or non-planar quality of theinterfacial boundary 150 creates an interlocking feature—best seen as interlockingfeature 760 inFIG. 7 and interlocking feature 960 in FIG. 9—between thediamond segments 110, thereby reducing the likelihood thatadjacent PCD segments 110 will move relative to each other and, therefore, reducing the likelihood of aPCD segment 110 being torn and/or damaged and/or removed undesirably from the PCD compact 101 during use. - The PCD compact 101 also includes a second table or
layer 115, also referred to as atransition layer 115. ThePCD segments 110 are positioned upon and bonded to thesecond layer 115. Thesecond layer 115 optionally comprises an abrasive material selected from a group that includes, but is not limited to, tungsten carbide, cubic boron nitride, thermally stable polycrystalline diamond, polycrystalline diamond, and the like. The embodiment of the PCD compact 101 illustrates asecond layer 115 that includes sinteredPCD grains 120 that is optionally interspersed with a metallic catalyst. Optionally, thesecond layer 115 is contiguous with and comprises the same material as theinterfacial boundary 150. In the embodiment of the PCD compact 101 illustrated inFIG. 1 , thesecond layer 115 has a diameter of 135 that is the same, within manufacturing tolerances, as thediameter 130 of thefirst layer 105. Of course, one of skill in the art will appreciate that thesecond layer 115 can optionally have different dimensions and different shapes, including ovoid, half-circle, square, and other such shapes, including dimensions and shapes different from thefirst layer 105, and that all of these embodiments fall within the scope of the disclosure. - The second table 115 is bonded to a
substrate 125 made from, for example, a metallic material. For example, thesubstrate 125 can be made from a metallic material selected from the group that includes, but is not limited to, tungsten carbide, titanium carbide, tungsten molybdenum carbide, tantalum carbide, combinations thereof, and other similar materials. In the embodiment of the PCD compact 101 illustrated inFIG. 1 , thesubstrate 125 has a diameter of 140 that is the same, within manufacturing tolerances, as thediameter 130 of thefirst layer 105 and thediameter 135 of thesecond layer 115. Of course, one of skill in the art will appreciate that thesubstrate 125 can optionally have different dimensions and different shapes, including ovoid, half-circle, square, and other such shapes, including dimensions and shapes different from thefirst layer 105 and/or thesecond layer 115, and that all of these embodiments fall within the scope of the disclosure. - As noted, the
PCD segments 110 typically are formed by sintering powdered diamond, and, optionally, various catalysts, typically metallic powders mixed with the diamond powder. The catalysts, typically metallic materials, such as cobalt and other similar metallic materials, act as a catalyst to reduce the temperature and/or the pressure at which the sintering process occurs and/or speeds the reaction by which the diamond grains and any other materials crystallize and form a granular structure. The diamond powder and any catalysts and/or other materials are placed in a canister or form that is compressed under a pressure and a temperature sufficient to sinter and crystallize the diamond powder and any other materials into a solid PCD segment. - Referring to
FIG. 3 , a sintered PCDgranular structure 300 comprises polycrystalline diamond grains orcrystals 301 and a catalyzingmaterial 310 dispersed between the polycrystalline diamond grains orcrystals 301. Optionally, the catalyzingmaterial 310 is selected from a group of metallic materials, including, but not limited to, cobalt, nickel, iron, ruthenium, rhodium, palladium, platinum, chromium, manganese, tantalum, osmium, iridium, and combinations thereof. - Cobalt and other catalysts, however, typically result in a PCD granular structure that typically suffers from thermal degradation at temperatures (typically around from about 650 degrees Celsius to about 700 degrees Celsius) that the PCD granular structure can be exposed to during normal use. That is, the PCD granular structure exhibits increased tendencies to fail, crack, chip, delaminate, or otherwise wear more quickly during use at normal operating temperatures, leading to premature wear and reduced life.
- To address the side-effect the
catalysts 310 have on the thermal stability of the PCDgranular structure 300, the PCD segments (such assegments 110 inFIG. 1 ) are processed after they have been sintered to reduce the amount ofcatalyst 310 present in the PCDgranular structure 300 or remove thecatalyst 310, either from the entire PCD segment or at least to a depth at which the PCD segment is heated through the transfer of heat generated during use less than the temperature at which the PCD granular structure begins to exhibit decreased thermal stability. Typically, the catalysts are removed via leaching and/or acid etching with acids that react with the catalysts and/or other known methods, leaving a PCD segment that is said to be thermally stable, typically referred to as thermally stable polycrystalline (TSP). - Illustrated in
FIG. 2 is an idealized microscopic level view of a sintered PCDgranular structure 200 that has been processed to remove the catalyst (e.g.,catalyst 220 inFIG. 3 ), thereby leavingvoids 220 andPCD grains 201, as discussed above. That is, the thermallystable PCD segments 110 ofFIG. 1 optionally have been processed in such a way to improve the thermal stability of thePCD segments 110 relative to PCD segments that have not undergone such processing. Improved thermal stability means that the diamond segments remain stable, e.g., do not exhibit increased tendencies to fail, crack, chip, delaminate, or otherwise wear more quickly during use at higher temperatures than these failure modes would otherwise manifest themselves. - The
PCD grains 201 typically are submicron in size, providing dimensional context for theFIGS. 2 and 3 , typically from about 1 micron to about 50 microns and, more preferably, from about 5 microns to about 35 microns and, more preferably still, from about 7 microns to about 25 microns. In some embodiments, the PCD granular structure is processed to providePCD grains 201 large enough such that thePCD grains 201 do not easily oxidize and burn up when subjected to the heat caused by friction during use. - Optionally, the PCD
granular structure 200 is then subjected to additional processing, such as another sintering process (i.e., double sintering) to cause thePCD grains 201 to grow and expand into the interstices or voids 220, leaving PCD granular structure that is substantially diamond dense. That is, the PCDgranular structure 200 comprises at least 90% PCD grains 201. - In other embodiments, the PCD
granular structure 200 is sintered while in contact with non-catalytic materials, i.e., those materials that typically do not catalyze or cause the PCD granular structure to change crystal structure (e.g., from diamond to graphite) and/or lower the temperature at which the PCDgranular structure 200 andPCD grains 201 begin to become thermally unstable. For example, anon-metallic catalyst 210 that is thermally stable, e.g., one having a coefficient of thermal expansion similar to that of thePCD grains 201 can be placed in contact with the PCDgranular structure 201 during the sintering process, thereby causing thenon-metallic catalyst 210 to infiltrate and/or grow within one or more of the interstices or voids 220. Thenon-metallic catalyst 210 can be selected from a group that includes, but is not limited to, silicon, silicon carbide, boron, carbonates, hydroxide, hydride, hydrate, phosphorus-oxide, phosphoric acid, carbonate, lanthanide, actinide, phosphate hydrate, hydrogen phosphate, phosphorus carbonate, combinations thereof, and other similar materials. - In yet other embodiments, the PCD
granular structure 200 is sintered with one or more thermallystable materials 215, including, but not limited to, cobalt silicide, titanium, niobium, molybdenum, tungsten, tantalum, combinations thereof, and other similar materials. A benefit of these thermallystable materials 215 is that they tend to act to make the PCDgranular structure 200 less brittle under impact loads. - Prior art PCD compacts typically had a PCD segment bonded directly to a substrate. This arrangement caused difficulties during manufacturing and use because, among other problems, the coefficient of thermal expansion differed, sometimes greatly, between the substrate and the PCD segment. During manufacturing, in which the PCD segment was to be bonded to the substrate, the different rates of thermal expansion often resulted in PCD segments that cracked due to the thermal stresses created at the interface of the substrate and the PCD segment as the substrate and PCD segment expanded and contracted at different rates while heating and cooling. Similar results occurred during use in which the PCD segment would be subjected to direct heating caused by friction, whereas the substrate is heated primarily through heat transferred by conduction through the PCD segment and to the substrate.
- A benefit of the second layer or
transition layer 115 is that it solves the previously unresolved problem of bonding a PCD segment to a substrate that has a different coefficient of thermal expansion. That is, embodiments of PCD compacts of the invention have improved thermal stability, improved bonding of the PCD segments to a substrate, improved reliability, and other benefits as described herein and one having skill in the art will understand by reading the disclosure. - Embodiments of methods of making first the
PCD segments 110 are first discussed. As noted above,PCD segments 110 are formed by sintering diamond powder or other similar material and, optionally, a catalyst. Illustrated inFIGS. 4 and 5 arediscs discs discs PCD segments 110. Thediscs more areas 415 in which thePCD segments 110 are formed, theareas 415 being separated by one ormore ribs 420 on afront surface 409 of thediscs ribs 420 may be straight, non-liner, curvilinear, non-planar, combinations thereof, and the like. (It should be noted that shape and location of theribs 420 is a mirror of the shape and location of theinterfacial boundary 150 of the PCD compact 101 discussed above. Thus, theribs 420 can optionally be of any shape and any dimension contemplated for the interfacial boundaries.) In addition, theribs 420 separate thePCD segments 110 from coming into contact with each other during the manufacturing process. - Embodiments of the method making PCD include providing a canister or can 601 as seen in
FIG. 6A . At least one disc or afirst disc 405 is placed within thecanister 601 and eacharea 415 of thedisc 405 is filled with, for example, diamond powder 650 (and any catalysts and other materials, which are considered present in the discussion of the diamond powder 650), as discussed above, that will be sintered to form thePCD segment 110, as discussed above. In those instances in which a plurality ofdiscs 405 are placed into thecanister 601 so as to form a plurality ofPCD segments 110, optionally anotherdisc 630 separates eachdisc 405 from thediamond powder 650 proximate to aback surface 407 of eachdisc 405. Thedisc 630 optionally is made of niobium and/or similar such materials, which prevents, at least to some degree, the flow ofdiamond powder 650 and the growth of crystallized diamond grains into theback surface 407 of thedisc 405 during sintering. The number ofdiscs 405 positioned in thecanister 601 and, consequently, the number ofPCD segments 110 produced, is a function, in part, of thethickness 655 of the layer ofdiamond powder 650 and thethickness 408 of thediscs 405. Of course, thethickness 655 of thediamond powder 650 and thethickness 408 of thedisc 405 optionally can be varied in thesame canister 601, thus producing PCD segments of different dimensions in one manufacturing batch. Further, as one having skill in the art will appreciate, the quantity ofPCD segments 110 produced is a function, in part, on the configuration and number ofribs 420 on eachdisc 405. Further,different discs 405 with different configurations ofribs 420 can be used in a givencanister 601, thus further affecting the yield ofPCD segments 110. - Prior to placing the
lid 660 on thecanister 601 and sealing thecanister 601, thediamond powder 650 may be tamped down or compacted with an applied pressure low enough to avoid breakage of any of thediscs canister 650 is heated to reduce or eliminate some or all of any impurities present in thediamond powder 650 and elsewhere in thecanister 601 before sealing thecanister 601. Typically, thelid 660 is sealed to thecanister 601 through welding, such as laser welding and other known methods. In some embodiments of the present invention, the canister is sealed using a process described in U.S. Pat. No. 7,575,425 to Hall et al., which is herein incorporated by reference for all that it contains. - After the
canister 601 is sealed, it is placed within a salt form (not shown). One or more salt forms are then stacked and placed on an anvil of a high-temperature, high-pressure press (not shown). The press applies a pressure and a temperature sufficiently high to cause the diamond powder 650 (and any catalysts and other materials) to sinter. During the sintering process, thediamond powder 650 typically reduces in volume as it becomes solid. - Once the sintering process is complete and the
canister 601 is removed from both the press and the salt form, thediamond powder 650 will have become thesintered PCD segments 110. An advantage of theribs 420 of thediscs 405 is that theseparate PCD segments 110 are easily separable from thediscs 420, thus eliminating a step of cutting thePCD segments 110 out a solid cylinder of polycrystalline diamond with an electron discharge machining (EDM), a process that typically is time consuming and expensive. The separatedPCD segments 110 are now ready for any post-sintering treatment such as leaching and/or acid baths, and other such treatments to improve the thermal stability of thePCD segments 110 as discussed above. - Embodiments of the method further include forming PCD compacts, such as those illustrated in
FIG. 1 , to combinePCD segments 110 with an unsintered abrasive powder or material that will form the second ortransition layer 115 and asubstrate 125. One ormore PCD segments 2610 are placed in a canister 2601, similar to thecanister 601, as illustrated inFIG. 6B . Unsintered abrasive material 2620, such as diamond powder, by way of example, is placed in the canister in between—at theinterfacial boundary 2650—and on top of thePCD segments 2610 that typically have been processed to improve the thermal stability of thePCD segments 2610, as discussed above. As noted above, the unsintered abrasive material optionally includes metallic catalysts and/or non-metallic catalysts and/or other thermally stable materials as discussed above. - The
substrate 2625 is placed on top of the unsintered abrasive material 2620. Prior to placing thelid 2660 on the canister 2601 and sealing the canister 2601, the unsintered abrasive material 2620 may be tamped down or compacted with an applied pressure low enough to avoid breakage of any of thePCD segments 2610. Optionally, the canister 2601 is heated to reduce or eliminate some or all of any impurities present in the unsintered abrasive material 2620 and elsewhere in the canister 2601 before sealing the canister 2601. Typically, thelid 2660 is sealed to the canister 2601 through welding, such as laser welding and other known methods. In some embodiments of the present invention, the canister is sealed using a process described in U.S. Pat. No. 7,575,425 to Hall et al. After the canister 2601 is sealed, it is placed within a salt form (not shown). One or more salt forms are then stacked and placed on an anvil of a high-temperature, high-pressure press (not shown). The press applies a pressure and a temperature sufficiently high to cause the unsintered abrasive material 2620 (and any catalysts and other materials) to sinter. During the sintering process, the abrasive material 2620 typically reduces in volume as it becomes solid. In addition, thePCD segments 2610 undergo a second, or double, sintering process, by which the PCD grains grow and/or other non-metallic catalysts and/or other thermally stable materials are incorporated and sintered into the PCD segments as discussed above. - During the sintering process, the abrasive material 2620 forms both a mechanical and a chemical bond or attachment with the
PCD segments 2610 at theinterfacial boundary 2650 and at alower surface 2611. For example, thePCD segments 2610 would exhibit, in part, growth of PCD grains 201 (FIG. 2 ) into the interstices and voids 220 (FIG. 2 ) across and into atransition zone 2621 of the now sintered abrasive material 2620. In so doing, a solid, rigid diamond layer at thetransition zone 2621 forms a mechanical bond between the sintered layer of abrasive material 2620 and thePCD segments 2610, reducing any residual stress concentrations that may otherwise occur. Further, the abrasive material 2620 may reduce in volume as it sinters, provided further space into which PCD grains may grow during the sintering process, further improving the mechanical bond. It should be noted that while the grain size of the PCD grains and the sintered abrasive material can vary substantially, a grain size that is similar between the PCD grains and the sintered abrasive material can improve and provide a more uniform bond between the two materials as compared to the bond that occurs when the grain sizes are dissimilar. - Another benefit is that whereas the
PCD segments 2610—typically processed to be thermally stable—and thesubstrate 2625 typically have coefficients of thermal expansion that are quite different, as discussed above, the layer of sintered abrasive material 2620 acts as a transition layer, and is typically selected and prepared to have a coefficient of thermal expansion somewhere between that of thePCD segments 2610 and thesubstrate 2625. In so doing, the gradient of thermal stresses is changed gradually throughout the PCD compact rather than having a sharp transition at each interface. That is, a first layer ofPCD segments 2610 is configured to remain thermally stable at a first temperature and a second layer or transition layer 2620 is configured to remain thermally stable at a second temperature lower than the first temperature. - Disclosed in
FIGS. 7-14 are various, non-limiting embodiments of PCD compacts comprising PCD segments of various shapes and the interfacial boundaries between each PCD segment. - For example, the PCD compact 710 includes two
PCD segments 710 and a singleinterfacial boundary 750 that is non-linear and non-planar and includes interlocking features 760, such as the illustrated dimples. - As illustrated in
FIGS. 7-14 , thePCD segments PCD segments PCD compacts - As noted, the
interfacial boundaries interfacial boundaries 950 includes a series of steps 960. The interlocking features 750, 850, 950, 1050, 1150, 1250, 1350, and 1450 optionally include also comprise complementary projections and recesses. For example, PCD compact 1201 inFIG. 12 includes aPCD segment 1210 that has ainterfacial boundary 1250 that is a plurality of oval openings. - Disclosed in
FIGS. 15-20 are cross-sections of various, non-limiting embodiments ofPCD compacts PCD compacts PCD segments interfacial boundary lower surface PCD segments upper surfaces substrates lower surfaces upper surfaces -
FIG. 21 shows an embodiment of adrag bit 2800 that includes a plurality of PCD compacts orshear cutters 2801 as described above. Theshear cutters 2801 are attached toblades 2880 that each extend from ahead 2890 of thedrag bit 2800 for cutting against the subterranean formation being drilled. -
FIG. 22 discloses an embodiment of a PCD compact or pointed cuttingelement 3101 that includesPCD segments 3110 arranged about the PCD compact or cuttingelement 3101. ThePCD segments 3110 can be arranged symmetrically or asymmetrically about the PCD compact 3101 as required for a particular application. A sinteredabrasive material 3120 having aconical surface 3123 supports thePCD segments 3110 that, in turn, is supported by asubstrate 3125. -
FIG. 23 shows an embodiment of anotherdrag bit 3100 that includes a plurality of pointed PCD compacts or cuttingelements 3101. ThePCD compacts 3101 may be pressed or machined into the desired shape or configuration. In other embodiments, the PCD compact 3101 may be used in road milling, pavement resurfacing, mining, and trenching applications. - Disclosed in
FIGS. 24-26 are various, non-limiting embodiments of arrangements of thePCD segments PCD compacts PCD segments 3110 and theconical PCD compacts 3101 inFIGS. 22 and 23 . ThePCD segments conical surface 3123 inFIG. 22 , as noted. Theinterfacial boundaries - Whereas the present invention has been described in particular relation to the drawings attached hereto, it should be understood that other and further modifications apart from those shown or suggested herein, may be made within the scope and spirit of the present invention.
- The present invention, in various embodiments, includes providing devices and processes in the absence of items not depicted and/or described herein or in various embodiments hereof, including in the absence of such items as may have been used in previous devices or processes, e.g., for improving performance, achieving ease and/or reducing cost of implementation.
- The foregoing discussion of the invention has been presented for purposes of illustration and description. The foregoing is not intended to limit the invention to the form or forms disclosed herein. In the foregoing Detailed Description for example, various features of the invention are grouped together in one or more embodiments for the purpose of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed invention requires more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate preferred embodiment of the invention.
- Moreover, though the description of the invention has included description of one or more embodiments and certain variations and modifications, other variations and modifications are within the scope of the invention, e.g., as may be within the skill and knowledge of those in the art, after understanding the present disclosure. It is intended to obtain rights which include alternative embodiments to the extent permitted, including alternate, interchangeable and/or equivalent structures, functions, ranges or steps to those claimed, whether or not such alternate, interchangeable and/or equivalent structures, functions, ranges or steps are disclosed herein, and without intending to publicly dedicate any patentable subject matter.
Claims (19)