US20060258249A1 - Elastic laminates and process for producing same - Google Patents
Elastic laminates and process for producing same Download PDFInfo
- Publication number
- US20060258249A1 US20060258249A1 US11/126,955 US12695505A US2006258249A1 US 20060258249 A1 US20060258249 A1 US 20060258249A1 US 12695505 A US12695505 A US 12695505A US 2006258249 A1 US2006258249 A1 US 2006258249A1
- Authority
- US
- United States
- Prior art keywords
- elastic
- adhesive
- continuous filaments
- facing
- nonwoven web
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method is provided for producing elastic composite laminates. The laminates contain elastic filaments that are stretched and laminated to at least one facing material. The continuous filaments are laminated to the facing material using a starved slot coat process. The starved slot coat process provides various benefits and advantages including the production of laminates having improved properties.
Description
- Articles requiring a degree of elasticity have been formed by combining elastic materials with inelastic, or less elastic, materials through various lamination processes. Often, such composite laminate articles will be stretchable because of the presence of the elastic material and the particular manner in which the elastic and inelastic materials have been bonded together during the laminating process.
- Typically, such stretchable laminates are formed by joining the inelastic material to the elastic material while the elastic material or sheet is in a stretched condition. After such joining of the materials, the laminated article is then allowed to relax, which results in the inelastic component gathering in the spaces between bonding sites on the elastic sheet. The resulting laminate article is then stretchable to the extent that the inelastic material gathered between the bond locations allows the elastic material to elongate. Examples of these types of composite laminate articles and materials are set forth in U.S. Pat. Nos. 4,720,415 and 5,385,775, each of which is incorporated herein by reference thereto.
- In some stretchable laminate articles, elastic strands of continuous filaments are bonded to relatively inelastic sheet materials while the elastic strands are in a stretched condition. Such elastic continuous filaments may, in certain articles, be sandwiched between two or more relatively inelastic sheets. The relatively inelastic sheets may include nonwoven webs formed by meltblowing or spunbonding various polymers. Examples of such laminates are shown in U.S. Pat. No. 5,385,775; in U.S. Pat. No. 6,057,024; and in U.S. Published Patent Application No. U.S. 2002/0104608, which are all incorporated herein by reference.
- As shown in the '775 patent, elastic continuous filaments may be extruded onto a horizontally moving sheet of material. The continuous filaments are extruded from above the horizontal plane of the sheet material and directly onto the material for bonding thereto. In the '024 patent, an alternative embodiment is disclosed in which the continuous filaments are extruded vertically in a downward direction. As the filaments are extruded in a downward direction, the filaments are stretched and then laminated to one or more sheet materials.
- In many embodiments in the past, an adhesive was used in order to adhere the elastic strands of continuous filaments to the sheet materials. In one embodiment, for instance, the adhesive was sprayed on the sheet material prior to contacting the filaments. Spraying the adhesive material onto the sheet materials, however, may have some drawbacks in various applications. For instance, spray devices may be difficult to control leading to over-application of the adhesive or leading to a non-uniform coverage of the adhesive on the sheet material, especially at high machine speeds and at low application rates. In fact, over-application of a hot adhesive during a spray process may cause filament breakage and machine downtime. Further, since the adhesive has to travel a distance prior to contacting the sheet material, the adhesives may experience a loss in tack prior to contacting the sheet material.
- In view of the above, a need currently exists for an improved method for applying an adhesive material in between stretched elastic filaments and a nonwoven facing. A need also exists for an elastic composite laminate that has improved properties due to the manner in which an adhesive is applied.
- In general, the present disclosure is directed to composite elastic materials that include a plurality of elastic continuous filaments bonded to at least one nonwoven web. The nonwoven web is laminated to the continuous filaments when the filaments are in a stretched state. Thus, when the filaments are relaxed, the nonwoven web gathers and allows the entire composite to stretch in at least one direction.
- The present disclosure is more particularly directed to a method for applying an adhesive material in between the elastic continuous filaments and the nonwoven web and is directed to composite nonwoven materials produced by the process. The adhesive material is applied to the nonwoven web using a “starved” slot coating process in which the adhesive is emitted through a slot extrusion die onto the nonwoven web to form a discontinuous coating. The discontinuous coating contains amorphous elements of the adhesive material. The adhesive material is applied to a surface of the nonwoven web in a substantially uniform manner in terms of amount per area.
- The starved coat process provides various benefits and advantages. For instance, the process allows for control over the placement of the adhesive on the nonwoven web. Further, the inventors have discovered that the process provides a very efficient use of the adhesive. In particular, relatively low amounts of adhesive are used that securely bond the elastic continuous filaments to the nonwoven web, even when the elastic filaments are present in a stretched state. Unexpectedly, the present inventors also discovered that the process produces composite nonwoven materials having a reduced porosity in comparison to similar composites made in which the adhesive is sprayed on the nonwoven web. The relatively low porosity provides various benefits when the composite material is used to construct various articles, such as when incorporated into absorbent garments including diapers, training pants, swim pants, adult incontinence products, feminine hygiene products, bandages and medical drapes, and the like.
- In one particular embodiment, for instance, the present disclosure is directed to a method for producing a composite nonwoven material. The method includes the steps of extruding continuous filaments. The filaments comprise an elastomeric material. The elastomeric material may include, for instance, elastic polyesters, elastic polyurethanes, elastic polyamides, elastic copolymers of ethylene and at least one vinyl monomer, elastic metallocene-catalyzed polyolefins, and elastic block copolymers.
- Once formed, the elastic continuous filaments are stretched and then laminated to the first side of a nonwoven web. In order to bond the stretched laminates to the nonwoven web, an adhesive material is applied to the nonwoven web from a slot extrusion die. The adhesive material forms a discontinuous coating comprising amorphous elements of the adhesive material. The adhesive material may be applied to the first side of the nonwoven web in an amount less than about 4.4 gsm, such as from about 0.5 gsm to about 3 gsm. The adhesive material may comprise, for instance, a styrenic block copolymer, a random copolymer of a polyolefin, or an amorphous polyalphaolefin. In addition to the above, any suitable hotmelt adhesive may be applied in accordance with the teachings of the present disclosure.
- During application of the adhesive material to the nonwoven web, the nonwoven web may be configured to contact and slide against the slot on the slot extrusion die. The adhesive material may contact the web at a viscosity of from 500 cp to about 50,000 cp, such as from about 2,000 cp to about 20,000 cp. The temperature of the adhesive may vary depending upon the particular adhesive material used. In one embodiment, for instance, the application temperature of the adhesive may be from about 320° F. to about 350° F.
- In one embodiment, the method can further include the step of laminating the elastic continuous filaments to a second nonwoven web. For example, the continuous filaments may be positioned in between the first nonwoven web and the second nonwoven web. The second nonwoven web may be laminated to the continuous filaments using an adhesive material as described above.
- The nonwoven webs that are laminated to the elastic continuous filaments may vary depending upon the particular application and desired result. The nonwoven webs may comprise, for instance, meltblown webs, spunbond webs, bonded carded webs, and the like. In one embodiment, for instance, the nonwoven web comprises a spunbond web having a basis weight of from about 7 gsm to about 100 gsm, such as from about 10 gsm to about 20 gsm.
- Other features and aspects of the present invention are discussed in greater detail below.
- A full and enabling disclosure of the present invention, including the best mode thereof to one skilled in the art, is set forth more particularly in the remainder of the specification, including reference to the accompanying figures, in which:
-
FIG. 1 is a perspective view of one embodiment of a process for producing composite nonwoven materials in accordance with the present invention; -
FIG. 2 is a side view of the system and process illustrated inFIG. 1 ; -
FIG. 3 is a partial view of an extrusion surface of an exemplary extruder head for extruding elastic continuous filaments; -
FIG. 4 is a magnified view of a portion of the surface illustrated inFIG. 3 ; -
FIG. 5 is a side view of another embodiment of a process that may be used to form composite nonwoven materials in accordance with the present invention; -
FIG. 6 is a plan view of one embodiment of a system and process for applying adhesive materials to nonwoven webs for use in the process of the present invention; and -
FIG. 7 is a perspective view of one embodiment of a slot extrusion die head that may be used in the process of the present invention. - Repeat use of reference characters in the present specification and drawings is intended to represent the same or analogous features or elements of the present invention.
- The term “continuous filaments”, as used herein, refers to strands of continuously formed polymeric filaments. Such filaments will typically be formed by extruding molten material through a die head having a certain type and arrangement of capillary holes therein.
- The term “elastic” or “elasticized”, as used herein, refers to a material which, upon application of a biasing force, is stretchable, which is elongatable to at least about 60 percent (i.e., to a stretched, biased length which is at least about 160 percent of its relaxed unbiased length), and which will recover at least 55 percent of its elongation upon release of the stretching force. A hypothetical example of an elastic material would be a one (1) inch sample of a material which is elongatable to at least 1.60 inches and which, when released, will recover to a length of not more than 1.27 inches. Many elastic materials may be elongated by more than 60 percent (i.e., more than 160 percent of their relaxed length). For example, some elastic material may be elongated 100 percent or more, and many of these will recover to substantially their initial relaxed length such as, for example, within 105 percent of their original relaxed length upon release of the stretching force.
- The term “composite nonwoven fabric”, “composite nonwoven”, “laminate”, or “nonwoven laminate”, as used herein, unless otherwise defined, refers to a material having at least one elastic material joined to at least one sheet material. In most embodiments such laminates or composite fabric will have a gatherable layer which is bonded to an elastic layer or material so that the gatherable layer may be gathered between bonding locations. As set forth herein, the composite elastic laminate may be stretched to the extent that the gatherable material gathered between the bond locations allows the elastic material to elongate. This type of composite elastic laminate is disclosed, for example, in U.S. Pat. No. 4,720,415 to Vander Wielen et al., which is incorporated herein in its entirety by reference thereto.
- As used herein, the term “nonwoven web” refers to a web having a structure of individual fibers or threads that are interlaid, but not in an identifiable, repeating manner. Nonwoven webs have been, in the past, formed by a variety of processes such as, for example, meltblowing processes, spunbonding processes and bonded carded web processes.
- As used herein, the term “meltblown fibers” means fibers formed by extruding a molten thermoplastic material through a plurality of fine, usually circular, die capillaries as molten thermoplastic material or filaments into a high velocity gas (e.g. air) stream which attenuates the filaments of molten thermoplastic material to reduce their diameter, which may be to microfiber diameter. Thereafter, the meltblown fibers are carried by the high velocity gas stream and are deposited on a collecting surface to form a web of randomly disbursed meltblown fibers. Such a process is disclosed, for example, U.S. Pat. No. 3,849,241 to Butin, which is incorporated herein in its entirety by reference thereto.
- As used herein, the term “spunbonded fibers” refers to small diameter fibers formed by extruding a molten thermoplastic material as filaments from a plurality of fine, usually circular, capillaries of a spinerette with the diameter of the extruded filaments then being rapidly reduced as by, for example, eductive stretching or other well-known spun-bonding mechanisms. The production of spun-bonded nonwoven webs is illustrated in patents such as, for example, U.S. Pat. No. 4,340,563 to Appel et al., and U.S. Pat. No. 3,692,618 to Dorschner et al. The disclosures of these patents are incorporated herein in their entireties by reference thereto.
- It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only, and is not intended as limiting the broader aspects of the present invention.
- The present disclosure is generally directed to a method for producing a composite elastic nonwoven material and to the material itself. More particularly, the present disclosure is directed to a starved slot coat process for applying an adhesive to a facing material in order to laminate the facing material to a plurality of stretched filaments. Through the above process, the adhesive has been found to firmly bond the elastic filaments in a stretched state to the facing material. Once relaxed, the facing material gathers forming a stretchbonded laminate that has elastic properties in at least one direction.
- In one embodiment, during the starved slot coat process, the facing material contacts the slot of the slot extrusion die (or “slot die”) as the adhesive is applied to the facing. The adhesive is applied to the facing at relatively low amounts forming a discontinuous coating on the nonwoven material. Even at relatively low adhesive application rates, the process has been found to securely bond the elastic filaments to the facing without problems of delamination.
- In the past, elastic filaments have been laminated to facing materials by spraying an adhesive onto the facing material, such as disclosed in U.S. Patent Application Publication No. U.S. 2002/0104608. The process of the present disclosure, however, provides many benefits and advantages in comparison to an adhesive spray process. For example, the slot coat process may allow lamination at higher line speeds and may produce laminates having a higher peel strength. Unexpectedly, the slot coat process also produces laminates having a lower porosity, which makes the material easier to handle during later converting processes. It is believed that the lower laminate porosity is due to the fact that the adhesive is applied as a discontinuous coating which creates amorphous elements of adhesive as opposed to spray fiberization which creates fine fibers that may not have as much resistance to air flow.
- The starved slot coat adhesive process has been found to efficiently place adhesive on the surface of the facing material. For example, the adhesive generally only covers the fibers of the facing material and does not bridge the void areas in the material. In a spray process, on the other hand, adhesive is applied everywhere on the substrate and typically collects in the void areas on the facing. When collected in the void areas, the adhesive does not substantially contribute to bonding the facing material to the elastic substrates.
- In some applications, the starved coat adhesive process has been found to only be applied to the surface of the facing material only on the fibers of the material and at substantially the high points of the material which are generally only the places on the material where the facing can be bonded to the elastic filaments.
- Another advantage to the process of the present disclosure in comparison to spray processes is that since the adhesive is applied immediately to the substrate as it is emitted from the slot extrusion die, no cooling or quenching of the adhesive occurs prior to being deposited on the material. As such, adhesives with higher or faster cure rates may be used.
- In the past, slot coat processes have been disclosed in which a slot die is used to dispense adhesive in order to form laminates. For instance, U.S. Pat. No. 5,750,444 to Jarrell, which is incorporated herein by reference, discloses a process for producing breathable laminates using a slot die. In the '444 patent, the adhesive is described as forming a porous random fibrous web. The adhesive is used to attach together two or more porous webs comprising woven or nonwoven materials to form laminates that remain breathable even after application of the adhesive in between the materials.
- In the process of the present disclosure, on the other hand, laminates are formed in which elastic filaments are stretched and then bonded to a facing material. It was discovered that the starved slot coat process of the present invention was capable of adequately bonding the stretched filaments to the facing even at relatively low adhesive application rates. Also, it was unexpectedly discovered that the slot coat process as disclosed herein increased the porosity of the laminate in comparison to spray processes. As will be described in more detail below, the increase in porosity facilitates handling of the laminate in later converting processes.
- Referring to
FIGS. 1 and 2 , one exemplary system and process for producing laminates in accordance with the present invention is illustrated. In the embodiment shown inFIG. 1 , the system may be considered a vertical filament lamination (hereinafter “VFL”) system since the elastic filaments are formed and stretched in a vertical arrangement. The system illustrated inFIGS. 1 and 2 , however, is merely for exemplary purposes. It should be understood that the process of the present invention may be configured in a horizontal system in which the filaments are cooled and stretched in a horizontal direction. One embodiment of a horizontal system, for instance, is illustrated in FIGS. 1 and 2 of U.S. Pat. No. 6,057,024, which is incorporated herein by reference. - As shown in
FIG. 1 , however, theVFL system 11 is vertically configured. Anextruder 15 is mounted for extruding continuousmolten filaments 14 downward from a die at a canted angle onto chilledpositioning roller 12.Chilled positioning roller 12 ensures proper alignment through the remainder of the system as it spreads the filaments. As the filaments travel over the surface ofchilled positioning roller 12, they are cooled and solidified as they travel towards and over the chilled surface ofchilled roller 13. The filaments then travel downward in an “s-shaped” progression to aroller 16 and then across the surface of aroller 17, aroller 18 and into the nip formed bynip roller 19 and niproller 20. - The
continuous filaments 14 formed in the process may have any desirable shape. In one embodiment, for instance, the filaments may have a ribbon-like shape. For instance, the filaments may have a width of from about 0.5 mm to about 1.5 mm in an unstretched state. The filaments all generally extend in the same direction and are generally parallel to each other. The actual number of continuous filaments utilized in any particular process may vary depending upon the particular characteristics desired in the final product. For example, the array of filaments may total more than about 100 strands, such as more than about 200 separate strands. For example, in one embodiment, the array of filaments may number from about 200 separate strands to as much as 2600 separate strands. A greater or lesser number of strands, however, is also possible. - As shown in
FIG. 1 , theextruder 15 may be positioned with respect to thefirst roller 12 so that the continuous filaments meet the first roller at a predetermined angle. In some embodiments, an angled, or canted, orientation provides an opportunity for the filaments to emerge from the die at an angle to the roll tangent point resulting in improved spinning, more efficient energy transfer, and generally longer die life. This configuration allows the filaments to emerge from the die and follow a relatively straight path to contact the tangent point on the roll surface. The angle between the die exit of the extruder and the vertical axis may be as little as a few degrees or as much as 90°. For example, the angle may be about 20°, about 35°, or about 45° away from vertical. - The continuous filaments may be combined at the nip with various types of facings. The facings, for example, may comprise nonwoven fabrics, woven fabrics including knitted fabrics, films, laminates, and the like. In the embodiment depicted in
FIG. 1 , a first non-woven spunbond facing 22 and a second non-woven spunbond facing 24 are combined on opposing surfaces of the continuous filaments to form a bondedlaminate 25. In some embodiments, only one facing may be used, and in other embodiments it is possible to combine the elastic continuous filaments with three, four, or more layers of facing material. - Bonding of the facings to the continuous filaments is done with an adhesive material. In accordance with the present disclosure, the adhesive is applied to the facings using a slot extrusion die. For instance, as shown in
FIGS. 1 and 2 , a first slot extrusion die 23 applies an adhesive to thenonwoven material 22, while a second slot extrusion die 53 applies an adhesive to thenonwoven material 24. As illustrated, thenonwoven material 22 contacts the slot extrusion die 23, while thenonwoven web 24 contacts the slot extrusion die 53 as the adhesive is being dispensed onto the nonwoven materials. To ensure proper contact, for instance,press rollers - In one embodiment, the adhesive application rates applied to the nonwoven materials can be relatively low. In fact, the adhesive rate is so low that the process can be referred to as a “starved” slot coat process. For example, in one embodiment, the adhesive is applied to each of the nonwoven materials in an amount less than about 4.4 gsm, such as from about 0.5 gsm to about 3 gsm, such as from about 0.8 gsm to about 2.5 gsm.
- At such low add-on rates, the adhesive does not completely coat the nonwoven materials. Instead, the adhesive forms a discontinuous coating. For example, in one embodiment, the adhesive may form amorphous elements placed over the surface of the nonwoven material. Of particular advantage, the adhesive primarily becomes applied to the nonwoven web at elevations on the web, which is the place where the web is capable of bonding with the
elastic filaments 14. More particularly, the adhesive tends to coat the top surface of the fibers on the web and fails to collect or bridge the void areas in the web. Thus, little to no adhesive is wasted creating maximum adhesive efficiency. - Although the adhesive forms a discontinuous coating, however, it should be understood that the adhesive is applied in a substantially uniform manner over the surface of the nonwoven material in terms of amount per area.
- In general, any suitable slot extrusion die may be used in the process of the present invention. For example, in one embodiment, a slot extrusion die commercially available from the Nordson Corporation of Westlake, Ohio may be used. One example of a Nordson slot extrusion die is disclosed in U.S. Pat. No. 5,750,444, which is incorporated herein by reference.
- For exemplary purposes only, one embodiment of a slot extrusion die system is illustrated in
FIGS. 6 and 7 . As shown inFIG. 6 , the system includes anadhesive supply 64 for receiving an adhesive material. The adhesive supply may comprise a reservoir, may comprise a heated reservoir, or may comprise an extruder as particularly shown inFIG. 6 . Theadhesive supply 64 feds an adhesive material into aline 66 to amultiple metering station 68. Themetering station 68 is connected to the slot extrusion die 23 for applying the adhesive material to thenonwoven material 22. More specifically, themetering station 68 is connected to a plurality oflines metering station 68, for instance, may be configured to supply adhesive to each of the lines which are in fluid communication with the slot extrusion diehead 23. It should be understood, however, that more or less lines may be fed between themetering station 68 and the slot extrusion die 23. - In one embodiment, the
multiple metering station 68 may include a pumping device placed in association with each of thelines 70A-70K. In this manner, each of the lines may be operated independently of the others. Thus, the amount of adhesive flowing through each line can vary from line to line. In other embodiments, however, each line may be supplied with equal amounts of adhesive. - In one embodiment, instead of containing a pumping device, each of the lines are fed directly from a screw extruder.
- Referring to
FIG. 7 , a perspective view of the slot extrusion die 23 is shown with cut away portions for purposes of illustrating the interior of the extruder. The slot extrusion die 23 includes aslot 72 through which the adhesive material is emitted. In one embodiment, theslot 72 is fed bymultiple segments 74. Eachsegment 74 may be connected, for example, to acorresponding line 70A-70K. By havingmultiple segments 74, the amount of adhesive dispensed from each location on the slot extrusion die may be varied. Further, the effective width of theslot 72 may be varied by turning on and off the outer lines. - In general, any suitable adhesive material may be dispensed onto nonwoven materials in accordance with the present invention. In general, the adhesive may be, for instance, a hotmelt adhesive that is heated prior to being applied to the nonwoven materials. The adhesive may have a viscosity exiting the slot extrusion die of from about 500 cp to about 50,000 cp, such as from about 2,000 cp to about 20,000 cp. The temperature of the adhesive may vary depending upon the adhesive being used. In one embodiment, however, the adhesive may be heated to a temperature of from about 250° F. to about 400° F., such as from about 320° F. to about 350° F.
- Particular adhesives that may be used in the present invention include various block copolymers, such as styrenic block copolymers. Such block copolymers include, for example, styrene-isoprene-styrene block copolymers, styrene-ethylene-butylene-styrene block copolymers, styrene-butadiene-styrene block copolymers, and the like.
- In other embodiments, the adhesive material may comprise a random copolymer of a polyolefin. The polyolefin may be, for example, a polyethylene or a polypropylene.
- In still other embodiments, an amorphous polyalphaolefin may be used. In still other embodiments, a metallocene-catalyzed elastomeric resin, such as a polyethylene or polypropylene resin can be utilized.
- Commercially available adhesive materials may be obtained from Bostik, Inc., from the Dow Chemical Company, and from various other commercial sources. In some embodiments, the adhesive material may need to be heated prior to being applied to the nonwoven materials. The adhesives, for instance, may be heated to temperatures greater than 100° F., such as from about 200° F. to about 400° F. In some embodiments, the adhesive may be blended with a tackifier or may be blended with other elastomers as desired.
- After the adhesive material is applied to the
nonwoven webs elastic filaments 14 while the filaments are in a stretched state. As shown inFIG. 1 , a take-up roll 21 may be employed for receiving and winding the bonded nonwoven material/continuous filament/nonwoven material laminate 25 for storage. -
FIG. 2 illustrates a side view of the VFL assembly, includingsupport frame 26 upon which the various components of the system are secured. Reference numerals are employed throughout the figures consistently to indicate the same components in the various views. As shown inFIG. 2 , first outer facingroll 27 and second outer facingroll 28 provide the desiredfacings Support strut 29 holds thenip roller 20 in place. The rollers can be seen in side view transferring the continuous filaments downward to the nip, where the filaments combine with the facings to form a bonded laminate. - Construction of the
continuous filaments 14 will now be described in greater detail including the manner in which the filaments are stretched prior to being bonded to the nonwoven facings in accordance with the present disclosure. As shown inFIGS. 1 and 2 , an elastomeric material is extruded through a die head for initially forming the filaments. -
FIG. 4 depicts an exemplary extruder diehead 30 with capillary holes 31. InFIG. 5 , a close-up view of the die head is depicted. The pattern and diameter of the capillary holes on the extruder die head may be varied to provide filaments, with the appropriate spacing, without having to utilize expensive combs, etc., to form a fabric having the correct elastic geometry. The distances d1 (distance between rows of capillary hole centers), d2 (distance between contiguous diagonal capillary hole centers on opposing rows) and d3 (distance between contiguous capillary hole centers in the same row) may be varied, depending on the particular features desired in the final products. For example, various hole densities may be utilized in the present process. In a 12-filament/inch example, the distance between center lines of the die holes (d1) may be approximately 2.12 millimeters. When a hole density of 18-filaments/inch is utilized, the distance between die hole center lines (d1) is approximately 1.41 mm. - The rollers that carry the continuous filaments are positioned and operated so as to cause the continuous filaments to be stretched as they vertically flow through the lamination system. When a number of rollers are employed, each successive roller turns in a direction opposite to the immediately preceding roller so that the strands of continuous filaments are handed off from roller to roller. In addition, the speed of each successive roller may be varied from the preceding roller so as to obtain the desired stretching and elongation characteristics. For example, any particular roller may operate at between 1 to 10 times, and more, the speed of any preceding roller. Typically, a separate controller, such as a servomotor or a Turner drive, may be utilized to allow individual speed control for each roll and will drive each individual roll. When the speed is varied, successive rollers may turn at a faster rate to stretch or elongate the strands as they move downwardly in the vertical process. In addition, the continuous filaments are ultimately reduced to a fiber size of approximately 0.008 to 0.040 inches in diameter, and in some cases to approximately 0.015 to 0.020 inches in diameter.
- The number of separate rollers used to convey the continuous filaments to the bonding location may vary depending on the particular attributes desired in the final product. In one particular embodiment, at least four rollers—a first chilled (or positioning) roller, a second chilled roller, a third unchilled roller, and a fourth unchilled roller—may be utilized. In another embodiment, only two chilled rollers may be needed before the continuous filaments are supplied to the laminator portion of the system which bonds the spunbond facing(s) to the continuous filaments in a roller nip.
- In certain embodiments, the rollers may be plasma coated to provide good release properties. In other embodiments, the rollers may additionally be grooved or channeled to ensure that the extruded continuous filaments maintain a proper separation between individual filaments as the filaments pass over the surface of the rolls and flow through the system. In some embodiments, smooth rolls maybe used for one or all of the rolls. In the case where plasma-coated rolls are employed, the continuous filaments will not slip as much as they do on smooth, uncoated rolls. The plasma-coatings grips the strands and promote increased uniformity of distances between the continuous filament strands.
- As suggested, any or all of the rollers may be chilled so as to more quickly quench, or harden, the continuous filaments as they are proceeding through the process. The chilled rolls may be chilled to a controlled temperature of between about 45° F. and about 60° F. (typically about 45° F. or about 50°). Simultaneous quenching and stretching may be optimized depending on the particular stretchability characteristics desired in the final product.
- In one particular embodiment, the series of rollers (or roller) may be enclosed within a sealed tower structure and conditioned air, with the moisture removed, may be utilized in order to control the chilling effects of the rollers. For example, the chilled rolls may be chilled to 50° F. or less relative to the controlled dewpoint. In such cases, the temperature to which the rolls are chilled may be significantly less than 50° F., but with the conditioned air environment, the rolls may remain at 50° F.
- Other various mechanisms may be utilized to quench the continuous filaments. For example, external air could be forced onto the fibers in order to control the hardening of the fibers. In other embodiments, one large roll could be used with sufficient surface area in order to quench the fibers.
- Maintaining a certain roller speed allows the appropriate degree of elastic stretch to allow the puckers to form in the final laminate. The positioning chilled
roller 12 normally turns at a surface speed in the range of about 3-10 feet per minute (“fpm”), while the first vertically-placed chilled roller turns at about 5 to about 15 fpm. The next roller turns at about 7 to about 18 fpm, while the last roller, when applied and used, turns at a speed of about 12 to about 100 fpm. These ranges are approximate, and can vary depending upon the conditions and final product configuration desired. - In one particular embodiment, the first roll may turn at approximately 5 fpm;
- the second roll at approximately 6 fpm; the third roll at approximately 11 fpm; and the fourth roll at approximately 26 fpm. Another embodiment utilizes a first roll speed of 10 fpm; a second roll speed of 20 fpm; a third roll speed of 40 fpm; and a fourth roll speed of 80 fpm. In this embodiment, the speed of the nip rollers is approximately 75 fpm. In a further embodiment, the speed of the first chilled roll may be approximately 400 fpm; the speed of subsequent rolls may be approximately 750 fpm to stretch the continuous filaments; the speed of the composite material being formed at the nip rollers may be approximately 1500 fpm; and the winding roller speed (to allow relaxation and, thus, gathering of the spunbond facings) may be approximately 700 fpm.
- After passing through the series of rollers and becoming stretched, the continuous filaments are then bonded to the
nonwoven materials nonwoven materials - The system employs nip rolls 19 and 20 to apply pressure to the adhesive-coated facing and the continuous filaments to result in the necessary lamination. The outer facing is bonded together with the continuous filaments at a fairly high surface pressure, which may be between about 20 and 300 pounds per linear inch (“pli”). A typical bonding pressure may be about 50 pli or about 100 pli.
- The bonder, or nip roll, (sometimes referred to as “laminator”) section of the laminating apparatus performs the primary stretching on the continuous filaments. The speed ratio of the bonder or nip rolls relative to the chilled rolls can be varied, and in most cases is between about 2:1 and 8:1 and in some is approximately 4:1 to 6:1.
- After bonding of the facing(s) to the continuous filaments to form a spunbond/elastomeric continuous filament/spunbond laminate, the laminate is then allowed to relax and contract to an unstretched or less stretched, condition. The laminate is then wound onto the take-
up roll 21 via a surface driven winder. The speed ratio of the winder relative to the bonder rollers results in relaxation of the stretched continuous filaments and a retraction of the laminate into a gathered state as the laminate is wound onto the roll. For example, the winder speed to bonder roll speed may be approximately 0.3 to about 1.0, and may be from about 0.5 to 1.0. The contraction of the continuous filaments results in a gathered, stretchable laminate article where the outer facing(s) is gathered between the bonding points. - The overall basis weight of the laminate can vary, but in some applications is between about 2 and about 4 ounces per square yard (“oz/yd2”). In one particular embodiment, the basis weight is between about 2.85 and about 3.2 ozlyd2.
- Various types of compositions and various processing conditions may be utilized to form the elastic continuous filaments. For example, a Kraton® brand elastic polymer may be fed into an extruder where the polymer is melted at a controlled temperature of between about 2600 and 460° F., and in certain instances at about 385°. In other embodiments, depending on the particular polymer employed, the melt temperature may be approximately 470° F. to 480° F. The polymer is then extruded through a predetermined number of apertures in a die head in a generally downward direction into separate continuous filaments at a pressure of approximately 300 to 4000 psi (typically from about 1500 to about 2000 psi). As explained below, various die hole configurations may be utilized in the present invention.
- One particular class of polymers that may be utilized in the present process is the Kraton® G series of polymers distributed by Shell Chemical Company (now available from Kraton Products U.S.-LLC). Various Kraton® polymers may be utilized.
- However, the present invention is not limited to this or any particular polymer or material from which to form the continuous filaments. For example, various materials, including the following, may be used: polypropylene, polyethylene, polyesters, polyethylene terephthalate, polybutane, polymethyldentene, ethylenepropylene co-polymers, polyamides, tetrablock polymers, styrenic block copolymers, polyhexamethylene adipamide, poly-(oc-caproamide), polyhexamethylenesebacamide, polyvinyls, polystyrene, polyurethanes, thermoplastic polymers, polytrifluorochloroethylene, ethylene vinyl acetate polymers, polyetheresters, polyurethane, polyurethane elastomerics, polyamide elastomerics, polyamides, viscoelastic hot melt pressure sensitive adhesives, cotton, rayon, hemp and nylon. In addition, such materials may be utilized to extrude single-constituent, bi-constituent, and bi-component filaments within the scope of the presently described invention.
- Other exemplary elastomeric materials that may be used include polyurethane elastomeric materials such as those available under the trademark ESTANE from B. F. Goodrich & Co., polyamide elastomeric materials such as those available under the trademark PEBAX from the Rilsan Company, and polyester elastomeric materials such as those available under trade designation HYTREL from E. I. DuPont De Nemours & Company.
- However, the invention is not limited to only such elastomeric materials. For example, various latent elastic materials such as the Arnitel-brand polymers may be utilized to provide the necessary elasticity characteristics to the continuous filaments.
- Likewise, the above-referenced materials, and others, may be utilized in forming the outer facings of the presently described laminate. In particular, various webs may be utilized that are formed from elastomeric or nonelastomeric fibers. Various polyester elastic materials are, for example, disclosed in U.S. Pat. No. 4,741,949 to Morman et al., which is incorporated herein in its entirety by reference thereto. Other useful elastomeric polymers also include, for example, elastic copolymers of ethylene and at least one vinyl monomer such as, for example, vinyl acetates, unsaturated aliphatic monocarboxylic acids, and esters of such monocarboxylic acids. The elastic copolymers and formation of elastomeric fibers from these elastic copolymers are disclosed in, for example, U.S. Pat. No. 4,803,117, which is also incorporated herein in its entirety by reference thereto.
- Various processing aids may also be added to the elastomeric polymers utilized in the present invention. For example, a polyolefin may be blended with the elastomeric polymer (e.g., the A-B-A elastomeric block copolymer) to improve the processability of the composition. The polyolefin should be one which, when so blended and subjected to an appropriate combination of elevated pressure and elevated temperature conditions, is extrudable in blended form with the elastomeric polymer. Useful blending polyolefin materials include, for example, polyethylene, polypropylene and polybutene, including ethylene copolymers, propylene copolymers and butene copolymers. A particularly useful polyethylene may be obtained from the U.S.I. Chemical Company under the trade designation Petrothene NA 601 (also referred to herein as PE NA 601 or polyethylene NA 601). Two or more of the polyolefins may be utilized. Extrudable blends of elastomeric polymers and polyolefins are disclosed in, for example, U.S. Pat. No. 4,663,220, which is incorporated herein in its entirety by reference thereto.
- Referring to
FIG. 5 , an alternative embodiment of a process for producing laminates in accordance with the present invention is shown. In this embodiment, theVFL system 111 is also vertically configured. As stated above, however, horizontally configured systems are equally applicable to the present invention. - As shown in
FIG. 5 , anextruder 115 is mounted for extruding continuousmolten filaments 114 downward from a die at a canted angle onto chilledpositioning roller 112.Chilled positioning roller 112 ensures proper alignment through the remainder of the system as it spreads the filaments. As the filaments travel over the surface ofchilled positioning roller 112, they are cooled and solidified as they travel towards and over the chilled surface ofchilled roller 113. The filaments then travel downward towards the laminator section of the system comprising a nip formed by anip roller 119 and a niproller 120. - The continuous filaments are combined at the nip with various types of facings. In the embodiment depicted in
FIG. 5 , a first nonwoven spunbond facing 122 and a second nonwoven spunbond facing 124 are combined on opposing surfaces of the continuous filaments to form a bondedlaminate 125. - In accordance with the present invention, a slot extrusion die 123 is used to apply an adhesive material to the facing 122, while a slot extrusion die 153 is used to apply an adhesive material to the spunbond facing 124.
- In the embodiment illustrated in
FIG. 5 , only two chill rolls are used as opposed to the greater number of chill rolls shown inFIG. 1 . - As stated above, the use of a starved slot coat extrusion process as described above provides various advantages. For example, unexpectedly it was discovered that the starved slot coat process decreases the porosity of the resulting laminate, even at relatively low adhesive application rates. For example, laminates as shown in
FIG. 1 can be produced having an air permeability of less than about 400 cfm per ft2, such as less than about 350 cfm per ft2, and, in one embodiment, may be less than about 300 cfm per ft2. In other embodiments, the air permeability of the laminate may be less than about 250 cfm per ft2, such as less than about 230 cfm per ft2. For laminates only containing a single facing material laminated to the continuous filaments, the air permeability may be less than about 300 cfm per ft2. For example, in applications particularly where the facing comprises a spunbond web, the air permeability of the composite material may be less than about 250 cfm per ft2, such as less than about 230 cfm per ft2. - Having a lower porosity facilitates handling of the material in later converting processes. For example, such laminates are well suited for use in the construction of absorbent articles, such as diapers. During the production of a diaper, the elastic laminate typically needs to be cut, manipulated and bonded into place. During these process steps, vacuum is often used in order to convey and move the material. Lowering the porosity of the material greatly facilitates the ability to manipulate the material using a vacuum or suction force. Ultimately, materials made according to the present invention may be processed at higher machine speeds greatly increasing throughput.
- The present invention may be better understood with respect to the following examples.
- Testing Procedures
- During the examples that follow, the following tests were performed on the samples that were produced.
- Porosity was measured using procedure number STM 3801. Porosity was measured using a Frazier air permeability tester. The units are cubic feet per minute per square foot (cfm per ft2).
- Elongation was measured test procedure number STM 529-W. Elongation may be tested using any suitable tensile testing equipment, such as those available from the Syntech Corporation of Cary, N.C., or from the Instron Corporation of Canton, Mass.
- In a Peel Test, a laminate is tested for the amount of force needed to pull the layers of the laminate apart. The peel strength was measured using testing procedure number STM 751-W. The samples were tested in the cross machine direction. Any suitable tensile testing equipment may be used in order to perform the procedure.
- The following example was performed in order to determine the effect of the slot coat extrusion process on the porosity of nonwoven laminates.
- In this example, two spunbond webs were laminated together. The spunbond webs used were made from polypropylene and had a basis weight of 0.42 osy.
- Nine samples were produced and tested. In the first three samples, an adhesive was sprayed between the spunbond webs using a uniform fiber depositor (“UFD”) available from ITW Dynatec of Hendersonville, Tenn. under the name Dynafiber™ UFD nozzle. The uniform fiber depositor had one inch wide nozzles and contained fourteen capillaries per nozzle. The adhesive used in conjunction with the spray device was adhesive number H2808-07 obtained from Bostik, Inc. and is an SIS-based adhesive. This particular adhesive is well suited for use in spray processes.
- When spraying the adhesive between the spunbond webs, two different uniform fiber depositors were used that were positioned adjacent to each web.
- In the remaining six samples produced, the spunbond webs were laminated together using a slot extrusion die. In particular, the slot extrusion die was model number BC62 obtained from the Nordson Corporation. The slot on the slot extrusion die has a 0.15 inch gap and was 20 inches wide.
- The adhesive used in conjunction with the slot extrusion die was HX9375-01 obtained from Bostik, Inc., which is a polyolefin copolymer blend. This particular adhesive is somewhat stiff and therefore does not always produce a uniform spray pattern. The adhesive is well suited for use with slot extrusion dies.
- The adhesive was heated prior to being applied to the nonwoven webs using the slot extrusion die. In sample numbers 4 and 5 below, the extruder was heated to a temperature of from about 340° F. to about 345° F. In the remaining samples, however, the extruder was heated to a temperature of from about 355° F. to about 360° F.
- The adhesive add-on rates were the same for both the spray process and the slot extrusion die process, and range from 1 gsm to 3 gsm.
- The following results were obtained:
TABLE NO. 1 Adh Adh Adhesive Nip Nip Sample How Head #1 Head #2 Total Pressure Speed Porosity No. Applied GSM GSM GSM PLI FPM CFM 1 Spray 0.5 0.5 1 100 1000 474 2 Spray 1 1 2 100 1000 424 3 Spray 1.5 1.5 3 100 1000 429 4 Slot Coat 1 n/a 1 40 1000 430 5 Slot Coat 2 n/a 2 40 1000 433 6 Slot Coat 3 n/a 3 40 1000 407 7 Slot Coat 1 n/a 1 40 1000 391 8 Slot Coat 2 n/a 2 40 1000 339 9 Slot Coat 3 n/a 3 40 1000 320 - As shown above, laminates formed using the slot extrusion die had a lower porosity than the laminates produced using the spray device.
- In this example, elastic laminates were produced according to the present invention and tested for various properties. In order to produce the laminates, a process similar to the one illustrated in
FIG. 5 was used. Specifically, a VFL process was used that contained two chill rolls. The laminates produced included two layers of material, namely a spunbond facing adhered to continuous elastic filaments. - The facing comprised a polypropylene spunbond web having a basis weight of 0.4 osy.
- The elastic continuous filaments were made from elastomeric block copolymers. Specifically, the elastic filaments were made using KRATON G2838 polymer available from Kraton products.
- The same two adhesives identified in Example No. 1 were applied to the spunbond facing to produce the different samples. In particular, in the first five samples, adhesive HX9375-01 available from Bostik, Inc. was used, while in the remaining seven samples, adhesive number H2808-07 also obtained from Bostik, Inc. was used. The adhesive was applied to the spunbond web in amounts from 1.5 gsm to 2.5 gsm. The elastic filaments were laminated to the spunbond web at a basis weight of 10 gsm and were stretched 5.6 percent when attached. The temperature of the adhesive was varied depending upon the sample.
- In one sample, Sample No. 12 below, the adhesive was applied using the uniform fiber depositor as described in Example 1 for purposes of comparison.
- The following results were obtained:
TABLE NO. 2 Stretch to Stop Temp of Adhesive Nip Nip (at 2000 Load @ Sample Extruder Total Pressure Speed grams) 50% Porosity Peel, CD No. Adhesive ° F. GSM PLI FPM % grams CFM grams 1 HX9375-01 345 1.5 100 800 266 328 239 1665 2 HX9375-01 345 2.0 100 800 265 317 245 2352 3 HX9375-01 365 1.5 100 800 282 330 237 1855 4 HX9375-01 365 2.0 100 800 266 322 224 2248 5 HX9375-01 365 2.5 100 800 252 319 238 3305 6 H2808-07 345 1.5 100 800 295 292 254 443 7 H2808-07 345 2.0 100 800 294 307 241 479 8 H2808-07 345 2.0 100 800 284 306 226 517 9 H2808-07 365 1.5 100 800 294 305 250 571 10 H2808-07 365 2.0 100 800 302 312 245 603 11 H2808-07 365 2.5 100 800 298 315 238 550 12 H2808-07 365 2.5 100 800 265 298 266 2981 (control) (with spray device) - As shown above, the samples made according to the present invention had a much lower porosity than the control sample. As shown in the above table, the peel strength of samples made with the H2808-07 adhesive was generally less than the peel strength of the laminates made with the HX9375-01 adhesive. As explained in Example No. 1 above, the HX9375-01 adhesive is better suited for use with a slot extrusion die.
- These and other modifications and variations to the present invention may be practiced by those of ordinary skill in the art, without departing from the spirit and scope of the present invention, which is more particularly set forth in the appended claims. In addition, it should be understood that aspects of the various embodiments may be interchanged both in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention so further described in such appended claims.
Claims (30)
1. A method for producing a composite material comprising:
extruding continuous filaments, the filaments comprising an elastomeric material;
stretching the continuous filaments;
applying an adhesive material to a first side of a facing material, the adhesive material being applied to the facing material from a slot extrusion die, the adhesive material forming a discontinuous coating comprising amorphous elements of the adhesive material; and
laminating the stretched continuous filaments to the first side of the facing material after the adhesive material has been applied.
2. A method as defined in claim 1 , wherein, in terms of basis weight per area, the adhesive material is applied in a substantially uniform manner over the first side of the facing material.
3. A method as defined in claim 1 , further comprising the step of applying an adhesive material to a first side of a second facing material, the adhesive material being applied to the second facing material from a slot extruder; and
laminating the stretched continuous filaments to the first side of the second facing material, the stretched continuous filaments being positioned in between the first facing material and the second facing material to form the composite material, the composite material having a porosity of less than about 300 cfm per ft2.
4. A method as defined in claim 3 , wherein the first facing material and the second facing material comprise spunbond webs.
5. A method as defined in claim 1 , wherein the slot extrusion die defines a slot through which the adhesive material is emitted, and wherein the first side of the facing material contacts the slot as the adhesive material is applied to the facing material.
6. A method as defined in claim 1 , wherein the adhesive material is applied to the first side of the facing material in an amount less than about 4.4 gsm.
7. A method as defined in claim 1 , wherein the adhesive material is applied to the first side of the facing material in an amount from about 0.5 gsm to about 3 gsm.
8. A method as defined in claim 1 , wherein the adhesive material comprises a styrenic block copolymer, a random copolymer of a polyolefin, an amorphous polyalphaolefin, or mixtures therof.
9. A method as defined in claim 1 , wherein the adhesive material comprises a hotmelt adhesive.
10. A method as defined in claim 1 , wherein the adhesive material has a viscosity of from about 500 cp to about 50,000 cp as the material is being applied to the first side of the facing material.
11. A method as defined in claim 1 , wherein the continuous filaments move vertically downward as they are formed and laminated to the first facing material.
12. A method as defined in claim 1 , further comprising the step of relaxing the composite nonwoven material after the continuous filaments are laminated to the facing material.
13. A method as defined in claim 1 , further comprising the step of applying an adhesive material to a first side of a second facing material, the adhesive material being applied to the second facing material from a slot extrusion die, the adhesive material forming a discontinuous coating comprising amorphous elements of the adhesive material; and
laminating the stretched continuous filaments to the first side of the second facing material after the adhesive material has been applied to the second facing material, the stretched continuous filaments being positioned in between the first facing material and the second facing material to form the composite nonwoven material.
14. A method as defined in claim 1 , wherein the continuous filaments are stretched by being conveyed over at least one roller.
15. A method as defined in claim 1 , wherein the facing material comprises a nonwoven web having a basis weight of from about 0.2 osy to about 1.5 osy.
16. A method as defined in claim 15 , wherein the nonwoven web comprises a spunbond web.
17. A method as defined in claim 1 , wherein the elastomeric material used to make the filaments comprises an elastomer selected from the group consisting of elastic polyesters, elastic polyurethanes, elastic polyamides, elastic copolymers of ethylene and at least one vinyl monomer, elastic metallocene-catalyzed polyolefins, and elastic block copolymers.
18. A method as defined in claim 1 , wherein the resulting composite material has at least three layers and has an air permeability of less than about 350 cfm per ft2.
19. A method as defined in claim 1 , wherein the resulting composite material comprises only two layers including the layer of continuous filaments in the facing material, the facing material comprising a spunbond web, the composite material having an air permeability of less than about 400 cfm per ft2.
20. A composite elastic material comprising:
elastic continuous filaments extending generally in the same direction, the continuous filaments comprising an elastomeric material;
a nonwoven web having a first side and a second side, the first side of the nonwoven web being laminated to the elastic continuous filaments, the elastic continuous filaments being laminated to the nonwoven web in a stretched state such that the nonwoven web gathers when the elastic continuous filaments are relaxed; and
an adhesive material bonding the elastic continuous filaments to the first side of the nonwoven web, the adhesive material comprising a discontinuous coating on the first side of the nonwoven web, the discontinuous coating comprising amorphous elements of the adhesive material, the adhesive material being present on the nonwoven web in an amount less than about 4.4 gsm.
21. A composite elastic material as defined in claim 20 , wherein the adhesive material is present on the first side of the nonwoven web in an amount from about 0.8 gsm to about 3 gsm.
22. A composite elastic material as defined in claim 20 , wherein the adhesive material comprises a styrenic block copolymer, a random copolymer of a polyolefin, an amorphous polyalphaolefin, or mixtures therof.
23. A composite elastic material as defined in claim 20 , wherein the adhesive material comprises a hotmelt adhesive.
24. A composite elastic material as defined in claim 20 , further comprising a second nonwoven web having a first side and a second side, the first side of the second nonwoven web being laminated to the elastic continuous filaments such that the elastic continuous filaments are positioned in between the first nonwoven web and the second nonwoven web; and
an adhesive material bonding the elastic continuous filaments to the first side of the second nonwoven web, the adhesive material comprising a discontinuous coating on the first side of the second nonwoven web, the discontinuous coating comprising amorphous elements of the adhesive material, the adhesive material being present on the first side of the second nonwoven web in an amount of less than about 4.4 gsm.
25. A composite elastic material as defined in claim 20 , wherein the nonwoven web comprises a spunbond web having a basis weight of from about 10 gsm to about 20 gsm.
26. A composite elastic material as defined in claim 20 , wherein the elastomeric material used to form the continuous filaments comprises an elastomer selected from the group consisting of elastic polyesters, elastic polyurethanes, elastic polyamides, elastic copolymers of ethylene and at least one vinyl monomer, elastic metallocene-catalyzed polyolefins, and elastic block copolymers.
27. A composite elastic material as defined in claim 24 , wherein the composite elastic material has an air permeability of less than about 350 cfm per ft2.
28. A composite elastic material as defined in claim 20 , wherein the adhesive material is present on the first side of the nonwoven web in a substantially uniform manner in terms of amount per unit area.
29. A composite elastic material as defined in claim 20 , wherein the composite elastic material only comprises two layers including a layer of the continuous filaments and the nonwoven web, the nonwoven comprising a spunbond web, the composite elastic material having an air permeability of less than about 400 cfm per ft2.
30. A composite elastic material as defined in claim 20 , wherein the adhesive only coats the surface fibers of the nonwoven web and does not appreciably deposit in any pores on the nonwoven web.