US20040047394A1 - Method for predicting temperature, test wafer for use in temperature prediction, and method for evaluating lamp heating system - Google Patents
Method for predicting temperature, test wafer for use in temperature prediction, and method for evaluating lamp heating system Download PDFInfo
- Publication number
- US20040047394A1 US20040047394A1 US10/638,062 US63806203A US2004047394A1 US 20040047394 A1 US20040047394 A1 US 20040047394A1 US 63806203 A US63806203 A US 63806203A US 2004047394 A1 US2004047394 A1 US 2004047394A1
- Authority
- US
- United States
- Prior art keywords
- semiconductor layer
- test wafer
- wafer
- temperature
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A test wafer for use in wafer temperature prediction is prepared. The test wafer includes: first semiconductor layer formed in a crystalline state; second semiconductor layer formed in an amorphous state on the first semiconductor layer; and light absorption film formed over the second semiconductor layer. Next, the test wafer is loaded into a lamp heating system and then irradiating the test wafer with a light emitted from the lamp, thereby heating the second semiconductor layer through the light absorption film. Thereafter, a recovery rate, at which a part of the second semiconductor layer recovers from the amorphous state to the crystalline state at the interface with the first semiconductor layer, is calculated. Then, a temperature of the test wafer that has been irradiated with the light is measured according to a relationship between the recovery rate and a temperature corresponding to the recovery rate.
Description
- The present invention relates to a method for predicting temperature, a test wafer for use in temperature prediction, and a method for evaluating a lamp heating system using the test wafer. More particularly, this invention provides measures to predict more accurately the actual temperature or temperature distribution of a wafer to be loaded into the lamp heating system.
- A method for predicting the actual temperature of a wafer to be loaded into a thermal system, in which the wafer should be subjected to intense heat in a semiconductor device fabrication process, was disclosed in PCT International Publication No. WO 98/57146.
- In the Publication, an amorphous layer is formed in the uppermost part of a silicon wafer by implanting ions. Then, the silicon wafer including the amorphous layer is loaded into a thermal processing system and heated therein. In this manner, the actual temperature of the silicon wafer is predicted.
- The present inventors carried out various experiments on the known method for predicting temperature. As a result of these experiments, it was found that the actual wafer temperature could not be predicted accurately enough by the known method when the method was applied to a lamp heating system as described later.
- It is therefore a first object of the present invention to predict accurately the actual temperature or temperature distribution of a wafer to be loaded into a lamp heating system.
- It is a second object to evaluate whether or not the lamp heating system including a lamp is affected by light emitted from the lamp and transmitted through the wafer.
- In order to achieve the first object, according to the present invention, a method is used for predicting, using a test wafer, a temperature of a wafer to be loaded into a lamp heating system including a lamp. The method includes the steps of: a) preparing the test wafer, which includes a first semiconductor layer formed in a crystalline state, a second semiconductor layer formed in an amorphous state on the first semiconductor layer, and a light absorption film formed over the second semiconductor layer; b) loading the test wafer into the lamp heating system and then irradiating the test wafer with a light emitted from the lamp, thereby heating the second semiconductor layer through the light absorption film; c) calculating a recovery rate at which a part of the second semiconductor layer that has been heated recovers from the amorphous state to the crystalline state at the interface with the first semiconductor layer; and d) measuring a temperature of the test wafer that has been irradiated with the light, according to a relationship between the recovery rate and a temperature corresponding to the recovery rate.
- According to the inventive method, a test wafer for use in temperature prediction includes a light absorption film formed over an amorphous second semiconductor layer. The light absorption film absorbs light that has been emitted from a lamp and transmitted through a first and the second semiconductor layers not to contribute a thermal process performed on the semiconductor layers. Thus, a recovery rate for obtaining the actual wafer temperature can be calculated much more accurately by the thickness of the second semiconductor layer subjected to heat. As a result, the actual temperature of the wafer loaded into a lamp heating system can be predicted accurately.
- In one embodiment, at least a part of the light may have a wavelength at which the first semiconductor layer transmits the light. Then, the effects of the present invention can be obtained as intended.
- In this particular embodiment, the light preferably has a wavelength at which the first semiconductor layer has a transmittance to the light and the transmittance increases at a temperature range. Then, the effects of the present invention can be obtained as intended.
- In another embodiment, the light may have a wavelength from about 1.0 μm to about 3.0 μm, both inclusive.
- In still another embodiment, the first semiconductor layer and the second semiconductor layer may be made of silicon and the light absorption film may be made of a conductive film containing a metal.
- In this particular embodiment, the light absorption film is preferably made of a metal that is usable for forming a silicide and the lamp heating system is preferably used for a silicidation process. Then, the light absorption film acts as a metal film to be used for the silicidation process. Thus, wafer temperature prediction can be performed under the same conditions as in the silicidation process.
- In this particular embodiment, the temperature range is preferably from about 450° C. to about 600° C., both inclusive.
- In this particular embodiment, the test wafer preferably includes a barrier film that prevents the second semiconductor layer and the light absorption film from reacting together. This barrier film is preferably formed between the second semiconductor layer and the light absorption film.
- In yet another embodiment, the test wafer may have a diameter of about 30.5 cm (12 inches) or more.
- An inventive test wafer is used for predicting a temperature of a wafer to be loaded into a lamp heating system. The test wafer includes: a first semiconductor layer formed in a crystalline state; a second semiconductor layer formed in an amorphous state on the first semiconductor layer; and a light absorption film formed over the second semiconductor layer.
- In one embodiment, the test wafer may further include a barrier film that prevents the second semiconductor layer and the light absorption film from reacting together. This barrier film may be formed between the second semiconductor layer and the light absorption film.
- In another embodiment, the test wafer may have a diameter of about 30.5 cm (12 inches) or more.
- In order to achieve the second object, an inventive method is used for evaluating a lamp heating system including a lamp. Specifically, this method, which utilizes a transmittance to a light emitted from the lamp, is used for evaluating whether or not respective temperatures of a first test wafer and a second test wafer loaded in the lamp heating system are affected by the light. The method includes the step of a) preparing: the first test wafer including a first semiconductor layer formed in a crystalline state and a second semiconductor layer formed in an amorphous state on the first semiconductor layer; and the second test wafer including a third semiconductor layer formed in a crystalline state, a fourth semiconductor layer formed in an amorphous state on the third semiconductor layer, and a light absorption film formed over the fourth semiconductor layer. The method also includes the step of b) loading the first test wafer and the second test wafer into the lamp heating system and then irradiating the first test wafer and the second test wafer with the light, thereby heating the second semiconductor layer and heating the fourth semiconductor layer through the light absorption film. The method further includes the step of c) obtaining a first rate of variation in thickness of the second semiconductor layer with respect to a period of time in which the second semiconductor layer is subjected to heat, and obtaining a second rate of variation in thickness of the fourth semiconductor layer with respect to a period of time in which the fourth semiconductor layer is subjected to heat. The method further includes the step of d) comparing the first rate with the second rate, thereby judging that the temperature of the first test wafer is not easily affected by the light transmitted through the first test wafer if the first rate is equal to the second rate, while judging that the temperature of the first test wafer is easily affected by the light transmitted through the first test wafer if the first rate is smaller than the second rate.
- According to an inventive method for evaluating a lamp heating system, variation in thickness of a second semiconductor layer (amorphous layer) in a first test wafer including no light absorption film and that of a fourth semiconductor layer (amorphous layer) in a second test wafer including a light absorption film are compared with each other. Then, whether or not the lamp heating system is easily affected by light emitted from the lamp and transmitted through the semiconductor layers.
- In this case, the system that is easily affected by the light is a system in which the first test wafer transmits a relatively large amount of the light and thus has its real temperature differ greatly from a temperature indicated by a thermometer made up of, for example, a thermocouple provided in the system.
- FIG. 1 is a cross-sectional view illustrating the structure of a known test wafer for use in temperature prediction.
- FIGS. 2A and 2B are cross-sectional views schematically showing wafer temperature prediction using the known test wafer. FIG. 2A illustrates the structure of a lamp heating system and FIG. 2B illustrates the structure of a heater heating system.
- FIG. 3 shows a result of the prediction shown in FIGS. 2A and 2B, and is a graph showing relationships between the heating time of the test wafer and the thickness of a second semiconductor layer. (an amorphous layer).
- FIG. 4 is a graph showing variations of light absorption of a silicon wafer depending on the wavelength and temperatures.
- FIG. 5 is a cross-sectional view illustrating the structure of a test wafer for use in temperature prediction according to a first embodiment of the present invention.
- FIGS. 6A through 6C are cross-sectional views showing structures of the test wafer corresponding to respective process steps for forming the test wafer of the first embodiment.
- FIG. 7 is a cross-sectional view schematically showing the structure of a lamp heating system for use in wafer temperature prediction using the test wafer of the first embodiment.
- FIGS. 8A and 8B are cross-sectional views showing structures of the test wafer corresponding to respective process steps in the temperature prediction of the first embodiment.
- FIG. 9 is a diagram illustrating the distribution of temperatures in a wafer plane obtained by the temperature prediction of the first embodiment.
- FIG. 10 is a flowchart showing the procedures of evaluating a lamp heating system in accordance with a second embodiment of the present invention.
- FIG. 11 are cross-sectional views schematically showing two types of lamp heating systems for a thermal treatment in a method for evaluating the lamp heating systems in accordance with the second embodiment.
- FIGS. 12A and 12B show respective rates of decrease in thickness of amorphous layers formed in test wafers for use in the evaluating method of the second embodiment. FIG. 12A is a graph for a heating system that is affected by the structure of the wafer. FIG. 12B is a graph for a heating system that is not affected by the structure of the wafer.
- FIG. 13 is a graph showing a relationship between a recovery rate of an amorphous layer and a temperature.
- Hereinafter, the temperature predicting method using a known test wafer, disclosed in PCT International Publication No. WO 98/57146, will be described. The known test wafer includes a first semiconductor layer formed in a crystalline state and a second semiconductor layer formed in an amorphous state on the first semiconductor layer.
- First, the second semiconductor layer of the test wafer is measured beforehand with a spectroscopic ellipsometer. At this time, the second semiconductor layer is supposed to have a thickness t0. Then, the test wafer is loaded into a thermal system, e.g., a thermal processing system, and subjected to heat for a period of time a (s). After being subjected to heat, the second semiconductor layer is supposed to have a thickness t1. Then, the thickness t1 is measured with a spectroscopic ellipsometer. In this case, the second semiconductor layer in the amorphous state has its thickness decreased from t0 to t1. This is because crystals start to grow epitaxially from the interface between the first and second semiconductor layers, thereby crystallizing the lowermost part of the second semiconductor layer.
- Next, using the initial thickness t0 and the thickness t1 of the second semiconductor layer, the decrease in thickness of the second semiconductor layer per unit time, i.e., the rate R at which that part of the second semiconductor layer recovers from the amorphous state to crystalline state, is calculated by
- R=|t1−t0|/a
- where 0≦t1≦t0.
- If the recovery rate R given by this equation is applied to the graph shown in FIG. 13, the actual temperature of a silicon wafer101 to be processed can be predicted. The graph shown in FIG. 13 illustrates a relationship between the recovery rate R and the temperature T and was drawn after J. Appl. Phys. Vol. 48, No. 10 (1997), p. 4234. It should be noted that the amorphous second semiconductor layer may be formed by implanting arsenic (As) ions into the wafer 101.
- The present inventors carried out an experiment of measuring the actual wafer temperatures, using a known
test wafer 10A shown in FIG. 1, in alamp heating system 1 as shown in FIG. 2A and aheater heating system 2 as shown in FIG. 2B. - As shown in FIG. 1, the
test wafer 10A includes afirst semiconductor layer 11 a of crystalline silicon and asecond semiconductor layer 11 b of amorphous silicon formed on thefirst semiconductor layer 11 a. - As shown in FIG. 2A, the
lamp heating system 1 includeshalogen lamps 4, which have been provided on the ceiling of achamber 3 and emit light having a wavelength of 1 μm or more. On the other hand, theheater heating system 2 includes aheater 5 over achamber 3. Although not shown, after thetest wafer 10A has been loaded into each of theheating systems test wafer 10A. - FIG. 3 shows relationships between the heating time of the
test wafer 10A and the thickness of the second semiconductor layer (i.e., an amorphous layer) 11 b. In FIG. 3, the ordinate represents the thickness of the amorphous layer, while the abscissa represents the heating time of the wafer. In this case, thetest wafer 10A loaded into each of theheating systems test wafer 10A is measured using the thermocouple placed in each of theheating systems - As shown in FIG. 3, if the decreases in thickness of the amorphous layers loaded into the lamp and
heater heating systems lamp heating system 1 is smaller than that formed with theheater heating system 2. - From these recovery rates and the graph shown in FIG. 13, it was found that the thermocouple provided in the
heater heating system 2 indicates the real temperature of thewafer 10A, while the thermocouple provided in thelamp heating system 1 does not indicate the real temperature of thewafer 10A. - The present inventors carried out various experiments to know why the decreases in thickness of the second semiconductor layers11 b differ greatly between the systems used for heating the
test wafer 10A. As a result of these experiments, the following conclusion was drawn. - Specifically, as shown in FIG. 4, the
silicon test wafer 10A has its absorptance with respect to light emitted from the lamps decreased at a temperature (i.e., the real temperature) of about 450-600° C. in a wavelength range from 1 μm to 3 μm. In other words, thetest wafer 10A has its transmittance to light emitted from the lamps increased. Thus, even when the temperature indicated by the thermocouple increases due to the emission of light, the real temperature of thetest wafer 10A does not reach the temperature indicated by the thermocouple. As a result, the real temperature of thetest wafer 10A obtained by using the recovery rate is erroneous as compared with the temperature indicated by the thermocouple provided in thelamp heating system 1. - As described above, the present inventors found that the actual wafer temperature in a
lamp heating system 1 cannot be accurately predicted by using atest wafer 10A, including asecond semiconductor layer 11 b of amorphous silicon formed on thefirst semiconductor layer 11 a, with a temperature to be predicted set in a range from about 450° C. to about 600° C. - Based on this finding, a test wafer including a light absorption film formed in the uppermost part of the test wafer was invented for absorbing light emitted from the lamps.
- Moreover, whether or not the actual wafer temperature in a lamp heating system is affected by light emitted from the lamps can be evaluated by comparing a decrease rate of an amorphous layer in a test wafer including no light absorption film with that of a test wafer including a light absorption film.
- If the
second semiconductor layer 11 b of thetest wafer 10A is formed by implanting, for example, arsenic ions, the temperature that can be predicted ranges from, for example, about 475° C. to about 575° C., depending on the conditions for the ion implantation. - Preferred
Embodiment 1 - Hereinafter, a first embodiment of the present invention will be described with reference to the drawings.
- FIG. 5 shows a cross-sectional structure of a test wafer for use in temperature prediction according to the first embodiment.
- As shown in FIG. 5, a
test wafer 10B according to the first embodiment is made up of: afirst semiconductor layer 11 a of single crystalline silicon; asecond semiconductor layer 11 b of amorphous silicon; abarrier film 12 of silicon dioxide; and alight absorption film 13 of titanium nitride (TiN), for example. Thesecond semiconductor layer 11 b is formed on thefirst semiconductor layer 11 a and has a thickness of 41 nm. Thebarrier film 12 is formed on thesecond semiconductor layer 11 b and has a thickness of about 3 nm. Thelight absorption film 13 is formed on thebarrier film 12 and has a thickness of about 20 nm. - Hereinafter, process steps for forming the
test wafer 10B having such a structure will be described with reference to FIGS. 6A through 6C. - First, as shown in FIG. 6A, a
silicon wafer 11A is thermally oxidized in a dinitrogen oxide (N2O) ambient, thereby forming abarrier film 12 of silicon dioxide with a thickness of about 3 nm in the uppermost part of thesilicon wafer 11A. - Next, as shown in FIG. 6B, arsenic ions are implanted into the
silicon wafer 11A through thebarrier film 12 at a dose of about 3×1014 cm−2 with an accelerating voltage of about 30 keV, thereby forming asecond semiconductor layer 11 b of amorphous silicon in thesilicon wafer 11A. As a result, the part of thesilicon wafer 11A other than thesecond semiconductor layer 11 b now becomes afirst semiconductor layer 11 a of single crystalline silicon. - Then, as shown in FIG. 6C, a sputtering process is performed in a nitrogen ambient using a titanium target, for example, thereby depositing a
light absorption film 13 of titanium nitride over thebarrier film 12. - If the
test wafer 10B of the first embodiment is applied to a lamp heating system, thelight absorption film 13 formed in the uppermost part of thetest wafer 10B absorbs light emitted from the lamps, even in a situation where the real temperature of thetest wafer 10B ranges from about 450° C. to about 600° C. and a wavelength of the light ranges from about 1.0 μm to about 3.0 μm. As a result, transmittance of thetest wafer 10B to the light does not change in such a situation. - As described above, some lamp heating systems include lamps that emit light with a wavelength range or a temperature range where a silicon wafer transmits a large percentage of the light. If the
test wafer 10A including only thesecond semiconductor layer 11 b of amorphous silicon in the uppermost part thereof is applied to such systems, the actual wafer temperature cannot be accurately predicted. - In contrast, if the
test wafer 10B of the first embodiment is applied, thelight absorption film 13 that has been formed in the uppermost part thereof and faces a light source absorbs light emitted from the lamps. As a result, the actual wafer temperature can be accurately predicted. - In the first embodiment, the
light absorption film 13 is made of titanium nitride (TiN). However, the present invention is not limited to this embodiment. That is to say, even when the transmittance of the silicon wafer to light emitted from the lamps varies according to the temperature of the wafer, a material may be used so long as the material absorbs the light. For example, a metal of, e.g., cobalt (Co), nickel (Ni) or platinum (Pt) or a metal compound including such a metal may be used. - If a metal such as titanium, cobalt, nickel or platinum, which can be used for silicidation, is used for a
light absorption film 13 of atest wafer 10B, temperature prediction using thetest wafer 10B is preferably performed on a process where a metal film is deposited over a silicon wafer. The temperature prediction is more preferably applied to a heating system for silicidation process. This is because a temperature of thetest wafer 10B can be measured in the same situation as that in an actual process. - The
test wafer 10B of the first embodiment includes abarrier film 12 of silicon dioxide between thelight absorption film 13 andsecond semiconductor layer 11 b. Thebarrier film 12 does not always have to be provided. However, in a situation where thesecond semiconductor layer 11 b is silicided with thelight absorption film 13, thebarrier film 12 is preferably provided because thebarrier film 12 will acts as a protective film that prevents thesecond semiconductor layer 11 b from being silicided. - The
barrier film 12 is not necessarily made of silicon dioxide, but may be made of silicon nitride or silicon oxinitride. - The first and second semiconductor layers11 a and 11 b of the
test wafer 10B are not necessarily made of silicon, but may be made of gallium arsenide (GaAs), germanium (Ge) or indium phosphide (InP). - Hereinafter, a method for predicting the actual temperature of a wafer, using the
test wafer 10B of the first embodiment will be described. - First, as shown in FIG. 7, the
test wafer 10B including asecond semiconductor layer 11 b with an initial thickness to of 41 nm is loaded into achamber 3 of a rapid thermal annealing (RTA)system 2A for heating a wafer.Halogen lamps 4 are provided on the ceiling of thischamber 3. - Next, the
test wafer 10B is subjected to heat at a temperature of 550° C. for 30 seconds. At this time, the temperature indicated by a thermometer, which is made up of a thermocouple (not shown), for example, and provided in theRTA system 2A, is used for setting the temperature inside the chamber. - Then, as shown in FIG. 8A, the
test wafer 10B is unloaded from thechamber 3. Thereafter, as shown in FIG. 8B, thelight absorption film 13 of thetest wafer 10B is etched away using a chlorine gas, for example. The interface between the non-processed first and second semiconductor layers 11 a and 11 b is indicated as the broken line drawn in thefirst semiconductor layer 11 a shown in FIGS. 8A and 8B. - The
light absorption film 13 is removed so as to measure a thickness t1 of the processedsecond semiconductor layer 11 b with a spectroscopic ellipsometer. Subsequently, the thicknesses t1 of the processedsecond semiconductor layer 11 b are measured through thebarrier film 12 with a spectroscopic ellipsometer at points all over the surface of thetest wafer 10B. - Thereafter, the difference between the initial thickness t0 of the non-processed second semiconductor layer (amorphous layer)11 b and the thickness t1 of the processed
second semiconductor layer 11 b is calculated, thereby obtaining a recovery rate R per unit time by - R=|t1−t0|/a
- where 0≦t1≦t0.
- If the recovery rate R given by this equation is applied to the graph shown in FIG. 13, the actual temperature is predicted.
- Since the
test wafer 10B has the same structure as a silicon wafer to be loaded into a heating system and made into semiconductor chips, the actual temperature of the wafer to be loaded can be predicted accurately. In addition, as shown in FIG. 9, the in-wafer-plane distribution of temperatures can also be predicted more accurately at points all over the wafer, including the periphery as well as the center thereof. As a result, even for a wafer that has a diameter of 30.5 cm (12 inches) or more and thus is likely to lack in-wafer-plane uniformity of temperatures, the wafer temperature can be easily controlled as intended. - Moreover, it is also possible to detect the difference between the actual wafer temperature and a temperature that has been set using the temperature indicated by the thermometer provided in the
RTA system 2A. - In this embodiment, the RTA system using halogen lamps as the light source thereof has been described. Alternatively, any other heating system with a lamp that emits light as the heat source thereof may be used. Even if the
test wafer 10B of the first embodiment is applied to a system where a wafer transmits light emitted from the lamp in a temperature range, and thus having a temperature thereof lower than a temperature that has been set, the actual wafer temperature can still be accurately predicted using no thermocouple. - Preferred
Embodiment 2 - Hereinafter, a second embodiment of the present invention will be described with reference to the drawings.
- FIG. 10 shows a flowchart illustrating the procedure for evaluating a lamp heating system in accordance with the second embodiment.
- According to the second embodiment, temperature predictions are preformed under the same conditions using two types of test wafers with mutually different structures, thereby evaluating whether or not a temperature indicated by a thermometer provided in a lamp heating system is affected by a transmittance of a wafer with respect to light emitted from the lamps, i.e., by the structure of the wafer.
- Specifically, if a wafer including an insulating or a conductive film and a wafer including neither insulating nor conductive film are used, it is possible to determine whether or not temperatures of the wafers indicated by thermometers provided in the lamp heating system are different from each other. The light irradiated onto the wafers is used for not only heating the wafers but also measuring temperatures of the wafers during the heat treatment.
- In the second embodiment, the
test wafer 10A shown in FIG. 1 having the exposedsecond semiconductor layer 11 b is used as a first wafer for the two types of the test wafers. On the other hand, thetest wafer 10B shown in FIG. 5 in which thesecond semiconductor layer 11 b is covered with thebarrier film 12 andlight absorption film 13 is used as a second wafer for the two types of the test wafers. - Hereinafter, a method for evaluating a lamp heating system will be described in detail.
- First, in the first step ST1 shown in FIG. 10, a first set of first and
second wafers chamber 3 of a first or a secondlamp heating system second wafers - Next, in the second step ST2 shown in FIG. 10, the first set of
wafers lamp heating system 21 is heated at a temperature of 550° C. for 30 seconds. Subsequently, the first set ofwafers second wafers wafers lamp heating system 22, the first set ofwafers wafers - Thereafter, in the third step ST3, the second set of
wafers systems wafers second wafer 10B with thelight absorption film 13, after thelight absorption film 13 has been removed, the thickness of the amorphous layer is measured. - Then, in the fifth step ST5, a decrease rate (a first decrease rate) of the amorphous layer in the
first wafer 10A and a decrease rate (a second decrease-rate) of the amorphous layer in thesecond wafer 10B are calculated, for example. In this case, the decrease rate is, a rate of decrease in thickness of the amorphous layer per unit time. - FIG. 12A shows the respective first and second decrease rates of the first and
second wafers lamp heating system 21. FIG. 12B shows the respective first and second decrease rates of the first andsecond wafers lamp heating system 22. In the second embodiment, the variations in thickness of the amorphous layers in the first andsecond wafers test wafers - Next, in the sixth step ST6, whether or not the temperatures indicated by the thermometers provided in the
heating systems - Specifically, as shown in FIG. 12A, the first decrease rate in the
first wafer 10A including nolight absorption film 13 is smaller than that in thesecond wafer 10B including thelight absorption film 13. This shows that thesecond semiconductor layer 11 b in thefirst wafer 10A is not heated to the same temperature as thesecond semiconductor layer 11 b in thesecond wafer 10B. In other words, thefirst wafer 10A in the firstlamp heating system 21 unintentionally transmits at least part of the light emitted from the lamps, and hence does not have its real temperature increased to the same extent as that of thesecond wafer 10B. Thus, the firstlamp heating system 21 is affected by the structure of a wafer. - On the other hand, as shown in FIG. 12B, the first decrease rate in the
first wafer 10A is equal to that in thesecond wafer 10B. That is to say, thefirst wafer 10A in the secondlamp heating system 22 hardly transmits light emitted from the lamps, and hence has its real temperature increased to the same extent as that of thesecond wafer 10B. Thus, the secondlamp heating system 22 is not affected by the structure of a wafer. - In this manner, whether or not a temperature indicated by a thermometer provided in a lamp heating system is affected by the structure of a wafer can be determined.
- In addition, if this evaluation is applied to a system such as the first
lamp heating system 21 that is affected by the structure of a wafer, thesecond wafer 10B having a constant transmittance to light emitted from the lamps is effective in predicting the actual wafer temperature accurately. - On the other hand, to predict, the actual wafer temperature in a system such as the second
lamp heating system 22 that is not affected by the structure of a wafer, either of the first andsecond wafer first wafer 10A having no light absorption film is preferably used. - In the second embodiment, a recovery rate at which part of the
second semiconductor layer 11 b recovers to a crystalline layer is not calculated. This is because it is sufficient to determine whether or not a lamp heating system itself is affected by the structure of a wafer, even without predicting the actual wafer temperature by calculating the recovery rate.
Claims (13)
1. A method for predicting, using a test wafer, a temperature of a wafer to be loaded into a lamp heating system including a lamp, the method comprising the steps of:
a) preparing the test wafer, which includes a first semiconductor layer formed in a crystalline state, a second semiconductor layer formed in an amorphous state on the first semiconductor layer, and a light absorption film formed over the second semiconductor layer;
b) loading the test wafer into the lamp heating system and then irradiating the test wafer with a light emitted from the lamp, thereby heating the second semiconductor layer through the light absorption film;
c) calculating a recovery rate at which a part of the second semiconductor layer that has been heated recovers from the amorphous state to the crystalline state at the interface with the first semiconductor layer; and
d) measuring a temperature of the test wafer that has been irradiated with the light, according to a relationship between the recovery rate and a temperature corresponding to the recovery rate.
2. The method of claim 1 , wherein at least a part of the light has a wavelength at which the first semiconductor layer transmits the light.
3. The method of claim 2 , wherein the light has a wavelength at which the first semiconductor layer has a transmittance to the light, the transmittance increasing at a temperature range.
4. The method of claim 1 , wherein the light has a wavelength from about 1.0 μm to about 3.0 μm, both inclusive.
5. The method of claim 1 , wherein the first semiconductor layer and the second semiconductor layer are made of silicon and the light absorption film is made of a conductive film containing a metal.
6. The method of claim 5 , wherein the light absorption film is made of a metal that is usable for forming a silicide and the lamp heating system is used for a silicidation process.
7. The method of claim 3 , wherein the temperature range is from about 450° C. to about 600° C., both inclusive.
8. The method of claim 5 , wherein the test wafer includes a barrier film that prevents the second semiconductor layer and the light absorption film from reacting together, the barrier film being formed between the second semiconductor layer and the light absorption film.
9. The method of claim 1 , wherein the test wafer has a diameter of about 30.5 cm or more.
10. A test wafer for predicting a temperature of a wafer to be loaded into a lamp heating system, the test wafer comprising:
a first semiconductor layer formed in a crystalline state;
a second semiconductor layer formed in an amorphous state on the first semiconductor layer; and
a light absorption film formed over the second semiconductor layer.
11. The test wafer of claim 10 further comprising a barrier film that prevents the second semiconductor layer and the light absorption film from reacting together, the barrier film being formed between the second semiconductor layer and the light absorption film.
12. The test wafer of claim 10 , wherein the test wafer has a diameter of about 30.5 cm or more.
13. A method for evaluating a lamp heating system including a lamp, the method, which utilizes a transmittance to a light emitted from the lamp, is used for evaluating whether or not respective temperatures of a first test wafer and a second test wafer loaded in the lamp heating system are affected by the light, the method comprising the steps of:
a) preparing the first test wafer, which includes a first semiconductor layer formed in a crystalline state and a second semiconductor layer formed in an amorphous state on the first semiconductor layer, and the second test wafer, which includes a third semiconductor layer formed in a crystalline state, a fourth semiconductor layer formed in an amorphous state on the third semiconductor layer, and a light absorption film formed over the fourth semiconductor layer;
b) loading the first test wafer and the second test wafer into the lamp heating system and then irradiating the first test wafer and the second test wafer with the light, thereby heating the second semiconductor layer and heating the fourth semiconductor layer through the light absorption film;
c) obtaining a first rate of variation in thickness of the second semiconductor layer with respect to a period of time in which the second semiconductor layer is subjected to heat, and obtaining a second rate of variation in thickness of the fourth semiconductor layer with respect to a period of time in which the fourth semiconductor layer is subjected to heat; and
d) comparing the first rate with the second rate, thereby judging that the temperature of the first test wafer is not easily affected by the light transmitted through the first test wafer if the first rate is equal to the second rate, while judging that the temperature of the first test wafer is easily affected by the light transmitted through the first test wafer if the first rate is smaller than the second rate.