US20050142432A1 - Fuel cell with randomly-dispersed carbon fibers in a backing layer - Google Patents
Fuel cell with randomly-dispersed carbon fibers in a backing layer Download PDFInfo
- Publication number
- US20050142432A1 US20050142432A1 US10/747,373 US74737303A US2005142432A1 US 20050142432 A1 US20050142432 A1 US 20050142432A1 US 74737303 A US74737303 A US 74737303A US 2005142432 A1 US2005142432 A1 US 2005142432A1
- Authority
- US
- United States
- Prior art keywords
- catalyst
- fuel cell
- secured
- flow field
- backing layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A fuel cell (40) includes first and second catalysts (12′), (14′) secured to opposed surfaces of an electrolyte (16′); a first flow field (26′) secured in fluid communication with the first catalyst (12′) defining a plurality of flow channels (30A′, 30B′, 30C′, 30D′) between a plurality of ribs (32A′, 32B′, 32C′, 32D′, 32E′) of the first flow field (26′); and a backing layer (42) secured between the first flow field (26′) and the first catalyst (12′). The backing layer (42) includes a carbon black, a hydrophobic polymer, and randomly-dispersed carbon fibers (44). The carbon fibers (44) are at least twice as long as a width (46) of the flow channels (30A′, 30B′, 30C′, 30D′) defined in the adjacent first flow field (26′). The backing layer (42) replaces a known substrate (22) and diffusion layer (18).
Description
- The present invention relates to fuel cells that are suited for usage in transportation vehicles, portable power plants, or as stationary power plants, and the invention especially relates to a fuel cell having a backing layer secured between a flow field and a catalyst.
- Fuel cells are well-known and are commonly used to produce electrical energy from reducing and oxidizing reactant fluids to power electrical apparatus, such as apparatus on-board space vehicles, transportation vehicles, or as on-site generators for buildings. Each individual fuel cell generally includes an anode catalyst and a cathode catalyst separated by an electrolyte, such as a proton exchange membrane (“PEM”) as known in the art. Frequently, a diffusion layer is secured between the catalyst and a substrate layer. The substrate layer is usually secured between the diffusion layer and a flow field. If there is no diffusion layer, the substrate is secured between the catalyst and the flow field. Flow fields define flow channels for directing reactant streams through the fuel cell in fluid communication through the diffusion and substrate layers with the catalysts. As is known, the flow fields may be porous water transport plates or solid separator plates.
- The diffusion layer is typically a highly porous, electrical conductor made from carbon black and a hydrophobic polymer, such as polytetrafluoroethylene. Depending on the fuel cell design, the diffusion layer is usually hydrophobic, however, the diffusion layer may be partially hydrophobic and partially hydrophilic to facilitate simultaneous liquid and gaseous transport through the layer. The diffusion layer is usually about 25-100 microns thick. The diffusion layer facilitates transfer of the reactant streams through the fuel cell by minimizing the thickness of water films on the surface of the catalysts. The diffusion layer also facilitates the removal of product water from the fuel cell.
- The substrate layer adjacent the diffusion layer is highly porous and made from expensive carbon fibers and a well known manufacturing process that requires high temperature graphitizing. Depending on the cell design, the substrate layer may be either hydrophobic or hydrophilic. The substrate is usually about 150-300 microns thick. The substrate facilitates the transport of reactant streams, water vapor, liquid water and electrons. The substrate conducts electrons both through the plane of the substrate and in the plane of the substrate from a centerline of an adjacent flow channel to ribs of the flow field, wherein the flow channel is defined between ribs of the flow field. The substrate also facilitates the diffusion and flow of reactant streams and product water both through the plane of the substrate and in the plane of the substrate from the flow channel to the centerline of the flow channel beneath the rib of the flow field, or vice versa. Also, the substrate must have a flexural strength adequate to distribute an axial pressure load relatively uniformly over total surface areas of adjacent layers. For example, the pressure load must be distributed evenly across the flow channels of the flow field to prevent the substrate from deforming into the flow channels. An exemplary flexural strength is about 200 kilogram force per square centimeter (“kgf /cm2”). U.S. Pat. No. 4,851,304 to Miwa et al. describes properties of typical fuel cell substrates. Planar types of fuel cells are secured in compression in a fuel cell stack by a combination of pressure plates and tie-rods, as is well known. This axial compressive force minimizes the resistance of the cells and is required to obtain suitable fluid seals. The substrate must have a compressive strength that is typically at least two times the axial force on the cell stack. Typical compressive strength of a prior art substrate is greater than 10 kgf/cm2.
- In fuel cells of the prior art, it is known that carbon or graphite layers or papers are traditionally secured between the catalysts and flow fields as diffusion and/or substrate layers. However, the use of known carbon or graphite layers or papers presents significant problems, including high manufacturing costs, impeding the diffusion of hydrogen and oxygen through pores defined by the layers, and impeding the outflow of fuel cell product water from a cathode catalyst.
- A partial solution to the use of carbon or graphite paper is disclosed in U.S. Pat. No. 5,707,755, entitled “PEM/SPE Fuel Cell” that issued on Jan. 13, 1998 to Grot. The patent discloses, instead of the carbon or graphite layers or papers, the use of a plurality of electrically conductive filaments secured with a specific orientation with respect to flow channels, or grooves of a flow field. The specific orientation is longitudinal so that the filaments extend across, and do not fall into, the flow channels, or grooves, that direct reactant flow through the fuel cell.
- Nonetheless, the prior art has limitations. Manufacturing a fuel cell with conductive filaments having such a specific orientation imposes substantial cost and manufacturing burdens. Moreover, the prior art fails to rectify the significant substrate manufacturing costs associated with the mass production of fuel cells. The substrates are costly because they include expensive carbon fibers and are manufactured through a costly high temperature graphitizing process well known in the art. Accordingly, there is a need for a fuel cell that minimizes substrate costs by replacing the prior art substrates with a cost effective material.
- The invention is a fuel cell with randomly-dispersed carbon fibers in a backing layer of the fuel cell. The fuel cell produces electricity from reducing fluid and oxygen containing oxidant reactant streams, and comprises first and second catalysts secured to opposed surfaces of an electrolyte, such as a proton exchange membrane (“PEM”) well known in the art. A first flow field is secured in fluid communication with the first catalyst, the first flow field defining a plurality of flow channels between a plurality of ribs of the first flow field. The backing layer is secured between and in fluid communication with the first flow field and the first catalyst so that the backing layer is at least coextensive with the first flow field and the first catalyst. The backing layer is made from between 5 weight percent (“wt%”) and 25 wt % carbon black, between 50 wt % and 90 wt % carbon fibers, and between 5 wt % and 25 wt % of a hydrophobic polymer. For purposes herein, a “hydrophobic polymer” is defined as a polymer having a surface energy that is less than 40 dynes/cm2. Examples of hydrophobic polymers known in the art are polytetrafluoroethylene and polyvinyldene fluoride. The carbon fibers are randomly dispersed with the carbon black and hydrophobic polymer so that the backing layer, which is bonded to the first catalyst layer and secured between the first catalyst and the first flow field, has a thickness between the first catalyst and the first flow field of between about 25 and about 250 microns, and a compressive strength greater than 5 Kgf/cm2. Because the backing layer replaces the costly substrate and diffusion layers, fuel cell manufacturing costs and requirements are minimized.
- In a preferred embodiment, the first catalyst is an anode catalyst and the fuel cell includes a diffusion layer and substrate or substrate layer between the second catalyst and second flow field. The invention includes a method of manufacturing the backing layer including the steps of: (a) dispersing the carbon black, carbon fibers, and hydrophobic polymers in an aqueous suspension, (b) removing the water by filtration; (c) thermally processing the constituents of the layer to melt or cure the hydrophobic polymer. The layer may then be bonded to the anode catalyst by known means.
- Accordingly, it is a general purpose of the present invention to provide a fuel cell with randomly-dispersed carbon fibers in a backing layer that overcomes deficiencies of the prior art.
- It is a more specific purpose to provide a fuel cell with randomly-dispersed carbon fibers in a backing layer that provides a cost effective fuel cell by substituting an anode backing layer for substrate and diffusion layers.
- These and other purposes and advantages of the present fuel cell with randomly-dispersed carbon fibers in a backing layer will become more readily apparent when the following description is read in conjunction with the accompanying drawings.
-
FIG. 1 is a simplified schematic representation of a prior art fuel cell. -
FIG. 2 is a simplified schematic representation of a preferred embodiment of a fuel cell with randomly-dispersed carbon fibers in a backing layer constructed in accordance with the present invention. - Referring to the drawings in detail, a typical prior art fuel cell is shown in
FIG. 1 and is designated by thereference numeral 10. As is well known in the art, thefuel cell 10 includes afirst catalyst 12, such as an anode catalyst, and asecond catalyst 14, such as a cathode catalyst, secured to opposed surfaces of anelectrolyte 16, such as a proton exchange membrane (“PEM”). Thefuel cell 10 also includes ananode diffusion layer 18 secured to thefirst catalyst 12 and acathode diffusion layer 20 secured to thesecond catalyst 14; ananode substrate 22 or substrate layer secured to theanode diffusion layer 18 and acathode substrate 24 secured to thecathode diffusion layer 20; afirst flow field 26 secured in fluid communication with thefirst catalyst 12; and, asecond flow field 28 secured in fluid communication with thesecond catalyst 14. - The
first flow field 26 defines a plurality offlow channels ribs first flow field 26. Thesecond flow field 28 defines a plurality offlow channels ribs flow field 28. The operation of such a priorart fuel cell 10 is well known in the art as disclosed in U.S. Pat. No. 6,322,915, entitled “Humidification System For A Fuel Cell Power Plant” that issued on Nov. 27, 2001 to Collins et al., which patent is owned by the owner of all rights in the present invention. -
FIG. 2 shows the present invention of a fuel cell with randomly-dispersed carbon fibers in a backing layer and is generally designated by thereference numeral 40. For purposes of efficiency, those components of the present invention that are virtually the same as comparable elements as the priorart fuel cell 10 described above and shown inFIG. 1 are shown inFIG. 2 having a prime of the same reference numeral shown inFIG. 1 . For example, theproton exchange membrane 16 shown inFIG. 1 is designated by thereference numeral 16′ inFIG. 2 . - The present invention of a fuel cell with randomly-dispersed carbon fibers in a backing layer includes a
first catalyst 12′, such as an anode catalyst, and asecond catalyst 14′, such as a cathode catalyst, secured to opposed surfaces of anelectrolyte 16′, such as a “PEM”. Thefuel cell 40 also includes acathode diffusion layer 20′ secured to thesecond catalyst 14′; acathode substrate 24′ secured to thecathode diffusion layer 20′; asecond flow field 28′ secured in fluid communication with thesecond catalyst 14′; and, afirst flow field 26′ secured in fluid communication with thefirst catalyst 12′. Thefirst flow field 26′ defines a plurality offlow channels 30A′, 30B′, 30C′, 30D′ between a plurality ofribs 32A′, 32B′, 32C′, 32D′, 32E′ of thefirst flow field 26′. - The
fuel cell 40 also includes abacking layer 42 secured between and in fluid communication with thefirst catalyst 12′ and thefirst flow field 26′. Thebacking layer 42 replaces theanode diffusion layer 18 andanode substrate 22 of the priorart fuel cell 10 as shown inFIG. 1 . Thebacking layer 42 is made from between 5 weight percent (“wt%”) and 25 wt % carbon black, between 50 wt % and 90 wt % carbon fibers, and between 5 wt % and 25 wt % of a hydrophobic polymer. Thecarbon fibers 44 have a length that is at least twice as long as awidth 46 of awidest flow channel 30D′, wherein thewidth 46 of thewidest flow channel 30D′ is a shortest distance betweenflow field ribs 32D′, 32E′ defining thewidest flow channel 30D′ of thefirst flow field 26′. Thecarbon fibers 44 are randomly dispersed with the carbon black and hydrophobic polymer within thebacking layer 42, resulting in thelayer 42 having a thickness between about 25-250 microns thick, wherein the thickness is a shortest distance through the layer between thefirst catalyst 12′ and thefirst flow field 26′. Thelayer 42 also has a compressive strength of greater than 5 Kg/cm2. - Exemplary carbon blacks appropriate for use in the
backing layer 42 include a carbon black available under the product name “VULCAN XC-72” from the Cabot Corporation of Billerica, Mass., U.S.A. A suitable hydrophobic polymer is polytetrafluoroethylene (“PTFE”) available under the product name “PTFE Grace 30” from the E.I. du Pont de Nemours and Company of Wilmington, Del., U.S.A. Other acceptable hydrophobic polymers are known in the art. A suitable carbon fiber is available under the product name “SIGRAFIL C” from the SGL Carbon Group company of St. Marys, Pa., U.S.A. A family of high strength carbon fibers is also available from the BP Amoco Performance Products company of Warrensville Heights, Ohio, U.S.A. -
FIG. 2 shows thefuel cell 40 having parallel flow channels of similar or identical widths, and wherein the carbon fibers have a length that is at least twice as long as thewidth 46 offlow channel 30D′. WhileFIG. 2 shows thefuel cell 40 having parallelfirst flow channels 30A′, 30B′, 30C′, 30D′, other exemplary flow channels, such as serpentine channels, voids of various dimensions, or voids in a “checkerboard” arrangement around square-shaped flow field ribs, may be used as known in the art. The operation of a fuel cell with flow channels in such a “checkerboard” arrangement is well known as disclosed in U.S. Pat. No. 5,503,944, that issued on Apr. 2, 1996 to Meyer et al., which patent is owned by the owner of all rights in the present invention. For purposes of the present invention where flow channels (not shown) have dissimilar widths, the length of thecarbon fibers 44 would be at least twice as long as a width of a widest flow channel (not shown) of dissimilar width flow channels. - The
carbon fibers 44 serve to enhance electrical conductivity within thefuel cell 40 and to contribute to thebacking layer 42 having a minimal thickness with an adequate flexural and compressive strength so that thelayer 42 can withstand an axial pressure load and prevent thelayer 42 from deforming intoflow channels 30A′, 30B′, 30C′, 30D′. - As is known, prior art fuel cells generate water at a cathode catalyst as fuel cell product water. If the product water is not efficiently removed from the cathode catalyst, the product water will accumulate adjacent the cathode catalyst effectively “flooding” the catalyst. By “flooding” the catalyst, it is meant that a gaseous oxidant reactant stream cannot efficiently flow or diffuse into contact with the cathode catalyst. Because the oxidant cannot contact the flooded cathode catalyst, performance of the fuel cell is degraded. Therefore, in order to efficiently remove fuel cell product water, known
cathode diffusion layer 20 andcathode substrate layer 24 are dimensioned to define specific ranges of pore sizes and porosities, or percent pore volumes. However, such efficient movement of fuel cell product water is not a requirement of the priorart fuel cell 10anode diffusion layer 18 oranode substrate layer 22. - Consequently, in a preferred embodiment of the present invention, the
backing layer 42 is only secured adjacent theanode catalyst 12′, as shown inFIG. 2 . Thebacking layer 42 secured adjacent theanode catalyst 12′ may therefore be thinner and more hydrophilic than the priorart anode substrate 22 that is secured adjacent to theanode catalyst 12′ of the priorart fuel cell 10. Hence, a preferred embodiment of the invention is thefuel cell 40 with thebacking layer 42 secured adjacent to theanode catalyst 12′. However, alternative embodiments of the invention include afuel cell 40 withbacking layers 42 secured adjacent to both the anode andcathode catalysts 12′, 14′, or secured adjacent to only thecathode catalyst 14′. - The invention includes a method of manufacturing the
backing layer 42 including the steps of: (a) randomly dispersing the carbon black,carbon fibers 44, and hydrophobic polymer in an aqueous suspension, (b) then removing the water from the aqueous suspension by filtration or other water removal methods known in the art, (c) and then thermally processing the carbon black,carbon fibers 44 and hydrophobic polymer constituents of the layer to melt the hydrophobic polymer. The thermal processing is normally done in air for 5-15 minutes at a temperature equal to or within plus or minus 15 degrees centigrade of the melting point or cure point of the hydrophobic polymer. The resulting backing layer may then be bonded to an anode catalyst by known means. - Where the invention is the
FIG. 2 embodiment having thebacking layer 42 secured only adjacent thesecond catalyst 12′, thefuel cell 40 may be fabricated as follows. First, thecathode diffusion layer 20′ is applied to thecathode substrate 24′ by known means. Second, anode andcathode catalysts 12′, 14′ are applied to anelectrolyte 16′, such as a “PEM” to form a membrane electrode assembly (“MEA”). Then the “MEA” is bonded to acathode diffusion layer 20′. Finally, thebacking layer 42, made as described above, is bonded to theanode catalyst 12′ by known means. - The patents referred to above are hereby incorporated herein by reference.
- While the present invention has been described and illustrated with respect to a particular construction of a fuel cell with randomly-dispersed carbon fibers in a backing layer it is to be understood that the invention is not to be limited to the described and illustrated embodiments. Accordingly, reference should be made primarily to the following claims rather than the foregoing description to determine the scope of the invention.
Claims (7)
1. A fuel cell (40) for producing electricity from reducing fluid and oxygen containing oxidant reactant streams, the fuel cell (40) comprising:
a. a first catalyst (12′) and a second catalyst (14′) secured to opposed surfaces of an electrolyte (16′);
b. a first flow field (26′) secured in fluid communication with the first catalyst (12′), the first flow field (26′) defining a plurality of flow channels (30A′, 30B′, 30C′, 30D′) between a plurality of ribs (32A′, 32B′, 32C′, 32D′, 32E′) of the first flow field (26′);
c. a backing layer (42) secured between and in fluid communication with the first flow field (26′) and the first catalyst (12′); and,
d. wherein, the backing layer (42) includes:
i. between 5 wt % and 25 wt % carbon black;
ii. between 50 wt % and 90 wt % carbon fibers (44), where the carbon fibers (44) have a length that is at least twice as long as a width (46) of a widest flow channel (30′D), wherein the width (46) of the widest flow channel (30′D) is a shortest distance between flow field ribs (32D′, 32E′) defining the widest flow channel (30D′) of the first flow field (26′);
iii. between 5 wt % and 25 wt % of a hydrophobic polymer; and,
iv. the carbon fibers (44) being randomly dispersed with the carbon black and hydrophobic polymer so that the resulting backing layer (42) has a thickness between the first catalyst (12′) and the first flow field (26′) of between about 25 and 250 microns, and a compressive strength greater than 5 Kgf/cm2.
2. The fuel cell (40) of claim 1 , wherein the first catalyst (12′) is an anode catalyst and the second catalyst (14′) is a cathode catalyst secured to a cathode diffusion layer (20′) that is secured to a cathode substrate (24′).
3. The fuel cell (40) of claim 1 , further comprising a second backing layer secured between the second catalyst (14′) and second flow field (28′).
4. The fuel cell (40) of claim 1 wherein the first catalyst (12′) is a cathode catalyst and the second catalyst (14′) is an anode catalyst secured to an anode diffusion layer (20′) that is secured to an anode substrate (24′).
5. The fuel cell (40) of claim 1 , wherein the electrolyte (16′) is a proton exchange membrane.
6. A method of manufacturing a backing layer (42) for use adjacent a catalyst (12′, 14′) in a fuel cell (40), the method comprising the steps of:
a. randomly dispersing a carbon black, carbon fibers (44), and a hydrophobic polymer in an aqueous suspension, wherein the carbon fibers (44) have a length that is at least twice as long as a width (46) of a widest flow channel (30′D) of a flow field (26′) secured in fluid communication with the catalysts (12′, 14′);
b. removing the water from the aqueous suspension;
c. thermally processing the carbon black, carbon fibers (44), and hydrophobic polymer of the layer (42) to melt the hydrophobic polymer.
7. A method of manufacturing a fuel cell (40) comprising the steps of:
a. securing a cathode diffusion layer (20′) to a cathode substrate (24′);
b. securing an anode catalyst (12′) and a cathode catalyst (14′) to opposed surfaces of an electrolyte (16′) to form a membrane electrode assembly;
c. bonding the cathode catalyst (14′) to the cathode diffusion layer (20′); and,
d. bonding the backing layer (42) of claim 1 to the anode catalyst (12′).