US20040248415A1 - Polishing method and polishing liquid - Google Patents
Polishing method and polishing liquid Download PDFInfo
- Publication number
- US20040248415A1 US20040248415A1 US10/485,349 US48534904A US2004248415A1 US 20040248415 A1 US20040248415 A1 US 20040248415A1 US 48534904 A US48534904 A US 48534904A US 2004248415 A1 US2004248415 A1 US 2004248415A1
- Authority
- US
- United States
- Prior art keywords
- polishing
- workpiece
- weight
- nitride film
- less
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- The present invention relates to a polishing method and a polishing liquid, and more particularly to a polishing method and a polishing liquid for polishing a workpiece such as a semiconductor wafer with a fixed abrasive.
- As semiconductor devices become more highly integrated in recent years, circuit interconnections have become finer and distance between those circuit interconnections becomes smaller. In case of photolithography which can form interconnections that are at most 0.5 μm wide, it is required that surfaces on which pattern images are to be focused by a stepper should be as flat as possible because a depth of focus of an optical system is relatively small. A polishing apparatus for performing chemical mechanical polishing (CMP) has been used for planarizing a semiconductor wafer.
- This type of chemical mechanical polishing (CMP) apparatus comprises a polishing table having a polishing pad attached thereon, and a top ring. A workpiece to be polished is disposed between the polishing pad and the top ring and pressed against the polishing table by the top ring, while a polishing liquid (slurry) is being supplied onto the polishing pad, and hence the workpiece is polished to a flat mirror finish.
- The CMP apparatus is used in an STI (Shallow Trench Isolation) forming process for forming a transistor circuit on a lowermost layer of a semiconductor device, for example. FIGS. 3A through 3F are schematic cross-sectional views showing an example of the STI forming process. A nitride film110 (generally, a film of silicon nitride Si3N4) is formed on a silicon substrate 100 (see FIG. 3A), and the
silicon substrate 100 is etched using thenitride film 110 as a mask, thus forming a trench (groove) 120 (see FIG. 3B). Then, asilicon oxide film 130 made of an insulating material is embedded in the trench 120 (see FIG. 3C). - When the
silicon oxide film 130 is embedded in thetrench 120, since an excessive layer of thesilicon oxide film 130 is left on the surface as shown in FIG. 3C, the excessive layer of thesilicon oxide film 130 is removed by CMP, thereby exposing the surface of the nitride film 110 (see FIG. 3D). Then, thenitride film 110 is etched away, thus forming agroove 130 a of the silicon oxide film (see FIG. 3E). Atransistor 140 is then formed usingsuch groove 130 a of the silicon oxide film (see FIG. 3F). - In the STI forming process described above, the purpose of the polishing step using CMP is to completely remove the excessive silicon oxide film formed on the nitride film. If the excessive silicon oxide film is not removed completely, then the subsequent etching of the nitride film will be impaired.
- However, the polishing step in the above-mentioned conventional STI forming process employs a polyurethane-based polishing pad and a slurry with silica abrasive particles dispersed therein. Since the
nitride film 110 is less liable to be polished than thesilicon oxide film 130, thesilicon oxide film 130 is excessively polished, thus developing dishing as shown in FIG. 4. Furthermore, the nitride film tends to be polished unevenly, resulting in insufficient within-wafer uniformity. In the STI forming process, it is necessary to strictly control the thicknesses of the nitride film and the silicon oxide film in the trench, i.e., to uniformize the film thickness within the surface of the wafer, and it is important to suppress dishing for within-wafer uniformity. - Recently, it has been attempted to solve the above problems by polishing wafers using a polyurethane-based polishing pad and a slurry with ceria abrasive particles dispersed therein, while adding a trace amount of a high concentration surface-active agent. If the dishing amount developed using a silica slurry is 500 Å, for example, then the dishing amount can be reduced to a range from 200 to 300 Å by this process. However, this process cannot eliminate the above dishing completely because it also uses the soft polishing pad. Another problem of this process is that the high concentration surface-active agent causes ceria to agglomerate, and that the agglomerated ceria scratches the wafer.
- In an effort to solve the problems of the polishing processes using an abrasive liquid (slurry) containing abrasive particles and a soft polishing pad, there has been proposed a polishing process using a fixed abrasive as disclosed in Japanese laid-open patent publication No. 2000-173955. Specifically, in Japanese laid-open patent publication No. 2000-173955, there has been proposed a process for polishing a wafer with a fixed abrasive containing ceria and a polishing liquid which contains 1% by weight of ammonium polyacrylate having a molecular weight of 10000, and has an alkaline pH value. The purpose of this process is to increase the polishing rate by making the pH alkaline to sufficiently increase the dispersion of dropped abrasive particles. However, because ammonium polyacrylate to be added has a relatively high concentration, aggregation is liable to occur, and hence it is difficult to sufficiently prevent scratches from occurring. Further, since the pH is alkaline, it is difficult to suppress dishing and obtain good within-wafer uniformity.
- The present invention has been made in view of the above problems in the prior art. It is therefore an object of the present invention to provide a polishing method and a polishing liquid which can suppress dishing in a workpiece having a nitride film and an oxide film formed on the nitride film, and obtain within-wafer uniformity.
- In order to solve the problems in the prior art, according to a first aspect of the present invention, there is provided a polishing method for polishing a workpiece by pressing the workpiece to be polished against a fixed abrasive and bringing the workpiece in sliding contact with the fixed abrasive, the polishing method comprising: polishing the workpiece while supplying a polishing liquid which contains an anionic surface-active agent and does not contain abrasive particles.
- The concentration of the anionic surface-active agent in the polishing liquid is preferably 0.001% by weight to 5% by weight, more preferably 0.001% by weight to 0.15% by weight. The pH of the polishing liquid is preferably 5 to 10, more preferably 4 to 6.5. Further, the anionic surface-active agent preferably contains an organic compound having a hydrophilic group selected from COO− group and SO3 − group. Further, the workpiece preferably has a nitride film and a silicon oxide film deposited on the nitride film.
- Furthermore, the anionic surface-active agent is preferably polyacrylic acid and/or its salt having a weight average molecular weight of not less than 13000 and not more than 60000.
- In the neutral to acidic pH region of the polishing liquid, the surfaces of the abrasive particles of the fixed abrasive and the surface of the nitride film are principally charged positively (though part of the surfaces possess a negative charge, a positive charge is predominant). Accordingly, the anionic surface-active agent supplied onto the fixed abrasive strongly adheres to the surfaces of the abrasive particles of the fixed abrasive and to the surface of the nitride film electrically. Since the abrasive particles of the fixed abrasive and the nitride film are both covered with the anionic surface-active agent to interact repulsively. Therefore, polishing of the nitride film is hard to proceed and the polishing rate of the nitride film becomes extremely low. The polishing selectivity is, for example, oxide film:nitride film=10 or higher:1, and the nitride film acts as a polishing stopper. Since the polishing rate of the nitride film is extremely lowered and stock removal decreases, the resulting nitride film can be prevented from becoming uneven in the film thickness and within-wafer uniformity of the nitride film can be obtained.
- At this point, it may be considered that because of the above-described polishing selectivity, the nitride film is not polished and only the silicon oxide film is polished, and the above-described dishing will proceed. In fact, however, dishing does not proceed, and depth of the dishing amount can be controlled, for example, within 100 Å or less. This is considered to be due to the following reasons:
- {circle over (1)} The anionic surface-active agent adheres not only to the surface of the nitride film, but also to the silicon oxide film in small amount, whereby a coat of the anionic surface-active agent is formed on the surface of the silicon oxide film. When a surface pressure having a certain value or more is applied to the silicon oxide, a coat on the surface of the silicon oxide film breaks or becomes fragile, and therefore polishing of the silicon oxide film proceeds. As the polishing proceeds to a certain extent, however, the level of the surface of the silicon oxide film becomes lower than that of the nitride film. Accordingly, the surface pressure on the silicon oxide film decreases, and hence a coat of the anionic surface-active agent is formed thick on the silicon oxide film and the progress of polishing is retarded.
- {circle over (2)} Since the anionic surface-active agent used here is a polymer, the anionic surface-active agent, which has adhered to the nitride film, covers part or a considerable area of the trench portion, and hence polishing of the silicon oxide film by the abrasive particles in the fixed abrasive is impeded.
- Further, according to the polishing method of the present invention, the concentration of the anionic surface-active agent in the polishing liquid is made low so that the abrasive particles, which have dropped out of the fixed abrasive, do not agglomerate and thus the formation of scratches can be reduced.
- Further, the present invention uses a fixed abrasive as a polishing surface. A fixed abrasive provides a hard polishing surface which hardly deforms elastically. Such a polishing surface, as compared to a conventional polishing pad having elasticity, is less likely to cause dishing and can provide a flatter finished surface.
- Thus, according to the present invention, polishing of a workpiece is carried out while supplying the polishing liquid which contains an anionic surface-active agent at a low concentration and does not contain abrasive particles, and has an acidic pH, onto the fixed abrasive, whereby a nitride film, for example, is allowed to act as a polishing stopper. Accordingly, the polishing method of the present invention can lower the polishing rate of a nitride film to obtain within-wafer uniformity of the nitride film and can suppress dishing, thus enabling a high-flatness polishing with fewer scratches.
- FIG. 1 is a plan view showing an overall construction of a polishing apparatus according to an embodiment of the present invention;
- FIG. 2 is a front view of the polishing chamber of FIG. 1;
- FIGS. 3A through 3F are schematic views showing an example of an STI forming process; and
- FIG. 4 is a schematic view showing dishing caused by a conventional polishing apparatus.
- A polishing apparatus according to embodiments of the present invention will be described in detail below with reference to the drawings. FIG. 1 is a plan view showing a whole arrangement of a polishing apparatus according to an embodiment of the present invention.
- As shown in FIG. 1, the polishing apparatus comprises four load/unload
stages 2 each for receiving awafer cassette 1 which accommodates a number of semiconductor wafers. The load/unloadstages 2 may have a lifting and lowering mechanism. Atransfer robot 4 is provided onrails 3 so that thetransfer robot 4 can access therespective wafer cassettes 1 on the respective load/unloadstages 2. - The
transfer robot 4 has upper and lower hands. The lower hand of thetransfer robot 4 is a vacuum attraction-type hand for holding a semiconductor wafer under vacuum, and is used only for removing a semiconductor wafer from awafer cassette 1. The vacuum attraction-type hand can hold and transport the semiconductor wafer even if the semiconductor wafer is not located at a normal position in the wafer cassette due to a slight displacement. The upper hand of thetransfer robot 4 is a recess support-type hand for supporting a peripheral edge of a wafer, and is used only for returning the semiconductor wafer to thewafer cassette 1. The recess support-type hand can transport the semiconductor wafer while keeping the semiconductor wafer clean because dust is not collected, unlike the vacuum attraction-type hand. In this manner, since a clean wafer which has been cleaned is held by the upper hand, the clean semiconductor wafer is not further contaminated. - Two
cleaning units wafer cassettes 1 with respect to therails 3 of thetransfer robot 4. Thecleaning units transfer robot 4. Each of thecleaning units - Between the two
cleaning units wafer station 12 having four semiconductor wafer supports 7, 8, 9 and 10 is disposed at a position accessible by thetransfer robot 4. Atransfer robot 14 having two hands is disposed at a position where hands of thetransfer robot 14 can access thecleaning unit 5 and the threesupports 7, 9 and 10. Atransfer robot 15 having two hands is disposed at a position where hands of thetransfer robot 15 can access thecleaning unit 6 and the threesupports 8, 9 and 10. - The
support 7 is used to transfer a semiconductor wafer between thetransfer robot 4 and thetransfer robot 14, and thesupport 8 is used to transfer a semiconductor wafer between thetransfer robot 4 and thetransfer robot 15. These supports 7, 8 havesensors - The support9 is used to transfer a semiconductor wafer from the
transfer robot 15 to thetransfer robot 14, and the support 10 is used to transfer a semiconductor wafer from thetransfer robot 14 to thetransfer robot 15. These supports 9, 10 havesensors nozzles - The supports9 and 10 are disposed in a common water-scatter-prevention cover which has an opening defined therein for transferring wafers therethrough. At the opening, there is provided a
shutter 22. The support 9 is disposed above the support 10. The upper support 9 serves to support a wafer which has been cleaned, and the lower support 10 serves to support a wafer to be cleaned. With this arrangement, the wafer is prevented from being contaminated by rinsing liquid which would otherwise fall thereon. Thesensors nozzles shutter 22 are schematically shown in FIG. 1, and their positions and shapes are not exactly illustrated. - A
cleaning unit 24 is disposed at a position adjacent to thecleaning unit 5 and is accessible by the hands of thetransfer robot 14. Further, acleaning unit 25 is disposed at a position adjacent to thecleaning unit 6 and is accessible by hands of thetransfer robot 15. These cleaningunits - The respective upper hands of the
transfer robot 14 and thetransfer robot 15 are used for transporting a semiconductor wafer that has been cleaned to the cleaning units or the supports of thewafer station 12. On the other hand, the respective lower hands of thetransfer robot 14 and thetransfer robot 15 are used for transporting a semiconductor wafer that has not cleaned or a semiconductor wafer to be polished. Since the lower hands are used to transfer a wafer to or from a reversing device (described later on), the upper hands are not contaminated by drops of rinsing liquid which fall from an upper wall of the reversing device. - As shown in FIG. 1, the
cleaning units shutters shutters shutters - The polishing apparatus has a
housing 26 for enclosing various components therein. An interior of thehousing 26 is partitioned into a plurality of areas (including areas A and B) bypartition walls - Area A in which the
wafer cassettes 1 and thetransfer robot 4 are disposed, and area B in which thecleaning units supports partition wall 28 so that cleanliness of area A and area B can be separated from each other. Thepartition wall 28 has an opening for transferring semiconductor wafers between area A and area B, and ashutter 38 is provided at the opening of thepartition wall 28. All of thecleaning units supports wafer station 12, and thetransfer robots - As shown in FIG. 1, in area C separated from area B by the
partition wall 34, a reversingdevice 40 for reversing a semiconductor wafer is provided at a position accessible by the hands of thetransfer robot 14. The semiconductor wafer is transferred to the reversingdevice 40 by thetransfer robot 14. Further, in area C, a reversingdevice 41 for reversing a semiconductor wafer is provided at a position accessible by the hands of thetransfer robot 15. The semiconductor wafer is transferred to the reversingdevice 41 by thetransfer robot 15. Each of the reversingdevices - The
partition wall 34 forms a polishing chamber which is separated from area B. The polishing chamber is further divided into two areas C and D by thepartition wall 36. Thepartition wall 34 between area B and areas C, D has openings for transferring semiconductor wafers therethrough.Shutters devices partition wall 34. - As shown in FIG. 1, each of areas C and D has two polishing tables and one top ring for holding and pressing one semiconductor wafer against the polishing tables to polish the wafer. Specifically, area C has a
top ring 44, polishing tables 46, 48, a polishingliquid supply nozzle 50 for supplying a polishing liquid onto the polishing table 46, anatomizer 52 having a plurality of ejection nozzles (not shown) connected to a nitrogen gas supply source and a liquid supply source, adresser 54 for dressing the polishing table 46, and adresser 56 for dressing the polishing table 48. Similarly, area D has atop ring 45, polishing tables 47, 49, a polishingliquid supply nozzle 51 for supplying a polishing liquid onto the polishing table 47, anatomizer 53 having a plurality of ejection nozzles (not shown) connected to a nitrogen gas supply source and a liquid supply source, adresser 55 for dressing the polishing table 47, and adresser 57 for dressing the polishing table 49. - The polishing
liquid supply nozzles atomizers atomizers atomizers atomizers - The mixture of nitrogen gas with pure water or the chemical liquid is supplied in a state of {circle over (1)} liquid fine particles, {circle over (2)} solid fine particles as a result of solidification of the liquid, or {circle over (3)} gas as a result of vaporization of the liquid. These states {circle over (1)}, {circle over (2)} and {circle over (3)} are referred to as atomization. In these states, the mixture is ejected from the ejection nozzles of the
atomizers - The polishing tables48, 49 may be replaced with wet-type thickness measuring devices for measuring a thickness of a film formed on a wafer. With such wet-type thickness measuring devices, the thickness of a film formed on a wafer can be measured immediately after the wafer is polished, and hence it is possible to further polish the polished wafer or to control a polishing process for polishing a subsequent wafer based on measured results.
- A
rotary transporter 60 is disposed below the reversingdevices rotary transporter 60 has four stages for placing wafers W at equal angular intervals, and can hold a plurality of wafers thereon at the same time. - A wafer which has been transferred to the reversing
device rotary transporter 60 by elevating and lowering alifter rotary transporter 60 when a center of a stage of therotary transporter 60 is aligned with a center of the wafer held by the reversingdevice rotary transporter 60 is transported to a position below thetop ring 44 or thetop ring 45 by rotating therotary transporter 60 by an angle of 90°. At this time, thetop ring 44 or thetop ring 45 is positioned above therotary transporter 60 beforehand by a swinging motion of the top ring. A wafer held on the stage of therotary transporter 60 is transferred to thetop ring pusher rotary transporter 60 when a center of thetop ring - Next, the polishing chamber will be described below. Although only area C will be described below, the following description can be applied to area D. FIG. 2 shows a relationship between the
top ring 44 and the polishing tables 46, 48 in area C. - As shown in FIG. 2, the
top ring 44 is supported from atop ring head 72 by a topring drive shaft 70 which is rotatable. Thetop ring head 72 is supported by asupport shaft 74 which can angularly be positioned, and thetop ring 44 can access the polishing tables 46 and 48. - The
dresser 54 is supported from adresser head 78 by adresser drive shaft 76 which is rotatable. Thedresser head 78 is supported by asupport shaft 80 which can angularly be positioned, and thedresser 54 can be moved between a standby position and a dressing position above the polishing table 46. Thedresser 56 is similarly supported from adresser head 84 by adresser drive shaft 82 which is rotatable. Thedresser head 84 is supported by asupport shaft 86 which can angularly be positioned, and thedresser 56 can be moved between a standby position and a dressing position above the polishing table 48. - The polishing table46 has an upper surface composed of a fixed abrasive 46 a having abrasive particles and pores or a pore agent, which are fixed by a binder (resin). The fixed abrasive 46 a serves as a polishing surface for polishing a semiconductor wafer held by the
top ring 44. Such a fixed abrasive 46 a can be obtained, for example, by spray-drying a mixed liquid which is a mixture of a slurry of abrasive (dispersion of abrasive particles in a liquid) and a resin emulsion, filling the resulting mixed powder into a molding jig, and subjecting the mixed powder to a pressure/heat treatment. Ceria (CeO2) or silica (SiO2) having an average particle diameter of not more than 0.5 μm is preferably used as the abrasive particles. A thermoplastic resin or a thermosetting resin may be used as the binder. The thermoplastic resin is preferably used. - The polishing table48 has an upper surface composed of a soft nonwoven fabric. The nonwoven fabric serves as a cleaning surface for cleaning a semiconductor wafer after a polishing process to remove abrasive particles attached to a surface of the semiconductor wafer.
- Next, a polishing process for polishing a semiconductor wafer with the use of a polishing apparatus according to the present invention will be described below. Although a polishing process only in area C will be described below, the following description can be applied to a polishing process in area D. Further, though the following description illustrates application of the present invention to a polishing step in an STI formation, the present invention is also applicable, for example, to polishing of a semiconductor wafer having a pattern of interlayer dielectrics (ILD).
- 1) Polishing Process
- While the polishing table46 and the
top ring 44 are rotated about their own axes, respectively, a semiconductor wafer is pressed against the polishing table 46 to thereby polish a silicon oxide film on the semiconductor wafer until the fixed abrasive reaches a nitride film. During the polishing, a polishing liquid which contains an anionic surface-active agent and does not contain abrasive particles is supplied from the polishingliquid supply nozzle 50 onto the fixed abrasive 46 a. The concentration of the anionic surface-active agent is preferably 0.001% by weight to 5% by weight, more preferably 0.001% by weight to 0.15% by weight. From the viewpoints of suppressing dishing to obtain within-wafer uniformity and dispersing abrasive particles, which have dropped out of the fixed abrasive, to prevent scratches, the concentration is more preferably not less than 0.002% by weight, further more preferably not less than 0.003% by weight, and especially preferably not less than 0.004% by weight. Further, from the viewpoints of achieving a sufficiently high polishing rate and dispersing the dropped abrasive particles to prevent scratches, the concentration is preferably less than 0.15% by weight, more preferably less than 0.10% by weight, further more preferably less than 0.08% by weight, especially preferably less than 0.05% by weight. Accordingly, the concentration of the anionic surface-active agent is preferably not less than 0.001% by weight and less than 0.15% by weight, more preferably not less than 0.002% by weight and less than 0.10% by weight, further more preferably not less than. 0.003% by weight and less than 0.08% by weight, especially preferably not less than 0.004% by weight and less than 0.05% by weight. The purpose of the addition of the surface-active agent is, besides allowing the nitride film to function as a stopper, to control the polishing rate of the silicon oxide film to thereby suppress dishing (in the trench portion). A rise in the concentration of the surface-active agent can lower the polishing rate of the silicon oxide film and can therefore suppress dishing. If the concentration is excessively increased, the polishing rate is extremely lowered, thus requiring a long polishing time. This leads to a lowering of the productivity. For example, when ammonium polyacrylate is added at a concentration of 0.05% by weight, the polishing rate of the silicon oxide film decreases by about 30%, as compared to the case of pure water. There is a linear relationship between the surface-active agent concentration and the decrease in the polishing rate. Thus, the polishing rate decreases by about 60% at a concentration of 0.10%, and by about 90% at a concentration of 0.15%. In consideration of the productivity, it is desirable to set the upper limit of the concentration of the surface-active agent at 0.15,%. - The pH of the polishing liquid is preferably in the range of from 4 to 10, more preferably from 4 to 6.5. In particular, from the viewpoint of dispersing dropped abrasive particles to prevent scratches, the pH is more preferably over 4.5, further more preferably over 4.8, especially preferably over 5.0. Further, from the viewpoint of suppressing dishing to obtain within-wafer uniformity, the pH is more preferably less than 5.5, further preferably less than 5.4, especially preferably less than 5.3. Accordingly, the pH value is preferably higher than 4.5 and less than 5.5, more preferably higher than 4.8 and less than 5.4, especially preferably higher than 5.0 and less than 5.3.
- The anionic surface-active agent preferably contains an organic compound having a hydrophilic group which is either a COO− group or a SO3 − group. From the viewpoints of dispersing dropped abrasive particles to prevent scratches and suppressing dishing to obtain within-wafer uniformity, an organic compound having a COO− group is particularly preferred. Specific examples of such organic compounds include: sulfuric acid compounds, such as alkylsulfuric acid, alkyl ether sulfuric acid, and their salts; sulfonic acid compounds, such as alkylsulfonic acid, alkylbenzene sulfonic acid, alkylnaphthalene sulfonic acid, sulfosuccinic acid, a naphthalenesulfonic acid-formalin condensate, lignin sulfonic acid, polystyrene sulfonic acid, and their salts; carboxylic acid compounds, such as a soap, alkyl ether carboxylic acid, polyacrylic acid, polymethacrylic acid, a copolymer containing acrylic acid or metacrylic acid, and their salts; and phosphoric acid compounds, such as alkylphosphoric acid, alkyl ether phosphoric acid, and their salts. Of these compounds, polyacrylic acid and its salts are most preferable. Among polyacrylate, an ammonium salt is preferable.
- From the viewpoint of dispersing dropped abrasive particles to prevent scratches, the weight average molecular weight (Mw) of polyacrylic acid and its salt is preferably not less than 13000, more preferably not less than 14000, and most preferably not less than 15000. On the other hand, from the viewpoint of suppressing dishing to obtain within-wafer uniformity, the molecular weight is preferably not more than 60000, more preferably not more than 50000, and most preferably not more than 45000. Accordingly, the molecular weight is preferably not less than 13000 and not more than 60000, more preferably not less than 14000 and not more than 50000, and most preferably not less than 15000 and not more than 45000. The molecular weight values of polyacrylic acid and its salt were measured by gel permeation chromatography (GPC) carried out under the following condition:
- Pump: CCPD (Tosoh Corporation)
- Detector: RI-71 (Shodex)
- Data processing software: Gpc-8020 (Tosoh Corporation)
- Column: G4000PWXL (Tosoh Corporation) was used as a first-stage column, and G2500PWXL (Tosoh Corporation) was used as a second-stage column
- Eluent: A mixture of 0.2 M phosphoric acid buffer solution and CH3CN in the ratio of 9:1 (volume ratio) was used. The 0.2 M phosphoric acid buffer solution is a mixture of 0.2 mol/L aqueous KH2PO4 solution and 0.2 mol/L aqueous Na2HPO4 solution in the ratio of 1:1 (volume ratio).
- Flow rate: 1.0 mL/min
- Column temperature: 40° C.
- Sample amount: Aqueous solution of 0.5 wt % polyacrylic acid and its
salt 100 μL - Molecular weight conversion: using seven species of polyethylene glycol with known molecular weights (12000, 26000, 95000, 145000, 250000, 510000, 920000), a calibration curve was prepared for conversion of molecular weight.
- It is preferred that the polishing liquid of the present invention contains at least two types of anionic surface-active agents: polyacrylic acid and its salt which, from the viewpoint of dispersing dropped abrasive particles to prevent scratches, has a weight average molecular weight of not less than 25000 and not more than 60000; and polyacrylic acid and its salt which, from the viewpoint of suppressing dishing to obtain within-wafer uniformity, has a weight average molecular weight of not less than 13000 and less than 25000.
- The first polyacrylic acid and its salt, has a weight average molecular weight of not less than 25000 and not more than 60000, more preferably has a weight average molecular weight of not less than 27000 and not more than 45000, and most preferably has not less than 28000 and not more than 35000. From the viewpoints of dispersing dropped abrasive particles to prevent scratches and suppressing dishing to obtain within-wafer uniformity, the surface-active agent is added preferably in an amount of not less than 0.0005% by weight and less than 0.03% by weight, more preferably not less than 0.001% by weight and less than 0.02% by weight, most preferably not less than 0.005% by weight and less than 0.01% by weight.
- The second polyacrylic acid and its salt, has a weight average molecular weight of not less than 13000 and less than 25000, more preferably has a weight average molecular weight of not less than 14000 and not more than 24000, most preferably has not less than 15000 and not more than 23000. From the viewpoints of suppressing dishing to obtain within-wafer uniformity and achieving a sufficiently high polishing rate, the surface-active agent is added preferably in an amount of not less than 0.003% by weight and less than 0.12% by weight, more preferably not less than 0.01% by weight and less than 0.08% by weight, most preferably not less than 0.02% by weight and less than 0.04% by weight.
- The experimental results of polishing of STI substrates (SKW3-1, using MIT964 mask) by using a polishing apparatus according to the present invention which includes a fixed abrasive pad comprising ceria abrasive particles having an average particle diameter of 0.2 μm and a thermoplastic resin as a binder will be described. The following
polishing liquids liquid 2 containing 1.6% by weight of polyacrylic acid having a molecular weight of 31200, the pH of the polishing liquid being adjusted to 6.0 with ammonia; and polishing liquid 3 containing 1.0% by weight of polyacrylic acid having a molecular weight of 31200, the pH of the polishing liquid being adjusted to 9.0 with ammonia. When the STI substrate was polished using the polishingliquid 1, dishing was observed but the depth of dishing was not more than 100 Å, while no scratch was observed, thus good polishing was achieved. When the STI substrate was polished using the polishingliquid 2, though dishing was at the same level as the polishingliquid 1, some scratches were observed. When the STI substrate was polished using the polishingliquid 3, some scratches were observed and no improvement was found in terms of dishing. - In this manner, by polishing a substrate while supplying a polishing liquid which contains not less than 0.001% by weight and less than 0.15% by weight of anionic surface-active agent and does not contain abrasive particles and has a pH of 4 to 6.5, onto the fixed abrasive46 a, it becomes possible to allow a nitride film to act as a stopper, as described above. Accordingly, the polishing rate of the nitride film can be lowered to thereby obtain within-wafer uniformity of the nitride film and dishing of an oxide film can be suppressed. A high-flatness polishing with fewer scratches can thus be effected.
- As described above, according to the present invention, a workpiece is polished while supplying the polishing liquid which contains an anionic surface-active agent at a low concentration of not less than 0.001% by weight and less than 0.15% by weight and does not contain abrasive particles and has a pH of 4 to 6.5, onto a fixed abrasive. This makes it possible to allow a nitride film, for example, to act as a polishing stopper. Accordingly, the present invention makes it possible to lower the polishing rate of a nitride film, thereby obtaining within-wafer uniformity of the nitride film, and to suppress dishing, thus enabling a high-flatness polishing with fewer scratches.
- The present invention can be advantageously applied to a polishing method and a polishing liquid for polishing a workpiece such as a semiconductor wafer by using a fixed abrasive.
Claims (13)