US20070125303A1 - High-throughput deposition system for oxide thin film growth by reactive coevaportation - Google Patents
High-throughput deposition system for oxide thin film growth by reactive coevaportation Download PDFInfo
- Publication number
- US20070125303A1 US20070125303A1 US11/293,346 US29334605A US2007125303A1 US 20070125303 A1 US20070125303 A1 US 20070125303A1 US 29334605 A US29334605 A US 29334605A US 2007125303 A1 US2007125303 A1 US 2007125303A1
- Authority
- US
- United States
- Prior art keywords
- heater
- substrate support
- support member
- chamber
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A heater for growing a thin film on substrates contained on a substrate support member includes a plurality of heater elements. The substrate support member containing the substrates is at least partially surrounded by the plurality of heater elements. At least two of the plurality of heater elements are moveable with respect to one another so as to provide external access to the substrate support member. An oxygen pocket is formed in one of the heater elements or a separate oxygen pocket member and is used for oxidation of the film on the substrates.
Description
- The field of the invention generally relates to devices and methods used to produce thin films on a substrate. More specifically, the field of the invention relates to devices and methods used to form high-temperature superconducting (HTS) films in-situ.
- Since the discovery in the mid 1980s of the perovskite family of HTS materials, extensive strides have been made in the ability to deposit high quality HTS films. Thin films formed from HTS materials are highly desirable for a variety of superconductive electronics applications including, for example, detectors, digital circuits, and passive microwave devices (e.g., HTS-based filters).
- Over the years, several techniques have been developed for the deposition of thin films of HTS oxide materials. These techniques include sputtering, pulsed laser deposition (PLD), and metal-organic chemical vapor deposition (MOCVD). Illustrative HTS oxide materials include Yttrium Barium Copper Oxide (YBCO), Bismuth Strontium Calcium Copper Oxide (BSCCO), Thallium Barium Calcium Copper Oxide (TBCCO), and Mercury Barium Calcium Copper Oxide (HBCCO). Of these materials, YBCO is currently the favored compound for many applications due to YBCO's relatively smaller conduction anisotropy, high superconductive critical current in a magnetic field, and good chemical stability. In addition, as compared to the other HTS compounds, the relative ease with which high quality, single phase thin films of YBCO may be grown is perhaps its greatest attribute.
- Nonetheless, thin film growth of these materials has still been difficult. In order to obtain high quality films, oriented, epitaxial growth (in-plane and out-of-plane) is necessary, meaning that the films can be grown only at high temperatures, typically above 700° C. Therefore, growth is only possible on a handful of single crystal substrates that satisfy strict requirements of chemical compatibility, lattice constant match, and thermal expansion match. In addition, the properties of the substrate must be suitable for the required application. For example, MgO is a substrate that meets the growth needs and also has sufficiently low loss for microwave applications.
- Growth of HTS materials is further complicated by the fact that these compounds typically comprise at least three metallic species which are in oxide form. The growth methods employed must therefore be strictly controlled in order to achieve the proper film stoichiometry and uniformity. Furthermore, in-situ growth of these materials requires them to be oxygenated as they are grown, which is generally not compatible with many conventional techniques such as physical vapor deposition. Moreover, in certain applications, growth of HTS thin films on two sides of a single substrate is required.
- Conventional in-situ growth techniques such as sputtering, pulsed laser deposition, and metal-organic chemical vapor deposition have all been successfully used for the growth of HTS thin films. There are, however, serious limitations to these methods including slow growth rate (sputtering), difficulty in controlling composition, poor reproducibility, poor film uniformity (sputtering, MOCVD), difficulty of achieving large-area deposition (PLD), and difficulty of scalability (all aforementioned techniques).
- More recently, the technique of reactive coevaporation using a rotating oxygen-pocket heater has been used which addresses many of the limitations discussed above. In this technique, the substrates are held by gravity on a rotating substrate support member or turntable. The substrate support member containing the substrates is surrounded on the top, bottom, and sides by a cylindrically-shaped heater (i.e., a heater body) that radiatively heats the substrates to a uniform high temperature necessary for reaction. The substrate support member is rotatable inside the heater body and, during a portion of the rotation, is exposed to a vacuum chamber via a window disposed in the underside portion of the heater body. The vacuum chamber surrounds the heater body and contains the deposition sources for the reaction.
- In one embodiment, the heater body also includes an oxygen pocket region located in the bottom portion of the heater body. Oxygen is fed into the oxygen pocket region and thereby exposes the substrates to oxygen during a portion of the rotation. A large pressure differential is created between the oxygen pocket region and the surrounding vacuum chamber. The pressure differential is maintained by a narrow gap formed between the rotating substrate support member and the oxygen pocket region, thereby resulting in a low rate of oxygen leakage from the oxygen pocket.
- During the part of the rotation where the substrates are exposed to the vacuum chamber, the thin film constituents (typically metallic species) may be deposited onto the underside of the substrates using typical PVD techniques such as evaporation. Oxidation reactions take place when the substrates are rotated on the substrate support member into the oxygen pocket.
- Reactive coevaporation using a rotating oxygen pocket heater has several advantages including, for example, the ability to evaporate the metallic species in vacuum without complications that would arise under the high oxygen pressure conditions needed for growth of HTS films. In addition, the rotating oxygen pocket heater technique permits deposition on substrates having a relatively large surface area. Moreover, this technique has the ability to deposit HTS materials on multiple substrates at once. Because the heater approximates a blackbody radiator, different substrate materials can also be incorporated simultaneously even if they have different absortivities. Finally, reactive coevaporation using the rotating oxygen pocket heater allows one to deposit HTS materials on both sides of the substrate sequentially because neither side of the substrate is in direct contact with the heater body.
- While reactive coevaporation methods are well suited for the formation of HTS thin films, there remains a need to increase the capacity and stability of such methods so that reactive coevaporation can be implemented into a commercially viable manufacturing process. There thus is a need to increase the throughput and reliability of reactive coevaporation deposition systems and methods.
- In a first aspect of the invention, a device for performing reactive coevaporation includes a heater chamber containing a pocket heater, a source chamber containing a source holder, the source chamber being coupled to the heater chamber through a valve, and a transfer chamber containing an extendable transfer arm, the transfer chamber being coupled to the heater chamber via a valve, the extendable transfer arm being moveable into and out of the heater chamber via the valve, wherein the heater chamber, source chamber, and transfer chamber are coupled to a vacuum source. The device may be used to form oxide thin films, including for example, rare earth (RE) oxides such as (RE)BCO.
- In another aspect of the invention, a device for performing reactive coevaporation on at least one substrate having a front and back surface includes a heater chamber containing a pocket heater, a source chamber containing source holder, the source chamber being coupled to the heater chamber via a valve, a substrate support member for securing the at least one substrate, the substrate support member securing the at least one substrate by contacting one or both of the front and back surface of the at least one substrate, and an extendable transfer arm for holding the substrate support member, the extendable transfer arm being rotatable so as to expose either or both of the front or back surface of the at least one substrate toward the source chamber.
- In still another aspect of the invention, a pocket heater includes a heater cap or upper heater zone comprising a circular top plate having a cylindrical side wall about its periphery, the circular top plate and side wall having a heater element (e.g., heater wire) disposed therein, a lower heater plate having an upper and lower surface, a portion of the lower heater plate having a window disposed therein passing from the upper surface to the lower surface of the lower heater plate and a recessed pocket formed in a portion of the upper surface of the lower heater plate, and wherein the heater cap is moveable in a direction that is perpendicular with respect to a surface of the lower heater plate.
- In another aspect of the invention, a device for performing reactive coevaporation includes a pocket heater disposed in a heater chamber, a loading transfer chamber containing an extendable transfer arm, the loading transfer chamber being coupled to the heater chamber containing the pocket heater by a valve, and an unloading transfer chamber containing an extendable transfer arm, the unloading transfer chamber being coupled to the heater chamber containing the pocket heater by a valve.
- In still another aspect of the invention, a method of performing reactive coevaporation includes the steps of providing a pocket heater disposed in a heater chamber, the pocket heater including vertically moveable spindle passing through a portion of the pocket heater, providing a loading transfer chamber containing an extendable transfer arm, the loading transfer chamber being coupled to the heater chamber containing the pocket heater by a valve, and providing a source chamber containing source material.
- The substrate support member containing at least one substrate is loaded onto the extendable transfer arm inside the loading transfer chamber. Vacuum conditions are established inside the loading transfer chamber using a vacuum pump coupled to the loading transfer chamber. The valve between the heater chamber containing the pocket heater and the loading transfer chamber is then opened and the substrate support member containing at least one substrate is extended into the pocket heater using the extendable transfer arm. The spindle is raised so as to lift the substrate support member containing at least one substrate off the extendable transfer arm. The extendable transfer arm is retracted into the loading transfer chamber, and the source material is evaporated after the correct substrate temperature, pocket pressure, and substrate support member rotation speed have been established.
- In still another aspect of the invention, a device includes a heater cap or upper heater zone comprising a circular top having a cylindrical side wall about its periphery, the circular top and side wall having a heater element disposed therein, a lower heater plate having an upper and lower surface, a portion of the lower heater plate having a window disposed therein passing from the upper surface to the lower surface of the lower heater plate and a recessed pocket formed in a portion of the upper surface of the lower heater plate, a z-adjust assembly.
- In one aspect of the invention, the z-adjust assembly includes a rotatable spindle projecting through a center hole in the lower heater plate, a motor mechanically coupled to the spindle, and a roller. The inclined cam engages with the roller, wherein movement of the inclined cam in the horizontal direction imparts movement of the rotatable spindle, motor, and roller in the z-direction.
- In still another aspect of the invention, a device for performing reactive coevaporation includes a heater chamber containing a pocket heater, a source chamber containing source holder, the source chamber being coupled to the heater chamber via a valve, a monitor chamber containing at least one deposition monitor, the monitor chamber being coupled to the heater chamber containing the pocket heater via a valve.
- In yet another aspect of the invention, a device for performing reactive coevaporation includes a heater chamber containing a pocket heater, a source chamber containing coevaporation source material, the source chamber being coupled to the heater chamber via a valve.
- In another embodiment of the invention, a method of loading and unloading a substrate support member in a pocket heater includes the steps of: (1) providing a pocket heater having a heater cap (e.g., an upper heating zone) including a circular top and a cylindrical side wall about its periphery; (2) providing a lower heater plate (e.g., lower heating zone) having an upper and lower surface, a portion of the lower heater plate having a window disposed therein passing from the upper surface to the lower surface of the lower heater plate and a recessed pocket formed in a portion of the upper surface of the lower heater plate; (3) providing a first rotatable substrate support member for holding a plurality of substrates, the first rotatable substrate support member being interposed between the lower heater plate and the heater cap; (3) moving the heater cap into an unload position disposed away from the first rotatable substrate support member in a direction perpendicular to the upper surface of the lower heater plate; (4) removing the first rotatable substrate support member from the pocket heater; (5) inserting a second rotatable substrate support member into the pocket heater, the second rotatable substrate support member interposed between the heater cap and the lower heater plate; and (6) moving the heater cap into a loaded position disposed adjacent to the second rotatable substrate support member.
- It is an object of the invention to provide a device and method that increases the throughput of multi-component HTS films deposited/grown on substrates using reactive coevaporation. It is a further object of the invention to separate various aspects of the deposition process (e.g., source material evaporation, loading, unloading, monitoring, deposition) into interlinked but separate chambers. In this regard, it is an object of the invention to couple these chambers to vacuum sources which can be pumped independently of the remaining chambers, thereby limiting the overall pump down time of the device when vacuum conditions are broken in one of the separate chambers.
- These and further objects of the invention are described in more detail below.
-
FIG. 1 illustrates a perspective view of a device used in the high-throughput deposition of oxide thin films by reactive coevaporation according to one preferred aspect of the invention. -
FIG. 2A illustrates a substrate support member gravitationally held on a spindle. -
FIG. 2B illustrates the underside of the substrate support member shown inFIG. 2A . -
FIG. 3A illustrates a substrate support member gravitationally held on a spindle. -
FIG. 3B illustrates the underside of the substrate support member shown inFIG. 3A . -
FIG. 4A illustrates a substrate support member that is held circumferentially via a substrate support member holder. -
FIG. 4B illustrates a substrate support member holder and spindle. -
FIG. 5A illustrates a deposition chamber wherein the motor driving the spindle is located externally (top) with respect to the deposition chamber. -
FIG. 5B illustrates a deposition chamber wherein the motor driving the spindle is located externally (bottom) with respect to the deposition chamber. -
FIG. 6A illustrates a motor coupled to a spindle via a coupler. -
FIG. 6B illustrates a motor coupled to a spindle via gears. -
FIG. 6C illustrates a motor coupled to a spindle via a belt. -
FIG. 7A illustrates a top down view of a heater element having a slot therein for receiving a substrate support member. The width of the slot is represented by angle α. -
FIG. 7B illustrates a top down view of a heater element having a slot therein for receiving a substrate support member. The width of the slot is represented by angle β. -
FIG. 8A illustrates a heater element through which a spindle passes. -
FIG. 8B illustrates a heater element through which a spindle partially passes. -
FIG. 9 illustrates a substrate support member interposed between a lower heater plate (e.g., zone) and an upper heater plate (e.g., zone). -
FIG. 10A illustrates one embodiment of a separable heater element. -
FIG. 10B illustrates another embodiment of a separable heater element. -
FIG. 10C illustrates another embodiment of a separable heater element. -
FIG. 10D illustrates another embodiment of a separable heater element. -
FIG. 10E illustrates another embodiment of a separable heater element. -
FIG. 11 illustrates an embodiment of a heater element that is moveable with respect to a lower heater plate. -
FIG. 12 illustrates an embodiment of a lower heater plate that is moveable with respect to a stationary heater element. -
FIG. 13 illustrates a substrate support member and a lower heater plate that are moveable with respect to one another. -
FIG. 14 illustrates a partially exploded view of the pocket heater used inside the heater chamber of the device shown inFIG. 1 . -
FIG. 15 illustrates the top side of the lower plate heater portion of the pocket heater. The oxygen pocket and window passing through to the source chamber are illustrated. -
FIG. 16A illustrates a side view of an alternative embodiment of the pocket heater used inside the heater chamber of the device shown inFIG. 1 . -
FIG. 16B illustrates a bottom, perspective view of the pocket heater illustrated inFIG. 16A . -
FIG. 17A illustrates a vertically oriented spindle holding a substrate support member wherein the spindle passes through the top of a deposition chamber. -
FIG. 17B illustrates a vertically oriented spindle holding a substrate support member wherein the spindle passes through the bottom of a deposition chamber. -
FIG. 18 illustrates an embodiment of a z-adjust assembly wherein the motor and spindle are movable as a single unit. -
FIG. 19A illustrates a front view of a z-adjust device wherein a shaft of a motor is coupled via coupler to the spindle. -
FIG. 19B illustrates a side view of the z-adjust device ofFIG. 19A . -
FIG. 19C illustrates a front view of a z-adjust device wherein a shaft of a motor is coupled to the spindle via a belt. -
FIG. 20A illustrates a front view of a z-adjust device that uses a horizontal feedthrough and an elliptically-shaped cam. -
FIG. 20B illustrates a side view of the z-adjust device ofFIG. 20A . -
FIG. 21A illustrates a front view of a z-adjust device that uses a horizontally-oriented rotary feedthrough that drives a scissor jack device to raise and lower a vertically oriented support plate. -
FIG. 21B illustrates a side view of the z-adjust device ofFIG. 21A . -
FIG. 22 illustrates a z-adjust device that uses a vertically-oriented rotary feedthrough driving a jack screw. -
FIG. 23 illustrates a z-adjust device that uses a horizontal feedthrough and cam to raise and lower the vertically-oriented support plate. -
FIG. 24 illustrates the spindle shaft and motor assembly located on a vertical support plate. -
FIG. 25 illustrates a substrate support member containing substrates loaded on top of the lower plate heater. -
FIG. 26 illustrates the spindle shaft and motor assembly located on a vertical support plate. -
FIG. 27 illustrates a cam device used to raise and lower the spindle shaft and motor assembly shown inFIG. 26 . -
FIG. 28A illustrates one aspect of a load-lock chamber used to store one or more QCMs. -
FIG. 28B illustrates another aspect of a load-lock chamber used to store one or more QCMs. -
FIG. 29 illustrates a load-lock chamber having three QCMs disposed therein. -
FIG. 30 illustrates another embodiment of a load-lock chamber in which the underside of the chamber includes a hole therein for providing access to the deposition chamber. -
FIG. 31A illustrates another embodiment of a load-lock chamber. The valve to the load-lock chamber is located inside the deposition chamber. -
FIG. 31B illustrates another embodiment of a load-lock chamber. The valve is disposed on the underside of the load-lock chamber and provides access to the deposition chamber when opened. -
FIG. 31C illustrates a top down view of the load-lock chamber shown inFIG. 31B . -
FIG. 32 is a perspective view of the monitor chamber in an open configuration showing the deposition monitors used to monitor the evaporation of source material contained in the source chamber. -
FIG. 33A illustrates a substrate support member and substrate according to one preferred aspect of the invention. -
FIG. 33B illustrates a transfer chamber used to load a substrate support member into the heater chamber of the device shown inFIG. 1 . -
FIG. 34 illustrates a computer used in for controlling as well as acquiring data from the device shown inFIG. 1 . -
FIG. 1 illustrates one embodiment of adevice 2 used in the high-throughput deposition of oxide thin films by reactive coevaporation. Thedevice 2 may also be used to deposit non-oxide materials such as, for example, Magnesium diboride (MgB2). U.S. patent application Ser. No. 10/726,232, entitled “Growth of In-Situ Thin Films By Reactive Evaporation”, incorporated by reference as if fully disclosed herein, discloses a method of forming MgB2 using a pocket heater device. It should be understood that a variety of materials may be deposited using thedevice 2. These include by way of illustration and not limitation, complex oxides, ruthenates, manganates, titanates, -magnetic materials, piezoelectrics, dielectrics, ferroelectrics, semiconductors, nitrides, etc. Thedevice 2 preferably includes several subsystems located on aframe 4 or other support structure which are integrated to form theoverall device 2. Thedevice 2 may include a plurality of separate chambers, namely, aheater chamber 10, asource chamber 30, twotransfer chambers monitor chamber 60. -
Heater chamber 10 is coupled to a source ofvacuum 12 such as, for example, a vacuum pump. The source ofvacuum 12 is separated from theheater chamber 10 by avalve 14 such as, for instance, a gate valve. Prior to the deposition of HTS film, theheater chamber 10 is evacuated using the source ofvacuum 12. - The
device 2 also includes asource chamber 30 which contains the source of flux material (80 a, 80 b, 80 c) used in the deposition process. Thesource chamber 30 is similarly connected to a source ofvacuum 32 such as, for example, a vacuum pump. Thesource chamber 30 is separated from the source ofvacuum 32 by avalve 34 such as, for instance, a gate valve. - A
valve 36 is also disposed between theheater chamber 10 and thesource chamber 30. Preferably, thevalve 36 is a gate valve. The gated arrangement advantageously allows the two chambers (i.e.,heater chamber 10 and source chamber 30) to be pumped to vacuum separately. This is important because, for example, the flux sources located in thesource chamber 30 can be changed without disturbing theheater chamber 10 or exposing it to atmospheric conditions. Similarly, maintenance or the like can be performed on components contained in theheater chamber 10 without disturbing the vacuum conditions inside thesource chamber 30. This arrangement reduces the total amount of “pump down” time needed because the volume of space that must be pumped is reduced by isolating the various subsystems of thedevice 2. This aids in increasing the overall throughput of thedevice 2. - Still referring to
FIG. 1 , thedevice 2 includes twotransfer chambers heater chamber 10. Preferably, onetransfer chamber 40 is a loading chamber and the remainingtransfer chamber 50 is an unloading chamber. Bothtransfer chambers vacuum transfer chambers vacuum transfer chambers heater chamber 10 byvalves 41. Unloadingchamber 50 may also be used as an oxygen soak. - In one aspect of the invention, the
device 2 thus consists of five separate vacuum chambers (i.e.,heater chamber 10, asource chamber 30, twotransfer chambers device 2 may have fewer than fivechambers 50 or, alternatively, more than fivechambers 50. Each of these chambers may be pumped to vacuum pressures independent of the other chambers if desired. In this regard, any one or multiple chambers may be vented to atmosphere while the remaining chambers remain under vacuum. This eliminates the need to pump down theentire device 2 each time it is opened, for example, to clean parts of thedevice 2, for reloading flux sources into thesource chamber 30, for replacing and/or adjusting deposition monitors 64 in themonitor chamber 60 or in theheater chamber 10, for loading/unloading of the substrate support member 110 (e.g., carrier) into theheater chamber 10, or for maintenance or the like on the components in one or more the chambers. - Referring to
FIGS. 2A, 2B , 3A, 3B, 4A, 4B, 5A, and 5B in one aspect of the invention, asubstrate support member 110 is held on a vertically orientedspindle 112 through acenter hole 113. The vertically orientedspindle 112 may hold thesubstrate support member 110 either from above or below.FIGS. 2A and 2B illustrate an embodiment wherein thesubstrate support member 110 is held from below by thespindle 112 passing through thecenter hole 113. In this embodiment, thesubstrate support member 110 is gravitationally held by thespindle 112. In another embodiment, as shown inFIGS. 3A and 3B , the vertically orientedspindle 112 holds thesubstrate support member 110 from above. For example, thespindle 112 may pass through acenter hole 113 and terminate in anattachment member 115 that secures thesubstrate support member 110. In yet another embodiment, as shown inFIGS. 4A and 4B ,substrate support member 110 is held circumferentially via a substratesupport member holder 117. - The
substrate support member 110 may be rotated by rotational movement of thespindle 112. A frictional fit between thesubstrate support member 110 andspindle 112 imparts rotational movement of thespindle 112 to thesubstrate support member 110. The spindle 112 (and thus substrate support member 110) may be driven via a motor (such asmotor 122 described below). Themotor 122 may be located either within a deposition chamber (e.g., chamber 10) containing thesubstrate support member 110 or external to thedeposition chamber 10, as shown inFIGS. 5A and 5B . In the case where the motor is located outside thedeposition chamber 10 holding thesubstrate support member 110, thespindle 112 may be connected to a rotary vacuum feedthrough located either above or below thesubstrate support member 110 and vacuum chamber. The motor may be mechanically coupled directly to thespindle 112 as is shown inFIGS. 5A and 6A . Alternatively, the motor may be mechanically coupled to thespindle 112 viagears 111,belt 126, chain, or the like, for example, as shown inFIGS. 5B, 6B and 6C. - As stated above, the
substrate support member 110 is at least partially contained in aheater chamber 10 that is used during thin-film formation. In one aspect of the invention, theheater chamber 10 contains apocket heater 100 that is a near-blackbody radiator. Thepocket heater 100 may include one or more heating elements 101 (e.g., zones) and aslot 10 b (as shown inFIGS. 7A and 7B ) contained therein through which asubstrate support member 110 may be inserted and retracted via a transfer mechanism (e.g., a transfer arm). Thespindle 112 may then be extended from either above or below theheater 100 in order to support and rotate thesubstrate support member 110.FIGS. 8A and 8B illustrate two exemplary embodiments wherein thespindle 112 passes through a heating element in theheater chamber 10. - The above arrangement permits the
substrate support member 110 to be introduced into and removed from the heater in one direction, for example, as shown inFIG. 7A . Alternatively, as shown in the embodiment inFIG. 7B , thesubstrate support member 110 may be introduced into and removed from the heater in multiple directions (e.g., from the sides) by use of a longer slot 10(b). - During the thin film formation process, there may be a minimum temperature above which the
substrate support member 110 cannot be removed from theheater chamber 10. This may be because thesubstrate support member 110 is too hot or because the films being deposited (e.g., (RE)BCO) are too far above their structural phase transition temperature to be removed from theheater chamber 10. Consequently, if thesubstrate support member 110 remains in close proximity to theheater element 101, the cooldown time of the substrates 116 (e.g., wafers) will be limited to that of theheater element 101. Because thesubstrate support member 110 should be heated uniformly, theheater element 101 is generally large and requires a long cooldown time. The overall cooldown time may be reduced by using cooling coils or the like to extract heat contained in theheater element 101 andsubstrate support member 110. Even using cooling devices such as coils and the like, the cooldown time of thesubstrate support member 10 and associatedsubstrates 116 is limited by the heater components. Ideally, thesubstrate support member 110 andsubstrates 116 may be rapidly cooled by physically separating the substrate support member 110 (and substrates 116) from theheater element 101. - When a
pocket heater 100 is used in theheater chamber 10, thesubstrate support member 110 should be located close to the oxygen pocket region because a small gap is required to be maintained near the oxygen pocket. In one embodiment, the oxygen pocket region may be formed integral with a lower heater zone or element. In such case, the top and/or side heater zones may be located farther from thesubstrate support member 10 as is shown, for example, inFIG. 9 (showing top zone disposed some distance from substrate support member 110). Such arrangement allows passage of thesubstrate support member 110 into and out of the heater andheater chamber 10. However, the heater zones would have to be hotter than the desiredsubstrate 116 temperature since theheater 100 is no longer acting as a blackbody radiator. If the oxygen pocket is not heated directly, the heating element(s) 101 would have to be far hotter than the desired temperature of thesubstrates 116 which may make the design complicated and impractical. - In one aspect of the invention, a solution is proposed to physically separate the heater element(s) 101 from the
substrate support member 110 following deposition of a thin film. This may be accomplished by moving the heating element(s) 101 away from thesubstrate support member 10 or alternatively, moving thesubstrate support member 10 away from the heating element(s) 101. Advantageously, thesubstrate support member 110 may be removed from the heating element(s) 101 so that it can be freely or actively cooled in oxygen. Moreover, by moving thesubstrate support member 110 relative to the heating element(s) 101 (or vice versa) this aids in the transfer of the substrate support member 110 (and associated substrates 116) into and out of the deposition chamber (e.g., heater chamber 10). - Assuming that the
pocket heater 100 is or approximates a blackbody-type oven, FIGS. 10A-E, 11, and 12 illustrate several exemplary ways of moving the heating element(s) 101 relative to thesubstrate support member 110. Generally, the embodiments shown in FIGS. 10A-E, 111 and 12 permit thesubstrate support member 110 to move in the vertical direction (i.e., raised) from aheater element 101 from either above or below and also to be moved horizontally out of theheater chamber 10.FIG. 10A , for example, illustrates an embodiment in which the heating elements 101 (e.g., top and side heating zones, or top, side, and lower heating zones) are separated into two halves by movement of each respective half in the direction of arrows A and B.FIG. 10B illustrates an embodiment in which avertical hinge 107 is provided that permits the two halves to open.FIG. 10C illustrates an embodiment in which a horizontally positionedhinge 107 permits the opening of the top andside heater elements 101.FIG. 10D illustrates an embodiment wherein a horizontally positionedhinge 107 permits thetop heater element 101 or zone to flip open with respect to the remaining heater element 101 (e.g. side heater element). In yet another embodiment, as shown inFIG. 10E , avertical hinge 107 permits thetop heater element 101 to pivot or swing with respect to the remaining heater element(s) 101. -
FIGS. 11 and 12 illustrate additional embodiments in which theheater element 101 includes a bottom heater element orzone 101 a (e.g., lower heater plate) and two upper heater elements orzones FIG. 11 , the twoupper heater zones lower heater zone 101 a, thereby enabling separation of theheater element 101 from thesubstrate support member 110 contained therein (not shown inFIGS. 11 and 12 ). In still another embodiment, as shown inFIG. 12 , theupper heater zones lower heater zone 101 a is moveable in a vertical direction.FIG. 13 illustrates aheater element 101 a that is moveable with respect to a moveablesubstrate support member 110. Thisheater element 101 a may or may not incorporate an oxygen pocket. - In one aspect of the invention, the
heater chamber 10 contains a rotationally drivenpocket heater 100 which is used to deposit and/or grow multi-component HTS oxide thin films.FIG. 14 illustrates the various components used for thepocket heater 100. Thepocket heater 100 includes heated cap portion 102 (e.g.,upper heating zone 101 b as shown inFIGS. 11 and 12 ) which includes a circular upper plate surface 102(a) and a downwardly projecting cylindrical side wall 102(b) (heating zone 101 c as shown inFIGS. 11 and 12 ) which forms an interior portion 102(c) into which various components of thepocket heater 100 are inserted (described below). Theheated cap portion 102 may be fabricated from insulated heater wire (heating element) that is wrapped to form the upper surface 102(a) and the cylindrical side 102(b) wall. Preferably, the upper surface 102(a) and the cylindrical side wall 102(b) each are formed from a single segment of insulated wire such that the upper surface 102(a) and cylindrical side wall 102(b) may be heated independently of one another for temperature uniformity. Current is run through the insulated wires to generate heat. - The
heated cap portion 102 of thepocket heater 100 is advantageously moveable in the z-direction to open thepocket heater 100 so that the substrate support member 110 (described below) can be loaded into thepocket heater 100 prior to thin-film deposition and removed after deposition. Theheated cap portion 102 is, for instance, secured to anactuator 103 which extends through a top wall of the heater chamber as is seen inFIG. 1 . Theactuator 103 provides the vertical movement (i.e., motion in the z-direction) to theheated cap portion 102 of thepocket heater 100. - Referring to
FIG. 14 andFIG. 15 , in one aspect of the device, thepocket heater 100 includes a lower heater plate 104 (e.g.,lower heater zone 101 a as shown inFIGS. 11 and 12 ) which is a third, independent heating zone. Thelower plate heater 104 is stationary and may be anchored to the top, bottom, or side walls of theheater chamber 10. Thelower heater plate 104 is preferably formed from a single piece of metal, preferably INCONEL, that is machined into the desired shape. Of course, theheater plate 104 may be formed from other materials. Thelower plate heater 104 is machined to include a window opening 104(a) (best seen inFIG. 15 ) which passes completely through the plate and is exposed to thesource chamber 30 and source flux contained therein. - The
lower plate heater 104 further includes a pocket 104(b) (as best seen inFIG. 15 ) which is machined into the upper surface of thelower plate heater 104. During operation of thedevice 2, for example, oxygen (O2) gas is introduced into the pocket 104(b) for the reaction portion of thin-film growth/deposition. The oxygen gas is introduced into the pocket 104(b) by one ormore ports 105. The underside of the lower plate heater 104(c) includes a pocket (not shown) into which is brazed insulated thermal wiring. Current is run through this wiring to heat thelower plate heater 104. U.S. Pat. No. 5,126,533, which is incorporated by reference as if set forth fully herein, discloses a method of brazing insulated wire to form a heater of this type. - Alternatively, a wholly separate
oxygen pocket member 108 may exist independent of the lower heater zone. Theoxygen pocket member 108 includes anoxygen pocket 108 a that may not be part of the lower heater zone, as shown, for example, inFIGS. 16A and 16B . Thus, theoxygen pocket member 108 may or may not contain heating elements. Generally, the purpose of theoxygen pocket 108 a is to provide a localized region of oxygen adjacent to the substrates for film oxidation. In this arrangement, theoxygen pocket member 108 andsubstrate support member 110 both are contained within the quasi-blackbody heater, the heating elements of which may surround both theoxygen pocket member 108 and support plate on multiple or all sides. Theoxygen pocket member 108 is preferably formed from a single piece of metal, such as, for example, INCONEL, that is machined into the desired shape. Of course, theoxygen pocket member 108 may be formed from other materials. Theoxygen pocket member 108 is machined to include awindow opening 108 b which passes completely through themember 108 and is exposed to thesource chamber 30 and source flux contained therein. In this embodiment, thelower heater zone 101 a may be fabricated from insulated heater wire (heating element) that is wrapped. Thelower heater zone 101 a may be formed from a single segment of insulated wire such that thelower heater zone 101 a, andheater zones - Referring back to
FIG. 14 andFIG. 16A , thepocket heater 100 preferably includes aheat shield 106 disposed beneath thelower plate heater 101 a. As seen inFIG. 14 , theheat shield 106 includes a window 106(a) therein which provides access to the window opening 104(a) of thelower plate heater 104 and to thesource chamber 30 containing the source of flux. - With reference now to
FIGS. 17A, 17B , 18, 19A, 19B, 19C, 20A, 20B, 21A, 21B, 22, and 23, a z-adjustassembly 121 is provided to adjust the gap between the rotatingsubstrate support member 110 and the oxygen pocket 104(b) which may exist in the lower plate heater 104 (as shown, for example, inFIGS. 14 and 15 ) or as part of a separateoxygen pocket member 108. The width of the gap is important in order to maintain a high differential pressure between theoxygen pocket 104 b, 108 a and the deposition chamber. A small and uniform gap is desirable because it maximizes the oxygen pressure in thepocket 104 b, 108 a while minimizing any leakage of oxygen out of thepocket 104 b, 108 a. In addition, a small and uniform gap minimizes the background pressure in the deposition chamber. The size of the gap depends on the temperature of thelower plate heater 104 or of theoxygen pocket member 108 and thesubstrate support member 110 as well as their respective thermal histories. These components expand and contract as a function of temperature and they also distort to different degrees depending on the temperature profile and heater ramp cycle. - There thus is a need to adjust the gap in situ at any time during the heating cycle and deposition run in order to maintain the optimal gap width. To accomplish this, either the substrate support member 110 (containing the substrates 116) or the
lower plate heater 104 oroxygen pocket member 108 need to be able to be adjusted vertically as shown generally inFIG. 13 . - In one aspect of the invention, the
lower plate heater 104 oroxygen pocket member 108 is vertically adjusted through the use of cams, scissors, jack screws, lead screws, servos, and other mechanisms known to those skilled in the art. In another embodiment, thesubstrate support member 110 is vertically adjusted by vertical movement of thespindle 112 as is shown, for example, inFIGS. 17A, 17B , 18, 19A, 19B, 19C, 20A, 20B, 21A, 21B, 22, and 23.FIG. 17A illustrates a z-adjustable spindle 112 that holds thesubstrate support member 110 from the top and extends through the top of theheater chamber 10. Thespindle 112 may be connected or coupled to a motor (not shown) to rotationally drive thespindle 112 andsubstrate support member 110. Thespindle 112 may be adjusted in the vertical direction (arrow A) by using a linear vacuum feedthrough or linear slide (or other compatible z-adjust mechanisms).FIG. 17B illustrates an embodiment in which thespindle 112 holds thesubstrate support member 110 from below and extends through the bottom of theheater chamber 10. Thespindle 112 may be rotationally driven and raised/lowered in the direction of arrow A. - In one aspect of the invention, as shown in
FIG. 18 , theentire spindle 112 is located inside the deposition chamber (i.e., heater chamber 10) and is driven via an in-vacuum motor assembly such as in-vacuum motor 122 described in more detail below. - The
spindle 112 may be moved separately from the in-vacuum motor 122 if suitable coupling mechanisms are employed. Preferably, as disclosed below, themotor 122 andspindle 112 are moved together as a unit.FIGS. 19A and 19B illustrate an embodiment wherein a shaft of themotor 122 is coupled viacoupler 123 to thespindle 112. Themotor 122 is secured or otherwise attached to a vertically orientedsupport plate 118.FIG. 19C illustrates an alternative embodiment in which the in-vacuum motor 122 is secured to thespindle 112 via abelt 126 or the like. -
FIGS. 20A and 20B illustrate an embodiment in which arotary shaft 125 drives a rotatable cam 127 that moves a vertically orientedsupport plate 118.FIGS. 21A and 21B illustrate a horizontally-orientedrotary shaft 125 that drives ascissor jack device 129.FIG. 22 illustrates a vertically-orientedrotary shaft 125 driving ajack screw 131. In another embodiment, as shown for example inFIG. 23 , a linear feed-through 133 drives acam 132 that engages the vertically orientedsupport plate 118. In still another aspect of the invention, a second in-vacuum motor (not shown) may be used to drive the shaft/feedthrough (125, 133) and cam (127, 133), thereby minimizing the number of feedthroughs into the vacuum chamber. - Referring to
FIG. 24 andFIG. 25 , in one preferred aspect of the invention, a vertically orientedsupport plate 118 contains the spindle shaft and motor assembly 120 (z-adjust assembly). Thesupport plate 118 is moveable in the z-direction as shown, for example, by arrow A inFIG. 24 . The spindle shaft andmotor assembly 120 includes a motor 122 (preferably an in-vacuum motor 122) affixed to thesupport plate 118. The in-vacuum motor 122 includes adrive shaft 124 that is mechanically coupled to the spindle shaft 112(a) via abelt 126 or other linkage assembly. The in-vacuum motor 122 provides variable speed rotation to thesubstrate support member 110. Thesupport plate 118 further includes aroller 128 that is used to move the spindle shaft andmotor assembly 120 in the z-direction (explained in more detail below). In an alternative configuration, themotor assembly 120 may be provided ex-situ rather than in-situ. - Referring to
FIG. 24 andFIG. 25 , in one aspect of the invention, thesubstrate support member 110 is held between theupper heater zones pocket heater 100 and thelower heater zone 101 a. Thespindle 112 passes through center holes located in theheat shield 106 andlower plate heater 104. Thespindle 112 is rotatably coupled to a motor (described in more detail below) and is also movable in the z direction as shown by arrow A inFIG. 24 . -
FIG. 25 illustrates asubstrate support member 110 held on therotatable spindle 112. Thesubstrate support member 110 is preferably held gravitationally on an upper end of thespindle 112. Thesubstrate support member 110 includes a plurality ofholes 114 cut into thesubstrate support member 110 that accept and holdsubstrates 116 onto which the HTS material is deposited. Thesubstrates 116 may include substrates formed from, for example, magnesium oxide (MgO). Other materials may, of course, be used in accordance with the invention described herein. Thesubstrates 116 are preferably gravitationally held in place by small fingers or a ridge located along the lower edge of thesubstrate support member 110 where theholes 114 are located. Thus, thesubstrate support member 110 allows for essentially contact-less suspension of thesubstrates 116 during the heating and deposition process. - In addition, this configuration permits the growth and/or deposition of HTS thin films on a single side of the
substrate 116, namely, the lower side of the substrates 116(a) as seen inFIG. 25 . The upper side (or backside) of the substrates 116(b) is undisturbed and may be deposited in a subsequent deposition process by turning thesubstrate 116 over. - The
substrate support member 110 may be designed to accommodate a smaller number oflarger diameter substrates 116 or a larger number ofsmaller diameter substrates 116. In addition, theholes 114 in the substrate support member may also be designed to accommodatesubstrates 116 having different shapes. - The
device 2 advantageously permits thesubstrate support member 110 to be introduced into theheater chamber 10 in situ when thepocket heater 100 is opened, i.e., when theheated cap portion 102 is raised from thelower heater plate 104. Theheated cap portion 102 is then lowered over and around thesubstrate support member 110 during the run and can then be raised at the end of the run or at such time when thepocket heater 100 has cooled sufficiently. This ability to open thepocket heater 100 and load/unload thesubstrate support member 100 improves the cycle time of the deposition process because thesubstrate support member 110 does not have to be attached to thepocket heater 100 when thepocket heater 100 is cold. Rather, thesubstrate support member 110 can be loaded/unloaded after thepocket heater 100 is only partway through its heat-up and cool-down cycle. - In an alternative embodiment, the
substrate support member 110 allows for gripping thesubstrates 116 from both the lower 116(a) and upper surfaces 116(b) of the substrates simultaneously such that the entiresubstrate support member 110 may be flipped over between deposition runs. Preferably, thesubstrate support member 110 can be flipped over in-situ within theheater chamber 10 or within thetransfer chambers device 2, thereby significantly increasing the throughput of thedevice 2 and process. In this embodiment, thetransfer arm 45 may be rotatable about its long axis to flip thesubstrate support member 110 from one side to another. -
FIG. 26 illustrates the in-vacuum motor 122 used in accordance with a preferred aspect of the invention. The in-vacuum motor 122 includes a motor 122(a) housed inside an enclosed pressure vessel 122(b). The pressure vessel 122(b) effectively isolates the motor 122(a) from the vacuum conditions inside theheater chamber 10. Thedrive shaft 124 extends from the interior of the pressure vessel 122(b) to the outside of the pressure vessel 122(b) via a vacuum feedthrough (not shown). A pressure line 122(c) is secured to the pressure vessel 122(b) and delivers pressurized dry air inside the space of the pressure vessel 122(b) surrounding the motor 122(a). The pressurized dry air removes heat from the motor 122(a). Another conduit 122(d) is coupled to the pressure vessel 122(b) for delivering power and other control wires needed to operate the motor 122(a). - In an alternative embodiment, the
motor 122 may include an air or gas-driven motor which is powered by a source of compressed or otherwise pressured source of air or gas. Mechanical, electrical, or even optical feedback may be employed for speed control of themotor 122. -
FIG. 27 illustrates anexemplary cam device 130 used to impart z-direction movement (arrow A inFIG. 27 ) in the spindle shaft andmotor assembly 120. Thecam device 130 includes acam 132 having multiple inclined surfaces 132(a) and 132(b) for engaging with theroller 128 secured to thesupport plate 118. Preferably, thecam 132 is machined from a solid piece of stainless steel plate. First inclined surface 132(a) is inclined at an angle α while the second inclined surface 132(b) is inclined at an angle β. Preferably, angle β is greater than angle α. The different angles permit rough and fine course adjustments of the z-direction of the spindle shaft andmotor assembly 120. In an alternative configuration, thecam 132 may have a surface in the form of a continuous or semi-continuous arc (not shown). - The
cam 132 is moveable in the horizontal direction (arrow B inFIG. 27 ) by anactuator 134 which is connected to thecam 132 via a feed-through 133. Preferably, theactuator 134 is located external to theheater chamber 10 and includes a feed-through 133 passing through a side wall of theheater chamber 10. The movement of theactuator 134 is preferably controlled by a computer 200 (SeeFIG. 34 ) or microprocessor which allows dynamic movement of the spindle 112 (and thus substrate support member 110) in real time during the deposition process. In this regard, the gap between thesubstrate support member 110 holding thesubstrates 116 and thelower heater plate 104 can be optimized. - During operation of the
device 2, the second inclined surface 132(b), that is the surface with the steeper inclination, is used when thesubstrate support member 110 needs to be raised and lowered from thelower heater plate 104 for purposes of loading and unloading and for separating thesupport member 110 from the heater assembly. In contrast, the first inclined surface 132(a), namely, the surface with the shallower inclination, is used to allow fine z-axis adjustment of thesubstrate support member 110 for placing thesubstrate support member 110 as close as possible to thelower heater plate 104, thereby adjusting the gap between thesubstrate support member 110 and thelower heater plate 104. - The evaporation rate of metal species used to form HTS thin films should be carefully monitored and controlled in order to produce the desired film composition. While it has been known to use QCMs and associated electronics to monitor this deposition process, these crystals must generally be replaced after every deposition run, particularly because the signals generated by the crystals tend to become noisy from large amounts of deposited materials and oxides. Opening the
heater chamber 10 for the purpose of replacing these crystals is undesirable, however, because the large volume of theheater chamber 10 must then be cleaned and pumped again to vacuum. This adversely affects the throughput of the device. Thepresent device 2, however, with theseparate monitor chamber 60 allows for the replacement of the deposition monitors 64 (e.g., QCMs) without disturbing the heater chamber 10 (or other chambers). -
FIGS. 28A, 28B , 29, 30, 31A, 31B, and 31C illustrate aspects of themonitor chamber 60 in which the QCMs (or other rate, flux, or thickness monitors) are retractable within a load-lockedchamber 70 or housing that is differentially pumped. The load-locked chamber is coupled to a source ofvacuum 68 to provide the differential pumping aspect. The advantage of this embodiment is that it permits the replacement of QCMs (or other sensors) without breaking vacuum and opening the deposition chamber either during a run or between runs. In addition, the vacuum pumped load-lockedchamber 70 minimizes the QCM from oxygen exposure which degrades their rate monitoring abilities. -
FIG. 28A illustrates a load-lockedchamber 70 connected to a main deposition chamber (e.g., heater chamber 10). The load-lockedchamber 70 includes avalve 72 such as a gate valve to separate the interior of the deposition chamber from the interior of the load-lockedchamber 70. As seen inFIG. 28A , a vacuum bellowsdrive mechanism 73 is used to move the QCMs (sensor(s) 64) laterally into and out of the deposition chamber.FIG. 28B illustrates an alternative aspect of the invention in which theQCMs 64 are moved into and out of the deposition chamber using a magnetically-coupledtransfer arm mechanism 74 that includes a moveableexternal magnet 74 a that is used to drive amagnetic transfer 74 b arm.FIG. 29 illustrates three QCMs which are retractable within a single load-lockedchamber 70 through avalve 72. Alternatively, a separate load-lockedchamber 70 may be used for each QCM. -
FIGS. 30 , and 31A-C illustrate an embodiment wherein the load-lockedchambers 70 extend into thedeposition chamber 10 and are continually pumped using a source ofvacuum 68 to reduce the amount of residual oxygen near the QCM heads.FIG. 30 , for example, illustrates a load-lockedchamber 70 having a slit orhole 75 located on the underside of thechamber 70 such that evaporated species can enter thechamber 70 and be deposited on theQCMs 64. Avalve 72 separates the interior of thedeposition chamber 10 from the interior of the load-lockedchamber 70. Multiple QCMs may be incorporated into a single load-locked chamber 70 (e.g., three QCMs). - In an alternative embodiment, as shown in
FIG. 31A , thevalve 72 may be located on the load-lockedchamber 70 such that thevalve 72 is within or inside thedeposition chamber 10. Alternatively, thevalve 72 may form the slit itself (e.g., slit valve) as is shown inFIGS. 31B and 31C . By opening theslit valve 72, the evaporated species are then exposed to the QCMs. - The elements of
FIGS. 31B and 31C are incorporated into one preferred embodiment of themonitor chamber 60 used in connection with thedevice 2. This preferred embodiment is illustrated inFIG. 32 . Themonitor chamber 60 includes afront face plate 62 that is slidable within themonitor chamber 60. The slidablefront face plate 62 permits easy access to one or more deposition monitors 64 positioned on therails 65. The deposition monitors 64 are aimed downward toward thesource chamber 30 and preferably include dividers or the like (not shown) that direct each monitor 64 to a particular flux source in thesource chamber 30. In a preferred aspect of the invention, the deposition monitor 64 is a crystal quartz monitor (QCM). - The deposition monitors 64 are located on the
rails 65 such that when thefront face plate 62 is closed against themonitor chamber 60, the deposition monitors 64 are disposed above a slit valve 66 located on the underside of themonitor chamber 60. The slit valve 66 opens/closes access to thesource chamber 30 containing the flux sources. In this manner, themonitor chamber 30 is load-locked from thesource chamber 30 via the slit valve 66. - When the slit valve 66 is open, the deposition monitors 64 are exposed to the evaporated flux that rises from the
source chamber 30 into theheater chamber 10, and thus the deposition rate of the flux species may be monitored. When the slit valve 66 is closed, themonitor chamber 60 may be vented to atmosphere separately from the other chambers, and the deposition monitors 64 removed from themonitor chamber 60 using the slidablefront face plate 62. In this manner, the deposition monitors 64 may be inspected and replaced without disturbing the rest of the vacuum system. - Still referring to
FIG. 32 , avacuum source 68 such as, for example, a vacuum pump, is coupled to themonitor chamber 30 and is used to pump down themonitor chamber 30 during operation of thedevice 2. Thevacuum source 68 is preferably a high vacuum pump such as, for instance, a turbomolecular pump. - In addition, as explained above, QCMs can become unreliable, particularly in the presence of oxygen and oxides. Should a QCM fail during a run, the
device 2 allows the replacement of the QCM during the deposition run without stopping the deposition process. Therefore, run efficiency and throughput are greatly enhanced in the event of QCM failure. In addition, the slit valve 66 can be closed following deposition prior to the time when theheater chamber 10 is flooded with oxygen, thereby further minimizing the amount of contact between the QCMs and oxygen/oxides. - A device that uses multiple, rotatable quartz crystals inside the
heater chamber 10 may also be used, thereby limiting the number of times in which the crystals need to be changed (the device rotates to the next crystal thereby avoiding pump down between runs). Atomic absorption techniques may also be employed to monitor the deposition process. For example, radiation beams used in atomic absorption measurements may be passed through the deposition plume inside the heater through entry and exit ports or windows located in the heater chamber 10 (not shown). - With reference now to
FIGS. 33A and 33B , in one aspect of thedevice 2, twotransfer chambers substrate support member 110 containing substrate(s) 116.FIG. 33B depicts one of theloading transfer chamber 40. Bothtransfer chambers FIG. 1 , the twotransfer chambers heater chamber 10. Of course, thetransfer chambers heater chamber 10. A slit in the wall of theheater chamber 10 allows passage of thesubstrate support member 110 into and out theheater chamber 10. Theheater chamber 10 is isolated from the twotransfer chambers FIG. 1 ). - Referring back to
FIG. 33B , during operation, thesubstrate support member 110 is taken from a room temperature and pressure environment and placed into theloading transfer chamber 40 using adoor 44 located on top of thetransfer chamber 40. When thedoor 44 is closed, thetransfer chamber 40 is pumped to vacuum using a source of vacuum 42 (52 in the case of unloading transfer chamber 50). Thesubstrate support member 110 is placed on anextendable transfer arm 45 includingmultiple tines 47 for holding thesubstrate support member 110. Theextendable transfer arm 45 is moveable in the direction of arrow A shown inFIG. 33B . - A rotary drive disposed on the underside of the transfer chamber 40 (not shown) provides horizontal displacement of the
transfer arm 45 using magnetic coupling. In this regard, the motorized components are contained outside thetransfer chambers transfer arm 45 to the external rotary drive, there is no need to expose the drive mechanism to a vacuum environment. - When the
transfer chamber 40 has been pumped to vacuum, the valve 41 (as seen inFIG. 1 ) connecting thetransfer chamber 40 theheater chamber 10 is opened, and thesubstrate support member 110 is extended into theheater chamber 10 by activating the rotary drive. - For unloading operations, the reverse sequence of events occurs in the unloading
transfer chamber 50. In particular, thetransfer arm 45 retrieves thesubstrate support member 110 from theheater chamber 10 and retracts into thetransfer chamber 50. Thetransfer chamber 50 can then be vented to atmosphere or a soak routine can be employed. Thedoor 44 can then be opened and thesubstrate support member 110 retrieved. - An optional heater (not shown) may be included in the
transfer chamber 40 to pre-heat the substrate-ladensubstrate support member 110 prior to introduction into theheater chamber 10. Preferably, thesubstrate support member 110 is heated radiatively. This pre-heating may be accomplished by heater lamps, coils, or other heating elements disposed on thetransfer chamber 40. - Referring back to
FIG. 1 , thesource chamber 30 of thedevice 2 includes one or more evaporation sources e.g.,sources sources crucibles crucible 81 a while Copper (Cu) might be placed incrucible 81 b. Source material is placed inside thecrucible - The following is a description of a process used to deposit YBCO or other oxide films using reactive coevaporation.
- First, the quartz crystals used to monitor the overall flux in the
heating chamber 10 are replaced by first venting theheater chamber 10, opening the heater chamber door 10(a), replacing the quartz crystals, closing the heater chamber door 10(a), and pumping down theheater chamber 10 to vacuum conditions. - Next, the deposition monitors 64 (e.g., QCMs) are changed in the
monitor chamber 60. This is accomplished by venting themonitor chamber 60, opening thefront face 62, replacing the deposition monitors 64, close thefront face 62, and pumping down the deposition monitor 64 to vacuum conditions. - If necessary, source materials are loaded into
crucibles source chamber 30 is vented to atmosphere and opened. Additional and/or replacement source material is loaded into one or more of thecrucibles source chamber 30 is then closed and pumped to vacuum. -
Substrates 116 are loaded in thedevice 2 by initially loading one ormore substrates 116 onto thesubstrate support member 110.Transfer chamber 40 is vented to atmosphere and thedoor 44 is opened. The loadedsubstrate support member 110 is then placed on thetines 47 of thetransfer arm 45. Thedoor 44 is then closed and thetransfer chamber 40 is pumped to vacuum. Thevalve 41 between thetransfer chamber 40 and theheater chamber 10 is opened to provide access to theheater chamber 10. In addition, theheated cap portion 102 of thepocket heater 100 is raised by theactuator 103. Thetransfer arm 45 containing thesubstrate support member 110 is then extended into theheater chamber 10. - When the
substrate support member 110 is centrally located beneath theheated cap portion 102 of thepocket heater 100, thespindle 112 is raised in the z-direction to engage thesubstrate support member 110. Thesubstrate support member 110 is lifted off thetines 47 of thetransfer arm 45 by the raisedspindle 112. Thetransfer arm 45 is then withdrawn back into thetransfer chamber 40. Thevalve 41 is closed and thespindle 112 is lowered to the desired height to form the gap between thesubstrate support member 110 and thelower heater plate 104. - Next, the
upper heater zones pocket heater 100 are lowered into position using theactuator 103. Rotation of thesubstrate support member 110 is then initiated. Thesubstrate support member 110 is lowered toward thelower heater plate 104 until the desired gap is established. Oxygen flow is initiated to the reaction pocket, and the flow rate and gap (i.e., distance between thesubstrate support member 110 and lower heater plate 104) are adjusted to provide the desired oxygen pressure inside the pocket. The heater coils are energized to ramp thepocket heater 100 to the desired temperature. The source materials are then evaporated. At this point, thegate valve 36 is opened between theheater chamber 10 and thesource chamber 30. A shutter is interposed between thesubstrate support member 110 andsource chamber 30 to prevent deposition onto thesubstrates 116. A second shutter located in the source chamber that is interposed between the source materials and thegate valve 36 is also opened. The slit valve 66 in themonitor chamber 60 is opened and evaporation rates of the source materials are adjusted based on measurements made with the deposition monitors 64. - Once the
pocket heater 100 is at the desired temperature and the desired rates of evaporation of the source materials are reached, the shutter interposed between thesubstrate support member 110 andsource chamber 30 is opened to allow deposition onto therotating substrates 116. - Once the desired thickness of film has been reached, the first and second shutters described above are closed. After the two shutters are closed, the
gate valve 36 between theheater chamber 10 and thesource chamber 30 is closed. Theheater chamber 10 is then backfilled with oxygen gas. The temperature of thepocket heater 100 is then ramped down. Thecrucibles heated cap portion 102 of thepocket heater 100 is raised in the vertical direction via theactuator 103. Thesubstrate support member 110 is raised from thelower heater plate 104 using themoveable spindle 112. - With the
substrate support member 110 raised form thelower heater plate 104, the pressure in the transfer chamber (unloading) 50 is equalized with the pressure of theheater chamber 10 using an equalization circuit. Thevalve 41 is opened and thetransfer arm 45 is extended into theheater chamber 10. Thesubstrate support member 110 is then lowered onto thetines 47 of thetransfer arm 45 using thecam device 130. The transfer arm 35 (and substrate support member 110) is then withdrawn back into thetransfer chamber 50 and thevalve 41 is closed. When thesubstrate support member 110 is cool, thetransfer chamber 50 is vented to atmosphere. Thedoor 44 can be opened and thesubstrate support member 110 containing the HTS thin film-laden substrates 116 is removed. - In a preferred aspect of the invention, the
device 2 and process described above is run by acomputer 200 such as that shown inFIG. 34 (i.e., microprocessor) having software loaded thereon that is able to control and monitor the deposition process. Thecomputer 200 advantageously controls the pumps, heaters, valves, transfer arms, actuators, motors, cam device, flux sources and the like. In addition, thecomputer 200 is able to acquire data from thedevice 2 such as, for example, temperatures and pressures in the various chambers of the device. Thecomputer 200 also receives data from the deposition monitors 64 in order that the deposition process can be monitored during a particular run. Preferably, the software is implemented using a graphical user interface (GUI) making the software user friendly. - While the invention is susceptible to various modifications, and alternative forms, specific examples thereof have been shown in the drawings and are herein described in detail. It should be understood, however, that the invention is not to be limited to the particular forms or methods disclosed, but to the contrary, the invention is to cover all modifications, equivalents and alternatives falling within the spirit and scope of the appended claims.
Claims (22)
1. A heater for growing a thin film on substrates contained on a substrate support member comprising:
a plurality of heater elements, wherein the substrate support member containing the substrates is at least partially surrounded by the plurality of heater elements, and wherein at least two of the plurality of heater elements are moveable with respect to one another so as to provide external access to the substrate support member.
2. The heater of claim 1 , wherein the heater comprises a top heater element, a side heater element, and a bottom heater element.
3. The heater of claim 1 , wherein one of the plurality of heater elements is moveable with respect to a stationary heater element.
4. The heater of claim 3 , wherein the bottom heater includes a window opening in a portion thereof.
5. The heater of claim 3 , wherein the bottom heater element is stationary and the top heater element and the side heater element are movable with respect to the bottom heater element.
6. The heater of claim 3 , wherein the top heater element and the side heater element are stationary and the bottom heater element is moveable with respect to the top and side heater elements.
7. The heater of claim 1 , wherein at least two of the plurality of heater elements are connected via a hinge.
8. The heater of claim 1 , wherein the substrate support member is supportable on a vertically oriented spindle.
9. The heater of claim 8 , wherein the substrate support member is gravitationally held on the spindle.
10. The heater of claim 1 , wherein the spindle is rotatable.
11. The heater of claim 9 , wherein the substrate support member is moveable in a vertical direction.
12. A heater for growing a thin film on substrates comprising:
a heater cap comprising a top plate having a side wall about its periphery, the top plate and side wall each having a heating element disposed therein;
a lower heater plate having an upper and lower surface, a portion of the lower heater plate having a window disposed therein passing from the upper surface to the lower surface of the lower heater plate and a recessed pocket formed in a portion of the upper surface of the lower heater plate; and
wherein the heater cap and lower heater plate are moveable with respect to one another in a direction perpendicular to the upper face of the lower heater plate.
13. The heater of claim 12 , wherein the lower heater plate is stationary and the heater cap is moveable with respect to the lower heater plate.
14. The heater of claim 12 , wherein the heater cap is stationary and the lower heater plate is moveable with respect to the heater cap.
15. The heater of claim 12 , further comprising an actuator for moving the heater cap with respect to the lower heater plate.
16. A heater for growing a thin film on substrates comprising:
an upper heater zone comprising a top member having a side wall about its periphery, the top member and side wall each having a heating element disposed therein;
a lower heater zone having a heating element disposed therein;
an oxygen pocket member having an upper and lower surface, a portion of the oxygen pocket member having a window disposed therein passing from the upper surface to the lower surface and a recessed pocket formed in a portion of the upper surface of the oxygen pocket member, the oxygen pocket member at least partially surrounded by at least one of the upper heater zone and lower heater zone; and
wherein the upper heater zone is moveable in a direction perpendicular to the upper face of the oxygen pocket member.
17. A method of unloading and loading a substrate support member in a heater comprising the steps of:
providing a heater having a plurality of heater elements, wherein the substrate support member is at least partially surrounded by the plurality of heater elements, and wherein at least two of the plurality of heater elements are moveable with respect to one another so as to provide external access to the substrate support member;
moving the plurality of heater elements into an unload position;
removing the substrate support member from the heater;
inserting a second substrate support member into the heater; and
moving the plurality of heater elements into a loaded position.
18. The method of claim 17 , wherein heater is disposed in a vacuum chamber.
19. The method of claim 17 , further comprising the step of depositing a thin film on substrates disposed on the substrate support member.
20. The method of claim 18 , wherein the removal and insertion of the substrate support members occurs under vacuum conditions.
21. The method of claim 17 , wherein the at least two of the plurality of heater elements are moveable with respect to one another in a vertical direction.
22-43. (canceled)