US20040142558A1 - Apparatus and method for atomic layer deposition on substrates - Google Patents
Apparatus and method for atomic layer deposition on substrates Download PDFInfo
- Publication number
- US20040142558A1 US20040142558A1 US10/728,126 US72812603A US2004142558A1 US 20040142558 A1 US20040142558 A1 US 20040142558A1 US 72812603 A US72812603 A US 72812603A US 2004142558 A1 US2004142558 A1 US 2004142558A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- gas
- temperature
- reactor
- channels
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A deposition station allows atomic layer deposition (ALD) of films onto a substrate. The station comprises an upper and a lower substantially flat part between which a substrate is accommodated. The parts are positioned opposite each other and parallel to the substrate during processing. At least one of the parts is provided with a plurality of gas channels that allow at least two mutually reactive reactants to be discharged out of that part to the substrate. The discharge is configured to occur in a sequence of alternating, separated pulses for ALD. In addition, each part is preferably configured to be about 1 mm or less from the substrate to minimize the volume of the reaction chamber to increase the efficiency with which gases are purged from the chamber. Also, for each reactant, the upper and lower parts are preferably kept at a temperature outside of the window in which optimal ALD of that reactant occurs, thereby minimizing deposition of that reactant on deposition station surfaces.
Description
- This application claims the priority benefit under 35 U.S.C. §119(e) of provisional application No. 60/431,337, filed Dec. 5, 2002.
- The invention relates generally to the field of semiconductor processing and, more particularly, to an apparatus and method for the atomic layer deposition (ALD) of films onto semiconductor substrates.
- Various types of reactors are used for atomic layer deposition (ALD) of thin films on semiconductor substrates. During ALD, a semiconductor substrate is exposed to alternating and sequential pulses of at least two mutually reactive reactants. The substrate temperature is chosen to be in a window above the reactants condensation temperatures and below the reactant's thermal decomposition temperatures, so that during a reactant pulse a monolayer of the reactant adsorbs onto the substrate in a self-saturating manner without condensing or decomposing. After exposing the substrate to a first reactant, the process chamber is purged to remove any excess first reactant from the substrate and to remove any residual first reactant from the gas phase. The substrate is then exposed to a second reactant pulse, the second reactant being reactive with the first reactant.
- Adequate purging and/or evacuating between the alternating reactant pulses is vital for good control of the deposition process. As purging takes time, the ALD process is generally a slow process.
- Because of continual pressures within the semiconductor processing industry for increased throughput, there is a need for methods and apparatuses for ALD that allow efficient purging between subsequent reactant pulses, so that the purge time between pulses can be reduced and the overall deposition rate of the ALD process can be increased. In addition, because contaminating reactants can remain in a chamber by being deposited onto reactor walls there is also a need for reactors for ALD wherein deposition on the reactor walls is reduced or prevented.
- In accordance with one preferred embodiment of the invention, a film deposition station is provided for depositing a film onto a substrate. The deposition station comprises a first part and a second part for accommodating a semiconductor substrate between them. The first part and the second part are positioned opposite each other and parallel to a substrate, upon retention of the substrate between the first and second parts. The first part and the second part are also configured to be spaced less than about 2 mm from a main surface of a substrate accommodated between them. At least one of the parts is provided with a heater for heating that part and each part is provided with a set of gas supply channels connected to a source of gas. The source of gas for the first part is configured to supply mutually reactive reactants in a sequence of alternating, separated pulses for atomic layer deposition (ALD).
- In accordance with another preferred embodiment, a reactor is provided for semiconductor processing. The reactor comprises an upper reactor block and a lower reactor block for accommodating a semiconductor substrate therebetween. The upper and the lower reactor blocks are configured to be less than about 2 mm from a major surface of the substrate when the substrate is retained therebetween. Also, the reactor is configured to discharge mutually reactive reactants from at least one of the reactor blocks to the substrate in sequential alternating, separated pulses. The at least one of the reactor blocks comprises a set of gas channels configured to transport and discharge the sequential alternating, separated pulses of reactant to the substrate.
- In accordance with yet another preferred embodiment, a method is provided for depositing a layer on a semiconductor substrate. The method comprises providing an apparatus having a first side section and a second side section located opposite one another. The side sections each have facing planar surfaces and at least one of the side sections is heated to a temperature higher than about 200° C. The substrate is placed in the apparatus between the first and second side sections and two gas streams, in opposing directions, are applied from the first and second side sections to two opposing planar sides of the semiconductor substrate. The spacing between each of the first and second side sections and the semiconductor substrate is at most about I mm and the facing planar surfaces of the side sections extend completely across the opposing planar sides of the semiconductor substrate. At least one of the gas streams provides different reactants in a sequence of alternating, separated pulses for an atomic layer deposition (ALD) process.
- In accordance with another preferred embodiment, a method is provided for semiconductor processing. The method comprises providing a processing apparatus having a first and a second reactor block. A substrate is positioned between the first and the second reactor blocks, wherein the substrate is less than about 2 mm from each of the first and the second reactor blocks after positioning. Mutually reactive reactants are discharged from the first reactor block in alternating, temporally separated pulses onto the substrate. The substrate is heated using the first or second reactor block to one or more desired substrate temperatures, wherein the first reactor block is at a first temperature at which condensation or decomposition of the mutually reactive reactants is substantially prevented.
- In accordance with yet another preferred embodiment, a method is provided for semiconductor processing. The method comprises loading a substrate in a reaction chamber and completely supporting the substrate on a gas cushion in the chamber. While completely supporting the substrate on the gas cushion, mutually reactive reactants are discharged in alternating, temporally separated pulses onto a major surface of the substrate.
- In accordance with another preferred embodiment of the invention, a film deposition station is provided for depositing a film onto a substrate. The deposition station comprises a first part and a second part for accommodating a semiconductor substrate between them. The first part and the second part are positioned opposite each other and parallel to the substrate upon retention of the substrate between the first and second parts. The first part is provided with a first set of gas supply channels connected to a source for a first reactant and a second set of gas supply channels connected to a source for a second reactant. The first and second set of gas supply channels are configured to keep the reactants separated until discharging the reactants out from the gas supply channels to the substrate, wherein the first and the second reactant are mutually reactive. The deposition station also comprises controls to supply the first and the second reactant from the source for a first reactant and from the source for a second reactant in sequential alternating separated pulses for atomic layer deposition (ALD).
- The invention will be better understood from the detailed description of the preferred embodiments and from the appended drawings, which are meant to illustrate and not to limit the invention, and wherein:
- FIG. 1 shows a graph of the theoretical reaction regimes of different process recipes for a particular set of ALD reactants in different temperature ranges;
- FIG. 2 shows, schematically, a cross-sectional side view of a reactor having a top and a bottom part between which a substrate is accommodated, wherein one reactor part is heated and the other reactor part is cooled, in accordance with certain preferred embodiments of the invention;
- FIG. 3 shows, schematically, a cross-sectional side view of the reactor of FIG. 2, wherein both reactor parts are heated, in accordance with other preferred embodiments of the invention;
- FIG. 4 shows, schematically, a cross-sectional plan view of one of the two reactor parts of FIG. 3 as viewed along line A-A and showing gas channels, in accordance with preferred embodiments of the invention;
- FIG. 5 shows, schematically, a cross-sectional side view of the reactor part of FIG. 4 as viewed along line B-B;
- FIG. 6 shows, schematically, a cross-sectional side view of a reactor in which the top reactor part comprises two separated sets of gas supply channels, in accordance with another preferred embodiment of the invention;
- FIG. 7 shows, schematically, a cross-sectional side view of the reactor parts of FIG. 6, showing a first set of the gas channels in the top reactor part;
- FIG. 8 shows, schematically, a cross-sectional side view of the reactor parts of FIG. 6, showing a second set of the gas channels in the top reactor part;
- FIG. 9 shows, schematically, a cross-sectional side view of a reactor in accordance with yet another preferred embodiment of the invention; and
- FIG. 10 shows, schematically, a cross-sectional side view of a more complete reactor module using the reactor of FIG. 9, in accordance with another preferred embodiment of the invention.
- According to preferred embodiments of the invention, a deposition station is provided for depositing films by exposing a substrate to mutually reactive reactants, preferably in alternating pulses, such as for an atomic layer deposition process. The station preferably comprises two parts which delimit a reaction chamber in which the substrate is accommodated. To prevent unintended reaction of the reactants, at least one of the parts is provided with a plurality of gas channels which allow multiple reactants to be flowed through that part without contacting one another until being discharged into the reaction chamber. Preferably, as discussed below, the two parts are positioned close to the substrate during processing to minimize the volume of the reaction chamber and to allow quicker purging and cycling of reactants into the chamber. In addition, as discussed below, at least one of the two parts delimiting the reaction chamber can be heated. Preferably, the temperatures of these two parts are different from the desired process temperature of the substrate and are out of the window of temperatures in which deposition rate is optimized, thus minimizing deposition of reactants on the deposition station surfaces. Advantageously, by minimizing the purge time and the contamination of deposition station surfaces, reactor throughput and the quality of deposited layers are improved.
- A. Preferred Reactor Module
- While the preferred embodiments can be applied to other reactors known to those of skill in the art, use of a floating substrate reactor is particularly advantageous. In a floating substrate reactor, a substrate can be processed without being mechanically supported; that is, the substrate can be processed without being directly contacted by a solid support. This enables very uniform and rapid heating of the substrate without the cold spots that can occur in reactors where substrates are mechanically contacted during a semiconductor fabrication process. In addition, parts of the reactor surrounding the substrate are preferably relatively massive such that each has a high heat capacity relative to the substrate, helping to stabilize the temperature of the substrate and minimizing the susceptibility of the reactor to temperature fluctuations upon loading and unloading of the substrate into the reactor. The basic configuration of such a floating substrate reactor is available commercially under the trade name Levitor® from ASM International N.V. of Bilthoven, The Netherlands. In this reactor, a substrate, such as a wafer, is typically accommodated between relatively massive upper and lower blocks. More detailed information about the Levitor® can be found in U.S. Pat. No. 6,183,565, the disclosure of which is incorporated herein by reference.
- In addition, a Low Temperature (LT) module of the Levitore, also available from ASM International N.V. of Bilthoven, The Netherlands, allows for processing at low temperatures and permits the annealing of copper (Cu) films at temperatures in the range of about 200-400° C. A short description of the Levitor® Low Temperature module is provided below. More detailed information about the Levitor® Low Temperature copper anneal module can be found in WO 01/50502 and U.S. patent application Publication No. 2002/0092584, the disclosures of which are incorporated herein by reference.
- In some preferred embodiments, both upper and lower reactor blocks of the reactor are provided with heaters, and the temperature of the blocks can be controlled such that the blocks have different temperatures: one block at a higher temperature and the other block at a lower temperature, wherein the desired substrate temperature lies between the high temperature and the low temperature. In other preferred embodiments, both blocks are heated to substantially the same temperature, which is preferably equal to the desired substrate temperature. The substrate temperature can also be regulated by varying the heat transference between the substrate and the reactor blocks. Methods for controlling the substrate temperature by varying heat transference are described in greater detail in co-pending U.S. application Ser. No. 10/186,269, METHOD AND APPARATUS FOR THE TREATMENT OF SUBSTRATES, filed Jun. 27, 2002 and METHOD FOR THE HEAT TREATMENT OF SUBSTRATES, filed Oct. 31, 2003, attorney docket No. ASMINT.057AUS, the disclosure of which is incorporated herein by reference.
- Also, in some embodiments, to allow a substrate to be processed at a temperature within a processing window for optimal deposition while the upper and lower blocks are maintained at temperatures outside that window and to be able to quickly cool the substrate, the upper and lower blocks can be set at different temperatures, as noted above. For example, the upper block of the Levitor® Low Temperature module can be kept hot, preferably about 50° C. or more above the desired substrate treatment temperature, while the lower block is kept cold, preferably about 50° C. or more below the desired substrate treatment temperature or, more preferably, at 40° C. or less. The upper block is preferably heated by an array of heating elements, and the lower block is preferably water-cooled. The blocks are provided with a plurality (preferably about 60 to 100) of gas injection channels, spaced from each other and distributed over the surface of the block facing the semiconductor substrate. When the blocks are in a closed position with a substrate loaded between them, the gap between the substrate and each of the blocks is preferably less than about 2.0 mm, more preferably less than about 1.0 mm, and most preferably less than about 0.5 mm. In the illustrated embodiments the gap is about 0.2 mm. Typical powers required to maintain a temperature difference, ΔT, of about 400° C. between the blocks are in a range of roughly about 5-8 kW for 300 mm semiconductor wafers.
- The temperature of a substrate within the reactor can be varied by switching the type of gas above and below the substrate between a high thermal conductivity gas and a low thermal conductivity gas (e.g., He or N2, respectively), and/or by varying the position of the substrate relative to the two blocks (e.g., the relative distance of the substrate from each block). When the blocks are at different temperatures, switching the composition of the gases on one or both sides can change the thermal conductivity of the medium between the substrate and the blocks. Thus, switching the gas compositions on one or both sides of the substrate can be employed to change the substrate temperature within a range between the temperatures of the two blocks. In addition, switching the relative flow rates of gases on either side of the substrate can move the substrate closer to one or the other of the blocks, thereby also changing the substrate temperature.
- When the blocks are in a closed position and arranged close to a substrate, large gas flows (preferably greater than about 5 slm and, in a some embodiments, about 10 slm on each side) ensure that the substrate surfaces are effectively protected from the outside ambient. For example, this allows a Cu film to be annealed in the Levitor® Low Temperature module without the need to apply an additional gate valve to prevent oxidation of the Cu film. Because of the large gas flows, the substrate only comes into contact with outside air when the blocks are open and the substrate is relatively non-reactive (i.e., when the substrate is cold in comparison to its temperature during treatment). Preferably, to ensure that the substrate is relatively cold, the substrate temperature is switched to a low value at the end of processing, e.g., by appropriately switching the gases flowing above and below it, before opening the blocks.
- In arrangements where the blocks are maintained at different temperatures, however, the substrate is susceptible to temperature non-uniformities. This is caused by the fact that temperature differences on different sides of a substrate produce a temperature gradient through the thickness of the substrate and thus can cause bowing of the substrate, which can immediately result in a temperature non-uniformity. For example, when the same gas is used on both sides of the substrate, with a ΔT between the blocks of about 400° C., and a gap of about 0.2 mm between each block and the substrate, a temperature non-uniformity across the substrate of about 1° C. per 1 μm bow can result. Thus, for a typical rest bow of about 10 μm, the difference in temperature of different parts of the substrate can be up to about 10° C. Advantageously, however, this non-uniformity can be reduced when the ΔT between the blocks is made smaller or when different gases are used on both sides of the substrate in order to reduce the differences in temperature between the two sides of the substrate.
- Heat-up and cool-down with such an arrangement can advantageously be fast. Using good heat conduction in the thin gas layers results in typical heat-up and cool-down times of preferably less than about 5 seconds and, more preferably, between about 2-3 seconds.
- As noted above, the blocks are preferably relatively massive compared to the substrate. The blocks thus have sufficient heat capacity such that, when heated, heat is transferred to an unheated substrate loaded between the side sections with negligible temperature loss from the blocks. The blocks preferably are formed of metal and have a preferred vertical thickness of greater than about 10 mm, more preferably greater than about 40 mm.
- It will be appreciated that it is not trivial to deposit films from more than one reactant in reactors such as the Levitor® reactor, as suggested in U.S. Pat. No. 6,183,565, the disclosure of which is incorporated herein by reference. For example, with conventional CVD processes, it has been found that when deposition gases are pre-mixed, there is a tendency to cause deposition in the gas channels and in the tubing. In addition, there is a tendency toward depletion of reactants in the small volume in between the substrate and the block surface. This depletion can lead to relatively heavy deposition on the substrate immediately below the gas inlet channels, and to less deposition on areas of the substrate in between such inlet points. Consequently, processing using multiple reactants in these reactors can be problematic both in terms of adversely affecting reactor surfaces and in terms of their deposited layers on substrates, which exhibit poor uniformity of both thickness and coverage.
- B. ALD in the Preferred Reactor Module
- It has been found that the problems that can exist when depositing films using multiple reactants in reactors such as the Levitor® reactor can be avoided when ALD processes are used to deposit the films.
- These problems can advantageously be avoided for a number of reasons. For example, in accordance with some preferred embodiments, when independent gas inlet channels are used for different reactants, there typically will be no deposition in the gas inlet channels.
- Also, when a block facing the substrate device side is kept at a relatively low temperature (but high enough to avoid condensation), there will be substantially reduced ALD growth on the surfaces of that (typically colder) block facing the substrate. Alternatively, when the block facing the substrate device side is kept at a relatively high temperature (but not so high that thermal decomposition of a reactant occurs), such that the reaction conditions are outside the optimal process window for ALD, substantially reduced ALD deposition will occur on surfaces of this block due to a tendency for reactants to desorb.
- Moreover, even where reactant depletion occurs, self-saturating pulses and true self-limiting reactions do not generally cause non-uniformity in ALD films. This is due to the saturation of absorption sites for reactants, which typically prevents an excess build-up of reactants. Thus, the problems with deposition on reactor surfaces and with poor quality deposited layers can be avoided.
- In addition, various other features of the preferred reactor make it particularly advantageous for ALD processes. For example, the reactor volume is particularly small, due to the small spacing of the substrate from each of the upper and lower reactor blocks of about 2 mm or less, preferably about 1 mm or less and, more preferably, of about 0.2 mm or less. The small reactor volume allows a rapid switching between the alternating reactant pulses in ALD; any traces of a reactant pulse still residing in the reactor after termination of the pulse can be purged from the reactor in a very short time.
- Not only is the reaction space volume small, but the gas distribution system used with the preferred reactor, described in further detail below, also has a small volume. Unlike conventional showerheads, the gas distribution system does not comprise a relatively voluminous gas distribution section to distribute gas laterally and uniformly over the substrate. Instead, the gas distribution system preferably comprises a set of horizontal channels to distribute the gas in a lateral direction over the substrate, which is typically placed in the reactor in a horizontal position. Preferably, a set of vertical channels, each vertical channel preferably in communication at one end with one of the horizontal channels and at the other end with the reaction space, discharges the gas into the reaction space. The channels are preferably drilled in the reactor blocks, which are preferably massive plates. The horizontal channels are relatively small in diameter, preferably about 3-5 mm and more preferably about 4 mm in diameter. The vertical channels are preferably about 1-3 mm in diameter and more preferably about 2 mm in diameter. Consequently, the total volume of the set of horizontal and vertical channels is small and easily purged in comparison to a conventional showerhead that comprises a relatively open gas distribution volume upstream of a perforated faceplate. In addition, the small gas volumes at both sides of the substrate further ensure that the total reactor volume is purged particularly efficiently.
- Another advantage of the preferred reactor for ALD is the ability to control the temperature of the substrate at a value different from the temperature of the reactor blocks, thereby helping to minimize deposition on the reactor blocks. It will be appreciated that true self-limited atomic layer deposition will only occur in a certain temperature window. Preferably, the reactor block from which the reactants are dispersed is maintained at a temperature outside the window for optimized ALD growth, and preferably at a temperature where little or no growth occurs, so that little or no deposition occurs on this block, while the substrate is maintained at a temperature within the window for ALD growth.
- An additional advantage of the preferred reactor, e.g., the Levitor® LT module is that, during processing, the temperature of the substrate can rapidly be switched. This can beneficially be exploited in a manner as disclosed by Kurabayashi et. al. in a paper entitled “Temperature synchronized molecular layer epitaxy,” Applied Surface Science 82/83 (1994) 97-102, the disclosure of which is incorporated herein by reference. Kurabayashi describes, among other examples, a process wherein a GaAs film is deposited on a substrate by exposing the substrate sequentially and repeatedly to pulses of AsH3 and TMG (Tri Methyl Gallium), and wherein the substrate temperature is 500° C. during the AsH3 pulse and 450° C. during the TMG pulse. The higher temperature during the AsH3 pulse is preferred for achieving a sufficient reaction rate, whereas the lower temperature during the TMG pulse is preferred for avoiding premature thermal decomposition of the TMG. In general, this technique allows the use of temperature sensitive precursors during the low temperature part of the cycle whereas the high temperature part of the cycle ensures that a sufficient reaction rate and/or film quality is achieved. This is beneficial in the deposition of metals, metal oxides, and metal nitrides.
- In some situations, cycling the temperature is a good alternative to the use of a plasma during the deposition process. Further, when depositing multicomponent materials, temperature cycling allows the use of combinations of reactants, in particular metal compounds, whose respective process windows do not match.
- Advantageously, the preferred reactor is well suited for rapid switching of substrate temperature without requiring a large peak power and large variations in power for the heating system. It will be recognized that the temperatures between which processing is switched can be tailored depending on the reactants used. Also, the timing of the temperature switching can be tailored with respect to the timing of the gas pulses, to achieve optimum results. After supplying a first reactant at a first substrate temperature, the temperature of the substrate can be switched to the second temperature at the beginning, during or after the supply of the second reactant pulse. Although the moment of temperature switching can be shifted in time with respect to the moment of reactant switching, it will be appreciated that the period in which the reactor is at the first temperature should overlap with presence of the first reactant and the period in which the reactor is at the second temperature should coincide with the presence of the second reactant. Preferably, the duration of the period between which the temperature and reactants are switched is the same and switching of the temperature and reactants occurs at substantially the same frequency.
- C. Detailed Description of the Figures
- Reference will now be made to the Figures, wherein like numerals refer to like parts throughout.
- With reference to FIG. 1, the temperature window for optimal ALD is explained in further detail. In this figure, the growth of the film per cycle is given as a function of temperature. The horizontal axis indicates the deposition temperature and the vertical axis indicates the amount of film growth per deposition cycle. W denotes the temperature window in which optimized atomic layer deposition occurs. In an ideal case for the temperature window W, represented in the drawings as a horizontal line across the vertical growth axis, one monolayer of film is deposited per full cycle. It will be appreciated, however, that due to surface reconstruction or steric hindrance by large surface ligands, less than a monolayer per cycle is typically deposited in an actual ALD process performed within this window, but optimal self-limited growth still obtains.
- Outside the window, various factors can cause greater than or less than optimized growth per cycle. For example, at the low temperatures at the low end of the temperature window (W), depending on whether a reactant condenses at those temperatures, more or less than a monolayer can be deposited. L1 denotes a region of increased growth per cycle, exhibited by reactants that condense at those temperatures. L2 denotes a region of decreased growth per cycle, for other reactant combinations. The temperature dependence described by L2 is indicative of a process with combinations of reactants for which the reaction is activation energy limited, where the reactivity of the reactants becomes too low. It should be noted, however, that even for chemistries exhibiting a low-temperature curve like L2, increased deposition can eventually occur at lower temperatures than those shown, since condensation usually will take place at a low enough temperature.
- On the other hand, at temperatures at the high end of the temperature window, other factors can lead to deposition of greater than or less than one monolayer per cycle. H1 indicates a situation where the growth per cycle is above the optimized, self-limited growth. This can occur for some process recipes when the temperature is so high that thermal decomposition of one of the reactants occurs or where non-volatile reaction by-products are formed. H2 represents a situation where the growth per cycle is less than one monolayer. This may be the result of desorption or dissociation of a surface ligand that is needed to activate the surface for the next reactant. It should be noted, however, that even for chemistries exhibiting a high-temperature curve like H2, increased deposition can eventually occur at even higher temperatures than those shown, when thermal decomposition causes deposition of more than one monolayer per cycle.
- As shown in FIG. 1, maintaining the substrate surface temperature within a certain window is important for achieving the desired amount of growth of a thin film on a substrate by ALD. Preferably, information about the growth curve for a particular reaction is used to select an appropriate substrate temperature. Thus, a substrate temperature is preferably chosen that falls within the window in which ALD occurs. Advantageously, the preferred embodiments also take advantage of the other information available from the growth curves to minimize deposition on the reactor walls and to provide an improved ALD method and apparatus.
- Exemplary embodiments will now be described with reference to FIGS.2-9. FIG. 2 shows schematically a
reactor 100 having the general features of a Levitor® Low Temperature module. Thereactor 100 comprises anupper reactor block 120 and alower reactor block 160, between which a substrate orwafer 110 is accommodated. It will be appreciated that the surfaces of theblocks wafer 110. Theupper reactor block 120 is preferably heated through resistance heating, using an array ofheating elements 122, each heating element connected withwires 123 to a source of electrical energy. Gas flows through theupper block 120 via a gas inlet opening 124, andgas inlet channels major surface 110 a of thewafer 110 via a plurality ofgas dispersion channels 128 in communication with thegas inlet channel 126. Finally, the gas is discharged from theupper block 120 towards afirst surface 110 a throughgas injection channels 129. - Shown on the other side of the
wafer 110, thelower reactor block 160 is provided withcooling channels 162 for the passage of a cooling fluid. Gas flows through thelower block 160 via a gas inlet opening 164 andgas inlet channels second surface 110 b via a plurality ofgas dispersion channels 168 in communication with thegas inlet channel 166. Finally, the gas is discharged from thelower block 160 towards the secondmajor surface 110 b ofwafer 110, opposite thefirst surface 110 a, throughgas injection channels 169. In the reaction space between theblocks peripheral gap 130 between theblocks - It will be appreciated that the
gas dispersion channels surfaces gas inlet channel gas inlet channel entire surface gas inlet channel surface - It will also be appreciated that a lower block need not be actively cooled. For example, in another embodiment, as shown in FIG. 3, the
lower block 150 is provided with theheating elements 152, instead of cooling fluid channels, to maintain thelower block 150 at a raised temperature. The temperature of thelower block 150 can be the same as the temperature of theupper block 120 or it can be a different temperature. Preferably, theheating elements 152 are resistive heaters and are each connected viawires 153 to a source of electrical energy. Gas is flowed through thelower block 150 via a gas inlet opening 154 andgas inlet channels entire wafer surface 110 b via a plurality ofgas dispersion channels 158 in communication with the verticalgas inlet channel 156. Finally, the gas is discharged from thelower block 150 towards thesecond surface 110 b of thewafer 110, opposite thefirst surface 110 a, throughgas injection channels 159. - The configuration of the gas channels in the blocks is shown in greater detail in FIGS. 4 and 5. FIG. 4 shows a horizontal cross-section of a
block 420 similar to theblock 120 of FIG. 3, taken across plane A-A of FIG. 3. Like elements are referenced by reference numerals having like last two digits relative to the elements of FIG. 3. Theblock 420 is provided with thegas dispersion channels 428 in a radial configuration. Eachgas dispersion channel 428 is provided with a plurality ofgas injection channels 429. - FIG. 5 shows a vertical cross-section taken along plane B-B in FIG. 4. Gas enters the
block 420 through theinlet 424, which is in communication with thegas inlet channel 425, through which gas is discharged into the annularvertical inlet channel 426. Thegas dispersion channels 428 are in communication with thevertical channel 426. The annular channel is formed by inserting aplug 434 into acylindrical hole 433 in theblock 420. As theplug 434 has, over a part of its length, a smaller diameter than thecylindrical hole 433, thevertical inlet channel 426 is left open. Thegas dispersion channels 428 are preferably drilled in theblock 420 and their radially outward ends are preferably closed by insertingplugs 432. - Preferably, the cross-sectional area of each of the
gas dispersion channels 428, as represented by, e.g., their diameter(s), is larger than the cross-sectional area of each of the gas injection channels 429 (FIG. 4), so that a roughly homogeneous distribution of gas through thegas dispersion channels 428 and verticalgas injection channels 429 is achieved. In a preferred embodiment, the diameter of thegas dispersion channels 428 is about 3-5 mm and more preferably about 4 mm and the diameter of thegas injection channels 429 are about 1-3 mm and more preferably about 2 mm. - In addition, the
gas injection channels 429 themselves preferably comprise a first section with a relatively small first diameter, directly connected to thegas dispersion channels 428, and a second section with a wider second diameter, which opens to the reaction space occupied by the substrate 110 (FIGS. 2 and 3). Preferably, the first diameter is about 1 mm or less and the second diameter is about 1 mm or more. In one preferred embodiment, the first diameter is about 0.25 mm and the second diameter is about 2 mm, the length of the first section is about 1 mm and the first section is at an upstream end intersecting with agas dispersion channel 428 whereas the length of the second section is about 3 mm. The downstream end of the first section is in communication with the upstream end of the second section. The downstream end of the second section opens into the reaction space. In this way, a narrow restriction ingas injection channel 429 is provided, whereas the second wider section allows expansion of the gas jet and reduction of the gas velocity before discharging the gas into the reaction space, so that the occurrence of gas jet marks on the substrate is advantageously avoided. - It will be appreciated that various other arrangements are possible for the gas channels, so long as they allow for gas to be distributed over a substrate surface. For example, the
gas dispersion channels 428 need not be in a radial configuration but, e.g., can be arranged according to a pattern of parallel, equidistant lines, connected at one end with a gas inlet channel oriented perpendicular to the gas dispersion channels, forming a rake type configuration. Further, the two sets of separated gas dispersion channels need not necessarily be vertically displaced but they can be, e.g., two oppositely oriented, interlaced rakes, disposed at about the same vertical level. Similarly, it will also be appreciated that various other arrangements are possible for thegas inlet 424 and thegas inlet channels gas dispersion channels 428. - With reference to FIG. 6, a particularly advantageous embodiment is shown, wherein the
upper block 120 is provided with two different, separated sets of gas distribution channels, one set of channels for each one of the two mutually reactive reactants typically used during the deposition process. The first set comprises a gas inlet opening 124, in communication with one end of agas inlet channel 125, the other end of thegas inlet channel 125 in communication with avertical inlet channel 126, discharging into an annulargas distribution channel 127. A plurality ofgas dispersion channels 128 is in communication with the annulargas distribution channel 127. Finally, gas is discharged from thegas dispersing channels 128 throughgas injection channels 129 towards thefirst surface 110 a of thewafer 110. - A second set of gas distribution channels, separated from the first set, is configured similarly to the first set. The second set comprises a second gas inlet opening144, in communication with one end of a second
gas inlet channel 145, the other end of the secondgas inlet channel 145 being in communication with a secondvertical inlet channel 146, discharging into a second annulargas distribution channel 147. A plurality of secondgas dispersion channels 148 are in communication with the annulargas distribution channel 147. Finally, gas is discharged from thegas dispersing channels 148 through the secondgas injection channels 149 towards thefirst surface 110 a ofwafer 110. Preferably, other features in FIG. 6 are similar as those in FIG. 3. - It will be appreciated that FIG. 6 is a schematic, cross-sectional side view, showing both sets of channels in the
upper block 120 simultaneously. Preferably, the two sets of horizontally extendinggas dispersion channels gas injection channels 149 communicating with the upper set ofgas dispersion channels 148 do not intersect the lower set ofgas dispersion channels 128. - An exemplary such arrangement is illustrated in greater detail in FIGS. 7 and 8. In FIG. 7, which is a cross-sectional view taken through a first plane, the first set of gas channels124-129 is shown. Also shown is the annular
gas distribution channel 147, which is an annular ring and visible at any cross-section taken through the center axis of the reactor blocks 120 and 150. In FIG. 8, which is a cross-sectional view taken through a second plane, slightly rotated with respect to the first plane, the second set of gas channels 144-149 is shown. Also shown is the annulargas distribution channel 127. It will be appreciated that while no channels are illustrated in thelower block 150 for clarity of illustration, thelower block 150 can be provided with channels, as discussed herein. - It will be appreciated that the number of sets of channels such as the gas channels124-129 and 144-149 is not limited to two; rather, the number of separated sets of channels is only limited by the number of set of channels that can be accommodated in the
block 120. For example, in other arrangements, three or more separated sets of channels can be accommodated in theblock 120. Also, thelower block 150 can be provided with separated sets of channels, which can be arranged differently or can mirror those of theupper block 120. - A further embodiment is shown in FIG. 9. The
gas inlets upper block 120 are now provided at the top and through the center of theupper block 120 and thegas inlet 154 of thelower block 150 is provided at the bottom and through the center of thelower block 150. It will be appreciated that thegas inlets gas lines more controllers 250, which preferably comprise separate valves commonly controlled by a computer programmed to provide gases to thegas inlets controller 250 is preferably also connected toreactant sources - FIG. 10 is a schematic cross section of an ALD module based on Levitor® principles in accordance with another preferred embodiment. The configuration of the
blocks upper wall 190 and alower wall 192. Theupper block 120 is stationary and in fixed connection with theupper wall 190. Thelower block 150 is vertically movable to allow for loading and unloading of thewafer 110 in between and out from between theblocks opening 195. The mechanism for vertically moving thelower block 150 is schematically indicated by 194. Aremovable shield 193 is preferably connected to thelower block 150. Reaction gases are exhausted from the reaction space between the blocks via theannular channel 196. - In a preferred embodiment, the
upper block 120 is maintained at a relatively low temperature, below the desired substrate temperature, and thelower block 150 is kept at a relatively high temperature, above the desired substrate temperature. Preferably, theremovable heat shield 193 is kept at the same (relatively high) temperature as thelower block 150. As theshield 193 extends inwards such that its inside edge falls underneath thewafer 110 and reactant not adsorbed or reacted on thewafer 110 flows off thetop surface 110 a of the wafer and down to theshield 193, atomic layer deposition on the process system surfaces is concentrated on thisshield 193, and not on other parts of the system. Advantageously, by removing and replacing the shield, e.g., once every 10-20 μm of film deposition, a low particle generation level can be obtained. In addition, by making theshield 193 longer, so that it extends further downwardly into theannular channel 196, it can also fulfill the role of largely depleting the outgoing gas stream of reactants, in that way cleaning up the gas that is exhausted. - It will be appreciated that the system for supplying gas to the
reactor 100 can be configured in various ways known to those of skill in the art. Typically, the gas supply system will comprise one or more controllers which are programmed to provide separate, alternating gas pulses to thereactor 100. In some arrangements, each of the blocks of a Levitor® reactor can have separate gas inlets which can be connected to separate gas feeds, as described in U.S. Pat. No. 6,183,565, the disclosure of which is incorporated herein by reference, or as shown in the FIGS. 6 and 9 discussed herein. In such a case, it will be appreciated that a gas switching mechanism is preferably provided upstream to allow for an ALD sequence of alternating and repeating reactant pulses, separated by reactant removal (e.g., purging) steps. An exemplary switching arrangement is sometimes referred to as. “inert gas valving,” and is described in U.S. patent application Publication 2001/0054377, the disclosure of which is incorporated herein by reference. In such an arrangement, pulses of reactant vapor are directed from the reactant source container towards the reaction chamber and, through switching of an inert gas flow, the reactant vapor flow is alternatingly: (i) directed to the reaction chamber by an inert gas flow from the source container towards the reaction chamber and then (ii) prevented from flowing from the source container to the reaction chamber by an inert gas flow in a reverse direction in a part of the conduit connecting the source container and the reaction chamber. The inert gas valving system is most particularly useful with liquid reactants that are vaporized prior to being employed in deposition. In other embodiments, the switching system can comprise conventional valves and valve control systems, particularly when more volatile gas sources are employed. - In the arrangements described above having separate gas inlets and separated sets of gas distribution channels in a block, each inlet can be connected to a different gas feed. For example, the separate channels can comprise a “spoke” arrangement, in which different spokes are connected to different reactant gas feeds.
- In the preferred embodiments, deposition of a film can be performed by maintaining a ΔT of, e.g., about 100° C. or more and, more preferably, about 200° C. or more between the blocks. In the
reactor 100 of FIG. 2, thelower block 160 is cooled and can be at a temperature below about 40° C. Theupper block 120 can be heated to a temperature of about 350° C. By the appropriate choice of the types of gases and gas flow ranges below and above thewafer 110, a wafer temperature between that of the upper andlower blocks - In other embodiments, the lower
upper block 150 can be heated, rather than cooled, but still maintained at a temperature that is lower than the desired wafer temperature, while the upper block 120 (FIGS. 3 and 6-10) is maintained at a temperature that is higher than the desired wafer temperature. - In yet another embodiment, the
upper block 120 can be maintained at a lower temperature than the desired wafer temperature. When the desired wafer temperature is, e.g., about 300° C., one can keep theupper block 120 at about 230° C. and thelower block 150 at about 330° C. As noted above, this can be realized by the appropriate choice of the types of gases and flows below and above thewafer 110. For example, because the temperature of thelower block 150 is relatively close to the desired wafer temperature, one possibility is to physically keep thewafer 110 close to thelower block 150 to heat thewafer 110 to the desired wafer temperature, which is closer to the lower block temperature than it is to the upper block temperature. The temperature of theupper block 120 is preferably not be so low that condensation of the reactant occurs on it. In other words, for the block at about 230° C., the process is not in the L1 regime, as discussed above regarding FIG. 1. Preferably, for theupper block 120 at about 230° C., the process is in the L2 regime. - Processing according to the embodiments of the invention offers numerous advantages. For example, for embodiments employing separated channels for each reactant, by eliminating pre-mixing of the gases in the gas introduction manifold up to the point where the gases enter the deposition volume, deposition in the gas channels leading to the reaction chamber is substantially prevented. In addition, a small nitrogen purge is preferably constantly flowed through the gas channels to ensure that the gas inlet system remains clean up to the final injection point facing the wafer.
- By preferably keeping the temperature of the upper block outside the window for optimal ALD growth, but outside the range in which thermal decomposition can occur and outside the range in which condensation can occur, deposition on the upper block is also substantially prevented. To prevent thermal decomposition or condensation, the temperature of the upper block can be kept sufficiently below (e.g., about 70° C.) or above, respectively, that of the wafer. As noted above, in addition to the wafer process temperature, the selection of temperatures also depends on the reactants used. Similarly, the temperature of the lower block is preferably also outside of the window for optimal ALD growth. Note that all the embodiments described herein can simply be inverted so that the reactants flow through the lower block, or reactants can flow through both blocks for double-sided deposition.
- The inert gas that preferably flows through the gap in between the wafer and the lower block substantially prevents deposition on the backside of the wafer, or on the lower block surface facing the wafer. Calculations indicate that the reactants present in the flow above the wafer typically will not penetrate the narrow space between the wafer and the lower block. This is because the flow rate below the wafer is relatively large (greater than about 5 slm) and the gap narrow (about 0.2 mm). As the Reynolds number is very small, this flow is expected to be substantially laminar.
- As none of the reactants typically enter the volume between the wafer and the lower block, back feeding of reactants from this volume to the volume between the wafer and the upper block, into which reactants are introduced, can be substantially eliminated. Consequently, by preventing the different reactant gases from coming into contact with one another, CVD growth can be prevented.
- The preferred embodiments advantageously allow reactants to be switched quickly. In principle, gas switching is much faster at low pressures than under atmospheric conditions. This has been a primary reason why conventional ALD reactors operate at reduced pressures. However, the extremely small reaction volume in a reactor according to the preferred embodiments, such as a Levitor® reactor, in combination with relatively large gas flows, ensures a high gas velocity, even at atmospheric pressure. For example, when a flow of, e.g., about 10 slm is distributed in the volume above the wafer, and the gap is about 0.2 mm, the gas velocity at the edge of a 300 mm wafer is about 0.9 m/s at room temperature. More generally, the gas velocity is preferably arranged to be about 0.1 m/s to 10 m/s. Under the preferred conditions, a typical distance of the wafer radius, i.e., about 0.15 m, is traversed in about 0.02 seconds to about 2 seconds, or about 0.17 seconds in this particular example. At temperatures above room temperature this time will even be shorter due to thermal expansion of the gases. Thus, the reactors can be quickly cleared of reactants for the next reactant pulse, regardless of whether separated gas channels are provided for the reactants.
- In some embodiments, rotation (preferably about 20 rpm) of the wafer can be introduced by flowing gas through a number of additional gas channels. Arrangements for such rotation are known to those of skill in the art and was accomplished, for example, in the first version of the Levitor® 4000 reactor, produced by ASM International N.V. of Bilthoven, The Netherlands. Such rotation can improve uniformity by more evenly exposing the wafer to reactants. Also, the uniformity can be further improved by the fact that the wafer tends to be self-centering in such arrangements, positioning itself at the center of the reactor.
- In addition, in reactors according to the preferred embodiments, the heat-up rate is fast, preferably on the order of a few seconds. In contrast, in conventional systems this can take several 10's of seconds. Thus, the fast heat-up rate minimizes the time needed for the wafer to reach the equilibrium temperature.
- Also, particle generation is typically low. This is because the preferred large flow above the wafer prevents foreign material from penetrating the space above the wafer. Moreover, by preventing deposition on the blocks facing a wafer, build up of films on that surface is prevented, thus preventing formation of particles.
- The cost of processing according to the preferred embodiments is advantageously low. The main reasons for this are that no vacuum is required, and, given the relatively low temperatures involved, easy to machine materials (e.g., aluminum) can be used for the reactor.
- The footprint of the preferred reactors is also advantageously small. For example, the current Levitor® LT module has a width of about 45 cm and a depth of about 75 cm. In addition, two LT modules can be placed above one another, further minimizing the area occupied by the reactors.
- In an advantageously simple embodiment of the invention, the apparatus described above is operated at atmospheric pressure, so that the use of vacuum pumps can be omitted. It is not necessary, however, to operate the apparatus at atmospheric pressure. A pressure of about 10 mbar to about 100 mbar would still be high enough to have a wafer supported by a gas cushion. In addition, an advantage of reducing the pressure is that it results in an expansion of the gas flows and a more efficient purging of the reaction space.
- It will be appreciated that while discussed with reference to a Levitor® reactor for ease of description, the preferred embodiments are not limited to such a reactor. For example, the gas distribution system and the heating arrangement described above can readily be applied to other reactors to similar advantageous effect.
- It will also be appreciated that although the invention has been described in terms of certain preferred embodiments, various other combinations, omissions, substitutions and modifications can be made to the embodiments described above without departing from the scope of the invention. All such modifications and changes are intended to fall within the scope of the invention. Accordingly, the present invention is not intended to be limited by the descriptions of the preferred embodiments, but instead is to be defined by referenced to the appended claims.
Claims (61)
1. A film deposition station for depositing a film onto a substrate comprising, a first part and a second part for accommodating a semiconductor substrate between them, the first part and the second part positioned opposite each other and parallel to the substrate upon retention of the substrate between the first and second parts, wherein the first part and the second part are configured to be spaced less than about 2 mm from a major surface of a substrate accommodated between them, wherein at least one of the parts is provided with a heater for heating that part, and wherein each part is provided with a set of gas supply channels connected to a source of gas, wherein the source of gas for the first part is configured to supply mutually reactive reactants in a sequence of alternating, separated pulses for atomic layer deposition (ALD).
2. The film deposition station of claim 1 , wherein each set of gas supply channels comprises a plurality of horizontal gas dispersion channels connected to a plurality of vertical gas injection channels, the plurality of horizontal gas dispersion channels providing gas to the plurality of vertical gas injection channels, wherein the plurality of vertical gas injection channels are configured to discharge gas onto a major surface of the substrate.
3. The film deposition station of claim 2 , wherein the horizontal gas dispersion channels have a larger cross-sectional area than the vertical gas injection channels.
4. The film deposition station of claim 3 , wherein the horizontal gas dispersion channels each have a diameter of about 3-5 mm and the vertical gas injection channels each have a diameter of about 1-3 mm.
5. The film deposition station of claim 2 , wherein the vertical gas injection channels each comprise a first and a second section, wherein the first section opens to one of the plurality of horizontal gas dispersion channels and has a larger cross-sectional area than the second section, wherein the second section opens to a space for accommodating the substrate.
6. The film deposition station of claim 2 , wherein the vertical gas injection channels are positioned to extend uniformly across an entire major surface of the substrate.
7. The film deposition station of claim 2 , wherein the horizontal gas dispersion channels extend radially across an interior of the first and the second parts.
8. The film deposition station of claim 1 , wherein the mutually reactive reactants are supplied through the first part, wherein the first part comprises a set of separated gas supply channels for each reactant, wherein the sets of separated gas supply channels are vertically and horizontally displaced relative to one another.
9. The film deposition station of claim 1 , wherein the gas supply channels are configured to discharge gas to fully support the substrate between the first part and the second part.
10. The film deposition station of claim 1 , wherein one of the parts is configured to be at a higher temperature than the other one of the parts, wherein the film deposition station is configured to supply the reactants in alternating, separated pulses from the one of the parts that is at a higher temperature.
11. The film deposition station of claim 1 , wherein one of the parts is configured to be at a lower temperature than the other one of the parts, wherein the film deposition station is configured to supply the reactants in alternating, separated pulses from the one of the parts that is at a lower temperature.
12. The film deposition station of claim 1 , wherein the first part and the second part are configured to be spaced less than about 1 mm from a major surface of a substrate.
13. The film deposition station of claim 12 , wherein the first part and the second part are configured to be spaced less than about 0.5 mm from a major surface of a substrate.
14. The film deposition station of claim 1 , wherein the gas supply channels are configured to cause rotation of the substrate.
15. A reactor for semiconductor processing, comprising:
an upper reactor block and a lower reactor block for accommodating a semiconductor substrate therebetween,
wherein the upper and the lower reactor blocks are configured to be less than about 2 mm from a major surface of the substrate when the substrate is retained therebetween, and wherein the reactor is configured to discharge mutually reactive reactants from at least one of the reactor blocks to the substrate in sequential alternating, separated pulses, wherein the at least one of the reactor blocks comprises a set of gas channels configured to transport and discharge the sequential alternating separated pulses of reactant to the substrate.
16. The reactor of claim 15 , wherein the upper and the lower reactor blocks are configured to be heated to temperatures at which condensation or decomposition of the mutually reactive reactants is substantially prevented.
17. The reactor of claim 16 , wherein the upper and lower reactor blocks are configured to be heated to different temperatures.
18. The reactor of claim 17 , wherein the upper and the lower reactor blocks are configured to heat the substrate to a different temperature during each pulse.
19. The reactor of claim 15 , wherein the lower block is vertically movable relative to the upper block to allow for decreasing and increasing the distance between the substrate and the reactor blocks for loading and unloading of the substrate.
20. The reactor of claim 15 , wherein the upper block is configured to be at a lower temperature than the lower block, further comprising a removable shield attached to the lower block, wherein the reactor is configured to concentrate deposition of the at least two mutually reactive reactants on the removable shield relative to other surfaces of the reactor.
21. The reactor of claim 20 , wherein the removable heat shield is configured to be heated to the same temperature as the lower block.
22. The reactor of claim 15 , wherein the upper and the lower reactor blocks are configured to be less than about 1 mm from a major surface of the substrate.
23. A method of depositing a layer on a semiconductor substrate, comprising:
providing an apparatus having a first side section and a second side section located opposite one another, the side sections each having facing planar surfaces, wherein at least one of the side sections is heated to a temperature higher than about 200° C.;
placing the substrate in the apparatus between the first and second side sections; and
applying two gas streams, in opposing directions, from the first and second side sections to two opposing planar sides of the semiconductor substrate, wherein a spacing between each of the first and second side sections and the semiconductor substrate is at most about 2 mm, wherein the facing planar surfaces of the side sections extend completely across the opposing planar sides of the semiconductor substrate,
wherein at least one of the gas streams provides different reactants in a sequence of alternating, separated pulses for an atomic layer deposition (ALD) process.
24. The method of claim 23 , further comprising, after placing the semiconductor substrate between the side sections, moving the side sections closer to one another until the spacing between each of the side sections and the substrate is no more than about 2 mm.
25. The method of claim 24 , wherein one side section is at a first temperature and the other side section is at a second temperature.
26. The method of claim 25 , further comprising periodically changing at least one of the gas streams so that the substrate temperature is periodically switched between a first and a second substrate temperature, wherein a frequency for switching the substrate temperature substantially coincides with a frequency for alternating the reactants.
27. The method of claim 26 , further comprising switching the relative distance of the substrate to each of the first and the second side sections to switch between the first and the second substrate temperature.
28. The method of claim 26 , wherein the substrate is at the first temperature during supplying of a first reactant and wherein the substrate temperature is switched to the second substrate temperature and switched back to the first temperature again before supplying the first reactant in a next pulse.
29. The method of claim 23 , wherein a first gas is discharged from the first side section and a second gas is discharged from the second side section, wherein the second gas has thermal conduction properties different from those of the first gas.
30. The method of claim 23 , further comprising changing the composition of one of the gas streams.
31. The method of claim 30 , wherein changing the composition of one of the gas streams alters the temperature of the substrate.
32. The method of claim 23 , further comprising changing the flow of one of the gas streams to change a position of the substrate.
33. The method of claim 23 , wherein the side sections are massive relative to the substrate, wherein the side sections have sufficient heat capacity so that, when heated, heat is transferred to an unheated substrate loaded between the side sections with a negligible decrease in temperature of the side sections.
34. The method of claim 23 , further comprising cooling the substrate before removing the substrate from between the first and the second side sections.
35. The method of claim 23 , wherein applying two gas streams causes rotation of the substrate:
36. The method of claim 23 , wherein applying two gas streams suspends the substrate between the first and the second side sections without any mechanical support.
37. A method for semiconductor processing, comprising:
providing a processing apparatus having a first and a second reactor block;
positioning a substrate between the first and the second reactor blocks, wherein the substrate is less than about 2 mm from each of the first and the second reactor blocks after positioning;
discharging, from the first reactor block, mutually reactive reactants in alternating, temporally separated pulses onto the substrate; and
heating the substrate using the first or second reactor block to one or more desired substrate temperatures, wherein the first reactor block is set at a first temperature at which condensation or decomposition of the mutually reactive reactants is substantially prevented.
38. The method of claim 37 , wherein heating the substrate comprises setting the second reactor block at a second temperature.
39. The method of claim 38 , wherein the first temperature and the second temperature are outside of a temperature window in which optimal atomic layer deposition rates of the reactants being discharged occur.
40. The method of claim 39 , wherein the first temperature and the second temperature are different.
41. The method of claim 40 , wherein the first temperature and the second temperature differ by about 100° C. or more.
42. The method of claim 41 , wherein the first temperature and the second temperature differ by about 200° C. or more.
43. The method of claim 37 , wherein the first block is actively heated and the second block is actively cooled.
44. The method of claim 37 , wherein at least one of the mutually reactive reactants self-limitingly adsorbs on the substrate.
45. The method of claim 37 , wherein discharging mutually reactive reactants in alternating, temporally separated pulses comprises flowing each of the two mutually reactive reactants through separate sets of gas channels at different times.
46. The method of claim 45 , further comprising continuously flowing an inert gas through each separate set of gas channels.
47. The method of claim 46 , wherein the inert gas is nitrogen gas.
48. The method of claim 37 , wherein discharging mutually reactive reactants is performed with the apparatus operated at atmospheric pressure.
49. A method for semiconductor processing, comprising:
loading a substrate in a reaction chamber;
completely supporting the substrate on a gas cushion in the chamber; and
directing mutually reactive reactants in alternating, temporally separated pulses onto a major surface of the substrate while completely supporting the substrate on the gas cushion.
50. The method of claim 49 , wherein supporting the substrate comprises generating a gas cushion on each major side of the substrate.
51. The method of claim 49 , wherein the reaction chamber comprises two reactor blocks, wherein one reactor block is configured to be on one side of the substrate and the other reactor block is configured to be on an opposite side of the substrate, wherein each reactor block is positioning about 1 mm or less from the substrate after loading.
52. The method of claim 51 , wherein directing mutually reactive reactants comprises discharging all the mutually reactive reactants from the same reactor block.
53. The method of claim 49 , wherein a time from directing one reactant onto the major surface to directing the one reactant to the major surface again constitutes a deposition cycle, wherein about a monolayer or less of reactant is deposited on the substrate per deposition cycle.
54. The method of claim 49 , wherein directing mutually reactive reactants comprises maintaining and flowing the reactant in separate channels before discharging the reactants onto a major surface of the substrate.
55. A film deposition station for depositing a film onto a substrate, comprising:
a first part and a second part for accommodating a semiconductor substrate between them, the first part and the second part positioned opposite each other and parallel to the substrate upon retention of the substrate between the first and second parts, wherein the first part is provided with a first set of gas supply channels connected to a source for a first reactant and a second set of gas supply channels connected to a source for a second reactant, wherein the first and second set of gas supply channels are configured to keep the reactants separated until discharging the reactants out from the gas supply channels to the substrate, wherein the first and the second reactant are mutually reactive; and
controls to supply the first and the second reactant from the source for a first reactant and from the source for a second reactant in sequential alternating separated pulses for atomic layer deposition (ALD).
56. The film deposition station of claim 55 , wherein at least one of the parts is provided with a heater.
57. The film deposition station of claim 55 , wherein each set of gas supply channels comprises a plurality of horizontal gas dispersion channels connected to a plurality of vertical gas injection channels, the plurality of horizontal gas dispersion channels providing gas to the plurality of vertical gas injection channels, wherein the plurality of vertical gas injection channels are configured to discharge gas onto a major surface of the substrate.
58. The film deposition station of claim 57 , wherein the horizontal gas dispersion channels for one set of gas supply channels are horizontally displaced relative to the horizontal gas dispersion channels for the other set.
59. The film deposition station of claim 57 , wherein the horizontal gas dispersion channels for one set of gas supply channels are vertically displaced relative to the horizontal gas dispersion channels for the other set.
60. The film deposition station of claim 55 , wherein the second part is provided with a set of gas supply channels to discharge gas onto a second major surface of the substrate, opposite to the major surface.
61. The film deposition station of claim 55 , wherein the first and the second part are configured to be spaced less than about 2 mm from a major surface of the substrate accommodated between them.