US20100173074A1 - Method and apparatus for modulation of precursor exposure during a pulsed deposition process - Google Patents
Method and apparatus for modulation of precursor exposure during a pulsed deposition process Download PDFInfo
- Publication number
- US20100173074A1 US20100173074A1 US12/702,747 US70274710A US2010173074A1 US 20100173074 A1 US20100173074 A1 US 20100173074A1 US 70274710 A US70274710 A US 70274710A US 2010173074 A1 US2010173074 A1 US 2010173074A1
- Authority
- US
- United States
- Prior art keywords
- chamber
- pedestal
- volume
- reaction
- precursor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method of depositing material on a substrate comprises providing a reactor with a reaction chamber having a first volume, and contacting a surface of a substrate in the reaction chamber with a first precursor at the first chamber volume to react with and deposit a first layer on the substrate. The method further includes enlarging the reaction chamber to a second, larger volume and removing undeposited first precursor and any excess reaction product to end reaction of the first precursor with the substrate.
Description
- This application is a divisional of U.S. patent application Ser. No. 10/821,092 entitled “Method And Apparatus For Modulation of Precursor Exposure During A Pulsed Deposition”, filed on Apr. 8, 2004.
- 1. Field of the Invention
- The present invention relates to reactors used in the semiconductor manufacturing industry and, in particular, to a reactor for pulsed layer deposition of thin films in the fabrication of integrated circuits.
- 2. Description of Related Art
- A primary goal of the semiconductor manufacturing industry is to reduce the size of integrated circuits in order to them to perform more operations in a shorter time. As integrated circuit device features become smaller, several technical difficulties are presented. One such problem is depositing conformal thin films in holes or trenches having a small diameter or a small width-to-depth ratio. One standard technique for depositing such thin films has been chemical vapor deposition (CVD), which works well for feature sizes on the order of 120 nm and smaller. However, CVD may not be extendable to high aspect ratio features at these dimensions. Pulsed layer deposition (PLD) has been seen as a likely replacement for film deposition and holes below 120 nm in width and for the high aspect ratio features.
- PLD is useful for depositing thin films having two components. The process generally consists of four steps, which may be repeated to produce films of desired thickness. The steps are normally conducted in a reactor with a controlled environment. The first step consists of saturating a surface with the first precursor or reactant needed to create the film, followed by removing the excess byproducts of the first reaction and any unreacted precursor from the reactor. The next step consists of saturating the surface with a second precursor or reactant in order to form the desired film. The last step is to remove unwanted excess byproducts from the third step and any unreacted precursor.
- The precursor exposure steps of PLD are said to be self-limiting, that is, the amount of material deposited on the surface stops depositing after a relatively short period of time. However, in order for the deposition reactions of steps one and three to go to completion, the surface must receive a high exposure of the precursor. This is achieved if the precursor is allowed to remain for a long period above the surface or if the concentration of the precursor above the wafer is high. Provided the precursor exposures are high and the purging performed during the second and third steps are sufficient, there results a thin film consisting of the reaction product of the two components. The purging steps are sufficient if concentrations of the un-reacted precursors and reaction byproducts are low enough to minimize or eliminate one precursor or its byproducts from contacting, and possibly reacting with, the second precursor or its byproducts.
- In addition to the steps outlined above, there are additional practical requirements. First, each step should be as short as possible to fulfill the requirement that the thin film be formed as fast as possible to make the entire process commercially viable for ultra large scale integration (ULSI) of the circuits. Second, the smallest possible amount of precursor should be used because precursor costs must be minimized to make the process commercially viable, and un-reacted precursor and byproducts must be minimized to reduce the need for abatement of environmentally harmful substances. Accordingly, the requirements for a rapid process and use of minimum amount of precursor, coupled with the requirements of high exposure and sufficient purging, necessitate trade offs to be made in the PLD process.
- Bearing in mind the problems and deficiencies of the prior art, it is therefore an object of the present invention to provide a method and apparatus for depositing films in a pulsed layer deposition process.
- It is another object of the present invention to provide a method and apparatus for controlling exposure of precursors or reactants to a substrate during a pulsed layer deposition process.
- A further object of the present invention is to provide a method and apparatus which reduces the amount of precursor or reactant needed to deposit a film in a pulsed layer deposition process.
- It is yet another object of the present invention to provide a method and apparatus that reduces the amount of excess byproduct and unreacted precursor or reactant in a pulsed layer deposition process.
- Still other objects and advantages of the invention will in part be obvious and will in part be apparent from the specification.
- The above and other objects, which will be apparent to those skilled in art, are achieved in the present invention which is directed to a method of depositing material on a substrate comprising providing a reactor with a reaction chamber having a first volume, and contacting a surface of a substrate in the reaction chamber with a first precursor at the first chamber volume to react with and deposit a first layer on the substrate. The method further includes enlarging the reaction chamber to a second, larger volume and removing undeposited first precursor and any excess reaction product to end reaction of the first precursor with the substrate.
- The method may further include reducing the reaction chamber to the first chamber volume, and contacting the first layer in the reaction chamber with a second precursor at the first chamber volume to react with and deposit a second layer on the first layer, thereby forming a film. The method then includes enlarging the reaction chamber to the second volume and removing undeposited second precursor and any excess reaction product to end reaction of the second precursor.
- The removal of undeposited first precursor and any excess reaction product may be by purging the reaction chamber at the second volume with a gas, and/or by exposing the reaction chamber at the second volume to a vacuum.
- The reaction chamber preferably includes a pedestal adapted to secure the substrate during the deposition and which is movable between first and second positions. A first chamber section is above the pedestal in the first position and defines the first chamber volume. A second chamber section is outside the first chamber section. The reaction chamber is enlarged to the second, larger volume by moving the pedestal to the second position such that the first and second chamber sections together with the pedestal in the second position define the second chamber volume.
- In another aspect, the present invention is directed to an apparatus for depositing a film on a substrate comprising a reactor having a variable volume reaction chamber for reacting one or more precursors with the substrate to deposit a film thereon, and a pedestal in the reaction chamber adapted to secure the substrate during the deposition. The pedestal is movable between first and second positions, so that a first chamber section is above the pedestal in the first position, and a second chamber section is outside the first chamber section. Volume of the reaction chamber may be varied by moving the pedestal between the first position, where the first chamber section together with the pedestal in the first position define a first chamber volume, and the second position, where the first and second chamber sections together with the pedestal in the second position define a second, larger chamber volume.
- The pedestal is preferably movable upwards to the first position and downwards to the second position. The second chamber section may be on one or more sides of the pedestal, or below the pedestal. The apparatus may further include a perforated plate, above the pedestal in the first chamber section, which is adapted to diffuse the precursors. It may also include an environmental control for maintaining the first chamber section at a different temperature than the second chamber section.
- The features of the invention believed to be novel and the elements characteristic of the invention are set forth with particularity in the appended claims. The figures are for illustration purposes only and are not drawn to scale. The invention itself, however, both as to organization and method of operation, may best be understood by reference to the detailed description which follows taken in conjunction with the accompanying drawings in which:
-
FIG. 1 is a cross-sectional elevational view of the preferred reactor apparatus of the present invention, with the pedestal in the raised position providing a smaller reaction chamber volume. -
FIG. 2 is a cross-sectional elevational view of the preferred reactor apparatus ofFIG. 1 , showing the pedestal in the lowered position providing a larger purging reactor chamber volume. -
FIG. 3 is a flow chart showing the preferred method of practicing the process of the present invention. -
FIG. 4 is a cross-sectional elevational view of an alternate embodiment of the reactor apparatus ofFIG. 1 , with the pedestal in the raised position. - In describing the preferred embodiment of the present invention, reference will be made herein to
FIGS. 1-4 of the drawings in which like numerals refer to like features of the invention. - The invention is a reactor apparatus and method for pulsed layer deposition of thin films that meets the requirements of high exposure of precursor and sufficient purging while maintaining low precursor usage and fast process time. The reactor consists of an isolated chamber with a pedestal for holding a wafer, a feed through for uniformly introducing precursor and purging fluid over the wafer surface, and a drain or vacuum source to permit the precursor, byproducts and purging fluids egress. The reactor has two zones, a small volume zone, and a large volume zone. The pedestal and wafer is placed in the small volume zone during precursor exposure, and then moved to the high volume zone, maintained at a lower pressure, to allow un-reacted precursor and byproduct an exit. Concurrently with moving the pedestal to the purge position, or immediately following, the purge fluid is turned on so un-reacted precursor and byproducts are both drawn out by the vacuum source and pushed out by the purge fluid.
- The preferred reactor apparatus for practicing the present is depicted in
FIGS. 1 and 2 .Reactor 10 comprises areaction chamber housing 100 having internalreactor chamber sections chamber section 104, communicates with apassageway 106 leading to a high vacuum source (not shown), with a shut offvalve 107 controlling communication therewith. Process fluids enter from a source (not shown) throughcontrol valve 108 andpassageway 111 intoreaction chamber 103. This source may hold solid, liquid or gaseous compounds, which are then processed by conventional means to provide the precursor in gaseous form throughpassageway 111. Perforateddiffusion plates chamber section 103 belowpassageway 111, and have different size openings therein in order to diffuse the flow of process fluids evenly into the reaction chamber. - Below
reactor chamber section 103 is disposed a moveablecircular pedestal 102 for securing awafer substrate 105 on which the film is to be deposited.Pedestal 102 is moveable between an upper position as shown inFIG. 1 , and a lower position as shown inFIG. 2 . Acolumnar pedestal base 115, on which thepedestal 102 is secured, is slideable in conjunction with a flexible, pleatedmetal housing section 114 to move between the two positions, while maintaining a sealed environment within the reaction chamber. - In the upper position (
FIG. 1 ), an initial, relatively small reactor chamber volume is defined by the upper andside walls 117 ofchamber section 103 and the surface ofpedestal 102. In this embodiment,pedestal 102 is of a diameter that is slightly smaller than the spacing between oppositereactor side walls 117, so that the pedestal may move upward to a position above the lower portion ofwalls 117.Reactor chamber section 104 is located below and on at least one side of, preferably completely around,pedestal 102. When the pedestal is moved down to its lowered position (FIG. 2 ), a subsequent larger reactor chamber volume is defined by the combined volume of bothchamber sections pedestal 102.Pedestal 102 may also be moveable to securewafer 105 in any intermediate position between the upper and lower positions depicted. - In order to control the temperature of
reactor chamber section 103 at a temperature different from the remainder of the reactor chamber, there are providedheating elements 112 along side the sidewalls ofchamber section 103, and coolingcoils 113 containing a re-circulating fluid in the overhead wall ofchamber section 103. Theseelectric heaters 112 andcooling coil 113 provide environmental controls for heating or cooling the wafer while in the smaller reactor chamber volume. - Operation of the apparatus is depicted in the process steps as shown in
FIG. 3 . At the start of theprocess 20, the pedestal is moved to the desired wafer loading position, and the wafer secured to the top ofpedestal 102. The reactor is then pressurized to its base pressure, 22. The pedestal is then moved upward to the reactor top, compacted position, 24, and the first precursor or reactant is flowed intochamber section 103 throughvalve 108 andpassageway 111. The temperature inreactor vessel 103 is also adjusted byenvironmental controls wafer surface 105 receives a high exposure of the first precursor. Because of the limited volume, smaller amounts of gaseous precursor may achieve higher desired concentration for reaction. Once the desired reaction is achieved along a layer of the wafer surface, the pedestal is moved to the bottom, expanded position 26, and the chambers are evacuated throughvalve 107 and simultaneously purged with a reaction-limiting purge gas throughvalve 108. The higher volume within combinedreaction chamber sections wafer substrate 105, the pedestal is again moved to the top position, 28, and the second precursor is flowed into the smallerinitial chamber volume 103 as described instep 24. Again, once the reaction with the second precursor is achieved, and a desired film thickness is deposited onwafer 105 surface, the pedestal is moved to the bottom position, 30, and vacuum and purge gas flow is again initiated in order to stop the reaction and remove excess second precursor and unwanted reaction byproducts from the larger volume reaction chamber. - Process steps 24-30 may be repeated as necessary to achieve the desired thickness of the deposited layer on the surface of
wafer substrate 105. Once the film deposition is completed, the pedestal is moved back to the desired wafer loading position, 32, and the reaction chamber is pumped to the wafer transfer pressure. A reactor isolation valve (not shown) is then opened and the wafer may be removed from the reaction chamber. - An example of pulse layer deposition utilizing the method and apparatus of the present invention is described below.
- With the reactor in the compacted position, trimethyl aluminum at a pressure of 12 torr is introduced into the chamber by opening
valve 108 for approximately 1 sec, to deposit an approximately monoatomic layer of aluminum oxide on to the wafer surface. The wafer pedestal is then lowered to the reactor expanded position, and an inert purge gas such as nitrogen is introduced at a high rate by openingvalve 108 to purge the remaining precursor and reactant gases over the wafer. Simultaneously,valve 107 is opened to evacuate the expanded chamber. Subsequently, the pedestal is moved up, to the reactor compacted position, and a silanol precursor, such as tris-t-pentoxysilanol, is introduced into the chamber by openingvalve 108. The silanol gas is at a pressure of about 1 Torr and the valve is opened for about 5 to 20 seconds, until the polymerization reaction at the wafer surface results in a silicon dioxide layer of about 100-150 angstroms thickness. The aluminum oxide layer serves to catalyze the reaction that deposits the silicon dioxide. The pedestal is then lowered to expand the reaction chamber, and the purge gas is again introduced to stop the reaction and evacuate the chamber. -
FIG. 4 depicts an alternate embodiment of the reactor apparatus ofFIG. 1 , with the pedestal in the raised position. In this embodiment,pedestal 102 has a diameter larger than the spacing betweenside walls 117.Pedestal 102 has chamferededges 116 that correspond with the lower chamferedcorners 118 ofreactor walls 117. If film builds up on the reactor walls, the space between the pedestal and walls as inFIG. 1 will not become sealed, and the pedestal will not bind to the walls, even if the pedestal contacts chamferedcorners 118. - Accordingly, the present invention provides an improved method and apparatus for a pulsed layer deposition in the fabrication of microelectronic circuits. The variable reactor chamber volume makes the process partially viable for ULSI processing. Additionally, the variable reaction chamber volume reduces the amount of precursors used while enabling high concentrations and fast reaction times to be achieved.
- While the present invention has been particularly described, in conjunction with a specific preferred embodiment, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art in light of the foregoing description. It is therefore contemplated that the appended claims will embrace any such alternatives, modifications and variations as falling within the true scope and spirit of the present invention.
Claims (19)
1. A method of depositing material on a substrate comprising:
providing a reactor with a reaction chamber having a first volume;
contacting a surface of a substrate in the reaction chamber with a first precursor at the first chamber volume to react with and deposit a first layer on the substrate; and
enlarging the reaction chamber to a second, larger volume and removing undeposited first precursor and any excess reaction product to end reaction of the first precursor with the substrate.
2. The method of claim 1 further including:
reducing the reaction chamber to the first chamber volume;
contacting the first layer in the reaction chamber with a second precursor at the first chamber volume to react with and deposit a second layer on the first layer, thereby forming a film; and
enlarging the reaction chamber to the second volume and removing undeposited second precursor and any excess reaction product to end reaction of the second precursor.
3. The method of claim 1 wherein removing undeposited first precursor and any excess reaction product is by purging the reaction chamber at the second volume with a gas.
4. The method of claim 1 wherein removing undeposited first precursor and any excess reaction product is by exposing the reaction chamber at the second volume to a vacuum.
5. The method of claim 1 wherein the reaction chamber includes a pedestal adapted to secure the substrate during the deposition and movable between first and second positions, a first chamber section above the pedestal in the first position defining the first chamber volume, and a second chamber section outside the first chamber section; and wherein the reaction chamber is enlarged to the second, larger volume by moving the pedestal to the second position such that the first and second chamber sections together with the pedestal in the second position define the second chamber volume.
6. The method of claim 1 wherein the second chamber section is on one or more sides of the pedestal.
7. The method of claim 1 wherein the second chamber section is below the pedestal.
8. A method of depositing a film on a substrate comprising:
providing a reactor with a reaction chamber having a first volume;
contacting a surface of a substrate in the reaction chamber with a first precursor at the first chamber volume to react with and deposit a first layer on the substrate;
enlarging the reaction chamber to a second, larger volume and removing undeposited first precursor and any excess reaction product to end reaction of the first precursor with the substrate;
reducing the reaction chamber to the first chamber volume;
contacting the first layer in the reaction chamber with a second precursor at the first chamber volume to react with and deposit a second layer on the first layer, thereby forming a film; and
enlarging the reaction chamber to the second volume and removing undeposited second precursor and any excess reaction product to end reaction of the second precursor.
9. The method of claim 8 wherein the reaction chamber includes a pedestal adapted to secure the substrate during the deposition and movable between first and second positions, a first chamber section above the pedestal in the first position defining the first chamber volume, and a second chamber section outside the first chamber section; and wherein the reaction chamber is enlarged to the second, larger volume by moving the pedestal to the second position such that the first and second chamber sections together with the pedestal in the second position define the second chamber volume.
10. The method of claim 1 wherein the second chamber section is on the side of and below the pedestal.
11. An apparatus for depositing a film on a substrate comprising:
a reactor having a variable volume reaction chamber for reacting one or more precursors with the substrate to deposit a film thereon;
a pedestal in the reaction chamber adapted to secure the substrate during the deposition, the pedestal being movable between first and second positions;
a first chamber section above the pedestal in the first position;
a second chamber section outside the first chamber section,
wherein volume of the reaction chamber may be varied by moving the pedestal between the first position, where the first chamber section together with the pedestal in the first position define a first chamber volume, and the second position, where the first and second chamber sections together with the pedestal in the second position define a second, larger chamber volume.
12. The apparatus of claim 11 wherein the pedestal is movable upwards to the first position and downwards to the second position.
13. The apparatus of claim 11 wherein the second chamber section is on one or more sides of the pedestal.
14. The apparatus of claim 11 wherein the second chamber section is below the pedestal.
15. The apparatus of claim 11 further including a perforated plate above the pedestal in the first chamber section, the perforated plate being adapted to diffuse the precursors.
16. The apparatus of claim 11 further including an environmental control for maintaining the first chamber section at a different temperature than the second chamber section.
17. An apparatus for depositing a film on a substrate comprising:
a reactor having a variable volume reaction chamber for reacting one or more precursors with the substrate to deposit a film thereon;
a pedestal in the reaction chamber adapted to secure the substrate during the deposition, the pedestal being movable between an upper position and a lower position;
a first chamber section above the pedestal in the upper position;
a second chamber section along side or below the first chamber section,
wherein volume of the reaction chamber may be varied by moving the pedestal between the upper position, where the first chamber section together with the pedestal in the first position define a first chamber volume, and the lower position, where the first and second chamber sections together with the pedestal in the lower position define a second, larger chamber volume.
19. The apparatus of claim 11 further including a perforated plate above the pedestal in the first chamber section, the perforated plate being adapted to diffuse the precursors.
20. The apparatus of claim 11 further including an environmental control for maintaining the first chamber section at a different temperature than the second chamber section.