US20100203350A1 - Methods and Apparatuses for Manufacturing Cast Silicon from Seed Crystals - Google Patents
Methods and Apparatuses for Manufacturing Cast Silicon from Seed Crystals Download PDFInfo
- Publication number
- US20100203350A1 US20100203350A1 US12/669,521 US66952108A US2010203350A1 US 20100203350 A1 US20100203350 A1 US 20100203350A1 US 66952108 A US66952108 A US 66952108A US 2010203350 A1 US2010203350 A1 US 2010203350A1
- Authority
- US
- United States
- Prior art keywords
- silicon
- crucible
- solid body
- temperature
- cast
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application claims the benefit of U.S. Provisional Application No. 60/951,155, filed Jul. 20, 2007. The entire disclosure of U.S. Provisional Application No. 60/951,155 is hereby incorporated by reference into this specification.
- 1. Technical Field
- The present invention generally relates to the field of photovoltaics and to methods and apparatuses for manufacturing cast silicon for photovoltaic applications. The invention further relates to new forms of cast silicon that can be used to manufacture devices, such as photovoltaic cells and other semiconductor devices. The new silicon can have a monocrystalline, near-monocrystalline, bi-crystal, or geometric multicrystalline structure and can be manufactured by a casting process utilizing seed crystals.
- 2. Background Information
- Photovoltaic cells convert light into electric current. One of the most important features of a photovoltaic cell is its efficiency in converting light energy into electrical energy. Although photovoltaic cells can be fabricated from a variety of semiconductor materials, silicon is generally used because it is readily available at reasonable cost, and because it has a suitable balance of electrical, physical, and chemical properties for use in fabricating photovoltaic cells.
- In a known procedure for the manufacture of photovoltaic cells, silicon feedstock is doped with a dopant having either a positive or negative conductivity type, melted, and then crystallized by either pulling crystallized silicon out of a melt zone into ingots of monocrystalline silicon (via the Czochralski (CZ) or float zone (FZ) methods), or cast into blocks or “bricks” of multi-crystalline silicon or polycrystalline silicon, depending on the grain size of the individual silicon grains. As used herein, the term “monocrystalline silicon” refers to a body of single crystal silicon, having one consistent crystal orientation throughout. Further, conventional multi-crystalline silicon refers to crystalline silicon having centimeter scale grain size distribution, with multiple randomly oriented crystals located within a body of multi-crystalline silicon. As used herein, however, the term “geometrically ordered multicrystalline silicon” (hereinafter abbreviated as “geometric multicrystalline silicon”) refers to crystalline silicon, according to embodiments of the present invention, having a geometrically ordered centimeter scale grain size distribution, with multiple ordered crystals located within a body of multi-crystalline silicon. For example, in geometric multi-crystalline silicon, the grains are typically an average of about 0.5 cm to about 5 cm in size, and grain orientation within a body of geometric multi-crystalline silicon is controlled according to predetermined orientations. Further, as used herein, the term “polycrystalline silicon” refers to crystalline silicon with micrometer scale grain size and multiple grain orientations located within a given body of crystalline silicon. For example, the grains are typically an average of about submicron to about micron in size (e.g., individual grains are not visible to the naked eye), and grain orientation distributed randomly throughout. In the procedure described above, the ingots or blocks are cut into thin substrates, also referred to as wafers, by known slicing or sawing methods. These wafers may then be processed into photovoltaic cells.
- Monocrystalline silicon for use in the manufacture of photovoltaic cells is generally produced by the CZ or FZ methods, both being processes in which a cylindrically shaped boule of crystalline silicon is produced. For a CZ process, a seed crystal is touched to a pool of molten silicon and the boule is slowly pulled out of the pool while heat is extracted through the solid part of the boule. As used herein, the term “seed crystal” refers to a piece of crystalline material that is brought in contact with liquid silicon such that, during solidification, the liquid silicon adapts to the crystallinity of the seed. For a FZ process, solid material is fed through a melting zone, melted upon entry into one side of the melting zone, and re-solidified on the other side of the melting zone, generally by contacting a seed crystal.
- Recently, a new technique for producing monocrystalline or geometric multicrystalline material in a casting station has been invented, as disclosed in U.S. patent application Ser. Nos. 11/624,365 and 11/624,411 and published as U.S. Patent Application Publication Nos.: 20070169684A1 and 20070169685A1, filed Jan. 18, 2007. Casting processes for preparing multicrystalline silicon ingots are known in the art of photovoltaic technology. Briefly, in such processes, molten silicon is contained in a crucible, such as a quartz crucible, and is cooled in a controlled manner to permit the crystallization of the silicon contained therein. The block of cast crystalline silicon that results is generally cut into bricks having a cross-section that is the same as or close to the size of the wafer to be used for manufacturing a photovoltaic cell, and the bricks are sawn or otherwise cut into such wafers. Multi-crystalline silicon produced in such manner is an agglomeration of crystal grains where, within the wafers made therefrom, the orientation of the grains relative to one another is effectively random. Monocrystalline or geometric multicrystalline silicon has specifically chosen grain orientations and (in the latter case) grain boundaries, and can be formed by the new casting techniques disclosed in the above-mentioned patent applications by bringing liquid silicon in contact with a large seed layer that remains partially solid during the process and through which heat is extracted during solidification. As used herein, the term ‘seed layer’ refers to a crystal or group of crystals with desired crystal orientations that form a continuous layer. They can be made to conform with one side of a crucible for casting purposes.
- In order to produce the best quality cast ingots, several conditions should be met. Firstly, as much of the ingot as possible have the desired crystallinity. If the ingot is intended to be monocrystalline, then the entire usable portion of the ingot should be monocrystalline, and likewise for geometric multicrystalline material. Secondly, the silicon should contain as few imperfections as possible. Imperfections can include individual impurities, agglomerates of impurities, intrinsic lattice defects and structural defects in the silicon lattice, such as dislocations and stacking faults. Many of these imperfections can cause a fast recombination of electrical charge carriers in a functioning photovoltaic cell made from crystalline silicon. This can cause a decrease in the efficiency of the cell.
- Many years of development have resulted in a minimal amount of imperfections in well-grown CZ and FZ silicon. Dislocation free single crystals can be achieved by first growing a thin neck where all dislocations incorporated at the seed are allowed to grow out. The incorporation of inclusions and secondary phases (for example silicon nitride, silicon oxide or silicon carbide particles) is avoided by maintaining a counter-rotation of the seed crystal relative to the melt. Oxygen incorporation can be minimized using FZ or Magnetic CZ techniques as is known in the industry. Metallic impurities are generally minimized by being left in the potscrap or the tang end after the boule is brought to an end.
- According to some embodiments, this invention relates to a method and apparatus for improved casting of materials for solar cells, such as silicon. Desirably, the invention utilizes a shaped crucible with walls tapered inward and/or outward as viewed from the top looking at the bottom of the crucible
- During silicon casting, unwanted formation of multicrystalline material reduces the yield of monocrystalline material, particularly when forming bricks or blocks. A straight walled crucible results in an angled boundary of the usable silicon and the undesirable silicon, such that a vertical cut results in either usable silicon discarded with the undesirable silicon or inclusion of undesirable silicon in with the usable silicon. The multicrystalline material limits the yield of the monocrystalline material as it continues up a side of the crucible and extends in towards the bulk of the silicon.
- Desirably using the shaped crucibles of this invention, the multicrystalline material can be reduced and/or suppressed by monocrystalline material resulting in a boundary and/or interface of the monocrystalline silicon and the multicrystalline silicon at the crucible wall and/or outside the majority of the crucible volume, for example. Desirably, the seeded material grows vertically and/or in a convex mushroom shape from the seed out to the crucible wall. The shaped crucibles of this invention can produce a generally vertical boundary between the usable silicon and the undesirable silicon to increase yields of the usable silicon when forming blocks, bricks, wafers, and the like.
- As used herein, the term “near-monocrystalline silicon” refers to a body of crystalline silicon, having one consistent crystal orientation throughout for greater than 50% by volume of the body, where, for example, such near-monocrystalline silicon may comprise a body of single crystal silicon next to a multicrystalline region, or it may comprise a large, contiguously consistent crystal of silicon that partially or wholly contains smaller crystals of silicon of other crystal orientations, where the smaller crystals do not make up more than 50% of the overall volume. Preferably, the near-monocrystalline silicon may contain smaller crystals which do not make up more than 25% of the overall volume. More preferably, the near-monocrystalline silicon may contain smaller crystals which do not make up more than 10% of the overall volume. Still more preferably, the near-monocrystalline silicon may contain smaller crystals which do not make up more than 5% of the overall volume.
- As used herein, the term “bi-crystal silicon” refers to a body of silicon, having one consistent crystal orientation throughout for greater than or equal to 50% by volume of the body, and another consistent crystal orientation for the remainder of the volume of the body. For example, such bi-crystal silicon may comprise a body of single crystal silicon having a one crystal orientation next to another body of single crystal silicon having a different crystal orientation making up the balance of the volume of crystalline silicon. Preferably, the bi-crystal silicon may contain two discrete regions within the same body of silicon, the regions differing only in their crystal orientation.
- In accordance with the invention as embodied and broadly described, there is provided a method of manufacturing cast silicon, comprising: placing a crucible filled with silicon on a layer, the layer comprising: a thermally conducting material in contact with a heat sink, and a thermally insulating area, where a thermally conductive part of the layer is in contact with about 5% to about 99% of a bottom surface of the crucible; and solidifying the silicon by extracting heat through the thermally conducting layer. The heat extraction may occur after part or all of the silicon is melted, in order to direct seeded growth by bringing the cast silicon to a first temperature and then cooling it to a second temperature.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising placing silicon in a crucible having walls tapered inwards towards a center of the crucible, melting the silicon, and solidifying the silicon by extraction of heat through a bottom of the crucible. The method may optionally include, bringing the cast silicon to a first temperature, cooling the silicon down to a second temperature different from the first temperature, extracting the cast silicon from the crucible and then cutting sections from the cast silicon.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising placing silicon in a crucible having walls tapered outwards away from a center of the crucible, and melting the silicon, solidifying the silicon by extraction of heat through a bottom of the crucible. The method may optionally include bringing the cast silicon to a first temperature, cooling the silicon down to a second temperature different from the first temperature, extracting the cast silicon from the crucible and then cutting sections from the cast silicon.
- In accordance with the present invention, there is also provided a crucible for the casting of silicon having a bottom surface and a plurality of side walls, wherein at least one of the plurality of side walls tapers inwards toward a center of the crucible at an angle from about 1° to about 25° with respect to a plane perpendicular to a bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface. The tapered side wall or walls may reduce the vessel cross-sectional area taken in the direction away from the bottom surface.
- In accordance with the present invention, there is also provided a crucible for the casting of silicon having a bottom surface and a plurality of side walls, wherein at least one of the plurality of side walls tapers outwards from a center of the crucible at an angle greater than about 2°, with respect to a plane perpendicular to a bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface. The tapered side wall or walls may increase the vessel cross-sectional area taken in the direction away from the bottom surface.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising: coating inner side walls of a crucible with a release coating, leaving a bottom wall uncoated; placing silicon seed crystals in contact with the uncoated wall, placing silicon feedstock in the crucible, melting the feedstock while maintaining the seed crystals in at least a partially solid state, solidifying the silicon by extracting heat through the seed crystals, bringing silicon to a first temperature and cooling the silicon to a second temperature.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising: slicing a previously cast ingot into slabs, chemically treating the slabs to remove impurities, placing the slab in a crucible for use as a seed layer and then filling the crucible with feedstock for casting.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising: placing a layer of monocrystalline silicon seed crystals on at least one surface in a crucible such that seed crystals in a center region of the layer have one crystal pole direction perpendicular to the surface and cover about 50% to about 99% of the layer area, while the remaining seed crystals on the edges of the layer have at least one different crystal pole direction perpendicular to the surface and cover the remaining layer area; adding feedstock silicon and bringing the feedstock and a portion of the seed layer to a molten state; solidifying the silicon by extracting heat through the seed layer; bringing the silicon to a predetermined, for example, uniform first temperature and then preferably uniformly cooling the silicon down to a uniform second temperature.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising: placing at least one monocrystalline seed crystal having at least about 10 cm by about 10 cm area on a bottom surface of a crucible that rests on a partially insulating base plate; introducing solid or liquid silicon feedstock and partially melting the seed crystal, extracting heat through the seed crystal in such a way that a convex solid boundary increases the cross-sectional area of monocrystalline growth; bringing the silicon to a first temperature and cooling it, preferably uniformly, down to a second temperature; cutting a slab from a side of the cast silicon opposite the seed crystal; cleaning the slab using a chemical process; and using the large slab as a new seed layer for a subsequent casting process.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising: loading a seed layer of crystalline silicon together with solid silicon feedstock into a crucible having a lid or cover; melting and solidifying the silicon while maintaining part of the seed layer as solid and while flowing at least one of argon and nitrogen gas through at least one hole in the lid or cover while at least another hole exits the gas; and cooling the silicon preferably uniformly.
- In accordance with the present invention, there is also provided a method of manufacturing cast silicon, comprising: loading a seed layer of crystalline silicon into a crucible, covering the crucible having a lid; introducing liquid silicon into the crucible, the liquid silicon preferably being superheated; allowing part of the seed layer to melt; solidifying the silicon while flowing at least one of argon and nitrogen gas through at least one hole in the lid while at least one other hole exits the gas; and cooling the silicon.
- In accordance with the present invention, there is also provided a process for manufacturing cast silicon comprising loading a seed layer of crystalline silicon together with solid feedstock; melting the feedstock and part of the seed layer while maintaining a solid/liquid interface that is essentially flat over a center portion of the seed layer, and convex at the edges of the seed layer; solidifying the silicon by extracting heat through the seed layer while at least initially maintaining the same solid/liquid interface shape; bringing the silicon to a first temperature and cooling the silicon to a second temperature, the heating and cooling preferably being uniform.
- In accordance with the present invention, there is also provided a process for manufacturing cast silicon comprising loading a seed layer of crystalline silicon together with solid feedstock; melting the feedstock and part of the seed layer while maintaining a solid/liquid interface that is substantially flat over the entire seed layer; solidifying the silicon by extracting heat through the seed layer while at least initially providing extra heat in a region comprising the edges of the seed layer; bringing the silicon to a first temperature and preferably uniformly cooling the silicon to a second temperature, the heating and cooling preferably being uniform.
- In accordance with the present invention, there is also provided an apparatus for the casting of silicon comprising heaters surrounding a crucible resting on a heat sink, the heaters being provided for the melting of silicon ; a means for controlled extraction of heat through the heat sink; a port for introduction of a gas; and at least one loop of insulated, water cooled tube residing with the primary heaters and encircling the crucible, wherein the loop can be energized to provide inductive heating at different regions within the crucible.
- The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the features, advantages, and principles of the invention. In the drawings:
-
FIGS. 1A-1B illustrate an exemplary system where a thermally insulating layer is combined with a thermally conducting layer below a crucible in a casting station, according to an embodiment of the present invention; -
FIGS. 2A-2D illustrate two examples of tapered crucibles together with illustrations of the desired effects on the silicon cast therein, according to embodiments of the present invention; -
FIG. 3 illustrates an example of silicon feedstock loaded into a partially coated crucible, according to an embodiment of the present invention; -
FIG. 4 illustrates an example of a method for recycling seed layer material, according to an embodiment of the present invention; -
FIG. 5 illustrates an exemplary arrangement of single crystal silicon to form a seed layer, according to an embodiment of the present invention; -
FIG. 6 illustrates an exemplary method for creating large single crystal seed layers, according to an embodiment of the present invention; -
FIGS. 7A-7B illustrate an exemplary apparatus for casting low carbon monocrystalline or multicrystalline silicon, according to an embodiment of the present invention; -
FIG. 8 illustrates an exemplary apparatus for casting monocrystalline or multi-crystalline silicon, according to embodiments of the present invention; -
FIG. 9 illustrates an exemplary tapered wall crucible, according to embodiments of the present invention; -
FIG. 10 illustrates an exemplary tapered wall crucible, according to embodiments of the present invention; -
FIG. 11 illustrates an exemplary silicon ingot, according to embodiments of the present invention; -
FIG. 12 illustrates an exemplary lifetime scan of a silicon ingot made with a conventional crucible; -
FIG. 13 illustrates an exemplary lifetime scan of a silicon ingot, according to embodiments of the present invention; -
FIG. 14 illustrates an exemplary lifetime scan of a silicon ingot, according to embodiments of the present invention; and -
FIG. 15 illustrates an exemplary silicon ingot, according to embodiments of the present invention. - Reference will now be made in detail to embodiments of the present invention, examples of which are illustrated in the accompanying drawings. Wherever possible, the same or similar reference numbers will be used throughout the drawings to refer to the same or like parts.
- In embodiments consistent with the invention, the crystallization of molten silicon is conducted by casting processes using seed crystals. As disclosed herein, such casting processes may be implemented so that the size, shape, and orientation of crystal grains in the cast body of crystallized silicon is controlled. As used herein, the term “cast” means that the silicon is formed by cooling molten silicon in a mold or vessel used to hold the molten silicon. By way of example, the silicon can be formed by solidification in a crucible, where solidification is initiated from at least one wall of the crucible, and not through a cooled foreign object drawing silicon out of the crucible. Thus, the crystallization of molten silicon is not controlled by “pulling” a boule either by moving a seed or moving the mold, vessel, or crucible. Further, consistent with an embodiment of the present invention, the mold, vessel, or crucible includes at least one hot side wall surface for solidifying the molten silicon. As used herein, the term “hot-wall” refers to a surface that is isothermal or hotter than molten silicon. Preferably, a hot-wall surface remains fixed during processing of the silicon.
- Consistent with embodiments of the invention, the crystallized silicon can be either continuous monocrystalline, or continuous multi-crystalline having controlled grain orientations. As used herein, the term “continuous monocrystalline silicon” refers to single crystal silicon, where the body of silicon is one homogeneous body of monocrystalline silicon and not smaller pieces of silicon joined together to form a larger piece of silicon. Further, as used herein, the term “continuous multi-crystalline silicon” refers to multi-crystalline silicon where the body of silicon is one homogeneous body of multi-crystalline silicon and not smaller pieces of silicon joined together to form a larger piece of silicon.
- Casting of silicon, according to embodiments of the present invention, can be accomplished by positioning a desired collection of crystalline silicon “seeds” in, for example, the bottom of a vessel, such as a quartz crucible that can hold molten silicon. The seeds may cover all, or most, or substantially all, of the bottom of the crucible. As used herein, the term “seed” refers to a geometrically shaped piece of silicon with a desired crystal structure, having a side that conforms to a surface of a vessel in which it may be placed. Such a seed can be either a monocrystalline piece of silicon or a piece of geometrically ordered multi-crystalline silicon. Consistent with the present invention, a seed may have a top surface that is parallel to its bottom surface, although this does not have to be the case. For example, a seed can be a piece of silicon, varying in size from about 2 mm to about 10 mm across, to about 100 mm to about 1000 mm across. The piece of silicon may have a thickness of about 1 mm to about 1000 mm, preferably about 10 mm to about 50 mm. A suitable size and shape of the seed may be selected for convenience and tiling. Tiling, which will be described in more detail below, is where silicon seed crystals are arranged in a predetermined geometric orientation or pattern across either the bottom or the sides and bottom surfaces of a crucible.
- Silicon feedstock may then be introduced into the crucible over the seeds, and then the feedstock is melted. Alternatively, molten silicon may be poured directly into the crucible and over the seeds. When molten silicon is poured, the crucible is preferably first brought very close to or up to the melting temperature of silicon, and then the molten silicon is poured in. Consistent with embodiments of the invention, a thin layer of the seeds can be melted before solidification begins.
- The molten silicon is then allowed to cool and crystallize in the presence of the seeds, preferably in a manner such that the cooling of the molten silicon is conducted so that the crystallization of the molten silicon starts at or below the level of the original top of the solid seeds and proceeds away, preferably upwards away, from the seeds. This can be accomplished by extracting the heat of fusion through the seed crystals to a heat sink. As used herein, the term “heat sink” refers to a body of material used to extract heat from another body of material. A heat sink may extract heat by means of conduction of heat from a higher temperature area to a lower temperature area, by convection with a lower temperature fluid or by direct radiation of energy to a lower temperature object. A thermal gradient is generally maintained across a heat sink such that one side is in equilibrium with the object to be cooled while the other exchanges energy with a cooler area.
- According to embodiments of the invention, the liquid-solid interface between the molten silicon and the crystallized silicon, during melting or solidification, need not be maintained substantially flat throughout the casting process. That is, the solid-liquid interface at an edge of the molten silicon is controlled during the cooling so as to move in a direction that increases a distance between the molten silicon and the silicon seed crystal. As the solidification of the molten silicon starts, the solidification front is initially substantially flat, preferably with a strong curvature at the horizontal edges of the growing solid mass of silicon. The shape of the solid-liquid interface thus may have a controlled profile throughout the casting process.
- By conducting the crystallization of the molten silicon in a manner consistent with embodiments of the invention, cast silicon having specific, rather than random, grain boundaries and specific grain sizes can be made. Additionally, by aligning the seeds in a manner such that all seeds are oriented the same relative direction to each other, for example the (100) pole direction being perpendicular to a bottom of the crucible and the (110) pole direction at 45° to the sides of a rectangular or square cross-section crucible, large bodies of cast silicon can be obtained that are, or are essentially, monocrystalline silicon in which the pole direction of such cast silicon is the same as that of the seeds. Similarly, other pole directions may be perpendicular to the bottom of the crucible. Moreover, one or more seeds may be arranged so that any common pole direction is perpendicular to a bottom of the crucible. Furthermore, consistent with an embodiment of the invention, seed crystals of two or more different pole directions can be used together to maximize the effectiveness of the crystal growth, creating a volume of silicon as large as possible with the desired crystal orientation.
- The seeds used for casting processes, consistent with embodiments of the invention, can be of any desired size and shape, but are suitably geometrically shaped pieces of monocrystalline, or geometrically ordered multi-crystalline, silicon, such as square, rectangular, hexagonal, rhomboid or octagonal shaped pieces of silicon. They can be shaped conducive to tiling, so they can be placed or “tiled” edge-to-edge and conformed to the bottom of a crucible in a desired pattern. Also consistent with embodiments of the invention, seeds can be placed on one or more sides of the crucible. Such seeds can be obtained, for example, by sawing a source of crystalline silicon, such as a boule of monocrystalline silicon, into pieces having the desired shapes. The seeds can also be formed by cutting them from a sample of silicon made by a process according to the embodiments of the invention, such that seeds for use in subsequent casting processes can be made from an initial casting process. For example, a smaller piece of dislocation-free seed material can used to grow a large dislocation free single crystal, sufficient to cover the entire bottom of the crucible for use as a new seed crystal layer.
- Processes and apparatuses for preparing silicon in accordance with embodiments of the invention will now be described. However, it is to be understood that these are not the only ways to form silicon consistent with the embodiments of the invention.
- Referring to
FIGS. 1A and 1B , the cross-section of a casting station hot zone is depicted inFIG. 1A , showingliquid silicon 100 andsolid silicon 101 at the end of the melting stage of a seeded casting process. The silicon is positioned in a bottomed andwalled crucible 110, which may be, for example, a fused quartz or silica crucible. At this point,solid silicon 101 incrucible 110 is entirely constituted from a seed layer of silicon previously loaded at the bottom of the crucible. Feedstock silicon (not shown) is introduced on top of the seed layer. Feedstock silicon can either be loaded as a solid and then melted in the crucible, or melted in a separate container and introduced as a liquid on top of the seeds. In either case, the original silicon seed layer is partially melted andsolid silicon 101 is entirely composed of the remainder of the silicon seed layer. Preferably,crucible 110 has a release coating such as one made from silica, silicon nitride, or a liquid encapsulant, to aid in the removal of crystallized silicon fromcrucible 110. - Still referring to
FIG. 1A , in this depiction of a furnace hot zone,resistive heaters 120 provide the energy to maintain the temperature required to melt silicon, whileinsulation 130 prevents the escape of heat to an outer chamber (not shown). Consistent with an embodiment of the invention,crucible 110 is supported by a number of layers which also serve to conduct heat away from the silicon in a controlled way. For example, aheat conducting block 140 radiates heat to a water cooled chamber (not shown), thereby cooling the hot-zone components above it. Agraphite support plate 142, shown in cross section inFIG. 1A and in three dimensions inFIG. 1B , conducts heat fromheat conducting layer 141, which in turn conducts heat away fromcrucible 110 andsilicon layer 150 may surroundheat conducting layer 141, in an exemplary configuration, in order to alter the heat removal path and consequently alter the shape of the solidification front. Solidgraphite side plates 143surround crucible 110 and provide structural support to the crucible. Consistent with embodiments of the invention, the casting station may have agraphite support plate 142, though a tailored heat conduction path controlled by conductinglayer 141 and thermally insulatinglayer 150 is not required. - Still referring to
FIGS. 1A and 1B ,graphite side plates 143 may rest ongraphite support plate 142, and conduct heat directly toplate 142, which may create cold spots at the bottom edges of the crucible. The effect of the tailored heat conduction, vis-à-vislayers crucible 110 hotter, resulting in only a small amount of lateral melting. For example, as shown inFIG. 1A ,solid silicon 101 has a high curvature at its left and right edges due to the heat exchange occurring in materials belowcrucible 110. Such a curvature can result in the lateral expansion of the solid and outward growth of a seeded crystal structure. InFIG. 1 A, crystal growth directions ofsolid silicon 101 are indicated by black arrows. - Referring to
FIGS. 2A-2D , crystal growth of silicon maybe altered by altering the shape of the crucible. For example, crystal growth can be accomplished in an outwardlytapered crucible 200, as shown inFIGS. 2A and 2B , where the curvature ofliquid silicon 220 to thesolid silicon 221 promotes lateral expansion of the seeded crystal (not shown), whose growth direction is indicated by arrows inFIG. 2B . In another example, crystal growth can be accomplished in an inwardly taperedcrucible 210, as shown inFIGS. 2C and 2D , which, likecrucible 200 inFIG. 2A , also has the advantage of maximizing the amount ofusable cast silicon 222, and minimizing the amount of unusable orundesirable silicon 223 to be removed during cutting of the cast silicon ingot (222+223) into bricks (shown by dashed lines). The tapered shape ofundesirable silicon 223 on a side wall of the cast silicon (viewed in cross-section inFIG. 2D ) is due to the extra time that the silicon at the bottom of the crucible spends at a high temperature state during solidification and crystal growth compared with the silicon at the top of the ingot, which is cooled more quickly. -
FIG. 3 illustrates a cross-section of silicon (feedstock 300 and crystalline seeds 301) loaded intocrucible 310 for casting.Release coating 320, such as silicon nitride or silicon carbide, may be applied to areas ofcrucible 310 wherefeedstock 300contacts crucible 310, which corresponds to areas ofsilicon 300 that will become completely melted during casting. No coating has been applied belowcrystalline seeds 301.Seeds 301 will not be completely melted and thus will not adhere tocrucible 110. -
FIG. 4 illustrates a process for the reuse of a crystalline silicon seed layer. As shown inFIG. 4 , castingot 400 grown fromseed layer 401 is first sliced along the dotted lines to remove a slab of material containingseed layer 401. The slab of material is then trimmed at the dotted edges to remove excess material that might interfere with its placement in another crucible. Trimmedslab 402, having been trimmed to the size and shape oforiginal seed layer 401, is then treated, potentially with other similar pieces of silicon, in acontainer 410, such as a tank or a tub containing a suitable liquid or other material, to remove contaminants and debris from layer 401 (and possibly other pieces of silicon) before being placed in anew crucible 420 for use as a seed layer in a subsequent casting process. -
FIG. 5 illustrates an exemplary arrangement of single crystal silicon pieces arranged to form a seed layer. The (001) crystal orientation has been shown to have advantageous properties for the manufacture of silicon solar cells. (001) silicon may be chemically etched in such a way as to produce a pattern pyramids covering its entire surface, which can improve the light-trapping ability of the silicon by both decreasing reflection and increasing the path length of light in the material. Chemical etching may be accomplished by known methods. However, the casting of (001) silicon is made difficult by its tendency to grow grain boundaries at acute angles to its (001) pole direction when located next to a multicrystalline region of silicon. To counteract the growth of multicrystalline silicon, a geometric arrangement of a plurality of monocrystalline silicon seed crystals can be placed on at least one surface in a crucible (not shown), e.g., a bottom surface of a crucible, wherein the geometric arrangement includes close-packed polygons. As shown inFIG. 5 , a piece of (001)silicon 500 is surrounded by a periphery of rectangles of (111)silicon 501. The pole orientation of theperipheral silicon 501 is shown as (111), but it could be any crystal orientation that is competitively favored when grown next to a multicrystalline region. In this way, the majority of a resulting cast ingot (not shown) will be composed of (001) silicon, and the competitively favored (111) grains grown fromsilicon 501 will limit the growth of multicrystalline silicon in the region occupied by (001) silicon oversilicon 500. Similarly, silicon crystal grains produced by casting a body of multi-crystalline silicon, consistent with embodiments of the invention, may be grown in a columnar manner. Further, such crystal grains may have a cross section that is, or is close to, the shape of the seed from which it is formed, instead of having an (001) cross-sectional area that shrinks as solidification proceeds. When making silicon that has such specifically selected grain boundaries, preferably the grain boundary junctions only have three grain boundaries meeting at a corner, a condition met in the arrangement shown inFIG. 5 . -
FIG. 6 illustrates a process for manufacturing large area, dislocation-free single crystals for use as seed layers. In this process, depicted in cross-section,polycrystalline feedstock 600 is loaded together with asingle crystal seed 601 which may have lateral dimensions from about 25 cm2 to about 10,000 cm2 in area and a thickness from about 3 mm to about 1000 mm.Feedstock 600 is placed incrucible 610, which is then placed in a station (not shown) on top oflayers parts 620 should preferably be about the same shape of bottom ofcrucible 610, having a lateral area from about 50% to about 150% that ofseed crystal 601. During melting, heat is extracted through thermally conductingarea 620 to asupport plate 621, while heat is prevented from passing through thermally insulatinglayer 630. Heat is conducted out through thermally conductingarea 620 even during the melting phase of casting, in order to prevent the complete melting ofseed crystal 601. Once allfeedstock 600 and a small portion ofseed crystal 601 are melted intoliquid silicon 602, remainingsolid silicon 603 then acts as the nucleation layer for the solidification process. The presence of insulatinglayer 630 helps control the shape ofsolid silicon 603 during nucleation and growth, as well as the direction of solidification, indicated by arrows inFIG. 6 . The strong curvature in the solidification surface causes an outward growth ofsolid silicon 603, whilemulticrystalline regions 605 are minimized. Onceingot 604 is cast, horizontal layers may be cut (dashed lines) from the upper parts of the ingot to be used asnew seed slabs 606.Slabs 606 can be cleaned, trimmed, and used as a complete seed layer for a new ingot in anew crucible 610, or as a starting point for an even larger single crystal, again using the process just described. -
FIGS. 7A and 7B are depictions of the cross-section of an apparatus for the casting of low carbon monocrystalline or multicrystalline silicon in a seeded ingot. As shown inFIG. 7A ,seed crystal 700 is loaded together withfeedstock 701 incrucible 710 located in a furnace hot zone (unlabeled).Crucible 710, though illustrated as covered with ceramic lid 711 (also shown inFIG. 7B ), may be uncovered and completely open to the surrounding atmosphere. In casting, carbon can be incorporated into an ingot from detached pieces ofgraphite insulation 720 which may fall intocrucible 710, or by a gas phase reaction where oxygen fromcrucible 710 dissolves into the silicon melt and then evaporates as SiO molecules (not shown). These molecules can adhere tographite parts - The CO gas molecule enters the liquid where SiC forms and O is again liberated to repeat the cycle. By introducing ceramic lid 711 (shown in
FIG. 7B ) tocrucible 710, and carefully controlling process gas 730 (which may be, for example, argon), both mechanisms of carbon incorporation can be effectively stopped, or severely restricted.Ceramic lid 711 can be made of a number of materials including, for example, fused silica, quartz, silicon carbide, silicon nitride, and the like. It is desirable for the design that a fresh supply of an inert gas, such as argon, come in throughchannel 740 and exit through another channel (not shown) in order to prevent the above-described carbon gas reaction. - Still referring to
FIGS. 7A and 7B , the casting process can be operated either by loading one ormore seeds 700 andfeedstock 701 prior to installingcrucible 710 in the furnace, or by loading only one ormore seeds 700 and later introducingliquid silicon 750 into the crucible from a separate melt chamber. -
FIG. 8 illustrates an apparatus consistent with embodiments of this invention for modifying the shape of the solid-liquid interface during casting. As shown inFIG. 8 ,primary heaters 820 and anadditional heater 840 are placed in the hot zone (shown surrounded by insulation 831) of a casting station to introduce targeted heating tomaterial Liquid material 800 on top ofsolid seed material 801 has an interface that is curved at the edges, near the side walls ofcrucible 810.Primary heaters 820 together with primary heat sink 860 normally work to produce a substantially flat solid-liquid interface (not shown). However,additional heater 840 couples an electric current directly tomaterial material crucible 810, and thereby meltssolid material 801 in its vicinity. -
Additional heater 840, as shown inFIG. 8 , is a coil of conductive metal, which may be, for example, copper, that is cooled with circulatingliquid 850 and thermally insulated fromprimary heaters 820 by surroundinglayer 830.Additional heater 840 may be a single turncoil surrounding crucible 810 in a loop, as illustrated inFIG. 8 , or it may have multiple loops forming a helix having any desired spacing between loops constituting the helix.Additional heater 840 may also be configured so that it can move relative to the walls ofcrucible 810 in order to affect the solid-liquid interface (not shown).Additional heater 840 operates by electrical current flowing through the copper pipe while the water cools it so the current through the pipe forms a strong magnetic field which couples with the liquid silicon, inducing a corresponding current in the silicon. Resistive heat from the current in and/or through the silicon provides the heating action in a localized way and/or manner. - Alternately, resistive heaters could be used as
additional heaters 840, but resistive heaters may not be as efficient in targeting the heat application to a specific volume of material, such asmaterial FIG. 8 ,additional heater 840 would only be activated near the end of the melting cycle, so as not to overly meltseed material 801.Additional heater 840 would continue to apply heat tocrucible 810 through at least about the first 20% of the solidification process.Additional heater 840 may also continue to apply heat tocrucible 810 through the entire solidification process until implementation of the cooling stage. - As disclosed herein, embodiments of the invention can be used to produce large bodies of monocrystalline silicon, near-monocrystalline silicon, bi-crystal silicon, or geometric multi-crystalline silicon, by a simple and cost-effective casting process. The silicon feedstock used in processes consistent with embodiments of the invention, and thus the silicon produced, can contain one or more dopants selected from a list including: boron, aluminum, lithium, gallium, phosphorus, antimony, arsenic, and bismuth. The total amount of such dopant or dopants can be about 0.01 parts per million (ppm) by atomic % (ppma) to about 2 ppma. Preferably, the amount of dopant or dopants in the silicon is an amount such that a wafer made from the silicon has a resistivity of about 0.1 to about 50 ohm-cm, preferably of about 0.5 to about 5.0 ohm-cm. Alternately, other materials having a suitable liquid phase can be cast using the processes and apparatuses disclosed here. For example, germanium, gallium arsenide, silicon germanium, sapphire, and a number of other III-V or II-VI materials, as well as metals and alloys, could be cast according to embodiments of the present invention.
- Moreover, although casting of silicon has been described herein, other semiconductor materials and nonmetallic crystalline materials may be cast without departing from the scope and spirit of the invention. For example, the inventors have contemplated casting of other materials consistent with embodiments of the invention, such as germanium, gallium arsenide, silicon germanium, aluminum oxide (including its single crystal form of sapphire), gallium nitride, zinc oxide, zinc sulfide, gallium indium arsenide, indium antimonide, germanium, yttrium barium oxides, lanthanide oxides, magnesium oxide, calcium oxide, and other semiconductors, oxides, and intermetallics with a liquid phase. In addition, a number of other group III-V or group II-VI materials, as well as metals and alloys, could be cast according to embodiments of the present invention.
- The terms “crucibles” refers broadly to a vessels, receivers, or containers capable of withstanding elevated temperatures, such as greater than about 500° C. Crucibles may include any suitable size and/or shape. Typical shapes include square, rectangle, round and urn. Desirably, the walls of the crucible angle and/or taper inwards and/or outwards with respect to a plane perpendicular to a bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface. Typically, but not necessarily, the crucible walls are linear, such as to facilitate fabrication. Curved and/or profiled sidewalls are possible as well. Typical ranges of the ratio of width to height includes about from 3:2 to about 4:1. A wall thickness generally, but not necessarily, remains generally constant with respect to height, such as to provide uniform thermal resistance.
- Crucibles may include suitable materials, such as alumina, graphite, silica, fused silica, and/or any other high temperature material at least mostly inert to molten silicon. Crucibles may be single use and/or multiple uses. According to some embodiments, the crucible splits and/or fractures upon solidification of the silicon, such as to facilitate removal of the solid body.
- The first temperature, such as a range of between about 1410° C. and about 1300° C. usually includes a temperature gradient across and/or through the solid body. The second temperature, such as about 1350° C. on average usually includes a reduced temperature gradient and/or a uniform temperature profile across and/or through the solid body. Alternately, the first temperature may include a range of between about 1410° C. to about 1450° C. and the second temperature may include a range of between about 1200° C. and about 1400° C. The step of reducing the temperature gradient may be referred to sometimes as annealing in the context of this disclosure. Annealing may include closing up the insulation, for example.
- In some embodiments, the method for the manufacture of cast silicon includes placing and/or forming molten silicon in a crucible or vessel having tapered inward walls, with respect to a plane perpendicular to a bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface. The method may include forming a solid body of silicon by extraction of heat through the bottom surface of the crucible and bringing the solid body to a first temperature. The solid body can be processed by cooling the solid body to a second temperature, extracting the solid body from the crucible, and slicing the solid body into bricks, blocks, wafers, seed crystals, and the like, for example. The tapered inward walls may comprise any suitable angle, such as an angle of between about 1° and about 25°, desirably between about 5° and about 10°, and more desirably about 5°.
- In some embodiments, the method includes placing a seed crystal on the bottom surface of the crucible and maintaining the seed crystal in at least a partially solid state during a casting and/or manufacturing process.
- The casting process may include any suitable temperatures, such as a first temperature including a range of between about 1410° C. to about 1450° C. and a second temperature including a range of between about 1200° C. and about 1400° C. In another embodiment, the first temperature is greater than about ambient conditions and the second temperature is about ambient conditions.
- In some embodiments, a vertical boundary between a portion of usable cast silicon and a portion of undesirable silicon forms at least generally perpendicular to a bottom surface of the crucible and at least generally planar. The term boundary refers to an interface, a limit and/or an intersection to two substances and/or materials having at least one different characteristic or attribute, such as monocrystalline silicon and multicrystalline silicon, or such as high and low lifetime silicon. The boundary may be perpendicular with respect to the bottom of the crucible. The term planer includes being able to be sliced and or separated, such as with a band saw and/or other suitable cutting device in a single pass between usable silicon and undesirable silicon. Desirably, but not necessarily, the portion of usable cast silicon comprises at least generally monocrystalline silicon.
- In some embodiments, a method of manufacturing cast silicon includes placing and/or forming molten silicon in a crucible having walls that are tapered outwards with an angle greater than 5°, with respect to a plane perpendicular to a bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface. The method further includes solidifying the silicon by extraction of heat through the bottom surface of the crucible, bringing the solid body to a first temperature, cooling the solid body to a second temperature, extracting the solid body from the crucible, and slicing the solid body into bricks, blocks, wafers, seed crystals, and the like, for example.
- In some embodiments, the invention includes a crucible for the casting of silicon having a bottom surface and plurality of side walls, wherein at least one of the plurality of side walls tapers inwards toward a center of the crucible at an angle from about 1° to about 25° with respect to a plane perpendicular to the bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface, reducing the vessel cross-sectional area taken in the direction away from the bottom surface.
- Desirably, but not necessarily, the crucible includes silica and/or any other suitable material. The crucible includes any suitable, size and/or shape, such as a ratio of a width to a height about from 3:2 to about 4:1.
- In some embodiments, the invention includes a crucible for the casting of silicon with a bottom surface and a plurality of side walls, wherein at least one of the plurality of side walls tapers outwards from a center of the crucible at an angle greater than about 5°, with respect to a plane perpendicular to the bottom surface of the crucible and viewed in a direction extending upwards from the bottom surface, increasing the vessel cross-sectional area taken in the direction away from the bottom surface.
- In some embodiments, the invention includes a solid body of silicon, with a portion of usable cast silicon comprising generally planar and generally perpendicular sides, and a portion of undesirable silicon surrounding at least one side of the portion of usable cast silicon. Desirably, but not necessarily, the usable cast silicon forms a rectangular block and/or a cube. The usable silicon may include monocrystalline silicon and/or any other suitable material. The undesirable silicon generally has a vertical interface with the usable silicon, such as easily cut with a band saw. The undesirable silicon may surround a bottom and at least one side of the usable silicon, as shown in
FIG. 2D , for Example. The undesirable, silicon may surround a bottom and lateral sides, such as four sides, for example. The undesirable silicon may have an outside shape generally, conforming to an interior shape of the crucible and/or vessel including tapered inward and/or tapered outwards, for example. - The following examples are experimental results consistent with embodiments of the invention. These examples are presented for merely exemplifying and illustrating embodiments of the invention and should not be construed as limiting the scope of the invention in any manner.
- Crucible preparation: A crucible was placed on a supporting structure consisting of two layers. The bottom layer of the supporting structure is a solid isomolded graphite plate measuring 80 cm by 80 cm by 2.5 cm which supported a composite layer. The upper composite layer had an inner region that was a thermally conducting isomolded graphite plate measuring 60 cm by 60 cm by 1.2 cm, and was surrounded on all sides by a 10 cm perimeter of thermally insulating graphite fiber board of 1.2 cm thickness. In this way, the composite layer completely covered the bottom layer.
- Seed preparation: A boule of pure Czochralski (CZ) silicon (monocrystalline), obtained from MEMC, Inc. and having 0.3 ppma of boron, was cut down along its length using a diamond coated band saw so that it had a square cross section measuring from 140 mm per side. The resulting block of monocrystalline silicon was cut through its cross section using the same saw into slabs having a thickness of about 2 cm to about 3 cm. These slabs were used as monocrystalline silicon seed crystals, or “seeds.” The (100) crystallographic pole orientation of the silicon boule was maintained. The resulting single crystal silicon slabs were then arranged in the bottom of a quartz crucible so that the (100) direction of the slabs faced up, and the (110) direction was kept parallel to one side of the crucible. The quartz crucible had a square cross section with 68 cm on a side and a depth of about 40 cm. The slabs were arranged in the bottom of the crucible with their long dimension parallel to the bottom of the crucible and their sides touching to form a single, complete layer of such slabs on the bottom of the crucible.
- Casting: The crucible was loaded with the seed plates and then filled up to a total mass of 265 kg of solid silicon feedstock at room temperature. A few wafers of highly boron doped silicon were added to provide enough boron for a total ingot doping of ˜0.3 ppma. The filled crucible was first surrounded with graphite support plates that rested on the thermally insulating portion of the support structure, and was then loaded into an in-situ melting/directional solidification casting station used to cast multi-crystalline silicon. The melt process was run by heating resistive heaters to approximately 1550° C., and the heaters were configured so that the heating came from the top while heat was allowed to radiate out the bottom by opening the insulation a total of 6 cm. This configuration caused the melting to proceed in a top-down direction towards the bottom of the crucible. The passive cooling through the bottom caused the seed crystals to be maintained in solid state at the melting temperature, as was monitored by a thermocouple. The extent of melting was measured by a quartz dip rod that was lowered into the melt every ten minutes. The dip rod height was compared with a measurement taken on an empty crucible in the station to determine the height of the remaining solid material. By dip rod measurement, first the feedstock melted, and then the melting phase was allowed to continue until only a height of about 1.5 cm of the seed crystals remained. At this point, the heating power was dropped to a temperature setting of 1500° C., while the radiation from the bottom was increased by opening the insulation to 12 cm. One or two additional millimeters of seed crystals melted before solidification began, as observed by dip-rod measurements. Then seeded single crystal growth proceeded until the end of the solidification step. The growth stage and the remainder of the casting cycle were performed with the normal parameters where the top-to-bottom thermal gradient is evened out, and then the entire ingot is slowly cooled to room temperature. The cast silicon product was a 66 cm by 66 cm by 24 cm ingot. The region of crystallinity consistent with the seeds began at the bottom and conformed with the edge of the unmelted material, and from there grew laterally outwards toward the crucible walls as growth began, and stabilized to a constant size towards the end of crystallization. The monocrystalline silicon structure was evident from visually inspecting the faces of bricks cut from the ingot.
- Seeding was accomplished as in Example 1, and an ingot was cast containing a large monocrystalline volume. After cooling, the ingot was stood on its side and loaded into a band saw with fixed diamond abrasive for cutting. The bottom of the ingot was cut off as a single layer with a thickness of 2 cm. This layer was then fixed horizontally on a cutting table. In the same band saw, the edges of the layer were trimmed such that approximately 1.5 cm was removed from each side. The slab was then sandblasted to remove glue and foreign materials, after which it was etched in a hot sodium hydroxide bath, rinsed, and dipped in a HCl bath to remove metals. The slab was then placed on the bottom of a standard crucible of the same size as the previous ingot. Silicon feedstock was loaded to a total mass of 265 kg and the casting process was repeated, producing a second seeded ingot.
- Seed preparation: A seed layer was prepared, starting with 18 kg of square, (100), plates used to line the bottom of a crucible, providing a coverage area of 58 by 58 cm and a thickness ranging from 2-3 cm. These plates were placed together into a larger square that was centered in the crucible. Next, this square was surrounded by a 2 cm thick layer of (111) oriented seed crystals, making the total seed layer a 63 cm by 63 cm square.
- Casting: The crucible containing the seeds was filled with silicon to a total mass of 265 kg and placed in a casting station. Casting was performed as in Example 1, monitoring the process to assure that the seed layer remained intact through the end of melt and beginning of solidification. The resulting ingot was cut into a 5×5 grid of 12.5 cm bricks. Optical inspection of the crystal structure of the bricks showed that the (111) crystals acted as a buffer layer, preventing the ingress of randomly nucleated grains into the (100) volume.
- Crucible preparation: A standard 69 cm2 crucible was placed on a support structure composed of two layers. The layers were composed as in Example 1 except that the dimensions of the composite layer were different. The bottom solid graphite layer had dimensions of 80×80×2.5 cm3 as before, but the heat conducting portion of the composite layer measured only 20×20×1.2 cm3, centered on top of the bottom layer. The remainder of the bottom layer was covered with heat insulating graphite fiber board.
- Seed preparation: A single piece of (100)-oriented single crystal silicon with a size of 21 cm by 21 cm by 2 cm was centered in the bottom of the crucible. The crucible was then filled with a balance of silicon feedstock to a total mass of 265 kg.
- Casting: The crucible and support plates were placed in a casting station and cycled as in Example 1, except that additional time was allowed for the solidification of the silicon, given the smaller heat extraction area. After cooling down, the ingot was sectioned. Visual inspection of the sectioned ingot verified the strong outwards growth of the crystals from the controlled heat extraction.
- Crucible preparation: A standard 69 cm2 crucible was placed on a graphite support plate and loaded with a seed layer, feedstock and dopant as in Example 1, except that the feedstock contained no silicon recycled from previous ingots. A fused silica lid that had dimensions of 69×69×12 cm3 was then placed on the crucible. A casting station was modified such that a telescoping tube was attached to the hole in the top insulation where the process gas is introduced. The charge was then loaded into the station and raised up to engage the telescope. The casting station was run using an altered recipe to allow better gas control and altered solidification settings to compensate for the effects of the crucible lid. The resulting ingot was measured to have 1/10th of the carbon concentration found in a typical ingot, and additionally had a mirror-like top surface and fewer included foreign particles than typical ingots.
- The
crucible 210 of this example and the corresponding cover are shown inFIG. 9 . An inward taperedwall crucible 210 or sometimes referred as an inverted tapered receiver was designed and fabricated. Plaster molds were cast and ceramics were then cast from the plaster molds. A two-piece mold pattern was used to form the inward tapered wall shape. The crucible was slip cast and then fired. Thecrucible 210 was coated with silicon nitride as a release coating - The
crucible 210 from Example 6 was then placed inside a larger receiver, as shown inFIG. 10 . The splash shield also shown inFIG. 10 was not utilized during the test. The integrity of thecrucible 210 of Example 6 was tested by pouring molten silicon into theunseeded crucible 210 and then cooled. Thecrucible 210 remained intact and casting parameters were measured. The resultingtapered ingot 225, as shown inFIG. 11 , was cut into a slab and lifetime scanned. The lifetime scans were relatively low since low purity recycle material was used during the test. - The lifetime scan refers to materials analysis for measuring a materials minority carrier lifetime using a microwave photo conductance decay (micro-PCD) instrument. The minority carrier lifetime is the metric that determines bulk photovoltaic quality for a material, and it indicates the average time (actually 1/e decay time) that minority charge carriers (electrons for p-type material, holes for n-type material) exist after being created by the absorption of incident light.
-
FIG. 12 shows a lifetime scan of a silicon block fabricated in a conventional straight wall crucible. The scan shows an “edge effect” within the encapsulated cells. Without being bound by theory, the edge effect may occur due to the solid state diffusion of impurities from the receiver or crucible into the bulk of the ingot. The edge effect is generally more pronounced near the ingot bottom and along the side walls, where the material sits in a solid state at elevated temperatures longer than the remainder of the ingot so the impurities can diffuse in further near the bottom than the top of the ingot.FIG. 12 shows a brick with the edge effect along the left side and the bottom which reduces the amount ofusable silicon 222 from the ingot, since a vertical saw cut results inusable silicon 222 lost with theundesirable silicon 223 or containsundesirable silicon 223 with the block ofusable silicon 222. - In contrast,
FIG. 13 shows the cross section lifetime scan of theingot 225 of Example 7 with lines added to indicate where blocks would be sized from theingot 225.FIG. 13 shows the edge effect has tracked the crucible shape and benefits material quality. As would be hoped, theusable silicon 222 of theingot 225 has a vertical and planar boundary with theundesirable silicon 223 and perpendicular to the bottom of the crucible, unlike the angled boundary showing inFIG. 12 . The scan ofFIG. 13 is unable to completely display the shape of the taperedingot 225 due to a rectangular scanning area. - Another casting was made according to Example 7, but the temperature was lowered to 1460° C. instead of 1470° C.
FIG. 14 shows the lifetime scan of the resultingingot 225. The edge effect orundesirable silicon 223 remained outside of most of the cross sectional area. Some seeding did occur with this test. As shown on the right side inFIG. 15 , the front of theingot 225 included a predominantly single crystal (monocrystalline) 222 with somemulticrystalline silicon 223.FIG. 14 is unable to completely display the shape of the tapered ingot due to a rectangular scanning area. - The tapered wall crucible desirably reduced and/or eliminated the edge effect for some wafers and/or cells. Future work may include using larger casting stations and/or crucibles.
- Thus, consistent with embodiments of the invention and the examples described above, wafers made from the silicon consistent with embodiments of the invention are suitably thin and can be used in photovoltaic cells. For example, wafers can be about 10 microns thick to about 300 microns thick. Further, the wafers used in the photovoltaic cells preferably have a diffusion length (Lp) that is greater than the wafer thickness (t). For example, the ratio of Lp to t is suitably at least 0.5. It can, for example, be at least about 1.1, or at least about 2. The diffusion length is the average distance that minority carriers (such as electrons in p-type material) can diffuse before recombining with the majority carriers (holes in p-type material). The Lp is related to the minority carrier lifetime T through the relationship Lp=(Dπ)1/2, where D is the diffusion constant. The diffusion length can be measured by a number of techniques, such as the Photon-Beam-Induced Current technique or the Surface Photovoltage technique. See for example, “Fundamentals of Solar Cells”, by A. Fahrenbruch and R. Bube, Academic Press, 1983, pp. 90-102, which is incorporated by reference herein, for a description of how the diffusion length can be measured.
- The wafers can have a width of about 100 millimeters to about 600 millimeters. Preferably, the wafers have at least one dimension being at least about 50 mm. The wafers made from the silicon of the invention, and consequently the photovoltaic cells made by the invention can, for example, have a surface area of about 100 to about 3600 square centimeters. The front surface of the wafer is preferably textured. For example, the wafer can be suitably textured using chemical etching, plasma etching, or laser or mechanical scribing. If a monocrystalline wafer is used, the wafer can be etched to form an anisotropically textured surface by treating the wafer in an aqueous solution of a base, such as sodium hydroxide, at an elevated temperature, for example about 70° C. to about 90° C., for about 10 to about 120 minutes. The aqueous solution may contain an alcohol, such as isopropanol.
- Thus, solar cells can be manufactured using the wafers produced from cast silicon ingots according to the embodiments of the invention, by slicing the solid body of cast silicon to form at least one wafer; optionally performing a cleaning procedure on a surface of the wafer; optionally performing a texturing step on the surface; forming a p-n junction by doping the surface; optionally depositing an anti-reflective coating on the surface; optionally forming a back surface field with, for example, an aluminum sintering step; and forming electrically conductive contacts on at least one surface of the wafer.
- In a typical and general process for preparing a photovoltaic cell using, for example, a p-type silicon wafer, the wafer is exposed on one side to a suitable n-dopant to form an emitter layer and a p-n junction on the front, or light-receiving side of the wafer. Typically, the n-type layer or emitter layer is formed by first depositing the n-dopant onto the front surface of the p-type wafer using techniques commonly employed in the art such as chemical or physical deposition and, after such deposition, the n-dopant, for example, phosphorus, is driven into the front surface of the silicon wafer to further diffuse the n-dopant into the wafer surface. This “drive-in” step is commonly accomplished by exposing the wafer to high temperatures. A p-n junction is thereby formed at the boundary region between the n-type layer and the p-type silicon wafer substrate. The wafer surface, prior to the phosphorus or other doping to form the emitter layer, can be textured. In order to further improve light absorption, an anti-reflective coating, such as silicon nitride, is typically applied to the front of the wafer, sometimes providing simultaneous surface and or bulk passivation.
- In order to utilize the electrical potential generated by exposing the p-n junction to light energy, the photovoltaic cell is typically provided with a conductive front electrical contact on the front face of the wafer and a conductive back electrical contact on the back face of the wafer, although both contacts can be on the back of the wafer. Such contacts are typically made of one or more highly electrically conducting metals and are, therefore, typically opaque.
- Thus, solar cells consistent with the embodiments described above may comprise a wafer sliced from a body of continuous monocrystalline silicon being substantially free of radially-distributed defects, the body having at least two dimensions each being at least about 35 cm, a p-n junction in the wafer, an anti-reflective coating on a surface of the wafer; and a plurality of electrically conductive contacts on at least one surface of the wafer, wherein the body is substantially free of swirl defects and substantially free of oxygen-induced stacking fault defects.
- Also, solar cells consistent with the embodiments described above may comprise a wafer sliced from a body of continuous multi-crystalline silicon being substantially free of radially-distributed defects, the body having a predetermined arrangement of grain orientations with a common pole direction being perpendicular to a surface of the body, the body further having at least two dimensions each being at least about 10 cm, a p-n junction in the wafer; an anti-reflective coating on a surface of the wafer, and a plurality of electrically conductive contacts on at least one surface of the wafer, wherein the multi-crystalline silicon includes silicon grains having an average grain boundary length of about 0.5 cm to about 30 cm, and wherein the body is substantially free of swirl defects and substantially free of oxygen-induced stacking fault defects.
- It will be apparent to those skilled in the art that various modifications and variations can be made in the disclosed structures and methods without departing from the scope or spirit of the invention. Other embodiments of the invention will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered exemplary only, with a true scope and spirit of the invention being indicated by the following claims.
Claims (22)