DE3540820A1

DE3540820A1 - Security element, especially for locks

Info

Publication number: DE3540820A1
Application number: DE19853540820
Authority: DE
Inventors: Burckhard Schneider; Rolf-Dieter Bettzieche; Horst Krause
Original assignee: Interturbine Germany Vac Hyd Processing GmbH
Current assignee: Interturbine Germany Vac Hyd Processing GmbH
Priority date: 1985-11-16
Filing date: 1985-11-16
Publication date: 1987-05-21
Also published as: DE3540820C2

Abstract

The invention relates to security elements, especially for door locks, which consist of a support component (1) and, applied thereto, a layer (2) which essentially consists of carbide and impedes attack, the carbide particles having a maximum particle size of 1.0 mm and being applied to the support component, using a soldering material, in a ratio of 1:1 to 5:1, as a layer which is at most 3 mm thick. <IMAGE>

Description

Die Erfindung betrifft ein Sicherungselement, insbesondere für Schlösser, Schließzylinder, Beschläge und Tresore, bestehend aus einem Trägerteil und einer darauf aufgebrachten Karbidschicht nach dem Oberbegriff des Anspruchs 1.The invention relates to a securing element, in particular for locks, lock cylinders, fittings and safes from a carrier part and one attached to it Carbide layer according to the preamble of claim 1.

In den letzten Jahren sind verstärkte Bemühungen unternommen worden, Türschlösser, wie sie insbesondere bei Haustüren verwendet werden, präventiv gegen Angriffe durch Einbrecher zu schützen. Ein Angriff mit üblichen Werkzeugen soll dabei nicht nur verzögert, sondern nach Möglichkeit verhindert werden. Die Sicherheitsbehörden haben verschiedene Angriffskriterien entwickelt, gegen deren Einsatz die von außen zugänglichen Teile eines Schlosses resistent sein müssen. Als Kriterien der Angriffssicherheit bei Türschlössern und Türschilden gelten z. B. Hammer, Bohrer, insbesondere Hartmetallbohrer und Schlagbohrer, Sägen und Schlagwerkzeuge, wie Körner und Durchschlag.Increased efforts have been made in recent years been, door locks, such as those in particular Front doors are used to prevent attacks by To protect burglars. An attack with common tools should not only be delayed, but if possible be prevented. The security authorities have several Attack criteria developed against their use the parts of a lock that are accessible from the outside are resistant have to be. As criteria of attack security at Door locks and door plates apply e.g. B. hammer, drill, in particular hard metal drills and impact drills, saws and striking tools such as grains and punch.

Es hat sich gezeigt, daß Türschlösser im allgemeinen dort angegriffen werden, wo sie den direktesten und leichtesten Zugangsweg aufweisen. Dieser befindet sich im Bereich des Türschildes, so daß in den letzten Jahren verstärkt Anstrengungen unternommen wurden, die Türschilde durch entsprechende Wahl der zu verwendenden Materialien angriffsfest zu machen. Neben Türschilden aus Hartmetall werden auch Türschilde verwendet, die einen Hohlraum aufweisen, in die Keramikplatten eingelegt sind. Allerdings sind Keramikplatten durch Schlageinwirkung relativ leicht zu zersprengen.It has been shown that door locks are generally there be attacked where they are the most direct and lightest Have access route. This is in the area of Door sign, so that in recent years efforts have increased were made, the door shields by appropriate Choice of materials to be used against attack close. In addition to door plates made of hard metal also door shields are used which have a cavity, are inserted in the ceramic plates. However Ceramic plates relatively easy due to impact explode.

In der DE-OS 34 16 126 ist ein plattenförmiges Sicherheitselement und dessen Verwendung in einer Sicherheitsblende beschrieben, bei dem in einem lotartigen Material Hartstoffkörper, z. B. aus Wolfram-Karbid, eingebettet sind, und diese Schicht in einen wannenförmigen Träger eingelötet ist, der als Sicherheitsblende verwendbar ist. Die Körnung der Wolfram-Karbid-Teilchen ist dabei so gewählt, daß deren Mindestdurchmesser 1,0-1,5 mm und deren größter Durchmesser 3,0-4,0 mm beträgt. Die angegebene Schichtstärke beträgt etwa 3,0 mm.In DE-OS 34 16 126 is a plate-shaped security element and its use in a security bezel described, in which in a solder-like material hard material body, e.g. B. of tungsten carbide are embedded, and soldered this layer into a trough-shaped carrier which can be used as a safety cover. The Grain of the tungsten carbide particles is chosen so that that their minimum diameter 1.0-1.5 mm and their largest Diameter is 3.0-4.0 mm. The specified layer thickness is about 3.0 mm.

Ein derartiges Sicherheitselement ist zwar gegen übliche Angriffe nach den für Haustüren geltenden Kriterien resistent, jedoch ist die Herstellung relativ kostenintensiv. Darüber hinaus läßt sich eine derartige Schicht nur für bestimmte Anwendungen verwenden, wie z. B. in der Sicherheitsblende. Such a security element is against conventional ones Attacks resistant to the criteria applicable to front doors, however, the manufacture is relatively expensive. About that In addition, such a layer can only be used for certain ones Use applications such as B. in the security cover.

Der Erfindung liegt die Aufgabe zugrunde, ein Sicherungselement, insbesondere für Schlösser, anzugeben, das kostengünstig herstellbar ist, zur Absicherung von sicherheitsempfindlichen Teilen für jede Art von Sicherungseinrichtungen verwendbar ist und üblichen Angriffen standhält, sowie universell einsetzbar ist.The invention has for its object a securing element, especially for locks, to indicate that inexpensive can be manufactured, for the protection of security-sensitive Parts for every type of security device is usable and withstands common attacks, as well is universally applicable.

Diese Aufgabe wird durch die im Anspruch 1 angegebene Erfindung gelöst. Vorteilhafte Weiterbildungen der Erfindung sind in Unteransprüchen angegeben.This object is achieved by the invention specified in claim 1 solved. Advantageous developments of the invention are specified in subclaims.

Das erfindungsgemäße Sicherungselement ist mit üblichen Angriffswerkzeugen, wie z. B. Hammer, Säge, Bohrer, Körner nicht angreifbar. Aufgrund der geringen Schichtdicke von z. B. 1-1,8 mm kann eine derartige Schicht auch auf Einsteckschlössern angebracht werden, so daß es hierbei nicht notwendig ist, spezielle Sicherheitsblenden zu verwenden. Vorzugsweise befindet sich die Schicht auf der einem Angriff ausgesetzten Seite eines Schlosses. Durch die geringe Korngröße des verwendeten Karbidmaterials wird nur relativ wenig Lotmaterial benötigt, welches lediglich erforderlich ist, um den Zusammenhalt der Karbidteilchen zu gewährleisten. Wenn eine Mischung von Karbidteilchen verschiedener Korngröße verwendet wird, füllen die Karbidteilchen kleiner Korngröße die Zwischenräume der größeren Karbidteilchen aus. Die Menge des zu verwendenden Lotmaterials kann damit sehr klein gehalten werden.The fuse element according to the invention is usual Attack tools, such as B. hammer, saw, drill, grains not vulnerable. Due to the small layer thickness of e.g. B. 1-1.8 mm, such a layer can also on mortise locks be attached so that it is not it is necessary to use special safety covers. The layer is preferably on an attack exposed side of a castle. Because of the low The grain size of the carbide material used is only relative requires little solder material, which is only necessary is to ensure the cohesion of the carbide particles. If a mixture of carbide particles different Grain size is used to fill the carbide particles smaller Grain size the spaces between the larger carbide particles out. The amount of solder material to be used can be changed be kept very small.

Die Erfindung wird nachstehend anhand eines Ausführungsbeispiels näher erläutert.The invention is described below using an exemplary embodiment explained in more detail.

Es zeigen:Show it:

Fig. 1 ein Sicherheitselement im Querschnitt von der Seite betrachtet, Fig. 1 shows a security element in cross section viewed from the side,

Fig. 2 ein Sicherheitselement von der Außenseite gesehen,See Fig. 2 a security element from the outside,

Fig. 3 eine Zwischenplatte. Fig. 3 an intermediate plate.

Fig. 1 zeigt ein erfindungsgemäßes Sicherungselement mit einem Trägerteil 1 und einer darauf aufgebrachten Schicht 2. Die Schicht 2 besteht aus einzelnen unregelmäßig geformten Karbid-Teilchen, z. B. Wolfram, Titan oder Tantal-Karbid. Derartige Karbid-Teilchen sind handelsüblich lieferbar und z. B. durch Aufbereitung von Hartmetallwerkzeug-Abfällen hergestellt. Die Korngröße der verwendeten Karbid- Teilchen liegt bei max. 1,0 mm, vorzugsweise werden Korngrößen von 0,5-1 mm verwendet. Wenn eine Mischung verschiedener Korngrößen verwendet wird, kann das zu verwendende Lotmaterial in der Menge beträchtlich reduziert werden, da die kleineren Korngrößen für einen verbindenden Halt der größeren Karbid-Teilchen sorgen. Fig. 1 shows an inventive security element with a support part 1 and a layer 2 applied thereto. Layer 2 consists of individual irregularly shaped carbide particles, e.g. B. tungsten, titanium or tantalum carbide. Such carbide particles are commercially available and z. B. produced by processing hard metal tool waste. The grain size of the carbide particles used is max. 1.0 mm, preferably grain sizes of 0.5-1 mm are used. If a mixture of different grain sizes is used, the amount of solder material to be used can be considerably reduced, since the smaller grain sizes ensure a connecting hold of the larger carbide particles.

Zur Herstellung der Sicherheitsschicht wird ein Gemisch aus Karbid-Teilchen und dem handelsüblich in pulverförmiger, rieselfähiger Form vorliegenden Lotpulver gebildet und dieses auf das Trägerteil aufgebracht, entweder mit einem Spachtel oder aufgeschüttet. Das Gemisch kann jedoch auch unter Zuhilfenahme eines Binders pastös angemengt werden, welches die Verarbeitungseigenschaften verbessert, wobei ggf. Vorkehrungen getroffen werden müssen, daß bei der Verlötung im Wärmeofen auftretende Dämpfe entfernbar sind. Die Mischung wird auf oder in den abzusichernden Bereich des Trägerteils 1 aufgebracht, ohne daß es einer speziellen Abgrenzung zum übrigen Bereich bedarf. Sofern jedoch eine genaue Abgrenzung gewünscht ist, kann die Mischung auch in einer Ausformung des Trägerteils eingebracht sein.To produce the security layer, a mixture of carbide particles and the solder powder, which is commercially available in powdery, free-flowing form, is formed and this is applied to the carrier part, either with a spatula or poured on. However, the mixture can also be mixed in paste-like manner with the aid of a binder, which improves the processing properties, whereby precautions may have to be taken that vapors occurring in the heating furnace during soldering can be removed. The mixture is applied to or in the area of the carrier part 1 to be protected, without requiring a special delimitation from the rest of the area. However, if a precise delimitation is desired, the mixture can also be introduced into a shape of the carrier part.

Trägerteil 1 und aufgebrachte Schicht 2 werden nun einer Wärmebehandlung unterzogen, die zur Vermeidung von Verzunderungen vorzugsweise unter Schutzgas oder im Vakuum stattfindet. Die Verarbeitungstemperatur bestimmt sich nach dem verwendeten Lotmaterial, wobei bei Verwendung von Nickelbasisloten die Temperatur zwischen 950 und 1100°C liegt. Bei Verwendung von Silber-, Kupfer- oder Messingloten liegt die Temperatur im Bereich von 500-950°C.Carrier part 1 and applied layer 2 are now subjected to a heat treatment, which preferably takes place under protective gas or in a vacuum in order to avoid scaling. The processing temperature is determined by the solder material used, whereby when using nickel-based solders the temperature is between 950 and 1100 ° C. When using silver, copper or brass solders, the temperature is in the range of 500-950 ° C.

Die Verwendung von Loten, die selbst eine gewisse Härte aufweisen, wird bevorzugt.The use of solders, which themselves have a certain hardness have is preferred.

Neben dem eigentlichen Verbinden der Karbid-Teilchen durch das verwendete Lotmaterial findet zusätzlich eine Versinterung der Karbid-Teilchen statt sowie eine Eindiffusion des Lotmaterials in das Trägerteil. Dies führt zu einer zusätzlichen Festigkeit der Sicherheitsschicht.In addition to actually connecting the carbide particles through the solder material used is also sintered of the carbide particles instead of diffusion of the Solder material in the carrier part. This leads to an additional one Strength of the security layer.

Für das Trägerteil wird vorzugsweise Stahl 37 verwendet.Steel 37 is preferably used for the carrier part.

Die Sicherheitsschicht 2 kann zwar auf der Angriffen abgewandten Seite einer Blende oder des Abdeckbleches eines Einsatzschlosses vorgesehen sein, vorzugsweise wird die Schicht jedoch auf der üblichen Angriffen zugekehrten Seite angeordnet. Damit wird verhindert, daß bei einem Angriff mit Bohrern das Trägerteil zunächst durchbohrt werden könnte und anschließend mit Durchschlägen die Sicherheitsschicht weggedrückt werden könnte. Wenn die Schicht dem Bohrer unmittelbar ausgesetzt ist, besteht keine Möglichkeit, die Schicht zu zerstören. Um der Sicherheitsblende oder dem Schloß nach außen hin ein ansprechendes Äußeres zu verschaffen, kann die Schicht mit einem Abdeckmaterial versehen sein oder durch eine Zierblende abgedeckt sein.The security layer 2 can indeed be provided on the side of a panel facing away from the attacks or the cover plate of an insert lock, but the layer is preferably arranged on the side facing the usual attacks. This prevents the carrier part from being pierced first in the event of an attack with drills and then the safety layer from being pushed away with punctures. If the layer is directly exposed to the drill, there is no way to destroy the layer. In order to provide the outside of the security cover or the lock with an attractive exterior, the layer can be provided with a covering material or be covered by a decorative cover.

Fig. 2 zeigt die Aufsicht einer Sicherheitsblende. Die Sicherheitsschicht 2 wird vorzugsweise um die Schließzylinderöffnung angeordnet, da in diesem Bereich sich der Schließmechanismus des Schlosses befindet. Um zusätzlich zu verhindern, daß die Schraubenbolzen bzw. Buchsen zur Befestigung der Sicherheitsblende an der Tür aufgebohrt werden können, kann in diesem Bereich ebenfalls eine Sicherheitsschicht 3 vorgesehen sein. Fig. 2 shows the supervision of a safety cover. The security layer 2 is preferably arranged around the lock cylinder opening, since the lock mechanism of the lock is located in this area. In order to additionally prevent the bolts or bushings for fastening the security cover from being drilled onto the door, a security layer 3 can also be provided in this area.

Die Sicherheitsschicht kann auch als Stirnplättchen in Zylinderschlössern angeordnet werden, um auch diesen Bereich eines Schlosses abzusichern. Sofern der verfügbare Platz dort nicht ausreicht, eine Schicht vorzusehen, kann in einer weiteren Ausgestaltung der Erfindung ein Sperrstift eines Zylinderschlosses als Rohrabschnitt mit eingefüllter Sicherheitsschicht versehen sein. Diese Schicht besteht aus den gleichen Materialien wie eine auf einem Träger angeordnete Schicht, wobei jedoch vorzugsweise Körnungen geringer Größe verwendet werden.The security layer can also be used as a face plate Cylinder locks are arranged around this area as well to secure a castle. If available There is not enough space there to provide a shift, can be in a further embodiment of the invention Locking pin of a cylinder lock as a pipe section with filled security layer. These Layer consists of the same materials as one layer arranged on a carrier, but preferably Small size grits can be used.

Das Mischungsverhältnis zwischen Lot- und Karbid-Teilchen beträgt je nach Korngröße und deren Mischung und der Sicherheitsanforderung an die Schicht etwa 1 : 5 bis 1 : 1, vorzugsweise 1 : 3.The mixing ratio between solder and carbide particles depends on the grain size and their mixture and the security requirement for the shift is about 1: 5 to 1: 1, preferably 1: 3.

Die Menge an erforderlichem Lotmaterial kann ebenfalls sehr klein gehalten werden, wenn die Sicherheitsschicht gem. Fig. 3 in eine Zwischenplatte eingefüllt wird, wobei diese zusammen mit den Karbid-Teilchen und dem Lotmaterial in einem Arbeitsvorgang mit dem Trägerteil verlötet wird. Durch Verwendung der Zwischenplatte 5 kann die Menge des benötigten Karbid-Materials gering gehalten werden, sowie gleichzeitig der Anteil des benötigten Lotes klein gehalten werden. Die Zwischenplatte besteht vorzugsweise aus einer Stahlplatte der gewünschten Schichtdicke, in die unregelmäßig bzw. stark verzahnte Löcher eingestanzt sind. Zwischen den Löchern sind schmale Stege vorhanden. Durch die unregelmäßigen, sternförmigen Löcher 6 ist es nicht möglich, daß ein auf eine derartige Schicht aufgesetzter Bohrer allein mit der Zwischenplatte in Berührung kommt, sondern wird immer auf das eine oder andere Loch 6 mit eingefülltem Material treffen. Dadurch kann ein Bohrer, auch ein Hartmetallbohrer, sehr schnell abplatzen und damit zerstört und unbrauchbar werden.The amount of solder material required can also be kept very small if the security layer acc. Fig. 3 is filled into an intermediate plate, which is soldered together with the carbide particles and the solder material in one operation with the carrier part. By using the intermediate plate 5 , the amount of carbide material required can be kept low, and at the same time the proportion of the solder required can be kept small. The intermediate plate preferably consists of a steel plate of the desired layer thickness, into which irregularly or strongly toothed holes are punched. There are narrow bars between the holes. Due to the irregular, star-shaped holes 6 , it is not possible for a drill placed on such a layer to come into contact with the intermediate plate alone, but will always hit one or the other hole 6 with the filled material. As a result, a drill bit, also a hard metal drill bit, can flake off very quickly and thus become destroyed and unusable.

Die verwendete geringe Schichtdicke erlaubt es, diese kostengünstig herzustellen und in vielen Anwendungsbereichen einzusetzen. Insbesondere kann die Schicht auf Einsteckschlössern, Zuhaltungen, Beschlägen, Sicherheitstüren, Sicherheitsbehältern wie Tresoren, Schließfächern und Alarmanlagen eingesetzt werden.The small layer thickness used allows this inexpensive to manufacture and in many applications to use. In particular, the layer can be on Mortise locks, tumblers, fittings, security doors, Security containers such as safes, lockers and alarm systems are used.

Die verwendete geringe Schichtdicke, insbesondere bei Verwendung einer Zwischenplatte erlaubt das verzugsfreie Herstellen von Sicherheitselementen sowie eine Volumen- und Gewichtsminderung. Tiefzieh-Blechteile sind nicht mehr erforderlich.The small layer thickness used, especially at The use of an intermediate plate allows distortion-free Manufacture of security elements as well as a volume and weight loss. Deep-drawn sheet metal parts are not more needed.

Claims

1. Security element, in particular for locks, consisting of a carrier part ( 1 ) and an applied thereon, essentially carbide-containing, anti-attack layer ( 2 ), which consists of a mixture of carbide particles in a solder material, characterized in that the carbide Particles a max. Have grain size of 1.0 mm and with a solder material in a ratio of 1: 1 to 5: 1 on the carrier part ( 1 ) in a layer thickness of max. 3 mm are applied.

2. Securing element according to claim 1, characterized in that the layer ( 2 ) is applied to the side of the carrier part ( 1 ) which is usually exposed to attacks.

3. Security element according to claim 2, characterized in that the carrier part ( 1 ) forms the security cover of a lock.

4. Securing element according to claim 2, characterized in that the carrier part is the front part of the locking cylinder of a castle.

5. Securing element according to claims 3 or 4, characterized in that the carrier part ( 1 ) is covered by a decorative panel.

6. Securing element according to claim 1, characterized in that the mixture of tungsten carbide in There is copper, silver, brass or nickel-based solder.

7. Securing element according to claim 1, characterized in that the carrier part is a hollow body, on the inside of which the layer is applied.

8. Securing element according to claim 7, characterized in that the hollow body is a pipe section.

9. Security element according to claim 8, characterized in that the pipe section the locking pin of a castle.

10. Fuse element according to claim 1, characterized in that the layer in openings ( 6 ) of an intermediate plate ( 5 ) with a thickness of max. 1.5 mm is introduced, which are separated from one another in a matrix-like manner by narrow webs.

11. Securing element according to claim 10, characterized in that the openings ( 6 ) are each formed by a plurality of circularly connected bores or punchings.

12. Method of making a securing element according to claim 1, characterized in that first a mixture of carbide powder with a maximum Grain size of 1.0 mm in a ratio of 1: 1 to 5: 1 and a powdered solder material which is in a layer thickness of 1-3 mm in or is applied to a carrier plate, and that then the coated carrier plate at the melting temperature of the solder with a heat treatment the mixture is connected.

13. The method according to claim 12, characterized in that that the mixing ratio is three parts tungsten carbide partly silver, copper, brass or nickel based Lot is and the solder hold time 5-30 minutes at a temperature of 500 to 1100 ° C.

14. The method according to claim 12, characterized in that heat treatment in vacuum or under protective gas he follows.