US20050170541A1 - Radical processing of a sub-nanometer insulation film - Google Patents
Radical processing of a sub-nanometer insulation film Download PDFInfo
- Publication number
- US20050170541A1 US20050170541A1 US11/086,396 US8639605A US2005170541A1 US 20050170541 A1 US20050170541 A1 US 20050170541A1 US 8639605 A US8639605 A US 8639605A US 2005170541 A1 US2005170541 A1 US 2005170541A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- film
- thickness
- oxide film
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method of nitriding an insulation film, includes the steps of forming nitrogen radicals by high-frequency plasma, and causing nitridation in a surface of an insulation film containing therein oxygen, by supplying the nitrogen radicals to the surface of the insulation film.
Description
- The present invention generally relates to semiconductor devices and more particularly to the fabrication process of ultrafine high-speed semiconductor devices having a high-K dielectric film.
- In the technology of recent advanced high-speed semiconductor devices, use of the gate length of 0.1 μm or less is becoming possible with the progress in the art of ultrafine semiconductor fabrication processes. Generally, operational speed of a semiconductor device is improved with device miniaturization, while there is a need, in such extremely miniaturized semiconductor devices, to reduce the thickness of the gate insulation film thereof with the decrease of the gate length achieved as a result of the device miniaturization.
- When the gate length has been reduced to 0.1 μm or less, on the other hand, the thickness of the gate insulation film has to be reduced to 1-2 nm or less when a conventional thermal oxide film is used for the gate insulation film. In such an extremely thin gate insulation film, however, there inevitably arises a problem of increased tunneling current, while such an increased tunneling current causes the problem of large gate leakage current.
- In view of the situation noted above, there has been a proposal of using a high-dielectric material (so-called high-K dielectric material) having a much larger specific dielectric constant as compared with a thermal oxide film and thus capable of achieving a small SiO2-equivalent thickness while maintaining a large physical thickness, for the gate insulation film. Such a high-K material includes Ta2O5, Al2O3, ZrO2, HfO2, ZrSiO4, HfSiO4, and the like. By using such a high-K dielectric material, it becomes possible to use the physical thickness of about 10 nm in ultra high-speed semiconductor devices having a gate length of 0.1 μm or less. Thereby, the gate leakage current caused by tunneling effect is successfully suppressed.
- For example, a Ta2O5 film has been formed by a CVD process while using Ta(OC2H5)5 and O2 as gaseous sources. In a typical example, the CVD process is conducted under a reduced pressure at a temperature of about 480° C. or more. The Ta2O5 film thus formed is then subjected to a thermal annealing process in an oxidizing ambient and the oxygen defects in the film are compensated. Further, the film undergoes crystallization. The Ta2O5 film thus crystallized shows a large specific dielectric constant.
- From the view point of increasing carrier mobility in the channel region, it is preferable to provide an extremely thin base oxide film having a thickness of 1 nm or less, preferably 0.8 nm or less, between the high-K dielectric gate oxide film and the silicon substrate. This base oxide film has to be extremely thin. Otherwise, the effect of using the high-K dielectric film for the gate insulation film is cancelled out. On the other hand, such an extremely thin base oxide film is required also to cover the silicon substrate surface uniformly, without forming defects such as surface states.
- Conventionally, rapid thermal oxidation (RTO) process of a silicon substrate has been used when forming a thin gate oxide film. When such an RTO process is used for forming a thermal oxide film with the desired thickness of 1 nm or less, there is a need of decreasing the processing temperature at the time of the film formation. However, such a thermal oxide film formed at low temperature tends to contain a large amount of surface states and is not suitable for the base oxide film of a high-K dielectric gate oxide film.
-
FIG. 1 shows the schematic construction of a high-speed semiconductor device 100 having a high-K dielectric gate insulation film. - Referring to
FIG. 1 , thesemiconductor device 100 is constructed on asilicon substrate 1 and includes a high-K dielectric gate insulation film such as Ta2O5, Al2O3, ZrO2, HfO2, ZrSiO4, HfSiO4, and the like, formed on thesilicon substrate 1 via a thinbase oxide film 2. Further, agate electrode 4 is formed on the high-K dielectricgate insulation film 3. - In the
semiconductor device 100 ofFIG. 1 , there is conducted nitrogen (N) doping on the surface part of thebase oxide film 2 within the extent that a flat interface is maintained between thesilicon substrate 1 and thebase oxide film 2. As a result of the nitrogen doping, thebase oxide film 2 includes anoxynitride film 2A. In view of the large specific dielectric constant of such a silicon oxynitride film larger than that of a silicon oxide, it becomes possible to reduce the oxide-equivalent thickness of thebase oxide film 2 further, by forming theoxynitride film 2A in thebase oxide film 2. - As explained before, it is preferable that the
base oxide film 2 has as small thickness as possible in such a high-speed semiconductor device 100. - However, it has been extremely difficult to form the
base oxide film 2 with the thickness of 1 nm or less, such as 0.8 nm or less, or even 0.3-0.4 nm, while simultaneously maintaining uniformity and reproducibility. In the case the film has the thickness of 0.3-0.4 nm, the oxide film has actually a thickness of only 2-3 atomic layers. - In order that the high-K dielectric
gate insulation film 3 formed on thebase oxide film 2 performs as a high-K dielectric film, it is necessary to crystallize the deposited high-Kdielectric film 3 by a thermal annealing process and conduct compensation process of oxygen vacancy defects. However, such a thermal annealing process applied to the high-K dielectricgate insulation film 3 causes an increase of thickness in thebase oxide film 2, and the desired decrease of the effective thickness of the gate insulation film, achieved by the use of the high-K dielectricgate insulation film 3, is more or less cancelled out. - Such an increase of thickness of the
base oxide film 2 associated with the thermal annealing process suggests the possibility of mutual diffusion of oxygen atoms and silicon atoms and associated formation of a silicate transition layer, or the possibility of growth of thebase oxide film 2 caused by the penetration of oxygen into the silicon substrate. Such a problem of increase of thebase oxide film 2 with thermal annealing process becomes a particularly serious problem in the case the thickness of the base oxide film is reduced to several atomic layers or less. - In view of the situation noted above, the inventor of the present invention has previously proposed the use of ultraviolet-excitation oxygen radical (UV-O2 radial) substrate processing apparatus for the formation of the base oxide film. By using such an ultraviolet-excitation oxygen radial processing apparatus, it becomes possible to grow a high-quality oxide film with low growth rate under low radical density.
-
FIG. 2 shows the construction of a conventional UV-O2 radialsubstrate processing apparatus 10. - Referring to
FIG. 2 , thesubstrate processing apparatus 10 includes aprocessing vessel 11 that holds asubstrate 12 therein under a reduced pressure environment, wherein thesubstrate 12 is held on astage 11A having aheater 11 a. Further, there is provided ashowerhead 11B in theprocessing vessel 11 so as to face thesubstrate 12 on thestage 11A, and an oxidizing gas such as oxygen, O3, N2O, NO, or a mixture thereof is supplied to theshower head 21B. - The
showerhead 11B is formed of a material transparent to ultraviolet radiation such as quartz, and theprocessing vessel 11 is formed with awindow 11C of quartz and the like, which is transparent to the ultraviolet radiation, such that thewindow 11C exposes thesubstrate 12 on thestage 11A. Further, aultraviolet source 13 is formed outside thewindow 11C such that theultraviolet source 13 is movable along the surface of thewindow 11C. - Thus, a silicon substrate is introduced in the
processing vessel 11 ofFIG. 2 as thesubstrate 12, and an oxidizing gas such as oxygen is introduced into theprocessing vessel 11 after evacuating the interior thereof. By activating theultraviolet source 13 under this state, active radicals such as O* are formed in the oxidizing gas. The radicals thus excited by the ultraviolet radiation cause oxidation on the exposed surface of thesilicon substrate 12, and as a result, there is formed an extremely thin oxide film of 0.5-0.8 nm thickness on the surface of thesilicon substrate 12. - In the
substrate processing apparatus 10 ofFIG. 2 , the oxide film can be formed with a uniform thickness by causing to move theultraviolet source 13 along theoptical window 11C. - Because of the oxide film is formed by the ultraviolet-activated oxidation process, the oxide film has an advantageous feature of small defect density such as surface states as is reported by Zhang et al. (Zhang, J-Y., et al. Appl. Phys. Lett. 71(20), 17 Nov. 1997, pp.2964-2966) and is suitable for the base oxide film to be formed under the high-K dielectric gate insulation film.
- As explained before, the base oxide film underneath the high-K dielectric gate insulation film has to be extremely thin, and a thickness of about 0.8 nm has been achieved for such a base oxide film by using the UV-O2 radical substrate processing apparatus. However, it has been difficult to reduce the thickness of the base oxide film further, and it was particularly difficult to form such an extremely thin oxide film with high-precision and with uniform thickness.
- Meanwhile, there has been an argument that formation of a metal oxide film having a small interatomic bond valence, and hence a “low rigidity”, on a surface of a single-crystal silicon substrate, which has a large interatomic bond valence and hence a “high rigidity”, would lead to a mechanical instability at the interface between the silicon substrate and the metal oxide film, and that such mechanical instability may cause defects (see for example G. Lucovisky, et al., Appl. Phys. Lett. 74, pp.2005, 1999). Further, in order to avoid this problem, there is a proposal to form a transitional layer of oxynitride at the interface between the silicon substrate and the metal oxide film by introducing a single layer of nitrogen atoms. Further, formation of such an oxynitride film for the base oxide film of a high-K dielectric gate insulation film is thought effective for suppressing diffusion of metal element or oxygen in the high-K dielectric gate insulation film to the silicon substrate or diffusion of silicon from the silicon substrate to the high-K dielectric gate, or for suppressing the diffusion of dopant element from the gate electrode.
- In order to form such an oxynitride film, there has been a proposal to oxidize the surface of an oxide film by using microwave-excited remote plasma. This technology, which achieves the desired nitridation by using a microwave, requires a very high-degree vacuum of the order of 1.33×10−1-1.33×10−4Pa (10−3-10−6 Torr). However, nitridation process conducted under such an extremely high-degree vacuum state raises the problem in that minute amount of impurity such as residual oxygen or water in the processing vessel, provides a profound effect on the process by way of oxidation. Such oxidation occurred at the time of the nitridation process causes the problem of unwanted increase of thickness of the oxide film. As noted before, such an increase of thickness of the oxide film at the process of forming the oxynitride film cancels out the effect of using the high-K dielectric gate insulation film.
- Conventionally, it has been extremely difficult to form such an extremely thin oxynitride film with reliability and reproducibility in a vacuum state easily achieved by an ordinary semiconductor process, without causing increase of film thickness by oxidation.
- Accordingly, it is a general object of the present invention to provide a novel and useful substrate processing method and apparatus wherein the foregoing problems are eliminated.
- Another and more specific object of the present invention is to provide a substrate processing method capable of forming an extremely thin insulation film on a substrate, a semiconductor device using such an insulation film, and fabrication process of such a semiconductor device.
- Another object of the present invention is to provide substrate processing method and apparatus capable of forming an extremely thin oxide film, typically having a thickness of 2-4 atomic layers or less, on a surface of a silicon substrate with reliability and further capable of forming an oxynitride film by causing nitridation in the oxide film thus formed.
- Another object of the present invention is to provide substrate processing method and apparatus capable of forming an extremely thin oxynitride film typically having a thickness of 2-4 atomic layers or less and further capable of forming an oxynitride film having a higher nitrogen concentration and a desired thickness by causing nitridation of the initial oxynitride film.
- Another object of the present invention is to provide a cluster-type substrate processing system including a substrate processing apparatus capable of forming an extremely thin oxide film or nitride film typically having a thickness of 2-4 nm or less, on the surface of a silicon substrate with reliability and further capable of nitriding the oxide film or nitride film thus formed with reproducibility and with reliability.
- Another object of the present invention is to provide a substrate processing method capable of forming an extremely thin oxynitride film on a silicon substrate directly with excellent reliability and reproducibility.
- Another object of the present invention is to provide a method of nitriding an insulation film containing therein oxygen, comprising the steps of:
-
- forming nitrogen radicals by using high-frequency plasma; and
- nitriding a surface of said insulation film by supplying said nitrogen radicals to said surface of said insulation film.
- Another object of the present invention is to provide a method of fabricating a semiconductor device, comprising the steps of:
-
- forming an insulation film on a silicon substrate surface;
- forming nitrogen radicals by high-frequency plasma;
- forming an oxynitride film by causing nitridation in a surface of said insulation film by supplying said nitrogen radicals to said surface of said oxynitride film; and
- forming a high-K dielectric film on said oxynitride film.
- Another object of the present invention is to provide a substrate processing apparatus, comprising:
-
- a nitrogen radical formation unit forming nitrogen radicals by high-frequency plasma; and
- a processing vessel holding a substrate formed with said insulation film,
- said processing vessel being supplied with said nitrogen radicals form said nitrogen radical formation part and causing nitridation of a surface of said insulation film by supplying said nitrogen radical to said surface of said insulation film.
- According to the present invention, it becomes possible to nitride the surface of an extremely thin oxide film with excellent reproducibility by using the nitrogen radicals excited by high-frequency plasma. Further, according to the present invention, it becomes possible to form an oxynitride film of high nitrogen concentration with a desired thickness by nitriding the surface of an extremely thin oxynitride film by using the nitrogen radicals excited by the high-frequency plasma. By using high-frequency plasma, it becomes possible to conduct the nitridation process at relatively high pressures, and it becomes possible to dilute any impurity gas components such as residual oxygen remaining in the processing vessel by the plasma gas by merely evacuating the processing vessel at the beginning of the nitriding process to a sufficiently low pressure. Thereby, the problem of unwanted oxidation caused by the residual oxygen and associated problem of increased thickness of the oxynitride film are successfully suppressed. Particularly, the present invention enables nitridation of an extremely thin base oxide film formed under a high-K dielectric gate insulation film, and as a result, the problem of mutual diffusion of metal element and silicon between the silicon substrate and the high-K dielectric gate insulation film, and the associated problem of formation of a transitional layer are effectively suppressed.
- While it is generally unavoidable that an extremely thin insulation film such as oxide film or oxynitride film undergoes increase of film thickness as a result of incorporation of nitrogen atoms at the time of the nitridation process, it is possible in the present invention to maintain the thickness of the insulation film after the nitridation process, in other words the thickness of the oxynitride film, to be extremely small, by controlling the thickness of the insulation film before the nitridation process to 2-4 atoms layers or less.
- Another object of the present invention is to provide a substrate processing apparatus comprising:
-
- a processing vessel defining a process space and having a stage in said process space for holding a substrate to be processed;
- a first radical source provided on said processing vessel;
- a second radical source provided on said processing vessel;
- a first evacuation path provided on said processing vessel for evacuating said process space to a first process pressure; and
- a second evacuation path provided on said processing vessel for evacuating said process space to a second process pressure.
- Another object of the present invention is to provide a cluster-type substrate processing system, comprising:
-
- a substrate transfer chamber; and
- a plurality of processing chambers connected to said substrate transfer chamber,
- one of said plurality of processing chambers comprising:
- a processing vessel having a substrate load/unload part connected to said substrate transfer chamber at a first end and a first radical source at a second end opposite to said first end, said processing vessel defining therein a process space;
- a stage provided in said process space rotatably between said first end and said second end, said stage holding thereon a substrate to be processed;
- a first process gas inlet provided in said process space between said first end and said stage, said first process gas inlet introducing a first process gas into said process space;
- a second process as inlet introducing a second process gas to said first radical source;
- a second radical source provided on said processing vessel so as to activate said first process gas between said first process gas inlet and said stage;
- a first evacuation port provided in said process space at a part closer to said first end with respect to said stage;
- a second evacuation port provided in said process space at a part closer to said second end with respect to said stage;
- a first pump connected to said first evacuation port so as to evacuate said process space to a first process pressure;
- a second pump connected to said second evacuation port so as to evacuate said process space to a second process pressure lower than said first process pressure;
- said second pump being disposed in the vicinity of said second end of said processing vessel.
- According to the present invention, it becomes possible to conduct ultraviolet-excited radical oxidation process of a silicon substrate to form an oxide film and a radical nitridation process of such an oxide film, formed by the ultraviolet-excited radical oxidation process by using radicals excited by high-frequency remote plasma, such that the radical nitridation process is conducted continuously to the radical oxidation process. Although the pressure suitable for ultraviolet-excited radical oxidation process and the pressure suitable for radical nitridation process conducted by using a high-frequency remote plasma are very much different, the present invention allows to conduct these two processes in the common processing vessel by providing two evacuation paths on the processing vessel. Particularly, the present invention enables nitridation of an extremely thin base oxide to be formed underneath a high-K dielectric gate insulation film, and as a result, the problem of mutual diffusion of metal element and silicon between the silicon substrate and the high-K dielectric gate insulation film or formation of transitional layer associated with such mutual diffusion, is successfully suppressed by forming the high-K dielectric gate insulation film on the base oxide film. Further, the present invention enables easy construction of a cluster-type substrate processing system while using the substrate processing apparatus, by arranging the first and second evacuation paths in the processing vessel such that a turbo molecular pump, which is necessary for realizing high degree vacuum in the processing vessel, is located at the outer end part of the processing vessel. Thereby, the substrate processing apparatus can be connected to a substrate transfer unit at an inner end part thereof.
- Another object of the present invention is to provide a semiconductor device, comprising:
-
- a silicon substrate; and
- an insulation film provided on said silicon substrate,
- said insulation film having a thickness of 2-4 atomic layers.
- Another object of the present invention is to provide a semiconductor device, comprising:
-
- a silicon substrate; and
- an insulation film provided on said silicon substrate,
- said insulation film being formed by nitriding an oxide film formed on said silicon substrate with a thickness of 1-4 atomic layers.
- Another object of the present invention is to provide a method of processing a substrate, comprising the step of forming an oxide film on a surface of a silicon substrate by an oxidation process,
-
- said oxidation process being conducted with oxygen radicals having a partial pressure in the range of 133-133×10−4 mPa.
- Another object of the present invention is to provide a method of fabricating a semiconductor device, comprising the steps of:
-
- forming a base oxide film on a surface of a silicon substrate;
- forming a high-K dielectric film on said base oxide film; and
- forming a gate electrode layer on said high-K dielectric film,
- said step of forming said base oxide film comprising an oxidizing step conducted by oxygen radicals having a partial pressure in the range of 133-133×10−4 mPa.
- According to the present invention, it becomes possible to form an extremely thin oxide film suitable for a base oxide film used between a silicon substrate and a high-K dielectric gate insulation film with a uniform thickness and with excellent reproducibility by utilizing the phenomenon film growth delay, which appears in the radical oxidation process of a silicon substrate surface in the case the oxide film has grown to a thickness of 2-4 atomic layers.
- Another object of the present invention is to provide a method of processing a substrate, comprising the steps of:
-
- supplying an NO gas to a surface of a silicon substrate; and
- forming an oxynitride film on said surface of said silicon substrate by exciting said NO gas with ultraviolet radiation.
- According to the present invention, it becomes possible to form an oxynitride film directly on a silicon substrate surface by exciting an NO ambient with ultraviolet radiation. Thereby, it becomes possible to suppress the occurrence of oxidation by choosing the wavelength of the ultraviolet radiation to be longer than 145 nm but not exceeding 192 nm, for example to 172 nm. Thereby, an oxynitride film having a high nitrogen concentration level is formed. Such an oxynitride film shows a delay of film growth at the film thickness of about 0.5 nm corresponding to two atomic layers. Thus, the oxynitride film can be formed stably and with excellent reproducibility to this film thickness.
- Other objects and further features of the present invention will become apparent from the following detailed description when read in conjunction with the attached drawings.
-
FIG. 1 is a diagram showing the construction of a semiconductor device having a high-K dielectric gate insulation film; -
FIG. 2 is a diagram showing the construction of a conventional UV-O2 radical substrate processing apparatus; -
FIG. 3 is a diagram showing the construction of a substrate processing apparatus according to a first embodiment of the present invention; -
FIGS. 4A and 4B are diagrams showing on oxidation process of a substrate conducted by the substrate processing apparatus ofFIG. 3 respectively in a side view and in a plan view; -
FIG. 5 is a diagram showing an oxidation process of a substrate conducted by using the substrate processing apparatus ofFIG. 3 ; -
FIG. 6 is a diagram explaining the procedure of measuring the film thickness by an XPS analysis as used in the present invention; -
FIG. 7 is another diagram explaining the procedure of measuring the film thickness by an XPS analysis as used in the present invention; -
FIG. 8 is a diagram schematically showing the phenomenon of delay of oxide film growth observed when forming an oxide film by the substrate processing apparatus ofFIG. 3 ; -
FIGS. 9A and 9B are diagrams showing the oxide film formation process on a surface of a silicon substrate; -
FIG. 10 is a diagram showing the leakage current characteristics of an oxide film obtained in the first embodiment of the present invention; -
FIGS. 11A and 11B are diagrams explaining the cause of the leakage current characteristics ofFIG. 10 ; -
FIGS. 12A-12C are diagrams showing the process of oxide film formation taking place in the substrate processing apparatus ofFIG. 3 ; -
FIG. 13 is a diagram showing the construction of a remote plasma source used in the substrate processing apparatus ofFIG. 3 ; -
FIG. 14A is a diagram comparing the characteristics of RF remote plasma and microwave plasma, whileFIGS. 14B and 14C are diagrams respectively showing the construction of a standard remote-plasma source and a microwave plasma source; -
FIG. 15 is another diagram comparing the characteristics of RF remote plasma and microwave plasma; -
FIGS. 16A and 16B are diagrams showing the nitridation process of an oxide film conducted by the substrate processing apparatus ofFIG. 3 respectively in a side view and a plan view; -
FIGS. 17A and 17B are diagrams comparing the relationship between nitrogen concentration and film thickness for an oxide film nitrided by using the RF remote plasma and an oxide film nitrided by using the microwave plasma; -
FIG. 18 is a diagram schematically showing the XPS analysis used in the present invention; -
FIG. 19 is a diagram showing the relationship between the nitridation time and the nitrogen concentration in an oxide film for the case the oxide film is nitrided by the remote plasma; -
FIG. 20 is a diagram showing the relationship between the duration of nitridation and the distribution of nitrogen for the case an oxide film is subjected to a nitridation process; -
FIG. 21 is a diagram showing the wafer-by-wafer film thickness variation of an oxynitride film formed by a nitridation process of an oxide film; -
FIG. 22 is a diagram showing the increase of film thickness of an oxide film associated with the nitridation process according to the first embodiment of the present invention; -
FIGS. 23A and 23B are diagrams showing in-plane uniformity of the nitridation process realized in the substrate processing apparatus ofFIG. 3 ; -
FIG. 24 is a diagram showing the relationship between the increase of film thickness and the nitrogen concentration of the film for the case an UV-O2 oxide film or an UV-NO oxynitride film is subjected to an RF nitridation process; -
FIG. 25 is a flowchart showing an RF nitridation process of an UV-O2 oxide film; -
FIGS. 26A-26C are diagrams showing the chemical shift appearing in an XPS spectrum of an Si2p orbital at the time a high-K dielectric film is formed on an oxynitride film obtained according to the first embodiment of the present invention; -
FIG. 27 is a diagram showing the increase of film thickness occurring in the oxynitride film obtained by the first embodiment of the present invention before and after the formation of the high-K dielectric film; -
FIGS. 28A and 28B are flowcharts showing a substrate processing method according to a second embodiment of the present invention; -
FIGS. 29A and 29B are diagrams respectively showing the film thickness and the nitrogen concentration in the film for an oxynitride film formed by the process ofFIGS. 28A and 28B ; -
FIGS. 30A and 30B are flowcharts showing the substrate processing method according to a comparative example of the second embodiment of the present invention; -
FIGS. 31A and 31B are diagrams respectively showing the film thickness and the nitrogen concentration in the film for an oxynitride film formed by the process ofFIGS. 30A and 30B ; -
FIG. 32 is a flowchart showing a substrate processing method according to a third embodiment of the present invention; -
FIGS. 33A and 33B are diagrams showing the thickness of the oxynitride film formed according to the substrate processing method of the third embodiment and the thickness of the oxynitride film formed according to a comparative example; -
FIG. 34 is a diagram showing a potential curve of an NO molecule for various excitation states thereof; -
FIG. 35 is a flowchart showing the RF nitridation process of a UV-NO oxide film; -
FIG. 36 is a diagram showing the distribution of nitrogen atoms in an oxynitride film obtained by the process ofFIG. 35 ; -
FIGS. 37A and 37B are diagrams showing an example of distribution state of nitrogen atoms in an oxynitride film; -
FIG. 38 is a diagram explaining the problem when a cluster-type substrate processing system is constructed by using the substrate processing apparatus ofFIG. 3 ; -
FIGS. 39A and 39B are diagrams showing the construction of a cluster-type substrate processing apparatus according to a fifth embodiment of the present invention; -
FIGS. 40A and 40B are diagrams showing oxidation processing of a substrate conducted by using the substrate processing system ofFIG. 39 ; -
FIGS. 41A and 41B are diagrams showing nitriding processing of a substrate conducted by using the substrate processing system ofFIG. 39 ; -
FIG. 42 is a diagram showing the construction of a semiconductor device according to a sixth embodiment of the present invention; -
FIG. 43 is a flowchart showing the substrate processing method according to the sixth embodiment; -
FIG. 44 is a diagram explaining the thickness distribution of an initial oxide film used in the sixth embodiment of the present invention; -
FIGS. 45A-45C are diagrams showing the thickness distribution of an oxynitride film formed according to the sixth embodiment of the present invention; -
FIGS. 46A-46D are diagrams explaining the kinetics of the oxynitride film formation process according to the sixth embodiment of the present invention; -
FIGS. 47A-47D are further diagrams explaining the kinetics of the oxynitride film formation process according to the sixth embodiment of the present invention; -
FIGS. 48A and 48B are diagrams showing the nitrogen doping mechanism of an oxide film in the oxynitride film formation process according to the sixth embodiment of the present invention; -
FIGS. 49A and 49B are diagrams showing the distribution of nitrogen atoms in an oxynitride film formed according to the sixth embodiment of the present invention together with the distribution of oxygen atoms and Si atoms; -
FIGS. 50A and 50B are further diagrams showing the distribution of nitrogen atoms in an oxynitride film formed according to the sixth embodiment of the present invention together with the distribution of oxygen atoms and Si atoms; -
FIG. 51 is a diagram showing the construction of a substrate processing apparatus according to a seventh embodiment of the present invention; -
FIGS. 52A-52C are diagrams showing the thickness distribution of an oxide film formed by using the substrate processing apparatus ofFIG. 51 ; -
FIG. 53 is a diagram showing the relationship between the processing time and film thickness for an oxide film formed by the substrate processing apparatus ofFIG. 51 ; -
FIGS. 54A-54E are further diagrams showing the thickness distribution of an oxide film formed by the substrate processing apparatus ofFIG. 51 ; -
FIGS. 55A-55E are further diagrams showing the thickness distribution of an oxide film formed by the substrate processing apparatus ofFIG. 51 ; -
FIGS. 56A and 56B are diagrams showing the thickness distribution of an oxide film according to a comparative example; -
FIG. 57 is a flowchart showing the procedure of determining the optimum scanning region in the substrate processing apparatus ofFIG. 51 ; -
FIG. 58 is a flowchart showing the procedure of determining the optimum drive energy of optical source in the substrate processing apparatus ofFIG. 51 ; -
FIG. 59 is a diagram showing the construction of a semiconductor device according to an eighth embodiment of the present invention; -
FIG. 60 is a diagram showing the construction of a cluster-type substrate processing system used in the eight embodiment; -
FIG. 61 is a diagram for determining the process conduction used in the eight embodiment; -
FIGS. 62A and 62B are diagrams showing the thickness distribution of an oxide film formed on a silicon substrate for the case the oxide film is subjected to a UV-NO processing according to a ninth embodiment of the present invention; -
FIGS. 63A and 63B are diagrams showing the thickness distribution of an oxynitride film for the case the oxynitride film is formed on a surface of a silicon substrate directly by the UV-NO processing; -
FIGS. 64A and 64B are diagrams showing the kinetics of oxynitride film formation on a silicon substrate surface by the UV-NO processing according to the ninth embodiment of the present invention; -
FIGS. 65A and 65B are further diagrams showing the kinetics of oxynitride film formation on a silicon substrate surface by the UV-NO nitriding processing according to the ninth embodiment of the present invention; -
FIGS. 66A and 66B are further diagrams showing the kinetics of oxynitride film formation on a silicon substrate surface by the UV-NO nitriding processing according to the ninth embodiment of the present invention; -
FIG. 67 is a diagram showing an example of an optical source; -
FIGS. 68A and 68B are diagrams showing the thickness distribution of an oxynitride film obtained according to a substrate processing process according to a tenth embodiment of the present invention; -
FIGS. 69A and 69B are diagrams showing an NO gas supply sequence according to an eleventh embodiment of the present invention; -
FIGS. 70A and 70B are diagrams showing the thickness of an oxynitride film formed by using the NO gas supplying sequence ofFIGS. 69A and 69B and a nitrogen concentration therein; -
FIGS. 71A-71E are diagrams showing the fabrication process of a semiconductor device according to a twelfth embodiment of the present invention; -
FIG. 72 is a diagram showing a preferred condition of RF-N2 processing according to the first embodiment of the present invention; -
FIG. 73 is a diagram showing the relationship between the process condition and film thickness distribution in the sixth embodiment of the present invention; -
FIGS. 74A and 74B are diagrams respectively showing an XPS spectrum of a silicon oxide film and the relationship between the chemical shift of the XPS spectrum and the film thickness; and -
FIG. 75 is a diagram showing the result of measurement of film thickness variation conducted by an improved ellipsometry on an oxynitride film formed on a wafer of 200 mm diameter by the UV-NO processing. -
FIG. 3 shows the general construction of asubstrate processing apparatus 20 according to a first embodiment of the present invention for forming the thinbase oxide film 2 on thesilicon substrate 1 ofFIG. 1 together with theoxynitride film 2A. - Referring to
FIG. 3 , thesubstrate processing apparatus 20 includes aprocessing vessel 21 accommodating therein astage 22 equipped with aheater 22A such that thestage 22 is movable vertically between a process position and a substrate load/unload position. Thestage 22 is rotated by adrive mechanism 22C, and theprocessing vessel 21 defines aprocess space 21B therein together with thestage 22. The inner surface of theprocessing vessel 21 is covered with aninner liner 21G of a quartz glass, and theinner liner 21G suppresses the metal contamination of the substrate to be processed to the level of 1×1010 atoms/cm2 or less. - Further, there is provided a
magnetic seal 28 at the connecting part of thestage 22 and thedrive mechanism 22C such that themagnetic seal 28 separates amagnetic seal chamber 22B held in a vacuum environment from thedrive mechanism 22C formed in the atomic environment. Because themagnetic seal 28 is a liquid, thestage 22 is held so as to be able to rotate freely. - In the illustrated state, the
stage 22 is held at the process position and there is formed a load/unloadchamber 21C underneath thestage 22 for loading and unloading the substrate. Theprocessing vessel 21 is connected to asubstrate transfer unit 27 via agate valve 27A, and thus, the substrate W is transported to thestage 22 from thesubstrate transfer unit 27 via thegate valve 27A in the state that stage 22 has been lowered to the load/unloadchamber 21C. Further, the processed substrate W is transferred to thesubstrate transfer unit 27 from thestage 22. - In the
substrate processing apparatus 20 ofFIG. 3 , there is formed anevacuation port 21A near thegate valve 27 of theprocessing vessel 21, and a turbomolecular pump 23B is connected to theevacuation port 21A via thevalve 23A and an APC (automatic pressure controller) 24B. The turbomolecular pump 23B is further connected to apump 24 formed of a dry pump and a mechanical booster pump via avalve 23C, and the pressure inside theprocess space 21B can be reduced to the level of 1.33×10−1-1.33×10−4 Pa (10−3-10−6 Torr) by driving the turbomolecular pump 23B and thedry pump 24. - It should be noted that the
evacuation port 21A is connected also to thepump 24 directly via avalve 24A and anAPC 24B, and thus, the pressure of the process space is reduced to the level of 1.33 Pa-1.33 kPa (0.01-10 Torr) by thepump 24 when thevalve 24A is opened. - The
processing vessel 21 is provided with a processgas supplying nozzle 21D at the side opposite to theevacuation port 21A across the substrate W, and an oxygen gas is supplied to the processgas supplying nozzle 21D. The oxygen gas thus supplied to the processgas supplying nozzle 21D is caused to flow in theprocess space 21B along the surface of the substrate W and is evacuated from theevacuation port 21A. - In order to activate the process gas thus supplied from the process
gas supplying nozzle 21D, thesubstrate processing apparatus 20 ofFIG. 3 is provided with an ultravioletoptical source 25 having aquartz window 25A on theprocessing vessel 21 in correspondence to the region located between the processgas supplying nozzle 21D and the substrate W. Thus, by driving theultraviolet source 25, the oxygen gas introduced in to theprocess space 21B from the processgas supplying nozzle 21D is activated, there are formed oxygen radicals and the oxygen radicals thus formed are caused to flow along the surface of the substrate W. As a result, it becomes possible to form a radical oxide film on the surface of the substrate W with a thickness of 1 nm or less, particularly with the thickness of about 0.4 nm, which corresponds to the thickness of 2-3 atomic layers. - Further, the
processing vessel 21 is provided with aremote plasma source 26 at the side thereof opposite to theevacuation port 21A with respect to the substrate W. Thus, nitrogen radicals are formed by supplying a nitrogen gas to theremote plasma source 26 together with an inert gas such as Ar and by activating the nitrogen gas thus supplied with plasma. The nitrogen radicals thus formed are caused to flow along the surface of the substrate W and causes nitridation of the substrate surface. By introducing oxygen into theremote plasma source 26 in place of nitrogen, it is also possible to oxidize the substrate surface. - In the
substrate processing apparatus 20 ofFIG. 3 , there is provided apurge gas line 21 c for purging the load/unloadchamber 21C with a nitrogen gas. Further, there is provided apurge line 22 b for purging themagnetic seal chamber 22B with a nitrogen gas and anevaluation line 22 c of the purge gas. - In more detail, the
evacuation line 22 c is connected to a turbomolecular pump 29B via avalve 29A, and the turbomolecular pump 29B is connected to thepump 24 via avalve 29C. Further, theevacuation line 22 c is connected directly to thepump 24 via avalve 29D. With this, it becomes possible to maintain themagnetic seal chamber 22B at various pressures. - The load/unload
chamber 21C is evacuated by thepump 24 via the valve 24C or by the turbomolecular pump 23B via thevalve 23D. Further, in order to avoid contamination in theprocess space 21B, the load/unloadchamber 21C is held at a lower pressure than theprocess space 21B, and themagnetic seal chamber 21B is held at a further lower pressure than the load/unloadchamber 21C by a conducting differential evacuation process. - Hereinafter, the ultraviolet radical oxidation process and the remote plasma radical nitridation process conducted subsequently to the radical oxidation process on the surface of the substrate W by using the
substrate processing apparatus 20 ofFIG. 3 will be explained. - Ultraviolet Radical Oxidation (UV-O2) Processing
-
FIGS. 4A and 4B are diagrams showing the radical oxidation process of the substrate W by using thesubstrate processing apparatus 20 ofFIG. 3 respectively in a side view and a plan view. - Referring to
FIG. 4A , an oxygen gas is supplied to the process space 12B from the processgas supplying nozzle 21D and the oxygen gas thus supplied is evacuated, after flowing along the surface of the substrate W, via theevacuation port 21A,APC 23D, turbomolecular pump 23B and thepump 24. By using the turbomolecular pump 23B and theAPC 23D, the base pressure in theprocess space 21B is set to the level of 1×10−3-10−6 Torr, which is needed for the oxidation of the substrate by oxygen radicals. - Simultaneously to this, the
ultraviolet source 25, preferably the one that produces ultraviolet radiation of 172 nm wavelength, is activated, and oxygen radicals are formed in the oxygen gas flow thus formed. The oxygen radicals thus formed cause oxidation of the substrate surface as they are caused to flow along the rotating substrate W. Thus, as a result of the oxidation of the substrate W by the ultraviolet-activated oxygen radicals (referred to hereinafter as UV-O2 processing), a very thin oxide film having a thickness of 1 nm or less, particularly the thickness of about 0.4 nm corresponding to the thickness of 2-3 atomic layers, is formed on a surface of a silicon substrate stably and with excellent reproducibility. -
FIG. 4B shows the construction ofFIG. 4A in a plan view. - Referring to
FIG. 4B , it can be seen that theultraviolet source 25 is a tubular light source extending in the direction crossing the direction of the oxygen gas flow. Further, it can be seen that the turbomolecular pump 23B evacuates theprocess space 21B via theevacuation port 21A. Further, it should be noted that the evacuation path, designated inFIG. 4B by a dotted line and extending directly from theevacuation port 21A to thepump 24, is closed by closing thevalve 24A. - As can be seen from the plan view of
FIG. 4B , the turbomolecular pump 23B is provided in an arrangement so as to extend laterally from the processing vessel. Thereby, the turbomolecular pump 23B successfully avoids thesubstrate transfer unit 27. -
FIG. 5 shows the relationship between the film thickness and oxidation time for the case a silicon oxide film is formed on a surface of a silicon substrate in the process ofFIGS. 4A and 4B by using thesubstrate processing apparatus 20 ofFIG. 3 by setting the substrate temperature at 450° C. and changing the ultraviolet radiation power and the oxygen gas flow rate or oxygen partial pressure variously. In the experiment ofFIG. 5 , it should be noted that any native oxide film on the silicon substrate surface is removed prior to the radical oxidation process. In some cases, the substrate surface is planarized by removing residual carbon from the substrate surface by using nitrogen radicals excited by ultraviolet radiation, followed by a high temperature annealing process conducted at about 950° C. in an Ar ambient. An excimer lamp having a wavelength of 172 nm is used for theultraviolet source 24B. - Referring to
FIG. 5 , the data ofSeries 1 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to 5% of a reference power (50 mW/cm2) at the window surface of theultraviolet radiation source 24B and the process pressure is set to 665 mPa (5 mTorr) and further the oxygen gas flow rate is set to 30 SCCM. On the other hand, the data ofSeries 2 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to zero, the process pressure is set to 133 Pa (1 Torr) and the oxygen gas flow rate is set to 3 SLM. - The data of
Series 3 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to zero, the process pressure is set to 2.66 Pa (20 mTorr) and the oxygen gas flow rate is set to 150 SCCM, while the data ofSeries 4 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to 100% of the reference power, the process pressure is set to 2.66 Pa (20 mTorr) and further the oxygen gas flow rate is set to 150 SCCM. - The data of
Series 5 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to 20% of the reference power, the process pressure is set to 2.66 Pa (20 mTorr) and the oxygen gas flow rate is set to 150 SCCM, while the data ofSeries 6 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to 20% of the reference power, the process pressure is set to about 67 Pa (0.5 Torr) and further the oxygen gas flow rate is set to 0.5 SLM. - Further, the data of
Series 7 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to 20% of the reference power, the process pressure is set to 665 Pa (5 Torr) and the oxygen gas flow rate is set to 2 SLM, while the data ofSeries 8 represents the relationship between the oxidation time and oxide film thickness for the case the ultraviolet radiation power is set to 5% of the reference power, the process pressure is set to 2.66 Pa (20 mTorr) and the oxygen gas flow rate is set to 150 SCCM. - In the experiment of
FIG. 5 , the thickness of the oxide film is obtained by an XPS analysis, in view of the fact that there is no standard process of obtaining the thickness of such an extremely thin oxide film having a film thickness less than 1 nm. - In view of the situation noted above, the inventor of the present invention obtained a film thickness d of an oxide film by first obtaining a Si2p 3/2 XPS spectrum shown in
FIG. 7 by applying, to an observed XPS spectrum of Si2p orbital shown inFIG. 6 , a background correction and separation correction for separating the 3/2 spin state and the 1/2 spin state, and then obtaining the film thickness d from the Si2p 3/2 XPS spectrum thus obtained by using Equation (1) and associated coefficients below according to the teaching of Lu et al (Z. H. Lu, et al., Appl. Phys. Lett. 71(1997), pp.2764),
d=λ sin α·ln[I X+/(βI 0+)+1] (1) -
- λ=2.96
- β=0.75
- In Eq. (1), it should be noted that a represents the detection angle of the XPS spectrum of
FIG. 6 and is set to 30° in the illustrated example. Further, IX+ in Eq. (1) represents an integral spectrum intensity (I1++I2++I3++I4+) of the oxide film and corresponds to the peak observed in the energy region of 102-104 eV ofFIG. 7 . On the other hand, I0+ corresponds to the integral spectral peak intensity corresponding to the energy region around 100 eV, wherein this spectral peak is caused by the silicon substrate. - Referring to
FIG. 5 again, it will be noted that the oxide film thickness increases gradually from the initial thickness of 0 nm with the oxidation time for the case the ultraviolet radiation power, and hence the oxygen radical density formed by the ultraviolet radiation, is set small (Series Series FIG. 8 . The growth of the oxide film is restarted only after a certain time has elapsed in the slowdown state. - The relationship of
FIG. 5 or 8 means that there is a possibility of forming an extremely thin oxide film of the thickness of about 0.4 nm stably in the oxidation process of a silicon substrate surface. Further, the fact that the slowdown state continues for some time as represented inFIG. 5 indicates that the oxide film thus formed has a uniform thickness. Thus, according to the present invention, it is possible to form an oxide film having a thickness of about 0.4 nm on a silicon substrate with uniform thickness. -
FIGS. 9A and 9B schematically depicts the manner of oxide film formation on such a silicon substrate. In these drawings, it should be noted that the structure formed on a (100) silicon substrate is very much simplified. - Referring to
FIG. 9A , it can be seen that two oxygen atoms are bonded to a single silicon atom at the surface of the silicon substrate, and thus, there is formed a single oxygen atomic layer. In this representative state, each silicon atom on the substrate surface are coordinated by two silicon atoms inside the substrate and two oxygen atoms at the substrate surface, and there is formed a sub-oxide. - In the state of
FIG. 9B , on the other hand, each silicon atom at the uppermost part of the silicon substrate is coordinated with four oxygen atoms and takes the stable state of Si4+. It is believed that this is the reason the oxidation proceeds fast in the state ofFIG. 9A and slows down when the state ofFIG. 9B has appeared. The thickness of the oxide film for the state ofFIG. 9B is about 0.4 nm, while this value is in good agreement with the oxide film thickness observed for the slowdown state inFIG. 5 . - In the XPS spectrum of
FIG. 7 , it should be noted that the weak peak observed in the energy range of 101-104 eV for the case the oxide film thickness is 0.1 or 0.2 nm corresponds to the sub-oxide ofFIG. 9A . On the other hand, the peak appearing in this energy range for the case the oxide thickness has exceeded 0.3 nm is thought as being caused by Si4+ and indicating the formation of an oxide film exceeding the thickness of 1 atomic layer. -
FIG. 74A shows a raw XPS spectrum of a silicon oxide film formed on a silicon substrate and a chemical shift caused in the XPS spectrum, whileFIG. 74B shows the relationship between the XPS film thickness of the silicon oxide film, in other words the film thickness obtained by the XPS analysis and the chemical shift ofFIG. 74A . - Referring to
FIGS. 74A and 74B , it can be seen that the magnitude of the chemical shift increases with increasing XPS film thickness, while it can also be seen that the chemical shift reaches the value of 4 eV, which is inherent to a silicon oxide film, when the XPS film thickness has reached the value between 0.3 nm and 0.4 nm. Further, it is noted that there appears saturation in the chemical shift at the point when the XPS film thickness has reached the value between 0.3 nm and 0.4 nm. As explained before, the thickness of such an extremely thin oxide film may change when the measurement apparatus is changed or when the value of the constants λ and β used in the equation (1) noted before is changed. In view of this, it is also possible to define the 0.4 nm thickness explained heretofore in the present invention as being the minimum slowdown film thickness (the film thickness in which the slowdown of film growth is observed) that provides the chemical shift of about 4 eV for the oxide film. - Such a slowdown of oxide film growth at the thickness of 0.4 nm is thought as not being limited to the UV-O2 radical oxidation process explained with reference to
FIGS. 4A and 4B . Rather, this phenomenon would be observed also in any oxide film formation process as long as it is capable of forming extremely thin oxide films with high precision. - By continuing the oxidation process further from the state of
FIG. 9B , the thickness of the oxide film starts to increase again. -
FIG. 10 shows the relationship between a thermal-oxide equivalent thickness Teq and leakage current Ig for a laminated structure in which a ZrSiOx film having a thickness of 0.4 nm and an electrode film are formed on an oxide film formed by the UV-O2 oxidation process ofFIGS. 4A and 4B (reference should be made toFIG. 11B to be explained later) by using the substrate processing apparatus ofFIG. 3 . It should be noted that the leakage current characteristics ofFIG. 10 are measured in the state a voltage of Vfb-0.8V is applied across the electrode film and the silicon substrate, wherein Vfb is a flat-band voltage used for the reference. For the sake of comparison,FIG. 10 also shows the leakage current characteristics of a thermal oxide film. Further, the illustrated equivalent thickness is for the structure including both the oxide film and the ZrSiOx film. - Referring to
FIG. 10 , it can be seen that the leakage current density exceeds the leakage current density of the thermal oxide film in the case the oxide film is omitted and hence the film thickness of the oxide film is 0 nm. Further, it can be seen that the thermal-oxide film equivalent thickness Teq also takes a large value of about 1.7 nm. - Contrary to this, it can be seen that the thermal-oxide equivalent thickness Teq starts to decrease when the thickness of the oxide film is increased from 0 nm to 0.4 nm. In such a state, the oxide film is interposed between the silicon substrate and the ZrSiOx film, and thus, there should be caused an increase of physical thickness. The observed decrease of the equivalent thickness Teq is therefore contrary to this increase of physical thickness. This observation suggests the situation that, in the case the ZrSiOx film is formed directly on the silicon substrate, there occurs extensive diffusion of Zr into the silicon substrate or Si into the ZrSiOx film as represented in
FIG. 11A , leading to formation of a thick interface layer between the silicon substrate and the ZrSiOx film. By interposing the oxide film of 0.4 nm thickness as represented inFIG. 11B , it is believed that the formation of such an interface layer is effectively suppressed and the decrease of the equivalent film thickness is achieved as a result. With this, the leakage current is reduced with increasing thickness of the oxide film. It should be noted thatFIGS. 11A and 11B shows a schematic cross-section of the specimen thus formed and shows the structure in which anoxide film 42 is formed on asilicon substrate 41 and aZrSiOx film 43 is formed on theoxide film 42. - When the thickness of the oxide film has exceeded 0.4 nm, on the other hand, the value of the thermal-oxide equivalent thickness starts to increase again. In this region in which the thickness of the oxide film has exceeded 0.4 nm, it can be seen that the value of the leakage current is decreased with increase of the thickness, suggesting that the increase of the equivalent thickness is caused as a result of increase of the physical thickness of the oxide film.
- Thus, it can be seen that the oxide film thickness of about 0.4 nm, in which there is caused slowdown of oxide film growth as observed in
FIG. 5 , corresponds to the minimum of the equivalent thickness of the system formed of the oxide film and high-K dielectric film, and that the diffusion of metal element such as Zr into the silicon substrate is effectively blocked by the stable oxide film shown inFIG. 9B . Further, it can be seen that the effect of blocking the metal element diffusion is not enhanced significantly even when the thickness of the oxide film is increased further. - It should be noted that the value of the leakage current for the case of using the oxide film of the foregoing 0.4 nm thickness is smaller than the leakage current of a thermal oxide film having a corresponding thickness by the order of two. Thus, by using an insulation film having such a structure for the gate insulation film of a MOS transistor, it becomes possible to minimize the gate leakage current.
- As a result of slowdown of the oxide film growth at the thickness of 0.4 nm explained with reference to
FIG. 5 orFIG. 8 , there occurs a slowdown of film thickness at the time of oxide film growth at the thickness of about 0.4 nm as represented inFIG. 12B even in the case there exists a change of film thickness or undulation in theinitial oxide film 42 formed on thesilicon substrate 41. Thus, by continuing the oxide film growth during the slowdown period, it becomes possible to obtain an extremelyflat oxide film 42 of uniform film thickness as represented inFIG. 12C . - As explained before, there is no standard measuring method of film thickness for such an extremely thin oxide film at the moment. Thus, a different value may be obtained for the film thickness of the
oxide film 42 ofFIG. 12C when a different measuring method is used. However, because of the reason explained before, it is determined that the slowdown of oxide film growth occurs at the thickness of two atomic layers. Thus, it is thought that the preferable thickness of theoxide film 42 is about two atomic layers. It should be noted that this preferable thickness includes also the case in which theoxide film 42 includes a region of 3 atomic layers in a part thereof such that the thickness of two atomic layers is maintained for the entirety of theoxide film 42. Thus, it is concluded that the preferable thickness of theoxide film 42 is in the range of 2-3 atomic layers. - Remote Plasma Radical Nitridation (RF-N2) Processing
-
FIG. 13 shows the construction of aremote plasma source 26 used in thesubstrate processing apparatus 20 ofFIG. 3 . - Referring to
FIG. 13 , theremote plasma source 26 includes ablock 26A typically formed of aluminum in which agas circulating passage 26 a is formed together with agas inlet 26 b and agas outlet 26 c communicating therewith. Further, there is formed aferrite core 26B on a part of theblock 26A. - Further, there is provided a
fluorocarbon resin coating 26 d on the inner surfaces of thegas circulating passage 26 a,gas inlet 26 b and thegas outlet 26 c, andplasma 26C is formed in thegas circulating passage 26 a by supplying a high-frequency (RF)power 400 kHz perpendicular to the coil wound around theferrite core 26B. - With the excitation of the
plasma 26C, nitrogen radicals and also nitrogen ions are formed in thegas circulating passage 26 a, wherein the nitrogen ions thus formed have a strong tendency of proceeding straight and are annihilated as they are circulated along the circulatingpassage 26 a and thegas outlet 26 c ejects nitrogen radicals N2* primarily. In the construction ofFIG. 13 , charged particles such as nitrogen ions are eliminated in the construction ofFIG. 13 by providing anion filter 26 e at thegas outlet 26 c in the state that theion filter 26 e is connected to the ground. Thereby, only the nitrogen radicals are supplied to theprocess space 21B. Even in the case theion filter 26 e is not grounded, theion filter 26 e functions as a diffusion plate and it becomes possible to eliminate charged particles such as nitrogen ions sufficiently. In the case of conducting a process that requires a large amount of N2 radicals, it is possible to eliminate theion filter 26 e so as to prevent annihilation of the N2 radicals caused by collision at theion filter 26 e. -
FIG. 14A shows the relationship between the number of ions and the electron energy formed by theremote plasma source 26 ofFIG. 13 in comparison with the case of using a standard plasma source shown inFIG. 14B and a standard microwave plasma source shown inFIG. 14C . - Referring to
FIG. 14A , ionization of nitrogen molecules is facilitated in the case the plasma is excited by a microwave power, and as a result, there are formed a very large amount of nitrogen ions. In the case the plasma is excited by a high-frequency (RF) power of 500 kHz or less, on the other hand, the number of the nitrogen ions formed by the plasma is reduced significantly. - In the case of using the high-frequency plasma, there is a tendency that the plasma contains relatively large proportion of ions having large electron energy and that such ions may cause damaging in the substrate. In the construction of
FIG. 13 , on the other hand, the nitrogen ions having the strong tendency of proceeding straight are effectively annihilated in thegas circulating passage 26 a, and it becomes possible to introduce the N2 radicals selectively into the processing vessel. - As noted above,
FIGS. 14B and 14C show the construction of a standard high frequency plasma source and a standard microwave plasma source, respectively. - Referring to
FIG. 14B , a process gas is introduced into a plasma chamber 426 covered with aquartz liner 426 d from agas inlet 426 b provided above, andplasma 426C is excited in theplasma chamber 426D by exciting the plasma gas by a high-frequency power. - The nitrogen ions and the nitrogen radicals formed with the plasma 426 are then introduced into a processing chamber provided below the plasma source, and plasma nitridation is conducted in the plasma chamber. In the plasma source of such a construction, however, it is difficult to remove the nitrogen ions, which tend to proceed straight, completely even in the case a
trap 426 c is provided. - The same situation holds also in the case of the microwave plasma source of
FIG. 14C . Only difference is that a microwave is used for exciting the plasma. Thus, it is difficult to remove the nitrogen ions, which tend to proceed straight, from the radicals, even in the case a trap is provided. - Thus, by using the radical source shown in
FIG. 13 , an ion distribution shown inFIG. 14A by a dotted line is obtained, and it becomes possible to conduct an ideal remote plasma nitridation processing with minimum amount of ions. - In the case the plasma processing is conducted by using a microwave, a high vacuum environment of 1.33×10−3-1.33×10−6 Pa (10−-10−4 Torr) is needed, while in the case the plasma processing is conducted by using a high-frequency plasma, it is possible to conduct the process at a relatively high pressure of 13.3 Pa-1.33 kPa (0.1-10 Torr).
- Next, consideration will be made on the plasma excitation frequency and process pressure suitable for the remote plasma processing.
-
FIG. 72 shows the relationship between the plasma excitation frequency and the pressure interval in which ignition of plasma is possible. - Referring to
FIG. 72 , it can be seen that the pressure range allowing plasma ignition changes with the plasma excitation frequency. In the case the plasma excitation frequency of 400 kHz, the plasma ignition takes place in the pressure range of 1.33 Pa-1.33 kPa (0.001-10 Torr). In the case the plasma excitation frequency is 2.45 GHz, the plasma ignition takes place in the pressure range of 13.3 mPa-1.33 kPa (0.1 mTorr-0.01 Torr). - Here, consideration will be made on the preferable pressure. When the process pressure is too low, the nitrogen radicals introduced in the processing vessel would cause diffusion and there would appear a non-uniform nitridation processing in which only the marginal part of the substrate, which is located close to the radical source, undergoes nitridation, even in the case the substrate W is rotated in the
substrate processing apparatus 20 ofFIG. 3 . Thus, in order to achieve a uniform nitridation processing in thesubstrate processing apparatus 20 ofFIG. 3 by using the remoteradical source 26 ofFIG. 13 , there is a need that the flow of the radicals can be controlled to some extent. For this, it is necessary to control the process pressure in theprocessing vessel 21 to be a pressure of 0.01 Torr (1.33 Pa) as shown by a line A inFIG. 72 . When the process pressure is to high in theprocessing vessel 21, on the other hand, the nitrogen radicals would be annihilated by causing collision. Thus, it is necessary to control the process pressure in theprocessing vessel 21 to the value of 3 Torr (399 Pa) or less as represented by a line B inFIG. 72 . - Next, consideration will be made on the preferable plasma excitation frequency. In the case the plasma excitation frequency becomes less than 4 kHz shown by a line C, there is caused acceleration of ions and there arises a problem that high energy ions cause damaging in the substrate. In the case the plasma excitation frequency exceeds 13.56 MHz represented in
FIG. 72 by a line D, on the other hand, it becomes difficult to conduct the plasma processing with large flow rate. Thus, it is preferable to set the plasma excitation frequency not exceeding 13.56 MHz. - In summary, it is preferable to set the process pressure and the frequency in the hatched area of
FIG. 72 defined by the lines A-D in the case a radical nitridation processing is to be conducted by thesubstrate processing apparatus 20 ofFIG. 3 while using theradical source 26 ofFIG. 13 . In the present invention, a frequency of about 400 kHz is used as a representative frequency, while this representation means that the foregoing range is included. In the range of 40 kHz-4 MHz, substantially the same plasma processing is realized. - Table 1 below compares the ionization energy conversion efficiency, pressure range capable of causing electric discharge, plasma power consumption and process gas flow rate between the case of exciting plasma by a microwave and the case of exciting plasma by a high-frequency (RF) power.
TABLE 1 pressure ionization range energy causing plasma process conversion electric power gas flow efficiency discharge consumption rate micro- 1.00 × 10−2 0.1 m-0.1 Torr 1-500 W 0-100 SCCM wave RF- 1.00 × 10−7 0.1-100 Torr 1-10 kw 0.1-10 SLM wave - Referring to Table 1, it can be seen that the ionization energy conversion efficiency is reduced to about 1×10−7 in the case of the RF-excited plasma as compared with respect to the value of about 1×10−2 for the case of the microwave-excited plasma. Further, it can be seen that the pressure range causing the electric discharge is about 0.1-100 Torr (13.3 Pa-13.3 kPa) for the case of the RF-excited plasma, while in the case of the microwave-excited plasma, the pressure range is about 0.1 mTorr-0.1 Torr (13.3 Pa-13.3 kPa). Associated with this, the plasma power consumption is increased in the case of the RF-excited plasma as compared with the case of the microwave-excited plasma and that the process gas flow rate for the case of the RF-plasma processing becomes much larger than the process gas flow rate for the case of the microwave plasma.
- In the substrate processing apparatus of
FIG. 3 , it should be noted that the nitridation processing of the oxide film is conducted not by nitrogen ions but by the nitrogen radicals N2*. Thus, it is preferable that the number of the excited nitrogen ions is suppresses as small as possible. This is also preferable in the viewpoint of minimizing damages caused in the substrate. In the substrate processing apparatus ofFIG. 3 , the number of the excited nitrogen radicals is small and is highly suitable for nitriding the extremely thin base oxide film formed underneath the high-K dielectric gate insulation film with the thickness of only 2-3 atomic layers. Hereinafter, such a nitridation processing of oxide film conducted by the nitrogen radicals exited by the high-frequency plasma is called RF-N2 processing. - As explained before, it is possible to introduce the process gas with large flow rate in the
substrate processing apparatus 20 ofFIG. 3 by using the remote plasmaradical source 26 ofFIG. 13 . Thus, in such an RF-N2 processing, it becomes possible to conduct a uniform nitridation processing such that a uniform nitrogen concentration distribution is realized on the substrate surface. - In the case the process gas flow rate is increased, on the other hand, the region where the nitridation takes place is limited to the area near the central axis of the substrate that connects the
plasma source 26 and theevacuation port 21A ofFIG. 3 , contrary to the case of using a small process gas flow rate. Thus, by controlling the process gas flow rate, which represents the total of the Ar gas flow rate and the nitrogen gas flow rate, it is possible to adjust the extension of the region where the nitridation reaction takes place in the direction toward theevacuation port 21A. Thus, by optimizing the foregoing extension and rotating the substrate W, it becomes possible to improve the uniformity of the nitrogen concentration on the substrate surface. In the construction ofFIG. 3 , it is also possible that the admixing of the Ar gas to the nitrogen gas provides the effect of prolonging the lifetime of the nitrogen radicals. Thus, there is also a possibility that the admixing of the Ar gas is contributing to the improvement of the in-plane uniformity in the RF-N2 processing of the present invention. - In the nitridation processing that uses the microwave plasma, on the other hand, there is also a possibility that an in-plane uniformity comparable to the in-plane uniformity achieved by the remote-plasma nitridation processing is attained in the event the nitridation processing can be achieved under the condition of large gas flow rate.
-
FIGS. 16A and 156B show the radical nitridation (RF-N2) processing conducted by thesubstrate processing apparatus 20 ofFIG. 3 respectively in a side view and a plan view. - Referring to
FIGS. 16A and 16B , the remote plasmaradical source 26 is supplied with an Ar gas and a nitrogen gas and nitrogen radicals are formed as a result of excitation of plasma with the high frequency power of several hundred kilohertz frequency. The nitrogen radicals thus formed are caused to flow along the surface of the substrate W and are evacuated via theevacuation port 21A and thepump 24. As a result, theprocess space 21B is held at a process pressure in the range of 1.33 Pa-1.33 kPa (0.01-10 Torr) suitable for the radical nitridation of the substrate W. Particularly, use of the pressure range of 6.65-133 Pa (0.05-1.0 Torr) is preferable. The nitrogen radicals thus formed cause nitridation in the surface of the substrate W as they are caused to flow along the surface of the substrate W. - In the nitridation process of
FIGS. 16A and 16B , it should be noted that there is conducted a purging process in advance to the nitridation process by opening thevalves valve 24A. Thereby, the pressure in theprocess space 21B is reduced to the level of 1.33×10−1-1.33×10−4 Pa, and any residual oxygen or water in the process space is purged. In the nitridation processing that follows, on the other hand, thevalves molecular pump 23B is not included in the evacuation path of theprocess space 21B. - Thus, by using the
substrate processing apparatus 20 ofFIG. 3 , it becomes possible to form an extremely thin oxide film on the surface of the substrate W and further nitriding the surface of the oxide film thus formed. -
FIG. 17A shows the nitrogen concentration profile in an oxide film for the case the oxide film formed on a silicon substrate by a thermal oxidation process with a thickness of 2.0 nm is subjected to an RF-N2 processing in thesubstrate processing apparatus 20 ofFIG. 3 by using the RFremote plasma source 26 ofFIG. 13 under the condition represented in Table 2. Further,FIG. 17B shows the relationship between the nitrogen concentration profile and the oxygen concentration profile in the same oxide film.TABLE 2 nitrogen Ar flow flow plasma rate rate power pressure temperature microwave 15 SCCM — 120 W 8.6 mTorr 500° C. RF wave 50 SCCM 2SLM 2 kw 1 Torr 700° C. - Referring to Table 2, the RF-N2 processing is conducted in the
substrate processing apparatus 20 under the pressure of 1 Torr (133 Pa) while supplying nitrogen with a flow rate of 50 SCCM and Ar with a flow rate of 2 SLM, wherein it should be noted that the internal pressure of theprocess space 21B is reduced once to the level of about 10-6 Torr (1.33×10−4 Pa) before the commencement of the nitridation process such that oxygen or water remaining in theprocess space 21B is purged sufficiently. Because of this, any residual oxygen in theprocess space 21B is diluted with Ar or nitrogen in the nitridation process (RF-N2 process), which is conducted at the pressure of about 1 Torr. Thereby, the concentration of residual oxygen, and hence the thermodynamic activity of the residual oxygen, is very small at the time of the foregoing nitridation processing. - In the case of the nitridation processing conducted by the microwave plasma, on the other hand, the process pressure at the time of the nitridation process is generally the same as the purging pressure, and thus, residual oxygen maintains a large thermodynamic activity in the plasma ambient.
- Referring to
FIG. 17A , it can be seen that the concentration of nitrogen incorporated into the oxide film is limited in the case the nitridation processing is conducted by the microwave plasma and that no substantial nitridation takes place in the oxide film. In the case of the nitridation processing that uses the RF-excited plasma as in the case of the present embodiment, it can be seen that the nitrogen concentration level changes linearly with depth in the oxide film and that a concentration level of near 20% is achieved at the surface part of the oxide film. -
FIG. 18 shows the principle of the measurement ofFIG. 17A conducted by the XPS (X-ray photo spectrometry) analysis. - Referring to
FIG. 18 , an X-ray is radiated to the specimen in which theoxide film 12 is formed on thesilicon substrate 11 with a predetermined angle, and detectors DET1 and DET2 are used to detect the spectrum of the excited X-rays with various angles. Thereby, it should be noted that the detector DET1 set to a deep detection angle of 90 degrees detects the excited X-ray that has traveled through theoxide film 12 with minimum path length. Thus, the X-ray spectrum detected by the detector DET1 contains information about the deep part of theoxide film 12 with relatively large proportion. On the other hand, detector DET2 set to a shallow detection angle detects the X-ray traveled over a long distance in theoxide film 12. Thus, the detector DET2 mainly detects the information about surface part of theoxide film 12. -
FIG. 17B shows the relationship between the nitrogen concentration and oxygen concentration in the oxide film. InFIG. 17B , it should be noted that the oxygen concentration is represented by the X-ray intensity corresponding to the O1s orbital. - Referring to
FIG. 17B , it can be seen that there occurs decrease of oxygen concentration with increase of nitrogen concentration in the case the nitridation processing is conducted by the RF-N2 processing that uses the RF-remote plasma, indicating that there occurs substitution of oxygen atoms with the nitrogen atoms in the oxide film. In the case the nitridation is conducted by the microwave plasma processing, on the other hand, no such substituting relationship is observed and no relationship of oxygen concentration decreasing with increasing nitrogen concentration is observed. InFIG. 17B , it is also noted that there is an increase of oxygen concentration for the case in which nitrogen is incorporated with 5-6% by the microwave nitridation processing. This indicates that there occurs increase of thickness of the oxide film with nitridation. Such an increase of the oxygen concentration associated with the microwave nitridation processing is believed to be caused as a result of the high activity of oxygen or water remaining in the process space, which in turn is caused as a result of use of high vacuum environment for the nitridation processing and absence of dilution of residual oxygen or water with Ar gas or nitrogen gas, unlike the case of the high-frequency remote radical nitridation processing. -
FIG. 19 shows the relationship between the nitridation time and the nitrogen concentration in the film for the case an oxide film is formed by thesubstrate processing apparatus 20 ofFIG. 3 to the thickness of 4 Å (0.4 nm) and 7 Å (0.7 nm) and nitridation is conducted further to the oxide film by the RF-N2 processing ofFIGS. 16A and 16B while using theremote plasma source 26. Further,FIG. 20 shows the segregation of nitrogen to the surface of the oxide film caused as a result of the nitridation processing ofFIG. 19 . It should be noted thatFIGS. 19 and 20 also show the case in which the oxide film is formed by a rapid thermal oxidation processing to the thickness of 5 Å (0.5 nm) and 7 Å (0.7 nm). - Referring to
FIG. 19 , it can be seen that the nitrogen concentration in the film increases with the nitridation time in any of the oxide films, while it is also noted that, because of the small oxide thickness such as 0.4 nm corresponding to the two atomic layer thickness for the case of the oxide film formed by the UV-O2 oxidation processing, or for the case of the thermal oxide film having a thickness of 0.5 nm near the foregoing thickness of 0.4 nm, a higher nitrogen concentration is achieved as compared with oxide films formed at the same condition. -
FIG. 20 shows the result of detection of nitrogen concentration for the case the detectors DET1 and DET2 ofFIG. 19 are set to 30 degrees and 90 degrees respectively. - As can be seen from
FIG. 20 , the vertical axis represents the X-ray spectral intensity from the nitrogen atoms segregated to the film surface obtained with the detection angle of 30 degrees divided by the X-ray spectral intensity of the nitrogen atoms distributed throughout the entire film. The vertical axis ofFIG. 20 is defined as nitrogen segregation ratio. In the case the value of the nitrogen segregation ratio is 1 or more, there is caused segregation of nitrogen to the film surface. - Referring to
FIG. 20 , it can be seen that the nitrogen segregation ratio becomes one or more in the case the oxide film is formed by the UV-O2 processing to the thickness of 7 Å, and the nitrogen atoms are segregated at first to the film surface and a situation similar to theoxynitride film 12A ofFIG. 1 is realized. After the RF-N2 processing for 90 seconds, on the other hand, the nitrogen atoms are distributed generally uniformly in the film. In other films, too, it can be seen that the distribution of the nitrogen atoms in the film becomes generally uniform as a result of the RF-N2 processing for 90 seconds. - In the experiment of
FIG. 21 , the UV-O2 processing and the RF-N2 processing are applied in thesubstrate processing apparatus 20 ofFIG. 3 repeatedly with respect to ten wafers (wafer #1-wafer #10). -
FIG. 21 shows the wafer-to-wafer variation of the film thickness of the oxynitride film thus obtained, wherein the result ofFIG. 21 is obtained for the case in which the UV-O2 processing is conducted in the construction ofFIG. 3 by driving theultraviolet source 25 such that an oxide film is formed to have the thickness of 0.4 nm as measured by the XPS analysis and in which the RF-N2 processing is conducted to the oxide film thus formed by driving theremote plasma source 26 such that the oxide film is converted to an oxynitride film containing nitrogen atoms with about 4%. - Referring to
FIG. 21 , the vertical axis represents the film thickness obtained for the oxynitride film thus obtained by ellipsometry, wherein it can be seen that the film thickness is uniform and has a value of about 8 Å (0.8 nm). -
FIG. 22 shows the result of examination with regard to the increase of film thickness for the case an oxide film is formed on a silicon substrate in thesubstrate processing apparatus 20 ofFIG. 3 with the thickness of 0.4 nm by the UV-O2 processing while using theultraviolet source 25 and further an RF-N2 processing is applied to the oxide film thus formed while using theremote plasma source 26. - Referring to
FIG. 22 , it can be seen that the oxide film has increased the thickness thereof from the initial thickness (the thickness in the state before the RF-N2 processing) of 0.38 nm to about 0.5 nm in the state nitrogen atoms are introduced by the RF-N2 processing with the concentration of 4-7%. In the case the nitrogen atoms are introduced to the level of about 15% by the RF-N2 processing, on the other hand, it can be seen that the film thickness increases to about 1.3 nm. In this case, it is believed that the nitrogen atoms thus introduced into the oxide film form a nitride film by causing penetration into the silicon substrate after passing through the oxide film. - In
FIG. 22 , the relationship between the nitrogen concentration and film thickness is represented also for an ideal model structure in which only one layer of nitrogen atoms are introduced into the oxide film of 0.4 nm thickness by ▴. - Referring to
FIG. 22 , it can be seen that the film thickness after introduction of the nitrogen atoms becomes about 0.5 nm in this ideal model structure. Thereby, the increase of the film thickness for this model case becomes about 0.1 nm, and the nitrogen concentration becomes about 12%. - Using this model as a reference, it is concluded that the increase of film thickness is preferably suppressed to the value of 0.1-0.2 nm close to the foregoing value in the case the
substrate processing apparatus 20 ofFIG. 3 is used for the nitridation of the oxide film. In this state, it is evaluated that the maximum amount of the nitrogen atoms incorporated in to the film would be about 12% in the maximum. -
FIGS. 23A and 23B show the result of measurement of nitrogen concentration distribution and film thickness distribution of an oxynitride film for the case the oxynitride film is formed from an oxide film formed on the silicon substrate W in thesubstrate processing apparatus 20 ofFIG. 3 to the thickness of 2 nm while rotating the silicon substrate W by thedrive mechanism 22C. It should be noted that the experiment ofFIGS. 23A and 23B is conducted at the substrate temperature of 450° C. under the pressure of 133 Pa while rotating the silicon substrate formed with the oxide film with the thickness of 2 nm, while supplying an Ar gas and a nitrogen gas with the respective flow rates of 2 SLM and 50 SCCM. InFIG. 23A , the bright part represents the part where there is caused nitrogen concentration. Further,FIG. 23B shows the thickness of the oxynitride film obtained by the ellipsometry and the nitrogen concentration obtained by the XPS analysis. - The result of
FIGS. 23A and 23B shows that it is possible to realize a generally uniform nitrogen distribution over the entire surface of the substrate W even in the case of using thesubstrate processing apparatus 20, in which an asymmetric radical flow is caused, by rotating the substrate W and optimizing the flow rate of the Ar gas and the flow rate of the nitrogen gas. -
FIG. 24 is a diagram corresponding toFIG. 22 explained before and shows the relationship between the nitrogen concentration and film thickness as measured by the XPS analysis for the oxynitride film obtained by according to the flowchart ofFIG. 25 in which an oxide film is formed by the UV-O2 processing (step S1) and an RF-N2 processing is applied to the oxide film thus formed (step S2). InFIG. 24 , it should be noted that the initial thickness of the oxide film prior to the RF-N2 processing is changed variously. - Referring to
FIG. 24 , ● represents the relationship between the XPS film thickness and the nitrogen concentration in the film for the case the oxide film has an initial thickness of 0.4 nm and thus corresponds to the case represented inFIG. 22 by ●. In the experiment ofFIG. 24 , it can be seen that the nitrogen concentration in the oxynitride film thus obtained increases generally linearly with the XPS film thickness as long as the film thickness is in the range up to about 0.8 nm. - On the other hand, ▪ in the drawing shows the case in which the initial oxide film thickness is set to 0.3 nm. Again, it can be seen that the nitrogen concentration in the obtained oxynitride film increases linearly with the XPS thickness, with a gradient generally identical with the gradient for the case the oxide film has the initial thickness of 0.4 nm.
- Thus, in the case such an oxynitride film is used for the
base oxide film 2 underneath the high-K dielectric gate insulation film as shown inFIG. 1 , there is a possibility, in view of the relationship ofFIG. 24 , that there may be caused an increase of physical thickness in the oxynitride film when the nitrogen concentration in the film is too high. In such a case, the effect of using the high-K dielectricgate insulation film 3 is cancelled out, in spite of the fact that oxidation of thesilicon substrate 1 may be successfully suppressed by introducing nitrogen into thebase oxide film 2. - Thus, in order to introduce nitrogen into the oxynitride film formed by applying an RF-N2 processing to an oxide film formed by an UV-O2 processing (referred to hereinafter as UV-O2 oxide film), it is necessary to set the initial thickness of the UV-O2 oxide film to be less than 0.4 nm. In other words, it is necessary to set the initial thickness of the UV-O2 oxide film to be less than 0.4 nm in the case an oxynitride film introduced with such high-concentration nitrogen is to be used for the base oxide film of the high-dielectric gate insulation film.
-
FIGS. 26A-26C show the spectrum of the Si2p orbital obtained by the XPS analysis for the structure in which theoxide film 2 is formed on thesilicon substrate 1 with the UV-O2 processing and a HfO2 film is formed on theoxide film 2 as the high-K dielectric film 3, whereinFIG. 26A shows the state in which theoxide film 2 alone is formed whileFIG. 26B shows the state in which the HfO2 film is formed on theoxide film 2. Further,FIG. 26C shows the spectrum of the structure in which the HfO2 film is annealed. Further, each ofFIGS. 26A-26C shows a corresponding schematic device structure. InFIGS. 26A-26C , those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted. - Referring to
FIGS. 26A-26C , it can be seen that there is a low spectral peak B of the Si2p orbital having a chemical shift in the state ofFIG. 26A in addition to the spectral peak A of the Si2p orbital, while the intensity of the spectral peak B increases in the state ofFIG. 26B , and the strength of the spectral peak B is increased to the level comparable to the intensity of the peak A after the state ofFIG. 26C in which the thermal annealing process is conducted. - It should be noted that the chemical shift corresponding to the peak B is caused as a result of a Si atom in the
substrate 1 or a Si atom in theoxide film 2 causing a bond with an oxygen atom from the HfO2 film. Assuming that the chemical shift of the spectral peak for the Si2p orbital is caused entirely by the surface reaction on thesilicon substrate 1, it is possible to evaluate the increase of the film thickness of theoxide film 2 caused by the thermal annealing process ofFIG. 26C from the area of the peak B. -
FIG. 27 shows the evaluation of change of the film thickness of theoxide film 2 before formation of an HfO2 film and after a thermal annealing process for the case the HfO2 film is formed on an oxide film of various initial thicknesses and further the thermal annealing process is conducted. InFIG. 27 , the horizontal axis represents the initial thickness of the oxide film corresponding toFIG. 26A before the formation of the HfO2 film while the vertical axis represents the oxide film thickness after the thermal annealing process corresponding toFIG. 26C . - Referring to
FIG. 27 , it can be seen that there is caused a decrease of the final film thickness or slowing down of the final film thickness in the case the initial thickness of the UV-O2 oxide film has exceeded 0.4 nm. Assuming that this slowing down of increase of the film thickness corresponds to the suppression of the interface reaction at the surface of the silicon substrate, there is a possibility that the optimum thickness of theoxide film 2 is located slightly larger than the foregoing thickness of 0.4 nm, which thickness is thought as being optimum in the previous embodiment of forming a ZrSiO4 film from the ground of the observed slowing down of the film formation occurring at this thickness of 0.4 nm, for minimizing the interface reaction. - The degree of the interface reaction changes depending on the type of the high-K dielectric film, its reactivity, the degree of subsequent thermal annealing process, and the like. Thus, there can be a case a film having a thickness exceeding 0.4 nm may be required for suppressing the interface reaction. Of course, the overall process of the high-K dielectric gate insulation film should be designed so as to minimize the interface reaction, while the thickness of the
base oxide film 2 should be ideally set to 0.4 nm. In conclusion, it is preferable that the base oxide film has a thickness in the range of 2-4 atomic layers and more preferably in the range of 2-3 atomic layers. Most preferably, the base oxide film has a thickness of two atomic layers. -
FIG. 28A is a flowchart for forming an oxynitride film on a surface of a silicon substrate according to a second embodiment of the present invention conducted by thesubstrate processing apparatus 20 ofFIG. 3 , whileFIG. 28B is a flowchart showing the process of forming an oxynitride film according to a comparative example ofFIG. 28A . In the comparative example ofFIG. 28B , an oxide film is formed on a silicon substrate in thesubstrate processing apparatus 20 ofFIG. 3 and the substrate is once taken out into the atmospheric environment. Further, the substrate is returned to theprocessing vessel 21 of thesubstrate processing apparatus 20 and the oxynitride film is formed as a result of the RF-N2 processing of the oxide film. - Referring to the comparative example of
FIG. 28B at first, a silicon oxide film is formed on the surface of the substrate W in thestep 21 in thesubstrate processing apparatus 20 ofFIG. 3 while using the ultraviolet-excited oxygen radicals formed according to the UV-O2 processing step explained before. Next, the substrate W is moved out from theprocessing vessel 21 in the step ofFIG. 22 and the interior of theprocessing vessel 21 is evacuated to a high-degree vacuum state. Thereafter, the substrate W is returned to thesubstrate 21. Further, an RF-N2 processing using the RF-excited nitrogen radicals explained before is conducted in thestep 23 and the silicon oxide film is converted to a silicon oxynitride film. - In the process of
FIG. 28B , the interior of theprocessing vessel 21 is evacuated to a high-degree vacuum state in thestep 22, and thus, the problem of oxygen contamination during the RF-N2 processing in thestep 22 is minimized. Thereby, unwanted increase of the thickness of the oxynitride film by oxidation is minimized. - In the step of
FIG. 28A , on the other hand, the substrate W finished with the UV-O2 processing in astep 11, which corresponds to thestep 21, is held in theprocessing vessel 21 for increasing the throughput of substrate processing. Thus, after conducting a purging process in astep 12, astep 13 corresponding to thestep 23 is conducted and the silicon oxide film is converted to a silicon oxynitride film as a result of the RF-N2 processing 13, which corresponds to thestep 23 and uses the RF-excited nitrogen radicals. -
FIG. 29A shows the thickness of the oxynitride film formed by the process ofFIG. 28A as measured by the XPS analysis with the thickness of the oxynitride film formed by the process ofFIG. 28B , also obtained by the XPS measurement. InFIG. 29A , the horizontal axis shows the nitridation time in thestep 13 ofFIG. 28A or in thestep 23 ofFIG. 28B . InFIG. 28A , ▪ represents the process ofFIG. 28A while ♦ represents the process ofFIG. 28B . - Referring to
FIG. 29A , it can be seen that there is caused an increase of thickness of the oxynitride film with the progress of the nitridation process while no substantial difference can be recognized between the process ofFIG. 28A and the process ofFIG. 28B . This means that sufficient oxygen purge is achieved also in the process ofFIG. 28A . -
FIG. 29B shows the concentration of the nitrogen atoms thus incorporated into the oxynitride film, whereinFIG. 29B compares the process ofFIG. 28A and the process ofFIG. 28B . InFIG. 29B , the horizontal axis represents the nitriding time of thestep 13 ofFIG. 28A or thestep 23 ofFIG. 28B . InFIG. 29B , ▪ represents the process ofFIG. 28A while ♦ represents the process ofFIG. 28B . - Referring to
FIG. 28B , it can be seen that there is no substantial difference in the concentration of the nitrogen atoms incorporated into the oxynitride film between the process ofFIG. 28A and the process ofFIG. 28B , and thus, it is interpreted that the increase of the film thickness observed inFIG. 29A is caused as a result of the introduction of nitrogen into the oxynitride film. - Next, the inventor of the present invention has conducted an experiment of forming an oxide film by using the
substrate processing apparatus 20 ofFIG. 3 , wherein oxygen radicals are formed by using theremote plasma source 26 rather than the ultraviolet optical source 25 (this process will be referred to hereinafter as RF-O2 process). From the oxide film thus formed by the RF-O2 processing, an oxynitride film is formed by conducting an RF-N2 nitridation processing that uses the nitrogen radicals formed by theremote plasma source 26. - In the experiment of
FIG. 30A , an RF-O2 processing is conducted in a step 31 by supplying an Ar gas and an O2 gas to theremote plasma source 26, followed by a purging process in astep 32 in which theprocessing vessel 21 is purged to a high-degree vacuum state. Thereafter, theprocessing vessel 21 is purged four times by Ar, and an RF-N2 processing is conducted in astep 33 by using theremote plasma source 26. - In the experiment of
FIG. 30B , on the other hand, Ar and O2 are introduced to theremote plasma source 26 in astep 41 similarly to the step 31 and an RF-O2 processing is conducted. Thereafter, the substrate W is moved to the outside of theprocessing vessel 21 in astep 42. In this state, the processing vessel is evacuated to a high-degree vacuum state, and the substrate W is returned to theprocessing vessel 21 again. Further, an RF-N2 processing similar to the one in thestep 33 is conducted. -
FIG. 31A compares the thickness of the oxynitride film obtained by the XPS analysis for the oxynitride film formed by the process ofFIG. 30A with the thickness of the oxynitride film obtained by the XPS analysis for the oxynitride film formed by the process ofFIG. 30B . InFIG. 31A , it should be noted that ▪ corresponds to the process ofFIG. 30A while ♦ corresponds to the process ofFIG. 30B . - Referring to
FIG. 31A , it can be seen that there is caused a substantial increase of film thickness in the case the oxide film is formed on the substrate W by the RF-O2 processing that uses theremote plasma source 26 according to the process ofFIG. 30A . -
FIG. 31B shows the concentration level of the nitrogen atoms in the oxynitride film formed by the process ofFIG. 30A in comparison with the concentration of the nitrogen atoms in the oxynitride film formed by the process ofFIG. 30B , wherein ▪ ofFIG. 31B corresponds to the process ofFIG. 30A while ♦ corresponds to the process ofFIG. 30B . - Referring to
FIG. 31B , it is noted that the nitrogen concentration level in the oxynitride film formed by the process ofFIG. 30A is lower than the nitrogen concentration level of the oxynitride film formed by the process ofFIG. 30B . This indicates that the increase of the film thickness as observed inFIG. 31A for the case the process ofFIG. 30B is used is primarily caused by residual oxygen. It is believed that such residual oxygen exists in the remoteradical source 26 and the oxygen radicals promoting the oxidation of the oxynitride film are formed form such residual oxygen at the same time the nitrogen radicals are formed in thenitridation step 33 ofFIG. 30A . - From the situation noted above, it is concluded that it is preferable to form the initial oxide film by using the UV-O2 processing that uses the ultraviolet-excited oxygen radicals in the case the
substrate processing apparatus 20 ofFIG. 3 is used for forming an extremely thin oxide film on the substrate surface and forming an oxynitride film therefrom by causing nitridation of the oxide film by an RF-N2 processing as set forth in the flowchart ofFIG. 25 . -
FIG. 32 shows a flowchart of the process of forming an oxynitride film according to a third embodiment of the present invention, wherein those parts ofFIG. 32 explained before are designated by the same reference numerals and the description thereof will be omitted. - Referring to
FIG. 32 , the process of formation of the oxynitride film of the present embodiment is somewhat similar to the process explained previously with reference toFIG. 28A except that the number of the purges conducted in the purging step of theprocessing vessel 21 in thestep 12 by using an Ar gas is changed variously from 0 times to 4 times. Each purge is formed by the step of flowing an Ar gas in theprocessing vessel 21 and the step of evacuating the processing vessel to a high-degree vacuum state. -
FIG. 33A shows the relationship between the number of the Ar purges conducted in thestep 12 ofFIG. 32 and the thickness of the oxynitride film obtained in thestep 13, wherein the thickness of the oxynitride film shown inFIG. 33A is obtained by ellipsometry. - Referring to
FIG. 33A , it can be seen that the thickness of the oxynitride film is constant and takes a value of about 1.4 nm irrespective of the number of the Ar purges. -
FIG. 33B , on the other hand, shows the thickness of the oxynitride film obtained for the case the number of the Ar purges of thestep 32 is changed variously in the process ofFIG. 30A . - Referring to
FIG. 33B , it can be seen that the thickness of the oxynitride film is decreased slightly with the number of purges, indicating that the purging in thestep 32 is necessary for suppressing the increase of film thickness caused by oxidation of the oxynitride film. - The results of
FIGS. 33A and 33B indicate that it is not always necessary to conduct the purging in thestep 12 in the case the formation of the oxynitride film is conducted by the process ofFIG. 30A and that there occurs no substantial increase of thickness in the oxynitride film even when this step is omitted. - The result of
FIG. 24 explained before indicates that a thickness of about 0.8 nm is inevitable for an oxynitride film in the case the oxynitride film is formed by an RF-N2 nitridation processing of a UV-O2 film so as to have a nitrogen concentration level of 20%. When the thickness of the oxynitride film is to be reduced further, it is necessary to reduce the initial oxide thickness to 0.2 nm or 0.1 nm or even smaller, as long as the nitridation is started from an UV-O2 oxide film. - In the present embodiment, instead of forming the UV-O2 oxide film explained before, an NO gas is introduced in the
substrate processing apparatus 20 ofFIG. 3 from thegas nozzle 21D and excitation of atomic state oxygen and atomic state nitrogen is caused by conducting ultraviolet excitation of the NO gas thus introduced (such a processing will be referred to hereinafter as UV-NO processing). The oxynitride film thus obtained, or the UV-NO film, contains nitrogen already in the initial state. Thus by nitriding such an UV-NO film by way of the RF-N2 processing, it becomes possible to introduce nitrogen into the film with high concentration while simultaneously minimizing the film thickness. -
FIG. 34 shows the potential curve of an NO molecule for various excitation states (see for example J. S. Chang, et al., “atomic and molecular processes of ionized gas” Tokyo Denki University Press, 1982). - In the ultraviolet-induced optical transition of NO molecules, existence of absorption bands corresponding to the transition from the ground state to the excited states such as A2Σ+, B2Πr, C2Π, D2Σ+, E2Σ+ is known, wherein the transition takes place at the optical wavelengths shorter than the wavelengths of 227 nm, 218 nm, 192 nm, 188 nm and 165 nm, respectively.
- On the other hand,
FIG. 34 also shows the wavelength in which atomic state oxygen (O3P) and atomic state nitrogen (N4S0) can be excited that such a wavelength falls in the range between 192 nm and 145 nm. Thus, it is possible to form the atomic state oxygen and atomic state nitrogen by exciting an NO molecule with an optical wavelength longer than 145 nm. When the optical wavelength becomes shorter than 145 nm, on the other hand, there starts excitation of radical oxygen (O1D), and oxidation reaction is expected to be predominant at the time of the substrate processing. - In view of the situation noted above, it becomes possible to form the desired UV-NO film by using an ultraviolet radiation source having a wavelength in the range of 192-145 nm for the
ultraviolet source 25 in thesubstrate processing apparatus 20 ofFIG. 3 . -
FIG. 35 shows the outline of the substrate processing according to the present embodiment in which an RF-N2 processing is conducted subsequently to the UV-NO processing. - Referring to
FIG. 35 , the surface of a silicon substrate is nitrided in a step 51 by the foregoing UV-NO processing, and an oxynitride film is formed as a result. - Next, in the step 52, the oxynitride film thus formed is subjected to an RF-N2 processing, and an oxynitride film having a high nitrogen concentration is obtained.
- Table 3 below shows an example of the process condition for the steps 51 and 52, wherein Table 3 below also shows the process condition of the UV-O2 processing (
step 1 ofFIG. 25 ) in relation to the step 51.TABLE 3 Flow Rate Press Temp Time Gas [SCCM] [Torr] [° C.] [sec] step UV—O2 O2 300 0.02 500 15-300 1 step UV—NO NO 200 0.05 450 20-120 51 step RF—N2 Ar + N2 1600 0.09 500 15-60 52 - Further, Table 4 below shows the allowable process condition of the foregoing steps 51 and 52.
- Similarly to Table 3, Table 4 shows the allowable process condition for both the UV-O2 processing and the UV-NO processing.
TABLE 4 Flow Rate Press Temp Time Gas [SCCM] [Torr] [° C.] [sec] step UV—O2 O2 300-4000 0.02-5 300-750 15-600 1 step UV—NO NO 10-1000 0.01-5 300-750 15-600 51 step RF—N2 Ar + 500-2500 1 × 10−3-10 300-750 10-180 52 N2 - Tables 3 and 4 indicate that the UV-O2 processing can be conducted in the pressure range of 0.02-5 Torr (0.0266-665 Pa) and the temperature range of 300-750° C. and that the UV-NO processing can be conducted in the pressure range of 0.01-5 Torr (0.0133 Pa-1.33 kPa) and the temperature range of 300-750° C. Particularly, the range of 0.67 Pa -13.3 kPa is preferable.
- On the other hand, it is possible to conduct the RF-N2 processing in the pressure range of 10−3-10 Torr (0.133 Pa-1.33 kPa) and in the temperature range of 300-700° C. Particularly, the range of 0.67 Pa-13.3 kPa is preferable.
- Referring back to
FIG. 24 explained before, ▴ and ▾ show the relationship between the nitrogen concentration and film thickness of the oxynitride film formed according to the process ofFIG. 35 . - Referring to
FIG. 24 , it can be seen that the oxynitride film already contains nitrogen with a concentration of about 10% in the state immediately after formation thereof by the UV-NO process. Thus, by applying the RF-N2 processing of the step 52 ofFIG. 35 to such an oxynitride film, it becomes possible to form an oxynitride film of higher nitrogen concentration. Thereby, the date represented in the drawing by ▴ represents the case in which the oxynitride film has a thickness of 0.5 nm in the state immediately after the UV-NO processing, while ▾ represents the case in which the oxynitride film has a thickness of 0.4 nm in the state immediately after the UV-NO processing. In the case of the film represented by ▾, in particular, it can be seen that a nitrogen concentration of 20% can be achieved while maintaining the film thickness to 0.6 nm or less in terms of the thickness measured by the XPS analysis, by conducting the RF-N2 processing. -
FIG. 36 shows the binding energy of a nitrogen atom of the is state contained in the oxynitride film, which is obtained according to the process of the previous embodiment in which the UV-O2 processing and the RF-N2 processing are conducted consecutively. Further,FIG. 36 shows similar binding energy for the oxynitride film formed by conducting the UV-NO processing explained before and also for an oxynitride film formed by a different process. InFIG. 36 , it should be noted that the vertical axis represents the full-width half-maximum (FWHM) of the XPS spectrum while the horizontal axis represents the binding energy of the N1s atom. - Referring to
FIG. 36 , the oxynitride film having particularly large binding energy corresponds to the case shown inFIG. 37A in which the nearest neighboring sites of a nitrogen atom are occupied by Si atoms and the second neighboring sites of the nitrogen atom are occupied by oxygen, while the oxynitride film having a large binding energy corresponds to the case shown inFIG. 37B in which the nearest neighboring sites of a nitrogen atom are occupied by Si atoms and the second nearest neighboring sites of the nitrogen atom are also occupied by Si atoms. There exists a difference of binding energy of about 0.6 eV between these two configurations, while it is noted that that this difference of binding energy agrees with the distribution of the data points on the horizontal axis inFIG. 36 . - Referring to
FIG. 37A , the nitrogen atoms are included in the oxide film in this state, and thus, the state ofFIG. 37A corresponds to the state such as the one shown inFIG. 1 , in which the nitrogen atoms exist in the interior of the oxide film or near the surface of the oxide film. InFIG. 37B , on the other hand, it should be noted that the state in which the Si atoms in one or more sites circled in the drawing by a dotted line are substituted with oxygen as represented by arrows corresponds to the case in which the nitrogen atoms are concentrated to the region of the oxynitride film near the interface between the silicon substrate and the oxynitride film. - Referring to
FIG. 36 , it can be seen that the value of the binding energy scatters over a wide range from the relatively low energy side of about 397.6 eV to the higher energy side of about 398.1 eV in the case of the oxynitride film formed by the RF-N2 processing of the UV-O2 oxide film. From this, and further in view of the fact that the half height width of the peak takes a large value in the case of such an oxynitride film, it is concluded that the state ofFIG. 37A and the state ofFIG. 37B are mixed in the film. - In the oxynitride film in which only the UV-NO processing is conducted, on the other hand, the value of the binding energy is distributed in the low energy side from about 397.5 eV to about 397.9 eV. From this, and further in view of the fact that the half-height width of the peak is reduced in such a film, it is estimated that, while there still exists a mixing of the state of
FIG. 37A and the state ofFIG. 37B in the film, the state ofFIG. 37B is slightly superior. In such a case, it is believed that the distribution of the nitrogen atoms in the oxynitride film is slightly shifted in the direction close to the silicon substrate. -
FIG. 36 also shows the result for the case of an oxynitride film (RTO/RFN) in which a thermal oxide film is subjected to the RF-N2 processing, the case of an oxynitride film (SPA) in which a thermal oxide film is subjected to a microwave-plasma nitridation process, and for the case of an oxynitride film (RTNO) in which a silicon substrate is subjected to a thermal nitridation processing. - In the case of the oxynitride film designated as RTO/RFN and the oxynitride film designated as SPA, the binding energy observed for the N1s state is relatively large and is believed that the state of
FIG. 37A is predominant. In the case of the oxynitride film RTNO, on the other hand, the observed binding energy of the N1s state is concentrated into the value of about 397.4 eV. It is believed that this indicates that there is a concentration of nitrogen atoms in the oxynitride film near the interface between the oxynitride film and the silicon substrate. - Thus, according to the formation process of the oxynitride film of the present invention that applies the RF-N2 processing to the UV-O2 oxide film, it is possible to realize a generally uniform distribution of the nitrogen atoms in the oxynitride film, with slight concentration in the side of the film surface. In the case of conducting the RF-N2 processing to an existing oxide film, the nitrogen atoms are distributed primarily at the side of the film surface in view of the result of UVO2/RFN, RTO/RFN or SPA of
FIG. 36 . From this, it is expected that a generally uniform distribution of nitrogen atoms is achieved in the oxynitride film from the interface between the silicon substrate and the film to the film surface by applying the RF-N2 processing to the oxynitride film formed by the UV-NO processing as represented inFIG. 36 . - In the case of fabricating a semiconductor device having a high-K dielectric gate insulation film of
FIG. 1 , it is necessary to form the high-K dielectric film 3 on thebase oxide film 2 thus formed by thesubstrate processing apparatus 20. - Typically, a CVD process is used to form such a high-
K dielectric film 3. In the case of forming a ZrO2 film, for example, ZrCl4 or other gaseous source containing Zr is used and the ZrO2 film is deposited by oxidizing such a gaseous source. - As it is preferable that the formation of such a high-
K dielectric film 3 is conducted subsequent to the nitridation process of the radical oxide film shown inFIGS. 16A and 16B , without contacting the substrate to the external air. Thus, it is preferable that thesubstrate processing apparatus 20 ofFIG. 3 is integrated into a cluster-type substrate processing system that includes a CVD chamber. -
FIG. 38 shows the schematic construction of such a cluster-typesubstrate processing system 30 according to a fifth embodiment of the present invention. - Referring to
FIG. 38 , the cluster-typesubstrate processing system 30 includescassette modules substrate transfer chamber 32 connected to thecassette modules substrate transfer chamber 32 is further connected to asubstrate cleaning chamber 33, a basefilm formation chamber 34, aCVD chamber 35 and athermal processing chamber 36. - Thus, the substrate W introduced into the
substrate transfer chamber 32 from thecassette module substrate cleaning chamber 33 first for removing a native oxide film or organic contamination therefrom. Next, the substrate W is transported to the base oxidefilm formation chamber 34 via thesubstrate transfer chamber 32 and thebase oxide film 12 and thenitride film 12A are formed. - Thereafter, the substrate W is forwarded to the
CVD chamber 35 through thesubstrate transfer chamber 32 for formation of the high-K dielectric film 13. The substrate W is further forwarded t thethermal processing chamber 36 for crystallization and oxygen-defect compensation processing. After the processing in thethermal processing chamber 36, the substrate W is transported to thecassette module substrate transfer chamber 32. - Meanwhile, each of the processing chambers 33-36 is provided with various cooperating devices, and because of this, the processing chambers requires an area represented in
FIG. 38 by a broken line, in addition to the area of the chamber itself. Thereby, it should be noted that available space is substantially limited at the side of the processing chamber close to thesubstrate transfer chamber 32 because of the reduced separation to adjacent chambers. - Thus, when the
substrate processing apparatus 20 ofFIG. 3 is to be used in such a cluster-typesubstrate processing apparatus 30, theprocessing chamber 12 is connected to thesubstrate transfer chamber 32 in place of being connected to thesubstrate transfer unit 27, wherein there arises a problem in that the turbomolecular pump 23B, extending laterally to theprocessing chamber 21 at the side thereof close to thesubstrate transfer chamber 32, may cause an interference with the adjacent processing chamber. - In order to conduct fast depressurization of the
processing vessel 21, it is necessary that the turbomolecular pump 23B is provided close to theevacuation port 21A, while there exists no space available for this purpose because of the fact that various devices including the transportation robot are provided underneath thesubstrate transfer chamber 32. Further, there is no available space underneath theprocessing vessel 21 for the turbomolecular pump 23B because of the fact that various devices including the substraterotating mechanism 22C are provided underneath theprocessing vessel 21. -
FIGS. 39A and 39B are diagrams showing the construction of asubstrate processing apparatus 40 according to a fifth embodiment of the present invention respectively in a side view and a plan view, wherein those parts ofFIGS. 39A and 39B explained before are designated by the same reference numerals and the description thereof will be omitted. - Referring to
FIGS. 39A and 39B , thesubstrate processing apparatus 40 disposes the turbomolecular pump 23B at the outer side of thesubstrate processing vessel 21, in other word the side opposite to thesubstrate transfer unit 27 where there is an available space when thesubstrate processing apparatus 40 is used to construct the cluster type substrate processing system such as the one shown inFIG. 38 . With this, there is formed anevacuation port 21E in theprocessing vessel 21 at the outer side thereof, in other words at the side opposite to the substrate transfer chamber. Further, theprocess gas nozzle 21D and the ultravioletoptical source 25 are provided to the side close to thesubstrate transfer chamber 27 with respect to the substrate W such that the oxygen radicals are caused to flow along the surface of the substrate W to theevacuation port 21E. - It should be noted that the turbo
molecular pump 23B is connected to the bottom part of theprocessing vessel 21 via thevalve 23A in a vertical state, in other words the state in which the inlet and the outlet are aligned vertically. Further, it should be noted that the outlet port of the turbomolecular pump 23B is connected to the evacuation line extending from theevacuation port 21A of theprocessing vessel 21 to thepump 24 via thevalve 24A at the part behind thevalve 24A. - In such a
substrate processing apparatus 40, in which the turbomolecular pump 23B is located at the side opposite to the side of thesubstrate transfer unit 27, there is caused no problem of the turbomolecular pump 23B causing interference with the adjacent processing chamber even when thesubstrate processing apparatus 40 is used to construct the cluster type substrate processing system as in the case ofFIG. 38 . -
FIGS. 40A and 40B are diagrams showing the process of forming thebase oxide film 12 conducted by using thesubstrate processing apparatus 40. - Referring to
FIGS. 40A and 40B , it can be seen that thevalves valve 24A is closed in the base oxide film formation process. As a result, theprocess space 23B is evacuated to the high-degree vacuum state of 1.33×10 −1-1.33×10−4 Pa (10−3-10−6 Torr) by the turbomolecular pump 23B ate the foregoingevacuation port 21E, and the oxygen gas is introduced into theprocess space 21B from theprocess gas nozzle 21D in this state. Further, by driving theultraviolet source 25 with a suitable energy while rotating the substrate W by the substraterotating mechanism 22C, there is caused a flow of oxygen radicals to the evacuation port 12E along the substrate surface, and the substrate surface is oxidized uniformly. With this, it becomes possible to form an extremely thin silicon oxide film having a thickness of 1 nm or less, particularly the thickness of about 0.4 nm corresponding to the film thickness of 2-3 atomic layers, on the silicon substrate surface uniformly and stably and with excellent reproducibility. Of course, it is possible to form a silicon oxide film having a thickness exceeding 1 nm. -
FIGS. 41A and 41B show the process of forming theoxynitride film 2A by using thesubstrate processing apparatus 40 of the present embodiment after the step ofFIGS. 40A and 40B by nitriding the surface of thebase oxide film 2 thus formed. - Referring to
FIGS. 41A and 41B , thevalve valve 24A is opened in the nitridation process. With this, the turbomolecular pump 23B is disconnected from the evacuation system and theprocess space 21B is evacuated directly by thepump 24 to the pressure of 1.33 Pa-13.3 kPa (0.01-100 Torr). - In this state, an Ar gas and a nitrogen gas are supplied to the
remove plasma source 26, and nitrogen radicals are formed by applying a high-frequency excitation to the nitrogen gas. The nitrogen radicals thus formed are caused to flow along the surface of the substrate W to theevacuation port 21A, and there is caused a uniform nitridation on the surface of the rotating substrate W. As a result of such a nitridation process the surface of thebase oxide film 2 is converted to theoxynitride film 2A. - By using the
substrate processing apparatus 40 of the present embodiment for theprocessing chamber 34 in the cluster type substrate processing system ofFIG. 38 , it becomes possible to form the high-K dielectric film 13 such as ZrO2, HfO2, Ta2O5, ZrSiO4, HfSiO4, Al2O3, and the like, on thebase oxide film 2 that includes therein theoxynitride film 2A. - In the explanation above, the
substrate processing apparatus 40 was explained with regard to the formation of very thin base oxide film. However, the present invention is not limited to such a specific embodiment and the present invention can be applied to the process of forming a high-quality oxide film, nitride film or oxynitride film on a silicon substrate or a silicon layer with a desired thickness. - In the embodiments above, the technology of forming the
base oxide film 2 in thesemiconductor device 100 ofFIG. 1 to the thickness of about 0.4 nm and further forming theoxynitride film 2A on the surface thereof by using thesubstrate processing apparatus 20 ofFIG. 3 . On the other hand, it is also possible to use thesubstrate processing apparatus 20 to form a thicker oxynitride film, which can be used for agate insulation film 3A as represented in asemiconductor device 200 ofFIG. 42 . - Referring to
FIG. 42 , thesemiconductor device 200 does not use the high-K dielectricgate insulation film 3 and thegate electrode 4 is formed directly on thegate insulation film 3A. InFIG. 42 , it should be noted that those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted. - In the
semiconductor device 200 ofFIG. 42 , it is not necessary to use the high-K dielectric film 3, and the gate insulation film can be formed by an oxynitride film which has been handled in the conventional semiconductor process technology. Thereby, the process of fabricating the semiconductor device is facilitated. On the other hand, it is necessary, in thesemiconductor device 200 ofFIG. 42 , to form thegate insulation film 3A, formed of an oxynitride film, to have a thickness of about 1.0 nm or more by using thesubstrate processing apparatus 20 explained with reference toFIG. 3 . -
FIG. 43 shows the process of forming such a thick oxynitride film according to the present embodiment. - Referring to
FIG. 43 , an oxide film is formed by the UV-O2 processing of the silicon substrate surface in the step 61 by the ultraviolet-excited oxygen radicals, and the oxide film thus formed is nitrided in the step 62 by the RF-N2 processing. In the present invention, on the other hand, the desired film thickness is achieved by conducting the processes in the steps 61 and 62 at a relatively high temperature of about 750° C. In view of the result of the experiment ofFIG. 32 , the purging step between the step 61 and the step 62 is omitted. -
FIG. 44 shows the thickness distribution over the silicon substrate surface for the oxide film obtained by the UV-O2 processing in the step 61. It should be noted that the thickness ofFIG. 44 is measured by using spectral ellipsometry. - Referring to
FIG. 44 , the silicon oxide film is formed under the pressure of 400 Pa (3 Torr) at the substrate temperature of 750° C. while rotating the substrate. It can be seen that a very uniform oxide film characterized by the variance a of 0.72% for the film thickness variation, is obtained. -
FIGS. 45A-45C are diagrams showing the process condition of the remote plasma nitridation processing of the oxide film ofFIG. 44 conducted in the step 62 ofFIG. 43 and the film thickness distribution of the obtained oxynitride film obtained according to the processing. - Referring to
FIG. 45A , the plasma nitridation processing is conducted under the pressure of 26.6 kPa (200 mTorr) at the substrate temperature of 750° C. while changing the nitrogen gas flow rate and the Ar gas flow rate in the range illustrated. InFIG. 45A , the line A represents the upper limit of the nitrogen gas flow rate in which ignition of plasma can take place, while the lines B and C represent the pressure range capable of being controlled by using thesubstrate processing apparatus 20 ofFIG. 3 . - As represented at the center drawing of
FIG. 45B , the distribution of the nitrogen concentration in the film, and hence the distribution of thickness of the oxynitride film, is uniform in the case the Ar gas flow rate and the nitrogen gas flow rate are chosen to be located on the line D. In this case, a very small variance value σ of 0.7% is achieved. - In the case the Ar gas flow rate and the nitrogen gas flow rate are chosen to be located at the position offset from the foregoing line D, on the other hand, there arises a distribution in which the nitrogen concentration increases at the marginal part of the substrate as represented in the left drawing of
FIG. 45B or a distribution in which the nitrogen concentration increases at the central part of the substrate as represented in the right drawing ofFIG. 45B . In these cases, it can be seen that there occurs increase of the variance σ for the film thickness distribution. - Thus, it can be seen that there appears a convex thickness distribution or a concave thickness distribution in the oxynitride film thickness, and hence a convex nitrogen concentration and a concave nitrogen concentration, in the case the process condition is at the right side of the line D and at the left side of the line D, respectively, while in the case the nitrogen gas flow rate and the Ar gas flow rate are chosen on the line D, a uniform thickness distribution is obtained for the oxynitride film.
-
FIG. 73 shows the relationship between the uniformity of the RF-N2 processing and the process pressure at the substrate temperature of 750° C., wherein the horizontal axis ofFIG. 73 shows the process pressure at the time of the RF-N2 processing, while the vertical axis represents the ratio in which the thickness of the oxynitride film thus subjected to the nitridation processing at the central part is divided by the thickness at the marginal part. Thus, inFIG. 73 , an ideal in-plane uniformity is achieved in the case the vertical axis ofFIG. 73 is 1. When the vertical axis has increased from 1, this means that the obtained oxynitride film has a convex film thickness distribution. In the case the vertical axis is smaller than 1, this means that the oxynitride film has a concave film thickness distribution. - In
FIG. 73 , ▴ represents the case the Ar gas flow rate is set to 800 SCCM and the nitrogen gas flow rate is set to 115 SCCM, while ▪ represents the case the nitrogen gas flow rate is set to 1150 SCCM. Further, ♦ represents the case in which the Ar gas flow rate is set to 1600 SCCM and the nitrogen gas flow rate is set to 1400 SCCM. Thus, it will be noted that the total flow rate of the process gas, defined as the sum of the Ar gas flow rate and the nitrogen gas flow rate, increases in the order of ▴, ▪ and ♦. - Referring to
FIG. 73 , it can be seen that the film thickness distribution changes from the concave distribution to the convex distribution and again to the concave distribution at the low pressure side when the pressure is changed under the condition that the total flow rate is fixed. Further, it will be noted that there exists two process pressures in each setting of the total flow rate in which an oxynitride film of uniform thickness is obtained. Further, it will be noted that the curves ofFIG. 73 shifts in the higher pressure side when the total flow rate is increased. Thus, it will be noted that adjustment of the process pressure can also realize the uniform processing in the RF-N2 processing of the present invention, in addition to the approach of controlling the total flow rate of the Ar gas and the nitrogen gas. - It should be noted that the line D of
FIG. 45A explained before corresponds to the point ▴ ofFIG. 73 . The relationship ofFIG. 73 also suggests the existence of another optimum point. This point, however, does not exist in practice because of the too low pressure needed. When this optimum point is to be used, therefore, it is necessary to use a pump of large power capable of handling a large evacuation load. -
FIG. 45C shows the relationship between the Ar gas flow rate and the thickness of the obtained oxynitride film for the case the Ar gas flow rate and the nitrogen gas flow rate are controlled on the line D ofFIG. 45A . InFIG. 45C , too, the thickness is measured by spectral ellipsometry. - Referring to
FIG. 45C , there can be seen an increase of thickness of the oxynitride film with increasing Ar gas flow rate, and hence with increasing nitrogen gas flow rate. This indicates that the thickness of the oxynitride film shown inFIG. 45A or 45B indeed reflects the nitrogen concentration in the film. -
FIGS. 46A-46D show the kinetics of the nitridation process conducted by the RF-N2 processing of the oxide film ofFIG. 44 at the temperature of 750° C. under the pressure of 200 mTorr, wherein it should be noted thatFIG. 46A represents the relationship between the thickness of the oxynitride film obtained by the XPS analysis and the time of the nitridation processing,FIG. 46B represents the relationship between the concentration of the nitrogen atoms incorporated into the oxynitride film and the time of the nitridation processing,FIG. 46C represents the relationship between the area of the O1s signal peak of the oxynitride film obtained by the XPS analysis and the time of the nitridation processing, andFIG. 46D represents the relationship between the peak area of the Si2p signal and the time of the nitridation processing, for the case the initial thickness of the oxide film is set to 1.0 nm, 1.2 nm and 1.3 nm in terms of the thickness value as measured by a monochrome ellipsometer. In the XPS analysis, the thickness values of about 0.8 nm, 1.0 nm and 1.3 nm are obtained respectively in correspondence to the foregoing thickness values. - Referring to
FIGS. 46A-46D , it can be seen that there occurs an increase of thickness and nitrogen concentration in the oxynitride film with the time of the nitridation processing irrespective of the initial thickness, while it can be seen also that there exists a change between the behavior of the O1s signal and the behavior of the Si2p signal with respect to the time of the nitridation processing, depending on the initial thickness of the oxide film. - More specifically, it can be seen that the O1s signal decreases with the nitridation time in the case of the RF-N2 processing of an oxide film having the initial thickness of 1.3 nm, indicating that there is caused dissociation of oxygen during the nitridation processing. In the case of the RF-N2 processing of the oxide film having the initial thickness of 1.0 nm, on the other hand, no substantial change is observed for the O1s signal. This indicates that the oxygen atoms dissociated as a result of introduction of the nitrogen atoms cause diffusion through the thin oxide film having the initial thickness of 1.0 nm and has caused precipitation at the interface to the silicon substrate. Thereby, there is caused a regrowth of an oxide film at such an interface.
- In the case of the RF-N2 processing of the oxide film having the initial thickness of 1.3 nm, on the other hand, it is believed that the dissociated oxygen atoms cannot reach the interface between the silicon substrate and the oxide film because of the large initial thickness of the oxide film and are escaping to the outside of the oxynitride film.
- With regard to the Si2p signal of
FIG. 46D , it can be seen that the Si2p signal does not change much in the case of the oxide film having the initial thickness of 1.3 nm until the duration of 30 seconds has elapsed after the start of the nitridation processing. It is believed that this reflects the situation that the nitrogen atoms introduced into the oxide film cause substitution of the oxygen atoms in the film and the nitrogen atoms to not reach the interface between the oxide film and the silicon substrate. On the other hand, in the case of the oxide film having the initial thickness of 1.0 nm, there is caused an increase of the Si2p signal with the start of the nitridation processing, indicating that there has been caused precipitation of oxygen at the interface between the silicon substrate and the oxide film and associated regrowth of the oxide film. -
FIGS. 47A-47D show the case in which the RF-N2 processing of oxide film is conducted according to the process ofFIG. 43 under the condition that nitridation reaction is facilitated while sacrificing the uniformity. More specifically, the process pressure is set to 400 mTorr in the experiments ofFIGS. 47A-47D . In order to achieve the promotion of the nitridation reaction and uniformity at the same time, on the other hand, it is necessary to use a large capacity pump capable of handling a larger evacuation load is used for thepump 24. Further, a more powerful radical source should be used for the remoteradical source 26. This is essentially the same thing explained previous with regard to the case of controlling the process pressure. - Referring to
FIGS. 47A-47D , it can be seen that the O1s signal strength decreases with the start of the RF-N2 processing even in the case of the thin oxide film having the initial thickness of 1.0 nm under the condition in which the process pressure is increased for facilitating the nitridation reaction. Further, as shown inFIG. 47D , it can be seen that the signal strength of the Si2p signal increases monotonously from the beginning of the nitridation process in the case of the oxide film having the initial thickness of 1.3 nm. This indicates that, in the experiments ofFIGS. 47A-47D , nitrogen is introduced with an amount corresponding to the nitrogen concentration in the case of the experiments ofFIGS. 44A-44D with short time period because of the promoted nitridation reaction and that the nitrogen atoms have reached the interface between the oxide film and the silicon substrate. Thus, when the nitridation processing is conducted under the condition in which the nitridation processing is facilitated, there is a possibility that, while it is certainly possible to reduce the time needed for the nitridation processing, the introduced nitrogen atoms may reach the foregoing interface unless the nitridation time is controlled optimum. -
FIG. 48A shows the mechanism of the nitridation processing achieved by the RF-N2 processing of an oxide film estimated from the results ofFIGS. 46A-46D and 47A-47D. InFIG. 48A , it should be noted that those parts corresponding to the parts described previously are designated by the same reference numerals and the description thereof will be omitted. - Referring to
FIG. 48A , it can be seen that the introduced nitrogen atoms are concentrated to the surface part of the oxide film by controlling the condition of the RF-N2 processing is appropriately, and that the problem of formation of surface states by the nitrogen atoms penetrating to the interface part of thesilicon substrate 1 and theoxynitride film 3 is suppressed. See Watanabe, K., et al., J. Appl. Phys. 90, pp.4701, 2001. - In the case the condition of such an RF-N2 processing is inappropriate, on the other hand, there is a possibility that the nitridation reaction proceeds excessively. In such a case, the nitrogen atoms may reach the interface between the
silicon substrate 1 and theoxynitride film 3A and interface states may be caused. Because of this, it is preferable that the process of the step 62 ofFIG. 43 is finished within 30 seconds. - Thus, in the present embodiment, the number of rotation of the substrate W per minute is set to 20 in the
substrate processing apparatus 20 ofFIG. 3 , and thus, the substrate W is rotated about 10 times during the RF-N2 processing continued for 30 seconds. -
FIGS. 49A and 49B show the depth profile of Si, N and O atoms respectively at the central part (C), intermediate part (M) and marginal part (E) obtained by a SIMS analysis for the case a UV-O2 oxide film having the initial thickness of 1 nm is nitrided for 30 minutes while rotating the substrate, wherein it should be noted thatFIG. 49B shows the surface part of the oxynitride film ofFIG. 49A in an enlarged scale. - Referring to
FIGS. 49A and 49B , it can be seen that the peak of the nitrogen concentration is located at the depth of about 0.5 nm from the surface of theoxynitride film 13A and that excellent in-plane uniformity is achieved. Concentration of nitrogen atoms at the interface between thesilicon substrate 1 and theoxynitride film 3A is not recognized. -
FIGS. 50A and 50B show the depth profile of Si, N and O atoms in the case a UV-O2 film having the initial thickness of 1.3 nm is subjected to the nitridation processing conducted by the RF-N2 processing. - In this case, too, a result similar to the case of
FIGS. 49A and 49B is obtained. -
FIG. 51 shows the construction of asubstrate processing apparatus 320 according to a seventh embodiment of the present invention. - Referring to
FIG. 51 , thesubstrate processing apparatus 320 includes aprocessing vessel 321 accommodating therein astage 321A for holding asubstrate 322 to be processed, wherein theprocessing vessel 321 is provided with ashowerhead 321B formed of a material transparent to ultraviolet radiation such as quartz such that theshowerhead 321B faces thesubstrate 322 held on thestage 321A. Theprocessing vessel 321 is evacuated from theevacuation port 321C and an oxidizing gas such as oxygen is supplied to the showerhead 321B form an external gas source. - It should be noted that the
processing vessel 321 is further provided with anoptical window 321D of a material transparent to the ultraviolet radiation such as quartz above theshowerhead 321B such that theshowerhead 321B and thesubstrate 322 underneath theshowerhead 321B are exposed by theoptical window 321D. In thestage 321A, there is provided aheater 321 a heating thesubstrate 322. - On the
processing vessel 321, there is provided aultraviolet exposure apparatus 324 via acoupling part 323 provided in correspondence to theoptical window 321D. - It should be noted that the
ultraviolet exposure apparatus 324 includes a quartz optical window 324A corresponding to theoptical window 321D and aultraviolet source 324B that radiates thesubstrate 322 with the ultraviolet radiation via the quartz optical window 324A and theoptical window 321D, wherein theultraviolet source 324B is held by arobot 324C so as to be movable in the direction parallel to the optical window 324A as represented by an arrow inFIG. 51 . In the illustrated example, theultraviolet source 324B is formed of a linear optical source extending perpendicularly to the moving direction. For example, an excimer lamp having the wavelength of 172 nm may be used for the linear optical source. - In the construction of
FIG. 51 , theconnection part 323 is supplied with an inert gas such as N2 from an external gas source (not shown) via aline 323A so as to avoid absorption of the ultraviolet radiation produced by theultraviolet radiation source 324B by oxygen in the air before the ultraviolet radiation being introduced into theprocessing vessel 321 through theoptical window 321D. The inert gas thus introduced flows into aspace 324D inside theultraviolet exposure apparatus 324 through a gap formed in the mounting part of the optical window 324A of theultraviolet exposure apparatus 324. - In order to suppress the mixing of oxygen in the air to the region right underneath the
ultraviolet source 324B with the driving of the ultraviolet source, there are provided blockingplates 324F at both lateral sides of theultraviolet source 324B, and the inert gas such as nitrogen is introduced into a narrow gap region having a gap width of about 1 mm or less formed between the optical window 324A facing theultraviolet source 324B via a pair oflines 324 b. In this region, the inert gas from theline 323A is also supplied, and as a result, oxygen that causes absorption of the ultraviolet radiation is effectively purged from this gap region. - The inert gas passed through the blocking
plates 324F are flooded into thespace 324D and are evacuated to the outside via anevacuation port 324E formed in theultraviolet exposure apparatus 324. - In the substrate processing apparatus of
FIG. 51 , it is possible to control the movement or scanning of theultraviolet source 324B in theultraviolet exposure apparatus 324 by therobot 324C, and as a result, it becomes possible to control the distribution of film thickness by controlling the ultraviolet radiation dose at the time of forming an oxide film on the surface of thesubstrate 322 by a UV-O2 process. It should be noted that acontroller 325 such as a computer is used to control therobot 324C. Further, thecontroller 325 also controls the driving of theultraviolet source 324B. -
FIGS. 52A-52C are diagrams showing the thickness of an oxide film formed on a silicon substrate by thesubstrate processing apparatus 320 ofFIG. 51 under various conditions, whereinFIGS. 52A-52C show the thickness obtained by ellipsometry in terms of A. In the experiments ofFIGS. 52A-52C , a silicon substrate having an eight-inch diameter is used for thesubstrate 322 in the state that a native oxide film on the substrate surface is removed by a surface preparation process to be explained later. In each of the experiments ofFIGS. 52A-52C , the internal pressure inside theprocessing vessel 321 is set to about 0.7 kPa (5 Torr) and the substrate temperature is set to 300° C. - It should be noted that the illustrated result is for the case in which an oxygen gas is supplied to the
processing vessel 321 for 5 minutes with the flow rate of 1 SLM, andFIG. 51A shows the case in which no ultraviolet radiation is made, whileFIGS. 51B and 51C show the cases in which the ultraviolet radiation is made by theultraviolet source 324B such that the luminance flux density becomes 30 mW/cm2 right underneath the optical source.FIG. 52B shows the case in which the foregoingultraviolet source 324B is caused to scan uniformly within the range of 410 mm such that the entire surface of thesubstrate 322 uniformly. - Referring to
FIG. 52A , the oxide film formed on the silicon substrate has a thickness of about 0.2-0.3 nm in the case no ultraviolet radiation is made, and thus, there is caused no substantial film formation. In the case ofFIG. 52B , on the other hand, it can be seen that there is formed an oxide film with the thickness of about 0.8 nm on the surface of the silicon substrate. In the case ofFIG. 52B , it is also noted that there is caused a decrease of oxide film thickness at the central part of the 8-inch silicon substrate 322 in spite of the fact that the scanning of theultraviolet source 400 is conducted uniformly over the range of 400 mm. As a result, the thickness variation of the oxide film thus formed on the silicon substrate has a relatively large value of 2.72% in terms of variance. It is believed that this reflects the specific peculiarity of the substrate processing apparatus that has been used for the experiments. -
FIG. 52C shows, on the other hand, the thickness distribution of the oxide film for the case theultraviolet source 324B is caused to scan over the central part of thesilicon substrate 322 with a limited stroke range of 100 mm. - Referring to
FIG. 52C , it can be seen that the thickness of the oxide film thus formed falls in the range of 0.92-0.93 nm and that the film thickness variation is reduced to 1.35% in terms of variance. -
FIG. 53 shows the relationship between the ultraviolet exposure time and the thickness of the oxide film formed as a result in the experiments ofFIGS. 52A-52C for the case the flow rate of the oxygen gas introduced into theprocessing vessel 321 is changed variously. - As can be seen from
FIG. 53 , the thickness of the oxide film formed as a result of the processing does not depend on the oxygen flow rate substantially and that there appears saturation at the value of about 1 nm when a time of 1 minute has elapsed. When the exposure time is shorter than 1 minute, the film thickness increases with the exposure time. The result ofFIG. 53 shows that a very short time processing is sufficient for forming a thin oxide film to be used as the base oxide film on the silicon substrate surface by using thesubstrate processing apparatus 320 ofFIG. 51 . -
FIGS. 54A-54E are diagrams showing the film thickness distribution of an oxide film obtained for the case the inner pressure of the processing vessel is set to about 0.7 kPa (5 Torr) and the substrate temperature is set to 450° C. in thesubstrate processing apparatus 320 ofFIG. 51 while supplying an oxygen gas with a flow rate of 1 SLM and causing a scanning of theultraviolet source 24B within the range of 100 mm. In the drawings, the thickness of the oxide film is represented in terms of angstroms. Further, the silicon substrate is represented by a rectangle for the sake of simplicity. -
FIG. 54A shows the case in which the scanning is made within the range of ±50 mm with respect to the center of the substrate, wherein it can be seen that there is a tendency of the oxide film thickness increasing from the center of the substrate toward upward direction along the y axis and toward the rightward direction along the x axis. In this case, the variation of the oxide film thickness is 3.73% in terms of variance. -
FIG. 54B , on the other hand, shows the thickness distribution of the same oxide film represented in terms of angstroms for the case the origin of the scanning is displaced in the downward direction from the center of the substrate along the y axis with the distance of 12.5 mm. As can be seen fromFIG. 54B , the film thickness variation has been reduced to 3.07% in terms of variance. -
FIG. 54C , on the other hand, shows the distribution of the oxide film thickness represented in terms of angstroms for the case the origin of the scanning is displaced from the center of the substrate in the downward direction along the y axis by the distance of 25.0 mm. As can be seen fromFIG. 54C , the variation of thickness of the oxide film is 3.07%. in terms of variance similarly to the case ofFIG. 54B . - Further,
FIG. 54D shows the distribution of the oxide film thickness represented in terms of angstroms for the case the origin of the scanning is displaced in the downward direction along the y axis from the center of the substrate by the distance of 37.5 mm. In this case, the film thickness variation of the oxide film is reduced to 2.70% in terms of variance. - In the case the origin of scanning is displaced from the center of the substrate in the downward direction along the y-axis by the distance of 50.0 mm as shown in
FIG. 54E , the variation of the oxide film thickness is increased to 5.08% in terms of variance. - From this, it is concluded that the film thickness variation of the oxide film formed on the substrate 3222 can be minimized also by optimizing the origin of scanning of the
ultraviolet source 324B with respect to the substrate in thesubstrate processing apparatus 320 ofFIG. 51 . -
FIGS. 55A-55E show the distribution of the film thickness of an oxide film formed in thesubstrate processing apparatus 320 ofFIG. 51 for the case of setting the scanning distance of theultraviolet source 324B to 100 mm and setting the origin of the scanning at the location offset from the center of thesubstrate 322 in the downward direction along the y axis with the distance of 37.5 mm and by changing the luminance flux density to 3 mW/cm2, 6 mW/cm2, 12 mW/cm2, 18 mW/cm2 and 24 mW/cm2, respectively. - Referring to
FIGS. 55A-55E , it can be seen that the variation of the film thickness is minimum in the case the luminance flux density is set to 3 W/cm2 and that the variation of the oxide film thickness increases with increasing amount of the luminance flux density. - The result of
FIGS. 55A-55E shows that the thickness variation of the oxide film can be minimized also by optimizing the luminance flux density of theultraviolet source 324B. -
FIGS. 56A and 56B show comparative examples in whichFIG. 56A shows the case of forming an oxide film under the condition identical with those ofFIGS. 55A-55E except that no ultraviolet irradiation is made, whileFIG. 56B shows the case of forming an oxide film by a conventional rapid thermal oxidation (RTO) process. In any of these cases, a film thickness variation exceeding 4% is observed. -
FIGS. 57 and 58 show a flowchart of seeking the optimum condition of substrate processing conducted in thesubstrate processing apparatus 320 ofFIG. 51 in view of the foregoing results, whereinFIG. 57 represents the flowchart for seeking the optimum scanning region whileFIG. 58 represents the flow chart for seeking the optimum luminance flux density. - Referring to
FIG. 57 , an arbitrary region on the substrate is specified in the step 71 and thesubstrate 322 is introduced into thesubstrate processing apparatus 320 in the step 72 and theultraviolet radiation source 324B is caused to scan the specified region of thesubstrate 322. Thereby, an oxide film is formed. Further, by repeating the steps 71 and 72, an oxide film is formed on anew substrate 322 in each cycle in the state that the foregoing region is displaced. - Next, in the step 73, the thickness distribution is obtained for the oxide films obtained in the experiments and the region that minimizes the thickness distribution becomes minimum is determined in the step 74.
- After the search of the optimum scanning condition of
FIG. 57 , the search of the optimum illumination condition shown inFIG. 58 is conducted. - Referring to
FIG. 58 , the optimum scanning region determined by the procedure ofFIG. 57 is specified in the step 81 and the driving energy of the ultraviolet source 224B is specified in the step 82. Next, in the step 83, thesubstrate 322 is introduced into thesubstrate processing apparatus 320 and theultraviolet source 324B is caused to scan over the specified optimum region of thesubstrate 322 while being driven with the driving energy specified in the step 312. Further, by repeating the steps 312 and 313, an oxide film is formed on anew substrate 322 in each cycle in the state that the foregoing driving energy is changed. - Further, in the step 314, the thickness distribution of the oxide film obtained in each experiment is evaluated and the optimum driving energy of the
ultraviolet source 324B that minimizes the film thickness variation is determined. Further, in the step 315, the program for controlling theultraviolet source 324B of thesubstrate processing apparatus 320 is determined such that the film formation is conducted at such an optimized energy. - Thus, the
controller 325 controls therobot 324C and theultraviolet source 324B, and as a result, theultraviolet source 324B scans the optimum region of the substrate with optimum energy, and it becomes possible to form an extremely thin and uniform radical oxide film on thesubstrate 324 with the thickness of 0.3-1.5 nm, preferably 1 nm or less, more preferably 0.8 nm or less, and most preferably with the thickness of 0.4 nm. - Similarly to the case explained before, there appears a slowdown of oxide film growth at the thickness of 0.4 nm or 2-3 atomic layers in the case an oxide film is formed on a silicon substrate according to such a UV-O2 processing by using the
substrate processing apparatus 320 ofFIG. 51 . Thus, the oxide film of this thickness can be formed stably and with excellent reproducibility. By combining the oxide film thus formed with a high-K dielectric film, it becomes possible to realize an extremely fine high-speed MOS transistor having a reduced effective thickness for the gate insulation film. - In the present embodiment, explanation has been made for the case the oxide film is the one formed by the UV-O2 processing. However, the oxide film is not limited to such a film but may be any oxide film as long as it is formed with precision oxidation process conducted under a low radical density.
-
FIG. 59 shows the construction of aMOS transistor 340 according to an eighth embodiment of the present invention. - Referring to
FIG. 59 , abase oxide film 342 of a silicon oxide film having a thickness of 2-3 atomic layers is formed on asilicon substrate 341, and a so-called high-K dielectric film 343 such as ZrO2, HfO2, Ta2O5, Al2O3, ZrSiO4 or HfSiO4 is formed on thebase oxide film 342. Further, agate electrode 344 of polysilicon or a metal is formed on the high-K dielectric film 343. Further, while the illustration is omitted, diffusion regions are formed in thesilicon substrate 341 at both lateral sides of thegate electrode 344. -
FIG. 60 shows the construction of a cluster-typesubstrate processing system 350 used for fabricating the MOS transistor ofFIG. 59 . - Referring to
FIG. 60 , thesubstrate processing system 350 is an apparatus configured to form a cluster system and includes aload lock chamber 351 for loading and unloading a substrate, apreprocessing chamber 352 used for removing native oxide film and carbon contamination from the substrate surface, a UV-O2 processing chamber 353 formed of thesubstrate processing apparatus 320 ofFIG. 51 , aCVD processing chamber 354 for depositing a high-K dielectric film such as Ta2O5, Al2O3, ZrO2, ZrSiO4, HfSiO4, and the like on a substrate, and acooling chamber 355 cooling the substrate in the state that the chambers 351-355 are connected to avacuum transfer chamber 356, wherein thevacuum transfer chamber 356 is provided with a transfer arm (not shown). - In operation, the substrate introduced into the load/
lock chamber 351 is transported to thepreprocessing chamber 352 along a path (1) and native oxide film or carbon contamination is removed therefrom. Next, the substrate thus processed in thepreprocessing chamber 352 is transported to the UV-O2 processing chamber 353 along a path (2) and thebase oxide film 342 ofFIG. 59 is formed by thesubstrate processing apparatus 320 ofFIG. 51 with a uniform thickness of 2-3 atomic layers. - The substrate thus formed with the base oxide film in the UV-O2 processing chamber 353 is then introduced into the
CVD processing chamber 354 along a path (3) and the high-K dielectricgate insulation film 344 shown inFIG. 59 is formed on the base oxide film. - The substrate is then transported from the
CVD chamber 344 to thecooling chamber 355 along a path (4) for cooling, and is then returned to theload lock chamber 351 for transportation to the outside. - In the
substrate processing system 350 ofFIG. 60 , it is also possible to provide a preprocessing chamber for conducting a planarization processing in an Ar atmosphere by way of high temperature annealing process. -
FIG. 61 is a diagram explaining the radical oxidation processing conducted in the UV-O2 processing chamber 53. -
FIG. 61 shows the condition of the radical oxidation processing conducted in the UV-O2 processing chamber 53. - Referring to
FIG. 61 , the horizontal axis shows a logarithmic representation of the partial pressure of the oxygen radicals excited in theprocessing vessel 321 ofFIG. 51 by theultraviolet source 324B in terms of Torr. Further, the vertical axis represents the process time until the slowdown phenomenon shown inFIG. 8 appears after the start of the processing and also the process time until such a slowdown phenomenon vanishes, in terms of logarithmic scale. It should be noted that the oxygen partial pressure on the horizontal axis corresponds to the oxygen radical density and is determined by the driving power or ultraviolet radiation power of theultraviolet source 324B and the ultraviolet wavelength. - Hereinafter, the relationship between the ultraviolet radiation power and the radical density will be explained for the case of using the wavelength of 172 nm.
- In the
substrate processing apparatus 320 ofFIG. 51 , and thus in theprocessing chamber 353 of thesubstrate processing system 350 ofFIG. 60 , theultraviolet source 324B produces a photon flux of 4.34×1016/cm2·sec in the case a ultraviolet source producing the ultraviolet radiation power of 50 mW/cm2 at the location right underneath the window in the state of 100% driving state is used for the ultraviolet source 343B and an oxygen gas is supplied to theprocessing vessel 321 with a flow rate of 150 SCCM under the process pressure of 0.02 Torr (2.26 Pa). Assuming the case of using a tubular lamp having a width of 2 cm for theoptical source 323 and irradiating a silicon wafer of 20 cm diameter with such a lamp, the average photon flux on the silicon wafer surface becomes 4.34×1015 cm2, which is about 1/10 the photon flux value noted before. - On the other hand, it is known that an oxygen molecule has an absorption cross-sectional area of 6×10−19 cm2 with regard to the ultraviolet radiation of the 172 nm wavelength. Thus, the transmittance of the ultraviolet radiation in the process ambient, which is given by the equation I/I0=exp(−σnx), is obtained as 0.9916. Here, it is assumed that the process pressure is 0.02 Torr (2.66 Pa) and the gas molecule density n in the process ambient is assumed to be 7.05×1014 cm−3 Further, it is assumed that the ultraviolet radiation propagates the distance of 20 cm in the
processing vessel 321. - Thus, the amount of the radicals corresponding to the absorption of the ultraviolet radiation propagating in the
processing vessel 321 for the distance of 20 cm is evaluated to be 3.65×1013 cm−2 sec by multiplying the factor of 0.0084 to the foregoing value of the photon flux of 4.34×10‥cm−2, and oxygen radicals are formed in theprocessing vessel 321 with this rate. - On the other hand, the flux of the oxygen gas in the
processing vessel 321 becomes 7.98×10−3 cc/cm2 sec in terms of volume in the standard state, assuming that theshower head 21B has the area of 314 cm2. In terms of the number of molecules, this value is converted to the value of 2.138×1017 cm−2 sec. Thus, from the ratio of the flux values of 3.65×1013/2.138×1017=1.71×10−4, the partial pressure of the oxygen radicals formed under the process pressure of 0.02 Torr (2.66 Pa) is obtained as 3.42×10−6 Torr (=1.71×1031 4×0.02). - Thus, it is evaluated that the concentration of the oxygen radicals formed in the
processing vessel 321 becomes about 3.42×10−6 Torr (4.54×10−4 Pa) in the case of the optical power of 100% and the process pressure (=internal pressure of the processing vessel) of 0.02 Torr (2.66 Pa). By conducting similar procedures, the radical density is calculated also for other various conditions. -
FIG. 61 represents the relationship between the radical density, and hence the radical partial pressure, and the duration of the slowdown phenomenon ofFIG. 5 explained before after the start of the substrate processing is represented. - Referring to
FIG. 61 , it can be seen that the slowdown effect appears immediately after the start of the process similarly to the case ofFIG. 5 in the event the radical density in theprocessing vessel 321 is large. In the case the radical density is small, on the other hand, the slowdown phenomenon appears after a long time has elapsed after start of the process. This corresponds to the situation that the growth rate of the oxide film is large in the case of large radical density and the stationary thickness of 0.4 nm is reached in short time, while in the case the radical density is small, it takes a long time until the foregoing stationary thickness of 0.4 nm is achieved because of the small oxide film growth rate. - Similarly, the slowdown duration defined as the duration after the appearance of the slowdown phenomenon up to the vanishing of the slowdown phenomenon changes also with the radical density such that the slowdown duration is decreased when the radical density is large and is increased when the radical density is small.
- From the viewpoint of the actual process of semiconductor device production, there occurs a problem of decrease of fabrication throughput when the process time until the occurrence of the foregoing slowdown effect is too long. Thus, there should be a lower limit for the radical density. On the other hand, when the duration of the slowdown phenomenon is too short, it becomes difficult to form the oxide film of desired thickness of 2-3 atomic layers or 2-4 atomic layers. Thus, there is an upper limit for the radical density.
- From
FIG. 61 , which shows the example of conducting the oxidation of the substrate at 450° C. by the radical oxidation process while using the ultraviolet radiation of the 172 nm wavelength, it can be seen that the lower limit of the radical partial pressure is determined to be 1×10−4 mTorr (133×10−7 Pa) assuming that the tolerable process time is 5 minutes (300 seconds) or less. Further, the upper limit of the radical partial pressure is determined to be 1 mTorr (1.33×10−3 Pa) assuming that the necessary slowdown interval is 100 seconds or more. The ultraviolet radiation power corresponding to this is determined to be 5-50 mW·cm−2 in the region right underneath theoptical source 23. - In
FIG. 61 , it may seem that the interval between the two lines respectively defining the appearance and vanishing of the slowdown phenomenon is decreased with the radical partial pressure. This, however, is merely an apparent effect caused by the fact that the vertical axis and the horizontal axis ofFIG. 61 are represented with logarithmic scale. The duration of the stationary interval is in fact decreased with the radical partial pressure. - Thus, in the foregoing UV-O2 processing, it is preferable to set the oxygen partial pressure to fall in the range of 6.65×10−3 Pa-133 Pa (0.05-1000 mTorr), more preferably the range of 1.33-13.3 Pa (10-100 mTorr).
- It is also possible to conduct the radical oxidation process conducted by using the
substrate processing apparatus 320 ofFIG. 51 also by using ultraviolet radiation of other wavelengths. In this case, it is necessary to change the drive energy of theultraviolet source 324B or the ambient gas composition in order to realize the foregoing radical density of 1×10−4 mTorr (1.33×10−2 mPa) or more but not exceeding 1 mTorr (133 mPa). - For example, in the case of using the ultraviolet radiation source of 146 nm wavelength for the
ultraviolet source 324B, it is necessary to set the oxygen partial pressure to the range of 0.05-50 mTorr (6.7 mPa-6.7 Pa) in view of the large optical absorption larger by 25 times as compared with the case of the wavelength of 172 nm. - It is also possible to nitride the oxide film having the thickness of 2-3 atomic layers thus formed to form an oxynitride film. Because of the larger specific dielectric constant, the use of such an oxynitride film enables further decrease of the thermal oxide film equivalent thickness of the gate insulation film of a MOS transistor.
- Hereinafter, a ninth embodiment of the present invention will be explained.
- In the present embodiment, the
substrate processing apparatus 320 ofFIG. 51 is used, and an oxynitride film is formed directly on a silicon substrate surface according to a UV-NO radical processing similar to the one explained before. -
FIG. 62A shows the thickness distribution of a film obtained for the case an oxide film, formed on the silicon substrate by using thesubstrate processing apparatus 320 ofFIG. 51 with the thickness of 0.4 nm, is subsequently subjected to an oxynitridation processing by supplying an NO gas to theshowerhead 321B, whereinFIG. 62A shows the thickness obtained by ellipsometry. Further, Table 5 below shows the actual thickness of the substrate ofFIG. 62A for the central part and the marginal part thereof obtained by the XPS analysis explained before, wherein the measurement ofFIG. 62A is conducted by setting the detection angle to 90 degrees and reducing the resolution. Thereby, the thickness was obtained conveniently from the ratio of the peaks corresponding to SiO+ and Si4+. The oxynitridation processing was conducted by supplying an NO gas to theshower head 321B with the flow rate of 200 SCCM and driving theultraviolet source 24B for 3 minutes within the foregoing reference power while maintaining the internal pressure of theprocessing vessel 321 at 3.9 Pa (0.03 Torr). The substrate temperature was set to 450° C.TABLE 5 90 degrees 90 degrees center periphery SiO+ 89.45 88.13 Si4+ 10.55 11.87 Si4+/SiO+ 0.117943 0.134687 Thickness (nm) 0.43 0.49 - Referring to
FIG. 62A and Table 5, it can be seen that the thickness after the oxynitridation processing is 0.43-0.49 nm in any of the central part and the marginal part of the substrate, and that there is no substantial difference in the film thickness from the initial thickness of about 0.4 nm. Further, XPS analysis conducted on the oxide film thus processed for detection of nitrogen atoms revealed that no signal from nitrogen atoms has been detected. This means that there has been caused no nitridation reaction at all in the oxide film in the foregoing oxynitridation processing. -
FIG. 62B shows the thickness distribution of a film obtained for the case an oxide film, formed on the silicon substrate similarly with the thickness of 0.7 nm, is subsequently subjected to an oxynitridation processing. Further Table 6 below shows the actual thickness obtained by ellipsometry for the central part and the marginal part by the XPS analysis while setting the detection angle to 90 degrees.TABLE 6 90 degrees 90 degrees center periphery SiO+ 83.49 83.88 Si4+ 16.51 16.12 Si4+/SiO+ 0.197748 0.192179 Thickness (nm) 0.69 0.68 - Referring to
FIG. 62B and Table 6, it can be seen that the thickness after the oxynitridation processing is 0.69-0.68 nm in any of the central part and the marginal part of the substrate, and that there is no substantial difference in the film thickness from the initial thickness of about 0.7 nm. Further, XPS analysis conducted on the oxide film thus processed for detection of nitrogen atoms revealed that no signal from nitrogen atoms has been detected. This means that there has been caused no nitridation reaction at all in the oxide film in the foregoing oxynitridation processing. - From the result of Table 6 and also from the result of Table 5 before, it is concluded that incorporation of nitrogen into the film is not possible by the oxynitridation processing conducted by the UV-NO processing on the oxide film already formed on a silicon substrate surface however small the thickness of the oxide film may be.
- On the other hand,
FIG. 63A shows the thickness distribution of the film formed on a silicon substrate for the case the silicon substrate is directly subjected to the UV-NO processing in thesubstrate processing apparatus 320 ofFIG. 51 after the native oxide film is removed, wherein the film thickness ofFIG. 63A is obtained by ellipsometry. Further, Table 3 shows the thickness of the film thus obtained at the central part and marginal part of the substrate by the XPS analysis while setting the detection angle to 90 degrees. In the experiment ofFIG. 63A , it should be noted that the experiments ofFIG. 63A is conducted in thesubstrate processing apparatus 320 ofFIG. 51 by supplying an NO gas to theshowerhead 321B with the flow rate of 200 SCCM and driving theultraviolet source 324B at the foregoing reference power for 3 minutes while maintaining the internal pressure of theprocessing vessel 321 at 3.99 Pa (0.03 Torr) similarly to the previous case. Thereby, the substrate temperature is set to 450° C. - Referring to
FIG. 63A , it can be seen that there is formed a film on the silicon substrate surface with a generally uniform thickness. From Table 7, it can be seen that the film thickness is about 0.5 nm at any of the central part and the marginal part of the substrate.TABLE 7 90 degrees 90 degrees center periphery SiO+ 86.81 86.92 Si4+ 13.2 13.07 Si4+/SiO+ 0.152056 0.150368 Thickness (nm) 0.55 0.54 - Further,
FIG. 63B shows the film thickness distribution obtained by ellipsometry for the case the oxynitridation processing is conducted under the pressure of 665 Pa (5 Torr) by setting the NO gas flow rate to 1 SLM and driving theultraviolet source 24B at the foregoing reference power for 1 minute. Further, Table 8 below shows the result of the film thickness measurement conducted on the film thus obtained by the XPS analysis while setting the detection angle to 90 degrees.TABLE 8 90 degrees 90 degrees center periphery SiO+ 87.78 87.57 Si4+ 12.22 12.42 Si4+/SiO+ 0.1339212 0.141829 Thickness (nm) 0.50 0.51 - Referring to
FIG. 63B , it can be seen that the film thickness distribution is generally uniform for the film formed on the substrate surface and that it can be seen from Table 8 that the film thickness is about 0.5 nm at any of the central part and the marginal part of the substrate. - Table 9 below shows the result of element analysis conducted on the film obtained by the experiment of
FIG. 63A by the XPS analysis.TABLE 9 atomic % center periphery 90 degree 30 degree 90 degree 30 degree O1s 67.23 63 66.88 66.13 N1s 11.18 10.19 9.13 9.63 Si2p 21.59 26.81 23.99 24.23 - Referring to Table 9, it can be seen that the signals corresponding to the O1s orbital, N1s orbital and Si2p orbital are observed in the film thus formed and that the film shows the oxygen atomic concentration of 67.23%, the nitrogen atomic concentration of 11.18% and the silicon atomic concentration of 21.59% at the central part of the substrate in the measurement conducted by setting the detection angle to 90 degrees. Further, it was confirmed that the film has the oxygen atomic concentration of 66.88%, the nitrogen atomic concentration of 9.13% and the silicon atomic concentration of 24.23% at the marginal part thereof. Thus, it was concluded that the film thus formed is an oxynitride film containing nitrogen.
- Similarly, Table 10 below shows the result of element analysis conducted on the film obtained by the experiment of
FIG. 63B by the XPS analysis.TABLE 10 atomic % center periphery 90 degree 30 degree 90 degree 30 degree O1s 67.3 63.84 67.2 64.2 N1s 11.66 10.36 11.44 10.43 Si2p 21.04 25.8 21.37 25.36 - Referring to Table 10, it is also noted that the signals corresponding to the O1s orbital, N1s orbital and Si2p orbital are observed in the film thus formed and that the film shows the oxygen atomic concentration of 67.3%, the nitrogen atomic concentration of 11.66% and the silicon atomic concentration of 21.24% at the central part of the substrate in the measurement conducted by setting the detection angle to 90 degrees. Further, it was confirmed that the film has the oxygen atomic concentration of 67.2%, the nitrogen atomic concentration of 11.44% and the silicon atomic concentration of 21.37% at the marginal part thereof. Thus, it was confirmed that the compositional uniformity of the film is improved further and that an oxynitride film having a uniform composition is formed on the silicon substrate surface.
- In the measurement of Table 10 in which the XPS spectrum is detected with the detection angle of 30 degrees, it is noted that the nitrogen concentration is decreased slightly as compared with the case of using the detection angle of 90 degrees both in the central part and in the marginal part. In such a measurement conducted by using a shallow detection angle, the signals caused by the photoelectrons emitted at the bottom part of the oxynitride film undergo attenuation as they are transmitted through the film obliquely. As a result, the composition of the upper part of the film is mainly detected by such a measurement. Thus, the result of Table 10 also indicates that the nitrogen atoms are mainly concentrated in the oxynitride film thus formed at the part near the interface to the silicon substrate. A similar tendency is observed also in the result of analysis of Table 9 for the central part of the substrate.
- Next, the kinetics of the oxynitride film formation on such a silicon substrate surface by the UV-NO processing will be explained.
-
FIGS. 64A and 64B show the thickness of an oxynitride film and a nitrogen concentration in the film for the case an NO gas is supplied to theshowerhead 321B of thesubstrate processing apparatus 320 ofFIG. 3 with the flow rate of 200 SCCM and theultraviolet source 324B is driven with the reference power for various durations while maintaining the process pressure at 3.99 Pa (20 mTorr) and the substrate temperature at 450° C. - Referring to
FIG. 64A , it can be seen that the thickness of the oxynitride film increases with time while it is also noted that there occurs a slowdown phenomenon of film growth similar to the one explained before with reference toFIGS. 5 and 8 at the moment the film thickness has reaches the value of about 0.5 nm. Further,FIG. 64A also shows the case in which driving of theultraviolet source 324B was not made during such a nitridation processing by ◯. In this case, it will be noted that there is caused no growth of the oxynitride film at all as can be seen fromFIG. 64A . - On the other hand,
FIG. 64B also indicates that the nitrogen concentration detected by setting the detection angle of the XPS analysis to 30 degrees appears smaller than the case the detection angle is set to 90 degrees in the period immediately after the start of the oxynitridation processing. This indicates that the nitrogen atoms are mainly concentrated to the interface region of the oxynitride film and the silicon substrate. Further,FIG. 64B also indicates that such a non-uniform distribution of nitrogen in the thickness direction is gradually resolved by continuing the oxynitridation processing. - The result of
FIG. 64B indicates that an oxynitride film of high nitrogen concentration is formed immediately after the start of the nitridation processing and that the nitrogen concentration in the film decreases gradually with time, while this indicates that oxidizing reaction becomes dominant in due course with time in the film growth mechanism. After 200 seconds from the start of processing, the observed non-uniformity of nitrogen concentration in the film thickness direction is resolved. -
FIGS. 65A and 65B are diagrams corresponding toFIGS. 64A and 64B respectively showing the case in which the oxynitridation processing is conducted by setting the driving power of theultraviolet source 324B to 20% of the reference power. It can be seen that a result similar to the case ofFIGS. 64A and 64B is obtained. Thus, there is caused a slowdown of film growth when the oxynitride film has reached the thickness of about 0.5 nm and that an oxynitride film of high nitrogen concentration is formed at the beginning of the film growth, with the concentration of the nitrogen atoms in the vicinity of the interface between the oxynitride film and the silicon substrate. -
FIGS. 66A and 66B respectively show the relationship between the film thickness and process time and the relationship between the nitrogen concentration in the film and the process time for the case the oxynitridation processing of a silicon substrate surface is conducted at the substrate temperature of 550° C. - Referring to
FIG. 66B first, it can be seen that the concentration of the nitrogen atoms incorporated into the film is substantially smaller than the case ofFIG. 64B orFIG. 65B in any of the cases in which the detection angle of the XPS analysis is set to 90 degrees or 30 degrees, indicating that the oxynitride film thus formed has a composition closer to that of an oxide film. It is believed that this result has been caused by the promotion of oxidizing reaction at the substrate temperature of 550° C. by residual oxygen remaining in theprocessing vessel 321. - In
FIG. 66A , it is noted that the slowdown of film growth takes place at the thickness of 0.46 nm, which is closer to the thickness of 0.4 nm in which the slowdown of film growth takes place for an oxide film as explained with reference toFIG. 5 or 8, wherein it is believed that this result is caused as a result of the oxynitride film thus formed having the composition closer to that of an oxide film. - It should be noted that the thickness of the oxynitride film is obtained by Eq. (1) explained before and associated parameters that are derived for an oxide film. Thus, there is a possibility that the film thickness is calculated to be slightly larger for those oxynitride films because of the effect of escaping depth of photoelectrons. In any case, it is believed that the oxynitride film formed by the present invention has a thickness controlled to about two atomic layers.
- Meanwhile, in the case of applying the
substrate processing apparatus 320 ofFIG. 51 to the oxynitridation processing of a silicon substrate, it is preferable to use an optical source capable of producing ultraviolet radiation in the wavelength range of 192-142 nm from the consideration similar to the one explained already with reference toFIG. 34 . - In view of applying the
substrate processing apparatus 320 ofFIG. 51 to a single-wafer semiconductor production process, it is preferable that such anoptical source 324B is the one capable of being turned on and turned off as desired. Currently, excimer lamps having the wavelengths of 308 nm, 222 nm, 172 nm, 146 nm and 126 nm are commercially available as a ultraviolet source capable of being turned on and turned off as desired. These excimer lamps have an advantageous feature of having a very sharp spectrum simultaneously. On the other hand, only the excimer lamp having the wavelength of 172 nm and the excimer lamp having the wavelength of 146 nm are the sole candidates for the lamp that satisfies the foregoing requirement. Thereby, it should be noted that the lamp having the wavelength of 146 nm has a half-height width of about 13 nm, and thus, a part of the spectrum becomes shorter than 145 nm. In such a case, therefore, there is a possibility that the oxygen radical excitation may not be caused, depending on the state of the lamp or the peculiarity of the individual lamps. From these considerations, it is concluded that the use of an excimer lamp of the 172 nm wavelength is most preferable for theultraviolet source 324B of thesubstrate processing apparatus 320 ofFIG. 51 in the case of choosing the excimer lamp form the commercially available excimer lamps. -
FIG. 67 shows the schematic construction of an excimer lamp (dielectric barrier discharge tube) 341 producing the ultraviolet radiation of 172 nm (reference should be made to the Japanese Laid-Open Patent Publication 7-196303 or 8-85861). - Referring to
FIG. 67 , theexcimer lamp 341 has a double cylindrical vessel including aninner quartz tube 342 and anouter quartz tube 343 and a Xe gas is confined into a space between theinner quartz tube 342 and theouter quartz tube 343 with a pressure of Xe gas of 33.25 kPa (250 Torr). Further, an aluminumthin film electrode 345 is formed on the inner surface of theinner quartz tube 342 and a mesh-state electrode 344 is formed on the outer side of theouter quartz tube 345. Further, agetter chamber 348 is formed at an axial end of thespace 347 and agetter 346 is provided inside thespace 347. Theexcimer lamp 341 is turned on and turned off as desired by applying an a.c. voltage from apower supply 350 across theelectrodes - For such an excimer lamp, it is possible to use the model UER20-172 marketed by the USHIO or the model HES1703S marketed by Hoya Schott.
- Of course, the ultraviolet source is not limited to those mentioned above and other optical sources such as a low-pressure mercury lamp. Further, if the situation allows, it is also possible to use an excimer laser.
- Next, formation of a uniform oxynitride film on a wafer surface by the UV-NO processing according to a tenth embodiment of the present invention will be explained.
- Referring to Table 7 again, it is noted that the oxynitride film formed under the process pressure of 3.99 Pa (0.03 Torr) and the 100% UV radiation power shows a generally uniform thickness at the central part and marginal part of the substrate, while it is also noted that the result of Table 9 shows that there exists a difference of about 2% in the nitrogen concentration and the distribution of the nitrogen concentration is not uniform. Thus, Table 9 indicates that it is an important issue in the oxynitride film formed by the UV-NO processing to achieve the uniformity of film thickness and nitrogen concentration at the same time.
-
FIG. 68A shows the thickness distribution of an oxynitride film formed under the same conduction as noted above except that the duration of the oxynitridation is set to 1 minute and 30 seconds. On the other hand,FIG. 68B shows the thickness distribution of an oxynitride film for the case of forming the oxynitride film under the same condition except that the ultraviolet lamp is moved back and forth. InFIGS. 68A and 68B , the number of measurement points is increased to seventeen. In the experiment ofFIG. 68B , the back and forth movement of the ultraviolet lamp is conducted such that the ultraviolet lamp is moved from a first wafer edge to a second, opposing wafer edge separated from the first wafer edge by the distance of 200 mm with a speed of 60 mm/sec and is moved back after stopping at the switchback point for 0.1 seconds. The ultraviolet lamp is also stepped for 1 second at the center of the wafer. - Comparing
FIGS. 68A and 68B , it can be seen that a more uniform film thickness distribution is achieved in the experiment ofFIG. 68B as compared with the experiment ofFIG. 68A by adopting the back and forth movement sequence of the ultraviolet lamp. - In order to ensure accuracy of the conclusion, Tables 11 and 12 are presented below showing the result of film thickness measurement conducted by the XPS analysis for the samples of
FIGS. 68A andFIG. 68B . In the results of Tables 11 and 12, the measurement at the marginal part includes two measuring points. Further, Table 13 below shows the result of measurement for the nitrogen concentration in the case of the sample ofFIG. 68A , while Table 14 below shows the result of measurement for the nitrogen concentration in the case of the sample ofFIG. 68B .TABLE 11 90 degrees 90 degrees 90 degrees center periphery 1 periphery 2SiO+ 87.76 87.2 86.11 Si4+ 12.23 12.81 13.89 Si4+/SiO+ 0.139357 0.146904 0.161305 Thickness 0.50 0.53 0.58 (nm) -
TABLE 12 90 degrees 90 degrees 90 degrees center periphery 1 periphery 2SiO+ 87.26 87.13 87.31 Si4+ 12.74 12.88 12.69 Si4+/SiO+ 0.146 0.147825 0.145344 Thickness 0.53 0.53 0.52 (nm) -
TABLE 13 atomic % center periphery 1 periphery 290 degree 30 degree 90 degree 30 degree 90 degree 30 degree O1s 69.89 66.76 70.98 67.52 69.98 66.42 N1s 9.82 9.38 8.88 8.75 9.95 9.36 Si2p 20.29 23.86 20.14 23.73 20.06 24.23 -
TABLE 14 atomic % center periphery 1 periphery 290 30 90 30 90 30 degree degree degree degree degree degree O1s 69.61 66.97 68.19 67.12 69.1 66.99 N1s 9.86 9.21 9.43 8.73 9.79 8.93 Si2p 20.53 23.83 22.38 24.14 21.11 24.08 - Comparing these results, it can be seen that a uniform film thickness distribution has become possible between the central part and marginal part of the wafer by causing a back and forth movement in the ultraviolet lamp. By doing so, it is also possible to achieve the uniform distribution for the nitrogen concentration. The foregoing results indicates that a uniform ultraviolet radiation is realized over the wafer surface by causing such a back and forth movement of the ultraviolet lamp.
-
FIG. 69A shows a NO gas sequence that has been used in the ninth and tenth embodiments of the present invention together with a temperature profile T. - Referring to
FIG. 69A , the heating of thesubstrate 322 is started immediately after incorporation of thesubstrate 322 into theprocessing vessel 321, wherein it will be noted that a nitrogen gas is introduced into theprocessing vessel 321 at the initial state of the heating process. This nitrogen gas is switched to the NO gas when the temperature has reached a predetermined holding temperature. Further, theultraviolet source 324B is driven for a predetermined period when the concentration of the NO gas has reached a predetermined level in theprocessing vessel 321. With this, the UV-NO processing explained before is conducted. - Thereafter, the
ultraviolet source 324B is turned off, and the supply of the NO gas is interrupted. Thesubstrate 322 is then taken out from theprocessing vessel 321 when the substrate temperature T has been lowered to the room temperature. -
FIG. 69B , on the other hand, shows a NO gas sequence according to an eleventh embodiment of the present invention used in place of the sequence ofFIG. 69A in thesubstrate processing apparatus 320 ofFIG. 51 . - Referring to
FIG. 69B , the heating of thesubstrate 322 is started immediately after the incorporation of thesubstrate 322 into theprocessing vessel 321, wherein it should be noted that introduction of the NO gas is started at the same time thesubstrate 322 has been incorporated in the case of the present invention. Thus, when the substrate temperature T has reached a predetermined temperature, theultraviolet source 324B is driven for a predetermined time and the desired UV-NO processing is conducted. - Thereafter, the
ultraviolet source 324B is turned off, the supply of the NO gas is turned off further. Thesubstrate 322 is then taken out of theprocessing vessel 321 when the substrate temperature T has been lowered to the room temperature. -
FIGS. 70A and 70B show the relationship between the process temperature and the thickness of the oxynitride film thus obtained and the relationship between the processing temperature and the nitrogen concentration in the oxynitride film. InFIGS. 70A and 70B , it should be noted that ● represents the case of using the NO sequence ofFIG. 69A while ∘ represents the case of using the NO sequence ofFIG. 69B , respectively. - Referring to
FIG. 70A , it can be seen that there exists no material difference between the case of using the NO sequence ofFIG. 69A and the case of using the NO sequence ofFIG. 69B as long as the substrate temperature is set to 500° C. or less. In the case the substrate temperature has exceeded 500° C., on the other hand, it can be seen that there is caused an increase in the film thickness of the obtained oxynitride film when the sequence ofFIG. 69B is used. - Comparing this result with the nitrogen concentration in the film shown in
FIG. 70B , it can be seen that the atomic concentration of nitrogen in the film is increased substantially by using the NO sequence ofFIG. 69B . This result shows that the observed increase of thickness of the oxynitride film inFIG. 70A is attributed primarily to the nitrogen atoms that are incorporated into the oxynitride film. - Thus, by introducing an NO gas into the processing vessel prior to the processing, it becomes possible to incorporate a large amount of nitrogen atoms into the oxynitride film at the time of the UV-NO processing.
- It should be noted that the NO gas sequence of
FIGS. 69A and 69B can be used also in thesubstrate processing apparatus 20 ofFIG. 3 for achieving a similar effect. -
FIGS. 71A-71E show the fabrication process of a semiconductor device according to a twelfth embodiment of the present invention. - Referring to
FIG. 71A ,diffusion regions silicon substrate 331 by an ion implantation process of an impurity element, and asurface region 331 c of thesilicon substrate 331 is exposed at anopening 337 formed in aninsulation film 335 and aninsulation film 336. - The exposed
surface region 331 c is then subjected to a process of removing a native oxide film, and the UV-NO processing is conducted thereafter in thesubstrate processing apparatus 320 ofFIG. 51 under the condition explained before by using the ultraviolet radiation of 172 nm wavelength. As a result, there is caused slowdown of film growth on the surface of thesilicon substrate 331, and anSiON film 332 having a thickness of about 0.5 nm is formed uniformly. - Next, in the step of
FIG. 71C , a high-K dielectric film 333 such as ZrSiOx, HfSiOx, ZrO2, HfO2, Ta2O5, Al2O3, and the like, is formed on theSiON film 332 by a CVD process. - Further, a
metal electrode layer 334 is deposited on the high-K dielectric film 333 thus formed in the step ofFIG. 71D , and ametal gate electrode 334G is formed by conducting an etch-back process in the step ofFIG. 72E . - In the present embodiment, it is preferable that the UV-NO processing is conducted at a temperature not exceeding 550° C. under the process pressure in the range of 1.33-1.33×103Pa.
- In the case of measuring the thickness of a very thin film formed on a wafer by way of ellipsometry, there is a case that a thickness value larger than the actual value is obtained because of the adsorption of organic molecules and the like on the film surface during the measurement process. In the case of measuring the film thickness at a number of points, in particular, there is a tendency that the measured value changes during the measurement and it is difficult to evaluate the exact uniformity of the film.
- In view of the situation noted above, the inventor of the present invention has made an improvement of film-thickness measurement process so as to ensure exactness on the uniformity of the film thickness.
- In the improvement of the inventor, the entire path of the substrate from the load/unload gate of the deposition apparatus up to the wafer stage of an ellipsometer is placed under the down flow stream of a chemical filter that is used for removing organic molecules. According to such a construction, it is possible to suppress the apparent increase of the film thickness within 0.02 nm (0.2 Å) even in the case the wafer is placed in the measurement ambient for 3 hours.
- When such an ellipsometry is used, about ten minutes are needed for conducting the film thickness measurement at 49 points on the wafer surface, while it is evaluated that the increase of the apparent film thickness during this interval is about 0.001 nm (0.01 Å). Further, it is confirmed that the measurement apparatus thus improved has the reproducibility of 0.006 nm (0.06 Å) in terms of the variance value a from the repeated measurement conducted at a fixed point.
- Now,
FIG. 75 shows the result of measurement of an oxynitride film formed on a wafer having a diameter of 200 nm with the thickness of 0.5 nm by using the UV-NO process under the condition explained before. The measurement was conducted by the measuring fixture explained above. InFIG. 76 , the film thickness was measured at 49 points on the wafer surface. - Referring to
FIG. 75 . it can be seen that the in-plane variance a of the film thickness is 0.65%. In terms of the thickness, this means that the film thickness variation is in the order of 0.0065 nm (0.065 Å). In other words, the variation of the film thickness has been reduced to near the detection limit. Thus, it should be noted that a completely uniform oxynitride film is obtained over the wafer of the 200 mm diameter. - In the similar measurement of the oxide film formed by the UV-O2 processing, on the other hand, it was also confirmed that a film of excellent uniformity characterized by the film thickness variance a of only about 0.7% is obtained for the oxide film having the thickness of 0.4 nm.
- Further, the present invention is not limited to the embodiments explained heretofore, but various variations and modifications may be made without departing from the scope of the invention.
Claims (26)
1. A substrate processing apparatus, comprising:
a nitrogen radical formation unit forming nitrogen radicals with high-frequency plasma; and a processing vessel holding a substrate formed with an insulation film,
said processing vessel causing nitridation of a surface of said insulation film by being supplied with said nitrogen radicals form said
nitrogen radical formation unit and supplying said nitrogen radicals to said surface of said insulation film.
2. The substrate processing apparatus as claimed in claim 1 , wherein said processing vessel carries said nitrogen radical formation unit on a sidewall surface thereof, said processing vessel supplying said nitrogen radicals to said surface of said insulation film in the form of being carried by a gas flow caused to flow along said surface of said insulation film.
3. The substrate processing apparatus as claimed in claim 2 , wherein said gas flow is formed in said processing vessel so as to flow from a first side of said substrate formed with said insulation film to a second, diametrically opposite side to said first side.
4. The substrate processing apparatus as claimed in claim 3 , wherein said processing vessel is evacuated at said second side of said substrate.
5. The substrate processing apparatus as claimed in claim 1 , wherein said radical formation unit comprises a gas passage and a high-frequency plasma formation part formed in a part of said gas passage for causing plasma excitation in a nitrogen gas flowing through said gas passage.
6. The substrate processing apparatus as claimed in claim 5 , wherein said high-frequency plasma formation unit causes said plasma excitation of said nitrogen gas at a frequency of 400-500 kHz.
7. The substrate processing apparatus as claimed in claim 1 , wherein said processing vessel is connected with an evacuation system capable of evacuating an interior space of said processing vessel to a pressure lower than a pressure used in said nitridation step of said insulation film surface.
8. A substrate processing apparatus, comprising:
a processing vessel defining a process space, said processing vessel accommodating a stage holding a substrate in said process space;
a first radical source provided on said processing vessel at a side of a first end of said processing vessel with respect to said stage;
a second radical source provided on said processing vessel at a side of said first end of said processing vessel with respect to said stage;
a first evacuation path provided on said processing vessel at a side of a second end of said processing vessel opposite to said first end, said first evacuation path evacuating said process space to a first process pressure; and
a second evacuation path provided on said processing vessel at a side of said second end of said processing vessel, said second evacuation path evacuating said process space to a second process pressure.
9. The substrate processing apparatus as claimed in claim 8 , wherein said first evacuation path is activated in the state when said first
radical source is activated, and wherein said second evacuation path is activated in the state when said second radical source is activated.
10. The substrate processing apparatus as claimed in claim 8 , wherein said first radical source includes an ultraviolet source exciting an oxygen gas supplied to said processing vessel, and wherein said second radical source comprises a remote plasma source supplied with a nitrogen gas and causing excitation of said nitrogen gas.
11. The substrate processing apparatus as claimed in claim 10 , wherein said first radical source includes a nozzle causing to flow said oxygen gas along a surface of said substrate held on said stage, and wherein said ultraviolet source is provided between said nozzle and said substrate so as to cause excitation of said oxygen gas through an optical window.
12. The substrate processing apparatus as claimed in claim 8 , wherein said first evacuation path includes a turbo molecular pump.
13. The substrate processing apparatus as claimed in claim 8 , wherein said second evacuation path includes a mechanical booster pump.
14. The substrate processing apparatus as claimed in claim 12 , wherein said turbo molecular pump is boosted by a mechanical booster pump.
15. The substrate processing apparatus as claimed in claim 8 , wherein said processing vessel has a substrate load/unload gate at said second end.
16. The substrate processing apparatus as claimed in claim 8 , wherein both of said first evacuation path and said second evacuation path evacuate said process space via an evacuation port provided in said processing vessel in the vicinity of said second end.
17. The substrate processing apparatus as claimed in claim 16 , wherein said first evacuation path includes a turbo molecular pump connected to said process space via said evacuation port.
18. The substrate processing apparatus as claimed in claim 8 , wherein said state is provided rotatably and wherein said substrate processing apparatus further comprises a rotating mechanism rotating said stage.
19. A substrate processing apparatus, comprising:
a processing vessel defining a process space, said processing vessel accommodating a state holding a substrate in said process space;
a first radical source provided on said processing vessel;
a second radical source provided on said processing vessel;
a first evacuation path provided on said processing vessel, said first evacuation path evacuating said process space to a first process pressure; and
a second evacuation path provided on said processing vessel, said second evacuation path evacuating said process space to a second process pressure,
wherein said first processing path is provided so as to evacuate said process space at a side opposite to said first radical source with respect to said substrate on said stage, and wherein said second evacuation path is provided so as to evacuate said process space at a side opposite to said second radical source with respect to said substrate on said stage.
20. A cluster-type substrate processing apparatus, comprising:
a substrate transfer chamber; and
a plurality of process chambers connected to said substrate transfer chamber, one of said plurality of process chambers comprising:
a processing vessel having a substrate load/unload opening at a first end thereof in connection with said substrate transfer chamber and a first radical source at a second end opposite to said first end, said processing vessel defining a process space therein;
a stage provided in said process space between said first end and said second end in a rotatable manner, said stage holding a substrate thereon;
a first process gas inlet provided in said process space between said first end and said stage, said first process gas inlet introducing a first process gas into said process space;
a second radical source provided on said processing vessel so as to cause excitation of said fist process gas between said first gas inlet and said stage;
a first evacuation port provided in said process space at a part closer to said first end with respect to said stage;
a second evacuation port provided in said process space at a side closer to said second end with respect to said stage;
a first pump connected to said first evacuation port so as to evacuate said process space to a first process pressure; and
a second pump connected to said second evacuation port so as to evacuate said process space to a second process pressure lower than said first process pressure, wherein said second pump is disposed in the vicinity of said second end of said processing vessel.
21. A semiconductor device, comprising:
a silicon substrate; and
an insulation film formed on said silicon substrate with a thickness of 2-4 atomic layers.
22. The semiconductor device as claimed in claim 21 , wherein said insulation film has a uniform thickness within the range of 2-4 atomic layers.
23. The semiconductor device as claimed in claim 21 , wherein said insulation film comprises an oxide film.
24. The semiconductor device as claimed in claim 21 , wherein said insulation film comprises a silicon oxynitride film.
25. The semiconductor device as claimed in claim 21 , further comprising a high-K dielectric film formed on said insulation film and a gate electrode formed on said high-K dielectric film.
26. A semiconductor device, comprising: a silicon substrate; and
an insulation film formed on said silicon substrate,
said insulation film is formed by nitriding an oxide film formed on said silicon substrate with a thickness of 1-4 atomic layers.