DE2611996A1 - Siliconising chemical colour-reaction paper - by coating with polyurethane dispersion and crosslinking with silicone soln. contg. hardener - Google Patents
Siliconising chemical colour-reaction paper - by coating with polyurethane dispersion and crosslinking with silicone soln. contg. hardenerInfo
- Publication number
- DE2611996A1 DE2611996A1 DE19762611996 DE2611996A DE2611996A1 DE 2611996 A1 DE2611996 A1 DE 2611996A1 DE 19762611996 DE19762611996 DE 19762611996 DE 2611996 A DE2611996 A DE 2611996A DE 2611996 A1 DE2611996 A1 DE 2611996A1
- Authority
- DE
- Germany
- Prior art keywords
- layer
- reaction
- silicone
- paper
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Trennpapier und Verfahren zu seiner HerstellungRelease paper and process for its manufacture
Die Erfindung betrifft ein siliconisiertes Abdeckpapier für insbesondere Selbstklebe-Etiketten, -Folien und -Papiere sowie ein Verfahren zu seiner Herstellung.The invention relates to a siliconized masking paper for in particular Self-adhesive labels, foils and papers and a process for its production.
Siliconisierte Trennpapiere dienen in der Regel zum Abdecken selbstklebender Etiketten, Folien und Papiere. Das Trennpapier soll die Klebeschicht schützen und die Klebkraft unvermindert erhalten. Häufig dient das Trennpapier bei Selbstklebeetiketten auch als Transportband, wenn die Etiketten auf den Siliconpapier ausgestanzt, gegebenenfalls bedruckt und dann von einer Rolle durch eine maschinelle Vorrichtung abgenommen und aufgeklebt werden.Siliconized release papers are usually used to cover self-adhesive Labels, foils and papers. The release paper should protect the adhesive layer and maintain the bond strength undiminished. The release paper is often used for self-adhesive labels also as a conveyor belt if the labels are punched out on the silicone paper, if necessary printed and then removed from a roll by a mechanical device and glued on.
Zur Herstellung der Trennpapiere werden besondere und damit teurere Rohpapiere als Trägermaterial ausgewählt. Geeignet sind z.B dichte und glatte Papiere, die ein Minimum an Siliconauftrag erfordern. Da Silicone teure Produkte sind, kann man auf diese Weise trotz des ausgewählten teuren Papiers, bedingt durch den sehr dünnen Siliconauftrag relativ kostengünstige Trennpapiere herstellen.For the production of the release papers special and therefore more expensive Base papers selected as carrier material. For example, dense and smooth papers are suitable, which require a minimum of silicone application. Since silicones are expensive products, can one in this way despite the selected expensive paper, due to the very thin silicone application to produce relatively inexpensive release papers.
Verwendet werden hauptsächlich Pergamin, Pergamentersatz, Echtpergament und Sulfatpapiere mit und ohne Vorbeschichtung.Mainly parchment, parchment substitute and real parchment are used and sulphate papers with and without precoating.
Die Oberfläche dieser Papiersorten wird meist noch veredelt, um den Siliconauftrag weitestgehend zu verringern. Zudem werden die Papieroberflächen geschlossen.The surface of these types of paper is usually refined in order to achieve the To reduce silicone application as much as possible. In addition, the paper surfaces are closed.
Für die Beschichtung mit Siliconemulsionen eignen sich dagegen nur dicht gearbeitete und gut geleimte Papiere aus Sulfat- und Sulfitzellstoffen, die in der Regel ebenfalls noch einen Vorstrich erhalten.For coating with silicone emulsions, however, are only suitable densely worked and well sized papers made of sulphate and sulphite pulps, the usually also received a primer.
Das Trennpapier ist in der Kombination mit dem selbstklebenden Papier oder der selbstklebenden Folie in der Regel die teuerste Komponente des kaschierten Selbstklebelaminats. Außer die Selbstklebeschicht zu schützen, die Klebkraft zu erhalten und ein leichtes und problemloses Abziehen der Etikettenfolien oder Etikettenpapiere zu gewährleisten, erfüllt das Trennpapier keine weitere Aufgabe. Das bedeutet, daß es nach dem Gebrauch der Selbstklebeerzeugnisse weggeworfen wird. Seine Wiederverwendung ist wirtschaftlich nicht möglich. Insofern stellt die Nichtnutzung des vom Selbstklebeprodukt getrennten teuren Siliconpapiers wirtschaftlich einen erheblichen Verlust faktor dar.The release paper is in combination with the self-adhesive paper or the self-adhesive film is usually the most expensive component of the laminated Self-adhesive laminate. Besides protecting the self-adhesive layer, the adhesive strength increases and easy and problem-free removal of the label films or label papers To ensure this, the release paper fulfills no further task. It means that it is thrown away after using the self-adhesive products. Its reuse is not economically feasible. In this respect, the non-use of the self-adhesive product represents separate expensive silicone paper is a significant loss factor economically represent.
Aufgabe der Erfindung ist daher, ein Trennpapier für insbesondere se@bstklebende Etiketten, Folien oder Papiere sowie ein Verfahren zu seiner Herstellung zu schaffen, das außer den genannten Gigenschaften die Möglichkeit bietet, einer wirtschaflich sinnvollen Verwendung zu dienen.The object of the invention is therefore to provide a release paper for in particular se @ bst adhesive labels, foils or papers and a process for their production to create, which in addition to the properties mentioned, offers the possibility of a to serve economically meaningful use.
@ese Aufgabe wird erfindungsgemäß durch ein Trennpapier geist, das ich dadurch auszeichnet, daß es aus einem zumindest - seitlg siliconisierten chemischen Farbreaktionspapier be-@eht.@ese task is spiritually according to the invention by a release paper that I am characterized by the fact that it consists of at least one side siliconized chemical Color reaction paper required.
gemische rarbreaktionspapiere sind bekannt. Es handelt sich rei um ein mit zwei farblosen Chemikalien imprägniertes der. - ei die Chemikalien, wenn sie miteinander reagieren, Die @@@@ Substanz mit bestimmter und charakteristischer @@@@ engeben Die beiden Chemikalien sind auf dem Papier derart p@@@tioniert, daß sie ohne äußere Einwirkung nicht reazierenD cdes wird vorzugsweise dadurch erreicht, daß eine @@emik@@@ sich in sich mikroskopisch kleinen Kapseln befindet, die en der anderen Chemikalie umgeben sind. An den Stellen des ap@ers, auf die z.B. ein bestimmter Druck ausgeübt wird, arbrechex die Kapseln,und die Chemikalie aus den zerbrochenen kapseln dann mit der anderen Chemikalie reagieren, wodurch ein -ichtbatr-. farbiges Bild erzeugt wird. mixed color reaction papers are known. It's all about one that is impregnated with two colorless chemicals. - ei the chemicals, though they react with each other, the @@@@ substance with definite and characteristic @@@@ engabe The two chemicals are p @@@ tioned on the paper in such a way that they do not react without external influenceD cdes is preferably achieved by that a @@ emik @@@ is located in microscopic capsules, the end of the surrounded by another chemical. In the places of the ap @ er to which e.g. a certain Pressure is applied, the capsules arbrechex, and the chemical from the broken one capsules then react with the other chemical, creating a -ichtbatr-. colored Image is generated.
der atentschrift 3 383 121 wird ein Laminat aus hauptsächlie - -eSchichten beschrieben, dessenerste Schicrt aus einem Papier und dessen dritte Schicht aus einem chemischen Reaktionspapier besteht. Die zweite Schicht soll drucksensitiv klebend sein. In einer Ausführungsform soll die dritte Schicht einen die drucksensitive Klebeschicht abstoßenden Überzug tragen, während die erste Schicht mit einem die Klebeschicht anziehenden Überzug bedeckt sein soll. In dieser Druckschrift werden lediglich Anordnungen verschiedener Schichten beschrieben. Konkrete Wege zur Lösung der erfindungsgemäßen Aufgabe sind nicht einmal andeutungsweise angegeben. The patent specification 3 383 121 is a laminate of mainly - -e layers described, whose first dispatch one paper and its third Layer consists of a chemical reaction paper. The second layer is said to be pressure sensitive be sticky. In one embodiment, the third layer is intended to be pressure sensitive Adhesive layer wear repellent coating, while the first layer with a die Adhesive-attracting coating should be covered. In this publication only the arrangements of different layers are described. Concrete ways to the solution the object according to the invention are not even indicated in any way.
Das Siliconisieren des chemischen Farbreaktionspapiers lag keineswegs nahe, denn der Fachmann weiß, daß das System des Reaktionspapiers beim Auftragen des Silicon films - sei es z.B. durch die hohe Vernetzungstemperatur, sei es durch Weichmacher- oder Härterlösungen oder Lösungsmittel des Silicons -zerstört wird. Erfindungsgemäß ist es jedoch gelungen, den Siliconauftrag auf das chemische Farbreaktionspapier aufzutragen, ohne daß das Reaktionssystem zerstört wird, so daß das siliconisierte Produkt als Trennpapier zum Abdecken von z.B.The siliconization of the chemical color reaction paper was by no means close, because the person skilled in the art knows that the system of the reaction paper when applying of the silicone film - be it through the high cross-linking temperature, for example, or through Plasticizer or hardener solutions or solvents in the silicone are destroyed. According to the invention, however, it has been possible to apply the silicone to the chemical color reaction paper to apply without destroying the reaction system, so that the siliconized Product as release paper for covering e.g.
Selbstklebeetiketten, -folien oder -papieren verwendet werden und gleichzeitig als Durchschreibekopie dienen kann. Der Bedarf einer derartigen Kombination ist vielfältig und bedarf vorliegend keiner besonderen Erläuterung. Das Trennpapier für die selbstklebenden Erzeugnisse ist Informationsträger geworden und erfüllt damit eine wichtige Funktion. Es stellt kein nutzlos verlorenes Produkt mehr dar.Self-adhesive labels, foils or papers are used and can also serve as a carbon copy. The need for such a combination is diverse and does not require any special explanation in the present case. The release paper information carrier for self-adhesive products has become and fulfilled thus an important function. It is no longer a uselessly lost product.
Das erfindungsgemäße Trennpapier ist vorzugsweise derart aufgebaut, daß das chemische Farbreaktionspapier auf der Seite des Reaktionssystems siliconisiert ist. Es war insbesondere überraschend, daß gerade dann, wenn man den Siliconauftrag auf der Seite des Reaktionssystems aufbringt, ein besonders gutes Trennpapier entsteht und daß gerade dann eine Zerstörung des Reaktionssystems vermieden werden kann.The release paper according to the invention is preferably constructed in such a way that that the chemical color reaction paper siliconized on the side of the reaction system is. It was particularly surprising that just when you were applying the silicone on the side of the reaction system, a particularly good release paper is produced and that just then destruction of the reaction system can be avoided.
Wesentlich ist, daß zwischen der Farbreaktionspapieroberfläche und der Siliconschicht, insbesondere zwischen der Reaktionsschicht des Farbreaktionspapiers und der Siliconschicht, eine für sämtliche Bestandteile des Siliconauftrags, der in der Regel aus einer Siliconlösung mit Härtern oder einer Siliconemulsion mit Härtern besteht, undurchlässige Schicht angeordnet wird. Diese Zwischenschicht muß außerdem die Bedingungen erfüllen, daß sie sich insbesondere auf der Reaktionsschicht verankert, sich gegenüber den Chemikalien des Reaktionspapiers neutral verhält, beim Auftragen keine Veränderungen des Systems des Reaktionspapiers hervorgerufen werden und sie darüber hinaus mit der Siliconschicht vernetzbar ist.It is essential that between the color reaction paper surface and the silicone layer, especially between the reaction layer of the color reaction paper and the silicone layer, one for all components of the silicone application, the usually from a silicone solution with hardeners or a silicone emulsion with Hardener consists, impermeable layer is arranged. This intermediate layer must also meet the conditions that they are in particular on the reaction layer anchored, behaves neutrally towards the chemicals of the reaction paper, no changes in the system of the reaction paper caused during application and it can also be crosslinked with the silicone layer.
Diese Bedingungen werden in überraschender Weise von einer Polyurethan-Dispersionsschicht erfüllt. Besonders geeignet ist eine Schicht aus einer anionischen, feindispersen Kunststoffdispersion auf Basis von linearem Polyesterurethan, die frei von Lösungsmitteln, Weichmachern und freien Emulgatoren ist. Eine solche Dispersion (Polyurethan-Dispersion V) soll eine Dichte von etwa 1,09 g/l, einen pH-Wert von 5,5 bis 7, eine Haake-Viscosität, VT-02, von etwa 100 cP und einen Feststoffgehalt von 35 bis 42 Gews haben und sich außerdem durch ein hervorragendes Filmbildungsvermögen auszeichnen. Eine daraus auf die Reaktionsschicht aufgetragene ausgehärtete Beschichtung ist glänzend, flexibel, klebfrei, lichtecht, alterungsbeständig, heißsiegelfähig und geruchs- und geschmacksfrei.These conditions are surprisingly met by a polyurethane dispersion layer Fulfills. A layer composed of an anionic, finely dispersed layer is particularly suitable Plastic dispersion based on linear polyester urethane that is free from solvents, Plasticizers and free emulsifiers is. Such a dispersion (Polyurethane dispersion V) should have a density of about 1.09 g / l, a pH of 5.5 to 7, a Haake viscosity, VT-02, of about 100 cP and a solids content from 35 to 42 percent by weight and also have an excellent film-forming ability distinguish. A cured coating applied therefrom to the reaction layer is glossy, flexible, non-sticky, lightfast, non-aging, heat-sealable and odorless and tasteless.
Sie weist außerdem eine hohe Öl- und Fettdichtigkeit, gute Kalt- und Heißwasserfestigkeit sowie eine gute Wisch- und Kratzfestigkeit auf.It also has a high oil and grease tightness, good cold and Hot water resistance as well as good smear and scratch resistance.
Normalerweise neigt eine Beschichtung mit einer solchen Polyurethan-Dispersion bei erhöhter Lagertemperatur und Luftfeuchtigkeit sowie bei Druckbelastung zum Blocken, so daß sich ihre erfindungsgemäße Verwendung nicht anbot. Es hat sich jedoch gezeigt, daß, wenn die Beschichtung einer Trocken-Menge von 10 bis 18 g/qm aufgetragen wird, dennoch ausgezeichnete Ergebnisse erzielt werden. Da die Aushärtung bei niedrigen Temperaturen im Bereich von 70 bis 1100C erfolgt, ist auch dies für die Reaktionsschicht unschädlich.Usually a coating with such a polyurethane dispersion tends to occur with increased storage temperature and humidity as well as with pressure load for blocking, so that their use according to the invention was not an option. However, it has been shown that if the coating is applied in a dry amount of 10 to 18 g / m2, nevertheless excellent results can be achieved. Since curing at low Temperatures in the range from 70 to 1100C takes place, this is also true for the reaction layer harmless.
Auf die ausgehärtete Polyurethanschicht ist eine Silicon schicht aufgetragen. Wesentlich ist, daß die aufzutragende Siliconlösung oder Siliconemulsion mindestens einen Härter aufweist, der eine Vernetzung der Polyurethanschicht mit der Siliconschicht bewirkt.A silicone layer is applied to the cured polyurethane layer. It is essential that the silicone solution or silicone emulsion to be applied is at least has a hardener which cross-links the polyurethane layer with the silicone layer causes.
Besonders vorteilhaft ist, wenn ein Härter im Siliconauftrag enthalten ist, der sowohl die Siliconschicht selbst als auch die Siliconschicht mit der Polyurethanschicht vernetzen kann.It is particularly advantageous if a hardener is included in the silicone application which is both the silicone layer itself and the silicone layer with the polyurethane layer can network.
Derartige Härter sind bekannt und im Handel und können für die Zwecke der Erfindung ausgewählt und zusammengestellt werden.Such hardeners are known and in the trade and can be used for the purpose of the invention are selected and compiled.
Beispielsweise erfüllt ein Siliconmittelauftrag diese Bedingung in besonderem Maße, der aus einer klaren Lösung von Polyorganosiloxan in Toluol (Baysilon Abhäsiv PR) besteht.For example, applying a silicone agent fulfills this condition in especially that from a clear solution of polyorganosiloxane in toluene (Baysilon Adhesive PR).
Das Produkt hat einen Silicongehalt von etwa 20% und eine Viskosität von etwa 4000 cps bei einem spezifischen Gewicht von etwa 0,88 g/l. Es wird vor der Härterzugabe auf mindestens 1:1 mit aromatischen Kohlenwasserstoffen verdünnt und mit drei Härterlösungen (Nr. 178, 179, 181) versetzt. Mindestens eine dieser Härterlösungen vernetzt u.a. die Zwischenschicht mit der Silicon schichtbei der Aushärtung des Siliconauftrags im Temperaturbereich von 100 bis 110° C.The product has a silicone content of about 20% and a viscosity of about 4000 cps with a specific gravity of about 0.88 g / L. It will be before the addition of hardener diluted to at least 1: 1 with aromatic hydrocarbons and mixed with three hardener solutions (No. 178, 179, 181). At least one of these Hardener solutions cross-link the intermediate layer with the silicone layer in the Curing of the silicone application in the temperature range from 100 to 110 ° C.
Das Verfahren zur Herstellung des erfindungsgemäßen Trennpapiers weist zwei Stufen auf. In der ersten Stufe wird auf die Reaktionssystemseite einer handelsüblichen chemischen Farbreaktionspapierbahn eine anionische, feindisperse,von organischen Lösungsmitteln, Weichmachern und freien Emulgatoren freie Kunststoffdispersion auf der Basis von linearem Polyesterurethan mit einem Feststoffgehalt von 35 bis 42 Gew.%, vorzugsweise von 40 Gew.%, und einer Trocken-Menge von 10 bis 18 g/qm, vorzugsweise von 12 g/qm, aufgetragen. Der Auftrag kann auf jeder bekannten Streichanlage, vorzugsweise mit einer Luftbürste erfolgen. Die erforderliche Streichviscosität kann eingestellt werden, indem zur Verdünnung Leitungswasser und zur Verdickung das Ammoniumsalz der polymeren Acrylsäure oder Polyvinylalkohol oder Carboxymethylcellulose verwendet werden.The method for producing the release paper according to the invention has two levels up. In the first stage, a commercially available one is used on the reaction system side chemical color reaction paper web an anionic, finely dispersed, organic Plastic dispersion free of solvents, plasticizers and free emulsifiers based on linear polyester urethane with a solids content of 35 to 42 % By weight, preferably from 40% by weight, and a dry amount of 10 to 18 g / m², preferably of 12 g / qm, applied. The order can be on everyone known Coating system, preferably done with an air brush. The required coating viscosity can be adjusted by adding tap water for dilution and for thickening the ammonium salt of polymeric acrylic acid or polyvinyl alcohol or carboxymethyl cellulose be used.
Die Aushärtung der Polyurethanschicht erfolgt in einem Trockenkanal bei 70 bis 1100C, vorzugsweise bei 1000C. Nach der Trocknung wird die Bahn auf Raumtemperatur gekühlt und aufgewickelt. Das Aufwickeln kann entfallen, wenn die Bahn gleich weiterverarbeitet wird.The polyurethane layer is cured in a drying tunnel at 70 to 1100C, preferably at 1000C. After drying, the web is at room temperature chilled and wound up. Winding up can be omitted if the web is processed further straight away will.
In der zweiten Stufe erfolgt die Siliconisierung des Trennpapiers. Dabei wird auf die Polyurethanschicht eine Siliconschicht in an sich bekannter Weise aufgebracht. Für die Siliconschicht kann eine Lösung oder eine Emulsion verwendet werden.In the second stage, the release paper is siliconized. A silicone layer is applied to the polyurethane layer in a manner known per se upset. A solution or an emulsion can be used for the silicone layer will.
Vorzugsweise wird jedoch eine aus 80 bis 120 Gewichtsteilen, vorzugsweise 100 Gewichtsteilen, 20%ist Polyorganosiloxanlösung, 500 bis 700 Gewichtsteilen, vorzugsweise 600 Gewichtsteilen, Toluol und 16 bis 23 Gewichtsteilen von drei Härterlösungen (178, 179 und 181) im Verhältnis 1:1:1 bis 1:1:1,3, wobei zuerst Härter 181, dann Härter 17b und als letzter Härter 179 zugegeben worden sind, vorbereitete Lösung in einer Menge von 0,6 bis 1 g/ qm Trockensubstanz aufgetragen. Nach dem Auftrag wird im Trockenkanal bei 105 bis 1300C, vorzugsweise bei 1200C in zwanzig bis sechzig Sekunden die Siliconschicht ausgehärtet, wobei gleichzeitig eine Vernetzung mit der Polyurethanschicht erfolgt.However, preferably, one of 80 to 120 parts by weight is preferred 100 parts by weight, 20% is polyorganosiloxane solution, 500 to 700 parts by weight, preferably 600 parts by weight, toluene and 16 to 23 parts by weight of three hardener solutions (178, 179 and 181) in a ratio of 1: 1: 1 to 1: 1: 1.3, with hardener 181 first, then Hardener 17b and hardener 179 added as the last, prepared solution applied in an amount of 0.6 to 1 g / m² dry substance. After the order is in the drying tunnel at 105 to 1300C, preferably at 1200C in twenty to sixty Seconds the silicone layer cured, with simultaneous crosslinking with the polyurethane layer takes place.
Nach der Ilärtung wird auf Raumtemperatur abgekühlt auf 5 bis 6 % Feuchte rückgefeuchtet und die Bahn aufgewickelt.After curing, it is cooled to room temperature to 5 to 6% Moisture rewetted and the web wound up.
Die derart hergestellte Trennpapierbahn kann sofort in üblicher Weise zum Kaschieren mit Selbstklebeerzeugnissen verwendet werden.The release paper web produced in this way can immediately be used in the usual manner can be used for lamination with self-adhesive products.
Die kaschierten Selbstklebeerzeugnisse bestehen somit lediglich aus zwei Teilen, dem zu beschriftenden selbstklebenden Original und der gleichzeitig als Abdeckung dienenden Kopie. Sie sind daher sehr dünn und können in allen gängigen Schreib- und Druckvorrichtungen bearbeitet werden.The laminated self-adhesive products therefore only consist of two parts, the self-adhesive original to be labeled and the one at the same time as a cover copy. They are therefore very thin and can be used in all common Writing and printing devices are processed.
Anhand der Fig. 1 wird der schematische Aufbau des erfindungsgemäßen Trennpapiers beispielhaft dargestellt und im folgenden erläutert. Das handelsübliche chemische Farbreaktionspapier 1 besteht aus der Papierschicht 2 und der heaktionsschicht 3 mit der einen Chemikalie 4 und der anderen Chemikalie in den kapseln 5. Auf der Reaktionsschicht 3 haftet die Polyurethanschicht 6, die mit der Siliconschicht 7 vernetzt ist. Der Siliconschicht folgt schließlich das Etikett 9 mit der Selbstklebeschicht 8.1 shows the schematic structure of the inventive Release paper shown by way of example and explained below. The usual one chemical color reaction paper 1 consists of the paper layer 2 and the heat layer 3 with one chemical 4 and the other chemical in the capsules 5. On the Reaction layer 3 adheres to the polyurethane layer 6, which is adhered to the silicone layer 7 is networked. The silicone layer is finally followed by the label 9 with the self-adhesive layer 8th.
Die trtlhdung ist nicht auf die Kottibinatlon der auf der Reaktionsschicht haftenden Polyurethanschicht mit der Siliconschicht beschränkt. Vielmehr können auch andere Zwischenschichten aufgebracht werden, die dz huber der Reaktionsschicht des Farbreaktionspapiers geforderten Bedingungen erfüllen und mit der Sillaohschicht vernetzbar sind.The reaction is not due to the Kottibinatlon on the reaction layer adhesive polyurethane layer limited to the silicone layer. Rather, can other intermediate layers can also be applied, which cross over the reaction layer of the color reaction paper meet the required conditions and with the Sillaohschicht are networkable.
Claims (12)