US20090149284A1 - Hockey Stick Blade Having Fiber-Reinforced High Density Foam Core - Google Patents
Hockey Stick Blade Having Fiber-Reinforced High Density Foam Core Download PDFInfo
- Publication number
- US20090149284A1 US20090149284A1 US11/954,014 US95401407A US2009149284A1 US 20090149284 A1 US20090149284 A1 US 20090149284A1 US 95401407 A US95401407 A US 95401407A US 2009149284 A1 US2009149284 A1 US 2009149284A1
- Authority
- US
- United States
- Prior art keywords
- high density
- foam core
- plies
- fiber
- blade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A composite hockey stick blade including a fiber reinforced, high-density foam polymeric core material overlaid with a plastic wrap. The fiber reinforcement material, in the form of a plurality of milled or long fibers, provides increased toughness and stiffness of the high density polymeric foam core material. The hockey stick blade may be utilized as a replacement blade for a two-piece hockey stick, or may be a portion of a one-piece hockey stick.
Description
- The present invention relates generally to a hockey stick blade and, more particularly to, a hockey stick blade having a fiber reinforced high density foam core.
- Typical current hockey stick blades or replacement blades are generally made of a core material reinforced with one or more layers of synthetic material, such as fiberglass, carbon fiber or graphite. Traditionally, the core of the blade has been made of natural materials, such as wood or a wood laminate. Traditional wood constructions, however, are expensive to manufacture due to the cost of wood and the manufacturing processes employed. Further, wood sticks and blades are relatively heavy and have somewhat limited durability. Finally, due to variabilities relating to wood construction and manufacturing techniques, wood sticks are difficult to manufacture with consistent tolerances, and even the same model and brand of sticks and blades may have differences in terms of mechanical properties, such as stiffness and curvature.
- Recently, in an attempt to decrease the weight of the stick and blade, and to improve upon the durability and mechanical properties associated with the performance of the stick or blade, alternative core materials, such as synthetic materials reinforced with layers of fiber material, have been utilized. The fiber layers are usually made of woven filament fibers, typically soaked in a resin and glued to the surfaces of the core of the blade. Expandable fiber braids have also been used for covering the core of the blade. These composite sticks and blades have proven to have improved durability versus traditional wooden sticks and blades and have many of the mechanical attributes desired by hockey players. Further, these composite sticks and blades have less variability in terms of tolerances related to curvature and stiffness.
- Nevertheless, these sticks and blades still have disadvantages. For example, conventional foam core materials form blades are formed of polymeric materials that are limited in strength and durability by a combination of factors, including the type and density of the polymeric material forming the foam core, the thickness of the foam core, and the amount of curing of the foam core during processing.
- Accordingly, there is a demand for a composite blade having improved strength and durability, and hence improved playability characteristics, that utilizes conventional polymeric foam core materials and conventional forming techniques. These playability characteristics include improved response while handling and/or shooting a puck, the prevention of puck “flutter” that may occur when a player shoots or passes the puck, and the twisting of the blade as a puck is passed or shot.
- It is therefore an advantage of the present invention to provide a composite blade for a hockey stick with improved response while handling and/or shooting a puck.
- It is another advantage of the present invention to provide a composite blade for a hockey stick that assists in preventing puck “flutter” that may occur when a player shoots or passes the puck.
- It is a related advantage of the present invention to provide a composite blade for a hockey stick that minimizes twisting of the blade.
- It is still another advantage of the present invention to provide a composite blade for a hockey stick that has decreased weight without adversely affecting the performance or mechanical characteristics of the blade.
- In accordance with the above and the other advantages, the present invention provides a composite hockey stick blade having a high density foam core paddle coupled overlaid with, or coupled within, a plastic wrap. In addition, reinforcing materials such as chopped fibers are introduced to the high density foam core material to increase the toughness and durability of the blade to better withstand the rigors of play. The presence of the high density foam and fiber reinforcement allows the thickness of the plastic wrap to be decreased along the front face and rear face of the paddle while maintaining the desired performance and mechanical characteristics of the blade. The result is a durable, stiff, and light blade that can be formed as a part of a hockey stick or as a separate replacement blade for a hockey stick.
- These and other features and advantages of the present invention will become apparent from the following description of the invention, when viewed in accordance with the accompanying drawings and appended claims.
-
FIG. 1 is a view of the backside face of a blade according to one embodiment of the present invention; -
FIG. 2 is a cross-sectional view of a portion the blade ofFIG. 1 in the direction of arrows 2-2; and -
FIG. 3 is a cross-sectional view of a two-piece mold used to form the blades ofFIGS. 1-2 in accordance with one embodiment of the present invention. - Referring now to the
FIGS. 1-2 , ahockey blade 10 is depicted in accordance with a preferred embodiment of the present invention. It should be understood that while the preferred blade is intended for use in the sport of ice hockey, it can also be utilized in other sports, including roller hockey and field hockey. In general, theblade 10 comprises ahosel 12, aheel section 14, and a paddle (blade portion) 16. Theheel section 14 is located at the junction of thehosel 12 and thepaddle 16. Thehosel 12 includes atenon 18, or insert, adapted to be inserted into a hollow hockey stick shaft (not shown) made of aluminum, composite or graphite. It will be understood that the hockey stick shaft can be made of a variety of other materials, including but not limited to wood or wood laminate. Thepaddle 16 includes afront face 20 and arear face 22 and further comprises atop edge 24, atip region 26 and abottom edge 28. - The
blade 10, as shown inFIG. 2 , is preferably formed as a composite structure having aninner foam core 100 overlaid with, or sandwiched within, with aplastic wrap 101. Thehosel 12 andtenon 18 are preferably formed having one or more layers of the plastic wrap (shown as a plurality of plies 197 inFIG. 3 ) that are wrapped around a hollow cavity and may include an inner foam core (shown as 199 inFIGS. 1 and 3 ). - The
inner foam core 100 and foam core 199 (when present) are constructed of formulations of syntactic foam or non-syntactic polymeric foam, with syntactic foams preferred. A syntactic foam is formed by filling a polymeric matrix material with hollow particles called microballoons. The presence of microballoons results in lower density, higher strength, and lower thermal expansion coefficient core materials, which is desirable for hockey stick blades. The microballoons used in the present invention are typically glass microballoons or polymeric microballoons such as polypropylene microballoons. - The polymeric matrix material used in the
inner foam core blade 10. However, other polymeric materials, or blends of polymeric materials, or different forms of the general polymeric composition, and having one or more of these characteristics, is specifically contemplated by the present invention. - Chopped reinforcing
fibers 167, in the form of long or short (milled) fibers, are also preferably introduced to theinner foam core 100 and/or thefoam core section 199 to provide additional durability and/or stiffness torespective core fibers 167 that may be used include carbon fiber, graphite fiber, aramid fiber, glass fiber, polyethylene fiber, ceramic fiber, boron fiber, quartz fiber, polyester fiber or any other fiber that may provide the additional desired strength to theblade 10. - In one preferred embodiment, milled carbon fiber is introduced at a ratio of about 5% by weight of a non-expandable, syntactic high-density epoxy foam
inner foam core 100 or thefoam core section 199. In yet a more preferred embodiment, milled carbon fiber ( 1/32″) is introduced at a load of 1.7% by weight of the syntactic, non-expandable high density epoxy (greater than about 30 pounds per cubic foot and 0.55 SG)inner foam core 100 and/or thefoam core section 199. - The
plastic wrap 101 is preferably a fiber-reinforced prepreg material that includes one ormore layers 102 comprising one ormore plies 104 of substantiallycontinuous fibers 106 disposed in a matrix or resin basedmaterial 108. - Separate reinforcing
layers 110 of the same type and quantity asplies 104 may be placed on thetop edge 24 and thebottom edge 28 of theblade 10. It will be understood that theblade 10 may be formed as a replacement blade, i.e. separate from the shaft, or may alternatively be formed as a single integral unit with the shaft. Moreover, it will be understood that theinner foam core 100 may be reinforced with materials other thanplastic wrap 101 in other ways well known to those of ordinary skill in the art and is not meant to be limited to the preferred embodiment. - The
fibers 106 employed inplies 104, 197 may be comprised of carbon fiber, graphite fiber, aramid fiber, glass fiber, polyethylene fiber, ceramic fiber, boron fiber, quartz fiber, polyester fiber or any other fiber that may provide the desired strength. In addition, fiber may also be added to theoutermost ply 104, 197 to form a decorative appearance. For example, a graphite fiber outer ply preferably constitutes theoutermost ply 104 of thepaddle 16 to provide an aesthetically pleasing appearance. - The matrix or resin based
material 108 is preferably selected from a group of resin based materials, including thermoplastic materials such as polyetheretherketone (“PEEK”), polyphenylene sulfide (“PPS”), polyethylene (“PE”), polypropylene urethanes (“PPU”), and nylons such as Nylon-6. The matrix or resin basedmaterial 108 may also include or be entirely composed of a thermosetting material, such as urethanes, epoxy, vinyl ester, polycyanate, and polyester. - In order to avoid manufacturing expenses relating to transferring the resin into the mold after the foam-fiber layers are inserted into the mold, the
matrix material 108 employed is preferably pre-impregnated into theplies 104 prior to the uncured blade assembly being inserted into the mold and the mold being sealed. In addition, in order to avoid costs associated with the woven sleeve materials employed in contemporary composite blade constructs, it is preferable that the layers be comprised of one ormore plies 104 of non-woven unidirectional fibers. Suitable materials include unidirectional carbon fiber tape pre-impregnated with epoxy, unidirectional glass fiber tape pre-impregnated with epoxy, and unidirectional aramid fiber tape pre-impregnated with epoxy. - As used herein the term “ply” 104 shall mean a group of fibers which all run in a single direction, largely parallel to one another, and which may or may not be interwoven with or stitched to one or more other groups of fibers each of which may be or may not be disposed in a different direction. A “layer” 102 shall mean one or
more plies 104 that are laid down together. - The composition of the substantially
continuous fibers 106, and/or the composition of the matrix or resin basedmaterial 108, of eachindividual ply 104 may be similar or varied in composition to their respectiveadjacent ply 104. Moreover, the fiber orientation of thecontinuous fibers 106 within an individual ply may be the same, or varied, from the orientation of the immediatelyadjacent ply 104. For example, the fiber orientation of adjacent plies may be parallel to one another (i.e. the fibers are oriented at a 0 degree angle relative to the next adjacent ply, forming a 0/0 orientation), perpendicular to one another (i.e. the fibers are oriented at a 90 degree angle relative to the next ply, forming a 0/90 pattern), or may be oriented at an angle between 0 and 90 degrees (for example, at a 30 degree, or 60 degree, angle relative to the adjacent ply). In these ways, the performance characteristics of hockey blade, in terms of relative stiffness and relative durability, may be varied from blade to blade, and hence stick to stick. - Referring now to
FIG. 3 , one preferred method for forming theblade 10 as described above inFIGS. 1-2 is illustrated. - First, a
mold 175, corresponding to the shape of theblade 10, is formed having aninner surface 180 in the form of afront surface 177, arear surface 179, a top surface 181, and abottom surface 183 that define acavity 185 corresponding to the outer periphery of thefront face 20, therear face 22, thetop edge 24 and thebottom edge 28. Themold 175 also includes aninner surface 187 corresponding to the outer periphery of thehosel 12, and therein defines asecond cavity portion 189 that is preferably open and continuous with thecavity 185. The mold preferably consists of two ormore mold pieces cavities blade 10. - Next, one or
more plies 104 of aplastic wrap 101, here pre-impregnated substantially continuous fibers comprising eachrespective face blade 10, are placed into themold 175 along thefront surface 177 and therear surface 179. As stated above, a graphite fiber outermost ply is preferably introduced along thefront surface 177 and rear surface to provide an aesthetically pleasing outer appearance. In addition, one or more plies 197 of the pre-impregnated substantially continuous fibers are placed onto theouter surface 187 of the hosel region within thecavity region 189. - A long strip of
reinforcement 110 is placed onto thebottom surface 183 of the mold and also encloses theplies 104. Thereinforcement 110 preferably consists of one or more plies of the pre-impregnated substantially continuous fibers of similar composition to plies 104 and 197. - An inner
foam core material 100 is then introduced within theplies 104 within thefirst cavity region 185 and optionally within the plies 197 of thesecond cavity region 189. Finally, a second strip of thereinforcement 110 is draped over theinner foam core 100 and plies 104 and will couple to the top surface 181 of themold 175. - Last, the
plies 104 for theother face blade 10 are added or wrapped over afoam core 100 that is generally in the shape of theblade 10 illustrated inFIGS. 1 and 2 to create an uncured blade assembly. - The
mold 175 is closed using an automated press or tightened down by hand using bolts (not shown). Heat is then applied to themold 175 sufficient to cure theinner foam core 100, thefoam core 199 and the prepreg materials comprising theplies plies inner foam core foam core foam core - For one preferred core material, namely a syntactic, non-expandable epoxy foam core material having a density of about 30 pounds per cubic foot (0.55 SG), the core is cured at about 150 degrees Celsius (about 300 degrees Fahrenheit) for twenty minutes.
- When the mold cycle is complete, the
blade 10 is then removed from themold 175. For ablade 10 havingnon-expanding foam core blade 10 may be removed immediately. For a blade having an expandingfoam core blade 10 is first cooled below its curing and foam expansion temperature prior to removal from themold 175. - After removal, the
blade 10 is finished to a desired outer appearance. The finishing process may include aesthetic aspects such as paint or polishing and also may include structural modifications such as deburring. - The use of a high-density, fiber reinforced
inner foam core 100 in theblade 10 allows theplastic wrap 101 thickness of thepaddle 16, along thefront face 20 andrear face 22, to be decreased to between about 0.045 and 0.030 inches. The reduction in thickness of theplastic wrap 101 along thefront face 20 andrear face 22 forms alighter blade 10 that provides better impact capabilities, better flex loading and forgiveness without sacrificing strength or durability, over current composite blades having lower density foam cores and a plastic wrap thickness of around 0.060 inches. - While particular embodiments of the invention have been shown and described, numerous variations or alternate embodiments will occur to those skilled in the art. Accordingly, it is intended that the invention be limited only in terms of the appended claims.
Claims (11)
1-12. (canceled)
13. A method for forming a composite hockey stick blade having a hosel, a heel section, and a paddle portion, the method comprising:
providing a multi-piece mold having an inner cavity defined therewithin, said inner cavity shaped to correspond in size and shape to the composite hockey stick blade;
coupling one or more plies of a plastic wrap along a front surface and a rear surface of said inner cavity, said front surface corresponding to a front face of the paddle portion and said rear surface corresponding to a rear face of the paddle portion;
coupling one or more strips of reinforcement along a bottom surface of said inner cavity, said bottom surface corresponding to a bottom edge of the paddle portion;
coupling a fiber reinforced high density polymeric foam core section onto said innermost one of said one or more strips of reinforcement between said one or more plies along said front surface and said one or more plies on said rear surface;
coupling at least one ply of said plastic wrap onto a top surface of said fiber reinforced high density polymeric foam core section;
closing said multi-piece mold such that said fiber reinforced high density polymeric foam core section contacts one said plies of plastic wrap along said front surface and said rear surface, said fiber reinforced high density polymeric foam core section also contacting one of said one or more strips of reinforcement along said bottom edge and further contacting one of said at least one ply along said top surface;
applying heat and pressure within said multi-piece mold for a period of time sufficient to cure said fiber reinforced high density polymeric foam core section, said one or more plies of said plastic wrap, and said one or more plies of said reinforcement;
opening said multi-piece mold; and
removing the composite hockey stick blade.
14. The method of claim 13 , wherein said fiber reinforced high density polymeric foam core section comprises a high density epoxy foam and a plurality of chopped fiber.
15. The method of claim 14 , wherein said plurality of chopped fibers comprises a plurality of milled fibers.
16. The method of claim 14 , wherein said plurality of chopped fibers comprises a plurality of long fibers.
17. The method of claim 14 , wherein said plurality of milled fibers comprises between about 0 and 5 weight percent of said fiber reinforced high density polymeric foam core section.
18. The method of claim 13 , wherein said fiber reinforced high density polymeric foam core section comprises a high density, non-expanding epoxy foam and a plurality of chopped fiber.
19. The method of claim 13 , wherein said fiber reinforced high density polymeric foam core section comprises a high density expanding foam and a plurality of chopped fiber.
20. The method of claim 13 , further comprising:
providing a second cavity portion within said multi-piece mold that is open and continuous with said inner cavity, said second cavity portion corresponding to a hosel region of the composite hockey stick blade;
coupling one or more plies of said plastic wrap to each of the outer surfaces of said second cavity portion; and
optionally inserting a silicone plug within said one or more plies of said plastic wrap with said second cavity portion.
21. The method of claim 20 further comprising:
coupling a foam core section within said second cavity portion.
22-23. (canceled)