US20050089639A1 - Continuous plating method of filament bundle and apparatus therefor - Google Patents
Continuous plating method of filament bundle and apparatus therefor Download PDFInfo
- Publication number
- US20050089639A1 US20050089639A1 US10/986,990 US98699004A US2005089639A1 US 20050089639 A1 US20050089639 A1 US 20050089639A1 US 98699004 A US98699004 A US 98699004A US 2005089639 A1 US2005089639 A1 US 2005089639A1
- Authority
- US
- United States
- Prior art keywords
- filament bundle
- processing vessel
- bundle
- passes
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A filament bundle is rewound from a reel, and passes through various sorts of liquid in processing vessels to be used for plating. The filament bundle passes through a fixed guide roller and a movable guide roller while it travels within the liquid in the processing vessel. The movable guide roller is moved periodically, the filament bundle is stretched and slackened by turns, whenever the filament bundle is slackened or untied, the bundle is loosened. The filament bundle with each filament subjected to the plating is taken up to a take-up reel.
Description
- 1. Field of the Invention
- The present invention relates to a method of and an apparatus for applying plating to bundle of filaments or fibers continuously.
- 2. Prior Art
- First Prior Art (JP, 03-51831, B)
- This Prior Art is a method of applying electroplating to a bundle of carbon filaments continuously. A carbon filament bundle is rewound from a reel and then passes through an electrolytic degreasing vessel, a first electroplating vessel and a second electroplating vessel in sequence, and is subjected to electroplating and taken up to a roller. The electroplated carbon filaments are used as a reinforcing material of composite material or for shielding of electromagnetic wave.
- In order to apply electroplating to each carbon filament uniformly, the carbon filament bundle is untied during traveling within liquid of each vessel so that the carbon filaments are not contacted with each other. In the first electroplating vessel and the second electroplating vessel respectively, the electroplating liquid jetting from a nozzle is collided in the perpendicular direction with the carbon filament bundle traveling within the electroplating liquid. Thereby the carbon filament bundle is untied so that the electroplating liquid is easily exchanged between the inside and the outside of the carbon filament bundle. Also in the electrolytic degreasing vessel, the electrolytic degreasing liquid jetting from a nozzle is collided in the perpendicular direction with the carbon filament bundle traveling within the electrolytic degreasing liquid. The carbon filament bundle is untied thereby the electrolytic degreasing liquid is easily exchanged between the inside and the outside of the carbon filament bundle.
- Second Prior Art (JP, 01-156574, A)
- This is a method of applying electroless plating with silver to porous hollow yarns, not to a bundle of filaments. The porous hollow yarns of polyethylene, polypropylene or fluorine-contained resin are wound in loop state and are immersed in a silver salt solution and a reduction solution in sequence and subjected to electroless silver platting. The plated porous hollow yarns are used for filtration.
- Third Prior Art (JP, 2001-40578, A)
- This is a method of manufacturing white electroconductive yarns, not a bundle of plated filaments. In a plating vessel, a tubular shaft having a number of holes is provided. On this tubular shaft, a yarn wound body with yarn of polyester, nylon or acrylic fibers wound thereon is mounted. A plating liquid flows out of the holes of the tubular shaft and passes the yarn wound body from the inside to the outside thereof. An electroless plating of silver or platinum is applied to the yarn of the yarn wound body. The white electroconductive yarn is used for the shielding of the electromagnetic wave.
- The first object of the present invention is to solve the following problems in the first prior art and the third prior art. In the first prior art, in order to untie the carbon filament bundle in the liquid, the liquid jetting from the nozzle is collided with the carbon filament bundle traveling in the liquid. Therefore a pump device is required to supply the liquid at high-pressure state to the nozzle, and the pump device of large scale having large output is necessary In the third prior art, the plating liquid passes from the inside to the outside of the yarn wound body. Therefore the pump device to supply the plating liquid at high-pressure state is required, and the pump device of large scale having large output is necessary.
- The second object of the present invention is to solve the following problems in the second prior art and the third prior art. In the second prior art and the third prior art, the yarn per each definite length is subjected to the electroless plating. This is the batch process and not the continuous process. Therefore the efficiency of the plating is not high.
- The third object of the present invention is to solve the following problems in the first prior art. In the first prior art, the filament, which is subjected to the electroplating, is limited to the carbon filament having electric conductivity. Organic highpolymer filament without electric conductivity such as acrylic resin, aramid, nylon, polyester, rayon, can not be subjected to the electroplating. Further since the carbon filament is only degreased and then subjected to the electroplating, the adhesion property of the electroplating is not high.
- The present invention is as follows.
- 1) In a method of the present invention, a filament bundle is rewound from a reel and passes through various sorts of liquid in processing vessels to be used for plating. While the filament bundle travels within the liquid in the processing vessel it passes through a fixed guide roller and a movable guide roller. The movable guide roller is moved periodically. By the periodic movement of the movable guide roller, the filament bundle becomes stretched and slackened by turns while it travels within the liquid in the processing vessel. Whenever the filament bundle is slackened or untied, the bundle is loosened. The filament bundle with each filament subjected to the plating is taken up to the take-up reel. The filament bundle is plated continuously.
- 2) In the above-mentioned method in 1), the filament bundle passes through an inlet guide roller, an adjustment roller and an outlet guide roller. When the filament bundle is loosened, the adjustment roller gets away from the inlet guide roller and the outlet guide roller, and the slackness amount of the filament bundle is decreased.
- 3) In the above-mentioned method in 1) or 2), the filament bundle is a bundle of organic highpolymer filaments. It passes through an etching processing vessel, a surface adjustment processing vessel for adhering a silane coupling agent to adhere a catalyst, a catalyst processing vessel for adhering the catalyst, an accelerator processing vessel and an electroless plating processing vessel.
- 4) In the above-mentioned method in 3), the organic highpolymer filament bundle passes through an electroplating processing vessel after passing through the electroless plating processing vessel.
- 5) In the above-mentioned method in 1) or 2), the filament bundle is a bundle of carbon filaments. It passes through a catalyst processing vessel an accelerator processing vessel an electroless plating processing vessel and an electroplating processing vessel.
- 6) An apparatus of the present invention is provided with a rewinding part assembling a reel with filament bundle wound thereon, a take-up part assembling a take-up reel, and various sorts of liquid processing vessels to be used for the plating. The filament bundle is rewound from the reel and passes through each processing vessel. The filament bundle with each filament subjected to plating is taken up to the take-up reel. In the processing vessel, a fixed guide roller and a movable guide roller are provided where the filament bundle passes through. A mechanism for moving the position of the movable guide roller periodically is provided. By the periodic movement of the movable guide roller, the filament bundle becomes stretched and slackened by turns while it travels within the liquid in the processing vessel. The above-mentioned method in 1) is performed.
- 7) In the above-mentioned apparatus in 6), the fixed guide roller is arranged at one side within the processing vessel, and the movable guide roller is arranged at another side within the processing vessel. The filament bundle passes through the fixed guide roller at one side and the movable guide roller at another side by turns and is bent.
- 8) In the above-mentioned apparatus in 6) or 7), a mechanism is provided so as to decrease the slackness amount of the filament bundle when the filament bundle is loosened. The slackness decreasing mechanism is provided with an inlet guide roller, an adjustment roller being movable, and an outlet guide roller where the filament bundle passes through, and the adjustment roller is subjected to force in reverse direction to the force to be received from the filament bundle. When the filament bundle is loosened, the adjustment roller gets away from the inlet guide roller and the outlet guide roller, thereby the slackness amount of the filament bundle is decreased.
- The filament bundle becomes stretched and slackened by turns while it travels within the liquid of the processing vessel. Whenever the filament bundle is slackened or untied, the bundle is loosened. The liquid is easily exchanged between the inside and the outside of the filament bundle. The plating is easily applied uniformly to each filament of the filament bundle. The filament bundle with each filament subjected to electroless plating or electroplating uniformly can be manufactured continuously and efficiently.
- In the electroless plating and the electroplating, copper plating, nickel plating, silver plating, palladium plating, gold plating, platinum plating or the like are exemplified.
- In order to repeat the stretch and the slack in the filament bundle during traveling, the position of the movable guide roller may be moved periodically. A drive device of large scale having large output is not required.
- The electroplating can be applied not only to the carbon filament with electric conductivity but also to the organic highpolymer filament without electric conductivity. In the organic highpolymer filament, acrylic resin, aramid, nylon, polyester, rayon, polyphenylene sulfide, polypropylene, polyethylene, vinylon, polyvinyl chloride, vinylidene, acetate, cuprammonium rayon or the like are exemplified. Carbon filament can be subjected to the electroless plating and further subjected to the electroplating. The adhesion property of the electroplating becomes higher.
- When the organic highpolymer filament bundle is subjected to the electroless plating or is subjected to the electroless plating and further subjected to the electroplating, if silane coupling agent is adhered to the filament, adhesion of the catalyst to the filament becomes strong. The adhesion property of the electroless plating or the electroplating becomes higher.
- When the filament bundle is loosened, its slackness amount is decreased. Therefore the tangling of the filament bundle with each other due to the increase of the slackness amount of the filament bundle, the drop of the filament bundle from the guide roller, the contact of the filament bundle with the processing vessel, can be prevented.
-
FIG. 1 is a partly lateral sectional view of a continuous plating apparatus of a filament bundle in an embodiment of the invention; -
FIG. 1A is a partly lateral sectional view of a rewinding part, an etching part, a neutralization part and a surface adjustment part of the apparatus; -
FIG. 1B is a partly lateral sectional plan view of a catalyst part, an accelerator part and an electroless plating part of the apparatus; -
FIG. 1C is a partly lateral sectional plan view of an acid washing part, a first electroplating part and a second electroplating plating of the apparatus; -
FIG. 1D is a plan view of a warm wind drying part and a take-up part of the apparatus; -
FIG. 2 is a sectional view taken in line II-II inFIG. 1A ; -
FIG. 3 is a sectional view taken in line III-III inFIG. 2 ; -
FIG. 4 is a sectional view identical toFIG. 2 when distance between guide rollers at the right side and at the left side is reduced; -
FIG. 5 is an enlarged front view of a slackness decreasing mechanism of the apparatus; and -
FIG. 6 is a sectional view taken in line VI-VI inFIG. 5 . - [Construction of the Plating Apparatus]
- In the plating apparatus of the embodiment, an organic highpolymer filament bundle is subjected to electroless plating and farther subjected to electroplating.
- As shown in
FIG. 1A , the apparatus comprises a rewinding part 1, an etching part 6, aneutralization part 21 and asurface adjustment part 22 provided in one line in sequence. Awater washing part 20 is provided between the etching part 6 and theneutralization part 21. Also between theneutralization part 21 and thesurface adjustment part 22, awater washing part 20 is provided. Travelingdrive parts 4 are provided respectively at the front side and at the rear side of the etching part 6. Also travelingdrive parts 4 are provided respectively at the front side and at the rear side of theneutralization part 21, and also at the front side and at the rear side of thesurface adjustment part 22. - Subsequent to the
surface adjustment part 22, as shown inFIG. 1B , acatalyst part 23, anaccelerator part 24 and anelectroless plating part 25 are provided in one line in sequence. Awater washing part 20 is provided between thesurface adjustment part 22 and thecatalyst part 23. Alsowater washing parts 20 are provided respectively between thecatalyst part 23 and theaccelerator part 24, and between theaccelerator part 24 and theelectroless plating part 25. Travelingdrive parts 4 are provided respectively at the front side and the rear side of thecatalyst part 23. Also travelingdrive parts 4 are provided respectively at the front side and at the rear side of theaccelerator part 24, and at the front side and the rear side of theelectroless plating part 25. - Subsequent to the
electroless plating part 25, as shown inFIG. 1C , anacid washing part 26, afirst electroplating part 31 and asecond electroplating part 33 are provided in one line in sequence. Awater washing part 20 is provided between theelectroless plating part 25 and theacid washing part 26. Also awater washing part 20 is provided between theacid washing part 26 and thefirst electroplating part 31. Travelingdrive parts 4 are provided respectively at the front side and at the rear side of theacid washing part 26. Travelingdrive parts 30 serving as the cathode feeding parts are provided respectively at the front side and at the rear side of thefirst electroplating part 31. Also at the front side and at the rear side of thesecond electroplating part 33, travelingdrive parts 30 serving as the cathode feeding parts are provided respectively. - Subsequent to the
second electroplating part 33, as shown inFIG. 1D , a take-uppart 41 is provided. Awater washing part 20, a warmwater washing part 35 and a warmwind drying part 36 are provided in one line in sequence between thesecond electroplating part 33 and the take-uppart 41. A travelingdrive part 4 is provided between the warmwind drying part 36 and the take-uppart 41. - In the rewinding part 1, as shown in
FIG. 1A , ashaft 2 is provided vertically where a reel r with a filament bundle f wound thereon is mounted rotatably, and aguide roller 3 is provided where the filament bundle f rewound from the reel r passes through. - In each traveling
drive part 4, two drive rollers to grasp the filament bundle f are provided above and below. When both drive rollers are rotated in opposite directions, the filament bundle f travels. - In the etching part 6, as shown in
FIG. 1A , aprocessing vessel 7 to hold an etching liquid is provided, and collectingvessels 8 are provided at the front side and the rear side of theprocessing vessel 7 respectively. On walls at the front side and at the rear side of theprocessing vessel 7 and the collectingvessel 8, as shown inFIG. 2 andFIG. 3 ,slender passage ports 9 are provided respectively where the filament bundle f passes through. Liquid flowing out of thepassage ports 9 at the front side and at the rear side of theprocessing vessel 7 flows into the collectingvessels 8 at the front side and the rear side. A circulation mechanism, which is not shown in the drawings, is provided so that the liquid flowing into the collectingvessels 8 at the front side and the rear side is returned to theprocessing vessel 7. - In the
processing vessel 7, as shown inFIG. 1A , guiderollers 10 are provided vertically at the inside position of thepassage port 9 being inlet of the filament bundle f and at the inside position of thepassage port 9 being outlet of the filament bundle f respectively. Also in theprocessing vessel 7, guiderollers guide rollers 11 at one side and theguide rollers 12 at the other side have equal number and are arranged vertically in equal spacing. Theguide rollers 12 have the position movable in the lateral direction, and are the movable guide rollers. Theguide rollers 11 have the position fixed, and are the fixed guide rollers. - A guide roller moving mechanism is provided so as to move the position of the
movable guide roller 12 periodically. In the guide roller moving mechanism, as shown inFIG. 1A andFIG. 2 , amovable plate 13 is provided at one side in theprocessing vessel 7 and is movable in lateral direction, and theguide rollers 12 are mounted to themovable plate 13 in equal spacing. Themovable plate 13 is connected through acrank mechanism 14 andworm gear mechanism 15 to adrive shaft 16. When thedrive shaft 16 is rotated, as shown inFIG. 2 andFIG. 4 , themovable plate 13 and themovable guide rollers 12 reciprocate in lateral direction. And the distance between theguide roller 12 at one side and the fixedguide roller 11 at other side is increased or decreased periodically. - The
guide rollers 10 at front and rear, and theguide rollers processing vessel 7. - The filament bundle f traveling within the liquid of the
processing vessel 7, as shown inFIG. 1A , passes through theguide roller 10 at the inlet side, and then passes through theguide rollers guide roller 10 at the outlet side. The filament bundle f is bent in lateral direction at plural times in a zigzag way. When themovable guide rollers 11 reciprocate and the distance between theguide roller 12 and the fixedguide roller 11 is increased or decreased periodically, the filament bundle f becomes stretched and slackened by turns during traveling within the liquid of theprocessing vessel 7. The traveling speed of the filament bundle f and the reciprocation speed of themovable guide roller 12 are set so that the slack is generated in the filament bundle f during traveling. - In each of the
water washing parts 20, an air nozzle and a water nozzle are set along the traveling path of the filament bundle f The air flow jetting from the air nozzle and the water flow jetting from the water nozzle collide respectively with the filament bundle f during traveling. - The
neutralization part 21, as shown inFIG. 1A , is provided with aprocessing vessel 7 holding a neutralization liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide roller 12 in similar manner to the etching part 6. However, the number of theguide rollers - The
surface adjustment part 22 is provided with aprocessing vessel 7 holding a surface adjustment liquid, that is, silane coupling agent for adhering a catalyst, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide rollers 12 in similar manner to the etching part 6. - The
catalyst part 23, as shown inFIG. 1B , is provided with aprocessing vessel 7 holding a catalyst liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide rollers 12 in similar manner to the etching part 6. However, the number of theguide rollers - The
accelerator part 24 is provided with aprocessing vessel 7 holding an accelerator liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide roller 12 in similar manner to the etching part 6. - The
electroless plating part 25 is provided with aprocessing vessel 7 holding an electroless plating liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide roller 12 in similar manner to the etching part 6. However, the number of theguide rollers - The
acid washing part 26, as shown inFIG. 1C , is provided with aprocessing vessel 7 holding an acid washing liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide rollers 12 in similar manner to the etching part 6. However, the number of theguide rollers - The traveling
drive part 30 serving as the cathode feeding part is the same as the travelingdrive part 4 except that the drive roller serves as a cathode feeding part of an electroplating power source. In the travelingdrive part 30, the filament bundle f contacts with the drive roller serving as a cathode feeding part during traveling. - The
first electroplating part 31 is provided with aprocessing vessel 7 holding a first electroplating liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide rollers 12 in similar manner to the etching part 6. Further, ananode feeding part 32 corresponding to thecathode feeding part 30 serving as a traveling drive part is provided within theprocessing vessel 7. - The
second electroplating part 33 is provided with aprocessing vessel 7 holding a second electroplating liquid, collectingvessels 8,passage ports 9, guiderollers mechanism 13 to 16 for theguide roller 12, and ananode feeding part 32 in similar manner to thefirst electroplating part 31. - The warm
water washing part 35, as shown inFIG. 1C , is provided with an air nozzle and a warm water nozzle along a traveling path of the filament bundle f. An air flow jetting from the air nozzle and a warm water flow jetting from the warm water nozzle collide respectively with the filament bundle f during traveling. The warmwind drying part 36, as shown inFIG. 1D , is provided with a warm wind nozzle along the traveling path of the filament bundle f. A warm wind jetting from the warm wind nozzle collides with the filament bundle f during traveling. - In the take-up
part 41, as shown inFIG. 1D , amechanism 42 for decreasing the slackness amount of the filament bundle f during loosening of the filament bundle f is provided, and adrive shaft 43 assembling a take-up reel R is provided laterally. An apparatus, which is not shown in the drawings, is provided so as to rotate thedrive shaft 43. The filament bundle f with each filament subjected to electroplating passes through theslackness decreasing mechanism 42 and is taken up to the take-up reel R which is assembled to thedrive shaft 43. - The
slackness decreasing mechanism 42, as shown inFIG. 5 , is provided with aninlet guide roller 45 and anoutlet guide roller 46 at the inlet side and the outlet side. Twoguide columns 47 are provided at the inlet side and the outlet side with amovable body 48 being in movable vertically. Anadjustment roller 49 is mounted to themovable body 48. Theadjustment roller 49 is in movable vertically at lower position between theinlet guide roller 45 and theoutlet guide roller 46. Theinlet guide roller 45, theoutlet guide roller 46 and theadjustment roller 49 are provided with peripheral grooves where the filament bundle f passes. - The filament bundle f passes through upper side of the
inlet guide roller 45, lower side of theadjustment roller 49 and upper side of theoutlet guide roller 46 in sequence. In themovable body 48 and theadjustment roller 49, the weight of their own, that is, the downward force acts, also the upward force acts from the filament bundle f When the filament bundle f is loosened, themovable body 48 and theadjustment roller 49 are lowered by the weight of their own, and theadjustment roller 49 gets away from theinlet guide roller 45 and theoutlet guide roller 46, and the slackness amount of the filament bundle f is decreased. Tangling of the filament bundle f with each other due to the increase of the slackness amount, the drop of the filament bundle f from theguide rollers processing vessel 7 or the like can be prevented. - When the
movable body 48 andadjustment roller 49 reach the lower limit, that is, the far point, as shown in solid line inFIG. 5 , themovable body 48 operates a far point detection switch 50. When the switch 50 is operated, thedrive shaft 43 is rotated and the take-up reel R assembled to thedrive shaft 43 is rotated. Then the filament bundle f is taken up to the take-up reel R, and themovable body 48 and theadjustment roller 49 rise and gets close to theinlet guide roller 45 and theoutlet guide roller 46. When themovable body 48 and theadjustment roller 49 reach the upper limit, that is, the near point, as shown in chain line inFIG. 5 , themovable body 48 operates a nearpoint detection switch 51. When theswitch 51 is operated, thedrive shaft 43 is stopped and the take-up reel R is stopped. Then the take-up of the filament bundle f is stopped and the rise of themovable body 48 and theadjustment roller 49 is stopped. Again when the filament bundle f is loosened, theadjustment roller 49 gets away from theinlet guide roller 45 and theoutlet guide roller 46, and the slackness amount of the filament bundle f is decreased. - The
slackness decreasing mechanism 42 is provided with an adjustment mechanism for adjusting the slackness decrease amount. In the adjustment mechanism, as shown inFIG. 5 andFIG. 6 , apulley 52 is provided at the upper position of themovable body 48 and arope 53 is hung to thepulley 52. One end of therope 53 is connected to themovable body 48, and the other end is connected to aweight 54. The total weight of themovable body 48 and theadjustment roller 49 is heavier than that of theweight 54. Themovable body 48 and theadjustment roller 49 are moved downward by the force of the total weight subtracted by theweight 54, and the force pulls the filament bundle f. When the force for theadjustment roller 49 to pull the filament bundle f becomes large, the slackness decrease amount is increased. That is, the increase or decrease of the weight of theweight 54 can adjust the slackness decrease amount. - [Use Method of Plating Apparatus, Plating Method]
- In the take-up
part 41, an empty take-up reel R is assembled. In the rewinding part 1, a reel r with a filament bundle f wound thereon is assembled. The filament bundle f is rewound from the reel r. The filament bundle f passes through the parts arranged between the rewinding part 1 and the take-uppart 41 in sequence, and is connected to the take-up reel R of the take-uppart 41. Eachprocessing vessel 7 is supplied with a processing liquid. In thefirst electroplating part 31 and thesecond electroplating part 33 respectively, thecathode feeding part 30 and theanode feeding part 32 are energized. In each of the travelingdrive parts - Also the
drive shaft 16, which is common to the etching part 6, theneutralization part 21, thesurface adjustment part 22, thecatalyst part 23, theaccelerator part 24, theelectroless plating part 25, theacid washing part 26, thefirst electroplating part 31 and thesecond electroplating part 33, is rotated. In these parts, themovable guide rollers 12 reciprocate and move synchronously. - When the plating apparatus operates, the filament bundle f is rewound from the reel r in the rewinding part 1, and passes through the traveling
drive part 4 and further passes through the etching part 6. - In the etching part 6, the filament bundle f travels within the etching liquid in the
processing vessel 7, and passes through theguide roller 10 at the inlet side, as shown inFIG. 1A , and passes through theguide rollers guide roller 10 at the outlet side. Themovable guide rollers 12 reciprocate, and the distance between themovable guide roller 12 and the fixedguide roller 11 is increased or decreased periodically. The filament bundle f becomes stretched and slackened by turns while it travels within the etching liquid in theprocessing vessel 7. Whenever the filament bundle f is slackened or untied, the bundle is loosened and the etching liquid is exchanged between the inside and the outside of the bundle. Each filament of the filament bundle f is subjected to the etching processing uniformly. After the etching processing, the filament bundle f passes through the travelingdrive part 4 and then passes through thewater washing part 20, and is washed by the air and the water in thewater washing part 20. The filament bundle f passes through the travelingdrive part 4 and then passes through theneutralization part 21. - In the
neutralization part 21, the filament bundle f travels within the neutralization liquid in theprocessing vessel 7, and passes through theguide roller 10 at the inlet side, and passes through theguide rollers guide roller 10 at the outlet side. Themovable guide rollers 12 move in reciprocation, and distance between theguide rollers drive part 4 and then passes through thewater washing part 20, and is washed in thewater washing part 20. The filament bundle f passes through the travelingdrive part 4 and passes through thesurface adjustment part 22. - In the
surface adjustment part 22, the filament bundle f travels within the silane coupling agent for adhering the catalyst, that is, the surface adjustment liquid in theprocessing vessel 7, and passes through theguide roller 10 at the inlet side, and through theguide rollers guide roller 10 at the outlet side in sequence. Themovable guide rollers 12 move in reciprocation periodically. The filament bundle f becomes stretched and slackened by turns, and every time the bundle is untied, the bundle is loosened and the surface adjustment liquid is exchanged between the inside and the outside of the bundle. Each filament is subjected to the surface adjustment processing uniformly. After the surface adjustment, the filament bundle f passes thought the travelingdrive part 4 and then passes through thewater washing part 20, and passes thought the travelingdrive part 4 and then passes through thecatalyst part 23. - In the
catalyst part 23, the filament bundle f travels within the catalyst liquid in theprocessing vessel 7, and as shown inFIG. 1B , it passes through theguide rollers movable guide rollers 12 move in reciprocation periodically. The filament bundle f is stretched and slackened by turns, and every time the bundle is untied, the bundle is loosened and the catalyst liquid is exchanged between the inside and the outside of the bundle. Each filament is subjected to the catalyst processing uniformly. After the catalyst processing, the filament bundle f passes through the travelingdrive part 4 and thewater washing part 20, and passes through the travelingdrive part 4 and then passes through theaccelerator part 24. - In the
accelerator part 24, the filament bundle f travels within the accelerator liquid in theprocessing vessel 7 and passes through theguide rollers movable guide rollers 12 move in reciprocation periodically. The filament bundle f is stretched and slackened by turns, and every time the bundle is untied, the bundle is loosened and the accelerator liquid is exchanged between the inside and the outside of the bundle. Each filament is subjected to the accelerator processing uniformly. After the accelerator processing, the filament bundle f passes through the travelingdrive part 4, thewater washing part 20 and the travelingdrive part 4, and passes through theelectroless plating part 25. - In the
electroless plating part 25, the filament bundle f travels within the electroless plating liquid in theprocessing vessel 7, and passes through theguide rollers drive part 4, thewater washing part 20 and the travelingdrive part 4, and then passes through theacid washing part 26. - In the
acid washing part 26, the filament bundle f travels within the acid washing liquid in theprocessing vessel 7, and passes through theguide rollers drive part 4 and thewater washing part 20. And it passes through the travelingdrive part 30 at the inlet side serving as the cathode feeding part of thefirst electroplating part 31, and then passes through thefirst electroplating part 31 and the travelingdrive part 30 at the outlet side serving as the cathode feeding part of thefirst electroplating part 31. - In the
first electroplating part 31, the filament bundle f travels within the first electroplating liquid above theanode feeding part 32 in theprocessing vessel 7, and passes through theguide rollers drive part 30 at the inlet side serving as the cathode feeding part of thesecond electroplating part 33, and then passes through thesecond electroplating part 33 and the travelingdrive part 30 at the outlet side serving as the cathode feeding part of thesecond electroplating part 33. - In the
second electroplating part 33, the filament bundle f travels within the second electroplating liquid above theanode feeding part 32 in theprocessing vessel 7, and passes through theguide rollers - After the second electroplating is applied, the filament bundle f passes through the
water washing part 20, and then passes through the warmwater washing part 35 and is washed by the air and the warm water. Subsequently it passes through the warmwind drying part 36 and is dried by the warm wind. The filament bundle f passes through the travelingdrive part 4 and reaches the take-uppart 41. - In the take-up
part 41, the filament bundle f passes through theslackness decreasing mechanism 42 and is taken up to the take-up reel R. The filament bundle with each filament subjected to electroplating uniformly can be manufactured continuously and efficiently. - The filament bundle f is a bundle of polyester filaments of one hundred to several hundreds in number. The traveling speed of the filament bundle f is 50 cm per minute. In the
movable guide rollers 12, the reciprocating stroke is 10 cm and the reciprocating frequency is 3 to 4 times per minute. The distance between themovable guide roller 12 and the fixedguide roller 11 is about 50 cm. - The etching liquid is an aqueous solution in 5% of sodium hydroxide (NaOH), in which the temperature is 45 degrees C. and the immersion time is 5 minutes. The neutralization liquid is an aqueous solution in 5% of hydrochloric acid (HCl), in which the temperature is room temperature and the immersion time is 2 minutes.
- The silane coupling agent for adhering the catalyst, the surface adjustment liquid is an aqueous solution in 0.1% of alfa-aminoethyltriethoxy silane, in which the temperature is 50 degrees C. and the immersion time is 5 minutes. The catalyst liquid includes palladium chloride (PdCl2) 0.1 g, tin dichloride (SnCl2) 15 g and hydrochloric acid (HCl) 200 ml per 1 liter of the aqueous solution, in which the temperature is 40 degrees C. and the immersion time is 3 minutes. The accelerator liquid is an aqueous solution in 10% of sulfuric acid (H2SO4), in which the temperature is 40 degrees C. and the immersion time is 3 minute.
- The electroless plating liquid is for copper (Cu) plating, and includes copper sulfate (CuSO4.5H2O) 10 g, potassium sodium tartrate (C4H4O6KNa.4H2O, Rochelle Salt) 100 g, sodium hydroxide (NaOH) 12 g, formalin (HCHO) 20 ml and stabilizer of little amount per 1 liter of the aqueous solution, in which the temperature is 35 degrees C. and the immersion time is 15 minutes. The acid washing liquid is an aqueous solution in 10% of sulfuric acid (H2SO4), in which the temperature is room temperature and the immersion time is 1 minute.
- The first electroplating liquid and the second electroplating liquid are for copper (Cu) plating, and each includes copper sulfate (CuSO4.5H2O) 200 g and sulfuric acid (H2SO4) 50 g per 1 liter of the aqueous solution, in which the temperature is room temperature and the immersion time is 10 minutes. The current density is 0.5 A/dm2 in the first electroplating liquid and 2 A/dm2 in the second electroplating liquid.
- In the polyester filament bundle, each filament is subjected to electroplating of copper of 4 micro m thickness. The electroplating of copper was not peeled off in the tape test.
- The filament bundle f is a bundle of aramid filaments of one hundred to several hundreds in number. The traveling speed is 60 cm per minute. In the
movable guide rollers 12, the reciprocating stroke is 5 cm and the reciprocating frequency is 6 to 8 times per minute. The distance between themovable guide roller 12 and the fixedguide roller 11 is about 50 cm. - The etching liquid is an aqueous solution of chromic acid anhydride (CrO3) 30% and sulfuric acid (H2SO4) 15%, in which the temperature is 50 degrees C. and the immersion time is 5 minutes. The neutralization liquid is an aqueous solution in 10% of sodium bisulfate or sodium acid bisulfate (NaHSO3), in which the temperature is room temperature and the immersion time is 2 minutes.
- The silane coupling agent for adhering the catalyst, the surface adjustment liquid, the catalyst liquid and the accelerator liquid are the same as that in the Example 1 respectively.
- The electroless plating liquid is for nickel (Ni) plating, and includes nickel sulfate (NiSO4.7H2O) 20 g, sodium hypophosphate (NaPH2O2.H2O) 20 g, sodium citrate (Na3C6H5O7.2H2O) 40 g, aqua ammonia (NH3) 10 ml and stabilizer of little amount per 1 liter of the aqueous solution, in which the temperature is 30 degrees C. and the immersion time is 10 minutes. The acid washing liquid is the same as that in the Example 1.
- The first electroplating liquid and the second electroplating liquid are for nickel (Ni) plating, and each includes nickel sulfate (NiSO4.7H2O) 280 g, nickel chloride (NiCl2temperature is 50 degrees C. and the immersion time is 10 minutes. The current density is 0.5 A/dm2 in the first electroplating liquid and 2 A/dm2 in the second electroplating liquid.
- In the aramid filament bundle, each filament is subjected to electroplating of nickel of 6 micro m thickness. The electroplating of nickel was not peeled off in the tape test.
- The filament bundle f is a bundle of rayon filaments of one hundred to several hundreds in number. The traveling speed is 70 cm per minute. In the
movable guide rollers 12, the reciprocating stroke is 10 cm and the reciprocating frequency is 4 to 5 times per minute. The distance between themovable guide roller 12 and the fixedguide roller 11 is about 50 cm. - The etching liquid is an aqueous solution in 3% of sodium hydroxide (NaOH), in which the temperature is 45 degrees C. and the immersion time is 5 minutes. The neutralization liquid is an aqueous solution in 3% of hydrochloric acid (HCl), in which the temperature is room temperature and the immersion time is 2 minutes.
- The silane coupling agent for adhering the catalyst, the surface adjustment liquid, the catalyst liquid and the accelerator liquid are the same as that in the Example 1 respectively. The electroless plating liquid is for copper (Cu) plating, and is the same as that in the Example 1. The acid washing liquid is the same as that in the Example 1.
- The first electroplating liquid and the second electroplating liquid are for silver (Ag) plating, and each includes silver cyanide (AgCN) 60 g and potassium cyanide (KCN) 160 g per 1 liter of the aqueous solution, in which the temperature is room temperature and the immersion time is 7 minutes. The current density is 0.5 A/dm2 in the first electroplating liquid and 1 A/dm2 in the second electroplating liquid.
- In the rayon filament bundle, each filament is subjected to electroplating of silver of 5 micro m thickness. The electroplating of silver was not peeled off in the tape test.
- The filament bundle f is a bundle of polyphenylene sulfide filaments of one hundred to several hundreds in number. The traveling speed is the same as that in the Example 3. In the
movable guide rollers 12, the reciprocating stroke and the reciprocating frequency are the same as those in the Example 3. - The etching liquid is a solution of nitric acid (HNO3) that ammonium acid fluoride (NH4HF2) 130 g is added per 1 liter of the nitric acid, in which the temperature is 40 degrees C. and the immersion time is 5 minutes. The neutralization liquid is an aqueous solution in 1% of sodium hydroxide (NaOH), in which the temperature is room temperature and the immersion time is 2 minutes.
- The silane coupling agent for adhering the catalyst, the surface adjustment liquid, the catalyst liquid and the accelerator liquid are the same as those in the Example 1 respectively.
- The electroless plating liquid is for silver (Ag) plating, and comprises a first electroless plating liquid and a second electroless plating liquid. In the plating apparatus, the
electroless plating part 25 comprises a first electroless plating part of which processing liquid is the first electroless plating liquid, and a second electroless plating part of which processing liquid is the second electroless plating liquid. The filament bundle f passes through the first electroless plating part and the second electroless plating part in sequence. The first electroless plating liquid includes silver nitrate (AgNO3) 9 g and ammonium sulfate ((NH4)2SO4) 50 g per 1 liter of the aqueous solution, in which the temperature is room temperature and the immersion time is 10 minutes. The second electroless plating liquid includes formalin (HCHO) 50 mL in which the temperature is room temperature and the immersion time is 10 minutes. - The acid washing liquid is the same as that in the Example 1. The first electroplating liquid and the second electroplating liquid are the same as those in the Example 3 respectively.
- In the polyphenylene sulfide filament bundle, each filament is subjected to electroplating of silver of 5 micro m thickness. The electroplating of silver was not peeled off in the tape test.
- The filament bundle f is a bundle of carbon filaments of one hundred to several hundreds in number. The traveling speed is the same as that in the Example 1. In the
movable guide rollers 12, the reciprocating stroke and the reciprocating frequency are the same as those in the Example 1. - The etching liquid and the neutralization liquid are not used. In the plating apparatus, the etching liquid is not supplied to the etching part 6, and the neutralization liquid is not supplied to the
neutralization part 21. The filament bundle f passes through the etching part 6 of which theprocessing vessel 7 is empty, and theneutralization part 21 of which theprocessing vessel 7 is empty. Or the plating apparatus is not provided with the etching part 6 and theneutralization part 21. The filament bundle f passes through thesurface adjustment part 22 without passing the etching part 6 and theneutralization part 21. - The surface adjustment liquid, the catalyst liquid and the accelerator liquid are the same as those in the Example 1 respectively. The electroless plating liquid, the acid washing liquid, the first electroplating liquid and the second electroplating liquid are the same as those in the Example 1 respectively.
- In the carbon filament bundle, each filament is subjected to electroplating of copper of 4 micro m thickness. The electroplating of copper was not peeled off in the tape test.
Claims (9)
1. A method of continuous plating of filament bundle in which
a filament bundle is unwound from a reel,
the filament bundle passes through various sorts of liquid in processing vessels to be used for plating,
the filament bundle passes through a fixed guide roller and a movable guide roller while it travels within the liquid in the processing vessel, the movable guide roller is moved periodically, the filament bundle is stretched and slackened by turns, whenever the filament bundle is slackened or untied, the bundle is loosened,
the filament bundle with each filament subjected to the plating is taken up to a take-up reel.
2. A method according to claim 1 , wherein said filament bundle further passes through an inlet guide roller, an adjustment roller and an outlet guide roller, and when the filament bundle is loosened, the adjustment roller gets away from the inlet guide roller and the outlet guide roller, and the slackness amount of the filament bundle is decreased.
3. A method according to claim 1 , wherein said filament bundle is a bundle of organic highpolymer filaments, and passes through an etching processing vessel, a surface adjustment processing vessel for adhering a silane coupling agent to adhere a catalyst, a catalyst processing vessel for adhering the catalyst, an accelerator processing vessel and an electroless plating processing vessel.
4. A method according to claim 2 , wherein said filament bundle is a bundle of organic highpolymer filaments, and passes through an etching processing vessel, a surface adjustment processing vessel for adhering a silane coupling agent to adhere a catalyst, a catalyst processing vessel for adhering the catalyst, an accelerator processing vessel and an electroless plating processing vessel.
5. A method according to claim 3 , wherein said organic highpolymer filament bundle passes through an electroplating processing vessel after passing through the electroless plating processing vessel.
6. A method according to claim 4 , wherein said organic highpolymer filament bundle passes through an electroplating processing vessel after passing through the electroless plating processing vessel.
7. A method according to claim 1 , wherein said filament bundle is a bundle of carbon filaments, and passes through a catalyst processing vessel, an accelerator processing vessel, an electroless plating processing vessel and an electroplating processing vessel.
8. A method according to claim 2 , wherein said filament bundle is a bundle of carbon filaments, and passes through a catalyst processing vessel, an accelerator processing vessel, an electroless plating processing vessel and an electroplating processing vessel.
9-12. (canceled)