US20090137123A1 - Polishing Composition and Polishing Method - Google Patents
Polishing Composition and Polishing Method Download PDFInfo
- Publication number
- US20090137123A1 US20090137123A1 US12/360,557 US36055709A US2009137123A1 US 20090137123 A1 US20090137123 A1 US 20090137123A1 US 36055709 A US36055709 A US 36055709A US 2009137123 A1 US2009137123 A1 US 2009137123A1
- Authority
- US
- United States
- Prior art keywords
- polishing
- polishing composition
- ttha
- tmah
- wafer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A polishing composition contains at least one water soluble polymer selected from the group consisting of polyvinylpyrrolidone and poly(N-vinylformamide), and an alkali, and preferably further contains at least one of a chelating agent and an abrasive grain. The water soluble polymer preferably has a weight average molecular weight of 6,000 to 4,000,000. The polishing composition is mainly used in polishing of the surfaces of semiconductor wafers such as silicon wafers, especially used in preliminary polishing of the surfaces of such wafers.
Description
- This application claims priority from Japanese Application No.: 2006-227614, filed on Aug. 24, 2006, the entire content of which is hereby incorporated by reference.
- The present invention relates to a polishing composition mainly used in polishing of a semiconductor wafer and to a polishing method using the polishing composition.
- Polishing of a semiconductor wafer such as a silicon wafer is usually divided into at least two stages, preliminary polishing and finish polishing. Of these, preliminary polishing is further divided into two or more stages for the purpose of high quality and efficiency. As a polishing composition usable for finish polishing, a polishing composition described in Japanese Laid-Open Patent Publication No. 02-158684 is known, for example. The polishing composition of the publication comprises water, colloidal silica, a water soluble polymer such as polyacrylamide and sizofiran, and a water soluble salt such as potassium chloride.
- In recent years, as design rules for semiconductor devices have required thinner devices, there is a demand for reducing small size LPDs (light point defects), which had not been considered problematic but are now considered to affect the performance of a semiconductor device. An LPD is a kind of defect observed on the surface of a wafer polished by using a polishing composition. Specifically, LPDs with a size of 0.12 μm or larger had been mainly considered problematic, which were caused by particles attached to wafer surfaces. Thus, an improvement in washing technique has largely reduced such LPDs. However, LPDs with a size smaller than the above (>0.065 μm) are mainly caused by scars occurring on wafer surfaces during preliminary polishing, in other words attributable to the polishing process. In many cases, these cannot be removed by finish polishing or washing. In this regard, even when the polishing composition described in Japanese Laid-Open Patent Publication No. 02-158684 is used for finish polishing, the number of LPDs attributable to the polishing process cannot be reduced more than before.
- Accordingly, an object of the present invention is to provide a polishing composition, by using which the number of LPDs attributable to the polishing process can be reduced on the surface of a physical object after being polished, and a polishing method using the polishing composition.
- In accordance with a first aspect of the present invention, a polishing composition is provided. The polishing composition contains at least one water soluble polymer selected from the group consisting of polyvinylpyrrolidone and poly(N-vinylformamide), and an alkali.
- In accordance with a second aspect of the present invention, a method of polishing is provided. The method includes polishing a surface of a semiconductor wafer using the above polishing composition.
- Other aspects and advantages of the invention will become apparent from the following description, illustrating by way of example the principles of the invention.
- Hereafter, an embodiment of the present invention will be described.
- A polishing composition according to this embodiment is produced by mixing a given amounts of a water soluble polymer, an alkali, and abrasive grains with water. Therefore, the polishing composition of this embodiment consists of a water soluble polymer, an alkali, abrasive grains, and water. This polishing composition is used in polishing of semiconductor wafers such as silicon wafers, especially used in preliminary polishing of such wafers. When the preliminary polishing is divided into two or more stages, this polishing composition is used for a finish stage of preliminary polishing.
- A water soluble polymer contained in the polishing composition of this embodiment is at least one compound selected from the group consisting of polyvinylpyrrolidone and poly(N-vinylformamide). These water soluble polymers can form a hydrophilic film on a wafer surface. This hydrophilic film disperses a vertical force, relative to a wafer surface, given to a wafer by coarse particles including abrasive grains into a horizontal direction. As a result, it is expected that the occurrence of defects on the wafer surface during polishing is prevented, and the number of LPDs attributable to the polishing process is reduced.
- When a water soluble polymer contained in a polishing composition is polyvinylpyrrolidone, the number of LPDs attributable to the polishing process is reduced in comparison with the use of poly(N-vinyl formamide). Therefore, a water soluble polymer contained in a polishing composition is preferably polyvinylpyrrolidone.
- The content of a water soluble polymer in a polishing composition is preferably 0.0003 g/L or more, more preferably 0.001 g/L or more, still more preferably 0.003 g/L or more, and most preferably 0.005 g/L or more. As the content of a water soluble polymer increases, a hydrophilic film that is sufficient to prevent defects from occurring is easily formed on a wafer surface, thereby reducing the number of LPDs attributable to the polishing process. In this regard, when the content of a water soluble polymer in a polishing composition is 0.0003 g/L or more, specifically 0.001 g/L or more, more specifically 0.003 g/L or more, and still more specifically 0.005 g/L or more, the number of LPDs attributable to the polishing process is reduced to a particularly suitable level for practical use.
- Further, the content of a water soluble polymer in a polishing composition is preferably 0.1 g/L or less, more preferably 0.02 g/L or less, still more preferably 0.015 g/L or less, and most preferably 0.01 g/L or less. A hydrophilic film by a water soluble polymer allows a polishing composition to reduce the polishing rate (removal rate) of a wafer. Therefore, a decrease of the content of a water soluble polymer in a polishing composition prevents a hydrophilic film from reducing the polishing rate. In this regard, when the content of a water soluble polymer in a polishing composition is 0.1 g/L or less, specifically 0.02 g/L or less, more specifically 0.015 g/L or less, and still more specifically 0.01 g/L or less, the polishing rate reduction by a hydrophilic film is reduced to a particularly suitable level for practical use.
- A water soluble polymer contained in a polishing composition has a weight average molecular weight of preferably 6,000 or more. As the weight average molecular weight of a water soluble polymer becomes larger, a hydrophilic film that is sufficient to prevent defects from occurring is easily formed on a wafer surface, thereby reducing the number of LPDs attributable to the polishing process. In this regard, when a water soluble polymer in a polishing composition has a weight average molecular weight of 6,000 or more, the number of LPDs attributable to the polishing process is reduced to a particularly suitable level for practical use.
- Further, a water soluble polymer contained in a polishing composition has a weight average molecular weight of preferably 4,000,000 or less, and more preferably 3,000,000 or less. A smaller weight average molecular weight of a water soluble polymer prevents a hydrophilic film from reducing the polishing rate of a wafer. In this regard, when the weight average molecular weight of a water soluble polymer in a polishing composition is 4,000,000 or less, and specifically 3,000,000 or less, the polishing rate reduction by a hydrophilic film is reduced to a particularly suitable level for practical use.
- An alkali contained in the polishing composition of the present embodiment may be, for example, any of alkali metal hydroxides, ammonia, amines, and quaternary ammonium salts. These alkalis can chemically polish a wafer and increase the rate of polishing a wafer by a polishing composition.
- When an alkali contained in a polishing composition is an alkali metal hydroxide or a quaternary ammonium salt, the wafer polishing rate by the polishing composition largely increases and additionally an increase of surface roughness of a polished wafer is more prevented in comparison with the use of other alkalis. Therefore, an alkali contained in a polishing composition is preferably an alkali metal hydroxide or a quaternary ammonium salt.
- The content of an alkali in a polishing composition is preferably 0.1 g/L or more, more preferably 0.25 g/L or more, and still more preferably 0.5 g/L or more. As the content of an alkali in a polishing composition increases, the wafer polishing rate by the polishing composition increases. In this regard, when the content of an alkali in a polishing composition is 0.1 g/L or more, specifically 0.25 g/L or more, and more specifically 0.5 g/L or more, the wafer polishing rate by the polishing composition is increased to a particularly suitable level for practical use.
- Further, the content of an alkali in a polishing composition is preferably 5 g/L or less, more preferably 4 g/L or less, and more preferably 3 g/L or less. An alkali may cause an increase of surface roughness of a polished wafer. Thus, as the content of an alkali in a polishing composition decreases, an increase of surface roughness of a polished wafer is more prevented. In this regard, when the content of an alkali in a polishing composition is 5 g/L or less, specifically 4 g/L or less, and more specifically 3 g/L or less, an increase of surface roughness of a polished wafer is prevented to a particularly suitable level for practical use.
- Abrasive grains contained in the polishing composition of the present embodiment may be, for example, any of colloidal silica and fumed silica. These abrasive grains can mechanically polish a wafer and increase the rate of polishing a wafer by a polishing composition.
- When abrasive grains contained in a polishing composition are colloidal silica, the stability of a polishing composition is enhanced in comparison with the use of other abrasive grains. As a result, scratches on the surface of a polished wafer are decreased. Therefore, abrasive grains contained in a polishing composition are preferably colloidal silica.
- The content of abrasive grains in a polishing composition is preferably 1 g/L or more, more preferably 3 g/L or more, and still more preferably 5 g/L or more. As the content of abrasive grains in a polishing composition increases, the wafer polishing rate by the polishing composition is increased. In this regard, when the content of abrasive grains in a polishing composition is 1 g/L or more, specifically 3 g/L or more, and more specifically 5 g/L or more, the polishing rate is increased to a particularly suitable level for practical use.
- Further, the content of abrasive grains in a polishing composition is preferably 45 g/L or less, more preferably 35 g/L or less, and still more preferably 25 g/L or less. A decreased content of abrasive grains in a polishing composition enhances the colloid stability of the polishing composition. In this regard, when the content of abrasive grains in a polishing composition is 45 g/L or less, specifically 35 g/L or less, and more specifically 25 g/L or less, the colloid stability of the polishing composition is enhanced to a particularly suitable level for practical use.
- The average primary particle diameter of abrasive grains contained in a polishing composition is preferably 5 nm or more, more preferably 10 nm or more, and still more preferably 15 nm or more. A larger average primary particle diameter of abrasive grains strengthens the function of the abrasive grains for mechanically polishing a wafer, thereby increasing the wafer polishing rate by a polishing composition. In this regard, when the average primary particle diameter of abrasive grains is 5 nm or more, specifically 10 nm or more, and more specifically 15 nm or more, the wafer polishing rate by a polishing composition is increased to a particularly suitable level for practical use.
- Further, the average primary particle diameter of abrasive grains contained in a polishing composition is preferably 200 nm or less, more preferably 150 nm or less, and still more preferably 100 nm or less. A larger average primary particle diameter of abrasive grains may cause an increase of scratches on the surface of a polished wafer. Therefore, a smaller average primary particle diameter of abrasive grains prevents an increase of scratches on the surface of a polished wafer. In this regard, when the average primary particle diameter of abrasive grains is 200 nm or less, specifically 150 nm or less, and more specifically 100 nm or less, an increase of scratches on the surface of a polished wafer is prevented to a particularly suitable level for practical use.
- The present embodiment provides the following advantages.
- The polishing composition of the present embodiment contains at least one water soluble polymer selected from the group consisting of polyvinylpyrrolidone and poly(N-vinyl formamide). This water soluble polymer forms a hydrophilic film on a wafer surface, and the film works to reduce the number of LPDs attributable to the polishing process. Therefore, the polishing composition of the present embodiment reduces the number of LPDs, attributable to the polishing process, on the surface of a wafer polished by using the polishing composition.
- The above embodiment may be modified as follows.
- The polishing composition of the above embodiment may further contain a chelating agent. The chelating agent forms a complex ion with metal impurities in a polishing composition, thereby capturing the metal impurities. This prevents an object to be polished from being contaminated with metal impurities. The chelating agent may be aminocarboxylic acid-based chelating agents or phosphonic acid-based chelating agents. Among these, preferably contained is ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, triethylenetetraaminehexaacetic acid, ethylenediaminetetramethylphosphonic acid, or diethylenetriaminepentamethylphosphonic acid. Ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, triethylenetetraaminehexaacetic acid, ethylenediaminetetramethylphosphonic acid, and diethylenetriaminepentamethylphosphonic acid have a particularly high ability to capture metal impurities.
- Known additives such as a preservative or an antifoaming agent may be added, if necessary, to the polishing composition of the above embodiment.
- The polishing composition of the above embodiment may be prepared by diluting a liquid concentrate before use.
- The polishing composition of the above embodiment may be used in polishing of physical objects other than semiconductor wafers.
- Next, Examples of the present invention and Comparative Examples will be described.
- The polishing compositions of Examples 1 to 53 and Comparative Examples 1 to 26 were prepared by properly mixing a water soluble polymer, an alkali, abrasive grains, and a chelating agent with water. The detailed of the water soluble polymer, alkali, abrasive grains, and chelating agent in each polishing composition are shown in Tables 1 and 2.
- In the column entitled “water soluble polymer” of Tables 1 and 2:
- PVP*1 represents polyvinylpyrrolidone having a weight average molecular weight of 10,000;
- PVP*2 represents polyvinylpyrrolidone having a weight average molecular weight of 3,500,000;
- PVP*3 represents polyvinylpyrrolidone having a weight average molecular weight of 1,600,000;
- PVP*4 represents polyvinylpyrrolidone having a weight average molecular weight of 67,000;
- PNVF represents poly(N-vinyl formamide) having a weight average molecular weight of 100,000;
- PVA represents polyvinyl alcohol (saponification degree: 95%) having a weight average molecular weight of 62,000;
- PVME represents polyvinyl methyl ether having a weight average molecular weight of 10,000;
- PEG represents polyethylene glycol having a weight average molecular weight of 26,000;
- PEO represents polyethylene oxide having a weight average molecular weight of 200,000;
- PPP represents polyoxyethylene polyoxypropyrene block copolymer having a weight average molecular weight of 9,000;
- PEI represents polyethyleneimine having a weight average molecular weight of 10,000;
- PAA represents polyacrylic acid having a weight average molecular weight of 25,000;
- PAA-NH4 represents ammonium polyacrylate having a weight average molecular weight of 20,000;
- PAA-Na represents sodium polyacrylate having a weight average molecular weight of 20,000;
- PAAM represents polyacrylamide having a weight average molecular weight of 1,000,000;
- PSS-Na represents sodium polystyrene sulfonate having a weight average molecular weight of 100,000;
- HEC represents hydroxyethyl cellulose having a weight average molecular weight of 1,000,000;
- CMC-Na*1 represents sodium carboxymethylcellulose having a weight average molecular weight of 10,000;
- CMC-Na*2 represents sodium carboxymethylcellulose having a weight average molecular weight of 330,000;
- CMC-Na*3 represents sodium carboxymethylcellulose having a weight average molecular weight of 90,000; and
- CMC-Na*4 represents sodium carboxymethylcellulose having a weight average molecular weight of 20,000.
- In the column entitled “alkali” of Tables 1 and 2:
- TMAH represents tetramethylammonium hydroxide;
- KOH represents potassium hydroxide;
- NaOH represents sodium hydroxide;
- NH3 represents ammonia;
- PIZ represents anhydrous piperazine; and
- IMZ represents imidazole.
- In the column entitled “abrasive grains” of Tables 1 and 2:
- CS*1 represents colloidal silica having an average primary particle diameter of 35 nm;
- CS*2 represents colloidal silica having an average primary particle diameter of 200 nm;
- CS*3 represents colloidal silica having an average primary particle diameter of 150 nm;
- CS*4 represents colloidal silica having an average primary particle diameter of 100 nm;
- CS*5 represents colloidal silica having an average primary particle diameter of 55 nm;
- CS*6 represents colloidal silica having an average primary particle diameter of 15 nm;
- CS*7 represents colloidal silica having an average primary particle diameter of 10 nm; and
- CS*8 represents colloidal silica having an average primary particle diameter of 5 nm.
- In the column entitled “chelating agent” of Tables 1 and 2:
- TTHA represents triethylenetetraaminehexaacetic acid;
- DTPA represents diethylenetriaminepentaacetic acid; and
- EDTPO represents ethylenediaminetetramethylphosphonic acid.
- The polishing compositions of Examples 1 to 53 and Comparative Examples 1 to 26 were used in polishing of silicon wafers with a diameter of 200 mm and a thickness of 730 μm (p-type, crystal orientation <100>, and COP (crystal originated particle)-free). The polishing rates of the polishing compositions under the conditions of Table 3 were measured. Results thereof are shown in the column entitled “polishing rate” of Tables 1 and 2. The polishing rate was obtained by dividing a thickness difference of each wafer between before and after polishing by a polishing period. To measure a wafer thickness, NANOMETRO 300TT, a flatness tester (manufactured by Kuroda Precision Industries, Ltd.) was used.
- The polishing compositions of Example 1 to 53 and Comparative Examples 1 to 26 were used in polishing of silicon wafers, and the number of LPDs on the surface of each polished silicon wafer, attributable to the polishing process, was evaluated. Results thereof are shown in the column entitled “defects” of Tables 1 and 2. Specifically, silicon wafers with a diameter of 200 mm and a thickness of 730 μm (p-type, crystal orientation <100>, and COP-free) were subjected to preliminary polishing using the polishing compositions of Examples 1 to 53 and Comparative Examples 1 to 26 under the conditions shown in Table 3. Thereafter, GLANZOX-3900 manufactured by Fujimi Inc. was diluted in 20 times with pure water, and the obtained dilution was used in finish polishing under the condition shown in Table 4. Wafers obtained after finish polishing were subjected to SC-1 (Standard Clean 1) washing and IPA (isopropyl alcohol) steam drying. Then, a first measurement of LPDs of each wafer was performed using SURFSCAN SP1-TBI manufactured by KLA-Tencor Corporation. Thereafter, the same wafer was again subjected to SC-1 washing and IPA steam drying, and then a second measurement of LPDs was performed using SURFSCAN SP1-TBI. An LPD existing at the same location in the first and second measurements is defined as an LPD attributable to the polishing process, and the number of LPDs attributable to the polishing process per a wafer surface was measured. In the column entitled “defects”, “E” (excellent) indicates that the number of LPDs attributable to the polishing process per a wafer surface was less than 10; “G” (good) indicates that the number thereof was 10 or more to less than 20; “F” (fair) indicates that the number thereof was 20 or more to less than 30; and “P” (poor) indicates that the number thereof was 30 or more.
- In order to evaluate the formation of hydrophilic films on wafer surfaces by the action of water soluble polymers, the polishing compositions of Examples 1 to 53 and Comparative Examples 1 to 26 were used in polishing of silicon wafers under the conditions of Table 3. After polishing, wetting of the surface of each silicon wafer was evaluated. Results thereof are shown in the column entitled “wetting” of Tables 1 and 2. Specifically, a wafer after polishing was slightly washed with water and wetting status of its surface was visually observed and evaluated. In the column entitled “wetting”, numeral 0 indicates no wetting on a wafer surface; numeral 3 indicates that 30% of a wafer surface was wet; numeral 6 indicates that 60% of a wafer surface was wet; numeral 7 indicates that 70% of a wafer surface was wet; numeral 8 indicates that 80% of a wafer surface was wet; numeral 9 indicates that 90% of a wafer surface was wet; and numeral 10 indicates that 100% of a wafer surface was wet.
- The polishing composition of Comparative Example 11 was excessively gelated, and thus it was impossible to use the composition for polishing a wafer.
-
TABLE 1 water soluble chelating polymer alkali abrasive grains agent polishing content content content content rate name [g/L] name [g/L] name [g/L] name [g/L] [μm/min.] defects wetting Ex. 1 PVP*1 0.020 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.260 F 10 Ex. 2 PVP*1 0.015 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.270 G 10 Ex. 3 PVP*1 0.013 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.268 G 10 Ex. 4 PVP*1 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.286 E 10 Ex. 5 PVP*1 0.007 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.300 E 10 Ex. 6 PVP*1 0.005 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.305 E 10 Ex. 7 PVP*1 0.003 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.302 G 10 Ex. 8 PVP*1 0.002 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.292 F 10 Ex. 9 PVP*1 0.001 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.290 F 10 Ex. 10 PVP*1 0.010 TMAH 5.0 CS*1 18.7 TTHA 0.30 0.290 E 10 Ex. 11 PVP*1 0.010 TMAH 4.0 CS*1 18.7 TTHA 0.30 0.295 E 10 Ex. 12 PVP*1 0.010 TMAH 3.0 CS*1 18.7 TTHA 0.30 0.291 E 10 Ex. 13 PVP*1 0.010 TMAH 0.5 CS*1 18.7 TTHA 0.30 0.263 E 10 Ex. 14 PVP*1 0.010 TMAH 0.25 CS*1 18.7 TTHA 0.30 0.248 E 10 Ex. 15 PVP*1 0.010 TMAH 0.10 CS*1 18.7 TTHA 0.30 0.220 E 10 Ex. 16 PVP*1 0.010 KOH 1.5 CS*1 18.7 TTHA 0.30 0.240 E 10 Ex. 17 PVP*1 0.005 KOH 1.5 CS*1 18.7 TTHA 0.30 0.262 E 10 Ex. 18 PVP*1 0.010 NaOH 1.0 CS*1 18.7 TTHA 0.30 0.238 E 10 Ex. 19 PVP*1 0.010 NH3 0.87 CS*1 18.7 TTHA 0.30 0.222 E 10 Ex. 20 PVP*1 0.010 PIZ 3.0 CS*1 18.7 TTHA 0.30 0.428 E 10 Ex. 21 PVP*1 0.010 IMZ 3.0 CS*1 18.7 TTHA 0.30 0.410 E 10 KOH 1.5 Ex. 22 PVP*1 0.010 TMAH 2.0 CS*1 45.0 TTHA 0.30 0.325 E 10 Ex. 23 PVP*1 0.010 TMAH 2.0 CS*1 35.0 TTHA 0.30 0.316 E 10 Ex. 24 PVP*1 0.010 TMAH 2.0 CS*1 25.0 TTHA 0.30 0.302 E 10 Ex. 25 PVP*1 0.010 TMAH 2.0 CS*1 5.0 TTHA 0.30 0.268 E 10 Ex. 26 PVP*1 0.010 TMAH 2.0 CS*1 3.0 TTHA 0.30 0.259 E 10 Ex. 27 PVP*1 0.010 TMAH 2.0 CS*1 1.0 TTHA 0.30 0.231 E 10 Ex. 28 PVP*1 0.010 TMAH 2.0 CS*2 18.7 TTHA 0.30 0.306 E 10 Ex. 29 PVP*1 0.010 TMAH 2.0 CS*3 18.7 TTHA 0.30 0.299 E 10 Ex. 30 PVP*1 0.010 TMAH 2.0 CS*4 18.7 TTHA 0.30 0.292 E 10 Ex. 31 PVP*1 0.010 TMAH 2.0 CS*5 18.7 TTHA 0.30 0.290 E 10 Ex. 32 PVP*1 0.010 TMAH 2.0 CS*6 18.7 TTHA 0.30 0.284 E 10 Ex. 33 PVP*1 0.010 TMAH 2.0 CS*7 18.7 TTHA 0.30 0.276 E 10 Ex. 34 PVP*1 0.010 TMAH 2.0 CS*8 18.7 TTHA 0.30 0.249 E 10 Ex. 35 PVP*1 0.010 KOH 3.0 CS*5 18.7 TTHA 0.30 0.258 E 10 Ex. 36 PVP*1 0.010 KOH 1.5 CS*5 18.7 TTHA 0.30 0.243 E 10 Ex. 37 PVP*1 0.010 KOH 0.5 CS*5 18.7 TTHA 0.30 0.210 E 10 Ex. 38 PVP*1 0.010 PIZ 3.0 CS*5 18.7 TTHA 0.30 0.434 E 10 Ex. 39 PVP*1 0.010 KOH 1.5 FS 18.7 TTHA 0.30 0.254 E 10 Ex. 40 PVP*1 0.010 TMAH 2.0 CS*1 18.7 — — 0.289 E 10 Ex. 41 PVP*1 0.010 TMAH 2.0 CS*1 18.7 DTPA 0.30 0.283 E 10 Ex. 42 PVP*1 0.010 TMAH 2.0 CS*1 18.7 EDTPO 0.30 0.285 E 10 Ex. 43 PVP*2 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.290 E 10 Ex. 44 PVP*3 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.290 E 10 Ex. 45 PVP*4 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.280 E 10 Ex. 46 PVP*3 0.015 KOH 1.5 CS*5 18.7 TTHA 0.30 0.239 G 10 Ex. 47 PVP*3 0.005 KOH 1.5 CS*5 18.7 TTHA 0.30 0.252 E 10 Ex. 48 PNVF 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.290 E 10 Ex. 49 PNVF 0.010 TMAH 2.0 CS*5 18.7 TTHA 0.30 0.293 E 10 Ex. 50 PNVF 0.003 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.294 G 10 Ex. 51 PNVF 0.005 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.290 E 10 Ex. 52 PNVF 0.007 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.304 E 10 Ex. 53 PNVF 0.013 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.252 G 10 -
TABLE 2 water soluble chelating polymer alkali abrasive grains agent polishing content content content content rate name [g/L] name [g/L] name [g/L] name [g/L] [μm/min.] defects wetting C. Ex. 1 — — TMAH 2.0 CS*1 18.7 TTHA 0.30 0.285 P 0 C. Ex. 2 — — KOH 1.5 CS*1 18.7 TTHA 0.30 0.237 P 0 C. Ex. 3 — — KOH 1.5 CS*5 18.7 TTHA 0.30 0.243 P 0 C. Ex. 4 PVA 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.273 P 10 C. Ex. 5 PVA 0.010 TMAH 2.0 CS*5 18.7 TTHA 0.30 0.277 P 10 C. Ex. 6 PVME 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.000 P 0 C. Ex. 7 PEG 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.130 P 3 C. Ex. 8 PEG 0.10 KOH 1.5 CS*1 18.7 TTHA 0.30 0.290 P 0 C. Ex. 9 PEG 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.090 P 0 C. Ex. 10 PPP 0.050 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.128 P 0 C. Ex. 11 PEI 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 — — — C. Ex. 12 PAA 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.400 P 8 C. Ex. 13 PAA-NH4 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.470 P 8 C. Ex. 14 PAA-Na 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.530 P 6 C. Ex. 15 PAAM 0.050 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.155 P 0 C. Ex. 16 PSS-Na 0.50 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.490 P 8 C. Ex. 17 PSS-Na 0.10 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.420 P 8 C. Ex. 18 HEC 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.281 P 10 C. Ex. 19 CMC-Na*1 0.010 TMAH 2.0 CS*1 18.7 TTHA 0.30 0.285 P 10 C. Ex. 20 CMC-Na*2 0.10 KOH 1.5 CS*1 18.7 TTHA 0.30 0.330 P 0 C. Ex. 21 CMC-Na*3 0.50 KOH 1.5 CS*1 18.7 TTHA 0.30 0.290 P 0 C. Ex. 22 CMC-Na*3 0.10 KOH 1.5 CS*1 18.7 TTHA 0.30 0.420 P 0 C. Ex. 23 CMC-Na*4 0.50 KOH 1.5 CS*1 18.7 TTHA 0.30 0.200 P 9 C. Ex. 24 CMC-Na*4 0.10 KOH 1.5 CS*1 18.7 TTHA 0.30 0.420 P 7 C. Ex. 25 CMC-Na*1 0.50 KOH 1.5 CS*1 18.7 TTHA 0.30 0.330 P 10 C. Ex. 26 CMC-Na*1 0.10 KOH 1.5 CS*1 18.7 TTHA 0.30 0.400 P 7 -
TABLE 3 conditions for preliminary polishing conditions Polishing Machine: PNX-322 manufactured by Okamoto Machine Tool Works, Ltd. Polishing pad: SUBA 400 manufactured by Nitta Haas Inc. Wafer polishing pressure: 15 kPa Rotation speed of surface plate: 50 rpm Polishing period: 4 min. Supply rate of polishing composition: 1 L/min. Temperature of polishing composition: 20° C. Temperature of cooling water for surface plate: 20° C. Rotation speed of carrier: 50 rpm -
TABLE 4 conditions for finishing polishing polishing machine: PNX-322 manufactured by Okamoto Machine Tool Works, Ltd. polishing pad: Surfin 000FM manufactured by Fujimi Inc. wafer polishing pressure: 15 kPa rotational speed of platen: 30 rpm polishing period: 4 min. feed rate of polishing composition: 0.5 L/min. temperature of polishing composition: 20° C. temperature of cooling water for platen: 20° C. rotation speed of carrier: 30 rpm - As shown in Tables 1 and 2, the polishing compositions of Examples 1 to 53 were evaluated regarding defects as fair or better, and obtained practically satisfactory polishing rates. In contrast, the polishing compositions of Comparative Examples 1 to 26 were evaluated regarding defects as poor except Comparative Example 11, whereby polishing could not be performed.
Claims (16)
1.-5. (canceled)
6. A method of polishing, comprising polishing a surface of a semiconductor wafer using a polishing composition containing a water soluble polymer comprising poly(N-vinylformamide), abrasive grains, and an alkali.
7. The method according to claim 6 , wherein said polishing includes preliminary polishing a surface of a semiconductor wafer using said polishing composition and finish polishing a preliminary polished surface of the semiconductor using a polishing composition different from said polishing composition.
8. A method of polishing, comprising polishing a surface of a silicon wafer using a polishing composition containing a water soluble polymer comprising polyvinylpyrrolidone, and an alkali.
9. The method according to claim 8 , wherein said polishing includes preliminary polishing a surface of a silicon wafer using said polishing composition and finish polishing a preliminary polished surface of the silicon wafer using a polishing composition different from said polishing composition.
10. The method according to claim 8 , wherein the water soluble polymer has a weight average molecular weight of 6,000 to 4,000,000.
11. The method according to claim 8 , further comprising a chelating agent.
12. The method according to claim 8 , further comprising at least one abrasive grain selected from the group consisting of colloidal silica and fumed silica.
13. The method according to claim 11 , further comprising at least one abrasive grain selected from the group consisting of colloidal silica and fumed silica.
14. The method according to claim 11 , wherein the chelating agent is an aminocarboxylic acid-based chelating agent.
15. The method according to claim 11 , wherein the chelating agent is a phosphonic acid-based chelating agent.
16. The method according to claim 8 , wherein the water soluble polymer is contained in the polishing composition in an amount of 0.0003 to 0.1 g/L.
17. The method according to claim 16 , wherein the water soluble polymer is contained in the polishing composition in an amount of 0.005 to 0.01 g/L.
18. The method according to claim 8 , wherein the alkali is contained in the polishing composition in an amount of 0.1 to 5 g/L.
19. The method according to claim 18 , wherein the alkali is contained in the polishing composition in an amount of 0.5 to 3 g/L.
20. A method of polishing, comprising:
preparing a polishing composition containing:
polyvinylpyrrolidone of a content in a range of from 0.005 to 0.01 g/L in the polishing composition;
an alkali of a content in a range of from 0.5 to 3 g/L;
a chelating agent of a content of about 0.3 g/L;
colloidal silica or fumed silica of a content in a range of 5 to 25 g/L; and
water; and
polishing a surface of a silicon wafer using the polishing composition, wherein said polishing includes preliminary polishing a surface of a silicon wafer using said polishing composition and finish polishing a preliminary polished surface of the semiconductor silicon wafer using a polishing composition different from said polishing composition.