US20100096699A1 - Prevention of plasma induced damage arising from etching of crack stop trenches in multi-layered low-k semiconductor devices - Google Patents
Prevention of plasma induced damage arising from etching of crack stop trenches in multi-layered low-k semiconductor devices Download PDFInfo
- Publication number
- US20100096699A1 US20100096699A1 US12/645,404 US64540409A US2010096699A1 US 20100096699 A1 US20100096699 A1 US 20100096699A1 US 64540409 A US64540409 A US 64540409A US 2010096699 A1 US2010096699 A1 US 2010096699A1
- Authority
- US
- United States
- Prior art keywords
- wafer
- layer
- substrate
- dielectric
- interconnect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method of fabricating a semiconductor device begins by forming a lower interconnection dielectric on a substrate and forming at least one active or passive device in the lower interconnection dielectric. An etch stop layer is formed on the lower interconnection dielectric and an interconnect stack layer is formed on the etch stop layer. At least one interconnect trench structure and at least one crack stop trench are etched in the interconnect stack layer while maintaining electrical isolation between the interconnect structure and the crack stop trench.
Description
- This application is a divisional of U.S. patent application Ser. No. 11/404,738, filed Apr. 14, 2006, entitled “Prevention of Plasma Induced Damage Arising From Etching of Crack Stop Trenches in Multi-Layered Low-K Semiconductor Devices”, which is incorporated in its entirety by reference herein.
- The present invention relates generally to dual damascene interconnections for integrated circuits, and more specifically to a dual damascene interconnection having a low k layer with trenches to prevent cracking.
- The manufacture of integrated circuits in a semiconductor device involves the formation of a sequence of layers that contain metal wiring. Metal interconnects and vias which form horizontal and vertical connections in the device are separated by insulating layers or inter-level dielectric layers (ILDs) to electrically isolate wires from each other and to prevent crosstalk between the metal wiring that can degrade device performance. A popular method of forming an interconnect structure is a dual damascene process in which vias and trenches are filled with metal in the same step to create multi-level, high density metal interconnections needed for advanced high performance integrated circuits. The most frequently used approach is a via first process in which a via is formed in a dielectric layer and then a trench is formed above the via. Recent achievements in dual damascene processing include lowering the resistivity of the metal interconnect by switching from aluminum to copper, decreasing the size of the vias and trenches with improved lithographic materials and processes to improve speed and performance, and reducing the dielectric constant (k) of insulators or ILDs by using so-called low k materials to avoid capacitance coupling between the metal interconnects. The expression “low-k” material has evolved to characterize materials with a dielectric constant less than about 3.9. One class of low-k material that have been explored are organic low-k materials, typically having a dielectric constant of about 2.0 to about 3.8, which may offer promise for use as an ILD.
- One difficulty that arises when the dielectric layers are formed from low-k materials is that the reduced strength of the low-k materials, in combination with thinner layers, frequently results in cracking when such materials are subjected to mechanical and thermal stresses. Typical low-k materials in use have included carbon doped silicon dioxide such as commercially available Black Diamond™ and other materials that tend to be porous, thereby reducing the overall dielectric constant. Porous low-k materials have a drawback in that the porosity tends to weaken the overall strength and hardness of the material making crack initiation and propagation more likely. As the requirement for device density increases, the number of levels in an integrated circuit structure has increased to 4 to 10 or more levels. The increased number of material layers contributes to the buildup of compressive and tensile stresses in the multiple layers, especially when subjected to thermal and mechanical stresses, which frequently do not offset one another. The result is that cracking becomes more likely as the number of layers increase and the process wafer is subjected to externally induced stresses that arise when the wafer is cut into the individual dies.
- One known approach to alleviate these stresses is to provide crack stop trenches that are located at the die edge to prevent cracking of the die. The crack stop trench also prevents the diffusion of moisture into the device and thus it is also sometimes referred to as a moisture block trench or simply a moisture block. The crack stop trenches are generally formed simultaneously with the trenches and vias of the metal interconnects. That is, the same lithographic steps used in forming the interconnects, including patterning, etching of the pattern, removal of the mask, and etching of the interconnect trenches, are generally used to form the crack stop trenches.
- The etching of the trenches is typically performed by reactive ion etching. During this process a plasma is generated that gives rise to currents in the trenches as they are being etched. Unfortunately, the currents that are generated can produce voltages that damage the active or passive devices located in the integrated circuit. This damage, so-called plasma-induced damage, degrades the operational characteristics of the resulting device.
- Accordingly, it would be desirable to provide a method for reducing plasma-induced damage that can arise during formation of single and dual damascene interconnect structures that employ crack stop trenches.
- In accordance with the present invention, a method of fabricating a semiconductor device begins by forming a lower interconnection dielectric on a substrate and forming at least one active or passive device in the lower interconnection dielectric. An etch stop layer is formed on the lower interconnection dielectric and an interconnect stack layer is formed on the etch stop layer. At least one interconnect trench structure and at least one crack stop trench are etched in the interconnect stack layer while maintaining electrical isolation between the interconnect structure and the crack stop trench.
- In accordance with one aspect of the invention at least one electrically isolating region is formed in the lower interconnection dielectric below a location where the crack stop trench is to be etched.
- In accordance with another aspect of the invention, the electrically isolating region comprises a gate dielectric layer.
- In accordance with another aspect of the invention, the etching is a reactive ion etching process.
- In accordance with another aspect of the invention, the substrate is a SOI substrate.
- In accordance with another aspect of the invention, the SOI substrate includes a buried oxide layer that serves as an electrically isolating region that facilitates maintenance of the electrical isolation between the interconnect structure and the crack stop trench during etching.
- In accordance with another aspect of the invention, the crack stop trench is continuous and surrounds the interconnect stack layer.
- In accordance with another aspect of the invention, the interconnect stack layer comprises a low k dielectric material.
- In accordance with another aspect of the invention, the low k dielectric material includes an organosilicon material.
- In accordance with another aspect of the invention, the etch stop layer is formed of at least one of SiC, SiN, and SiCN.
- In accordance with another aspect of the invention, the dielectric material is formed using chemical vapor deposition.
- In accordance with another aspect of the invention, a capping layer is formed on the interconnect stack layer.
- In accordance with another aspect of the invention, the capping layer is formed of at least one of SiO2, SiOF, SiON, SiC, SiN and SiCN.
- In accordance with another aspect of the invention, a semiconductor wafer is provided. The wafer includes a lower interconnection dielectric located on a substrate, at least one active or passive device formed in the lower interconnection dielectric and at least one electrical isolating region formed in the lower interconnection dielectric. An etch stop layer is located over the lower interconnection dielectric and an interconnect stack layer is located over on the etch stop layer. At least one interconnect trench structure is located in the interconnect stack layer at least one crack stop trench is located in the interconnect stack layer over the electrical isolating region.
- In accordance with another aspect of the invention, the crack stop trenches are continuous and extend around a periphery of an individual die area.
-
FIG. 1 shows a plan view of a conventional semiconductor wafer. -
FIG. 2 shows a partial cross-sectional view through semiconductor wafer ofFIG. 1 . -
FIG. 3 shows another partial cross-sectional view through semiconductor wafer ofFIG. 1 to illustrate plasma induced damage that can arise during reactive ion etching. -
FIGS. 4-6 show various partial cross-sectional views through a semiconductor wafer constructed in accordance with the present invention. -
FIGS. 7-13 show the process steps involved in an exemplary process flow used to form a semiconductor wafer in accordance with the present invention. - The methods and structures described herein do not form a complete process for manufacturing semiconductor device structures. The remainder of the process is known to those of ordinary skill in the art and, therefore, only the process steps and structures necessary to understand the present invention are described herein.
- The present invention can be applied to microelectronic devices, such as highly integrated circuit semiconductor devices, processors, micro electromechanical (MEM) devices, optoelectronic devices, and display devices. In particular, the present invention is highly useful for devices requiring high-speed characteristics, such as central processing units (CPUs), digital signal processors (DSPs), combinations of a CPU and a DSP, application specific integrated circuits (ASICs), logic devices, and SRAMs.
- Herein, an opening exposing a lower interconnection is referred to as a via, and a region where interconnections will be formed is referred to as a trench. Hereinafter, the present invention will be described by way of an example of a via-first dual damascene process. However the present invention is also applicable to other dual damascene processes as well.
- As detailed below, plasma-induced damage to active or passive devices incorporated in microelectronic devices can be avoided or substantially reduced by electrically isolating the crack stop trenches from the conductive interconnect structures during the etching process.
-
FIG. 1 shows a plan view of semiconductor wafer 100 in accordance with the present invention, which includesmultiple dies 110. The individual dies, which each contain a distinct integrated circuit, are separated from one another alongscribe lines trenches 120 are formed around the periphery of each die 110 to prevent cracking of the die during the separation process. -
FIG. 2 shows a partial cross-sectional view throughsemiconductor wafer 100. As shown, a lower interconnection dielectric 105 (e.g., SiO2) is provided in which various active and passive devices are formed. For example, agate 125 andgate dielectric 127 of one such active device is shown inFIG. 1 for purposes of illustration. Aninterconnect stack layer 116 is located on top ofsubstrate 118.Stack layer 116 includes multiple layers of dielectric material and interconnecting electrical conductive structures such as the aforementioned trenches and vias. For example,conductive interconnect structures 117 are shown instack layer 116. Also shown inFIG. 2 arecrack stop trenches 120 located at the periphery of the individual dies 110, adjacent to thescribe lines FIG. 1 . The interconnecting electricallyconductive structures 117 are filled with metal (e.g., copper, aluminum, silver, gold) and electrically couple semiconductor devices (not shown) that are formed insubstrate 118. The multiple layers ofinterconnect stack layer 116 are generally formed by a dual damascene process. - As previously mentioned, the crack stop
trenches 120 are generally formed simultaneously withconductive interconnects 117. That is, the same lithographic steps used in forming theconductive interconnects 117, including patterning, etching of the pattern, removal of the mask, and reactive ion etching, are generally used to form the crack stoptrenches 120. - In reactive ion etching, an electric field is applied to a relatively inert molecular gas so that a reactive gas and chemically reactive species are produced. The atoms on a surface portion of the material not covered by a mask are chemically and physically removed by the resulting plasma beam. Material not covered by the mask is removed to a depth that is determined by a variety of factors including the length of time over which the plasma is applied. In this way well-defined features can be transferred from the mask to the material. During the reactive ion etching process, chemically active species such as ions and radicals of the reactive gas generated in the plasma are adsorbed on the surface of the material. The ions and radicals chemically react with the material and a surface reactive layer is generated that has a relatively low bond energy. Cations that are accelerated by the electric field in the plasma impact the surface of the material, and thus the surface reactive layer, which now has a relatively low bond energy, is removed by sputtering and/or evaporation. That is, reactive ion etching simultaneously employs both chemical action and physical action. As a result, reactive ion etching is selective with respect to particular materials.
- One problem that can arise with the use of reactive ion etching is sometimes referred to as RIE lag. RIE lag prevents the achievement of dimensional uniformity after the etching process. RIE lag is believed to occur because etching rates and profiles depend on feature size and pattern density. For instance, one cause of RIE is believed to be aspect ratio dependent etching, which occurs because trench openings with a large aspect ratio etch more slowly than trench openings with a small aspect ratio.
- As is evident from
FIG. 1 , the aspect ratio of crack stops are generally smaller than the aspect ratio of an interconnect formed in the same structure. This is because crack stops are generally defined by lines (which gives rise to a large feature width and hence a small aspect ratio) whereas interconnects are generally defined by relatively small holes or vias (which gives rise to a small feature width and hence a large aspect ratio). Accordingly, because of RIE lag, the etch rate of the crack stop is greater than the etch rate of the interconnect. - The RIE lag between a crack stop and an interconnect may cause process or plasma induced damage by charging the components (e.g., gates) of the active devices formed in the
lower interconnection 105, thereby degrading the electrical properties of the components. This damages the active device, degrades its operating characteristics and shortens its useful life. The mechanism by which RIE lag causes plasma induced damage is illustrated with reference toFIG. 3 , which for simplicity shows asingle crack stop 120 and asingle interconnect 117 adjacent thereto.FIG. 3 shows thecrack stop 120 andconductive interconnect 117 in the process of being etched. The current flow arising from the etch plasma in thecrack stop 120 and theinterconnect 117 is represented by lines designated byreference numerals crack stop 120 is greater than the current that develops through the depth of theconductive interconnect 117. As a result of this differential in current, a voltage develops on thegate dielectric 127. This voltage is the direct cause of the plasma induced damage. - In accordance with the present invention, process or plasma induced damage that arises during reactive ion etching of the trenches for an interconnect and a crack stop is reduced or eliminated by electrically isolating the crack stop.
FIGS. 4 and 5 show a cross-sectional view through one example of a semiconductor wafer constructed in accordance with the present invention. In the figures like elements are denoted by like reference numerals. As shown, an electrically isolatingregion 130 is provided in thelower interconnect 105. The isolatingregion 130 is situated directly below the crack stop 120 so that it makes contact therewith. The electrical isolatingregion 130 prevents the current that arises from etching the crack stop from penetrating across thesubstrate 118 to thegate dielectric 125. In this way the voltage buildup on thegate 125 that causes plasma induced damage is avoided. The RIE process terminates before the electrically isolatingregion 130 itself is etched. - The electrical isolating
region 130 may be any region that has a sufficient dielectric constant to prevent the plasma current from extending into thesubstrate 118 by any significant amount sufficient to cause plasma induced damage. In the example shown inFIGS. 4 and 5 , the electrical isolatingregion 130 is configured as apolysilicon gate 132 with agate dielectric 134. That is, the electrical isolatingregion 130 is largely similar to thegates 125 andgate dielectrics 127 of the active devices formed in thelower interconnection dielectric 105. This simplifies processing of the structure since thegate 132 and gate dielectric 134 can be formed in the same processing steps as thegate 125 andgate dielectric 127 of the active device. Of course, the present invention encompasses the use of any structure formed from any suitable material to serve as the electrical isolatingregion 130 provided that it reduces or eliminates plasma induced damage. -
FIG. 6 shows one alternative embodiment of the invention in which thesubstrate 118 shown inFIGS. 2-5 is replaced with a composite substrate such as a so-called silicon-on-insulator substrate 140. Silicon on-insulator (SOI) substrates or wafers comprise two silicon layers, one of which is thinner than the other, separated by a silicon oxide layer. One method of producing an SOI structure, known by the acronym SIMOX (separation by implanted oxygen) forms a buried oxide layer (BOX) in a semiconductor substrate by implanting oxygen ions into the substrate followed by a high temperature annealing step. The insulating layer provides electrical isolation of devices that are built in the superficial silicon layer. - In
FIG. 6 SOI substrate 140 includes anSi layer 142 having a thickness, for instance, of between about 20-70 angstroms. TheSi layer 142 is formed on a buried oxide (“BOX”)layer 146. Box layers are generally employed as isolation structures to electrically isolate semiconductor devices from one another.BOX layer 146 is formed on the surface of a silicon support substrate orwafer 144. AsFIG. 6 shows, thecrack stop 120 terminates onSi layer 142. In this way thecrack stop 120 is electrically isolated from theinterconnects 117 by theBOX layer 146. - A method of fabricating dual damascene interconnections according to an embodiment of the present invention will now be described with reference to
FIG. 7 through 14. For purposes of illustration only and not as a limitation on the invention, only a single die is shown inFIGS. 7-13 . Of course, more generally, the present invention encompasses wafers that include multiple dies that need to be separated from one another after fabrication. Likewise, only asingle interconnect structure 117 comprising a single trench and via are shown. More generally, of course, each die may include multiple interconnect structures each having multiple trenches and vias that may constitute upwards of, e.g., 4-10 interconnect levels. - As shown in
FIG. 7 , the process begins with the provision of asubstrate 300. Thesubstrate 300 may be, for example, a silicon substrate, a silicon on insulator (SOI) substrate, a gallium arsenic substrate, a silicon germanium substrate, a ceramic substrate, a quartz substrate, or a glass substrate for display. Various active devices and passive devices may be formed on thesubstrate 300. For instance, a lower inter-level dielectric layer (ILD) 305 is formed on thesubstrate 300 and includes agate 310 and gate dielectric 312 formed on thesubstrate 300. An electrical isolatingregion 350 is also formed on the substrate. In this particular example, the electrical isolatingregion 350 includes agate 354 and agate dielectric 352 that is similar togate 310 andgate dielectric 312. - Referring to
FIG. 8 , anetch stop layer 320, a low-k ILD 330, and acapping layer 340 are sequentially stacked on the surface of thesubstrate 300, and aphotoresist pattern 345 is formed on thecapping layer 340 to define a via located over thegate 310 and a crack stop over the electrical isolatingregion 350. - The
etch stop layer 320 is formed to prevent electrical properties of thelower interconnection 310 from being damaged during a subsequent etch process for forming a via and crack stop. Accordingly, theetch stop layer 320 is formed of a material having a high etch selectivity with respect to theILD 330 formed thereon. Preferably, theetch stop layer 320 is formed of SiC, SiN, or SiCN, having a dielectric constant of 4 to 5. Theetch stop layer 320 is as thin as possible in consideration of the dielectric constant of the entire ILD, but thick enough to properly function as an etch stop layer. - The
ILD 330 is formed of a hybrid low-k dielectric material, which has advantages of organic and inorganic materials. That is, theILD 330 is formed of a hybrid low-k dielectric material having low-k characteristics, which can be formed using a conventional apparatus and process, and which is thermally stable. TheILD 330 has a dielectric constant of e.g., 3.5 or less, to prevent an RC delay between thelower interconnection 310 and dual damascene interconnections and minimize cross talk and power consumption. For example, theILD 330 may be formed from a low-k organosilicon material such as Black Diamond™, Silk™, CORAL™, or a similar material. TheILD 330 can be formed using chemical vapor deposition (CVD), and more specifically, plasma-enhanced CVD (PECVD). TheILD 330 may be also formed from low k materials such as spin-on organics and organo silicates. TheILD 330 is formed to a thickness of about 3,000 angstroms to 20,000 angstroms or other appropriate thicknesses determined by those skilled in the art. - The
capping layer 340 prevents theILD 330 from being damaged when dual damascene interconnections are planarized using chemical mechanical polishing (CMP). Thus, thecapping layer 340 may be formed of SiO2, SiOF, SiON, SiC, SiN, or SiCN. Thecapping layer 340 may also function as an anti-reflection layer (ARL) in a subsequent photolithographic process for forming a trench. In this case thecapping layer 340 is more preferably formed of SiO2, SiON, SiC, or SiCN. - The
photoresist pattern 345 is formed by forming a layer of a photoresist and then performing exposure and developing processes using a photo mask to define a via and crack stop. Referring toFIG. 9 , theILD 330 is anisotropically etched (347) using thephotoresist pattern 345 as an etch mask to form via 315 and crackstop 360. TheILD 330 can be etched, for example, using a reactive ion beam etch (RIE) process, which uses a mixture of a main etch gas (e.g., CxFy and CxHyFz), an inert gas (e.g. Ar gas), and possibly at least one of O2, N2, and COx. Here, the RIE conditions are adjusted such that only theILD 330 is selectively etched and theetch stop layer 320 is not etched. Because of the provision of electrical isolatingregion 350, plasma induced damage togate 310 is substantially reduced or eliminated. - Referring to
FIG. 10 , thephotoresist pattern 345 is removed using a plasma etch, for example. Referring toFIG. 11 , atrench photoresist pattern 385 is formed, followed by formation of aninterconnect trench 390 inFIG. 12 . A trench is also defined in thecrack stop 360. Thecapping layer 340 is etched using thephotoresist pattern 385 as an etch mask, and then theILD 330 is etched to a predetermined depth to form the trenches. The resulting structure, shown inFIG. 12 , defines a dualdamascene interconnection structure 395, which includes the via 315 and thetrench 390 as well ascrack stop 360. - Referring to
FIG. 13 , theetch stop layer 320 exposed in the via 315 and crackstop 360 is etched until thelower interconnection 310 is exposed, thereby completing the dualdamascene interconnection region 395. Theetch stop layer 320 is etched so that thelower interconnection 310 is not affected and only theetch stop layer 320 is selectively removed. Abarrier layer 360 is formed on the dualdamascene interconnection region 395 and the crack stop 360 to prevent the subsequently formed conductive layer from diffusing intoILD 330. Thebarrier layer 360 is generally formed from a conventional material such as tantalum, tantalum nitride, titanium, titanium silicide or zirconium. After formation of thebarrier layer 360 the copper conductive layer is formed on the barrier layer by an electroplating process. Thebulk copper layer 365 is formed on the dualdamascene interconnection region 395 by electroplating and then planarized, thereby forming a dual damascene interconnection. - Although various embodiments are specifically illustrated and described herein, it will be appreciated that modifications and variations of the present invention are covered by the above teachings and are within the purview of the appended claims without departing from the spirit and intended scope of the invention. For example, those of ordinary skill in the art will recognize that the via-first dual damascene process described with reference to
FIGS. 7 through 13 can be applied to a trench-first dual damascene process.
Claims (17)
1. A semiconductor wafer comprising:
a lower interconnection dielectric located on a substrate;
at least one active or passive device formed in the lower interconnection dielectric;
at least one electrical isolating region formed in the lower interconnection dielectric;
an etch stop layer located over the lower interconnection dielectric;
an interconnect stack layer located over the etch stop layer;
at least one interconnect trench structure located in the interconnect stack layer; and
at least one crack stop trench located in the interconnect stack layer over the electrical isolating region,
wherein the at least one crack stop trench is continuous and extends around a periphery of an individual die area.
2. The wafer of claim 1 , wherein the electrically isolating region comprises a gate dielectric layer.
3. The wafer of claim 1 , wherein the substrate is a SOI substrate.
4. The wafer of claim 3 , wherein the SOI substrate includes a buried oxide layer that serves as an electrically isolating region that facilitates maintenance of the electrical isolation between the interconnect structure and the crack stop trench during etching.
5. The wafer of claim 1 , wherein the interconnect stack layer comprises a low k dielectric material.
6. The wafer of claim 5 , wherein the low k dielectric material includes an organosilicon material.
7. The wafer of claim 1 , wherein the etch stop layer is formed of at least one of SiC, SiN, and SiCN.
8. The wafer of claim 5 , wherein the dielectric material is formed using chemical vapor deposition.
9. The wafer of claim 1 , further comprising a capping layer on the interconnect stack layer.
10. The wafer of claim 9 , wherein the capping layer is formed of at least one of SiO2, SiOF, SiON, SiC, SiN and SiCN.
11. The wafer of claim 1 , wherein said at least one electrical isolating region comprises a polysilicon gate and a gate dielectric.
12. The wafer of claim 1 , wherein the substrate comprises a composite substrate.
13. The wafer of claim 12 , wherein the composite substrate comprises two silicon layers, one thinner than the other, separated by a silicon oxide layer.
14. The wafer of claim 1 , wherein said at least one crack stop trench includes a barrier layer.
15. The wafer of claim 1 , wherein said barrier layer comprises tantalum, tantalum nitride, titanium, titanium silicide or zirconium.
16. The wafer of claim 1 , wherein a copper conductive layer is formed on said barrier layer.
17. The wafer of claim 1 , wherein the substrate comprises a gallium arsenic substrate, a silicon germanium substrate, a ceramic substrate, a quartz substrate, or a glass substrate.