US20090054541A9 - To enhance the thermal insulation of polymeric foam by reducing cell anisotropic ratio and the method for production thereof - Google Patents

To enhance the thermal insulation of polymeric foam by reducing cell anisotropic ratio and the method for production thereof Download PDF

Info

Publication number
US20090054541A9
US20090054541A9 US11/584,688 US58468806A US2009054541A9 US 20090054541 A9 US20090054541 A9 US 20090054541A9 US 58468806 A US58468806 A US 58468806A US 2009054541 A9 US2009054541 A9 US 2009054541A9
Authority
US
United States
Prior art keywords
cell
foam
gel
foam material
thermoplastic polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US11/584,688
Other versions
US8557884B2 (en
US20070179206A1 (en
Inventor
Larry Miller
Raymond Breindel
Mitchell Weekley
Thomas Cisar
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Owens Corning Intellectual Capital LLC
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/160,817 external-priority patent/US20030225172A1/en
Application filed by Individual filed Critical Individual
Priority to US11/584,688 priority Critical patent/US8557884B2/en
Assigned to OWENS-CORNING FIBERGLAS TECHNOLOGY, INC. reassignment OWENS-CORNING FIBERGLAS TECHNOLOGY, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CISAR, THOMAS E., MILLER, LARRY M., BREINDEL, RAYMOND M., MITCHELL, Z. WEEKLEY
Publication of US20070179206A1 publication Critical patent/US20070179206A1/en
Assigned to OWENS CORNING INTELLECTUAL CAPITAL, LLC reassignment OWENS CORNING INTELLECTUAL CAPITAL, LLC ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: OWENS-CORNING FIBERGLAS TECHNOLOGY, INC.
Publication of US20090054541A9 publication Critical patent/US20090054541A9/en
Application granted granted Critical
Publication of US8557884B2 publication Critical patent/US8557884B2/en
Active legal-status Critical Current
Adjusted expiration legal-status Critical

Abstract

This invention relates to foam insulating products, particularly extruded polystyrene foam, with increasing the cell orientation and reducing cell anisotropic ratio, as well as the process method for making the products thereof for improving the insulating properties and for reducing the manufacturing cost of the foam products. Alternatively, foam insulating products having increased cell compressive strength may be made by decreasing the cell orientation and increasing the cell anisotropic ratio.

Description

    TECHNICAL FIELD
  • The present invention relates to enhance the thermal insulation value (or to decrease the thermal conductivity) of rigid foamed polymeric boards by reducing cell anisotropic ratio and by increasing the cell orientation ratio, as well as the process methods for the production thereof. More particularly, it relates to rigid extruded polystyrene foam board wherein low cell anisotropic ratio or high cell orientation ratio is reached to increase thermal insulating value of the rigid foamed board.
  • BACKGROUND OF THE INVENTION
  • The usefulness of rigid foamed polymeric boards in a variety of applications is well known. Rigid foamed plastic boards are extensively used as thermal insulating materials for many applications. For instance, polymeric foam boards are widely used as insulating members in building construction. In the past, infrared attenuating agents have been used as fillers in polymeric foam boards to minimize material thermal conductivity k which, in turn, will maximize insulating capability (increase R-value) for a given thickness (U.S. Pat. Nos. 5,373,026 and 5,604,265; EP 863,175). The heat transfer k through an insulating material can occur through solid conductivity, gas conductivity, radiation, and convection. The heat transfer k, or K-factor, is defined as the ratio of the heat flow per unit cross-sectional to the temperature drop per unit thickness. In U.S. units, this is defined as: Btu . in Hr . Ft 2 . °F
  • And the metric unit: W m k
  • In most polymeric foams of conventional cell size, i.e. 0.1 to 1.5 millimeters, the reduction of thermal conductivity k has been observed with decreasing the average cell size. This phenomenon is documented in “The Thermal Conductivity of Foamed Plastics,” Chemical Engineering Progress, Vol. 57, No. 10, pp. 55-59, authored by Richard E. Skochdopol of The Dow Chemical Co., and “Prediction of the Radiation Term in the Thermal Conductivity of Crosslinked Closed Cell Polyolefin Foams,” J. of Polymer Science: Part B: Polymer Physics, V 38, pp. 993-1004 (2000), by O. A. Almanza et al. of Universidad de Valladolid, which are herein incorporated by reference.
  • It is highly desirable to improve the thermal conductivity k without adding additives, or increasing the density and/or the thickness of foam product. Particularly, the architectural community desires a foam board having a thermal resistance value R equal to 10, with a thickness of less than 1 ¾ inches, for cavity wall construction, to keep at least 1 inches of the cavity air gap clean. The total thermal resistance R, also known as the R-value, is the ratio of thickness t of the board to thermal conductivity k.
  • It is also highly desirable to produce the above rigid polymer foam having retained or improved compressive strength, thermal dimensional stability, fire resistance, and water absorption properties.
  • It is also highly desirable to provide the above rigid polymer foam with infrared attenuating agents and other process additives, such as nucleating agent, fire retardant, gas barrier, which has overall compound effects on foam properties including improved thermal conductivity (decreased k-factor), and improved insulating value (increased R-value) for a given thickness and density.
  • It is also highly desirable to provide the above rigid polymer foam with variety of blowing agents to enhance the thermal insulation R-value. These blowing agents include partially or fully hydrogenated chloroflourocarbons (HCFC's), hydroflourocarbons (HFC's), hydrocarbons (HC's), water, carbon dioxide, and other inert gases.
  • It is also highly desirable to provide the process methods and foaming facility modification to control the cell morphology: reduce the cell anisotropic and increase cell orientation during foaming process, for use in the production of a rigid polymer foam.
  • It is also highly desirable to lower the cost of a polymeric foam product in a simple and economical manner.
  • SUMMARY OF THE INVENTION
  • The present invention, in one preferred embodiment, relates to foam insulating products, such as extruded polystyrene foam, with low cell anisotropic ratio or higher cell orientation in the x/z direction to enhance the thermal insulation, and to retain other properties as well. The higher cell orientation can be achieved easily through process and die/shaper modification. The low anisotropic or higher cell orientation ratio polystyrene foams of the present invention decrease both the initial and the aged thermal conductivity, or inversely, increase the thermal resistance (“R value”) as compared with substantially round cells.
  • In another preferred embodiment of the present invention, polymeric foams with a lower cell orientation ratio in the x/z direction and higher anistropic ratio can be achieved easily through process and die/shaper modification. Cells made in this way have improved compressive properties with only slight reductions in thermal conductivity and insulation R-values as compared with round cells.
  • The foregoing and other advantages of the invention will become apparent from the following disclosure in which one or more preferred embodiments of the invention are described in detail and illustrated in the accompanying drawings. It is contemplated that variations in procedures, structural features and arrangement of parts may appear to a person skilled in the art without departing from the scope of or sacrificing any of the advantages of the invention.
  • BRIEF DESCRIPTION OF DRAWINGS
  • FIG. 1 illustrates a rigid, low-density foam made according to the prior art;
  • FIG. 2 illustrates a rigid, low-density foam made according to one preferred embodiment of the present invention;
  • FIG. 3 illustrates a rigid, low-density foam made according to another preferred embodiment of the present invention;
  • FIG. 4 is a graphical illustration from 52 trials showing the thermal insulation R-value vs. cell orientation ratio (x/z) of rigid foam board with several density levels, over a period of 180 days, HCFC 142 b blowing agent, about 10.5 to bout 11.5 weight percentage of total solid was used;
  • FIG. 5 is a graph, showing test results from 39 trials, related to R-value vs. cell orientation of polystyrene foam boards with several density levels, over a period of 180 days, HFC134a, about 5.5 wt %, and ethanol, about 3 wt %, were used as blowing agent for foaming these boards; and
  • FIG. 6 is a graph, showing test results from 32 trials, related to R-value vs. the cell orientation ratio of polystyrene foam boards with several density levels, over a period of 40 days at equilibrium of gas diffusion, carbon dioxide, about 3.68 wt % and ethanol, about 1.4 wt % were used as blowing agent.
  • DETAILED DESCRIPTION AND PREFERRED EMBODIMENTS OF THE INVENTION
  • The present invention relates to foam insulating products, such as extruded or expanded polystyrene foam, that are extensively used as thermal insulating materials for many applications. For instance, polymeric foam boards are widely used as insulating members in building construction. FIG. 1 illustrates a cross-sectional view of the rigid foam materials 20 made according to the prior art, while FIG. 2 illustrates the foam cells having enhanced thermal insulation values made in accordance with a preferred embodiment of the present invention. FIG. 3 illustrates another rigid foam material 20 made in accordance with a preferred embodiment of the present invention having improved compression strength.
  • Referring to FIG. 1, a rigid foam plastic material 20, typically a foam board, made according to the prior art is shown as having a plurality of interior open cells 22 and exterior open cells 24. Each interior open cell 22 is separated from the next corresponding interior open cell 22 and/or exterior open cell 24 by a cell strut 26, i.e. each open cell 22 shares a cell strut 26 with the next respective open cell 22. Similarly, each exterior open cell 24 is separated from the next corresponding exterior open cell 24 by a cell strut 26. Further, each exterior open cell 24 is separated from the outer environment surrounding the rigid foam plastic materials 20 by a cell wall 28. The thickness of the cell wall 28 is less than the thickness of a cell strut 26. The cells 22, 24 are substantially round in shape and have an average cell size of approximately 0.1 to about 1.5 millimeters in diameter. As the cells 22, 24 are substantially round, the x/z cell orientation ratio is approximately 1.0. The cell orientation ratio is simply a ratio of the cell size in the direction desired. For example, the cell orientation in the machine direction (or extruded direction) is defined as x/z cell orientation ratio and in the cross machine direction as y/z cell orientation ratio.
  • Further, the cell anisotropic ratio of substantially round cells as in the FIG. 1 is also approximately 1.0. Here, the cell anisotropic ratio a is determined as:
    a=z/(xyz)1/3
    or, for easy calculation: a=10lg z-1/3(lg x·y·z)
  • where x is the cell 22, 24 size of the foamed plastic material 20 in extruded direction; y is the cell 22, 24 size in the cross machine direction of the material 20; and z is the cell 22, 24 size in vertical thickness direction of the material 20. The cell sizes are measured by optical microscope or scanning electron microscope (SEM); which are observed at least two sliced faces—in the x/z plane and y/z plane, and are characterized by image analysis program. The average cell 22, 24 size, c is calculated by:
    c=(x+y+z)/3
  • FIGS. 2 and 3 illustrate a rigid foam plastic material 20 made in accordance with the present invention in which the cell orientation ratio in the x/z direction is altered from about 1.0. As will be shown, the change in cell orientation ratio in the x/z direction results in new and unique properties for the rigid foam plastic materials 20.
  • FIG. 2 shows a rigid foam plastic material 20 having rigid foam cells 22, 24 made according to one preferred embodiment of the present invention. Here, the cell orientation ratio in the x/z direction is increased above 1.0 to between approximately 1.03 to about 2.0 while still maintaining a low cell anisotropic ratio between about 0.97 to about 0.6. Materials 20 made in accordance with FIG. 2 exhibit enhanced thermal insulation R-value, decreased thermal conductivity k, and decreased aged thermal conductivity without an increase in the amount of polymeric material per unit measure and without a substantial decrease in compressive strength.
  • In FIG. 3, the cell orientation in the x/z direction is decreased to between approximately 0.5 and about 0.97 while maintaining an anistropic ratio of between about 1.6 to about 1.03. Materials 20 made in accordance with FIG. 3 exhibit decreased thermal insulation R-value, increased thermal conductivity k, and increased aged thermal conductivity without an increase in the amount of polymeric material per unit measure. However, these materials 20 attain an increase in compressive strength.
  • The composition of the cell struts 26 and cell walls 28 of FIGS. 2 and 3 may be any such polymer materials suitable to make polymer foams. These include polyolefins, polyvinylchloride, polycarbonates, polyetherimides, polyamides, polyesters, polyvinylidene chloride, polymethylmethacrylate, polyurethanes, polyurea, phenol-formaldehyde, polyisocyanurates, phenolics, copolymers and terpolymers of the foregoing, thermoplastic polymer blends, rubber modified polymers, and the like. Also included are suitable polyolefins include polyethylene and polypropylene, and ethylene copolymers. Preferably, these thermoplastic polymers have weight-average molecular weights from about 30,000 to about 500,000.
  • A preferred thermoplastic polymer comprises an alkenyl aromatic polymer material. Suitable alkenyl aromatic polymer materials include alkenyl aromatic homopolymers and copolymers of alkenyl aromatic compounds and copolymerizable ethylenically unsaturated comonomers. The alkenyl aromatic polymer material may further include minor proportions of non-alkenyl aromatic polymers. The alkenyl aromatic polymer material may be comprised solely of one or more alkenyl aromatic homopolymers, one or more alkenyl aromatic copolymers, a blend of one or more of each of alkenyl aromatic homopolymers and copolymers, or blends of any of the foregoing with a non-alkenyl aromatic polymer.
  • Suitable alkenyl aromatic polymers include those derived from alkenyl aromatic compounds such as styrene, alphamethylstyrene, paramethylstyrene, ethylstyrene, vinyl benzene, vinyl toluene, chlorostyrene, and bromostyrene. A preferred alkenyl aromatic polymer is polystyrene. Minor amounts of monoethylenically unsaturated compounds such as C2-6 alkyl acids and esters, ionomeric derivatives, and C4-6 dienes may be copolymerized with alkenyl aromatic compounds. Examples of copolymerizable compounds include acrylic acid, methacrylic acid, ethacrylic acid, maleic acid, itaconic acid, acrylonitrile, maleic anhydride, methyl acrylate, ethyl acrylate, isobutyl acrylate, n-butyl acrylate, methyl methacrylate, vinyl acetate and butadiene.
  • Any suitable blowing agent may be used in the practice on this invention. Blowing agents useful in the practice of this invention include inorganic agents, organic blowing agents and chemical blowing agents. Suitable inorganic blowing agents include carbon dioxide, nitrogen, argon, water, air, nitrogen, and helium. Organic blowing agents include aliphatic hydrocarbons having 1-9 carbon atoms, aliphatic alcohols having 1-3 carbon atoms, and fully and partially halogenated aliphatic hydrocarbons having 1-4 carbon atoms. Aliphatic hydrocarbons include methane, ethane, propane, n-butane, isobutane, n-pentane, isopentane, and neopentane. Aliphatic alcohols include, methanol, ethanol, n-propanol, and isopropanol. Fully and partially halogenated aliphatic hydrocarbons include fluorocarbons, chlorocarbons, and chlorofluorocarbons. Examples of fluorocarbons include methyl fluoride, perfluoromethane, ethyl fluoride, 1,1-difluoroethane (HFC-152a), 1,1,1-trifluoroethane (HFC-143a), 1,1,1,2-tetrafluoro-ethane (HFC-134a), pentafluoroethane, difluoromethane, perfluoroethane, 2,2-difluoropropane, 1,1,1-trifluoropropane, perfluoropropane, dichloropropane, difluoropropane, perfluorobutane, and perfluorocyclobutane. Partially halogenated chlorocarbons and chlorofluorocarbons for use in this invention include methyl chloride, methylene chloride, ethyl chloride, 1,1,1-trichloroethane, 1,1-dichloro-1-fluoroethane (HCFC-141b), 1-chloro-1,1-difluoroethane (HCFC-142b), chlorodifluoromethane (HCFC-22), 1,1-dichloro-2,2,2-trifluoroethane (HCFC-123) and 1-chloro-1,2,2,2-tetrafluoroethane (HCFC-124), and the like. Fully halogenated chlorofluorocarbons include trichloromonofluoromethane (CFC-11), dichlorodifluoromethane (CFC-12), trichlorotrifluoroethane (CFC-113), 1,1,1-trifluoroethane, pentafluoroethane, dichlorotetrafluoroethane (CFC-114), chloroheptafluoropropane, and dichlorohexafluoropropane. Chemical blowing agents include azodicarbonamide, azodiisobutyro-nitrile, benzenesulfonhydrazide, 4,4-oxybenzene sulfonyl-semicarbazide, p-toluene sulfonyl semi-carbazide, barium azodicarboxylate, and N,N′-dimethyl-N,N′-dinitrosoterephthalamide and trihydrazino triazine. In the present invention it is preferable to use about 8 to about 14% by weight based on the weight of the polymer HCFC-142b or about 4 to about 12% of HFC-134a with 0 to 3% ethanol. Alternatively about 3 to about 8% carbon dioxide with 0 to about 4% lower alcohol, which include ethanol, methanol, propanol, isopropanol and butanol.
  • Optional additives which may be incorporated in the extruded foam product include additionally infrared attenuating agents, plasticizers, flame retardant chemicals, pigments, elastomers, extrusion aids, antioxidants, fillers, antistatic agents, UV absorbers, etc. These optional additives may be included in any amount to obtain desired characteristics of the foamable gel or resultant extruded foam products. Preferably, optional additives are added to the resin mixture but may be added in alternative ways to the extruded foam manufacture process.
  • Thus, for example, in the preferred embodiments having a structure as shown in FIGS. 2 and 3 above, the rigid foam plastic material 20 is formed from a plasticized resin mixture of polystyrene having a weight-average molecular weight of about 250,000, an infrared attenuation agent such as special asphalt, a blowing agent, and other process additives such as a nucleation agent, flame retardant chemicals, and a nano-gas barrier additive.
  • The rigid foam plastic material 20 of FIGS. 2 and 3 may be prepared by any means known in the art such as with an extruder, mixer, blender, or the like. The plasticized resin mixture, containing the thermoplastic polymer and preferably other additives, are heated to the melt mixing temperature and thoroughly mixed. The melt mixing temperature must be sufficient to plastify or melt the thermoplastic polymer. Therefore, the melt mixing temperature is at or above the glass transition temperature or melting point of the polymer. The melt mix temperature is from about 200 to 280° C., most preferably about 220 to about 240° C., depending on the amount of additives and the type of blowing agent used.
  • A blowing agent is then incorporated to form a foamable gel. The foamable gel is then cooled to a die melt temperature. The die melt temperature is typically cooler than the melt mix temperature, in the preferred embodiment, from about 100 to about 150° C., and most preferably from about 110 to about 120° C. The die pressure must be sufficient to prevent prefoaming of the foamable gel which contains the blowing agent. Prefoaming involves the undesirable premature foaming of the foamable gel before extrusion into a region of reduced pressure. Accordingly, the die pressure varies depending upon the identity and amount of blowing agent in the foamable gel. Preferably, in the preferred embodiment as shown in FIGS. 2 and 3, the pressure is from about 40 to about 70 bars, most preferably about 50 bars. The expansion ratio, foam thickness per die gap, is in the range of 20 to 70, typically about 60.
  • To make the materials 20 of FIG. 2 having a cell orientation ratio in the x/z direction of between about 1.03 about 2, the gap of the die lips and/or the shaper plates of the die are opened wider compared to those produced in the prior art as shown in FIG. 1. This produces materials 20 having greater than desired thickness. The line speed, or takeaway speed, of the conveyor is then used to pull down the materials 20 to the desired thickness. As described above, materials 20 made in accordance with FIG. 2 exhibit enhanced thermal insulation R-value, decreased thermal conductivity k, and decreased aged thermal conductivity without an increase in the amount of polymeric material per unit measure and without a substantial decrease in compressive strength as compared with substantially round celled materials 20 as in FIG. 1.
  • Conversely, for materials 20 having a cell orientation ratio in the x/z direction between about 0.97 to about 0.6, the gap of the die lips and/or shaper plates of the die are closed and the conveyor line speed is decreased as compared to the prior art as shown in FIG. 1 to cause the cells 22, 24 to grow in the z-direction. As described above, materials made in accordance with FIG. 3 have enhanced compressive strength without a substantial decrease in thermal insulation R-value as compared with substantially round celled materials 20 as in FIG. 1.
  • Of course, as those of skill in the art recognize, other factors used may influence the cell orientation ratio in the x/z direction. For example, it is more difficult to influence smaller cells 22, 24 than it is to effect larger cells 22, 24. Thus, blowing agents that produce smaller cell sizes, such as carbon dioxide, may be more difficult to influence than blowing agents that produce larger cell sizes, such as HCFC-142b.
  • In another preferred embodiment, an extruded polystyrene polymer foam similar to the foam material 20 of FIGS. 2 and 3 is prepared by twin-screw extruders (low shear) with flat die and plate shaper. A polystyrene pellet or bead is added into the extruder along with a nucleation agent, a fire retardant, and/or process agent by multi-feeders. Alternatively, a single screw tandem extruder (high shear) with radial die and a radial shaper may be used.
  • The polymeric foam material of the present invention comprises greater than about 95% closed cells and less than about 5% open cells. The foam material is a high strength, rigid insulation board with long term thermal performance and is water resistant. The polymeric foam material of the present invention is typically between about 0.50 to about 1.75 inches thick.
  • The polymeric foam material of the present invention meets the standard specifications according to Standard Specification for Rigid, Cellular Polystyrene Thermal Insulation, Designation: C578-04a, ASTM International, West Conshohocken, Pa., November, 2004, which is herein incorporated by reference in its entirety.
  • The polymeric foam material of the present invention has a maximum water absorption of less than about 0.10% by volume according to ASTM Test Method C 272. Preferably, the maximum water absorption of the foam is about 0.3% by volume. In the case of a 1.0 inch foam board, the foam material has a vapor permeance of 1.1 perm according to ASTM Test Method E 96. The polymeric foam material of the present invention has a flame spread of 5 according to ASTM Test Method E 84.
  • Applications of the present invention include placing the foam material under concrete slabs, over gravel fill that has been leveled and tamped. The foam material may be used in cavity walls, furred walls, and as sheathing material. The foam material is useful as exterior insulation wherein the foam board is placed on the exterior structure, i.e., a house, and siding is attached to the foam board. The foam material is also useful in residing applications and may be placed directly over old siding. New siding is then attached to the foam board.
  • Additionally, the foam material may be used in cold storage applications by installing the foam material under a concrete slab of an enclosure, in the sidewalls and on the roof of the enclosure. In typical cold storage applications, more than one layer of foam material is used according to the thermal requirements of the application.
  • The foam material may be used in agricultural applications, i.e., barns, on the sidewalls, under the concrete slab and under the roofing material of the barn. Additionally, the foam material may be used in roofing applications such as a roofing recovery board, below membrane roof insulation and in tapered roof applications.
  • The following are examples of the present invention suited to the preferred embodiment as shown in FIG. 2, and are not to be construed as limiting.
  • EXAMPLES
  • The invention is further illustrated by the following examples in which all foam boards were 1.5″ in thickness, and all R-values were 180 day aged R-value, unless otherwise indicated. The aged R-value (aged 180 days) of the polymeric foam material is between about 5.0 to about 5.81 K·m2/W for a 1.5 inch thick board.
  • In the following examples and control examples, rigid polystyrene foam boards were prepared by a twin screw co-rotating extruder with a flat die and shaper plate. Vacuum was applied in the extrusion processes for some examples.
  • Table 1, shows a summary of the process conditions for the twin-screw extruder. The polystyrene resins used were 70% polystyrene having a melt index of 3 and the 30% polystyrene, having a melt index of 18.8 (both from Deltech, with molecular weight, Mw about 250,000). The composite melt index was around 10.8 in compound. Stabilized hexabromocyclododecane (Great Lakes Chemical, HBCD SP-75) was used as flame retardant agent in the amount of 1% by the weight of the solid foam polymer.
    TABLE 1
    Key Operation Parameter Examples
    Wt. % of process additive 0 to 6
    Wt. % of talc 0-2
    Wt. % of HC 0 to 3
    Wt. % of HFC 134a 0 to 6
    Wt. % of HCFC-142b  0-12
    Wt. % of CO2 0-5
    Extruder Pressure, Kpa (psi) 13000-17000
    (1950-2400)
    Die Melt Temperature, ° C. 117-123
    Die Pressure, Kpa (psi) 5400-6600
    (790-950)
    Line Speed, m/hr (ft/min) 110-170
      (6-9.5)
    Throughput, kg/hr 100-200
    Die Gap, mm 0.4-1.8
    Vacuum KPa (inch Hg) 0-.4.25 (0 to 20)
  • The results of above examples, and a comparative example of the convention process with round cell structure shown in Table 2.
    TABLE 2
    Aged R-value Density Cell Average Cell
    180 days K · m2/W Kg/m3 Anisotropic Cell Orientation Vacuum Blowing
    Run # (F · ft2 · hr/Btu) (pcf) Ratio micron x/z Hg inch Agent
    428-2 1.023 (5.81) 32.48 (2.03) 0.856 272 1.36 6 1
    431-3 0.997 (5.66) 32 (2) 0.911 257 1.22 6.6 1
    443-2  0.97 (5.51) 27.52 (1.72) 0.888 273 1.3 12 1
    445-2 0.912 (5.18) 27.36 (1.71) 0.989 250 1.08 13.5 1
    448-5 0.965 (5.48) 24.32 (1.52) 0.901 260 1.26 16.4 1
    459-2 0.912 (5.13) 23.36 (1.46) 0.977 256 1.02 14 1
    509-8 0.895 (5.08) 28.8 (1.8) 0.888 252 1.21 12.6 2
    498-2 0.852 (4.83) 28.18 (1.76) 0.982 177 1.06 13 2
    191-2 0.743 (4.22) 50.56 (3.16) 1.095 279 0.79 No 3
    183-4 0.696 (3.95) 49.76 (3.11) 1.215 224 0.6 No 3

    * where, aged R-value is 40 days for carbon dioxide samples;

    ** Blowing agent 1: HCFC 142 b 11 wt %; 2: HFC 134a 5.5 wt % and ethanol 3 wt %; 3: carbon dioxide 3.68 wt % and ethanol 1.4 wt %

    *** All specimens are 38 to 42 mm (around 1.5″) in thickness
  • More completed data treatments of these trials are shown on FIG. 4 is a graphical illustration from 52 trials showing the thermal insulation R-value vs. cell orientation of rigid foam board with several density levels, over a period of 180 days, HCFC 142 b blowing agent, 10.5 to 11.5 weight percentage of total solid was used, which shows an R-value increase of 6 to 12% by changing cell orientation from 0.9 to 1.3 for a foam board with 1.6 pcf density.
  • FIG. 5 is a graph, showing test results from 39 trials, related to R-value vs. cell orientation of polystyrene foam boards with several density levels, over a period of 180 days, HFC134a 5.5 wt % and ethanol 3 wt % were used as blowing agent for foaming these boards, which shows an R-value increase of 5 to 10% by changing cell orientation from 0.9 to 1.3 for a foam board with 1.6 pcf density.
  • FIG. 6 is a graph, showing test results from 32 trials, related to R-value vs. the cell orientation of polystyrene foam boards with several density levels, over a period of 40 days at equilibrium of gas diffusion, carbon dioxide 3.68 wt % and ethanol 1.4 wt % were used as blowing agent, which shows an R-value increase of 4 to 8% by changing cell orientation from 0.7 to 0.9 for a foam board with 3 pcf density.
  • Based on the test data from all these trials from a multi-variable regression calculation yields the R-value vs. Cell Orientation (or Cell Anisotropic Ratio) as shown in FIGS. 4, 5 and 6, which shows an R-value increase of 3 to 12% by increase cell orientation 0.1 to 0.3 in comparison with projected R-values of same cell structure, without cell morphology change polymer foams with different foam densities.
  • While the invention has been described in terms of preferred embodiments, it will be understood, of course, that the invention is not limited thereto since modifications may be made by those skilled in the art, particularly in light of the foregoing teachings.

Claims (7)

1. A method of increasing the cell orientation ratio in the x/z direction of a rigid polymer foam material comprising:
providing a device capable of producing the rigid polymer foam material;
introducing a thermoplastic polymer resin to said device;
heating said thermoplastic polymer resin above its glass transition temperature and melting point;
incorporating one or more blowing agents into said thermoplastic polymer resin at a first pressure to form a gel, said first pressure sufficient to prevent pre-foaming of said gel;
cooling said gel to a die melt temperature; and
extruding the gel through a die gap of the device to a region of lower die pressure;
wherein said gel grows quicker in an x-direction relative to a z-direction to form the polymer foam material, wherein said x-direction is defined as the extruded direction of the polymer foam material and wherein said z-direction is defined as the vertical thickness direction of the polymer foam material
wherein the polymeric foam material comprises greater than about 95% closed cells.
2. The process of claim 1, wherein said device comprises an extruder, a mixer or a blender.
3. The process of claim 1, wherein the gel grows quicker in the x-direction relative to the z-direction by increasing the line pulling speed of the device through said die gap at a constant die gap thickness while maintaining a constant foam density of the polymeric foam material,
4. The process of claim 1, wherein introducing a thermoplastic polymer material to said device comprises introducing an alkenyl aromatic polymer to said device.
5. The process of claim 1, wherein incorporating one or more blowing agents comprises incorporating one or more blowing agents into said thermoplastic polymer resin at a first pressure to form a gel, said first pressure sufficient to prevent pre-foaming of said gel, said one or more blowing agents comprising partially or fully hydrogenated HCFC's, HFC's, HC's, carbon dioxide, other inert gases, and mixtures thereof.
6. The process of claim 1, wherein introducing a thermoplastic polymer resin to said device comprises introducing a thermoplastic polymer resin to said device, said thermoplastic polymer resin having a weight average molecular weight of between about 30,000 to about 500,000.
7. The method of claim 1, wherein the cell orientation ratio in the x/z direction of the rigid polymer foam materials is between about 1.03 to about 2.0.
US11/584,688 2002-05-31 2006-10-20 To enhance the thermal insulation of polymeric foam by reducing cell anisotropic ratio and the method for production thereof Active 2024-11-25 US8557884B2 (en)