Publication numberUS20050121120 A1
Publication typeApplication
Application numberUS 11/034,915
Publication date9 Jun 2005
Filing date14 Jan 2005
Priority date13 Apr 1999
Also published asDE60003654D1, DE60003654T2, EP1171173A1, EP1171173B1, US7087077, WO2000061203A1
Publication number034915, 11034915, US 2005/0121120 A1, US 2005/121120 A1, US 20050121120 A1, US 20050121120A1, US 2005121120 A1, US 2005121120A1, US-A1-20050121120, US-A1-2005121120, US2005/0121120A1, US2005/121120A1, US20050121120 A1, US20050121120A1, US2005121120 A1, US2005121120A1
InventorsBastiaan Van Dijk, Lukas Van Dijk
Original AssigneeElephant Dental B.V., Academisch Ziekenhuis Rotterdam Dijkzigt
Export CitationBiBTeX, EndNote, RefMan
External Links: USPTO, USPTO Assignment, Espacenet
Biomedical aid or implant
US 20050121120 A1
Abstract
The invention relates to a stent manufactured from an alloy which contains at least 60% by weight, based on the weight of the alloy, of one or more metals selected from the group of gold, platinum, palladium and silver, silver being used only in combination with gold, platinum and/or palladium, and the alloy having a yield point of at least 200 N/mm2 and an elongation at break of at least 8%.
Images(6)
Previous page
Next page
Claims(21)
1. (canceled)
2. The method according to claim 9, wherein the weight ratio of gold: palladium is between 3:1 and 0.5:1.
3. The method according to claim 9, wherein the weight ratio of silver: palladium is between 3:1 and 0.3:1.
4. The method according to claim 9, wherein the alloy contains at least 0.5% by weight, based on the weight of the alloy, of one or more metals selected from the group consisting of iridium, indium, gallium, tin, titanium, copper, zinc, and ruthenium.
5. The method according to claim 9, wherein the alloy has a yield point of at least 300 N/m2.
6. The method according to claim 9, wherein the alloy has an elongation at break of at least 20%.
7. The method according to claim 9, wherein the alloy further contains one or more of the metals selected from the group consisting of rhodium, rhenium, cerium, germanium, boron, iron, tantalum, nickel, cobalt, aluminum, niobium, zirconium, manganese, chromium, molybdenum and tungsten.
8. The method according to claim 9, wherein the alloy further contains one or more elements from the group consisting of silicon and carbon.
9. A method of use of an alloy which contains at least 60% by weight, based on the weight of the alloy, of a combination of gold and palladium, or of a combination of silver and palladium, and the alloy having a yield point of at least 200 N/mm2 and an elongation at break of at least 8%, comprising the step of manufacturing a biomedical aid or implant, comprising the alloy, for application in the human body at a site where the aid or implant is not exposed to the atmosphere.
10. A method according to claim 9, wherein the aid or implant is a stent, aneurysm clip, cardiac valve, occlusion coil, suture material, artificial joint or osteosynthesis material.
11. A method of use of an alloy which contains at least 60% by weight, based on the weight of the alloy, of a combination of gold and palladium, or of a combination of silver and palladium, and the alloy having a yield point of at least 200 N/mm2 and an elongation at break of at least 8%, comprising manufacturing a biomedical aid or implant having a structure comprising the alloy for increasing the MR compatibility of the biomedical aid or implant.
12. The method of claim 11, wherein the biomedical aid or implant has a higher MR compatibility than a second biomedical aid or implant which has the same structure as the biomedical aid or implant comprising the alloy but for comprising stainless steel 316 instead of the alloy.
13. The method of claim 11, wherein the biomedical aid or implant has a higher MR compatibility than a second biomedical aid or implant which has the same structure as the biomedical aid or implant comprising the alloy but for comprising nitinol instead of the alloy.
14. The method of claim 11, wherein the biomedical aid or implant has a higher MR compatibility than a second biomedical aid or implant which has the same structure as the biomedical aid or implant comprising the alloy but for comprising tantalum instead of the alloy.
15. The method of claim 9, wherein said manufacturing comprises forming a wire comprising the alloy.
16. The method of claim 9, wherein said manufacturing comprises forming a tube comprising the alloy.
17. The method of claim 11, wherein said manufacturing comprises forming a wire comprising the alloy.
18. The method of claim 11, wherein said manufacturing comprises forming a tube comprising the alloy.
19. The method of claim 11, wherein the weight ratio of gold: palladium is between 3:1 and 0.5:1.
20. The method of claim 11, wherein the weight ratio of silver: palladium is between 3:1 and 0.3:1.
21. The method of claim 11, wherein the alloy contains at least 0.5% by weight, based on the weight of the alloy, of one or more metals selected from the group consisting of iridium, indium, gallium, tin, titanium, copper, zinc, and ruthenium.
Description
  • [0001]
    This invention relates to a biomedical aid or implant. This invention relates in particular to biomedical aids such as stents, aneurysm clips, cardiac valves, occlusion coils, suture materials, artificial joints and osteosynthesis materials.
  • [0002]
    Stents are used in medicine inter alia for treating vascular stenoses and occlusions. In particular after Dotter treatments, stents are introduced into, often constricted or locally occluded, blood vessels to hold them open. Conventional areas of stent application are the coronary arteries in the heart, renal arteries, pelvic arteries and femoral arteries. Since a few years, stents have been used in combination with plastic (so-called stent-grafts) for the treatment of aneurysms, vascular occlusions or constrictions or arteriovenous fistulas.
  • [0003]
    A stent must satisfy a number of requirements. Important, first of all, are the mechanical properties. A stent is typically built up from thin wires or from a tube in which holes are provided, whilst the forces a stent is subject to in, for instance, an artery, can be considerable. Therefore it is important that the stent can resist sufficient pressure, but also that the stent is sufficiently elastic.
  • [0004]
    Further, a stent must be made of biocompatible material, so as not to give rise to hypersensitivity phenomena or even rejection phenomena.
  • [0005]
    For intravascularly used stents, at present, with the growing importance of Magnetic Resonance Imaging (MRI), MR compatibility is important. The stents commercially available at present are manufactured from a metal alloy. The alloys used most are ‘Stainless Steel 316’ and Nitinol. Another material that is sometimes used is tantalum. Particularly Stainless Steel 316, the material used most because of its favorable mechanical properties, induces a local disturbance of the magnetic field used in MRI, to the extent that imaging the blood vessel adjacent the stent is seriously impeded. Although Nitinol and tantalum behave more favorably in MRI, their MR compatibility is not considered to be sufficiently good.
  • [0006]
    Accordingly, there is a need for an improved stent which has the favorable mechanical properties of the known stents, in particular of the stents manufactured of Stainless Steel 316, while at the same time exhibiting minor image artifact in MRI examination. Also, the new stent should be biocompatible.
  • [0007]
    Surprisingly, it has presently been found that the desired properties can be given to a stent by manufacturing it from a specific alloy based on one or more precious metals. Accordingly, the invention relates to a stent manufactured from an alloy which contains at least 60% by weight, based on the weight of the alloy, of one or more metals selected from the group of gold, platinum, palladium and silver, silver being used only in combination with gold, platinum and/or palladium, and the alloy having a yield point of at least 200 N/mm2 and an elongation at break of at least 8%.
  • [0008]
    A stent manufactured from an alloy according to the invention has been found to yield significantly less disturbance of MRI images than does a stent manufactured from the materials conventionally used heretofore. In those cases where the more classic examination methods based on the use of X-rays are still employed, it is of advantage that the alloy of which the present stent is made further has a high radiopacity.
  • [0009]
    Further, the present stent possesses mechanical properties which are at least as good as those of the known stents. Furthermore, the alloy of which the present stent is manufactured has excellent wetting properties and can be processed in a very simple manner. By virtue of the favorable wetting properties, adhesion of substances from the environment takes place to a very minor extent only. It is to be noted here that, moreover, substantially no oxide film is formed on the surface of an object of the alloy, which is considered to be of advantage. Further, the present stent has a very good biocompatibility. It has been found that it is possible to make the stent nickel-free. Nickel is a material which is suspected to provoke allergic reactions in many people when used in vivo.
  • [0010]
    As stated, the alloy of which the present stent is manufactured is a precious metal alloy. At least 60% by weight, preferably at least 75% by weight, based on the weight of the alloy, consists of precious metal. In this connection, by the precious metals are meant the metals gold, platinum, palladium and silver. Of importance is further that silver is not the only precious metal in the alloy. If silver is present, at least one other element from the group of gold, platinum and palladium will be present in the alloy. Preferably, at least 5% by weight, more preferably at least 10% by weight, of gold, platinum and/or palladium is present. It has been found that when these conditions are met, an alloy is provided whose mechanical properties are sufficient for use in stents and other biomedical aids.
  • [0011]
    In a preferred embodiment, the alloy contains a combination of gold and palladium or a combination of silver and palladium. It has been found that through these combinations the alloy attains an optimum in magnetic properties and electrical conductivity. It has been found that to achieve good imaging in MRI, it is desirable that the alloy has a low magnetic susceptibility and a high electrical resistance.
  • [0012]
    When the alloy is based on a combination of gold and palladium, the relative weight ratio between gold and palladium will preferably be between 3:1 and 0.5:1, more preferably between 1.6:1 and 1:1. When the alloy is based on a combination of silver and palladium, the relative weight ratio between silver and palladium will preferably be between 3:1 and 0.3:1; more preferably between 1.3:1 and 0.4:1.
  • [0013]
    In addition to the precious metals referred to, the alloy preferably contains a number of dopes. The total amount of dopes is preferably between 0.5 and 40% by weight, more preferably between 4 and 40% by weight, depending on the amount of precious metal present. It is preferred that the alloy contains only metals, so that the total amount of dopes is preferably adjusted to the amount of precious metals present. Accordingly, in certain cases, the upper limit of the amount of dopes can be 25% by weight.
  • [0014]
    It will be clear that, though less desirable, the presence of very small amounts of impurities cannot be precluded. For instance, it does not constitute an insurmountable objection when very small amounts of silicon or carbon are present. These substances are preferably not present in amounts greater than 1.5% by weight for silicon and 1% by weight for carbon.
  • [0015]
    The dopes are preferably selected from the group of iridium, indium, gallium, tin, titanium, copper, zinc, and ruthenium. The dopes mentioned can be used both separately and in mutual combinations. It has been found that these dopes have a particularly favorable influence on the properties, in particular the mechanical properties, of the alloy. The dopes referred to are preferably present in the following amounts:
      • Iridium up to 30% by weight, more preferably from 0.1 to 10% by weight;
      • Indium up to 20% by weight, more preferably from 1 to 10% by weight;
      • Gallium up to 20% by weight, more preferably from 1 to 10% by weight; Tin up to 20% by weight, more preferably from 1 to 10% by weight;
      • Titanium up to 40% by weight, preferably up to 15% by weight, more preferably from 0.5 to 5% by weight;
      • Copper up to 20% by weight, preferably up to 15/o by weight, more preferably from 1 to 5% by weight;
      • Zinc up to 20% by weight, preferably up to 10% by weight, more preferably from 1 to 6% by weight; and
      • Ruthenium up to 20% by weight, preferably up to 10% by weight, more preferably from 0.1 to 1% by weight.
  • [0023]
    By manufacturing a stent from an alloy which contains these amounts of dopes, excellent mechanical properties are combined with a very minor image artifact in MRI.
  • [0024]
    In addition to the dopes already mentioned, further, a metal can be present, selected from the group of rhodium, rhenium, cerium, germanium, boron, iron, tantalum, nickel, cobalt, aluminum, niobium, zirconium, manganese, chromium, molybdenum and tungsten. These metals too can be used both separately and in combinations. In particular when they are used in the amounts specified hereinafter, these dopes too can have a favorable effect on the alloy properties relevant to the invention. Nonetheless, the effect of these dopes will generally be somewhat less than that of the above-discussed dopes. The preferred amounts of this second group of dopes are:
      • Rhodium up to 30% by weight, preferably up to 10% by weight, more preferably from 0.1 to 1% by weight;
      • Rhenium up to 5% by weight, more preferably from 0.1 to 1% by weight;
      • Cerium up to 5% by weight, more preferably from 0.1 to 1% by weight;
      • Germanium up to 5% by weight, more preferably from 0.1 to 3% by weight; Boron up to 3% by weight, more preferably from 0.1 to 0.5% by weight;
      • Iron up to 5% by weight, more preferably from 0.1 to 3% by weight;
      • Tantalum up to 5% by weight, more preferably from 0.1 to 2% by weight;
      • Nickel up to 30% by weight, more preferably from 1 to 10% by weight, still more preferably entirely absent;
      • Cobalt up to 30% by weight, more preferably from 1 to 10% by weight;
      • Aluminum up to 3% by weight, more preferably from 0.1 to 1% by weight;
      • Niobium up to 15% by weight, more preferably from 1 to 5% by weight;
      • Zirconium up to 5% by weight, more preferably from 0.1 to 2% by weight;
      • Manganese up to 5% by weight, more preferably from 0.1 to 2% by weight;
      • Chromium, molybdenum and tungsten jointly up to 5% by weight, more preferably from 0.1 to 1% by weight.
  • [0038]
    According to the invention, the alloy for manufacturing a stent must have a yield point of at least 200 N/mm2 and an elongation at break of at least 8%. Preferably, the yield point is at least 300 N/mm2 and the elongation at break is at least 20%. It has been found that through a suitable choice of the composition of the alloy, a yield point can be achieved of more than 400 N/mm2 with an elongation at break of about 30%.
  • [0039]
    In the framework of the invention, the yield point is defined as measured according to ISO 6892 on an alloy which has been hard-annealed The elongation at break is defined, according to the invention, as measured according to the same ISO 6892 on an alloy which has been soft-annealed. The conditions under which hard-annealing or soft-annealing occurred, are the optimum conditions for respectively hard- and soft-annealing the composition of the alloy. The artisan will be capable of choosing these on the basis of his ordinary skill in the art. For the measurement of the yield point and the elongation at break, a bar manufactured of the alloy to be measured is loaded incrementally on a tensile strength tester until break. The forces exerted on the bar are graphically represented and the elongation at break is determined by measuring the length of the parallel part of the bar before and after the test. More particularly, the following quantities can be calculated from the results of this test, in the following manner: tensile strength = F max A N / mm 2 ,
    where Fmax is the highest tensile force applied (expressed in Newton) and A is the surface area of the cross section of the parallel part of the bar prior to break (expressed in mm2); yield point = F 1 A N / mm 2 ,
    where F1 is the tensile force (expressed in Newton) at 0.2% permanent elongation; and elongation at break = L 1 - L 0 L 0 * 100 % ,
    where L1 is the length of the parallel part of the bar after the test, and L0 is that same length before the test.
  • [0040]
    On the basis of his ordinary skill in the art, the artisan will be able to choose the composition of the alloy, in particular the nature and amount of the dopes present therein, such that the above-mentioned requirements regarding the mechanical properties are met.
  • [0041]
    The preparation of the alloy, which, incidentally, is known as such for, for instance, applications in dentistry, can be carried out as described in European patent application 0 598 431. Important here is that an alloy of a homogeneous composition is obtained.
  • [0042]
    The known preparation referred to comprises the steps of preparing a melt comprising the desired metals in the desired amounts, casting the melt to form an ingot, homogenizing by tempering, cooling and hardening. Tempering can be carried out at a temperature between 650 and 1200 C. Preferably, tempering is done at a temperature of about 900 C. Cooling is preferably carried out by cooling the tempered alloy in water. To obtain optimum properties, preferably, cooling is done fast (immediately after tempering). Preferably, the cooled alloy is subsequently rolled out to a smaller thickness or drawn into a wire. Rolling preferably occurs in different steps, alternated by a tempering at a temperature of 650-1200 C., preferably about 900 C. The eventual hardening of the alloy preferably occurs at a temperature of 400-700 C., more preferably at a temperature of 500-650 C.
  • [0043]
    Of the alloy, a stent can be formed in a conventional manner. According to the invention, the alloy can be used for manufacturing all known kinds of stents. Examples are stents for arterial applications, such as in the abdominal, pelvic, femoral, cervical, renal and coronary arteries, stents for venous applications, including applications in the venae cavae and application in TIPS (Transjugular Intrahepatic Portosystemic Shunt), stents of the balloon-expandable or self-expandable type, the group formed by covered stents, stent-grafts, and endografts (i.e. stents combined with vascular prosthetic material for treating aneurysmal and stenosing vascular disease including application in abdominal aortic aneurysm), and stents for non-vascular applications, such as hepatobiliary, gastrointestinal, urological and bronchial applications. For a description of examples of different stents, their form and applications, reference is made to Becker G. J., ‘Vascular stents’ and Dake M. D., ‘Transluminal Placement of Endovascular Stent-Grafts for the Treatment of Thoracic Aortic Aneurysms’, both from Abrams' Angiography, Ed. Baum S., Pentecost M. J., Little, Brown & Co., pp. 85-118 and 356-365, respectively, Boston 1997; and Hopkinson B. et al., ‘Endovascular Surgery for Aortic Aneurysms’, Saunders W. B., London 1997.
  • [0044]
    It has further been found that the alloy of which the present stent is manufactured is suitable for manufacturing other biomedical aids or implants. In the framework of the invention, the term ‘biomedical aids or implants’ is understood to include all objects foreign to the body, which are permanently or temporarily deployed in the body. Often, these objects serve to support or replace body functions which have failed wholly or partly, and/or to assist in restoring certain body functions or parts of the body. The aids/implants involved here are particularly those where in a comparable manner the mechanical properties and MRI properties play a role, and which are utilized in the human body at a site where they are not exposed to the atmosphere, which is in effect understood to include all applications not belonging to dentistry.
  • [0045]
    Accordingly, the invention further relates to the use of the above-described alloy for manufacturing such biomedical aids or implants. Examples of such aids/implants comprise aneurysm clips, cardiac valves, occlusion coils (for therapeutic occlusion of arteries, veins and aneurysms), suture materials, artificial joints and osteosynthesis materials, such as screws, pins and plates for the purpose of surgical reconstruction of bone structures.
  • [0046]
    For a description of examples, as well as the applications and possible forms of the aids mentioned, reference is made to Pollak J. S., White R. I., ‘Mechanical Embolic Agents’, Abrams' Angiography, Ed. Baum S., Pentecost M. J., Little, Brown & Co., pp. 55-79, Boston 1997 (occlusion coils); Yasargil, M. G., ‘Microneurosurgery’, George Thieme Verlag, pp. 212-213 and 245-271, New York 1984 (aneurysm clips); Kirlin J. W., Barratt-Boyes B. G., ‘Cardiac Surgery’, 2nd edition, vol. 1, ch. 11, pp. 474-476, Churchill Livingstone Inc., New York 1993 (cardiac valves and sutures); Muller M. E., Allgower M., Schneider R., Willenegger H., ‘Manual of Osteosynthesis’, Springer Verlag 1979 and Browner B. D., Edwards C. C., ‘The Science and Practice of Intramedullary Nailing’, Lea & Febiger 1987 (both bone screws, bone pins and bone plates); and Lemons J. E., ‘Metallic Alloys’ and Rand J. A. et al., ‘Cemented Total Knee Arthroplasty’, both from ‘Joint Replacement Arthroplasty’, Ed. Morrey B. F., Churchill Livingstone, pp. 13-22 and 1007-1021, respectively, New York 1991, and pp. 147-240, 275-329 and 419-436 from the same book (artificial joints).
  • [0047]
    In the above text and the following example, all percentages are by weight and based on the total weight of the alloy, unless specified otherwise.
  • EXAMPLE
  • [0048]
    Analogously to the procedure described in the Example of EP-A-0 598 431, the alloys were prepared with the following compositions:
    Alloy A: Au  0.1% by weight
    Pt  0.5% by weight
    Pd 60.6% by weight
    Ag 28.0% by weight
    Sn  7.3% by weight
    In  2.0% by weight
    Ga  1.2% by weight
    Zn  0.2% by weight
    Ru  0.1% by weight
    Alloy B: Au  2.0% by weight
    Pd 78.9% by weight
    Cu 10.0% by weight
    Ga  9.0% by weight
    Ir  0.1% by weight
    Alloy C: Au 52.0% by weight
    Pd 38.0% by weight
    In  8.2% by weight
    Ga  1.6% by weight
    Ag  0.1% by weight
    Re  0.1% by weight
    Alloy D: Au 77.1% by weight
    Pt  7.7% by weight
    Pd  9.5% by weight
    Ag  2.0% by weight
    In  3.5% by weight
    Ir  0.2% by weight.
  • [0049]
    Of these alloys, the yield point and the elongation at break were determined in accordance with ISO 6892. Further, stents were manufactured from the alloys examined for their biocompatibility, allergenicity, radiopacity, MRI image and wetting picture. For examining biocompatibility, use was made of the standard EN 10993 from 1996, consideration being given inter alia to cytotoxicity and mutagenicity. The stents according to the invention were found to meet the standard. Wetting was tested by polishing a sample and successively dripping equal amounts of water, physiological saline solution and blood on it. The shape of the drop then gives a picture of the wetting (the flatter the drop, the more wetting, and hence more adhesion of substances).
  • [0050]
    The MRI image was determined by placing a stent in a plastic vessel filled with a copper sulfate solution suitable for in vitro MR testing. The concentration of copper sulfate was about 1 gram per liter. With a standard 1.5 Tesla MR scanner and gradient echo sequences (Philips ACS-NT), images of the stents were made and examined for signal loss.
  • [0051]
    The stents of the above alloys according to the invention were compared with commercially available stents for the properties mentioned. The properties of these stents were derived from tables. For Stainless Steel 316 (RVS 316) use was made of the ‘Stahlschlssel’, Verlag Stahlschlussel Wegst GmbH, 1983. The data of Nitinol were derived from ‘Das dental Vademecum’, Deutsche Arzte Verlag, no. 5, 1989. The data of tantalum are based on experimental data obtained by doing tensile tests according to ISO 6892. The results are represented in the tables below.
    TABLE I
    data of stents according to the invention
    Alloy A Alloy B Alloy C Alloy D
    Yield point 560 900 600 600
    (N/mm2)
    Elongation at  28  14  18  8
    break (%)
    Biocompatibility good good good good
    Allergenicity none none none none
    Radiopacity good good good good
    MRI-image very good good good good
    Wetting picture good good good good
  • [0052]
    TABLE II
    data of commercially available stents
    RVS 316* Nitinol** Tantalum***
    Yield point approx. 205 approx. 300 approx. 200
    (N/mm2)
    Elongation at approx. 45 approx. 40 approx. 35
    break (%)
    Biocompatibility reasonable reasonable good
    Allergenicity Nickel-containing Nickel-containing none
    Radiopacity reasonable moderate poor
    MRI-image poor reasonable reasonable
    Wetting picture good moderate poor

    *Wallstent 

    **Memotherm 

    ***Strecker