US20090218645A1 - multi-state spin-torque transfer magnetic random access memory - Google Patents
multi-state spin-torque transfer magnetic random access memory Download PDFInfo
- Publication number
- US20090218645A1 US20090218645A1 US12/397,255 US39725509A US2009218645A1 US 20090218645 A1 US20090218645 A1 US 20090218645A1 US 39725509 A US39725509 A US 39725509A US 2009218645 A1 US2009218645 A1 US 2009218645A1
- Authority
- US
- United States
- Prior art keywords
- layer
- state
- sttmram
- mtj
- sub
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application is a continuation-in-part of U.S. patent application Ser. No. 11/678,515 filed on Feb. 23, 2007, by Rajiv Yadav Ranjan and entitled “A High Capacity Low Cost Multi-State Magnetic memory” and U.S. patent application Ser. No. 11/866,830, filed on Oct. 3, 2007, by Rajiv Yadav Rajiv and entitled “An Improved High Capacity Low Cost Multi-State Magnetic Memory” and U.S. application Ser. No. 11/860,467, filed on Sep. 24, 2007, by Rajiv Yadav Ranjan and entitled “Low Cost Multi-State Magnetic Memory” and a continuation-in-part of U.S. patent application Ser. No. 11/674,124 entitled “Non-Uniform Switching Based Non-Volatile Magnetic Base Memory”, filed on Feb. 12, 2007, the disclosure of which is incorporated herein by reference, as though set forth in full.
- 1. Field of the Invention
- The present invention relates generally to non-volatile magnetic memory and particularly to multi-state magnetic memory having stacked magnetic tunnel junction (MTJ) with at least one MTJ having a storage layer with a magnetization direction being substantially perpendicular to the plane of the wafer (or substrate).
- 2. Description of the Prior Art
- It has become clear that non-volatile memories, such as non-volatile random access memories (NVRAMs) are finding increasingly new applications, and that their notoriety would not only continue but that it would explode due to the increasing demands in mobile devices and other applications. It is also believed that current volatile DRAM will be replaced by the current-switching version or spin-torque transfer magnetic random access memory (STTMRAM), in the coming future.
- It is really important that in order for STTMRAM to gain broad acceptance, the cost of the memory and hence the cell size to be smaller and scalable to smaller feature size such as below 65 nm.
- One of the ways to achieve higher density is by storing more than one bit of digital information in a memory cell of magnetic memory designs. Such memory cells are commonly referred to as multi-state (or multi-level) cells (MLCs). Current MLC designs include magnetic memory with a storage layer with a magnetization direction that is in-plane or parallel to the plane of the substrate or wafer. Such MLCs suffer from low density and therefore higher costs.
- Stated differently, current STTMRAM designs have storage layers with a magnetization direction that is parallel to the plane of the substrate. One of the key challenges for such type of designs using in-plane magnetization is that they cannot be scaled to lower feature sizes such as below 65 nm. This is primarily because as the feature size reduces, the reduced memory bit size (for example: for 90 nm, the memory bit size is 90 nm×180 nm, but for 45 nm this would be 45 nm×90 nm) becomes thermally unstable due to the reduction in the volume. The Perpendicular STTMRAM enables lower switching current (therefore lower program current), higher thermal stability and higher density.
- Moreover, perpendicular STTMRAM does not require in-plane elongated memory bit like in the case of in-plane STTMRAM, mentioned above. In-plane circular shape or square shape is typically preferred for perpendicular STTMRAM over an elongated shape because in the latter, features pose large manufacturing challenges especially at lower lithography geometry, such as below 90 nm. On the other hand, circular shape memory bit shapes allow for lower lithography and higher capacity memory, making the perpendicular STTMRAM a preferred choice for future applications. It should be pointed out that the perpendicular STTMRAM can utilize high anisotropy magnetic alloys as compared to the STTMRAM having in-plane magnetization, leading to higher thermal stability and thereby enabling scalability down to below 30 nm.
- What is needed is a multi-state current-switching version or spin-torque magnetic random access memory (STTMRAM) having stacked magnetic tunnel junctions (MTJs).
- To overcome the limitations in the prior art described above, and to overcome other limitations that will become apparent upon reading and understanding the present specification, the present invention discloses a method and a corresponding structure for a multi-state magnetic storage memory device that is based on current-induced-magnetization-switching having reduced switching current with high thermal stability in the magnetic memory.
- Briefly, an embodiment of the present invention includes a multi-state spin-torque transfer magnetic random access memory (STTMRAM) is formed on a film and includes a first magnetic tunneling junctions (MTJ) having a first fixed layer, a first sub-magnetic tunnel junction (sub-MTJ) layer and a first free layer. The first fixed layer and first free layer each have a first magnetic anisotropy. The STTMRAM further includes a non-magnetic spacing layer formed on top of the first MTJ layer and a second MTJ formed on top of the non-magnetic spacing layer. The second MTJ has a second fixed layer, a second sub-MTJ layer and a second free layer. The second fixed and second free layers each have a second magnetic anisotropy, wherein at least one of the first or second magnetic anisotropy is perpendicular to the plane of the film.
- These and other objects and advantages of the present invention will no doubt become apparent to those skilled in the art after having read the following detailed description of the preferred embodiments illustrated in the several figures of the drawing.
-
FIG. 1 shows relevant layers of a multi-state current-switchingmagnetic memory element 100 are shown, in accordance with an embodiment of the present invention. -
FIG. 2 shows various states of thememory element 100. -
FIG. 3 shows a graph of the level of resistance (R) of each of thelayers memory element 100. -
FIG. 4 shows agraph 250 of the tunneling magneto resistance (TMR), shown in the y-axis, vs. the resistance area (RA).FIG. 5 shows. -
FIG. 5 shows relevant layers of a multi-state current-switchingmagnetic memory element 600 are shown, in accordance with another embodiment of the present invention. -
FIG. 6 shows relevant layers of a multi-state current-switchingmagnetic memory element 700, in accordance with yet another embodiment of the present invention. -
FIG. 7 shows relevant layers of a multi-state current-switchingmagnetic memory element 800, in accordance with still another embodiment of the present invention. -
FIG. 8 shows a program/erase circuit for programming and/or erasing the memory elements of the various embodiments of the present invention. -
FIG. 9 shows a read circuit for reading the memory elements of the various embodiments of the present invention. -
FIG. 10 shows relevant layers of multi-state STTMRAM 1100, in accordance with an embodiment of the present invention. -
FIG. 11 shows relevant layers of multi-state STTMRAM 1153, in accordance with an embodiment of the present invention. -
FIG. 12 shows relevant layers of multi-state STTMRAM 1155, in accordance with an embodiment of the present invention. -
FIG. 13 shows relevant layers of multi-state STTMRAM 1160, in accordance with an embodiment of the present invention. -
FIG. 14 shows relevant layers of multi-state STTMRAM 1164, in accordance with an embodiment of the present invention. -
FIG. 15 shows relevant layers of multi-state STTMRAM 1166, in accordance with an embodiment of the present invention. -
FIG. 16 shows relevant layers of multi-state STTMRAM 1170, in accordance with an embodiment of the present invention. -
FIG. 17 shows relevant layers of multi-state STTMRAM 1180, in accordance with an embodiment of the present invention. -
FIG. 18 shows relevant layers of multi-state STTMRAM 1192, in accordance with an embodiment of the present invention. -
FIG. 19 shows relevant layers of multi-state STTMRAM 1200, in accordance with an embodiment of the present invention. -
FIG. 20 shows relevant layers of multi-state STTMRAM 1300, in accordance with an embodiment of the present invention. -
FIG. 21 shows relevant layers of multi-state STTMRAM 1400, in accordance with an embodiment of the present invention. -
FIG. 22 shows relevant layers of multi-state STTMRAM 1500, in accordance with an embodiment of the present invention. -
FIG. 23 shows relevant layers of multi-state STTMRAM 1600, in accordance with an embodiment of the present invention. -
FIG. 24 shows relevant layers of multi-state STTMRAM 1700, in accordance with an embodiment of the present invention. -
FIG. 25 shows relevant layers of multi-state STTMRAM 1800, in accordance with an embodiment of the present invention. -
FIG. 26 shows a flow chart of the steps performed, during a write or program operation, to write/program the multi-state STTMRAM, in accordance with an embodiment of the present invention. -
FIG. 27( a) shows top-down or in-plane view and side-view of shapes that any of the STTMRAMs 1100, 1153, 1155, 1160, 1164, 1166 or 1700 can have when their free and fixed layers have perpendicular magnetic orientation. -
FIG. 27( b) shows top-down or in-plane view and side-view of shapes that any of theSTTMRAMs - Table 1 shows certain exemplary characteristics of the embodiments of
FIGS. 1 , 5 and 6. - Table 2 shows certain exemplary characteristics of the embodiment of
FIG. 7 . - In the following description of the embodiments, reference is made to the accompanying drawings that form a part hereof, and in which is shown by way of illustration of the specific embodiments in which the invention may be practiced. It is to be understood that other embodiments may be utilized because structural changes may be made without departing from the scope of the present invention.
- In an embodiment of the present invention, a multi-state magnetic memory cell is disclosed. In one embodiment of the present invention, a stack of magnetic tunnel junction (MTJ) is formed, each MTJ being formed of at least three layers, a barrier layer formed between a fixed layer and a free layer, each MTJ being separated from another by a conductive layer, the stack forming a multi-state magnetic memory cell for storing at least two bits of digital information.
- Referring now to
FIG. 1 , relevant layers of a multi-state current-switching (or spin-torque)magnetic memory element 100 are shown, in accordance with an embodiment of the present invention. Thememory element 100 is shown to include abottom electrode 122 on top of which is shown formed a pinninglayer 120 on top of which is shown formed a fixedlayer 118, on top of which is shown formed abarrier layer 116, on top of which is formed afree layer 114, on top of which is shown formed anon-magnetic layer 112, on top of which is shown formed afree layer 110, on top of which is shown formed abarrier layer 108, on top of which is shown formed a fixedlayer 106, on top of which is shown formed a pinninglayer 104, on top of which is shown formed atop electrode 102. Thetop electrode 102 and thebottom electrode 122 are each made of Tantalum (Ta) in an exemplary embodiment although other suitable materials are contemplated. Thelayers MTJ 126 separated by thelayer 112 from anMTJ 124, which is formed from thelayers MTJ FIG. 1 , other number of MTJs may be stacked for storing additional bits of information. - In
FIG. 1 , theMTJ 126 is for storing a bit of information or two states, ‘1’ and ‘0’, while theMTJ 124 is for storing another bit of information and since each bit represents two binary states, i.e. ‘1’ and ‘0’, two bits represent four binary states, generally represented as ‘00’, ‘01’, ‘10’, ‘11’, or 0, 1, 2 and 3 in decimal notation, respectively. Thememory element 100 advantageously stores two bits of information thereby decreasing the real estate dedicated for memory and further increases system performance. This is particularly attractive for embedded memory applications. Additionally, manufacturing is made easier and less costly and scalability is realized. - In
FIG. 1 , the barrier layers of each of the MTJs, such as thelayer 116 acts as a filter for electrons with different spins giving rise to different amounts of tunneling current for electrons with different spins thereby causing two unique resistance values associated with each MTJ for two different orientations of the free layer. In the case where additional MTJs are employed, each MTJ similarly has associated therewith, a unique resistance value. - In one embodiment of the present invention, the thickness of the
layers MTJs - Examples of materials used to form each of the layers of the
memory element 100 will now be presented. It should be noted that these materials are merely examples and other types of materials may be employed. Thelayers layers 106 and [120] 118 are typically formed substantially of a magnetic material. Examples of such magnetic material include CoFeB or CoFe/Ru/CoFeB. Thelayers layer 112 is a non-magnetic layer made substantially of, for example, NiNb, NiP, NiV or CuZr. Thelayer 112 serves to insulate the two MTJs 124 and 126 from one another. In an embodiment employing more than two MTJs, another layer, such as thelayer 112 would be formed on top of thelayer 104 or on the bottom of thelayer 120. Thelayers layers top electrode 102 and thebottom electrode 122 are each made of tantalum (Ta), in one embodiment of the present invention, however, other types of conductive material may be employed. - The
layers layer 104 helps to pin the magnetic moment of thelayer 106. Similarly, the magnetic moment of thelayer 120 serves to pin the magnetic moment of thelayer 118. The magnetic moment of each of thelayers - Other choices of material for the
layers layers layer 112 is a non-magnetic layer which is substantially amorphous made of, for example, Nickel niobium (NiNb), Nickel phosphorous (NiP), Nickel vanadium (NiV), Nickel borom (NiB) or copper-zirconium (CuZr). It should be noted that the composition of these alloys is chosen in such a way that the resulting alloy becomes substantially amorphous, for example, for nickel niobium (NiNb), the typical Nb content is maintained between 30 to 70 atomic percent and for nickel phosphorous (NiP) the phosphorous (P) content is maintained between 12 and 30 atomic percent. Thelayer 112 serves to isolate the two MTJs 124 and 126 from one another. In an embodiment of the present invention, which employs more than two MTJs, another layer, such as thelayer 112 would be formed on top of thelayer 104 or on the bottom of thelayer 120. Thelayers layers - The
layers layer 104 helps to pin the magnetic moment of thelayer 106. Similarly, the magnetic moment of thelayer 120 serves to pin the magnetic moment of thelayer 118. The magnetic moment of each of thelayers memory element 100 under the application of a substantially uni-axial magnetic field of over 5 kilo-Oersteds and a temperature of over 350 degree centigrade for typically 2 hours. This annealing process also serves to re-crystallize thelayers free layers - Typical thicknesses for each of the layers of the
memory element 100 are now presented. However, these sizes are merely examples, as other thicknesses are anticipated. A typical thickness of each of thetop electrode 102 and thebottom electrode 122 is 30 to 200 nm. While a preferred thickness is typically 50 nm, the actual thickness choice may depend on the requirements from the metallization process. Thelayers layers layers free layers example layer 116 can be 1.5 to 2.5 nm thick while thesecond barrier layer 108 may be 0.8 to 1.2 nm thick, and vice-versa. Additionally, the thickness and the amounts of oxide in the free-layers non-magnetic layer 112 is typically 2 to 50 nm thick with a preferred range being 2 to 10 nm. It should be pointed out that while the [most] preferred material choice of thenon-magnetic isolation layer 112 consists of amorphous non-magnetic alloys, a crystalline non-magnetic alloy may also work. - During manufacturing, the layers of the
memory element 100 are formed in the manner described hereinabove. Additionally, an annealing process, which is well known, is performed heating thememory element 100 in the presence of a magnetic field after which channels are formed in each of thelayers layers layers layers - During operation, current is applied, in a perpendicular direction relative to the plane of the paper of
FIG. 1 , either from a direction indicated by thearrow 128 or a direction indicated by thearrow 130. When current is applied, depending on the level of current, the magnetic moment of thelayers MTJs MTJ 124 is approximately 1:1.3 to 1:1.5 while the aspect ratio for theMTJ 126 is approximately 1:2 to 1:2.5. Therefore, the switching current for theMTJ 126 is 3-5 times higher than that of theMTJ 124, in the foregoing embodiment. At high current levels both MTJs switch magnetic orientation, while at low current levels only theMTJ 124 having the smaller aspect ratio switches. - The state of the magnetic moment of each of the layers of the MTJ defines the state of the
memory element 100. As thelayers layer 118 defines one state, thelayer 114 defines another state, thelayer 110 defines yet another state and thelayer 106 defines still another state. For the sake of understanding, the states of each of thelayers states -
FIG. 2 shows various states of thememory element 100. Due to the use of two MTJs, four different states or two bits may be stored, therefore, the states 1-4 are shown. At each state, the directions of the arrows indicate the direction of the magnetic moments of free layers and pinning layers. The direction of thearrow 200 shows the direction of high current applied to thememory element 100 and in this case, the state of thememory element 100 is at an all ‘1’s or all ‘0’s state. The direction of thearrow 202 shows the direction of low current applied to thememory element 100 when atstate 1. The direction of thearrow 204 shows the direction of high current applied to thememory element 100 when the latter is atstate 2 and the direction of thearrow 206 shows the direction of low current applied to thememory element 100 when atstate 3. -
FIG. 3 shows a graph of the level of resistance (R) of each of thelayers memory element 100. Thus, at, for example, at 208, thememory element 100 has taken on the state 1 (corresponding to 202 onFIG. 2 ), at 210, thememory element 100 has taken on the state 2 (corresponding to 204 onFIG. 2 ), at 212, thememory element 100 has taken on the state 3 (corresponding to 206 onFIG. 2 ), and at 214, thememory element 100 has taken on the state 4 (corresponding to 200 onFIG. 2 ). The level of resistance for each of these states is indicated in Table 1, at a column labeled “Total R”. For example, atstate 1, the R, inFIG. 3 is indicated as being 3 kilo ohms (K Ohms) by Table 1. Atstate 2, the R, inFIG. 3 , is indicated as being 4 K Ohms and so on. The values used for resistance serve as examples only such that other values may be employed without departing from the scope and spirit of the present invention. - It should be noted that different aspect ratio or anisotropy associated with the
different MTJs memory element 100. In other embodiments, some of which will be shortly presented and discussed, the size of the barrier layers of the MTJs are changed to effectuate different resistances. In yet other embodiments, the size of the MTJs are changed to the same. -
FIG. 4 shows agraph 250 of the tunneling magneto resistance (TMR), shown in the y-axis, vs. the resistance area (RA). The TMR is defined as: -
TMR=(Rh−Rl)/Rl Eq. (1) - Wherein Rh is resistance at a high state and Rl is resistance at a low state.
- The
graph 250 ofFIG. 4 serves merely as an example to convey the difference in TMR or percentage increase as the RA increases. For instance, at an RA of 2 ohm-micro-meters squared, the TMR is 100% while at a RA of 10, the TMR is 150% where the thickness of the barrier layer of the MTJ is between 14-24 Angstroms. -
FIG. 5 shows relevant layers of a multi-state current-switchingmagnetic memory element 600 are shown, in accordance with another embodiment of the present invention. Thememory element 600 is shown to include abottom electrode 122 on top of which is shown formed a pinninglayer 120 on top of which is shown formed a fixedlayer 118, on top of which is shown formed abarrier layer 116, on top of which is formed afree layer 114, on top of which is shown formed anon-magnetic layer 112, as that shown inFIG. 1 . As previously indicated, relative toFIG. 1 , theMTJ 126 comprises thelayers FIG. 5 , theMTJ 612, which is made of afree layer 602, abarrier layer 604 and a fixedlayer 606, is smaller, in its planar dimension, than theMTJ 126 ofFIG. 1 , which causes theMTJ 612 to have a different resistance than that of theMTJ 126. - In
FIG. 5 , thefree layer 602 is shown to be formed on top of thelayer 112 and on top of thelayer 602 is shown formed thelayer 604, on top of which is shown formed thelayer 606, on top of which is shown formed apining layer 608, atop electrode 610. TheMTJs layer 112. TheMTJs FIG. 5 , other number of MTJs may be stacked for storing additional bits of information. - The difference in the planar dimension of the
MTJs 612 to that of theMTJ 126 is approximately 1 to 10 and typically 1 to 3, in one embodiment of the present invention. The material for each of the layers of thememory element 600 may be the same as that of counterpart layers of thememory element 100. For example, thelayer 602 is made of the same material as that of thelayer 110 and thelayer 604 is made of the same material as that of thelayer 108 and thelayer 606 is made of the same material as thelayer 106 and thelayer 608 is made of the same material as thelayer 104. Thetop electrodes MTJ 612 may be larger, in size, in the same planar dimension, than theMTJ 126. - The operation of the embodiment of the embodiment of
FIG. 5 is the same as that ofFIG. 1 . -
FIG. 6 shows relevant layers of a multi-state current-switchingmagnetic memory element 700, in accordance with yet another embodiment of the present invention. Thememory element 700 to include abottom electrode 122 on top of which is shown formed a pinninglayer 120 on top of which is shown formed a fixedlayer 118, on top of which is shown formed abarrier layer 116, on top of which is formed afree layer 114, on top of which is shown formed anon-magnetic layer 112, as that shown inFIGS. 1 and 6 . As previously indicated, relative toFIGS. 1 and 6 , theMTJ 126 comprises thelayers FIG. 6 , theMTJ 714, which is shown to comprise afree layer 710, abarrier layer 708 and a fixedlayer 706, is shown to be smaller in its planar dimension than theMTJ 126 causing theMTJ 714 to have a different resistance than that of theMTJ 126. - The
MTJs layers layer 704 serves to pin thelayer 706 while thelayer 702 serves to isolate theMTJ 126 and is an amorphous only to thelayer 114. Thelayer 702, in one embodiment of the present invention, is made of two non-magnetic layers, such as Ta and/or an amorphous alloy, the same as Nickel-niobium (NiNb) or nickel-phosphorus (NiP). TheMTJs FIG. 5 , other number of MTJs may be stacked for storing additional bits of information. - The difference in the planar dimension of the
MTJs 714 to that of theMTJ 126 is 1 to 10, and typically 1 to 3 in one embodiment of the present invention. The material for each of the layers of thememory element 700 may be the same as the counterpart layers of thememory element 100 or that of thememory element 600. For example, thelayer 710 is made of the same material as that of thelayer 110 and thelayer 708 is made of the same material as that of thelayer 108 and thelayer 706 is made of the same material as thelayer 106 and thelayer 704 is made of the same material as thelayer 104. Thetop electrodes MTJ 714 may be larger in size in the same planar dimension, than theMTJ 126. -
FIG. 7 shows relevant layers of a multi-state current-switchingmagnetic memory element 800, in accordance with still another embodiment of the present invention. InFIG. 7 , thememory element 800 is shown to include abottom electrode 802 on top of which is shown formed a pinninglayer 804 on top of which is shown formed two fixed layers on either side thereof. That is, a fixedlayer 806 is shown formed on one side of thelayer 804 and a fixedlayer 808 is shown formed on an opposite side of thelayer 804. - In
FIG. 7 , two MTJs are shown formed on either side or top of thelayer 804. Namely, anMTJ 820 is shown formed on one side of thelayer 804 and anotherMTJ 822 is shown formed on an opposite side of thelayer 804. TheMTJ 820 includes the fixedlayer 806, which is formed on top of thelayer 804 and thebarrier layer 810 shown formed on top of thelayer 806 and thefree layer 812 shown formed on top of thelayer 810. TheMTJ 822 is shown to include the fixedlayer 808, which is formed on top of thelayer 804 and thebarrier layer 814, which is shown formed on top of thelayer 808 and thefree layer 816, which is shown formed on top of thelayer 814. Atop electrode 818 is shown formed on top of theMTJs layers top electrode 818 is typically made of two layers, such as Ta and a conductive, non-magnetic material. - In forming the
memory element 800, thelayer 804 is formed on top of the bottom electrode and the layers of theMTJs layer 804 and on top of theMTJs top electrode 818. The layers of theMTJs layer 804 and atrench 824, which is basically an empty space or hole is formed, prior to depositing thetop electrode 818, by etching through the layers of theMTJs MTJs MTJs MTJs - In one embodiment of the present invention, the
trench 824 is filled with a dielectric material, such as silicon dioxide (SiO2) or silicon nitride (SiNx) to enhance stability. - After etching, the
top electrode 818 is deposited or formed on top of theMTJs FIG. 7 , as the embodiments ofFIGS. 6 , 5, and 1 store two bits of information, with [on]one bit stored in each MTJ. Thus, theMTJ 820 is for storing one bit and theMTJ 822 is for storing another bit of information. However, more bits may be stored by adding MTJs. InFIG. 7 , additional MTJs may be added on top of thelayer 804 or theMTJs FIG. 7 , additional trenches are formed between the MTJs, such as thetrench 824. - Table 2 shows certain exemplary characteristics of the embodiment of
FIG. 7 . It should be noted that similarly, Table 1 shows certain exemplary characteristics of the embodiments ofFIGS. 1 , 5 and 6. - For example, in Table 2, under the “Total R” column, there is shown the resistance at each state of the
memory element 800, such as thestate 1, thestate 2, thestate 3 and the state 4. As previously noted, each state represents a binary value such that four states, and represented by two bits are stored. The programming current, in micro amps, i.e. the current needed to program thememory element 800 to a given state, is indicated in the last column of Table 2, under the label “Prog I”. - In an alternative embodiment of the present invention, a non-uniform switching based non-volatile magnetic memory element, such as the non-uniform switching based non-volatile
magnetic memory element 100 disclosed in U.S. patent application Ser. No. 11/674,124 entitled “Non-Uniform Switching Based Non-Volatile Magnetic Base Memory”, filed on Feb. 12, 2007, may be employed to replace the MTJs of the various embodiments shown and discussed herein. For example, theMTJ 124 or theMTJ 126 may be replaced with a non-uniform switching based non-volatile magnetic memory element. Other MTJs discussed herein may also be replaced with non-uniform switching based non-volatile magnetic memory element. This advantageously further reduces the requisite switching current to enhance system performance. -
FIG. 8 shows a program/erase circuit for programming and/or erasing the memory elements of the various embodiments of the present invention. InFIG. 8 , acurrent source 902 is shown coupled to acurrent mirror circuit 904, which is shown coupled to theswitch 906, which is, in turn, shown coupled to theswitch 968, which is shown coupled to the multi-state current-switchingmagnetic memory cell 914, which is shown coupled to theswitch 916. Further shown inFIG. 8 , acurrent source 918 is shown coupled to acurrent mirror circuit 920 and further shown coupled to Vcc on an opposite end thereto. Thecircuit 920 is further shown coupled to theswitch 999. - The
circuit 904 is shown to include a P-type transistor 922, a P-type transistor 924 and a P-type transistor 926. The source of each of thetransistors transistor 922 is shown coupled to thecurrent source 902 and the opposite side of thecurrent source 902 is shown coupled to ground. The drain of thetransistor 922 is shown coupled to its gate as well as to the gate of thetransistor 924 and the gate of thetransistor 926. The drains of thetransistors switch 906. Thememory cell 914 is shown to include anMTJ 910, anMTJ 912 and anaccess transistor 940. TheMTJ 912 is shown coupled in series to theMTJ 912, which is shown coupled to the drain of thetransistor 940. The gate of thetransistor 940 is shown coupled to theword line 942. Theword line 942 selects a memory cell. The source of thetransistor 940 is shown coupled to theswitch 916. - While
memory cell 914 is shown to include two MTJs coupled in series, it is contemplated that thememory cell 914 can include more than two MTJs and that which would be coupled together in series. In this case, each MTJ may have a different switching current associated therewith. - The
circuit 920 is shown to include an N-type transistor 928, an N-type transistor 930 and an N-type transistor 932. The drains of thetransistors transistor 932 is coupled to thecurrent source 918 and is further coupled to the drain of thetransistor 932 and is further coupled to the gate of thetransistor 930 as well as to the gate of thetransistor 928. The drain of thetransistors switch 999. - Each of the
switches switches - The
MTJs FIGS. 1 and 6 . In an alternative embodiment, theMTJs FIG. 7 . EachMTJ - The size of the
transistor 926 is greater than the size of thetransistors transistor 928 is greater than the size of thetransistors - In operation, to program the
memory cell 914 to astate 1, a current of level of 50 micro Amps is applied by thecurrent source 902 to thecircuit 904, which is amplified to 4× the current level or 200 microAmps, as shown in Table 1 because thetransistor 926 is able to drive this level of current. This causes theswitch 906 to switch to the state indicated at 944. The switch 908 is set to ‘program’ state, as is theswitch 916, which causes the 200 micro amp current to flow through theMTJs transistor 940 is selected by raising the voltage on theword line 942. This results in programming ofstate 1. The magnetic moment of the free layers of theMTJs memory cell 914, as indicated in Table 1. - In programming the
memory cell 914 to astate 2, a current of level of 50 micro Amps is applied by thecurrent source 918 to thecircuit 920, which is the same current level as that generated by thecircuit 920. The current level forstate 2 is indicated in Table 1. Theswitch 999 is caused to be switched to the state indicated at 948. Theswitches 908 and 916 are both set to ‘erase’ state, which causes the 50 micro amp current to flow through theMTJs transistor 940 is selected by raising the voltage on theword line 942. This results in programming ofstate 2. The magnetic moment of the free layer of theMTJ 910 is caused to be switched to an anti-parallel state or a state that is in opposite to being aligned with its respective fixed layer. TheMTJ 912 remains in the state it was in atstate 1. The reason for this is, that in one embodiment of the present invention, with the aspect ratio of theMTJ 912 being higher than that ofMTJ 910, it is prevented from switching. This results in the resistance of thememory cell 914 indicated in Table 1. - In programming the
memory cell 914 to astate 3, a current of level of 50 micro Amps is applied by thecurrent source 918 to thecircuit 920, which causes the current level, generated by thetransistor 928 to be 4 times that of the level of the current source, or 200 micro amps. The current level forstate 3 is indicated in Table 1. Theswitch 910 is caused to be switched to the state indicated at 950. Theswitches 908 and 916 are both set to ‘erase’ state, which causes the 200 micro amp current to flow through theMTJs transistor 940 is selected by raising the voltage on theword line 942. This results in programming ofstate 3. The magnetic moment of the free layers of theMTJs memory cell 914 to be that indicated in Table 1. - To program the
memory cell 914 to a state 4, a current of level of 50 micro Amps is applied by thecurrent source 902 to thecircuit 904, which is the current level of thecircuit 904 and that which is indicated in Table 1 for state 4. This causes theswitch 906 to switch to the state indicated at 946. The switch 908 is set to ‘program’ state, as is theswitch 916, which causes the 50 micro amp current to flow through theMTJs transistor 940 is selected by raising the voltage on theword line 942. This results in programming of state 4. The magnetic moment of the free layer of theMTJ 910 will be caused to be aligned with the magnetic moment of that of its respective fixed layer. TheMTJ 912 remains in its anti-parallel state, the reason for this is due the difference in the aspect ratios of the two MTJs as discussed hereinabove. This results in a resistance of thememory cell 914 indicated in Table 1. -
FIG. 9 shows a read circuit for reading the memory elements of the various embodiments of the present invention.FIG. 9 is shown to include amemory cell 1002 coupled to asense amplifier circuit 1004, which is shown coupled to areference circuit 1006. Thememory cell 1002 is shown to include anaccess transistor 1008, anMTJ 1010 and anMTJ 1012. Thetransistor 1008 is shown to have a drain, a source and a gate. The gate of thetransistor 1008 is shown coupled to aword line 1014, the drain of the transistor is shown coupled to ground and the source of the transistor is shown coupled to theMTJ 1010. - It should be noted that wherever values are indicated herein, they are to merely serve as examples with the understanding that other suitable values are anticipated. It is further noted that while reference is made to an N-type or P-type transistor, either type or other suitable types of transistors may be employed, as the type of transistor indicated in the foregoing embodiments, merely serve as examples.
- The
circuit 1006 is shown to include a number of state reference circuits, indicated asstate reference circuit circuit 1020 is shown to include areference resistor 1026 coupled on one side to thecircuit 1004 and Vcc and on the other side to the drain of anaccess transistor 1028. The gate of thetransistor 1028 is shown coupled to a select signal, namely select 1signal 1040. - Similarly, the
circuit 1022 is shown to include areference resistor 1030 coupled on one side to thecircuit 1004 and Vcc and on the other side to the drain of anaccess transistor 1032. The gate of thetransistor 1032 is shown coupled to a select signal, namely the select 2signal 1042. Thecircuit 1024 is shown to include areference resistor 1034 coupled on one side to thecircuit 1004 and Vcc and on the other side to the drain of an access transistor 1036. The gate of thetransistor 1044 is shown coupled to a select signal, namely the select 3signal 1044. - The
MTJs FIG. 8 , are similar to the MTJs of the embodiments of the present invention except that in the case ofFIG. 7 , the MTJs of the read circuit would be coupled in parallel rather than in series, shown inFIG. 9 . - During a read operation, the
memory cell 1002 is selected by raising the voltage of theword line 1014. Thecircuit 1004 compares the total resistance of theMTJs MTJs 1010 and 1012 (collectively or added together) is compared to the resistance of theresistor 1026 and if it is determined to be less, the state of thememory cell 1002 is declared as binary value ‘00’ or perhaps,state 1. However, if the resistance of theMTJs resistor 1026, the former is then compared to the resistance of theresistor 1030 and there again, if the resistance of theMTJs resistor 1030, thestate 2 or binary value ‘01’. If the resistance of theMTJs resistor 1030, the resistance of theMTJs resistor 1034 and if the resistance of the former is determined to be lower, thestate 3 or binary value ‘10’ is declared (or read), otherwise, the state 4 or binary value ‘11’ is declared. - The select signal of each of the circuits 1020-1024 are used to select the corresponding circuit. For example, to compare the resistance of the MTJs to the resistance of the
resistor 1026, thesignal 1040 is activated thereby turning on thetransistor 1028. In the meanwhile, the remaining transistors of thecircuit 1006 are off. Similarly, to compare the resistance of the MTJs to the resistance of theresistor 1030, thesignal 1042 is activated thereby turning on thetransistor 1032. In the meanwhile, the remaining transistors of thecircuit 1006 are off. To compare the resistance of the MTJs to the resistance of theresistor 1034, thesignal 1044 is activated thereby turning on the transistor 1036. In the meanwhile, the remaining transistors of thecircuit 1006 are off. - Examples of resistance values of the reference resistors are averages of the resistances of the
MTJs resistor 1026 is the average of the resistances of theMTJs states 1 and 4, as indicated in Table 1. The resistance of theresistor 1030 is the average of the resistances of theMTJs states 2 and 4, as indicated in Table 1. The resistance of theresistor 1034 is the average of the resistances of theMTJs states resistor 1026 has a resistance of 3.5 kilo-ohm, which is the average of 3 and 4 kilo-ohms. The resistance of theresistor 1030 is 4.5 kilo-ohms, which is the average of 5 and 4 kilo-ohms and the resistance of theresistor 1034 is 5.5 kilo-ohms, which is the average of 5 and 6 kilo-ohms. - In various embodiments of the present invention, some of which are disclosed hereinbelow, a STTMRAM using two or more MTJs having perpendicular orientations or a combination of perpendicular and longitudinal MTJs, placed in the close proximity to each other is disclosed. One of the characteristics of such a STTMRAM is to advantageously have multiple resistances associated therewith allowing for the storage of multiple states, thereby having smaller cell size.
- At smaller litho dimensions the magnetic memory bits would have substantially perpendicular orientation of the magnetization direction.
- Bottom MTJ (or stack) is a memory structure where the fixed layer is formed below the free layer during MTJ fabrication and a top MTJ (or stack) is memory structure where the fixed layer is formed on top of the free layer during MTJ fabrication.
-
FIG. 10 shows a multi-state spin-torque transfer magnetic random access memory (STTMRAM) 1100, in accordance with an embodiment of the present invention. Themulti-state STTMRAM memory 1100 is shown to include bottom electrode (BE) 1104,underlayer 1106, fixedlayer 1108, spin polarization enhanced (interface) layers (SPEL) 1110 and 1114,free layer 1118,cap layer 1120,non-magnetic spacing layer 1122,underlayer 1128, fixedlayer 1130,SPEL 1134,tunneling layer 1136,SPEL 1138,free layer 1140,cap layer 1141 and top electrode (TE) 1143. -
Underlayer 1106 is shown formed on top ofBE 1104, which is generally formed on a substrate or film (or a metal post or line such as tungsten, aluminum or copper for) of a typical integrated circuit.Fixed layer 1108 is shown formed on top of fixedlayer 1108 andSPEL layer 1110 is shown formed on top of fixedlayer 1108. - In some embodiments,
SPELL 110 is a part of fixedlayer 1108. In some embodiments,SPELL 114 is a part offree layer 1118. - Referring still to
FIG. 10 ,tunneling layer 1112 is shown formed on top ofSPELL 110,SPEL 1114 is shown formed on top oftunneling layer 1112,free layer 1118 is shown formed on top ofSPEL 1114,cap layer 1120 is shown formed on top offree layer 1118,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,underlayer 1128 is shown formed on top ofnon-magnetic spacing layer 1122, fixedlayer 1130 is shown formed on top ofunderlayer 1128,SPEL 1134 is shown formed on top of fixedlayer 1130,tunneling layer 1136 is shown formed on top ofSPEL 1134,SPEL 1138 is shown formed on top oftunneling layer 1136,free layer 1140 is shown formed on top ofSPEL 1138,cap layer 1141 is shown formed on top offree layer 1140 andTE 1143 is shown formed on top ofcap layer 1141. - Magnetic tunnel junction (MTJ) 1124 comprises fixed
layer 1108,SPELL 1110,tunneling layer 1112,SPEL 1114 andfree layer 1118.MTJ 1126 comprises fixedlayer 1130,SPEL 1134,tunneling layer 1136,SPEL 1138 andfree layer 1140. In this manner,MTJ 1126 andMTJ 1124 are stacked. WhileMTJ 1124 andMTJ 1126 are each shown to have a bottom stacking structure with their respective free layers formed above their fixed layers, alternatively, they may have a top stacking structure where their respective fixed layers are formed above their free layers. - While two MTJs are shown in
FIG. 10 , it is understood that any number of MTJs may be stacked. -
SEPL 1134,tunneling layer 1136 andSPEL 1138, are collectively referred to as sub-magnetic tunnel junction (sub-MTJ)layer 1132. Similarly,SEPL 1110,tunneling layer 1112 andSPEL 1114 are collectively referred to as sub-magnetic tunnel junction (sub-MTJ)layer 1159. -
ULs - In some embodiments, SPELs are not employed in either of
MTJs MTJs SPEL 1110 is used andSPEL 1114 is absent or onlySPEL 1114 is used andSPEL 1110 is absent. In yet other embodiments, as discussed above, SPEL is part of an adjacent layer. For example,SPEL 1134 is part of fixedlayer 1130 orSPEL 1138 is part offree layer 114 orSPEL 1134 is part of fixedlayer 1130 andSPEL 1138 is part offree layer 1140. - The functions of
BE 1104 andTE 1143 are as known to those skilled in the art.Fixed layers multi-state STTMRAM cell 1100. The magnetization direction of each of thefree layers multi-state STTMRAM 1100. In fact, the parallel and anti-parallel states define the logical state of a free layer which define the logical state of the corresponding MTJ. For example,free layer 1118's magnetization state being in a parallel state relative to fixedlayer 1108 defines a different logical state thanfree layer 1118's magnetization direction being in an anti-parallel state relative to fixedlayer 1108. An example of logic states are ‘0’ or ‘1’. - The direction of magnetization of fixed
layer 1108, which is shown by thearrow 1123, is fixed in the direction of thearrow 1123 and it is perpendicular to the surface of the substrate onto which themulti-state STTMRAM 1100 is formed. The direction of magnetization offree layer 1118, which switches relative to that of fixedlayer 1108, as shown by thearrow 1127, is also perpendicular to the plane of the substrate. - In some embodiments, the thickness of each of
underlayers BE 1104 andunderlayer 1106 and in betweennon-magnetic spacing layer 1122 andunderlayer 1128. In some embodiments, the seedlayer thickness is 2 nm to 50 nm. In some embodiments, fixedlayers free layers 1118 and 140 is typically 1 to 10 nm. In some embodiments, the thickness of each oftunneling layers non-magnetic isolation layer 1122 is 5 nm-100 nm. In some embodiments, the thickness ofcaplayer 1141 is 2 to 100 nm and typically 5 to 50 nm. In some embodiments, the thickness oftop electrode 1143 and bottom electrode choice and thickness depend on the device design and are typically thicker than 10 nm. - The material of which each of the
underlayers Fixed layers layers tunneling layers Cap layers - The
function UL 1106 is to provide the proper crystal structure template in order to grow the adjacent and subsequent magneticfixed layers arrow 1123. This is typically characterized by measuring the delta theta 50 of the preferred easy axis. As known to those skilled in the art, this is carried out typically by using an x-ray diffractometer such as one designed by Rigaku Coporation, Tokyo, Japan. A smaller delta-theta 50 indicates, such as typically below 5 degrees, a more oriented film. A typical value of the delta-theta 50 is below 10 degrees. The function of SPEL layer is to enhance the tunneling magneto-resistance (TMR) of the MTJs through proper crystal structure matching during the magnetic annealing process. - The function of fixed
layers layer 1108 acts as a reference layer with fixed magnetic orientation forMTJ 1124 and fixedlayer 1140 acts as a reference layer with fixed magnetic orientation forMTJ 1126. - The function of each of
tunneling layers - The function of each of
free layers - While
STTMRAM 1100 is shown to include two MTJs, in other embodiments, it may include more than two MTJs. In fact, any number of MTJs may be employed in any of the STTMRAM of the various embodiments of the present invention. In the case where more than two MTJ are employed, a unique switching current switches the state of each MTJ. For example, a STTMRAM with three MTJs, coupled in series, and coupled to an n-channel MOSFEL (NMOS) type of access transistor may exhibit switching currents of 75 micro Amps for one MTJ, 50 micro Amps for a second MTJ and 25 micro Amps for the third MTJ. - It is noted that an MTJ is a variable resistive element. In this regard, any of the MTJs discussed and/or shown herein may be replaced with a variable resistive element without departing from the scope and spirit of the present invention.
- In operation, during a write operation, electric current is applied in a direction that is either from
BE 1104 through the subsequent layers that are on top ofBE 1104 or in a direction fromTE 1143 through the subsequent layers formed belowTE 1143. - It is noted that the direction of magnetization of the free and fixed layers of the MTJs in the
FIGS. 10 through 25 is indicated by the direction of the arrows used therein. -
FIG. 11 shows amulti-state STTMRAM 1153, in accordance with an alternative embodiment of the present invention. Themulti-state STTMRAM 1153 includesMTJ 1126, which is shown formed on top of the anti-ferromagnetic (AFM)layer 1128, which is shown formed top ofUL 1150 The top portion of themulti-state STTMRAM 1153, i.e., the layers on top of the fixedlayer 1130 are analogous to common layers of that ofmulti-state STTMRAM 1100. - Anti-ferromagnetic (AFM)
layer 1128 is shown formed on top ofUL 1150, which is shown formed on top ofnon-magnetic spacing layer 1152 which is formed on top of thecap layer 1120, which is shown formed on top offree layer 1118, which is shown formed on top ofSPEL 1114. The layers formed belowSPEL 1114 are analogous to that of like locations ofmulti-state STTMRAM 1100.AFM layer 1148 is shown formed betweenUL 1106 and fixedlayer 1108.UL 1106 is shown formed on top ofBE 1104, which is typically formed on film or substrate of an integrated circuit. In this respect, the embodiment ofFIG. 11 is analogous to that ofFIG. 10 except that each AFM layer separates its respective MTJ from the corresponding UL. - Each of the AFM layer is used to establish perpendicular orientation of its respective fixed layer. In some embodiments, each of the
AFM layer -
FIG. 12 shows amulti-state STTMRAM 1155, in accordance with an alternative embodiment of the present invention.Layers multi-state STTMRAM 1100. On top ofUL 1128, there is shown formed fixedlayer 1130 and on top of fixedlayer 1130, there is shown formedSPEL 1134. Ontop SPEL 1134, three is shown formedtunneling layer 1136 and on top oftunneling layer 1136, there is shown formedSPEL 1138. On top ofSPEL 1138, there is shown formedfree layer 1140 and on top offree layer 1140, there is shown formedAFM layer 1154. On top ofAFM layer 1154, there is shown formedcap layer 1141 and on top ofcap layer 1141, there is shown formedTE 1143. -
AFM layer 1154 is analogous toAFM layers -
FIG. 13 shows amulti-state STTMRAM 1160, in accordance with an alternative embodiment of the present invention. Themulti-state STTMRAM 1160 is shown to includeMTJ 1124, formed on top ofUL 1106, which is formed on top ofBE 1104, as in the embodiment ofFIG. 10 . On top ofMTJ 1124 is shown formedcap layer 1120 on top of which is formednon-magnetic spacing layer 1122. On top ofnon-magnetic spacing layer 1122 is shown formedUL 1128. On top ofUL 1128 is shown formed fixedlayer 1130 and on top of fixedlayer 1130 is shown formedsub-MTJ stack 1132. On top ofsub-MTJ stack 1132 is shown formed a compositefree layer 1157. Compositefree layer 1157 comprises oflayers 1158,layer 1160 andlayer 1156. Each oflayers layer 1118. -
Layer 1160 is also known as a nano-current channel (NCC) layer and is comprised of magnetic and non-magnetic regions as depicted by the darker rectangles and white or no-color rectangles. The darker rectangular regions represent the magnetic regions and the while rectangular regions represent the non-magnetic regions although vice versa is contemplated. The magnetic part is typically an alloy of one or more of the elements chosen from Co, Fe, Ni, Ti, Ta, Cr, Si, B, P, C, W, Al, Zr and the non-magnetic portion is one or more of oxides, nitrides and phosphides of Al, Si, Ti, Ta, W, Zr. - The
layers free layer 1157, as are similarly structured layers where a NCC is formed between two free layers. - In one embodiment, composite
free layer 1157 comprises oflayers free layer 1157 comprises oflayers free layer 1157 comprises oflayers layer 1156 is thinner thanlayer 1158 by more than a factor of two. - It is expected that the
MTJ2 1162 ofmulti-state STTMRAM 1160 has lower programming current than theMTJ1 1124 by over a factor of two times. -
FIG. 14 shows a multi-state STTMRAM 1164, in accordance with another embodiment of the present invention. The top portion of the multi-state STTMRAM 1164 is analogous to the top portion ofmulti-state STTMRAM 1100.AFM layer 1128 is shown formed on top ofUL 1150, which is shown formed on top of thenon-magnetic spacing layer 1152 which is formed on top ofcap layer 1120, which is shown formed on top of compositefree layer 1157, which is shown formed on top ofsub-MTJ layer 1159, which is shown formed on top oflayer 1108, which is shown formed on top ofAFM layer 1148, which is shown formed on top ofUL 1106, which is shown formed on top ofBE 1104. Thelayers 1108,sub-MTJ layer 1159 and the compositefree layer 1157form MTJ 1161. - In operation, the
MTJ1 1161 requires a lower programming current than theMTJ2 1126. -
FIG. 15 shows amulti-state STTMRAM 1166, in accordance with another embodiment of the present invention. InFIG. 15 ,UL 1106 is shown formed on top ofBE 1104. On top ofUL 1106 is shown formedMTJ 1124 and on top ofMTJ 1124 is shown formedcap layer 1120. On top ofcap layer 1120 is shown formednon-magnetic spacing layer 1122 and on top oflayer 1122 is shown formedUL 1128. On top ofUL 1128 is shown formed compositefree layer 1157 and on top of the compositefree layer 1157 is shown formed thesub-MTJ layer 1132. On top ofsub-MTJ layer 1132 is shown formed fixedlayer 1163 and on top of fixedlayer 1163 is shown formedAFM layer 1154. On top ofAFM layer 1154 is shown formedcap layer 1141 and on top ofcap layer 1141 is shown formedTE 1143. Thelayers MTJ 1161. - In the embodiment of
FIG. 15 ,MTJ 1161 is shown formed on top ofMTJ 1124 therefore creating a stacked MTJ structure. As with all embodiments shown inFIGS. 10 through 25 , while two MTJs are shown to be stacked, in various embodiments of the present invention, any number of MTJs may be stacked. - As earlier stated, the magnetization of fixed
layers arrows non-magnetic spacer layer 1122 is made thicker than 20 nm to ensure no magnetic interactions between theMTJ 1124 andMTJ 1161. -
FIG. 16 shows amulti-state STTMRAM 1170, in accordance with an alternative embodiment of the present invention. In the embodiment ofFIG. 16 ,MTJ 1126 is shown stacked on top ofMTJ 1176. MTJ is shown formed on top ofUL 1106, which is shown formed on top ofBE 1104.Cap layer 1120 is shown formed on top ofMTJ 1176 and on top ofcap layer 1120 is shown formednon-magnetic spacing layer 1122. On top ofnon-magnetic spacing layer 1122 is shown formedUL 1128 and on top ofUL 1128 is shown formedMTJ 1126. On top ofMTJ 1126 is shown formedcap layer 1141 and on top ofcap layer 1141 is shown formedTE 1143. -
MTJ 1176 is shown formed of fixedlayer 1172,SPEL 1171, tunneling layer 1178,SPEL 1173, andfree layer 1174.Fixed layer 1172 is formed on top of theAFM layer 1179, which is shown formed on top of theUL 1106. Unlike the MTJs ofFIGS. 10 through 15 where the direction of magnetization of the free layers and fixed layers were perpendicular to the surface of the substrate (perpendicular magnetic anisotropy), the direction of magnetization of the free and fixed layers ofMTJ 1176 are parallel or in-plane relative to the surface of the substrate on which the amulti-state STTMRAM 1170 is built. In the case where more than two MTJs are stacked, there may be an MTJ with in-plane magnetic anisotropy formed on top ofMTJ 1126 and an MTJ with perpendicular magnetic anisotropy formed on top it and so on with alternating magnetic anisotropy. Alternatively, there may be an MTJ with perpendicular anisotropy formed on top ofMTJ 1126 and on top of it is formed an in-plane magnetic anisotropy MTJ where the MTJs of varying magnetic anisotropy skip by two. Alternatively, the MTJs may skip by any number. -
FIG. 17 shows amulti-state STTMRAM 1180, in accordance with yet another embodiment of the present invention. In the embodiment ofFIG. 17 ,UL 1106 is shown formed on top ofBE 1104 and on top ofUL 1106 is shown formedMTJ 1124. On top ofMTJ 1124 is shown formedcap layer 1120 and on top ofcap layer 1120 is shown formedMTJ 1190. On top ofMTJ 1190 is shown formedcap layer 1141 and on top ofcap layer 1141 is shown formedTE 1143. -
MTJ 1190 is shown comprised of:AFM layer 1187, fixedlayer 1183,SPEL 1182,tunneling layer 1184,SPEL 1186 andfree layer 1185.Fixed layer 1183 is shown formed on top ofAFM layer 1187,SPEL 1182 is shown formed on top of fixedlayer 1183,tunneling layer 1184 is shown formed on top ofSPEL 1182,SPEL 1186 is shown formed on top oftunneling layer 1184 andfree layer 1185 is shown formed on top ofSPEL 1186.SPEL 1182,tunneling layer 1184 andSPEL 1186 collectively comprisesub-MTJ layer 1188. As in the embodiment ofFIG. 16 ,non-magnetic spacing layer 1122 separates the two MTJs ofFIG. 17 . -
FIG. 18 shows amulti-state STTMRAM 1192, in accordance with yet another embodiment of the present invention. The multi-state STTMRAM is shown to includeBE 1104,UL 1106,AFM layer 1196, fixedlayer 1172,sub-MTJ layer 1175,free layer 1174,cap layer 1120,non-magnetic spacing layer 1122,AFM layer 1150,MTJ 1126,cap layer 1141 andTE 1143. In the embodiment ofFIG. 18 ,UL 1106 is shown formed on top ofBE 1104,MTJ 1194 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1194,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,non-magnetic spacing layer 1122 is shown formed on top ofAFM layer 1150,MTJ 1126 is shown formed on top ofAFM layer 1150,cap layer 1141 is shown formed on top ofMTJ 1126 andTE 1143 is shown formed on top ofcap layer 1141. -
Layers free layer 1174 collectively compriseMTJ 1194. - The direction of magnetization of each of the fixed
layer 1172 andfree layer 1174, ofMTJ 1194, is parallel relative to the surface of the substrate onto whichmulti-state STTMRAM 1192 is made, whereas, the free and fixed layers ofMTJ 1126 each have a direction of magnetization that is perpendicular to the plane of the substrate onto whichmulti-state STTMRAM 1192 is formed. Accordingly, the embodiment ofFIG. 18 shows an MTJ with a perpendicular magnetic anisotropy formed on top of one having an in-plane magnetic anisotropy. -
FIG. 19 shows multi-stateSTTMRAM 1200, in accordance with an alternative embodiment of the present invention. Themulti-state STTMRAM 1200 is shown to includeBE 1104,UL 1106,MTJ 1124,cap layer 1120,non-magnetic spacing layer 1122,MTJ 1190,cap layer 1141 andTE 1143.MTJ 1190 is shown to includeAFM layer 1250, fixedlayer 1240,sub-MTJ layer 1232 andfree layer 1230. Thesub-MTJ layer 1232 is shown to includeSPEL 1238,tunneling layer 1236 andSPEL 1234. -
UL 1106 is shown formed on top ofBE 1104.MTJ 1124 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1124,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120, andMTJ 1190 is shown formed on top ofnon-magnetic spacing layer 1122.Cap layer 1141 is shown formed on top ofMTJ 1190 and TE is shown formed on top ofcap layer 1141. - More specifically,
AFM layer 1250 is shown formed on top ofnon-magnetic spacing layer 1122, fixedlayer 1240 is shown formed on top ofAFM layer 1250,SPEL 1238 is shown formed on top of fixedlayer 1240, tunneling layer is shown formed on top ofSPEL 1238,SPEL 1234 is shown formed ontop tunneling layer 1236 andfree layer 1230 is shown formed on top ofSPEL 1234. - The direction of magnetization of each of
free layer 1230 and fixedlayer 1240 is in-plane relative to the plane of the substrate. Accordingly, the embodiment ofFIG. 19 shows an MTJ with an in-plane magnetic anisotropy formed on top of one having a perpendicular magnetic anisotropy. -
FIG. 20 shows multi-stateSTTMRAM 1300, in accordance with another embodiment of the present invention. In the embodiment ofFIG. 20 ,multi-state STTMRAM memory 1300 is shown to includeBE 1104,UL 1106,MTJ 1194,cap layer 1120,non-magnetic spacing layer 1122,UL 1128,MTJ 1162,cap layer 1141 andTE 1143.UL 1106 is shown formed onBE 1104,MTJ 1194 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1194,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,UL 1128 is shown formed on top ofnon-magnetic spacing layer 1122,MTJ 1162 is shown formed on top ofUL 1128,cap layer 1141 is shown formed on top ofMTJ 1162,cap layer 1141 is shown formed on top ofMTJ 1162 and TE is shown formed on top ofcap layer 1141. - In
FIG. 20 , the magnetic anisotropy of each of the free and fixed layers ofMTJ 1162 is perpendicular and the magnetic anisotropy of each of the free and fixed layers ofMTJ 1194 is in-plane. -
FIG. 21 shows multi-stateSTTMRAM 1400, in accordance with another embodiment of the present invention. In the embodiment ofFIG. 21 ,multi-state STTMRAM 1400 is shown to includeBE 1104,UL 1106,MTJ 1161,cap layer 1120,non-magnetic spacing layer 1122,UL 1128,MTJ 1190,cap layer 1141 andTE 1143.UL 1106 is shown formed onBE 1104,MTJ 1161 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1161,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,UL 1128 is shown formed on top ofnon-magnetic spacing layer 1122,MTJ 1190 is shown formed on top ofUL 1128,cap layer 1141 is shown formed on top ofMTJ 1190,cap layer 1141 is shown formed on top ofMTJ 1190 and TE is shown formed on top ofcap layer 1141. - In
FIG. 21 , the magnetic anisotropy of each of the free and fixed layers ofMTJ 1190 is in-plane and the magnetic anisotropy of each of the free and fixed layers ofMTJ 1161 is perpendicular. -
FIG. 22 shows multi-stateSTTMRAM 1500, in accordance with another embodiment of the present invention. In the embodiment ofFIG. 22 ,multi-state STTMRAM 1500 is shown to includeBE 1104,UL 1106,MTJ 1502,cap layer 1120,non-magnetic spacing layer 1122,UL 1150,AFM layer 1128,MTJ 1126,cap layer 1141 andTE 1143.UL 1106 is shown formed onBE 1104,MTJ 1502 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1502,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,UL 1150 is shown formed ontop cap layer 1120,AFM layer 1128 is shown formed on top ofUL 1150,MTJ 1126 is shown formed on top ofAFM layer 1128,cap layer 1141 is shown formed on top ofMTJ 1126, andTE 1143 is shown formed on top ofcap layer 1141. -
MTJ 1502 is shown to includeAFM layer 1196, fixedlayer 1172,sub-MTJ layer 1175,free layer 1512 and compositefree layer 1514. Compositefree layer 1514 is shown to includefree layer 1169,NCC 1510 andfree layer 1514. The free layers positioned above and below the NCC layer are sometimes referred to as “sub-free layers”. For example,free layer 1169 andfree layer 1508 may be each referred to assub-free layer 1169 andsub-free layer 1508, respectively. -
AFM layer 1196 is shown formed on top ofUL 1106, fixedlayer 1172 is shown formed on top ofAFM layer 1196,sub-MTJ layer 1175 is shown formed on top of fixedlayer 1172,free layer 1512 is shown formed on topsub-MTJ layer 1175, compositefree layer 1514 is shown formed on top offree layer 1172, andcap layer 1120 is shown formed on top of compositefree layer 1514. Compositefree layer 1514 is formed ofNCC 1510 formed on top offree layer 1169 andfree layer 1508 is shown formed on top ofNCC 1510. In one embodiment, thelayer 1172 is - In
FIG. 22 , the magnetic anisotropy of each of thelayers MTJ 1126 is perpendicular. -
FIG. 23 shows multi-stateSTTMRAM 1600, in accordance with another embodiment of the present invention. In the embodiment ofFIG. 23 ,multi-state STTMRAM 1600 is shown to includeBE 1104,UL 1106,MTJ 1124,cap layer 1120,non-magnetic spacing layer 1122,UL 1128,MTJ 1602,cap layer 1141 andTE 1143.UL 1106 is shown formed onBE 1104,MTJ 1124 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1124,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,MTJ 1602 is shown formed on top ofnon-magnetic spacing layer 1122cap layer 1141 is shown formed on top ofMTJ 1602, andTE 1143 is shown formed on top ofcap layer 1141. -
MTJ 1602 is analogous except that it is formed on top ofMTJ 1124 and more specifically, on top ofnon-magnetic spacing layer 1122. Thus,NCC 1606 is analogous toNCC 1514. - In
FIG. 23 , the magnetic anisotropy of each of the free and fixed layers ofMTJ 1602 is in-plane and the magnetic anisotropy of each of the free and fixed layers ofMTJ 1124 is perpendicular. -
FIG. 24 shows multi-stateSTTMRAM 1700, in accordance with another embodiment of the present invention. In the embodiment ofFIG. 24 ,multi-state STTMRAM 1700 is shown to includeBE 1104,UL 1106,MTJ 1161,cap layer 1120,non-magnetic spacing layer 1122,UL 1128,MTJ 1162,cap layer 1141 andTE 1143.UL 1106 is shown formed onBE 1104,MTJ 1161 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1161,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,UL 1128 is shown formed on top ofnon-magnetic spacing layer 1122,MTJ 1162 is shown formed on top ofUL 1128,cap layer 1141 is shown formed on top ofMTJ 1162, andTE 1143 is shown formed on top ofcap layer 1141. - In
FIG. 24 , the magnetic anisotropy of each of the free and fixed layers ofMTJ 1161 is perpendicular and the magnetic anisotropy of each of the free and fixed layers ofMTJ 1162 is perpendicular. It should be noted that in some embodiments, the NCC of each of the composite free layers of theMTJs MTJs -
FIG. 25 shows multi-stateSTTMRAM 1800, in accordance with another embodiment of the present invention. In the embodiment ofFIG. 25 ,multi-state STTMRAM 1800 is shown to includeBE 1104,UL 1106,MTJ 1502,cap layer 1120,non-magnetic spacing layer 1122,AFM layer 1154,MTJ 1162,cap layer 1141 andTE 1143.UL 1106 is shown formed onBE 1104,MTJ 1502 is shown formed on top ofUL 1106,cap layer 1120 is shown formed on top ofMTJ 1502,non-magnetic spacing layer 1122 is shown formed on top ofcap layer 1120,AFM layer 1154 is shown formed on top ofnon-magnetic spacing layer 1122,MTJ 1162 is shown formed on top ofUL 1128,cap layer 1141 is shown formed on top ofMTJ 1162, andTE 1143 is shown formed on top ofcap layer 1141. - In
FIG. 25 , the magnetic anisotropy of each of the free and fixed layers ofMTJ 1502 is in-plane and the magnetic anisotropy of each of the free and fixed layers ofMTJ 1162 is perpendicular. - While various combinations of MTJs are shown in
FIGS. 10 through 25 , such as in-plane, perpendicular, with/without AFM layer, with/without NCC, and the like, various other combinations and configurations of MTJs are contemplated. - In each of the embodiments of
FIGS. 10 through 25 , while two MTJs are shown, any number of MTJs may be employed. Moreover, the perpendicular vs. in-plane MTJs not only may alternate but they may also be every configured to be of the same orientation for some number of MTJs that are stacked on top of each other prior to a MTJ having an opposite orientation being formed thereon. Any such combination is contemplated. -
FIG. 26 shows a flow chart of the steps performed, during a write or program operation, to write/program one or more of the MTJs of the various embodiments of the present invention. InFIG. 26 ,process 1900 outlines relevant steps of the write operation. - In one embodiment of the present invention, the steps of
process 1900 ofFIG. 16 are performed by the program/erasecircuit 900 ofFIG. 8 . Atstep 1902, data to be programmed is received. Next, a determination is made at 1904 as to whether or not the most significant bit (MSB) of the received data is the value ‘0’ and if so,process 1900 proceeds to step 1908, otherwise,process 1900 proceeds to step 1906. Atstep 1906, a negative high (H) current is applied to the MTJ or memory cell being programmed. In one embodiment, the memory cell sought to be programmed isMTJ 912, in other embodiments, the MTJ sought to be programmed is any one of the memory cells that include one or more of the MTJs of the various embodiments of the present invention. - Negative H current, as used herein, refers to sufficient negative current allowing switching (or changing states) of an MTJ having no NCC and being programmed. Negative low current, as used herein, refers to sufficient negative current allowing switching (or changing states) of an MTJ having NCC and being programmed. Positive H current, as used herein, refers to sufficient positive current allowing switching (or changing states) of an MTJ not having NCC and being programmed. Positive low current, as used herein, refers to sufficient positive current allowing switching (or changing states) of an MTJ including NCC and being programmed.
- Referring back to
process 1900, atstep 1908, positive H current is applied to the MTJ being programmed. Next, afterstep 1908, a determination is made at 1910 as to whether or not the least significant bit (LSB) of the received data is zero and if not,process 1900 proceeds to step 1920, otherwise,process 1900 proceeds to step 1914. Atstep 1920, a negative low current is applied to the MTJ being programmed atstep 1914, no current or zero current is applied to the MTJ being programmed. Afterstep 1914,process 1900 proceeds to the end of theprogramming step 1922. Similarly, afterstep 1920,process 1900 proceeds to the end of theprogramming step 1922. - After
step 1906, a determination is made at 1912 as to whether or not the LSB of the received data is zero and if not,process 1900 proceeds to step 1918, otherwise,process 1900 proceeds to step 1916. Atstep 1918, zero or no current is applied to the MTJ being programmed atstep 1916, positive low current is applied to the MTJ being programmed. Afterstep 1916,process 1900 proceeds to the end of theprogramming step 1922. Similarly, afterstep 1918,process 1900 proceeds to the end of theprogramming step 1922. - In alternative embodiments of the present invention, the MTJs (or memory elements) disclosed in U.S. patent application Ser. No. 11/674,124 entitled “Non-Uniform Switching Based Non-Volatile Magnetic Base Memory”, filed on Feb. 12, 2007, may be employed in the embodiments of
FIGS. 8 and 9 herein. - It should be noted that the objects of the drawings or figures discussed and presented herein are not necessarily drawn to scale.
- In some embodiment, those free or fixed layers of the
STTMRAMs FIGS. 10 , 11, 12, 13, 14, 15 and 24, have largely a circular (or cylindrical) shape in-plane. This is further described in US Patent Publication No. US 2008/019125 entitled, “Non-Volatile Magnetic Memory With Low Switching Current And High Thermal Stability”, the contents of which is incorporated herein by reference as though set forth in full. This is particularly useful during manufacturing of such STTMRAM, especially for smaller feature sizes such as below 90 nano meters (nm) because the in-plane STTMRAM typically requires an elongated shape such as rectangular or ellipse, having an aspect ratio of two or three; such designs are difficult to form with high degree of uniformity for smaller feature sizes below 90 nm and pose a greater design and cost challenge for the photo-masks required for printing such structures. The perpendicular STTMRAM, on the other hand, requires an aspect ratio closer to one and this does not require special designs for the photo-mask requiring high-aspect ratio shape control like the in-plane STTRAM. - In some embodiments, where the
STTMRAMs FIGS. 16 , 17, 18, 19, 20, 21, 22, 23 and 25, the preferred in-plane shape is rectangular or ellipsoid as shown inFIG. 27( b). It is likely that such designs may not be scalable well below 65 nm feature size for the reasons mentioned above. -
FIG. 27( a) shows top-down or in-plane view and side-view of shapes that any of theSTTMRAMs -
FIG. 27( b) shows top-down or in-plane view and side-view of shapes that any of theSTTMRAMs - Although the present invention has been described in terms of specific embodiments, it is anticipated that alterations and modifications thereof will no doubt become apparent to those skilled in the art. It is therefore intended that the following claims be interpreted as covering all such alterations and modification as fall within the true spirit and scope of the invention.
- What is claimed is:
-
TABLE 1 MLC cell with two or more stacked MTJ with different anisotrophy. I density 100 n = 2 Parallel Anti-parallel Anisotrophy ratio 2 R(K Ω) large 1 2 Large Small R(K Ω) small 2 4 Fixed layers Free layer 1Free layer 2State Total R Prog I (uA) → → → 1 3 200 → → ← 2 5 −50 → ← ← 3 6 −200 → ← → 4 4 50 -
TABLE 2 MLC cell with two or more MTJs side by side with different anisotrophy. I density 50 n = 2 Parallel Anti-parallel Anisotrophy ratio 1.3 R(K Ω) large 3 6 Small Large R(K Ω) small 3.9 7.8 Fixed layer Free layer Free layer State Total R Prog I (uA) → → → 1 1.70 −134.5 → → ← 2 2.36 50 → ← ← 3 3.39 134.5 → ← → 4 2.17 −50 From one state to another 1 to 2 2 to 3 3 to 4 R differences 0.67 1.03 1.22 0.47 between different states
Claims (50)