DE4131229C1

DE4131229C1 -

Info

Publication number: DE4131229C1
Application number: DE19914131229
Authority: DE
Inventors: Karlheinz Dr. 5205 Sankt Augustin De Schmidt
Original assignee: DR KARLHEINZ SCHMIDT APPARATEBAU 5205 SANKT AUGUSTIN DE
Current assignee: DR KARLHEINZ SCHMIDT APPARATEBAU 5205 SANKT AUGUSTIN DE
Priority date: 1991-09-19
Filing date: 1991-09-19
Publication date: 1993-01-21
Anticipated expiration: 2011-09-20
Also published as: WO1993005732A1

Abstract

To achieve negative refraction, it is proposed to make the intraocular lens (5) of a material with a lower refractive index than that of the aqueous humour. Alternatively, a hollow intraocular lens (5") may be used. The outer edges of the intraocular lenses are thinner than the centres so that they espouse the natural shape of the eye well on being implanted, especially when the intraocular lens is implanted in addition to the actual natural lens (3).

Description

Es ist bekannt, bei der Trübung der natürlichen Augenlinse diese zu entfernen und durch eine implantierte Intraokular linse zu ersetzen.It is known to cloud the natural eye lens remove this and through an implanted intraocular to replace the lens.

Es ist auch bekannt, starke Fehlsichtigkeit durch Implantation einer zusätzlichen Intraokularlinse in die vordere Augen kammer zu korrigieren, wobei die natürliche Augenlinse erhalten bleibt. Für diese zusätzliche Korrektur sind, abhängig von der Art der Fehlsichtigkeit des Patienten, Sammellinsen mit positivem Dioptrienwert bzw. Zerstreuungs linsen mit negativem Dioptrienwert notwendig.It is also known to have severe ametropia through implantation an additional intraocular lens in the front eyes correct the chamber, taking the natural eye lens preserved. For this additional correction, depending on the type of ametropia of the patient, Lenses with a positive diopter value or diverging lenses with a negative diopter value necessary.

Erfordert die Fehlsichtigkeit eine Zerstreuungslinse, so wird diese als plankonkave oder bikonkave Intraokularlinse ausgebildet. Die Linse hat zusätzlich eine Haptik, d. h. Stütz- oder Befestigungselemente, mit der die Lage der Linse in der Vorderkammer fixiert ist. Als Haptik werden z. B. gebogene Federschenkel verwendet, die die Intraokularlinse im Kammerwinkel abstützen oder Klemmelemente, um die Intraoku larlinse in die Peripherie der Iris zu klemmen.If the ametropia requires a diverging lens, see above this is called a plano-concave or biconcave intraocular lens educated. The lens also has a feel, i. H. Supporting or fastening elements with which the position of the Lens is fixed in the anterior chamber. As a haptic e.g. B. curved spring legs used the intraocular lens support in the chamber angle or clamping elements to the intraocu clamp lar lens in the periphery of the iris.

Als Stand der Technik sei die WO 91/07 147 A1 genannt, in der eine plankonkave Intraokularlinse beschrieben ist, die in die Vorderkammer des Auges implantiert ist und als Zer streuungslinse dient. Die natürliche Augenlinse wird hierbei nicht entfernt.The state of the art is WO 91/07 147 A1, in which a plano-concave intraocular lens is described that is implanted in the anterior chamber of the eye and as a Zer Scattering lens is used. The natural eye lens is hereby not removed.

Der schwere Nachteil dieser plankonkaven oder bikonkaven Vorderkammerlinsen liegt darin, daß diese Zerstreuungs linsen an ihrem Rand wesentlich dicker sind als in der Mitte und daher der natürlichen Geometrie innerhalb des Auges zuwiderlaufen. Der dicke Rand der Intraokularlinse liegt daher sehr nahe an der vorderen Innenwand des Auges, so daß es dort zu Berührungen kommen kann, die auf Dauer eine Trübung der Hornhaut nach sich ziehen.The serious disadvantage of this plano-concave or biconcave Anterior chamber lenses lies in the fact that these are diverting lenses are much thicker on their edges than in the Middle and therefore the natural geometry within the To run counter to the eye. The thick edge of the intraocular lens is therefore very close to the front inner wall of the eye, so that there can be permanent contacts cause corneal opacity.

Es ist weiterhin aus den US-Patentschriften 47 69 035 und 48 71 363 bekannt, Intraokularlinsen entweder in der Hinter kammer oder in der Vorderkammer des Auges zu implantieren, ohne daß dabei die natürliche Augenlinse entfernt wird.It is also known from U.S. Patents 4,769,035 and 48 71 363 known, intraocular lenses either in the rear chamber or to implant in the anterior chamber of the eye, without removing the natural eye lens.

Die dort beschriebenen Intraokularlinsen sind, sofern sie als Sammellinsen ausgebildet sind, wie üblich am Rande dünner als in der Mitte; es sind jedoch auch Zerstreuungslinsen angegeben, die, ebenfalls üblich, aufgrund ihrer etwa bi konkaven Konfiguration am Rande dicker sind als in der Mitte.The intraocular lenses described there are, provided they are are formed as converging lenses, as usual on the edge thinner than in the middle; however, they are also diverging lenses specified, which, also common, due to their approximately bi concave configuration are thicker on the edge than in the Center.

Der Erfindung liegt die Aufgabe zugrunde, eine implantier bare Intraokularlinse anzugeben, die im implantierten Zu stand zwar als Zerstreuungslinse wirkt, die aber im Gegen satz zu normalen Zerstreuungslinsen am Rand dünner ist als in der Mitte.The invention has for its object an implant bare intraocular lens to be specified in the implanted Zu stood as a diverging lens, but in the opposite set to normal diverging lenses is thinner at the edge than in the middle.

Diese Aufgabe ist gemäß der Erfindung durch das im kenn zeichnenden Teil des Patentanspruches 1 angegebenen Merk mal gelöst.This object is according to the invention by the in the kenn drawing part of claim 1 specified note times solved.

Gemäß der Erfindung wird somit ein Linsenmaterial mit einem Brechungsindex verwendet, der kleiner als derjenige des Kammerwassers ist. Damit kann man eine bikonvexe, plan konvexe oder konkav/konvexe Intraokularlinse herstellen, die gleichwohl als Zerstreuungslinse, d. h. als Minuslinse, wirkt. Eine derartige Linse ist demnach an den Rändern relativ dünn und in der Mitte relativ dick, paßt sich demnach der natürlichen Gestalt des Auges im Vorderkammerbereich an. Zu Berührungen der Innenwand des Auges kommt es daher nicht, so daß auch Trübungen der Hornhaut vermieden werden.According to the invention, a lens material with a Refractive index used that is smaller than that of the Is aqueous humor. It can be used as a biconvex, plan manufacture convex or concave / convex intraocular lens, which nevertheless serves as a diverging lens, d. H. as a negative lens, works. Such a lens is therefore on the edges relatively thin and relatively thick in the middle, fits accordingly the natural shape of the eye in the anterior chamber area at. There is therefore contact with the inner wall of the eye not, so that clouding of the cornea can also be avoided.

Als Material für derartige Intraokularlinsen kommen z. B. fluorhaltige, transparente Polymere in Frage, z. B. Fluor polymere, die einen Brechungsindex bis zu 1,295 aufweisen. Beispiele für derartige Materialien sind Polytetrafluor ethylen (PTFE).As material for such intraocular lenses such. B. fluorine-containing, transparent polymers in question, for. B. fluorine polymers that have a refractive index up to 1.295. Examples of such materials are polytetrafluor ethylene (PTFE).

Geht man z. B. von dem angegebenen Brechungsindex von 1,295 für ein Fluorpolymer aus, dann beträgt bei einer plankonvexen Intraokularlinse von -10 Dioptrien der Radius der Konvexi tät 4,1 mm, entsprechend der Differenz des Brechungsindex 1,336 des Kammerwassers und 1,295 des Fluorpolymers. Diese Linse ist somit in der Mitte sehr viel dicker als außen und paßt sich so den anatomischen Verhältnissen im Auge an.If you go z. B. from the specified refractive index of 1.295 for a fluoropolymer, then for a plano-convex Intraocular lens of -10 diopters the radius of the convexi 4.1 mm, corresponding to the difference in the refractive index 1.336 aqueous humor and 1.295 fluoropolymer. These The lens is therefore much thicker in the middle than outside and thus adapts to the anatomical conditions in the eye at.

Es sind zwar für Intraokularlinsen Materialien bekannt, die fluorhaltige Polymere enthalten; vgl. z. B. die US- PS 49 55 900. Die Brechungsindices dieser bekannten Mate rialien liegen jedoch deutlich über dem Brechungsindex für das Kammerwasser, nämlich bei Werten oberhalb 1,6.Materials are known for intraocular lens, which contain fluorine-containing polymers; see. e.g. B. the US PS 49 55 900. The refractive indices of this known mate However, materials are well above the refractive index for the aqueous humor, namely at values above 1.6.

Die Erfindung ist in Ausführungsbeispielen anhand der Zeich nung näher erläutert. In dieser stellen dar:The invention is in exemplary embodiments with reference to the drawing tion explained in more detail. In this represent:

Fig. 1 einen Teilquerschnitt durch ein Auge, in das zusätz lich zur vorhandenen natürlichen Augenlinse eine Intraokularlinse gemäß der Erfindung eingesetzt ist; Figure 1 is a partial cross section through an eye, in which an intraocular lens according to the invention is used in addition to the existing natural eye lens.

Fig. 2 mehrere Querschnitte von Intraokularlinsen gemäß der Erfindung; FIG. 2 shows several cross-sections of intraocular lenses according to the invention;

Fig. 3 bis 5 Darstellungen einer Intraokularlinse gemäß einem weiteren Ausführungsbeispiel der Erfindung. Fig. 3 to 5 views of an intraocular lens according to another embodiment of the invention.

In Fig. 1 ist ein schematischer Teilquerschnitt durch ein menschliches Auge mit Hornhaut 1, Iris 2 und natürlicher Augenlinse 3 gezeigt. Der Hohlraum des Auges ist mit Kammer wasser 4 ausgefüllt. In die Vorderkammer ist eine plan konvexe Intraokularlinse eingesetzt, wobei das Material der Linse einen Brechungsindex kleiner als 1,336 aufweist. Das Material ist z. B. PTFE mit einem Brechungsindex von 1,295.In Fig. 1 is a schematic partial cross section through a human eye with the cornea 1, iris 2 and the natural eye lens 3. The cavity of the eye is filled with water 4 chamber. A plane convex intraocular lens is inserted into the anterior chamber, the material of the lens having a refractive index less than 1.336. The material is e.g. B. PTFE with a refractive index of 1.295.

In Fig. 2 sind mehrere Intraokularlinsen aus einem Material mit einem Brechungsindex n von 1,295 in einem Maßstab von 10 : 1 angegeben, wobei die Brechkraft bzw. die Dioptrien D-8, -6, -5 bzw. -10 ist. Sämtliche Linsen sind an den Rändern dünner als in der Mitte.In Fig. 2 several intraocular lenses made of a material with a refractive index n of 1.295 on a scale of 10: 1 are given, the refractive power or the diopter being D-8, -6, -5 or -10. All lenses are thinner at the edges than in the middle.

In den Fig. 3 bis 5 ist eine Intraokularlinse 5′ dargestellt, deren Linsenteil 6 konkav/konvex ist. Der Linsenteil 6 ist in eine Haptik 7 integriert, die zu beiden Seiten der Intraokularlinse als flächiger Flügel ausgebildet ist. Diese Intraokularlinse 5 kann entsprechend Fig. 5 zwischen natürlicher Augenlinse 3 und Iris 2 eingesetzt sein. Die Haptik 7 weist eine Krümmung entsprechend der normalen Krümmung der Augenlinse 3 auf.In FIGS. 3 to 5, an intraocular lens is shown 5 ', whose lens portion 6 / is concave convex. The lens part 6 is integrated in a haptic 7 , which is designed as a flat wing on both sides of the intraocular lens. This intraocular lens 5 may be inserted 5 between the natural eye lens 3 and the iris 2 in accordance with Fig.. The haptic 7 has a curvature corresponding to the normal curvature of the eye lens 3 .

Als Material für die Intraokularlinsen können neben dem erwähnten PTFE z. B. Polychlortrifluoroethlyen, Ethylen- Clortrifluorethylen-Copolymere, Hexafluorpropylen, amorphe Fluorpolymere sowie Mischungen solcher Stoffe mit anderen Stoffen verwendet werden.As a material for the intraocular lenses, in addition to the mentioned PTFE z. B. polychlorotrifluoroethylene, ethylene Clortrifluoroethylene copolymers, hexafluoropropylene, amorphous Fluoropolymers and mixtures of such substances with others Fabrics are used.

Claims

1. Intraocular lens, in particular additional, to the natural union lens in the anterior or posterior chamber of the eye implantable intraocular lens, characterized in that a material with a refractive index smaller than the refractive index of the aqueous humor is used for the intraocular lens.

2. intraocular lens according to claim 1, characterized net that the material is a fluorine-containing polymer or is a material with an addition of fluoropolymers.

3. Intraocular lens according to one of the preceding claims, characterized in that the intraocular lens ( 5 , 5 ', 5 '') has a biconvex, plano-convex or concave / convex lens part to achieve a negative refractive power.