US20090186249A1 - Titanate and metal interconnects for solid oxide fuels cells - Google Patents
Titanate and metal interconnects for solid oxide fuels cells Download PDFInfo
- Publication number
- US20090186249A1 US20090186249A1 US12/005,655 US565507A US2009186249A1 US 20090186249 A1 US20090186249 A1 US 20090186249A1 US 565507 A US565507 A US 565507A US 2009186249 A1 US2009186249 A1 US 2009186249A1
- Authority
- US
- United States
- Prior art keywords
- electrode
- solid oxide
- fuel cell
- oxide fuel
- interconnect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A solid oxide fuel cell (SOFC) includes a plurality of sub-cells. Each sub-cell includes a first electrode in fluid communication with a source of oxygen gas, a second electrode in fluid communication with a source of a fuel gas, and a solid electrolyte between the first electrode and the second electrode. The SOFC further includes an interconnect between the sub-cells. In one embodiment, the SOFC has a first surface in contact with the first electrode of each sub-cell and a second surface that is in contact with the second electrode of each sub-cell; and the interconnect consists essentially of a doped M-titanate based perovskite, wherein M is an alkaline earth metal. In another embodiment, the interconnect includes a first layer in contact with the first electrode of each sub-cell, and a second layer in contact with the second electrode of each sub-cell. The first layer includes an electrically conductive material selected from the group consisting of an metal, a metal alloy and a mixture thereof. The second layer includes a doped M-titanate based perovskite, wherein M is an alkaline earth metal. A solid oxide fuel cell described above is formed by connecting each of the sub-cells with an interconnect described above.
Description
- This application claims the benefit of U.S. Provisional Application Nos. 60/877,503 and 60/877,504, both filed Dec. 28, 2006. The entire teachings of these applications are incorporated herein by reference.
- A fuel cell is a device that generates electricity by a chemical reaction. Among various fuel cells, solid oxide fuel cells use a hard, ceramic compound of metal (e.g., calcium or zirconium) oxide as an electrolyte. Typically, in the solid oxide fuel cells, an oxygen gas, such as O2, is reduced to oxygen ions (O2−) at the cathode, and a fuel gas, such as H2 gas, is oxidized with the oxygen ions to from water at the anode.
- Interconnects are one of the critical issues limiting commercialization of solid oxide fuel cells. Currently, most companies and researchers working with planar cells are using coated metal interconnects. For example, ferritic stainless steel based metal interconnects, such as Crofer 22 APU, and powder metallurgy formulations from Plansee AG in Austria, have good CTE (coefficient of thermal expansion) mismatch and good compatibility with solid oxide fuel cells. However, oxidation of metal interconnects during operation, thereby forming metal oxides, such as Cr2O3, and subsequent migration of metals of the metal oxides (e.g., chromium migration) to an electrode layer and/or electrode-electrolyte interface is one of the primary mechanisms leading to performance degradation in solid oxide fuel cells.
- While metal interconnects are relatively easy to fabricate and process, they generally suffer from high power degradation rates (e.g. 10%/1,000 h) partly due to formation of metal oxide, such as Cr2O3, at an interconnect-anode/cathode interface during operation. Ceramic interconnects based on lanthanum chromites (LaCrO3) have lower degradation rates than metal interconnects partly due to relatively high thermodynamic stability and low Cr vapor pressure of LaCrO3 compared to Cr2O3 formed on interfaces of the metal interconnects and electrode. However, doped LaCrO3 generally suffers from dimensional changes, such as warping or some other forms of distortion, and consequent seal failures in reducing conditions. Another issue related to LaCrO3 is its relatively low sinterability.
- Therefore, there is a need for development of new interconnects for solid oxide fuel cells, addressing one or more of the aforementioned problems.
- The invention is directed to a solid oxide fuel cell (SOFC) that includes a plurality of sub-cells and to a method of preparing the SOFC. Each sub-cell includes a first electrode in fluid communication with a source of oxygen gas, a second electrode in fluid communication with a source of a fuel gas, and a solid electrolyte between the first electrode and the second electrode. The SOFC further includes an interconnect between the sub-cells.
- In one embodiment, the interconnect has a first surface in contact with the first electrode of each sub-cell, and a second surface that is in contact with the second electrode of each sub-cell. The interconnect consists essentially of a doped M-titanate based perovskite, wherein M is an alkaline earth metal.
- In another embodiment, the interconnect includes a first layer in contact with the first electrode of each sub-cell, and a second layer in contact with the second electrode of each sub-cell. The first layer includes an electrically conductive material selected from the group consisting of an metal, a metal alloy and a mixture thereof. The second layer includes a doped M-titanate based perovskite, wherein M is an alkaline earth metal.
- The invention also includes a method of forming a solid oxide fuel cell described above. The method includes connecting each of the sub-cells with an interconnect described above.
- It is believed that the doped M-titanates (e.g., MTiO3) in the invention, particularly, n-doped M-titanates, such as n-doped SrTiO3 or CaTiO3, exhibit less oxygen vacancy formation during operation of SOFCs, as compared to conventional p-doped LaCrO3, thereby limiting or eliminating lattice expansion problems associated with conventional p-doped LaCrO3. In addition, the doped M-titanates can function as an effective oxidation barrier to thereby extend operation life of SOFCs.
-
FIG. 1 is a schematic cross-sectional view of one embodiment of the invention. -
FIG. 2 is a schematic cross-sectional view of another embodiment of the invention. -
FIG. 3 is a schematic diagram of an embodiment of a fuel cell of the invention, having a planar, stacked design. -
FIG. 4 is a schematic diagram of still another embodiment of a fuel cell of the invention, having a tubular design. - The foregoing will be apparent from the following more particular description of example embodiments of the invention, as illustrated in the accompanying drawings in which like reference characters refer to the same parts throughout the different views. The drawing is not necessarily to scale, emphasis instead being placed upon illustrating embodiments of the present invention.
-
FIG. 1 showsfuel cell 10 of the invention.Fuel cell 10 includes a plurality ofsub-cells 12. Eachsub-cell 12 includesfirst electrode 14 andsecond electrode 16. Typically, first andsecond electrodes fuel cell 10,first electrode 14 at least in part defines a plurality offirst gas channels 18 in fluid communication with a source of oxygen gas, such as air.Second electrode 16 at least in part defines a plurality ofsecond gas channels 20 in fluid communication with a fuel gas source, such as H2 gas or a natural gas which can be converted into H2 in situ atsecond electrode 16. - Although, in
FIG. 1 ,first electrodes 14 andsecond electrodes 16 define a plurality ofgas channels FIG. 2 ,first gas channel 18 is defined at least in part byfirst electrode 14 and by at least in part by interconnect 24, andsecond gas channel 20 is defined at least in part bysecond electrode 16 and by at least in part by interconnect 24. - Any suitable cathode materials known in the art can be used for
first electrode 14, for example, in “High Temperature Solid Oxide Fuel Cells: Fundamentals, Design and Applications,” pp. 119-143, Dinghal, et al. Ed., Elsevier Ltd. (2003), the entire teachings of which are incorporated herein by reference. In one embodiment,first electrode 14 includes a La-manganate (e.g, La1-aMnO3, where a is equal to or greater than zero, and equal to or less than 0.1) or La-ferrite based material. Typically, the La-manganate or La-ferrite based material is doped with one or more suitable dopants, such as Sr, Ca, Ba, Mg, Ni, Co or Fe. Examples of doped La-manganate based materials include LaSr-manganates (LSM) (e.g., La1-kSrkMnO3, where k is equal to or greater than 0.1, and equal to or less than 0.3, (La+Sr)/Mn is in a range of between about 1.0 and about 0.95 (molar ratio)) and LaCa-manganates (e.g., La1-kCakMnO3, k is equal to or greater than 0.1, and equal to or less than 0.3, (La+Ca)/Mn is in a range of between about 1.0 and about 0.95 (molar ratio)). Examples of doped La-ferrite based materials include LaSrCo-ferrite (LSCF) (e.g. La1-qSrqCo1-jFejO3, where each of q and j independently is equal to or greater than 0.1, and equal to or less than 0.4, (La+Sr)/(Fe+Co) is in a range of between about 1.0 and about 0.95 (molar ratio)). In one specific embodiment,first electrode 14 includes at least one of a LaSr-manganate (LSM) (e.g., La1-kSrkMnO3) and a LaSrCo-ferrite (LSCF). Common examples include (La0.8Sr0.2)0.98MnO 3+δ (δ is equal to or greater than zero, and equal to or less than 0.3) and La0.6Sr0.4Co0.2Fe0.8O3. - Any suitable anode materials known in the art can be used for
second electrode 16, for example, in “High Temperature Solid Oxide Fuel Cells: Fundamentals, Design and Applications,” pp. 149-169, Dinghal, et al. Ed., Elsevier Ltd. (2003), the entire teachings of which are incorporated herein by reference. In one embodiment,second electrode 16 includes a nickel (Ni) cermet. As used herein, the phrase “Ni cermet” means a ceramic metal composite that includes Ni, such as about 20 wt %-70 wt % of Ni. Examples of Ni cermets are materials that include Ni and yttria-stabilized zirconia (YSZ), such as ZrO2 containing about 15 wt % of Y2O3, and materials that include Ni and Y-zirconia or Sc-zirconia. An additional example of an anode material is Cu-cerium oxide. A specific example of an Ni cermet includes 67 wt % Ni and 33 wt % YSZ. - Typically, the thickness of each of first and
second electrodes second electrodes -
Solid electrolyte 22 is betweenfirst electrode 14 andsecond electrode 16. Any suitable solid electrolytes known in the art can be used in the invention, such as those described, in “High Temperature Solid Oxide Fuel Cells: Fundamentals, Design and Applications,” pp. 83-112, Dinghal, et al. Ed., Elsevier Ltd. (2003), the entire teachings of which are incorporated herein by reference. Examples include ZrO2 based materials, such as Sc2O3-doped ZrO2, Y2O3-doped ZrO2, and Yb2O3-doped ZrO2; CeO2 based materials, such as Sm2O3-doped CeO2, Gd2O3-doped CeO2, Y2O3-doped CeO2 and CaO-doped CeO2; Ln-gallate based materials (Ln=a lanthanide, such as La, Pr, Nd or Sm), such as LaGaO3 doped with Ca, Sr, Ba, Mg, Co, Ni, Fe or a mixture thereof (e.g., La0.8Sr0.2Ga0..8Mg0.2O3, La0.8Sr0.2Ga0.8Mg0.5Co0.05O3, La0.9Sr0.1Ga0.8Mg0.2O3, LaSrGaO4, LaSrGa3O7 or La0.9A0.1Ga3 where A=Sr, Ca or Ba); and mixtures thereof. Other examples include doped yttrium-zirconate (e.g., YZr2O7), doped gadolinium-titanate (e.g., Gd2Ti2O7) and brownmillerites (e.g., Ba2In2O6 or Ba2In2O5). In a specific embodiment,electrolyte 22 includes ZrO2 doped with 8 mol % Y2O3 (i.e., 8 mol % Y2O3-doped ZrO2.) - Typically, the thickness of
solid electrolyte 22 is in a range of between about 5 μm and about 20 μm, such as between about 5 μm and about 10 μm. Alternatively, the thickness ofsolid electrolyte 22 is thicker than about 100 μm (e.g., between about 100 μm and about 500 100 μm). In this embodiment employingsolid electrolyte 22 having a thickness greater than about 100 μm,solid electrolyte 22 can provide structural support forfuel cell 10. -
Fuel cell 10 further includesinterconnect 24 betweencells 12. Referring toFIG. 1 , in one embodiment,interconnect 24 hasfirst surface 26 in contact withfirst electrode 14, andsecond surface 28 in contact withsecond electrode 16.Interconnect 24 consists essentially of a doped M-titanate based perovskite, wherein M is an alkaline earth metal. As used herein, the phrase “consists essentially of” means thatinterconnect 24 does not include any other metal oxides that may substantially affect the property ofinterconnect 24. Examples of suitable dopant materials include La, Y, Nb, Mn, V, Cr, W, Mo, Si, Sr, Ca, Mg, Ni, Co, V and Ti. In a specific embodiment, the M-titanate based perovskite is Sr-titante (e.g., SrTiO3), Ca-titanate (e.g., CaTiO3), Ba-titanate (e.g., BaTiO3), or Mg-titanate (e.g., MgTiO3). In another specific embodiment, the M-titanate based perovskite is n-doped, such as n-doped Sr-titanate or n-doped Ca-titanate. In yet another specific embodiment, the M-titanate based perovskite is a Sr-titanate doped with at least one dopant selected from the group consisting of La, Y, Nb, Mn, V, Cr, W, Mo and Si. - In another embodiment, as shown in
FIG. 2 ,interconnect 24 includesfirst layer 36 in contact withfirst electrode 14, andsecond layer 38 in contact withsecond electrode 16.First layer 36 includes an electrically conductive material selected from a metal, a metal alloy and a mixture thereof. Examples of the electrically conductive materials suitable forfirst layer 36 include Cr-based alloys, ferritic steels, Ni-based super alloys and Ni—Fe—Y2O3 alloys.Second layer 38 includes a doped M-titanate based perovskite, wherein M is an alkaline earth metal. Preferably, the material included insecond layer 38 is n-doped. Examples of suitable dopant materials include La, Y, Nb, Mn, V, Cr, W, Mo, Si, Sr, Ca, Mg, Ni, Co, V and Ti. Suitable n-dopants include La, Y, Nb, Mn, V, Cr, W, Mo and Si. In a specific embodiment, the M-titanate based perovskite is Sr-titante (e.g., SrTiO3), Ca-titanate (e.g., CaTiO3), Ba-titanate (e.g., BaTiO3), or Mg-titanate (e.g., MgTiO3). In another specific embodiment, the M-titanate based perovskite is n-doped, such as n-doped Sr-titanate or n-doped Ca-titanate. In yet another specific embodiment, the M-titanate based perovskite is a Sr-titanate doped with at least one dopant selected from the group consisting of La, Y, Nb, Mn, V, Cr, W, Mo and Si. - M-titanate based perovskite has the perovskite structure known in the art, for example, in “High Temperature Solid Oxide Fuel Cells: Fundamentals, Design and Applications,” pp. 120-123, Dinghal, et al. Ed., Elsevier Ltd. (2003), the entire teachings of which are incorporated herein by reference. The perovskite structure is adopted by many oxides that have the chemical formula ABO3. The general crystal structure is a primitive cube with the A-cation in the center of a unit cell, the B-cation at the comers of the unit cell, and the anion (i.e., O2−) at the centers of each edge of the unit cell. The idealized structure is a primitive cube, but differences in ratio between the A and B cations can cause a number of different so-called distortions, of which tilting is the most common one. As used herein, the phrase “M-titanate based perovskite” also includes such distortions. In the “M-titanate based perovskites,” M atoms generally occupy the A-cation sites, while Ti atoms generally occupy the B-cation sites.
-
Interconnect 24 can be in any shape, such as a planar shape (seeFIGS. 1 and 2 ) or a microstructured (e.g., grooved) shape (seeFIG. 3 ). In one specific embodiment, at least oneinterconnect 24 offuel cell 10 is substantially planar. - In one embodiment, the thickness of
interconnect 24 is in a range of between about 10 μm and about 1,000 μm. Alternatively, the thickness ofinterconnect 24 is in a range of between about 0.005 mm and about 2.0 mm. In one specific embodiment, the thickness ofinterconnect 24 is in a range of 10 μm and about 500 μm. In another embodiment, the thickness ofinterconnect 24 is in a range of 10 μm and about 200 μm. In yet another embodiment, the thickness ofinterconnect 24 is between about 10 μm and about 100 μm. In yet another embodiment, the thickness ofinterconnect 24 is between about 10 μm and about 75 μm. In yet another embodiment, the thickness ofinterconnect 24 is between about 15 μm and about 65 μm. - In one specific embodiment,
first electrode 14 and/orsecond electrode 16 has a thickness of between about 0.5 mm and about 2 mm thick, more specifically between about 1 mm and about 2 mm thick; andinterconnect 24 has a thickness of between about 10 μm and about 200 μm, specifically between about 10 μm and about 200 μm, and more specifically between about 10 μm and about 100 μm. - In another specific embodiment,
second layer 28 includes a SrLa-titanate based perovskite described above; andinterconnect 24 has a thickness of between about 10 μm and about 100 μm, specifically between about 10 μm and about 75 μm, and more specifically between about 15 μm and about 65 μm. - In yet another specific embodiment, at least one
cell 12 includes porous first andsecond electrodes solid electrolyte 22 has a thickness of between about 5 μm and about 20 μm; andinterconnect 24 is substantially planar and has a thickness of between about 10 μm and about 200 μm. - In yet another specific embodiment,
interconnect 24 is substantially planar; each of first andsecond electrodes first electrode 14 includes a La-manganate or La-ferrite based material (e.g., La1-kSrkMnO3 or La1-qSrqCojFe1-jO3, wherein values of each of k, l and j independently are as described above), andsecond electrode 16 includes a Ni cermet (e.g., 67 wt % Ni and 33 wt % YSZ). In one aspect of this specific embodiment,electrolyte 22 includes 8 mol % Y2O3-doped ZrO2. - In yet another specific embodiment,
first electrode 14 includes (La0.8Sr0.2)0.98MnO 3+δ or La0.6Sr0.4Co0.2Fe0.8O3; andsecond electrode 16 includes 67 wt % Ni and 33 wt % YSZ. In this embodiment, specifically,electrolyte 22 includes 8 mol % Y2O3-doped ZrO2. -
Fuel cell 10 of the invention can include any suitable number of a plurality ofsub-cells 12. In one embodiment,fuel cell 10 of the invention includes at least 30-50 sub-cells 12. Sub-cells 12 offuel cell 10 can be connected in series or in parallel. - A fuel cell of the invention can be a planar stacked fuel cell, as shown in
FIG. 3 . Alternatively, as shown inFIG. 4 , a fuel cell of the invention can be a tubular fuel cell. Fuel cells shown inFIGS. 3 and 4 independently have the characteristics, including specific variables, as described forfuel cell 10 shown inFIGS. 1 and 2 (for clarity, details of cell components are not depicted inFIGS. 3 and 4 ). Typically, in the planar design, as shown inFIG. 3 , the components are assembled in flat stacks, with air and fuel flowing through channels built into the interconnect. Typically, in the tubular design, as shown inFIG. 4 , the components are assembled in the form of a hollow tube, with the cell constructed in layers around a tubular cathode; air flows through the inside of the tube and fuel flows around the exterior. - The invention also includes a method of forming fuel cells as described above. The method includes forming a plurality of sub-cells 12 as described above, and connecting each sub-cell 12 with
interconnect 24. Fabrication of sub-cells 12 andinterconnect 24 can employ any suitable techniques known in the art, for example, in “High Temperature Solid Oxide Fuel Cells: Fundamentals, Design and Applications,” pp. 83-225, Dinghal, et al. Ed., Elsevier Ltd. (2003), the entire teachings of which are incorporated herein by reference. For example, planar stacked fuel cells of the invention can be fabricated by particulate processes or deposition processes. Tubular fuel cells of the invention can be fabricated by having the cell components in the form of thin layers on a porous cylindrical tube, such as calcia-stabilized zirconia. - Typically, a suitable particulate process, such as tape casting or tape calendering, involves compaction of powders, such as ceramic powders, into fuel cell components (e.g., electrodes, electrolytes and interconnects) and densification at elevated temperatures. For example, suitable powder materials for electrolytes, electrodes or interconnects of the invention, are made by solid state reaction of constituent oxides. Suitable high surface area powders can be precipitated from nitrate and other solutions as a gel product, which are dried, calcined and comminuted to give crystalline particles. The deposition processes can involve formation of cell components on a support by a suitable chemical or physical process. Examples of the deposition include chemical vapor deposition, plasma spraying and spray pyrolysis.
- In one specific embodiment,
interconnect 24 consists essentially of a doped M-titanate based perovskite, and is prepared by disposing a material of a doped M-titanate based perovskite over eitherelectrode interconnect 24. Generally, the material of a doped M-titanate based perovskite is disposed at a temperature in a range of between about 50° C. and about 80° C. with a loading of between about 5 and about 50 tons. Generally, the material of a doped M-titanate based perovskite is sintered to forminterconnect 24 having a high theoretical density (e.g., greater than about 90% theoretical density, or greater than about 95% theoretical density). - In another specific embodiment,
interconnect 24 includesfirst layer 36 andsecond layer 38, and is formed by depositing an electrically conductive material overelectrode 14 using any suitable deposition method known in the art, such as chemical vapor deposition to fromfirst layer 36, and disposing a material of a doped M-titanate based perovskite overfirst layer 36. Generally, the material of a doped M-titanate based perovskite is disposed at a temperature in a range of between about 50° C. and about 80° C. with a loading of between about 5 and about 50 tons. Generally, the material of a doped M-titanate based perovskite is sintered to forminterconnect 24 having a high theoretical density (e.g., greater than about 90% theoretical density, or greater than about 95% theoretical density). - The SOFCs of the invention can be portable. Also, the SOFCs of the invention, can be employed as a source of electricity in homes, for example, to generate hot water.
- While this invention has been particularly shown and described with references to example embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the scope of the invention encompassed by the appended claims.
Claims (34)
1. A solid oxide fuel cell, comprising;
a) a plurality of sub-cells, each sub-cell including:
i) a first electrode in fluid communication with a source of oxygen gas;
ii) a second electrode in fluid communication with a source of a fuel gas; and
iii) a solid electrolyte between the first electrode and the second electrode; and
b) an interconnect between the sub-cells, the interconnect having a first surface in contact with the first electrode of each sub-cell and a second surface that is in contact with the second electrode of each sub-cell, the interconnect consisting essentially of a doped M-titanate based perovskite, wherein M is an alkaline earth metal.
2. The solid oxide fuel cell of claim 1 , wherein each sub-cell further includes a first gas channel in fluid communication with the oxygen gas source and with the first electrode, and a second gas channel in fluid communication with the fuel gas source and with the second electrode.
3. The solid oxide fuel cell of claim 2 , wherein the first electrode at least in part defines the first gas channel, and the second electrode at least in part defines the second gas channel.
4. The solid oxide fuel cell of claim 1 , wherein each of the first and second electrodes is porous.
5. The solid oxide fuel cell of claim 4 , wherein the interconnect is substantially planar.
6. The solid oxide fuel cell of claim 1 , wherein the M-titanate based perovskite is selected from the group consisting of Sr-titanate, Ca-titanate, Ba-titanate and Mg-titanate.
7. The solid oxide fuel cell of claim 6 , wherein the interconnect includes an n-doped Sr-titanate or n-doped Ca-titanate.
8. The solid oxide fuel cell of claim 7 , wherein the interconnect includes a Sr-titanate doped with at least one dopant selected from the group consisting of La, Y, Nb, Mn, V, Cr, W, Mo and Si.
9. The solid oxide fuel cell of claim 1 , wherein the solid electrolyte includes at least one material selected from the group consisting of ZrO2 based material, CeO2 based material and lanthanide-gallate based material.
10. The solid oxide fuel cell of claim 1 , wherein the first electrode includes a La-manganate based material.
11. The solid oxide fuel cell of claim 1 , wherein the second electrode includes a nickel cermet.
12. The solid oxide fuel cell of claim 1 , wherein the thickness of each of the first and second electrodes of at least one of the cells is in a range of between about 1 mm and about 2 mm.
13. The solid oxide fuel cell of claim 12 , wherein the thickness of the interconnect is in a range of between about 10 μm and about 1,000 μm.
14. The solid oxide fuel cell of claim 13 , wherein the thickness of the interconnect is in a range of between about 10 μm and about 200 μm.
15. The solid oxide fuel cell of claim 14 , wherein the thickness of the interconnect is in a range of between about 50 μm and about 200 μm.
16. The solid oxide fuel cell of claim 1 , wherein the cells are connected with each other in series.
17. A method of forming a solid oxide fuel cell cell that includes a plurality of sub-cells, comprising the step of connecting each of the sub-cells with an interconnect, wherein each sub-cell includes:
i) a first electrode in fluid communication with a source of oxygen gas,
ii) a second electrode in fluid communication with a source of a fuel gas, and
iii) a solid electrolyte between the first electrode and the second electrode, and
wherein the interconnect consists essentially of a doped M-titanate based perovskite, wherein M is an alkaline earth metal, the interconnect having a first surface in contact with the first electrode of each cell and a second surface that is in contact with the second electrode of each sub-cell.
18. A solid oxide fuel cell, comprising;
a) a plurality of sub-cells, each sub-cell including:
i) a first electrode in fluid communication with a source of oxygen gas;
ii) a second electrode in fluid communication with a source of a fuel gas; and
iii) a solid electrolyte between the first electrode and the second electrode; and
b) an interconnect between the sub-cells, the interconnect including:
i) a first layer that includes an electrically conductive material selected from the group consisting of a metal, a metal alloy and a mixture of metals, wherein the first layer is in contact with the first electrode of each sub-cell; and
ii) a second layer that includes a doped M-titanate based perovskite, wherein M is an alkaline earth metal, and wherein the second layer is in contact with the second electrode of each sub-cell.
19. The solid oxide fuel cell of claim 18 , wherein each sub-cell further includes a first gas channel in fluid communication with the oxygen gas source, and a second gas channel in fluid communication with the fuel gas source.
20. The solid oxide fuel cell of claim 19 , wherein the first electrode at least in part defines the first gas channel, and the second electrode at least in part defines the second gas channel.
21. The solid oxide fuel cell of claim 18 , wherein each of the first and second electrodes is porous.
22. The solid oxide fuel cell of claim 21 , wherein the interconnect is substantially planar.
23. The solid oxide fuel cell of claim 18 , wherein the doped M-titanate based perovskite is selected from the group consisting of a doped Sr-titanate, a doped Ca-titanate, a doped Ba-titanate and a doped Mg-titanate.
24. The solid oxide fuel cell of claim 23 , wherein the doped M-titanate based perovskite includes an n-doped Sr-titanate or n-doped Ca-titanate.
25. The solid oxide fuel cell of claim 24 , wherein the doped M-titanate based perovskite includes a Sr-titanate doped with at least one dopant selected from the group consisting of La, Y, Nb, Mn, V, Cr, W, Mo and Si.
26. The solid oxide fuel cell of claim 18 , wherein the solid electrolyte includes at least one material selected from the group consisting of ZrO2 based material, CeO2 based material and lanthanide-gallate based material.
27. The solid oxide fuel cell of claim 18 , wherein the first electrode includes a La-manganate based material.
28. The solid oxide fuel cell of claim 18 , wherein the second electrode includes a Ni cermet.
29. The solid oxide fuel cell of claim 18 , wherein the first layer of the interconnect includes at least one material selected from the group consisting of Cr-based alloys, ferritic steels, Ni-based super alloys and Ni—Fe—Y2O3 alloy.
30. The solid oxide fuel cell of claim 18 , wherein the thickness of each of the first and second electrodes of at least one of the cells is in a range of between about 1 mm and about 2 mm.
31. The solid oxide fuel cell of claim 30 , wherein the thickness of the interconnect is in a range of between about 10 μm and about 1,000 μm.
32. The solid oxide fuel cell of claim 31 , wherein the thickness of the interconnect is in a range of between about 10 μm and about 200 μm.
33. The solid oxide fuel cell of claim 32 , wherein the thickness of the interconnect is in a range of between about 50 μm and about 200 μm.
34. A method of forming a solid oxide fuel cell that includes a plurality of sub-cells, comprising the step of connecting each of the sub-cells with an interconnect, wherein each sub-cell includes:
i) a first electrode in fluid communication with a source of oxygen gas,
ii) a second electrode in fluid communication with a source of a fuel gas, and
iii) a solid electrolyte between the first electrode and the second electrode, and
wherein the interconnect includes:
i) a first layer of an electrically conductive metal, a metal alloy or a mixture of metals, wherein the first layer is in contact with the first electrode of each cell; and
ii) a second layer that includes a doped M-titanate based perovskite, wherein M is an alkaline earth metal, and wherein the second layer is in contact with the second electrode of each sub-cell.