DE19628930C1 - Forming dental crowns and bridges avoiding high temperature stages

Info

Publication number: DE19628930C1
Application number: DE19628930A
Authority: DE
Inventors: Rolf Eykmann; Helmut Grigereit; Dieter Dr Schoedel; Martin Dr Schuster; Wulf Dr Braemer
Original assignee: Heraeus Kulzer GmbH
Current assignee: Ivoclar Vivadent AG
Priority date: 1996-07-18
Filing date: 1996-07-18
Publication date: 1997-10-09
Anticipated expiration: 2016-07-19
Also published as: WO1998003128A1

Abstract

The invention concerns a method of producing a dental prosthesis part, according to which method the dental prosthesis part is modelled onto a tooth stump (8) or unit die, the exterior of a crown core (2) being at least partially veneered with a synthetic dental material or dental ceramic (4). In order to adapt the dental prosthesis part with high fitting accuracy and low expenditure and avoiding heat treatment for melting or sintering precious metals whilst the dental prosthesis part is being shaped, the crown core, whose internal dimensions are larger than the dimensions of the tooth stump, is filled with a synthetic dental material (5), the filling volume being larger than the volume between the crown core and the tooth stump when the crown core has been placed thereon. The crown core is subsequently pressed onto the tooth stump and the synthetic dental material then sets.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung eines Zahnersatzteiles, bei dem das Zahn ersatzteil auf ein Zahnstumpfmodell aufmodelliert wird, wobei ein Kronenkern an seiner Außenseite mit einem Dentalkunststoff oder einer Dentalkeramik wenigstens teilweise verblen det wird. Die Erfindung betrifft weiterhin einen Kronenkern zur Durchführung des Verfahrens.The invention relates to a method for producing a tooth replacement part, in which the tooth spare part is modeled on a tooth stump model, with a crown core on its Fade the outside at least partially with a dental plastic or a dental ceramic det. The invention further relates to a crown core for performing the method.

Derartige Verfahren sind aus dem Stand der Technik vielfach bekannt. Beispielsweise in DE 87 03 951 ist eine Dentalkappe (Kronenkern) offenbart, die aus einer ebenen und an den Seiten geschlitzten Edelmetallfolie gebildet wird. Die Edelmetallfolie wird eng an das Zahn stumpfmodell angepaßt, so daß es an dessen Flächen anliegt. Anschließend wird eine Ver schmelzung der sich überlappenden Flächen der Edelmetallfolie durchgeführt, um eine ge schlossene Dentalkappe zu erreichen. Diese Dentalkappe wird dann mit Keramik oder Kunst stoff verblendet. Um ein enges Anliegen am Zahnstumpf zu gewährleisten, ist ein sehr genaues Arbeiten erforderlich. Das Verschmelzen der sich bei der Formgebung überlappenden Folientei le zu einer Dentalkrone von gleichmäßiger Dicke erfordert einen hohen Aufwand und setzt eine gewisse Erfahrung des damit befaßten Dentaltechnikers voraus. Die für das Verschmelzen er forderliche Wärme führt in einer großen Zahl der Anwendungsfälle zu einem Verzug der Form, so daß diese dann nicht mehr formschlüssig am Zahnstumpf anliegt.Such methods are widely known from the prior art. For example in DE 87 03 951 discloses a dental cap (crown core) which consists of a flat and an the sides slotted precious metal foil is formed. The precious metal foil gets close to the tooth blunt model adapted so that it rests on its surfaces. Then a ver melting of the overlapping surfaces of the precious metal foil is carried out to form a ge to reach a closed dental cap. This dental cap is then made with ceramic or art fabric veneered. To ensure a close fit to the tooth stump is a very precise one Work required. The fusion of the foil overlapping during the shaping Le to a dental crown of uniform thickness requires a lot of effort and sets one certain experience of the dental technician involved. The one for merging it required heat leads to a distortion of the shape in a large number of applications, so that it no longer fits positively on the tooth stump.

Ein ähnliches Verfahren ist aus der DE 39 11 966 A1 bekannt. Auch aus EP 0 252 412 A2 ist ein derartiges Verfahren bekannt. Hier wird eine Dentalhülse (Kronenkern) als Manschette um ei nen Stumpf gelegt und die Mantelfläche durch Punktschweißen der Enden der Folie geschlossen. Das Punktschweißen hat eine lokale und damit einseitige Erwärmung der Dental hülse zur Folge, was in der Regel zu einem Wärmeverzug führt. Aus EP 0 442 150 A2 ist eben falls die Verwendung von Metallfolien als Trägermaterial für die Zahnrestauration bekannt.A similar method is known from DE 39 11 966 A1. From EP 0 252 412 A2 is also a known method. Here is a dental sleeve (crown core) as a sleeve around an egg and the outer surface by spot welding the ends of the film closed. Spot welding has local and therefore one-sided heating of the dental sleeve, which usually leads to heat distortion. From EP 0 442 150 A2 is flat if the use of metal foils as a carrier material for tooth restoration is known.

Ein weiteres Verfahren zur Herstellung von Zahnersatzteilen mittels metallischer Dentalkappen (Kronenkern) ist das sogenannte Heratec-Verfahren, bei dem eine Sintertechnik zur Herstel lung der Dentalkappe angewendet wird. Dabei wird auf einen feuerfesten Metallstumpf Edelme tallpaste schichtweise aufgetragen und dann gesintert. Die Kappe wird anschließend mit Kera mik oder Dentalkunststoff verblendet. Das Verfahren stellt ebenfalls besondere Anforderungen an den Modellstumpf (Feuerfestigkeit). Es führt zu stabilen Zahnkronen, erfordert jedoch einen recht hohen, durch die Auftragtechnik bedingten Aufwand.Another process for the production of dental prosthetic items using metallic dental caps (Crown core) is the so-called Heratec process, in which a sintering technique for the manufacture the dental cap is applied. Edelme is placed on a fire-resistant stump Tallpaste applied in layers and then sintered. The cap is then covered with Kera veneered with mic or dental plastic. The process also has special requirements to the model stump (fire resistance). It leads to stable tooth crowns, but requires one quite a lot of effort due to the application technology.

Ausgehend von dem bekannten Stand der Technik ist es Aufgabe der Erfindung, ein Verfahren zur Herstellung eines Zahnersatzteiles anzugeben, bei dem eine hohe Paßgenauigkeit des Zahnersatzteiles mit geringem Aufwand erzielbar ist und bei dem auf eine Temperaturbehand lung zum Schmelzen oder Sintern von Edelmetallen während der Formgebung des Zahnersatz teiles verzichtet werden kann. Aufgabe ist es weiterhin, einen zur Durchführung des Verfahrens geeigneten Kronenkern anzugeben.Starting from the known prior art, the object of the invention is a method specify for the manufacture of a dental prosthetic item in which a high accuracy of fit Dental prosthesis part can be achieved with little effort and in the case of a heat treatment for melting or sintering precious metals during the shaping of the denture part can be dispensed with. The task is still to carry out the procedure specify suitable crown core.

Erfindungsgemäß wird die Aufgabe für das Verfahren dadurch gelöst, daß ein Kronenkern, des sen Innenmaße größer sind als die Abmessungen des Zahnstumpfmodelles mit einem Dental kunststoff gefüllt wird, wobei das Füllvolumen größer ist als das Volumen zwischen Kronenkern und Zahnstumpfmodell nach dem Aufsetzen des Kronenkernes auf das Zahnstumpfmodell, daß danach der Kronenkern auf das Zahnstumpfmodell aufgepreßt und daß anschließend der Den talkunststoff ausgehärtet wird. Mit dem Verfahren ist die Herstellung von Kronen und Brücken möglich. Die Anpassung an den Zahnstumpf erfolgt bei diesem Verfahren nicht durch eine ex akte Formgebung des Kronenkernes, sondern durch den in dem Kronenkern befindlichen Kunststoff.According to the invention the object for the method is achieved in that a crown core, the Internal dimensions are larger than the dimensions of the tooth stump model with a dental plastic is filled, the filling volume is greater than the volume between the crown core and tooth stump model after placing the crown core on the tooth stump model that then the crown core is pressed onto the tooth stump model and then the den talc plastic is cured. With the process is the manufacture of crowns and bridges possible. The adaptation to the tooth stump is not carried out by an ex Actual shape of the crown core, but by the one in the crown core Plastic.

Dadurch ist es möglich, konfektionierte Kronenkerne einzusetzen. Derartige Kronen kerne können beispielsweise durch Tiefziehverfahren leicht hergestellt und in unterschiedlichen Größen zur Verfügung gestellt werden, so daß der Zahntechniker einen vorgefertigten Kronen kern entsprechend den Abmessungen des Zahnstumpfes auswählen kann. Auch die ange strebte Form des Zahnersatzteiles kann bei der Auswahl des Kronenkerns berücksichtigt wer den. Es ist natürlich auch möglich, einen Kronenkern individuell anzufertigen. Da der Kronen kern zweckmäßigerweise aus einer Metallfolie gebildet wird, ist er flexibel und kann bei Bedarf auch vom Zahntechniker verformt werden, um eine gegebenenfalls vorhandene zu große Abweichung von der benötigten Form auszugleichen. Eine exakte Formgebung der Innenseite des Zahnersatzteiles, die ein exaktes Anliegen an dem Zahnstumpf garantiert, erfolgt durch ei nen Dentalkunststoff, der lediglich in einer solchen Menge in den Kronenkern gefüllt werden muß, daß er den zwischen dem Kronenkern und dem Zahnstumpfmodell vorhandenen Zwi schenraum ausfüllt. Der überschüssige Kunststoff quillt beim Aufpressen des Kronenkerns auf das Zahnstumpfmodell an der Unterkante des Kronenkerns aus dem Zwischenraum heraus und kann dort entfernt werden. Eine derartige Formgebung ist ohne großen Aufwand und ohne Temperaturbehandlung mit hohen Temperaturen möglich, da der Kunststoff beispielsweise als Paste vorliegt und damit sehr leicht verarbeitet werden kann. Selbstverständlich ist es erfin dungsgemäß auch möglich, den Kronenkern aus Dentalkunststoff oder Dentalkeramik zu bilden.This makes it possible to use assembled crown cores. Such crowns Cores can be easily manufactured, for example, by deep-drawing processes and in different Sizes are provided so that the dental technician can make a prefabricated crown core can be selected according to the dimensions of the tooth stump. Also the ange The desired shape of the tooth replacement part can be taken into account when choosing the crown core the. Of course, it is also possible to make a crown core individually. Because of the crowns Core is expediently formed from a metal foil, it is flexible and can if necessary can also be deformed by the dental technician to make any existing one too large Compensate for deviation from the required shape. An exact shape of the inside of the tooth replacement part, which guarantees an exact fit on the tooth stump, is done by ei a dental plastic that is only filled in such an amount in the crown core must that he the existing between the crown core and the tooth stump model fills the room. The excess plastic swells when the crown core is pressed on the tooth stump model on the lower edge of the crown core out of the space and can be removed there. Such a shaping is without great effort and without Temperature treatment at high temperatures possible because the plastic, for example, as Paste is present and can therefore be processed very easily. Of course it is invented according to the invention also possible to the crown core made of dental plastic or dental ceramic form.

Zweckmäßigerweise wird der Kronenkern vor dem Aufbringen des Dentalkunststoffes an seiner Oberfläche mit einem Haftvermittler versehen, insbesondere durch Acrylierung, Silikatisierung oder Silanisierung. Dadurch wird ein fester Kontakt zwischen Kronenkern und dem Dental kunststoff bzw. der Dentalkeramik gewährleistet.The crown core is expediently attached to it before the dental plastic is applied Provide the surface with an adhesion promoter, in particular through acrylation, silicatization or silanization. This creates a firm contact between the crown core and the dental plastic or dental ceramics guaranteed.

Zweckmäßig kann es sein, vor dem Aufpressen des Kronenkerns auf das Zahnstumpfmodell auf dieses einen Dentalkunststoff aufzubringen, um beispielsweise die Festigkeit des entste henden Verbundes zu erhöhen oder die weitere Bearbeitung bei einer Vollverblendung des Kro nenkerns zu erleichtern. Dieser auf das Zahnstumpfmodell aufgebrachte Dentalkunststoff kann vor dem Aufpressen gehärtet oder weich gelassen werden.It may be advisable to press the crown core onto the tooth stump model to apply a dental plastic to this, for example to ensure the strength of the first existing composite or further processing if the crown is fully veneered to facilitate core. This dental plastic applied to the tooth stump model can be hardened or left soft before pressing.

Vorteilhafterweise wird das Zahnstumpfmodell vor dem Aufpressen des Kronenkerns mit einem Isoliermittel behandelt, um das Abnehmen des Zahnersatzteiles zu erleichtern.Advantageously, the tooth stump model is pre-pressed with a Insulating agent treated to make it easier to remove the denture part.

Es ist zweckmäßig, zur Füllung des Kronenkerns einen chemisch härtenden, lichthärtenden oder heißhärtenden Dentalkunststoff zu verwenden. Als sinnvoll hat es sich erwiesen, daß der Kronenkern an seiner Außenseite vollständig verblendet wird. Dies ist nicht nur mit den übli chen Dentalkeramiken, sondern auch mit beispielsweise unter den Bezeichnungen Charisma und Artglass bekannten Dentalkunststoffen möglich.It is useful to fill the crown core with a chemically curing, light-curing or thermosetting dental plastic. It has proven useful that the Crown core is completely veneered on its outside. This is not only with the übli dental ceramics, but also with, for example, Charisma and Artglass known dental plastics possible.

Zweckmäßig ist es, daß zur Füllung und zur Verblendung des Kronenkerns der gleiche Dental kunststoff verwendet wird. Dabei hat es sich als vorteilhaft erwiesen, daß der Kronenkern voll ständig mit dem Dentalkunststoff umgeben wird. Dies ist leicht zu realisieren, da ein Teil des zur Füllung verwendeten Dentalkunststoffes am unteren Rand des Kronenkerns aus diesem austritt und hier leicht mit dem der Verblendung des Kronenkerns dienenden Dentalkunststoff stoffschlüssig verbunden werden kann. Dies hat zum einen den optischen Vorteil, daß das Ma terial (Metall) nach Fertigstellung des Zahnersatzteiles nicht mehr sichtbar ist, zum anderen kommt das Metall mit dem Patienten nicht mehr in Berührung, da es vollständig umschlossen ist. Dies ermöglicht den Einsatz einer breiten Palette auch solcher Metalle, die für den Einsatz im direkten Kontakt mit dem Patienten nicht geeignet sind.It is useful that the same dental for filling and for veneering the crown core plastic is used. It has proven advantageous that the crown core is full is constantly surrounded by the dental plastic. This is easy to do because part of the Dental plastic used for filling at the lower edge of the crown core from this emerges and here easily with the dental plastic used to veneer the crown core can be cohesively connected. On the one hand, this has the optical advantage that the Ma material (metal) is no longer visible after completion of the denture part, on the other the metal no longer comes into contact with the patient because it is completely enclosed is. This enables the use of a wide range of such metals that are suitable for use are not suitable in direct contact with the patient.

Zur Anfertigung größerer Zahnersatzteile (Brücken) können mehrere Kronenkerne miteinander verbunden werden. Es ist möglich, zwei Kronenkerne unmittelbar miteinander zu verbinden, (z. B. schweißen, kleben, laserschweißen, chemisch verbinden) um zwei nebeneinander liegen de Zähne zu formen. Es ist auch möglich, zwei Kronenkerne durch ein Verbindungsteil, bei spielsweise einen Steg miteinander zu verbinden, um einen fehlenden Zahn (Pontic) zu über brücken. Auf das Verbindungsteil kann ein Zahn aus Dentalkunststoff oder Dentalkeramik auf modelliert werden, um die Lücke zu schließen. Zur Fertigung solcher größerer Zahnersatzteile kann das Metall des Kronenkerns sehr leicht in die notwendige Form gebracht werden. Eine Verbindung mehrerer Kronenkerne durch Schweißen ist vor dem Aufsetzen auf das Zahn stumpfmodell möglich, so daß sich ein hitzebedingter Verzug des Metalles nicht auf die Form des fertigen Zahnersatzteiles auswirkt, da die endgültige Formgebung durch den verwendeten Dentalkunststoff erfolgt. Als Verblendmaterial kann neben den obengenannten Dentalkunststof fen jeder andere geeignete Dentalkunststoff verwendet werden. Insbesondere können auch lichthärtende Kunststoffe verwendet werden. Mit dem erfindungsgemäßen Verfahren wird die Schrumpfung des Kunststoffes sehr gering gehalten und eine hohe Paßgenauigkeit gesichert.Several crown cores can be used to make larger dental prostheses (bridges) get connected. It is possible to connect two crown cores directly together, (e.g. welding, gluing, laser welding, chemical bonding) lie next to each other by two to shape teeth. It is also possible to connect two crown cores through a connecting part for example, to connect a bar to each other to cover a missing tooth (pontic) bridges. A tooth made of dental plastic or dental ceramic can be placed on the connecting part be modeled to fill the gap. For the production of such larger dentures the metal of the crown core can be shaped very easily. A Connection of several crown cores by welding is before placing on the tooth butt model possible, so that a heat-related distortion of the metal does not affect the shape of the finished dental prosthetic item, since the final shape is influenced by the one used Dental plastic is done. As a veneering material, in addition to the dental plastic mentioned above any other suitable dental plastic can be used. In particular, too light-curing plastics are used. With the method according to the invention Shrinkage of the plastic kept very low and a high accuracy of fit ensured.

Die Aufgabe wird für einen Kronenkern dadurch gelöst, daß seine Innenmaße größer sind als die entsprechenden Abmessungen des Zahnstumpfes und/oder des Zahnstumpfmodelles, auf den bzw. auf das der Kronenkern aufgesetzt werden soll. Dabei ist unter größeren Abmessun gen zu verstehen, daß der entstehende Zwischenraum zwischen Kronenkappe und Zahnstumpf bzw. Zahnstumpfmodell ausreicht, um Dentalkunststoff in nennenswerter Menge aufzunehmen. Der Zwischenraum sollte also im Durchschnitt mindestens einige Zehntel Millimeter betragen.The task is solved for a crown core in that its internal dimensions are larger than the corresponding dimensions of the tooth stump and / or the tooth stump model the or on which the crown core is to be placed. It is under larger dimensions gene to understand that the resulting space between crown cap and tooth stump or tooth stump model is sufficient to accommodate dental plastic in significant quantities. The gap should therefore be at least a few tenths of a millimeter on average.

Im folgenden wird die Erfindung anhand eines Ausführungsbeispieles mit einer Zeichnung nä her erläutert. In der Zeichnung zeigtIn the following the invention based on an embodiment with a drawing ago explained. In the drawing shows

Fig. 1 einen Zahn mit Krone nach dem Stand der Technik und Fig. 1 shows a tooth with crown according to the prior art and

Fig. 2 einen Zahn mit erfindungsgemäßem Kronenkern. Fig. 2 shows a tooth with a crown core according to the invention.

Bei bisher bekannten Verfahren wird auf einen Zahnstumpf 1 eine auf einem Zahnstumpfmodell paßgenau angefertigte Metallkappe als Kronenkern 2 mittels eines Zementes 3 befestigt. Der Zement 3 ist üblicherweise ein Phosphatzement. Der Kronenkern 2 ist an seiner Außenseite mit Dentalkunststoff oder Dentalkeramik als Verblendmaterial 4 umgeben. Aus dem Verblendmate rial 4 ist die gewünschte Zahnform gebildet.In previously known methods, a metal cap, which is made to fit precisely on a tooth stump model, is attached to a tooth stump 1 as a crown core 2 by means of a cement 3 . The cement 3 is usually a phosphate cement. The crown core 2 is surrounded on the outside with dental plastic or dental ceramic as veneer material 4 . From the Verblendmate rial 4 , the desired tooth shape is formed.

Ein im Tiefziehverfahren hergestellter Kronenkern 2 aus einer Edelmetallfolie oder aus Dental kunststoffen wird an seiner Innenseite und an seiner Außenseite konditioniert, beispielsweise durch Silikatisierung. Die Silikatisierung wirkt als Haftvermittler zwischen dem Metall und einem auf den Kronenkern aufzubringenden Dentalkunststoff. Eine andere Methode ist die Aktivierung der Kunststoffoberfläche mittels entsprechenden Chemikalien (z. B. bekannt aus DE 42 33 886 A1. Auf den Haftvermittler kann eine Schicht eines Opakers aufgebracht werden, bevor das Verblendmaterial 4 aufgetragen wird. Beide Schichten sind sehr dünn und deshalb in der Zeichnung nicht dargestellt. Die Größe des Kronenkerns 2 wurde so ausgewählt, daß sein Innenraum etwas größer (etwa 0,2-1 mm im Durchschnitt) ist als der Zahnstumpf 1, auf den das fertige Zahnersatzteil aufzusetzen ist (Fig. 2) bzw. als das entsprechende Zahnstumpfmo dell, das aus einem Dentalgips angefertigt wurde. Anstelle von Metall kann als Material des Kronenkerns 2 auch Dentalkunststoff oder Dentalkeramik verwendet werden.A crown core 2 produced in a deep-drawing process from a noble metal foil or from dental plastics is conditioned on its inside and on its outside, for example by silicating. The silication acts as an adhesion promoter between the metal and a dental plastic to be applied to the crown core. Another method is the activation of the plastic surface by means of appropriate chemicals (eg known from DE 42 33 886 A1. A layer of an opaque can be applied to the adhesion promoter before the veneering material 4 is applied. Both layers are very thin and therefore in The size of the crown core 2 was selected so that its interior is somewhat larger (approximately 0.2-1 mm on average) than the tooth stump 1 on which the finished tooth replacement part is to be placed ( FIG. 2) or as the corresponding tooth stump model, which was made from a dental plaster. Instead of metal, dental plastic or dental ceramic can also be used as the material of the crown core 2 .

In den Innenraum des Kronenkerns 2 wird ein pastöser, chemisch härtender (kaltpolymerisie render) oder lichthärtender Dentalkunststoff 5, wie er beispielsweise unter der Bezeichnung "Artglass" oder aus DE 44 46 033 A1 bekannt ist, gefüllt. Anschließend wird der gefüllte Kro nenkern 2 nach vorheriger Behandlung des Zahnstumpfmodelles mit einem üblichen Isolier- und Trennmittel auf dieses Zahnstumpfmodell aufgepreßt. Dabei entweicht aus dem Spalt 6 an der Unterseite des Kronenkerns 2 der überschüssige Kunststoff. Der in dem Zwischenraum zwischen dem Zahnstumpfmodell und dem Kronenkern 2 verbleibende Dentalkunststoff 5 ent spricht in seinen Konturen nach seiner Aushärtung exakt den Konturen des Zahnstumpfes 1, auf den das fertige Zahnersatzteil aufzusetzen ist.In the interior of the crown core 2 , a pasty, chemically curing (cold polymerizing render) or light-curing dental plastic 5 , as known for example under the name "Artglass" or from DE 44 46 033 A1, is filled. Subsequently, the filled kernel core 2 is pressed onto this tooth stump model after prior treatment of the tooth stump model with a conventional insulating and separating agent. The excess plastic escapes from the gap 6 on the underside of the crown core 2 . The remaining in the space between the tooth stump model and the crown core 2 dental plastic 5 speaks ent in its contours after its curing exactly the contours of the tooth stump 1 , on which the finished dental prosthesis is to be placed.

Vor dem Aufpressen des gefüllten Kronenkerns 2 auf das Zahnstumpfmodell kann dieses auch mit einer Schicht des Dentalkunststoffes 5 versehen sein. Diese Schicht kann entweder vor dem Aufpressen ausgehärtet oder auch weichgelassen werden. Sie verbindet sich beim bzw. nach dem Aufpressen des gefüllten Kronenkerns 2 mit dem darin befindlichen Kunststoff zu ei ner einheitlichen Schicht. Before the filled crown core 2 is pressed onto the tooth stump model, this can also be provided with a layer of the dental plastic 5 . This layer can either be hardened before pressing or left soft. It connects during or after pressing the filled crown core 2 with the plastic therein to egg ner uniform layer.

Nach Aufpressen des gefüllten Kronenkerns 2 auf das Zahnstumpfmodell wird der Kronenkern 2 auch an seiner äußeren Oberfläche verblendet, wobei die gewünschte Zahnform modelliert wird. Als Verblendmaterial 4 wird ein geeigneter Dentalkunststoff, beispielsweise das unter der Bezeichnung "Artglass" bekannte Material verwendet. Der Kronenkern 2 wird mit dem Kunst stoff derart verblendet, daß die Verblendung 4 bis über den unteren Rand des Kronenkerns 2 hinaus geführt wird, wo sich das Verblendmaterial 4 mit dem während des Aufpressens des Kronenkerns 2 auf das Zahnstumpfmodell aus dem entstehenden Spalt 6 herausquellenden Dentalkunststoff 5 verbindet.After the filled crown core 2 has been pressed onto the tooth stump model, the crown core 2 is also veneered on its outer surface, the desired tooth shape being modeled. A suitable dental plastic, for example the material known under the name "Artglass", is used as the veneering material 4 . The crown core 2 is veneered with the plastic in such a way that the veneer 4 is guided to beyond the lower edge of the crown core 2 , where the veneer material 4 with the dental plastic swelling out of the resulting gap 6 during the pressing on of the crown core 2 onto the tooth stump model 5 connects.

Ein Haftvermittler kann auch nach dem aus DE 44 41 123 A1 bekannten Verfahren (Acrylieren der Oberfläche) auf die Dentalkappe aufgebracht werden, oder durch Silikatisieren.An adhesion promoter can also by the process known from DE 44 41 123 A1 (acrylic Surface) can be applied to the dental cap, or by silicating.

Zur Verblendung ist eine Vielzahl weiterer Dentalmaterialien geeignet, wie sie beispielsweise auch aus EP 0 486 775 A1 bekannt sind. Das fertige Zahnersatzteil wird adhäsiv mit einem Kronen zement 3 auf den Zahnstumpf 1 geklebt.A large number of other dental materials are suitable for veneering, as are also known, for example, from EP 0 486 775 A1. The finished tooth replacement part is adhesively bonded to the tooth stump 1 with a crown cement 3 .

Claims

1. A method for producing a dental prosthetic item, in which the dental prosthetic item is modeled on a tooth stump model, a crown core being at least partially veneered on the outside with a dental plastic or a dental ceramic, characterized in that the crown core ( 2 ), the internal dimensions of which are larger are the dimensions of the tooth stump model, filled with a dental plastic ( 5 ), where the filling volume is greater than the volume between the crown core ( 2 ) and the tooth stump model after the crown core ( 2 ) has been placed on the tooth stump model so that the crown core ( 2 ) pressed onto the tooth stump model and that the dental plastic ( 5 ) is then cured.

2. The method according to claim 1, characterized in that the crown core ( 2 ) is formed from a metal foil.

3. The method according to claim 1, characterized in that the crown core ( 2 ) is formed from Kera mic or plastic.

4. The method according to claim 1, characterized in that the crown core ( 2 ) on its surface before application of the dental plastic ( 5 ) is provided with an adhesion promoter.

5. The method according to claim 4, characterized in that the surface of the crown core nes is acrylated, silicated or silanized.

6. The method according to any one of claims 1 to 5, characterized in that a dental plastic is placed on the tooth stump model before pressing on the crown core ( 2 ).

7. The method according to any one of claims 1 to 6, characterized in that the tooth stump model is treated with an insulating agent before pressing the crown core ( 2 ).

8. The method according to any one of claims 1 to 7, characterized in that a chemical, light-curing or heat-curing dental plastic ( 5 ) is used for filling the crown core ( 2 ).

9. The method according to any one of claims 1 to 8, characterized in that the crown core ( 2 ) is completely blended on the outside with dental plastic or dental ceramic.

10. The method according to any one of claims 1 to 9, characterized in that the same dental plastic is used for filling and for veneering ( 4 ) of the crown core ( 2 ).

11. The method according to any one of claims 1 to 10, characterized in that the crown core ( 2 ) is completely surrounded by a dental plastic or dental ceramic ( 4 ; 5 ).

12. The method according to any one of claims 1 to 11, characterized in that a plurality of crown cores ( 2 ) are connected to one another.

13. The method according to claim 12, characterized in that two crown cores ( 2 ) are immediately connected to one another.

14. The method according to claim 12, characterized in that two crown cores ( 2 ) are connected to one another by a connecting part.

15. The method according to claim 14, characterized in that on the connecting part Tooth is modeled from dental plastic or dental ceramic.

16. The method according to claim 14 or 15, characterized in that the connecting part is designed as a web.

17. Crown core for performing the method according to one of the preceding Ansprü surface, suitable for placement on a tooth stump, characterized in that its internal dimensions are larger than the dimensions of the tooth stump ( 1 ) and / or the tooth stump ( 1 ) corresponding tooth stump model.

18. Crown core according to claim 17, characterized in that it is made of metal, dental Plastic or dental ceramic is made.