US20070151701A1 - Continuous Metal Matrix Composite Consolidation - Google Patents
Continuous Metal Matrix Composite Consolidation Download PDFInfo
- Publication number
- US20070151701A1 US20070151701A1 US11/623,103 US62310307A US2007151701A1 US 20070151701 A1 US20070151701 A1 US 20070151701A1 US 62310307 A US62310307 A US 62310307A US 2007151701 A1 US2007151701 A1 US 2007151701A1
- Authority
- US
- United States
- Prior art keywords
- tape
- junction
- prepeg
- metal matrix
- laser
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for the fabrication of large metal matrix composite structures comprising the continuous joining by brazing or welding of aluminum matrix tape using an infrared laser to melt the surface of the tape while applying pressure to the tape and simultaneously contacting it with previously applied tape layers on a rotating mandrel. The apparatus utilized to accomplish this fabrication process may include a variety of pre and post-contact heaters and preferably includes instruments for the continuous monitoring and control of the process.
Description
- This application is a continuation-in-part of U.S. patent application Ser. No. 09/733,566 filed Dec. 8, 2000 and copending herewith.
- The present invention relates to methods and apparatus for the continuous consolidation of metal matrix composite materials and more particularly to methods and apparatus for the consolidation of aluminum matrix, ceramic fiber reinforced metal matrix composites in prepeg tape form.
- The advantageous properties of metal matrix composites, especially aluminum matrix composites that incorporate ceramic reinforcing fibers are well known and recognized in the art and include high specific strength, high specific stiffness, maintenance of properties at extremes of high and low temperature and their resistance or lack of outgassing in a vacuum which is a major shortcoming of many competitive materials. These properties are of particular importance in aviation and space vehicle and structural applications. In fact, it has been estimated that the use of aluminum matrix composites of this type in, for example, launch vehicles could reduce their weight by as much as 30%, thus increasing their available payload by a like amount.
- What is inhibiting the use of such materials in launch and similar vehicles, is a cost effective manufacturing method for the production of large structures from these materials. The provision of such a method would permit such applications for these materials and provide all of the accompanying attendant benefits to such use.
- It is therefore an object of the present invention to provide a method for the manufacturing of large structural members from aluminum metal matrix composites (AMCs).
- It is another object of the present invention to provide a cost effective such manufacturing method.
- It is yet another object of the present invention to provide apparatus for the implementation of such a manufacturing method.
- According to the present invention, there is provided a method for the fabrication of large AMC structures comprising the continuous welding or brazing of an aluminum matrix bare or braze-clad fiber reinforced tape using an infrared laser to melt the aluminum or the braze cladding on the tape while applying pressure to the tape and simultaneously contacting it with previously applied tape layers on a rotating mandrel. The apparatus utilized to accomplish this fabrication process may include a variety of pre and post-contact heaters and preferably includes instruments for the continuous monitoring and control of the process.
-
FIG. 1 is a schematic perspective view of apparatus suitable for the manufacture of AMC structures in accordance with the process of the present invention. -
FIG. 2 is a schematic depiction of the area of contact between the mandrel surface, and the incoming prepeg tape at the point of application of infrared laser radiation in accordance with the process of the present invention. -
FIG. 3 is a schematic depiction of the area depicted inFIG. 2 except under the preferred alternative condition where the prepeg tape is not braze coated prior to consolidation. - The present invention provides a method for the cost effective fabrication/manufacture of large structural members of aluminum metal matrix composites. The feedstock for the process is a metal matrix composite (MMC), specifically an aluminum matrix composite (AMC), in prepeg tape form comprised of alumina (Al2O3) fibers in an aluminum/aluminum alloy matrix. The prepeg tape can be bare or coated with a “brazing” alloy, i.e. an aluminum alloy having a lower melting point than the aluminum matrix of the prepeg tape, prior to application in the process of the present invention. Fabrication is accomplished by applying the bare or braze material coated prepeg tape to a rotating mandrel with the application of pressure while simultaneously melting the braze coating or the surface of the bare metal, in the case of an non-braze coated tape, at the junction between the prepeg tape and the mandrel surface using a laser, preferably an infrared or diode laser that provides very limited and very localized heating and melting of the braze coat or surface layer of aluminum. The laser beam of infrared radiation preferably has a rectangular cross section to enhance heating efficiency in the area of the junction. As will be seen from the detailed description that follows, a variety of pre and post-contact heaters and process control devices are preferably used to control and monitor the process. The braze-coated feedstock just described can be prefabricated at a remote location and provided in coil form, or, as described hereinafter, can be prepared just prior to fabrication by coating the AMC prepeg with the braze coat in line just prior to exposure to the laser radiation and application to the mandrel.
- While any number of techniques such as spraying (thermal, arc, plasma, etc.), surface alloying, etc. can be used to apply the lower melting braze coating to the prepeg tape, in the case where the braze coating is applied in line with the consolidation operation, the prepeg tape is preferably guided through a pot of molten brazing, i.e. lower melting, metal, extracted from the pot of metal through a coating thickness control device such as a die or air knife, and then through a cooling chamber to solidify the coating. Preferably, the pot of molten metal is equipped with an ultrasonic pulse inducing element comprising a power supply, a transducer and a probe to facilitate coating of the matrix of the prepeg tape with the braze coating. When used, the ultrasonic probe is inserted into the pot of lower melting molten metal it produces a cavitation field that results in pressure waves that reduce the contact angle and improve the wetting of the lower melting material to the prepeg. The cooling chamber can be highly sophisticated, but can be as simple a metal tube through which is flowed a chilled gas such as nitrogen and through which the braze coated prepeg travels on exit from the coating pot and the thickness control device.
- Referring now to
FIG. 1 , theconsolidation apparatus 10 of the present invention, comprises a rotatingmandrel 12 supported on legs 14 (or any other suitable support system), alaser 16 that directs a beam ofinfrared radiation 18 to thejunction 20 between braze coated orbare prepeg tape 22 andsurface 24, acarriage unit 26 that supports and imparts lateral traversing motion tocompaction wheel 28, pre-heaters 30 and post heater(s) 32. According to a preferred embodiment of the present invention, anoptical pyrometer 33 can be used to monitor the temperature atjunction 20 and the signal therefrom used to control either the mandrel rotation an/or carriage unit traverse speeds or the intensity oflaser 16, to thereby control the temperature of the molten braze coating 36 (seeFIG. 2 ) or aluminum (seeFIG. 3 ) that occurs atjunction 20. - Referring now to
FIG. 2 that schematically depicts a side view ofconsolidation apparatus 10 and shows the relative positions oflaser 16,infrared radiation beam 18,compaction wheel 28,mandrel 12 and incoming braze-coatedprepeg tape 22 atjunction 20, it is readily observed that atjunction 20, there exists a “front” ofmolten metal 34 that comprises the molten or liquid form ofbraze coating 36 onprepeg tape 22.Front 34 is produced by the localized heating induced by the impact ofinfrared radiation beam 18 upon the surface ofbraze coating 36. It must be noted, that although not specifically depicted inFIG. 2 ,surface 24 ofmandrel 12 includes at least one wrap of previously appliedprepeg tape 22 to which incomingfeedstock prepeg tape 22 is adhered asbraze coating 36 melts due to the localized and controlled heating action ofinfrared radiation beam 18, and subsequently cools as it is removed from the area offront 34 due to rotation ofmandrel 12 in the direction shown byarrow 38 thereby building serial overlying layers of AMC joined to each other by alternating layers ofbraze material 36. Simultaneously with the creation offront 34 and the movement ofprepeg tape 22 in the direction indicated byarrow 38,compaction wheel 28 pushesprepeg tape 22, and consequently associated meltedbraze coating 36, into intimate contact withsurface 24 onmandrel 12 causingprepeg tape 22 to adhere firmly thereto. The specific conditions under which such fabrication can occur are described in greater detail hereinafter. -
Consolidation apparatus 10 fundamentally comprises a 2-axis filament winder of the type used in the fabrication of polymer matrix composites. According to a preferred embodiment,mandrel 12 can be up to 48 inches long and up to about 36 inches in diameter. Of course, larger dimensioned devices can be used in those cases where larger structural members are being fabricated. The rotational movement ofmandrel 12 and the linear traverse ofcompaction wheel 28 oncarriage unit 26 are controlled and coordinated by means of “Pattern Master” software or the like that are supplied with the filament winder unit, or custom deigned and implemented if a specific non-standard wrap pattern is required or desired. -
Laser 16 preferably comprises a stacked multi-bar infrared laser. An array ofoptical lenses 38 are used to shapeinfrared radiation beam 18 into a rectangular pattern that matches the cross-sectional dimension ofprepeg tape 22. According to a preferred embodiment of the invention,laser 16 is powered by a DC power supply capable of delivering 75 amps to the preferred stackedmulti-bar diode laser 16.Laser 16 in this configuration is designed to operate in a continuous wave mode at a power of up to 500 watts. In the embodiment depicted inFIG. 3 wherein a separate braze coating layer is not applied but rather a slightly thicker (by perhaps one or two thousandths of an inch) of metal that forms the matrix is used, a higher power laser is necessary due to the generally higher melting point of the matrix material as compared to the applied braze coating described herein. Thus, for alternative such processes it is preferred that the laser exhibit a power of between about 100 and about 1500 watts and preferably between about 500 and about 1000 watts. Water cooling of the laser head is required to maintain the life of the diodes and is conventionally accomplished by means of a water-to-air chiller unit (not shown). Multi-bar diode lasers of this type are commercially available from Opto Power Corporation, 3321 E. Global Loop, Tucson, Ariz. 85706. - Mandrel 12 must, of course be collapsible or otherwise removable once the finished structure is completed by completion of the wrapping operation. Similarly,
surface 24 ofmandrel 12 should be of a material that will resist adhesion to melted and cooledbraze coating 36, or matrix metal when performed as described in connection withFIG. 3 , and simultaneously minimize conductive heat loss from the parts during fabrication to provide better and more accurate process control, although in the latter case, alternative process controls may be used to minimize the effects of the material onsurface 24 on the brazing/welding process. In one embodiment of the present invention, a suitable ceramic tube fabricated from shale and fire clay was cut into three segments and attached to a chuck arrangement to allow for expansion and contraction. In this case, the amount of material removed during the cutting operation was minimized to preventsurface 24 from being out of round. - Referring now to
FIG. 3 , it is to be noted that the only fundamental difference between the embodiment depicted therein and inFIG. 2 is that in the embodiment depicted inFIG. 3 nobraze coating 36 and consequently brazingmaterial front 34 is present, rather amatrix material front 34A that is in effect a weld bead of molten matrix material derived from both opposing surfaces ofprepeg tape 22 is formed to consolidate the sequentially applied layers ofprepeg tape 22 asmandrel 12 is rotated. Of course, in such an instance, no mechanism is required for the application ofbraze coating 36. In all other respects, except those specifically differentiated hereinabove, the method and apparatus of this embodiment are identical to that of the previously described embodiment wherein a brazing layer is utilized. In the embodiment depicted inFIG. 3 , it is fair to characterize the layer bonding process as one of laser welding of the sequentially applied layers ofprepeg tape 22. - As shown in
FIG. 1 , immediately afterjunction 20prepeg tape 22 is contacted on itsreverse side 40 by compactingwheel 28 to accomplish consolidation. As withsurface 24 ofmandrel 12, compacting wheel is preferably fabricated from a ceramic material to minimize conductive heat loss fromjunction 20 during consolidation. A highly preferred material forcompaction wheel 28 is zirconium phosphate which exhibits these and other suitable properties. Of course, suitable alternative process controls can make the selection of materials forcompaction wheel 28 less critical.Compaction wheel 28 is arranged to ride at top dead center ofmandrel 12 and is guided in its movement bycarriage assembly 26.Compaction wheel 28 in addition to providing compressive energy for consolidation also has a second important function, in that it provides a V-shaped cavity atjunction 20 thereby reducing reflective losses by trapping some of the infrared radiation ofbeam 18 and creating a “multiple bounce” situation where most of the incoming radiation is used for heating and less of such radiation is lost due to reflection from the various surfaces atjunction 20. -
Preheat lamps 30, and where used post heat lamp(s) 32 preferably comprise reflector lamps as line sources of infrared energy to preheat or postheat prepeg tape 22 prior to or after exit fromjunction 20.Preheat lamps 30 preferablyheat prepeg tape 22 to a temperature of about 500° F. in order to reduce the heating load onlaser 16. As will be obvious to the skilled artisan, such preheating may not be required if a higher powered laser is used. Post heating lamp(s) 32 are similarly configured, and if and where applied can be used to control the cool down ofprepeg tape 22 as it exitsjunction 20 to reduce the thermal stresses that may be induced by the brazing/welding process. - According to another alternative preferred embodiment of the present invention, a
rotary ball vibrator 42 that induces vibration in the range of from about 1000 to about 25000 vibrations per minute is added toconsolidation apparatus 10 to provide a more thorough mixing of moltenbraze alloy front 34 atjunction 20.Rotary ball vibrator 42 is attached to ametal rod 44 that contacts prepegtape 22 just before it entersjunction 20. The presence ofrotary ball vibrator 42 causesprepeg tape 22 to vibrate at the same frequency asvibrator 42 which in turn induces oscillations infront 34 atjunction 20. Thus, these oscillations occur injunction 20 asprepeg tape 22 is addressed bycompaction wheel 28. - According to yet another alternative preferred embodiment of the present invention, a flow of inert gas is applied over the heated area at
junction 20 to minimize the formation of oxides infront 34 during brazing/welding. Free flowing argon, nitrogen or the like inert gas directed to the area ofjunction 20 appears to provide such benefit. -
Optical pyrometer 33 may be included to provide temperature feedback information to the control circuits oflaser 16 thereby assuring that the appropriate amount of heat is being applied atjunction 20 to achieve satisfactory melting ofbraze coating 36, or welding in the non-braze coated embodiment, and consolidation as described above. - Finally, at least in process development and refinement situations, it can be desirable to include a video camera (not shown) to closely monitor the area of
junction 20 to obtain the appropriate operating parameters for a specific givenprepeg tape 22 andbraze coating 34 composition. - In practice, the method of the present invention is carried out using the above-described
apparatus 10 by first wrapping an initial turn of a suitable prepeg tape of, for example, pure aluminum, 1100 alloy aluminum or any other suitable aluminum, titanium, magnesium etc. metallic matrix containing a ceramic reinforcing material, for example, Nextel 610™ aluminum oxide 1500 denier fibers commercially available from the 3M Corporation, Minneapolis, Minn. According to a specifically preferred embodiment of the present invention the prepeg tape, whatever its composition, is about 0.5 inches wide, 0.015 inches thick with a rectangular cross section aboutmandrel 12. As will be apparent to the skilled artisan, the particular dimensions ofprepeg tape 22 are largely a matter of the particular consolidatingapparatus 10 that is used, i.e. its dimensions, and, within easily understood limitations, the process is feasible with virtually any width and thickness ofprepeg tape 22 with appropriate alternative selection of consolidation conditions.Prepeg tape 22 is provided as a coil on a payoff for continuous feeding.Consolidation apparatus 10 is then activated.Mandrel 12 begins to turn,laser 16 is focused onjunction 20 andprepeg 22 is fed intojunction 20 for consolidation by compactingwheel 28. The specific process conditions are largely a matter of choice as dictated by the materials being consolidated (the AMC matrix alloy and the braze coating composition), the power oflaser 16, the rotational speed ofmandrel 12 etc. However, in the case of fabrication of the above-described prepeg tape bearing braze coatings of the types referred to in the examples below, melting temperatures in the range of from about 375 to about 1200° F. produced by a suitable laser operating at between about 100 and about 500 watts and prepeg tape feed rates on the order of between about 0.65 and 1.50 inches/sec. have been found useful and appropriate. In the case whereprepeg tape 22 bears nobraze coating 36 the power of the laser may be required to be significantly higher, for example, between about 500 and 1500 watts. - The following examples when considered in conjunction with the foregoing detailed description will serve to better illustrate the successful practice of the present invention.
- Prepeg tapes comprising Nextel 610™ fibers in pure aluminum were consolidated as described hereinabove using the following braze coatings and under the following tabularly presented operating conditions:
Braze Laser Braze Coating Temperature Power Tape Feed Rate 1) 96.5 Sn/3.5 Ag 430-500° F. 426 Watts 0.70 inches/sec. 2) 70 Sn/30 Zn 389-707° F. 110 Watts 1.06 inches/sec. 3) 84 Zn/11 Al/5Cu 715-845° F. 268 Watts 0.87 inches/sec. 4) 88 AL/12 Si 1070-1220° F. 373 Watts 1.27 inches/sec. - Under each of the foregoing conditions, satisfactory consolidated round structural shapes of the prepeg material indicated were fabricated.
- As the invention has been described, it will be apparent to the skilled artisan that the same may be varied in many ways without departing from the spirit and scope of the invention. Any and all such modifications are intended to be included within the scope of the appended claims.
Claims (11)
1.-13. (canceled)
14. An apparatus for the fabrication of structural members of metal matrix composites comprising:
a removable rotating mandrel having a peripheral surface;
a carriage mechanism;
a compaction device attached to said carriage mechanism so as to permit controlled traverse of said compaction device across said peripheral surface;
a metal matrix composite prepeg tape feeding mechanism that supplies metal matrix tape that addresses said peripheral surface to a junction between said peripheral surface and said compaction device; and
a fusing device generating a fusing beam that impacts said metal matrix tape in said junction causing it to fuse as said metal matrix tape passes under said compaction wheel.
15. The apparatus of claim 14 wherein said prepeg tape comprises a matrix of aluminum or an aluminum alloy encompassing ceramic fibers.
16. The apparatus of claim 15 wherein said laser comprises a stacked multi-bar infrared laser.
17. The apparatus of claim 16 wherein said stacked multi-bar infrared laser comprises optical lenses that shape the infrared beam into a pattern that matches the cross sectional dimensions of said prepeg tape.
18. The apparatus of claim 14 wherein said mandrel is collapsible so as to permit removal of multiple layers of applied prepeg tape therefrom when fabrication is complete.
19. The apparatus of claim 14 wherein said peripheral surface and said compaction wheel comprise ceramic materials.
20. The apparatus of claim 14 further comprising preheaters that heat said prepeg tape prior to entering said junction.
21. The apparatus of claim 20 wherein said preheaters comprise infrared reflector lamps.
22. The apparatus of claim 14 further comprising an optical pyrometer that addresses said junction and views said metal matrix prepeg tape in said junction and provides temperature feedback information for controlling the power of said laser or the rotation speed of said mandrel.
23. The apparatus of claim 14 further comprising a mechanism for inducing vibratory energy to said prepeg tape prior to entry into said junction at a frequency of between about 1000 and 15000 vibration per minute.