US20030186630A1 - Reinforced chemical mechanical planarization belt - Google Patents

Reinforced chemical mechanical planarization belt Download PDF

Info

Publication number
US20030186630A1
US20030186630A1 US10/112,447 US11244702A US2003186630A1 US 20030186630 A1 US20030186630 A1 US 20030186630A1 US 11244702 A US11244702 A US 11244702A US 2003186630 A1 US2003186630 A1 US 2003186630A1
Authority
US
United States
Prior art keywords
polymeric material
belt
fabric
continuous loop
processing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/112,447
Inventor
Jibing Lin
Diane Hymes
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lam Research Corp
Original Assignee
Lam Research Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lam Research Corp filed Critical Lam Research Corp
Priority to US10/112,447 priority Critical patent/US20030186630A1/en
Assigned to LAM RESEARCH CORPORATION reassignment LAM RESEARCH CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HYMES, DIANE J., LIN, JIBING
Priority to JP2003576832A priority patent/JP2005520335A/en
Priority to CNA038056542A priority patent/CN1639034A/en
Priority to PCT/US2003/007389 priority patent/WO2003078859A2/en
Priority to KR10-2004-7014272A priority patent/KR20040105766A/en
Priority to AU2003213823A priority patent/AU2003213823A1/en
Priority to EP03711516A priority patent/EP1483182A4/en
Priority to TW092105436A priority patent/TW586158B/en
Publication of US20030186630A1 publication Critical patent/US20030186630A1/en
Abandoned legal-status Critical Current

Abstract

A processing belt for use in chemical mechanical planarization (CMP), and methods for making the same, are provided. Embodiments of the processing belt include a polymeric material reinforced with a woven fabric or synthetic material encased between the polymeric material and an additional polymeric material layer to define the processing belt. The processing belt is fabricated so that the woven fabric forms a continuous loop and is positioned against a surface of the polymeric material. The additional polymeric material layer is applied over the woven fabric, permeating the woven fabric to bond to the polymeric material forming an integral structure of woven fabric reinforced polymeric material.

Description

    BACKGROUND OF THE INVENTION
  • 1. Field of the Invention [0001]
  • The present invention relates generally to wafer preparation belts, and more specifically to the fabrication of belt materials used in chemical mechanical planarization apparatus. [0002]
  • 2. Description of the Related Art [0003]
  • In the fabrication of semiconductor devices, a plurality of layers are typically disposed over a substrate, and features are defined in and through the layers. A surface topography of the substrate or wafer can become irregular during fabrication processes, and an un-corrected irregularity increases with the addition of subsequent layers. Chemical Mechanical Planarization (CMP) has developed as a fabrication process utilized to planarize the surface of a semiconductor wafer, as well as to perform additional fabrication processes including polishing, buffing, substrate cleaning, etching processes, and the like. [0004]
  • In general, CMP processes involve the application of a substrate or wafer against a processing surface with a controlled pressure. Both the processing surface and the wafer are caused to rotate, spin, or otherwise move independently of one another to create a frictional force for planarization and to ensure the entire surface of the wafer is consistently and controllably processed. Typical CMP apparatus include linear belt processing systems in which a belt having a processing surface is supported between two or more drums or rollers which move the belt through a rotary path presenting a flat processing surface against which the wafer is applied. The wafer is typically supported and rotated by a wafer carrier, and a polishing platen is configured on the underside of the belt traveling in its circular path. The platen provides a stable surface over which the belt travels, and the wafer is applied to the processing surface of the belt against the stable surface provided by the platen. In some applications, abrasives in an aqueous solution known as slurry is introduced to facilitate and enhance the planarization or other CMP process. [0005]
  • Additional CMP apparatus include rotary CMP processing tools having a circular pad configuration for the processing surface, an orbital CMP processing tool similar to the circular CMP processing tool, a sub-aperture CMP processing tool, and other CMP processing systems providing a plurality of apparatus and configurations that, in general, utilize friction to planarize, scrub, polish, buff, clean, or otherwise process the surface of a semiconductor wafer having integrated circuits or other structures fabricated thereon. [0006]
  • In the linear belt CMP system, the belt and processing surface are typically fabricated to provide a stable structure to withstand the stresses of the belt and drum configuration, as well as a stable processing surface upon which precise and controllable planarization can occur. In addition to the stretching and contraction caused by the belt and processing surface traveling around the drums that drive the system, the belt and processing surface are typically in a wet environment from the liquid from slurry and rinsing operations. Belts and processing surfaces are typically constructed of a plurality of materials such as, by way of example, a stainless steel supporting layer, a cushioning layer, and one or more processing surface layers. The plurality of layers are joined by adhesives, bonding, stitching, and the like to form the continuous belt structure with an outwardly facing processing surface against which a wafer is applied in a CMP process. [0007]
  • The fabrication of linear belts in a plurality of layers as described provides the necessary support to substantially prevent the stretching of linear CMP belts, but such belts can be difficult to work with, and manufacturing costs associated with belt construction are increased. Some CMP processing belts include substantially polymer material without the additional layers described above. The substantially polymer material belts, however, tend to stretch and otherwise deform with continued use. Attempts to reinforce substantially polymer CMP processing belts have been largely unsuccessful, with functional belts substantially resulting in multi-layer processing belts as described above. [0008]
  • Linear belts used in linear belt CMP systems can be costly to manufacture, and can be time consuming to replace. Replacement of linear belts requires down time for the CMP system resulting in decreased through put and increased manufacturing costs. Multiple-layer linear belts can be subject to such failures as delamination or separation of the layers due to such factors as the contraction and stretching forces during use, and the breakdown of adhesives or other bonding techniques over time and accelerated in the wet CMP environment. [0009]
  • In view of the foregoing, what is needed are methods, processes, and apparatus to fabricate a linear CMP processing belt that is resilient to the stresses of use, is less likely to delaminate or otherwise separate, is economical and easy to manufacture, and is easy to work with in a plurality of CMP processing tools and environments. [0010]
  • SUMMARY OF THE INVENTION
  • Broadly speaking, the present invention fills these needs by providing a reinforced polymeric CMP processing belt. The present invention can be implemented in numerous ways, including as a process, an apparatus, a system, a device, or a method. Several embodiments of the present invention are described below. [0011]
  • In one embodiment, a processing belt for use in chemical mechanical planarization is disclosed. The processing belt includes a fabric belt and a polymeric material encasing the fabric belt to define the processing belt to be used in chemical mechanical planarization operations. [0012]
  • In another embodiment, a belt for use in chemical mechanical planarization processing is disclosed. The belt includes a polymeric material cast into a continuous loop to define the belt, and a reinforcing fabric embedded between the polymeric material and an additional polymeric material layer. The reinforcing fabric is defined as a continuous loop within the polymeric material and the additional polymeric material layer. [0013]
  • In yet another embodiment, a processing belt for use in chemical mechanical planarization is disclosed. The processing belt includes a continuous loop reinforcing woven fabric, a continuous loop polymeric material, and a continuous loop additional polymeric material layer. The continuous loop additional polymeric material layer is bonded to the continuous loop polymeric material encasing the continuous loop reinforcing woven fabric between the bonded materials to define the processing belt to be used in chemical mechanical planarization operations. The continuous loop reinforcing woven fabric is defined from one of kevlar, nylon, polyimide, and polyester. [0014]
  • In still a further embodiment, a method for fabricating a belt for use in chemical mechanical planarization is disclosed. The method includes forming a belt-shaped fabric, and providing a mold configured to form a belt-shaped structure. A polymeric material is formed in the mold, and the belt shaped fabric is attached to the formed polymeric material. The method further includes applying an additional polymeric material layer over the belt-shaped fabric. The additional polymeric material layer is applied over and through the belt-shaped fabric such that the belt-shaped fabric is encased between the polymeric material and the additional polymeric material layer. The polymeric material and the additional polymeric material layer are bonded together. Such bond can form a chemical bond, and can be adhered together as an essentially integral structure. [0015]
  • The advantages of the present invention are numerous. One notable benefit and advantage of the invention is significantly increased lifetime of the polymeric CMP processing belt in the CMP process. Unlike a typical linear CMP processing belt of prior art, the present invention provides the necessary strength, support, and resilience without stacks of bonded layers subject to delamination or separation. The reinforcement of the present invention can be chemically bonded, and is at least adhered to the processing belt in a manner so as to be integral to the belt structure. Polymeric material provides the supporting structure which is reinforced and may include a separately fabricated processing surface, resulting in a CMP processing belt of significantly increased lifetime in the CMP process. [0016]
  • Another benefit is the lower cost and ease of manufacture. Unlike typical prior art processing belts, the present invention includes a supporting and predominate structure of polymeric material. The plurality of layers, adhesives, stitches, or other bonding materials between the plurality of layers are eliminated without compromise of strength, support, and resilience. Reinforcing material is easily obtained, easy to work with, and easily applied to a surface of the polymeric processing belt. [0017]
  • An additional benefit is the ability to readily integrate embodiments of the present invention with optical end point detection apparatus. The reinforcing layer of the present invention provides for fabrication of optical “windows” for use with end point detection apparatus, and without compromise of necessary strength, support, and resilience. Further, integration of optical end point detection structures does not increase the likelihood of delamination or separation, or decrease the useable life of the processing belt. [0018]
  • Other advantages of the invention will become apparent from the following detailed description, taken in conjunction with the accompanying drawings, illustrating by way of example the principles of the invention. [0019]
  • BRIEF DESCRIPTION OF THE DRAWINGS
  • The present invention will be readily understood by the following detailed description in conjunction with the accompanying drawings, wherein like reference numerals designate like structural elements. [0020]
  • FIG. 1A illustrates a typical linear belt CMP system. [0021]
  • FIG. 1B shows a side view of the linear belt CMP system described in FIG. 1A. [0022]
  • FIG. 2A shows a cross section of a typical linear CMP processing belt. [0023]
  • FIG. 2B shows the cross section of a typical linear CMP processing belt of FIG. 2A with an open section of belt for use with an in-situ optical end point detection system. [0024]
  • FIG. 3A is a cross section of a CMP processing belt in accordance with an embodiment of the present invention. [0025]
  • FIG. 3B is a cross section of a CMP processing belt in accordance with an embodiment of the present invention. [0026]
  • FIG. 4 shows a detail view of the application of the additional polymeric material layer described in reference to FIGS. 3A and 3B in accordance with one embodiment of the invention. [0027]
  • FIG. 5 shows a cross section of a CMP processing belt in accordance with another embodiment of the present invention. [0028]
  • FIG. 6 is a flow chart diagram illustrating the method operations for manufacturing a reinforced polymeric CMP processing belt in accordance with one embodiment of the present invention. [0029]
  • DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
  • An invention for a CMP processing belt and methods for making the same are disclosed. In preferred embodiments, the CMP processing belt includes a processing belt constructed of a polymeric material and reinforced with a woven fabric or synthetic material to define the processing belt to be used in CMP operations. [0030]
  • In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. It will be understood, however, to one skilled in the art, that the present invention may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail in order not to unnecessarily obscure the present invention. [0031]
  • FIG. 1A illustrates a typical linear [0032] belt CMP system 100. A linear CMP processing belt 102 is positioned around two drums 104. A wafer 106 for processing is attached to a wafer carrier 108 over the linear belt CMP system 100. The wafer carrier 108 is caused to rotate 110 which causes the wafer 106 to rotate, and the drums 104, also known as drive rollers 104, rotate causing the linear CMP processing belt 102 to move in direction 112. The rotating wafer carrier 108 having a wafer 106 attached thereto is applied against the linear CMP processing belt 102 which is moving around drums 104 in direction 112. Platen 114 is positioned under linear CMP processing belt 102 opposite (e.g., on the opposite side of the linear CMP processing belt 102 from) the wafer carrier 108 with a wafer 106 attached. Platen 114 provides additional support in order for the wafer 106 to be applied against the linear CMP processing belt 102 with sufficient force to accomplish the desired planarization or other CMP process, as well as providing a flat surface for consistent, measurable processing. FIG. 1B shows a side view of the linear belt CMP system 100 just described.
  • As can be appreciated from FIGS. 1A and 1B, the linear [0033] CMP processing belt 102 is subjected to various stresses during operation of the linear belt CMP system 100. By way of example, as a point on the linear CMP processing belt 102 travels around drums 104, it is subjected to a stretching force, with the outer region or exterior surface of the linear CMP processing belt 102 subjected to greater stretching than the inner region or interior surface of the linear CMP processing belt. As the point on the linear CMP processing belt continues travel off of and away from the drums 104, it is subjected to a contracting force as the belt straightens out and travels across the top or bottom of the linear belt CMP system 100 towards the next drum 104. Further, the linear belt CMP processing system 100 subjects the linear CMP processing belt 102 to processing stresses such as the downward force of the wafer against the processing surface, the frictional contact between the rotating wafer 106 and the linear CMP processing belt 102, and other such processing forces.
  • FIG. 2A shows a cross section of a typical linear [0034] CMP processing belt 120. The exemplary linear CMP processing belt 120 includes three layers 122, 124, and 126. The top polymeric layer 122 provides the processing surface against which the wafer 106 (see FIGS. 1A, 1B) is applied for CMP processing. A cushioning layer 124 is typically constructed between the processing surface polymeric layer 122 and the support or base layer 126, and provides a cushioning transition layer between the processing surface polymeric layer 124, and the rigid, hard support or base layer 126. Typically, the support or base layer 126 is a solid stainless steel or other similar metal belt or band over which has been fabricated the cushioning layer 124 and polymeric processing surface layer 122. The plurality of layers are typically joined by adhesives or other similar bonding of one layer to the next.
  • FIG. 2B shows the cross section of a typical linear [0035] CMP processing belt 120 of FIG. 2A with an open section 128 of belt for use with an in-situ optical end point detection (EPD) system. As can be appreciated in FIG. 2B, a section of the linear CMP processing belt 120 is removed, including the support or base layer 126, the cushioning layer 124, and the processing surface polymeric layer 122. When an open section 128 is constructed in a linear CMP processing belt 120, an open section 128 of sufficient size for optical EPD implementation is created in the linear processing belt 120. Typically, sufficient size includes a small circular, oval or square section of the linear CMP processing belt 120 that varies in size according to the particular processing tool with a typical dimension of about 1.25 inches in length and about 0.75 inches in width, and therefore not an entire width of the linear CMP processing belt 120, or of such a large size as to significantly weaken the structural integrity of the linear CMP processing belt 120. Construction of the open section 128 for EPD use typically includes forming a hole or opening in the linear CMP processing belt 120 and through each of the processing surface polymeric layer 122, the cushioning layer 124, and the support or base layer 126.
  • As described above, the stretching and contracting forces caused during normal use of the linear CMP processing system [0036] 100 (see FIGS. 1A and 1B) can cause delamination or separation in a linear CMP processing belt 120 such as exemplary belt illustrated in FIG. 2A. The effects of the stresses of normal wear are aggravated by the wet environment including the use of slurries, rinses, and the like. Structures such as the open section 128 illustrated in FIG. 2B can increase the likelihood for linear CMP processing belt 120 to suffer structural failure including delamination or separation due to the increased surface area subjected to stress, increased likelihood of exposure of the layer joints and adhesives or other bonds to the wet environment, structural weakening of the base or support layer 126 from the opening or openings created, and the like.
  • FIG. 3A is a cross section of a [0037] CMP processing belt 150 in accordance with an embodiment of the present invention. In the inventive CMP processing belt 150 shown in FIG. 3A, the CMP processing belt 150 is constructed substantially of a polymeric material 152 with a woven fabric or synthetic material reinforcing layer 154, and an additional polymeric material layer 156 sprayed on, or otherwise applied, bonding the woven fabric or synthetic material reinforcing layer 154 to the polymeric material 152. The polymeric material 152 can include any of a plurality of polymeric materials suitable for construction of CMP processing belts and surfaces, including polyurethane, polyester, PVC, polyacrylate, any of a plurality of epoxies, and the like.
  • In one embodiment, the woven fabric or synthetic [0038] material reinforcing layer 154 is a fabric of kevlar. In other embodiments, the fabric is constructed of synthetic materials such as synthetic fibers of nylon, polyimides, polyesters, and the like, and in some embodiments, the fabric is a combination of synthetic materials such as, by way of example, nylon material forming one direction of a weave, and polyester material forming another direction of the weave. In this manner, the most desirable properties of the particular synthetic such as strength, or rigidity, or elasticity, are selectively implemented along and across a CMP processing belt 150 according to particular processing needs.
  • In the embodiment illustrated in FIG. 3A, additional [0039] polymeric material layer 156 is shown bonding the woven fabric or synthetic material reinforcing layer 154 to the polymeric material 152. The additional polymeric material layer 156 can include any of the plurality of polymers suitable for use in the construction of a CMP processing belt including polyurethane, polyester, PVC, polyacrylate, any of a plurality of epoxies, and the like.
  • As illustrated in FIG. 3A, one embodiment of the present invention includes the application of the additional [0040] polymeric material layer 156 by spraying 162 the desired polymer using polymer spray applicator 160. The woven fabric or synthetic material reinforcing layer 154 is temporarily clamped, stapled, tacked, glued, or otherwise temporarily positioned (not shown in FIG. 3A) against the polymeric material 152. Polymer spray applicator 160 is used to spray 162 the additional polymeric material layer 156 such that the additional polymeric material layer 156 is applied over the woven fabric or synthetic material reinforcing layer 154, and also permeates the woven fabric or synthetic material reinforcing layer 154 forming a chemical bond, in one embodiment, between the polymeric material 152 and the additional polymeric material layer 156. In one embodiment, the polymeric material 152 and the additional polymeric material layer 156 are fabricated from the same polymer. In alternative embodiments, the polymeric material 152 and the additional polymeric material layer 156 are fabricated of different polymers. The properties of polymers, however, provide for strong, permanent, and in some cases chemical bonding between the layers, effectively encasing the woven fabric or synthetic material reinforcing layer 154 within the bonded polymers 152, 156.
  • In one embodiment, the woven fabric or synthetic [0041] material reinforcing layer 154 forms a reinforcing layer of the CMP processing belt and therefore has the same continuous loop, belt-shaped structure as the polymeric material 152 of the CMP processing belt 150. As described above, the fabrication of one embodiment of the present invention includes the temporary application of the woven fabric or synthetic material reinforcing layer 154 to the polymeric material 152 by such methods as clamping, stapling, tacking, the use of adhesives, and the like. As will be described in greater detail below in reference to FIG. 4, the woven fabric or synthetic material reinforcing layer 154 can be fabricated for and positioned against an interior surface of the polymeric material 152, or the woven fabric or synthetic material reinforcing layer 154 can be fabricated for and positioned against an exterior surface of the polymeric material 152. As used herein, an interior surface of the polymeric material 152 corresponds to an interior surface of the continuous loop, belt-shaped structure defining the CMP processing belt 150. The interior surface of the CMP processing belt 150 is that surface in contact with the drums 104 (see FIGS. 1A and 1B) and the platen 114 (see FIGS. 1A and 1B). The exterior surface, therefore, is that surface having a processing surface and against which a wafer is applied for processing.
  • FIG. 3B is a cross section of a [0042] CMP processing belt 150 in accordance with an embodiment of the present invention. Similar to the CMP processing belt 150 illustrated in FIG. 3A, the CMP processing belt in FIG. 3B includes a polymeric material 152, a woven fabric or synthetic material reinforcing layer 154, and an additional polymeric material layer 156. The woven fabric or synthetic material reinforcing layer 154 has been positioned against the polymeric material 152, and the additional polymeric material layer 156 has been applied over the woven fabric or synthetic material reinforcing layer 154 by spraying 162 or otherwise applying the additional polymeric material layer 156 such that the applied polymer permeates the woven fabric or synthetic material reinforcing layer 154 and forms a strong and permanent bond between the polymeric material 152 and the additional polymeric material layer 156, effectively encasing the woven fabric or synthetic material reinforcing layer 154 within the CMP processing belt 150. In some embodiments, the bond formed is a chemical bond between the polymeric material 152 and the additional polymeric material layer 156. The embodiment illustrated in FIG. 3B includes an EPD opening 158, functioning as described above in reference to FIG. 2B.
  • In one embodiment, the [0043] EPD opening 158 is fabricated in the woven fabric or synthetic material reinforcing layer 154 prior to the positioning of the woven fabric or synthetic material reinforcing layer 154 against the polymeric material 152. After the additional polymeric material layer 156 is applied, and the polymeric material 152 and the additional polymeric material layer 156 are bonded encasing the woven fabric or synthetic material reinforcing layer 154. In one embodiment, the EPD opening 158 is fabricated in the CMP processing belt 150 by creating an opening through the additional polymeric material layer 156 and the polymeric material 152 aligned with and through the opening already created in the woven fabric or synthetic material reinforcing layer 154. In some applications, a selected woven fabric or synthetic material is tough, strong, durable, and otherwise very difficult to cut or otherwise pierce in order to form an EPD opening. When the woven fabric or synthetic material is encased in polymeric material, the creation of an opening is extremely difficult, and therefore the opening is created prior to the positioning of the woven fabric or synthetic material reinforcing layer 154 against the polymeric material 152.
  • In another embodiment, the [0044] polymeric material 152 and the additional polymeric material layer 156 are thinned (not shown in FIG. 3B) at the region in which the EPD opening 158 is defined through the woven fabric or synthetic material reinforcing layer 154. In some implementations it is unnecessary to completely pierce through all of the polymeric material 152, the woven fabric or synthetic material reinforcing layer 154 and the additional polymeric material layer 156. Because the woven fabric or synthetic material reinforcing layer 156 has an EPD opening allowing for optical transmission through the reinforcing layer, the polymeric material 152 and the additional polymeric material layer 156 need only be thinned to allow optical transmission for EPD.
  • In other embodiments, the [0045] EPD opening 158 is fabricated by creating an opening in a fabricated CMP processing belt 150 through each of the integral polymeric material 152, the woven fabric or synthetic material reinforcing layer 154, and the additional polymeric material layer 156. In an alternative embodiment, an EPD opening 158 can be fabricated in the polymeric material 152 during casting of the continuous loop, belt-shaped structure, and an opening can be created in the woven fabric or synthetic material reinforcing layer 154 prior to positioning against the polymeric material 152 during fabrication of the CMP processing belt 150. The openings in the component layers are aligned when the woven fabric or synthetic material reinforcing layer 154 is positioned against the polymeric material 152. The additional polymeric material layer 156 is applied, bonding the layers together and encasing the woven fabric or synthetic material reinforcing layer 154 forming the CMP processing belt 150. The EPD opening 158 is then created by punching through the additional polymeric material layer 156 over the openings already created in the polymeric material 152 and the woven fabric or synthetic material reinforcing layer 154.
  • FIG. 4 shows a detail view of the application of the additional [0046] polymeric material layer 156 described in reference to FIGS. 3A and 3B in accordance with one embodiment of the invention. As described in reference to FIGS. 3A and 3B, the woven fabric or synthetic material reinforcing layer 154 is fabricated as a continuous loop, belt-shaped structure, and positioned against the polymeric material 152 which is also a continuous loop, belt-shaped structure. The woven fabric or synthetic material reinforcing layer 154 can be positioned against either an interior surface or an exterior surface of the polymeric material 152 according to desired implementation and use of the CMP processing belt 150. In one embodiment, the woven fabric or synthetic material reinforcing layer 154 is fabricated from kevlar. In other embodiments, the woven fabric or synthetic material reinforcing layer 154 is fabricated of any of a plurality of fabrics or synthetic materials including polyesters, rayon, nylon, polyimides, mixtures of synthetics, and the like. The selected woven fabric or synthetic material is generally porous to allow for the additional polymeric material layer 156 to permeate the woven fabric or synthetic material such that the polymer(s) of the polymeric material 152 and the additional polymeric material layer 156 form a bond, effectively encasing the woven fabric or synthetic material reinforcing layer within the polymeric material 152 and the additional polymeric material layer 156 defining an integral structure CMP processing belt 150. The integral structure thus formed is essentially not susceptible to delamination or separation of the layers typically used in the construction of some prior art CMP processing belts and surfaces.
  • As shown in FIG. 4, an embodiment of the present invention includes the application of the additional [0047] polymeric material layer 156 by spraying 162 polymeric material with a polymer spray applicator 160. The applied polymer or polymeric material of the additional polymeric material layer 156 can be the same polymer or polymeric material as that defining polymeric material 152, or in some embodiments, it can be a different polymer or polymeric material. In preferred embodiments, the selected polymers or polymeric materials have properties providing for the formation of a strong and permanent bond. In some embodiments, the bond formed is a chemical bond. Exemplary polymeric materials include polyurethane, polyester, PVC, polyacrylate, any of a plurality of epoxies, and the like. As can be appreciated in FIG. 4, the applied polymer permeates the woven fabric or synthetic material reinforcing layer 154, forming the strong and permanent bond between the polymeric material 152 and the additional polymeric material layer 156, and encasing the woven fabric or synthetic material reinforcing layer 154. The resulting structure defines a reinforced CMP processing belt as an integrated structural unit.
  • FIG. 5 shows a cross section of a [0048] CMP processing belt 170 in accordance with another embodiment of the present invention. In the embodiment illustrated in FIG. 5, the CMP processing belt 170 includes the polymeric material 152, the woven fabric or synthetic material reinforcing layer 154, and the additional polymeric material layer 156 as illustrated and described above in reference to FIGS. 3A, 3B, and 4. A processing surface layer 172 is cast, sprayed, or otherwise applied to the CMP processing belt 170 illustrated in FIG. 5. In the embodiments illustrated and described in FIGS. 3A, 3B, and 4, the polymeric material 152 defines the processing surface. In the embodiment illustrated in FIG. 5, a separate processing surface layer 172 is cast, sprayed, or otherwise fabricated over the polymeric material 152 to define the processing surface for the CMP processing belt 170.
  • The [0049] CMP processing belt 170 illustrated in FIG. 5 is fabricated in order to optimize the processing surface in applications in which it is desirable to have a processing surface layer 172 of a different hardness than underlying polymeric material 152 or additional polymeric material layer 156. As described above in reference to FIG. 4, the woven fabric or synthetic material reinforcing layer 154 can be positioned against either an interior surface of the polymeric material 152 or an exterior surface of the polymeric material 152. In this manner, differing hardnesses of the layers can be combined to optimize the hardness of the processing surface layer 172 according to processing conditions and desires. In one embodiment, the polymeric material 152, the woven fabric or synthetic material reinforcing layer 154 and the additional polymeric material layer 156 are fabricated as described above in reference to FIGS. 3A, 3B, and 4, and then the processing surface layer 172 is cast over the already fabricated layers to define the processing surface of CMP processing belt 170. In other embodiments, the polymeric material 152, the woven fabric or synthetic material reinforcing layer 154 and the additional polymeric material layer 156 are fabricated, and the processing surface layer 172 is sprayed over or otherwise applied over the fabricated layers to define the CMP processing belt 170.
  • The embodiment of the [0050] CMP processing belt 170 illustrated in FIG. 5 can also be utilized to control the thickness of the CMP processing belt 170 to meet performance requirements. A typical CMP processing belt 170, 150, in accordance with embodiments of the present invention as described above, ranges in thickness from about 80 mils to about 100 mils. In an embodiment of a CMP processing belt 170 according to the present invention, the thickness of the integral polymeric material 152, the woven fabric or synthetic material reinforcing layer 154, and the additional polymeric material layer 156 can be minimized to a range from about 20 mils to about 30 mils while retaining the desired strength and structural support properties. The overall thickness of the CMP processing belt 170 is then dependent upon the type and thickness of the processing surface layer 172. By way of example, if a thicker CMP processing belt 170 is desired, any of the polymeric material 152, the additional polymeric material layer 156, and the processing surface layer 172 can be fabricated to a desired thickness to achieve design goals. In a similar manner, the thickness and composition of the layers 172, 152, 156, can be adjusted to achieve desired hardness, rigidity, and the like according to processing conditions and desires.
  • FIG. 6 is a flow chart diagram [0051] 200 illustrating the method operations for manufacturing a reinforced polymeric CMP processing belt in accordance with one embodiment of the present invention. The illustrated method begins with operation 210 in which the woven fabric or synthetic material reinforcing layer is fabricated. In one embodiment, the woven fabric or synthetic material reinforcing layer is fabricated of kevlar. In other embodiments, the woven fabric or synthetic material reinforcing layer is fabricated of nylon, rayon, polyester, polyimide, a mixed synthetic material, or any other desired fabric or synthetic material to provide the desired reinforcement of the fabricated CMP processing belt. Examples of desired reinforcement qualities include strength, durability, a decrease in the tendency of the CMP processing belt to stretch with continued, sustained use, flexibility for use in a linear CMP processing tool or system, and the like.
  • In one embodiment, the woven fabric or synthetic material reinforcing layer is fabricated to be positioned against an interior surface of the polymeric material of the fabricated CMP processing belt. In another embodiment, the woven fabric or synthetic material reinforcing layer is fabricated to be positioned against an exterior surface of the fabricated CMP processing belt. In [0052] method operation 210 the woven fabric or synthetic material reinforcing layer is fabricated according to the desired dimension and positioning in a continuous loop, belt-like structure. In one embodiment, EPD openings are fabricated in the woven fabric or synthetic material reinforcing layer during fabrication of the layer according to processing desires.
  • The method continues with [0053] operation 212 and the preparation of a polymer to be molded into a CMP processing belt. In one embodiment, a polymer or polymeric material is prepared for molding into a polymeric CMP processing belt utilizing a polymeric mold. A polymeric mold is typically used to cast a polymeric CMP processing belt as a continuous loop, belt-like structure by injecting a desired polymer or polymeric material into a mold or form of the desired shape and dimension. In one embodiment, method operation 212 includes the preparation of the polymer or polymeric material to be used to cast the polymeric material described above in reference to FIGS. 3A, 3B, 4, and 5, and identified by reference numeral 152. In one embodiment, the preparation of the polymer or polymeric material in method operation 212 includes the preparation for the polymeric material and for preparation of the polymer or polymeric material for the additional polymeric material layer described above and identified by reference numeral 156.
  • Any desired polymer or polymeric material may be used in [0054] operation 212 according to the intended processing requirements. Generally, a flexible, durable, and tough material is desired for a linear CMP processing belt for effective wafer planarization without scratching. The selected polymer need not be fully elastic, and should not slacken or loosen with use. Different polymers may be selected to enhance certain features of the intended process. In one embodiment, the polymer may be polyurethane. In another embodiment, the polymer may be a urethane mixture that produces a processing surface of the completed polymeric CMP processing belt that is a microcellular polyurethane with a specific gravity of approximately 0.4-1.5 g/cm2 and a hardness of approximately 2.5-90 shore D. Typically, a liquid resin and a liquid curative are combined to form the polyurethane mixture. In another embodiment, a polymeric gel may be utilized to form the polymeric material.
  • After [0055] operation 212, the method proceeds to operation 214 in which prepared polymer is injected into the mold. In one embodiment, urethane or other polymer or polymeric material is dispensed into a hot cylindrical mold. In one embodiment, the injection of prepared polymer into a mold is to form the polymeric material identified by reference numeral 152 in the Figures described above.
  • In [0056] operation 216, the prepared polymer is heated and cured. It should be understood that any type of polymer may be heated and cured in any way that would produce the physical characteristics desired in a finished polymeric CMP processing belt. In one embodiment, a urethane mixture is heated and cured for a predetermined time at a predetermined temperature to form a urethane processing surface. Curing times and temperatures suitable to the selected polymer or polymeric material, or to achieve specific desired properties may be followed. In just one example, thermoplastic materials are processed hot and then become set by cooling.
  • After [0057] operation 216, the method advances to operation 218 and the polymeric material is de-molded by removing the belt from the mold. In one embodiment, the mold is a polymeric linear CMP processing belt molding container used to form the polymeric material to be reinforced with the woven fabric or other synthetic material reinforcing layer, and additional polymeric material to encase the woven fabric or synthetic material reinforcing layer within the polymeric structure of the CMP processing belt.
  • Then, in [0058] operation 220, the polymeric material is fabricated to a desired thickness and dimension according to processing requirements. In one embodiment, the polymeric material is lathed to predetermined dimensions. In operation 220, the polymeric material, in a molded continuous loop belt-shaped form, is cut to the desired thickness and dimensions for optimal linear CMP processing. In one embodiment, the polymeric CMP processing belt is lathed to a thickness ranging from about 0.02 inch to about 0.2 inch, with a preferred thickness of about 0.02 inch to about 0.05 inch, according to the CMP process for which the polymeric CMP processing belt is intended to be used.
  • The method proceeds with [0059] operation 222 in which the woven fabric or synthetic material reinforcing layer is positioned against polymeric material and temporarily attached. Methods of temporary attachment include clamping, stapling, tacking, use of adhesives, and the like in order to precisely position the woven fabric or synthetic material reinforcing layer against the polymeric material. In one embodiment, the woven fabric or synthetic material reinforcing layer is positioned against an interior surface of the polymeric layer. In another embodiment, the woven fabric or synthetic material reinforcing layer is positioned against an exterior surface of the polymeric material, according to processing and fabrication desires.
  • In [0060] method operation 224, additional polymeric material is applied to form the additional polymeric material layer and encase the woven fabric or synthetic material reinforcing layer within the polymeric structure of the fabricated CMP processing belt. In one embodiment, the additional polymeric material is applied by spraying the additional polymeric material over the woven fabric or synthetic material reinforcing layer. In another embodiment, the polymeric material with temporarily attached woven fabric or synthetic material reinforcing layer is positioned in a mold and the additional polymeric material is cast over the woven fabric or synthetic material reinforcing layer. However the additional polymeric material layer is applied, the polymer or polymeric material permeates the woven fabric or synthetic material and bonds with the polymeric material, encasing the woven fabric or synthetic material reinforcing layer to define an integral structure of the reinforced CMP processing belt.
  • The method continues with [0061] operation 226 in which the reinforced polymeric CMP processing belt, including the polymeric material, the woven fabric or synthetic material reinforcing layer, and the additional polymeric material layer as an integral structure, is fabricated into the desired thickness and dimension for the reinforced CMP processing belt. In one embodiment, the fabrication includes lathing, trimming, and the like to achieve the desired thickness and surface quality. If the polymeric linear CMP processing belt is an embodiment with EPD openings, one embodiment of operation 226 includes piercing, thinning and clearing of the polymeric regions at the EPD openings fabricated in the woven fabric or synthetic material reinforcing layer as described above. In one embodiment of fabrication of a CMP processing belt in accordance with the present invention, the mold or form used in method operation 214 includes structural definition of EPD openings within the mold or form. The woven fabric or synthetic material reinforcing layer is positioned in method operation 222 with fabricated EPD openings aligned with the structures defined in the polymeric material, and in operation 226, the final thinning or piercing of the EPD openings is accomplished as desired.
  • In one embodiment of [0062] method operation 226, the reinforced polymeric CMP processing belt is fabricated to a desired thickness and dimension according to processing requirements. In one embodiment, the integral polymeric material is lathed to predetermined dimensions. In one embodiment, the reinforced polymeric CMP processing belt is lathed to a thickness ranging from about 0.02 inch to about 0.2 inch, with a preferred thickness of about 0.07 inch to about 0.12 inch, according to the CMP process for which the polymeric CMP processing belt is intended to be used.
  • In one embodiment of [0063] method operation 226, edges of the reinforced polymeric CMP processing belt are trimmed, and the reinforced polymeric CMP processing belt is cleaned and prepared for use. In one embodiment, the polymeric linear CMP processing belt is 90-110 inches in length, 8-16 inches wide and 0.020-0.2 inches thick. It is therefore suitable for use in the Teres™ linear polishing apparatus manufactured by Lam Research Corporation.
  • In one embodiment, the fabrication of the integral structure reinforced polymeric CMP processing belt to the desired thickness and dimension completes the fabrication of a reinforced CMP processing belt, and the method is done. In one embodiment, the method includes [0064] additional method operation 228 in which a desired preparation surface is fabricated. In the fabrication of the preparation surface of method operation 228 grooves are formed on a processing surface of the reinforced polymeric CMP processing belt in accordance with one embodiment of the invention. In another embodiment, the grooves may be formed during molding by providing a suitable pattern on the inside of the mold. In one embodiment, the raw casting is turned and grooved on a lathe to produce a smooth polishing surface with square shaped grooves. In another embodiment, a separate polymer or polymeric material processing surface is applied to the reinforced CMP processing belt, the polymer(s) or polymeric material bonding to the reinforced CMP processing belt as an additional integral structure. Embodiments of additional processing surfaces include surfaces providing a different hardness than the underlying layers of the reinforced polymeric CMP processing belt, desired surface texturing, and the like. If the additional method operation 228 is accomplished, the reinforced polymer CMP processing belt is completed upon fabrication and preparation of the processing surface, and the method is done.
  • Although the foregoing invention has been described in some detail for purposes of clarity of understanding, it will be apparent that certain changes and modifications may be practiced within the scope of the appended claims. Accordingly, the present embodiments are to be considered as illustrative and not restrictive, and the invention is not to be limited to the details given herein, but may be modified within the scope and equivalents of the appended claims.[0065]

Claims (25)

What is claimed is:
1. A processing belt for use in chemical mechanical planarization (CMP), comprising:
a fabric belt; and
a polymeric material encasing the fabric belt to define the processing belt to be used in CMP operations.
2. The processing belt of claim 1, wherein the fabric belt forms a continuous loop within the polymeric material.
3. The processing belt of claim 1, wherein the fabric belt is defined of kevlar.
4. The processing belt of claim 3, further comprising openings in the fabric belt, the openings being configured to be suitable for optical transmissions through the opening in the fabric.
5. The processing belt of claim 4, wherein the polymeric material is made thinner at the opening in the fabric.
6. The processing belt of claim 1, wherein the fabric belt is defined of a synthetic material including polyester, polyimide, nylon, rayon, and PVC.
7. A belt for use in chemical mechanical planarization (CMP) processing, comprising:
a polymeric material being cast into a continuous loop to define the belt; and
a reinforcing fabric embedded between the polymeric material and an additional polymeric material layer, the reinforcing fabric being defined as a continuous loop within the polymeric material and the additional polymeric material layer.
8. The belt of claim 7, wherein the polymeric material includes polyurethane, polyester, PVC, polyacrylate, and epoxy.
9. The belt of claim 7, wherein the additional polymeric material layer is defined by one of polyurethane, polyester, PVC, polyacrylate, and epoxy.
10. The belt of claim 7, wherein the reinforcing fabric is defined as a woven and porous structure.
11. The belt of claim 7, further comprising openings fabricated in the reinforcing fabric, the openings being suitable for optical transmissions through the reinforcing fabric.
12. The belt of claim 11, wherein the polymeric material and the additional polymeric material layer are made thinner at the openings in the reinforcing fabric.
13. The belt of claim 7, wherein the reinforcing fabric is defined from kevlar.
14. The belt of claim 7, wherein the reinforcing fabric is defined of a synthetic fiber including nylon, polyester, polyimide, rayon, and PVC.
15. The belt of claim 7, further comprising:
a processing surface defined over the polymeric material, the polymeric material being a first polymeric material and the processing surface being defined from a second polymeric material bonded to the first polymeric material.
16. A processing belt for use in chemical mechanical planarization (CMP), comprising:
a continuous loop reinforcing woven fabric;
a continuous loop polymeric material; and
a continuous loop additional polymeric material layer bonded to the continuous loop polymeric material and encasing the continuous loop reinforcing woven fabric between the continuous loop polymeric material and the continuous loop additional polymeric material layer to define the processing belt to be used in CMP operations,
wherein the continuous loop reinforcing woven fabric is defined from one of kevlar, nylon, polyimide, and polyester.
17. The processing belt of claim 16, wherein the continuous loop reinforcing woven fabric includes openings that allow optical transmission to pass through the continuous loop reinforcing fabric.
18. The processing belt of claim 17, wherein the continuous loop polymeric material and the continuous loop additional polymeric material encasing the continuous loop reinforcing woven fabric are thinner at the openings than the continuous loop polymeric material and the continuous loop additional polymeric material encasing the continuous loop reinforcing woven fabric in regions other than at the openings.
19. A method for fabricating a belt for use in chemical mechanical planarization (CMP), comprising:
forming a belt-shaped fabric;
providing a mold configured to form a belt-shaped structure;
forming a polymeric material in the mold;
attaching the belt shaped fabric to the formed polymeric material; and
applying an additional polymeric material layer over the belt-shaped fabric, the applying being over and through the belt-shaped fabric such that the belt-shaped fabric is encased between the polymeric material and the additional polymeric material layer, the polymeric material and the additional polymeric material layer being bonded together.
20. The method of claim 19, further comprising:
defining a polymeric processing surface over the polymeric material.
21. The method of claim 19, wherein the forming a belt-shaped fabric includes forming openings through the belt-shaped fabric through which optical transmissions can pass.
22. The method of claim 19, wherein the belt-shaped fabric is formed of kevlar.
23. The method of claim 19, wherein the polymeric material includes polyurethane, polyester, PVC, polyacrylate, and epoxy.
24. The method of claim 19, wherein the additional polymeric material layer is defined of one of polyurethane, polyester, PVC, polyacrylate, and epoxy.
25. The method of claim 19, wherein the polymeric material and the additional polymeric material layer encasing the belt-shaped fabric are chemically bonded together.
US10/112,447 2002-03-12 2002-03-29 Reinforced chemical mechanical planarization belt Abandoned US20030186630A1 (en)