DE3430473A1 - Composite moulding - Google Patents

Composite moulding

Info

Publication number
DE3430473A1
DE3430473A1 DE19843430473 DE3430473A DE3430473A1 DE 3430473 A1 DE3430473 A1 DE 3430473A1 DE 19843430473 DE19843430473 DE 19843430473 DE 3430473 A DE3430473 A DE 3430473A DE 3430473 A1 DE3430473 A1 DE 3430473A1
Authority
DE
Germany
Prior art keywords
molded body
composite molded
body according
silicon particles
matrix mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19843430473
Other languages
German (de)
Inventor
Anton J. 7302 Ostfildern Vox
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE19843430473 priority Critical patent/DE3430473A1/en
Publication of DE3430473A1 publication Critical patent/DE3430473A1/en
Withdrawn legal-status Critical Current

Abstract

The invention relates to a composite moulding with a filling body which is provided on its surface with an outer layer. In order to achieve a very high stability, the filling body is formed by a cured matrix material which is pourable before curing and ferrosilicon particles embedded therein, at least 60 per cent by weight of the filling body being ferrosilicon particles.

Description

Verbund-Formkörper Composite molded body

Die Erfindung betrifft einen Verbund-Formkörper mit einem Füllkörper, der an seiner Oberfläche mit einer Außenschicht versehen ist.The invention relates to a composite molded body with a filler body, which is provided with an outer layer on its surface.

Für die verschiedenstartigen Zwecke verwendet man heutzutage Verbund-Formkörper z. B. plattenartiger Gestalt, bei denen Q8e; außen aufgebrachte(n) Schicht(en) im Material an die außen gewünschten Eigenschaften wie Korrosionsschutz, Oberflächenbeschaffenheit usw. angepaßt sind und den inneren Füllkörper, der dem Formkörper seine Stabilität verleiht, nach außen hin abdeckt, so daß man den Füllkörper ohne Berücksichtigung der gewünschten Außeneigenschaften ausbilden kann.Composite molded bodies are used nowadays for a wide variety of purposes z. B. plate-like shape, in which Q8e; externally applied layer (s) in Material to the externally desired properties such as corrosion protection, surface quality etc. are adapted and the inner packing, which gives the molded body its stability gives, covers to the outside, so that the packing without consideration can develop the desired external properties.

Der vorliegenden Erfindung liegt nun die Aufgabe zugrunde, einen solchen Verbund-Formkörper zu schaffen, der aus einfachen Materialien hergestellt ist und höchsten Stabilitätserfordernissen entspricht.The present invention is based on the object of such To create composite molded body which is made from simple materials and corresponds to the highest stability requirements.

Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß der Füllkörper von einer ausgehärteten und vor dem Aushärten gießfähigen Matrixmasse und darin eingebetteten Eisensiliziumteilchen gebildet wird, wobei mindestens 60 Gewichtsprozent des Füllkörpers Eisensiliziumteilchen sind.This object is achieved according to the invention in that the filler body of a hardened matrix mass which can be poured before hardening and therein embedded iron silicon particles is formed, at least 60 percent by weight of the filler body are iron silicon particles.

In besonders einfacher und billiger Weise kann die Matrixmasse von hydraulisch abgebundenem Zement gebildet werden.In a particularly simple and cheap way, the matrix mass of hydraulically set cement are formed.

Ein Formkörper mit einem solchen Füllkörper weist eine äußerst hohe Druck- und Bruchfestigkeit auf, wobei sich bei Versuchen für einen plattenförmigen Verbundkörper eine Bruchfestigkeit von 300 - 342 N/mm2 ergeben hat. Diese Festigkeit bleibt auch bei tiefen Temperaturen erhalten.A shaped body with such a filler body has an extremely high Compressive strength and breaking strength, with tests for a plate-shaped Composite body has shown a breaking strength of 300 - 342 N / mm2. This strength is retained even at low temperatures.

Die Dichte des Füllkörpers liegt zweckmäßigerweise im Bereich zwischen 5,0 utndi 6,4 g/cm3, sie ist also ebenfalls sehr hoch.The density of the packing is expediently in the range between 5.0 utndi 6.4 g / cm3, so it is also very high.

Für den angegebenen Füllkörper läßt sich ferner ein Schubmodul von zweckmäßigerweise 20 000 - 36 000 N/mm2 und ein Elastizitätsmodul bis zu 85 000 N/mm2 erzielen.A shear modulus of expediently 20,000 - 36,000 N / mm2 and a modulus of elasticity of up to 85,000 Achieve N / mm2.

Der erfindungsgemäße Verbundkörper kann somit bevorzugt überall da verwendet werden wo sehr hohe mechanische Beanspruchungen auftreten. Dabei ist eine Korrosion der Eisensiliziumteilchen nicht zu befürchten, da der Füllkörper ja nach außen hin abgedeckt ist. Gegebenenfalls könnte man die Eisensiliziumteilchen vor dem Herstellen des Füllkörpers auch mit einem Schutzüberzug beispielsweise durch Vernickeln oder Verchromen versehen.The composite body according to the invention can thus preferably be there anywhere used where very high mechanical loads occur. There is one Corrosion of the iron silicon particles is not to be feared, since the packing is after is covered on the outside. Optionally, the iron silicon particles could be presented the production of the filling body also with a protective coating, for example Nickel plating or chrome plating.

Ein bevorzugtes Anwendungsgebiet ist die Herstellung von Transport- und/oder Lagerbehältern für radioaktive Brennelemente eines Kernkraftwerks, bei denen auch ein Absturz aus mehreren Metern Höhe nicht zu einer die Umwelt gefährdenden Beschädigung des Behälters führen darf. In diesem Falle wird die Behälterwand und gegebenenfalls auch der Boden und der Deckel des Behälters gemäß vorliegender Erfindung ausgebildet. Dabei ist mit der Verwendung der Eisensiliziumteilchen der weitere Vorteil verbunden, daß diese plastisch verformbar sind, so daß beispielsweise bei einem Behälterabsturz ein großer Teil der Fallenergie durch plastische Verformung vernichtet wird.A preferred field of application is the production of transport and / or storage containers for radioactive fuel elements of a nuclear power plant which even a fall from a height of several meters does not endanger the environment Damage to the container. In this case the container wall and optionally also the bottom and the lid of the container according to the present invention educated. The use of iron silicon particles is the further one The advantage that these are plastically deformable, so that for example at In the event of a container crash, a large part of the fall energy is due to plastic deformation is destroyed.

Die Eisensiliziumteilchen und somit der gesamte Füllkörper (wegen der e«g'beieinanderliegenden Verteilung der Eisensiliziumteilchen behindert die Matrixmasse den Wärmeübergang kaum) besitzen des weiteren eine große Wärmeleitfähigkeit, was beispielsweise bei den genannten Behältern für radioaktive Brennelemente ebenfalls günstig ist. Die im Innenraum des Behälters sitzenden Brennelemente entwickeln nämlich eine große Wärmemenge, die möglichst schnell nach außen abgeführt werden muß. Ist die Behälterwand ein erfindungsgemäßer Verbund-Formkörper, erfolgt diese Wärmeabfuhr schnell und sicher durch die Behälterwand hindurch.The iron silicon particles and thus the entire filler body (because of the adjacent distribution of the iron silicon particles hinders the Matrix mass hardly any heat transfer) also have a high thermal conductivity, which is also the case, for example, with the aforementioned containers for radioactive fuel elements is cheap. The fuel elements sitting in the interior of the container develop namely a large amount of heat that must be dissipated to the outside as quickly as possible. is If the container wall is a composite molded body according to the invention, this heat dissipation takes place quickly and safely through the container wall.

Es versteht sich, daß sich diese Wärmeleiteigenschaft des Füllkörpers auch in anderen Anwendungsfällen günstig auswirkt, wenn es auf eine schnelle Wärmezufuhr oder -abfuhr durch den jeweiligen Formkörper hindurch ankommt.It goes without saying that this thermal conductivity property of the filler body also has a beneficial effect in other applications if it involves a rapid supply of heat or discharge by the respective shaped body arrives through.

Als Material für die Außenschicht oder bei plattenähnlichen Verbund-Formkörpern der beiden Außenschichten ist Stahl bestens geeignet. Dies beispielsweise deshalb, da der erfindungsgemäße Verbund-Formkörper eine Temperaturausdehnungszahl besitzt, die im Bereich der von Stahl liegt, so daß unabhängig von der herrschenden Temperatur stets ein sicherer Verbund gewährleistet ist. Auch behindert der Stahl den gegebenenfalls erwünschten Wärmedurchgang nicht.As a material for the outer layer or for panel-like composite molded bodies of the two outer layers, steel is ideal. This is because, for example, since the composite molding according to the invention has a coefficient of thermal expansion, which is in the range of steel, so that regardless of the prevailing temperature a secure network is always guaranteed. The steel also hampers this if necessary desired heat transfer not.

Es versteht sich, daß man je nach Verwendung des Verbund-Formkörpers auch andere Materialien als Stahl für die Außenschicht(en) wählen kann. So kommt beispielsweise auch Kupfer, Aluminium, Kunststoff (beispielsweise Polyamid), Asbest, Graphit, Eternit, Holz oder Gummi in Frage. Im Falle eines plattenartigen Verbund-Formkörpers mit zwei einander entgegengesetzten Außenschichten können diese auch aus unterschiedlichen Materialien bestehen.It goes without saying that, depending on the use of the composite molding can also choose materials other than steel for the outer layer (s). So come for example also copper, aluminum, plastic (e.g. polyamide), asbestos, Graphite, Eternit, wood or rubber are possible. In the case of a plate-like composite molded body with two opposing outer layers, these can also consist of different Materials exist.

Der Schichtaufbau bringt außerdem eine sehr einfache Fertigung des jeweiligen Formkörpers mit sich. Die Außenschichten können nämlich sozusagen als Schalungswände benutzt werden, zwischen die man die gießfähige Matrixmasse und die Eisensiliziumteilchen eingießen kann. Nach dem Aushärten der Matrixmasse liegt dann ohne zusätzliche Arbeiten der fertige Verbund-Formkörper vor.The layer structure also makes the production very easy respective shaped body with itself. The outer layers can be called, so to speak Formwork walls are used, between which the pourable matrix mass and the Can pour iron silicon particles. After the hardening of the matrix mass then lies the finished composite molding before doing any additional work.

Weitere Beispiele für die Verwendung des erfindungsgemäßen Verbund-Formkörpers sind die Herstellung von Tresorwänden, Panzerplatten, Maschinenteilen einschließlic-h Maschinenbetten, Motorenteilen, Walzen, Zylindern oder von Druckbehältern.Further examples of the use of the composite molding according to the invention are the production of safe walls, Armor plates, machine parts Including machine beds, engine parts, rollers, cylinders or pressure vessels.

Alle diese Gegenstände können als Verbund-Formkörper gemäß der vorliegenden Erfindung ausgebildet sein. Dabei sind der Verwendungsvielfalt keine Grenzen gesetzt.All of these articles can be used as composite molded articles according to the present invention Invention be formed. There are no limits to the variety of uses.

Zur weiteren Erhöhung der Festigkeit ist vorgesehen, daß die Eisensiliziumteilchen unregelmäßig geformt, zweckmäßigerweise gezackt sind. Bei einer solchen Gestalt sind die Teilchen sozusagen ineinander verhakt und stehen somit besser in Eingriff miteinander.To further increase the strength, it is provided that the iron silicon particles are irregularly shaped, suitably jagged. With such a figure the particles are hooked together, so to speak, and are therefore better engaged together.

Eine weitere zweckmäßige Maßnahme besteht darin, daß die Korngröße der Eisensiliziumteilchen variiert, wobei bezogen auf das Gesamtgewicht der Eisensiliziumteilchen die Gewichtsprozente mit ansteigender Korngröße zunehmen. Hiermit ist' gemeint, daß mehrere Teilmengen von Eisensiliziumteilchen <-mit unterschiedlicher Korngröße vorhanden sind, wobei das Gewicht der jeweiligen Teilmenge mit steigender Korngröße zunimmt. Dabei kann die Korngröße im Bereich von nahezu O bis etwa 30 - 40 mm variieren. Bei einer besonders günstigen Korngrößenverteilung ergeben sich im Gewichtsprozent der Eisensiliziumteilchen/Korngröße-Diagramm auf einer parabelähnlichen Kurve liegende Punkte.Another useful measure is that the grain size of iron silicon particles varies based on the total weight of iron silicon particles the weight percent increases with increasing grain size. This means' that several subsets of iron silicon particles <-with different grain size are present, the weight of the respective subset with increasing grain size increases. The grain size can vary in the range from almost 0 to about 30-40 mm. In the case of a particularly favorable grain size distribution, the result is in percent by weight the iron silicon particle / grain size diagram lying on a parabolic curve Points.

Hierbei ist zweckmäßigerweise etwa folgende Korngrößenverteilung vorhanden: Korngröße 0,2 5 0,5 1,0 2,0 4,0 8,0 16,0 55,5 GewichisprozenL 2 - 3 4 - 5 6 - 7 8 - 9 11-12 15-17 23-24 26-28 der FeSi-Teilehen ! Ist eine noch höhere Wärmeleitfähigkeit des Verbund-Formkörpers erwünscht, können in-dem Füllkörper zusätzlich zu den Eisensiliziumteilchen Metallteilchen, zweckmäßigerweise aus Kupfer, in die Matrixmasse eingebettet sein. Hierbei hat sich für einen Brennelement-Behälter als günstig herausgestellt, daß das Verhältnis von Eisensiliziumteilchen zu Kupferteilchen gewichtsmäßig etwa bei 5 liegt.The following grain size distribution is expediently available: Grain size 0.2 5 0.5 1.0 2.0 4.0 8.0 16.0 55.5 Weight percentage 2 - 3 4 - 5 6 - 7 8 - 9 11-12 15-17 23-24 26-28 the FeSi part! If an even higher thermal conductivity of the composite molding is desired, in addition to the iron-silicon particles, metal particles, advantageously made of copper, can be embedded in the matrix mass in the filler body. It has been found to be favorable for a fuel assembly container that the ratio of iron silicon particles to copper particles is approximately 5 in terms of weight.

In dem Füllkörper können des weiteren Stahlfasern und/oder Kunststoffasern, z.B. Polyamidfasern, in die Matrixmasse eingebettet sein, was vor allem der mechanischen Festigkeit förderlich ist.In addition, steel fibers and / or synthetic fibers, e.g. polyamide fibers, which can be embedded in the matrix mass, which is mainly the mechanical Strength is beneficial.

Der Füllkörper kann auch Versteifungsanker und/oder Versteifungsgerippe und/oder Hohlräume und/oder nach außen mündende Kanäle oder Rohrleitungen beispielsweise zum Durchführen eines Kühl- oder Heizmediums, z. B. Wasser, oder elektrischer Leitungen enthalten. Ein solcher Einbau kann je nach dem Verwendungszweck des Verbund-Formkörpers gewählt werden.The filler body can also stiffening anchors and / or stiffening frameworks and / or cavities and / or channels or pipelines opening out to the outside, for example for carrying out a cooling or heating medium, e.g. B. water, or electrical lines contain. Such an installation can, depending on the intended use of the composite molded body to get voted.

Oben wurde schon erwähnt, daß die Matrixmasse von hydraulisch abgebundenem Zement gebildet werden kann. Da bei einer solchen Matrixmasse die Festigkeit von dem Wasserzementwert der bei der Herstellung der Matrixmasse des Verbund-Formkörpers zu verwendenden Wasser/Zement-Mischung abhängt, wurde ein besonders günstiger Wasserzementwert ausgewählt. Dieser Wasserzementwert, d. h. das Verhältnis der Wassermenge in kg zur Zementmenge in kg, liegt im Bereich von etwa 0,4 -0,5, zweckmäßigerweise bei etwa 0,45.It was already mentioned above that the matrix mass of hydraulically set Cement can be formed. Since with such a matrix mass the strength of the water-cement value in the production of the matrix mass of the composite molding depends on the water / cement mixture to be used particularly favorable water-cement ratio selected. This water-cement value, i.e. H. The relationship the amount of water in kg to the amount of cement in kg is in the range of about 0.4-0.5, expediently at about 0.45.

Die Eigenschaften der Matrixmasse werden des weiteren dadurch optimiert, daß das Ausbreitmaß der bei ihrer Herstellung verwendeten Wasser/Zement-Mischung im Bereich von etwa 34 -38 cm liegt.The properties of the matrix mass are further optimized by that the slump of the water / cement mixture used in their manufacture is in the range of about 34-38 cm.

Der Matrixmasse können je nach Bedarf auch Gleitmittel beigegeben werden.If required, lubricants can also be added to the matrix mass will.

Anstelle aus abgebundenem Zement kann die Matrixmasse je nach Verwendung des Verbund-Formkörpers auch aus einem erstarrten, zuvor fließfähigen Kunststoff oder aus Metall, insbesondere aus Aluminium oder Kupfer bestehen.Instead of set cement, the matrix mass can be used depending on the use of the composite molding also made of a solidified, previously flowable plastic or made of metal, in particular aluminum or copper.

Anhand der Zeichnung wird nun noch ein Ausführungsbeispiel der Erfindung kurz beschrieben. Es zeigen: Fig. 1 einen plattenförmigen Verbund-Formkörper gemäß der Erfindung im Querschnitt und Fig. 2 ein Diagramm, das die im Anspruch 6 enthaltene Tabelle anschaulich wiedergibt.An exemplary embodiment of the invention will now be described with reference to the drawing briefly described. The figures show: FIG. 1 a plate-shaped composite molding according to FIG of the invention in cross section; and FIG. 2 is a diagram showing that contained in claim 6 Table clearly shows.

Der plattenförmige Verbund-Formkörper gemäß Fig. 1 besteht aus einem mittleren Füllkörper 1 und zwei Außtenschichten 2, 3, die jeweils auf eine der Oberflächen des Füllkörpers aufgesetzt sind. Es ergibt sich insgesamt ein schichtförmiger Aufbau, wobei die Füllkörperschicht 1, wie beschrieben, eine Vielzahl von Eisensiliziumteilchen 4 unregelmäßiger Gestalt mit verschiedenen Korngrößen enthält, die in eine Matrixmasse 5 eingebettet sind. Die beiden Außenschichten 2, 3 können von Stahlplatten gebildet werden, es sind jedoch auch andere Materialien möglich, wie ebenfalls schon beschrieben worden ist. Ferner ist in Fig. 1 noch ein in dem Füllkörper enthaltener und an der zugewandten Außenschicht 3 befestigter Versteifungsanker 6 angedeutet. Schließlich ist noch eine den Füllkörper 1 durchziehende Rohrleitung 7 eingezeichnet.The plate-shaped composite molding according to FIG. 1 consists of a middle packing 1 and two outer layers 2, 3, each on one of the surfaces of the packing are put on. Overall, the result is a layered one Structure, wherein the packing layer 1, as described, a plurality of iron silicon particles 4 contains irregular shape with different grain sizes, which in a matrix mass 5 are embedded. The two outer layers 2, 3 can be formed from steel plates However, other materials are also possible, as already described has been. Furthermore, in Fig. 1 is still contained in the packing and on the facing outer layer 3 of attached stiffening anchor 6 indicated. In the end a pipeline 7 extending through the filler body 1 is also shown.

Wie oben erläutert, sind bei einem bevorzugten Ausführungsbeispiel mehrere Teilmengen von Eisensiliziumteilchen mit unterschiedlicher Korngröße vorhanden, wobei das Gewicht der jeweiligen Teilmenge mit steigender Korngröße zunimmt.As explained above, in a preferred embodiment several subsets of iron silicon particles with different grain sizes are present, whereby the weight of the respective subset increases with increasing grain size.

Dies ist in Fig. 2 veranschaulicht, aus der außerdem leicht ersichtlich ist, daß die der Tabelle gemäß Anspruch 6 entsprechenden Punkte in diesem Diagramm etwa auf einer parabelförmigen Kurve liegen.This is illustrated in FIG. 2, from which it can also be easily seen is that the table according to claim 6 corresponding points in this diagram lie roughly on a parabolic curve.

- Leerseite -- blank page -

Claims (20)

Verbund-Formkörper Anspriäche 1. Verbund-Formkörper mit einem Füllkörper, der an seiner Oberfläche mit einer Außenschicht versehen ist, dadurch gekennzeichnet, daß der Füllkörper von einer ausgehärteten und vor dem Aushärten gießfähigen Matrixmasse und darin eingebetteten Eiçsensiliziumteilchen gebildet wird, wobei mindestens 60 Gewichtsprozent des Füllkörpers Eisensiliziumteilchen sind. Composite molded body Claims 1. Composite molded body with a filler body, which is provided with an outer layer on its surface, characterized in that, that the filler body is made of a hardened matrix mass which can be poured before hardening and forming ferrous silicon particles embedded therein, wherein at least 60 Weight percent of the packing is iron silicon particles. 2. Verbund-Formkörper nach Anspruch 1, dadurch gekennzeichnet, daß die Eisensiliziumteilchen unregelmäßig geformt, zweckmäßigerweise gezackt sind.2. Composite molded body according to claim 1, characterized in that the iron silicon particles are irregularly shaped, suitably jagged. 3. Verbund-Formkörper nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß die Korngröße der Eisensiliziumteilchen variiert, wobei bezogen auf das Gesamtgewicht der Eisensiliziumteilchen die Gewichtsprozente mit ansteigender Korngröße zunehmen.3. Composite molded body according to claim 1 or 2, characterized in that that the grain size of the iron silicon particles varies, based on the total weight of iron silicon particles, the weight percent increases with increasing grain size. 4. Verbund-Formkörper nach Anspruch 3, dadurch gekennzeichnet, daß die Korngröße im 3ereich von nahezu 0 bis etwa 30 - 40 mm variiert.4. Composite molded body according to claim 3, characterized in that the grain size varies in the range from almost 0 to about 30-40 mm. 5. Verbund-Formkörper nach Anspruch 3 oder 4, dadurch gekennzeichnet, daß sich im Gewichtsprozent der Eisensiliziumteilchen/Korngröße-Diagramm auf einer parabelähnlichen Kurve liegende Punkte ergeben (Fig. 2).5. Composite molded body according to claim 3 or 4, characterized in that that the weight percent of the iron silicon particles / grain size diagram on a Points lying in a parabola-like curve result (FIG. 2). 6. Verbund-Formkörper nach einem der Ansprüche 3 bis 5, dadurch gekennzeichnet, daß etwa folgende Korngrößenverteilung der Eisensiliziumteilchen vorhanden ist: Korngröße 0,25 0,5 1,0 2,0 4,0 8,0 16,0 31,5 Gewichtsprozent der FeSi-Teilehen 2 - 3 4 - 5 6 - 7 8 - 9 11-12 15-17 23-24 26-28
6. Composite molded body according to one of claims 3 to 5, characterized in that there is approximately the following grain size distribution of the iron silicon particles: Grain size 0.25 0.5 1.0 2.0 4.0 8.0 16.0 31.5 Weight percent of FeSi-parts 2 - 3 4 - 5 6 - 7 8 - 9 11-12 15-17 23-24 26-28
7. Verbund-Formkörper nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Matrixmasse von hydraulisch abgebundenem Zement gebildet wird.7. Composite molded body according to one of claims 1 to 6, characterized in that that the matrix mass is formed by hydraulically set cement. 8. Bei der Herstellung der Matrixmasse des Verbund-Formkörpers nach Anspruch 7 zu verwendende Wasser/Zement-Mischung, dadurch gekennzeichnet, daß der Wasserzementwert der Mischung, d. h. das Verhältnis der Wassermenge in kg zur Zementmenge in kg im Bereich von etwa 0,4 - 0,5, zweckmäßigerweise bei etwa 0,45 liegt.8. In the production of the matrix mass of the composite molding according to Claim 7 to be used water / cement mixture, characterized in that the Water-cement ratio of the mixture, d. H. the ratio of the amount of water in kg to the amount of cement in kg in the range of about 0.4-0.5, expediently about 0.45. 9. Bei der Herstellung der Matrixmasse des Verbund-Formkörpers nach Anspruch 7 zu verwendende Wasser/Zement-Mischung, dadurch gekennzeichnet, daß das Ausbreitmaß der Wasser/Zement-Mischung im Bereich von etwa 34 - 38 cm liegt.9. During the production of the matrix mass of the composite molding after Claim 7 to be used water / cement mixture, characterized in that the The slump of the water / cement mixture is in the range of about 34-38 cm. 10. Verbund-Formkörper nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Matrixmasse aus einem erstarrten, zuvor fließfähigen Kunststoff besteht.10. Composite molded body according to one of claims 1 to 6, characterized in that that the matrix mass consists of a solidified, previously flowable plastic. 11. Verbund-Formkörper nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Matrixmasse aus Metall, insbesondere aus Aluminium oder Kupfer besteht.11. Composite molded body according to one of claims 1 to 6, characterized in that that the matrix mass consists of metal, in particular aluminum or copper. 12. Verbund-Formkörper nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, daß die Dichte des Füllkörpers im Bereich zwischen 5,0 und 6,4 g/cm3 liegt.12. Composite molded body according to one of claims 1 to 11, characterized characterized in that the density of the packing is in the range between 5.0 and 6.4 g / cm3 lies. 13. Verbund-Formkörper nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, daß der Füllkörper einen Schubmodul von 20 000 - 36 000 N/mm2 besitzt.13. Composite molded body according to one of claims 1 to 12, characterized characterized in that the packing has a shear modulus of 20,000 - 36,000 N / mm2. 14. Verbund-Formkörper nach einem der Ansprüche 1 bis 13, dadurch gekennzeichnet, daß der Elastizitätsmodul des Füllkörpers bis zu 85 000 N/mm2 beträgt.14. Composite molded body according to one of claims 1 to 13, characterized characterized in that the modulus of elasticity of the packing is up to 85,000 N / mm2. 15. Verbund-Formkörper nach einem der Ansprüche 1 bis 14, dadurch gekennzeichnet, daß in dem Füllkörper außerdem Metallteilchen, zweckmäßigerweise aus Kupfer, in die Matrixmasse eingebettet sind.15. Composite molded body according to one of claims 1 to 14, characterized characterized in that in the packing also metal particles, expediently made of copper, in the matrix mass are embedded. 16. Verbund-Formkörper nach Anspruch 15, dadurch gekennzeichnet, daß das Verhältnis von Eisensiliziumteilchen zu Kupferteilchen gewichtsmäßig etwa 5 beträgt.16. Composite molded body according to claim 15, characterized in that the ratio of iron silicon particles to Copper particles by weight is about 5. 17. Verbund-Formkörper nach einem der Ansprüche 1 bis 16, dadurch gekennzeichnet, daß in dem Füllkörper Stahlfasern und/oder Kunststoffasern, z. B. Polyamidfasern, in die Matrixmasse eingebettet sind.17. Composite molded body according to one of claims 1 to 16, characterized characterized in that steel fibers and / or plastic fibers, for. B. Polyamide fibers in which the matrix mass is embedded. 18. Verbund-Formkörper nach einem der Ansprüche 1 bis 17, dadurch gekennzeichnet, daß der Füllkörper Versteifungsanker und/oder Versteifungsgerippe und/oder Hohlräume und/ oder nach außen mündende Kanäle oder Rohrleitungen beispielsweise zum Durchführen eines Kühl- oder Heizmediums, z.B.18. Composite molded body according to one of claims 1 to 17, characterized characterized in that the filling body stiffening anchor and / or stiffening framework and / or cavities and / or channels or pipelines opening out to the outside, for example for passing through a cooling or heating medium, e.g. Wasser, oder elektrischer Leitungen enthält.Contains water or electrical wiring. 19. Verbund-Formkörper nach einem der Ansprüche 1 bis 18, dadurch gekennzeichnet, daß die Außenschicht(en) aus Stahl bestehta bzw. bestehen.19. Composite molded body according to one of claims 1 to 18, characterized characterized in that the outer layer (s) consists of steel or consist. 20. Verwendung des Verbund-Formkörpers nach einem der Ansprüche 1 bis 19 zur Herstellung von Transport- und/oder Lagerbehältern für radioaktive Brennelemente eines Kernkraftwerks, Tresorwänden, Panzerplatten, Maschinenteilen, Motorenteilen, Walzen, Zylindern oder von Druckbehältern.20. Use of the composite molded body according to one of claims 1 to 19 for the production of transport and / or storage containers for radioactive fuel elements of a nuclear power plant, vault walls, armor plates, machine parts, engine parts, Rollers, cylinders or pressure vessels.
DE19843430473 1984-08-18 1984-08-18 Composite moulding Withdrawn DE3430473A1 (en)