DE102008060372A1 - Method for producing a silicon carbide-epitaxial layer on a single crystalline silicon carbide substrate by chemical gas phase deposition - Google Patents
Method for producing a silicon carbide-epitaxial layer on a single crystalline silicon carbide substrate by chemical gas phase deposition Download PDFInfo
- Publication number
- DE102008060372A1 DE102008060372A1 DE102008060372A DE102008060372A DE102008060372A1 DE 102008060372 A1 DE102008060372 A1 DE 102008060372A1 DE 102008060372 A DE102008060372 A DE 102008060372A DE 102008060372 A DE102008060372 A DE 102008060372A DE 102008060372 A1 DE102008060372 A1 DE 102008060372A1
- Authority
- DE
- Germany
- Prior art keywords
- silicon carbide
- epitaxial layer
- carbide epitaxial
- deposition
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die vorliegende Erfindung bezieht sich auf ein Verfahren zur Herstellung einer Siliziumkarbid-Epitaxieschicht auf einem Siliziumkarbid-Substrat und auf ein Siliziumkarbid-Bauelement mit einer Siliziumkarbid-Epitaxieschicht, die eine geringe Basalflächenversetzungsdichte aufweist.The The present invention relates to a method of manufacture a silicon carbide epitaxial layer on a silicon carbide substrate and to a silicon carbide device having a silicon carbide epitaxial layer, which has a low basal area dislocation density.
Die herausragenden Materialeigenschaften von Siliziumkarbid, wie z. B. sein großer Bandabstand ermöglicht es in Siliziumkarbid (SiC)-Bauelementen deutlich höhere Betriebstemperaturen als in Bauelementen aus konventionellen Halbleitern zu erzielen. Die Verlustwärme eines SiC-Bauelementes kann wegen der hohen Wärmeleitfähigkeit von SiC besser als in Bauelementen aus konventionellen Halbleitern abgeführt werden. Durch den größeren Bandabstand lassen sich außerdem wesentlich höhere Sperrspannungen als bei konventionellen Halbleiterbauelementen erzielen. Aus diesem Grunde ist Siliziumkarbid beispielsweise für Leistungshalbleiter und Hochtemperaturelektronikbauelemente ein viel versprechendes Herstellungsmaterial.The outstanding material properties of silicon carbide, such. B. its large band gap allows it in silicon carbide (SiC) devices significantly higher operating temperatures to achieve as in components of conventional semiconductors. The heat loss of a SiC device can because of high thermal conductivity of SiC better than in Components removed from conventional semiconductors become. Leave by the larger band gap In addition, much higher blocking voltages as achieved with conventional semiconductor devices. For this Silicon carbide is basically used, for example, for power semiconductors and High temperature electronics components a promising manufacturing material.
Zur Fertigung von Siliziumkarbid-Bauelementen, wie z. B. von PiN-Dioden aus Siliziumkarbid (SiC), werden n- und p-leitende Epitaxieschichten benötigt, welche eine möglichst geringe Zahl von Kristallfehlern aufweisen sollten.to Production of silicon carbide components, such. B. of PiN diodes silicon carbide (SiC), n- and p-type epitaxial layers are required, which is the lowest possible number of crystal defects should have.
Solche Siliziumkarbid-Dioden, die z. B. in Hochspannungsanwendungen eingesetzt werden, können für Sperrspannungen (VBr) von mehr als 3 kV ausgelegt sein. Im Betriebsfall können in solchen Dioden Strombelastungen von mehreren 100 A/cm2 auftreten. Die elektrische Charakterisierung solcher Siliziumkarbid-Dioden kann ergeben, dass nach einer Strombelastung mit 100 A/cm2 für eine Dauer von 30 Minuten einige dieser Dioden ein instabiles Stromspannungsverhalten in den Vorwärtskennlinien aufweisen (VF-Drift). Andere Dioden, die auf demselben Siliziumkarbid-Substrat aufgebaut sind, können dieses instabile Verhalten hingegen nicht aufweisen. Ursache für dieses instabile Stromspannungsverhalten können spezielle Defekte in dem Siliziumkarbid-Substrat und die Fortpflanzung dieser Defekte in die Epitaxieschicht des Siliziumkarbid-Bauelements sein; sowie die Entstehung von neuen Defekten während des Abscheidens der Siliziumkarbid-Epitaxieschicht.Such silicon carbide diodes z. B. used in high voltage applications, can be designed for reverse voltages (V Br ) of more than 3 kV. During operation, current loads of several 100 A / cm 2 may occur in such diodes. The electrical characterization of such silicon carbide diodes can show that after a current load of 100 A / cm 2 for a period of 30 minutes some of these diodes have an unstable current-voltage behavior in the forward characteristic curves (V F drift). On the other hand, other diodes built on the same silicon carbide substrate can not exhibit this unstable behavior. The cause of this unstable current-voltage behavior may be specific defects in the silicon carbide substrate and the propagation of these defects into the epitaxial layer of the silicon carbide device; and the emergence of new defects during the deposition of the silicon carbide epitaxial layer.
Ein Beispiel für das komplexe Zusammenwirken zwischen Kristalldefekten und der Zuverlässigkeit der Siliziumkarbid-Bauelemente sind sogenannte Basalflächenversetzungen (Basal Plane Dislocations – BPD). Es ist bekannt, dass diese Versetzungen die Langzeitstabilität von (bipolaren) Bauelementen wesentlich beeinflussen können. Die Basalflächenversetzungen können bereits bei der Herstellung des Grundmaterials während der Kristallzüchtung entstehen. Typischerweise besitzt ein Wafer aus Silizium-Karbid eine Basalflächenversetzungsdichte in der Größenordnung von ca. 10000 cm–2. Während des Betriebs des Bauelementes kann sich dieser Kristalldefekttyp, also die Basalflächenversetzung in einen neuen, in seinen elektrischen Eigenschaften wesentlich kritischeren Defekt, umwandeln. Bei diesem neuen Defekttyp kann es sich um einen Stapelfehler handeln, der dann zu einer Degradation des Bauelementes unter Strombelastung führen kann. Dadurch können beispielsweise die oben erwähnten Instabilitäten der Siliziumkarbid-Bauelemente verursacht werden.An example of the complex interaction between crystal defects and the reliability of silicon carbide devices is so-called basal plane dislocations (BPD). It is known that these dislocations can significantly affect the long-term stability of (bipolar) devices. The basal surface dislocations may already arise during the production of the base material during crystal growth. Typically, a silicon carbide wafer has a basal plane dislocation density on the order of about 10,000 cm -2 . During operation of the component, this type of crystal defect, ie the basal plane displacement, can be converted into a new defect, which is much more critical in terms of its electrical properties. This new type of defect can be a stacking fault, which can then lead to a degradation of the component under current load. As a result, for example, the above-mentioned instabilities of the silicon carbide devices can be caused.
In
dem US-Patent
Um eine Markteinführung von (bipolaren) Siliziumkarbid-Bauelementen zu erleichtern ist es aber wünschenswert, Siliziumkarbid-Epitaxieschichten mit einer geringen Basalflächenversetzungsdichte, kostengünstig, mit geringem Zeitaufwand und in möglichst wenig Prozessschritten herzustellen.Around a market introduction of (bipolar) silicon carbide devices however, it is desirable to facilitate silicon carbide epitaxial layers with a low basal area dislocation density, inexpensive, with little time and in as few process steps manufacture.
Die Aufgabe der vorliegenden Erfindung besteht darin, ein Verfahren zur Herstellung einer Siliziumkarbid-Epitaxieschicht auf einem Siliziumkarbid-Substrat mit einer geringen Basalflächenversetzungsdichte zu schaffen und darauf aufbauend Siliziumkarbid-Bauelemente zu schaffen, die sowohl ein stabiles Betriebsverhalten aufweisen als auch sehr kostengünstig, relativ einfach und mit einer geringen Anzahl von Prozessschritten realisierbar sind.The object of the present invention is to provide a method for producing a silicon carbide epitaxial layer on a silicon carbide substrate having a small basal area To create density and building on it to create silicon carbide devices that both have a stable performance and also very inexpensive, relatively simple and can be implemented with a small number of process steps.
Diese Aufgabe wird durch das Verfahren gemäß Anspruch 1 und 12, sowie dem Siliziumkarbid-Bauelement gemäß Anspruch 19 gelöst.These The object is achieved by the method according to claim 1 and 12, and the silicon carbide component according to claim 19 solved.
Die
Erkenntnis der vorliegenden Erfindung besteht darin, dass durch
die Kombination der Verwendung eines Siliziumkarbid-Subtrates mit
einer Fehlorientierung der (0001)- oder der (000
In
Ausführungsbeispielen ist ein Verfahren zur Herstellung
einer Siliziumkarbid-Epitaxieschicht auf einem Siliziumkarbid-Substrat
gezeigt. Das Verfahren umfasst ein Bereitstellen eines Siliziumkarbid-Substrates
mit einer Fehlorientierung der (0001)- oder der (000
Ferner weist das Verfahren ein Abscheiden einer Siliziumkarbid-Epitaxieschicht aus der Gasphase mit einem Kohlenstoff/Siliziumverhältnis von 0,6 bis 1 und einer Wachstumsrate von 5 μm/h bis 30 μm/h auf.Further the method comprises depositing a silicon carbide epitaxial layer from the gas phase with a carbon / silicon ratio from 0.6 to 1 and a growth rate of 5 μm / h to 30 μm / h on.
Die vorliegende Erfindung umfasst ferner ein Verfahren zur Herstellung eines Siliziumkarbid-Bauelementes auf einem einkristallinen Siliziumkarbid-Substrat durch Bereitstellen eines einkristallinen Siliziumkarbid-Substrates mit einer Fehlorientierung von 2° bis 6° und dem Abscheiden zweier unterschiedlich leitender Siliziumkarbid-Epitaxieschichten aus der Gasphase mit einem Kohlenstoff/Siliziumverhältnis von 0,6 bis 1 und einer Wachstumsrate von 5 μm/h bis 30 μm/h, so dass eine PN-Übergangszone zwischen den beiden unterschiedlich leitenden Siliziumkarbid-Epitaxieschichten ausgebildet wird.The The present invention further includes a method of preparation a silicon carbide device on a single crystal silicon carbide substrate by providing a monocrystalline silicon carbide substrate with a misalignment of 2 ° to 6 ° and the Depositing two different conductive silicon carbide epitaxial layers the gas phase with a carbon / silicon ratio of 0.6 to 1 and a growth rate of 5 μm / h to 30 μm / h, so that a PN junction between the two is different conductive silicon carbide epitaxial layers is formed.
Die Erfindung schafft zudem ein Siliziumkarbid-Bauelement mit einer Siliziumkarbid-Epitaxieschicht, welche eine Ba salflächenversetzungsdichte kleiner 10 cm–2 aufweist. Die Siliziumkarbid-Epitaxieschicht ist auf einem einkristallinen Siliziumkarbid-Substrat angeordnet, welches eine Fehlorientierung der Oberfläche des Siliziumkarbid-Substrates von 2° bis 6° aufweist.The invention also provides a silicon carbide component with a silicon carbide epitaxial layer, which has a Ba salflächenversetzungsdichte smaller 10 cm -2 . The silicon carbide epitaxial layer is disposed on a single crystal silicon carbide substrate having a misorientation of the surface of the silicon carbide substrate of 2 ° to 6 °.
Bevorzugte Ausführungsbeispiele werden nachfolgend Bezug nehmend auf die beiliegende Zeichnung näher erläutert.preferred Embodiments will be described below with reference to FIG the accompanying drawing explained in more detail.
Es zeigen:It demonstrate:
Bevor Bezug nehmend auf die Zeichnungen die vorliegende Erfindung anhand von Ausführungsbeispielen näher erläutert wird, wird darauf hingewiesen, dass gleiche Elemente oder ähnliche Elemente in diesen Figuren mit gleichen oder ähnlichen Bezugszeichen versehen sind, und dass eine wiederholte Beschreibung dieser Elemente vermieden wird.Before Referring to the drawings, the present invention with reference of exemplary embodiments explained in more detail It will be noted that the same elements or similar Elements in these figures with the same or similar Reference numerals are provided, and that a repeated description of these elements is avoided.
Die
Oberfläche kann also unter einen Winkel von 2° bis
6° gegenüber der (0001)- oder der (000
Im einem einkristallinen Siliziumkarbid-Kristall wird jedes Atom von 4 Atomen des jeweils anderen Elementes umgeben, so dass eine tetraedrische Struktur entstehen kann. Siliziumkarbid (SiC) weist eine Polytypie auf, d. h. es existiert in verschiedenen Kristallstrukturen. Bei allen bisher bekannten Polytypen von Siliziumkarbid ist jedes Silizium-Atom durch Atombindung mit 4 Kohlenstoff-Atomen verknüpft und umgekehrt.in the A single crystal silicon carbide crystal is used to atomize every atom Surrounded by 4 atoms of each other's element, leaving a tetrahedral structure can arise. Silicon carbide (SiC) has a polytype, i. H. it exists in different crystal structures. At all so far known polytypes of silicon carbide is each silicon atom by atomic bonding linked to 4 carbon atoms and vice versa.
Die sogenannte kubische Phase β-SiC mit einer Schichtfolge ABC – deshalb auch 3C (cubic) genannt – kristallisiert in einer Zinkblende-Struktur. Andere Polytypen des Siliziumkarbid besitzen eine hexagonale oder rhomboedrische Struktur, beispielsweise 15R (rhomboedrisch)-Siliziumkarbid, 21R-Siliziumkarbid etc. Für die Herstellung von Siliziumkarbid-Bauelementen finden häufig die Polytypen 4H (hexagonal)-Siliziumkarbid mit der Schichtenfolge ABCB, 6H (hexagonal)-Siliziumkarbid mit der Schichtenfolge ABCACB, sowie die oben erwähnten 3C- und die 15R-Modifikation Anwendung. Bei der Kristallmodifikation des 4H-Siliziumkarbid wechselt sich die kubische mit der hexagonalen Stapelform ab, und bei der Kristallmodifikation 6H-Siliziumkarbid folgt nach jeweils zwei kubisch gestapelten Schichten eine mit hexagonaler Stapelform. Weitere bekannte Modifikationen des Siliziumkarbids sind beispielsweise 2H, 8H und 9R.The so-called cubic phase β-SiC with a layer sequence ABC - therefore also called 3C (cubic) - crystallized in a zincblende structure. Other polytypes of silicon carbide have a hexagonal or rhombohedral structure, for example 15R (rhombohedral) silicon carbide, 21R silicon carbide, etc. For the production of silicon carbide components are common the polytypes 4H (hexagonal) -Siliziumkarbid with the layer sequence ABCB, 6H (hexagonal) silicon carbide with the layer sequence ABCACB, as well as the above-mentioned 3C and 15R modification application. In the crystal modification of 4H silicon carbide changes the cubic with the hexagonal stack shape, and in the crystal modification 6H silicon carbide follows one after every two cubically stacked layers with hexagonal stack shape. Other known modifications of the Silicon carbides are, for example, 2H, 8H and 9R.
Gemäß einiger
Ausführungsbeispiele der vorliegenden Erfindung kann also
beispielsweise ein 4H-Siliziumkarbid-Substrat oder ein 6H-Siliziumkarbid-Substrat
bereitgestellt werden, wobei das Siliziumkarbid-Substrat eine Fehlorientierung
seiner (0001)- oder der (000
Gemäß einem
Ausführungsbeispiel der vorliegenden Erfindung kann eine
Fehlorientierung beispielsweise 4° gegenüber der <11-20>-Richtung des Siliziumkarbidsubstrates
betragen. Gemäß Ausführungsbeispielen
der vorliegenden Erfindung ist, falls die (0001)-Oberfläche
eingesetzt wird, diese Oberfläche mit Silizium-Atomen terminiert.
Bei Nutzung der Rückseite, also der (000
Basalflächenversetzungen können in der sogenannten c-Ebene des SiC-Kristalls, die durch die Stapelrichtung (c-Achse) gegeben ist, angeordnet sein. Wenn solche Basalflächenversetzungen, die in der Basalebene (c-Ebene) liegen, die Oberfläche eines Siliziumkarbid-Substrates schneiden, so kann an diesen Stellen die Versetzung auf eine anschließende aufwachsende Epitaxieschicht übertragen werden. Dies soll nach Möglichkeit verhindert werden, da wie oben bereits erwähnt, diese Basalflächenversetzungen zu Stapelfehlern führen können und diese bei Strombelastung zu einer Degradation eines Siliziumkarbid-Bauelementes führen können. Neben den Basalflächenversetzungen finden sich in Siliziumkarbid-Einkristallen andere Kristalldefekte wie Stapelfehler, Mikroröhren, Schraubenversetzungen, Polytypeinschlüsse, sowie andere aus der Kristallographie bekannte Kristalldefekte bzw. Störungen.Basalflächenversetzungen can be found in the so-called c-plane of the SiC crystal, which is given by the stacking direction (c-axis), be arranged. If such basal surface dislocations occur in the basal plane (c-plane), the surface of a silicon carbide substrate cut, then at these points the transfer to a subsequent growing epitaxial layer are transmitted. This should be prevented if possible, as above mentions these basal plane dislocations to stacking faults can lead and this at current load too lead to a degradation of a silicon carbide component can. In addition to the Basalflächenversetzungen find In silicon carbide monocrystals, other crystal defects such as Stacking faults, microtubes, screw dislocations, polytype inclusions, as well as other crystal defects known from crystallography or Disorders.
Das
Abscheiden
Die chemische Gasphasenabscheidungs (chemical vapor deposition (CVD))-Technik kann dazu verwendet werden, die Siliziumkarbid-Epitaxieschicht abzuscheiden. Die chemische Gasphasenabscheidung kann dabei in einer CVD-Reaktionskammer durchgeführt werden. Dabei wird an der erhitzten Oberfläche eines Substrates in der Reaktionskammer, also z. B. des Siliziumkarbid-Substrates aufgrund einer chemischen Reaktion aus der Gasphase die epitaktische Siliziumkarbidschicht abgeschieden bzw. aufgewachsen. Beispielsweise können als Ausgangsstoffe bzw. Precursor-Stoffe für die Abscheidung der Siliziumkarbid-Epitaxieschicht chlorhaltige Carbonsilane mit der chemischen Grundformel CnH2n+1SinCl2n+1 verwendet werden.The chemical vapor deposition (CVD) technique can be used to deposit the silicon carbide epitaxial layer. The chemical vapor deposition can be carried out in a CVD reaction chamber. It is at the heated surface of a substrate in the reaction chamber, ie z. B. the silicon carbide substrate due to a chemical reaction from the gas phase, the epitaxial silicon carbide deposited or grown. For example, chlorine-containing carbon silanes with the basic chemical formula C n H 2n + 1 Si n Cl 2n + 1 can be used as starting materials or precursor substances for the deposition of the silicon carbide epitaxial layer.
In Ausführungsbeispielen der vorliegenden Erfindung können beispielsweise auch Propan (C3H8) und Silan (SiH4) als Ausgangsstoffe für das Abscheiden von Siliziumkarbid-Epitaxieschichten mittels CVD-Technik verwendet werden. Allgemein ist auch die Verwendung von Silanen mit der Summemformel SinH2n+2 denkbar. Bei einer für die Epitaxieabscheidung wichtigen Temperatur können sich dann in der CVD-Kammer das Silan und das Propan zersetzen und sich die Siliziumkarbid-Epitaxieschicht auf dem einkristallinen Siliziumkarbid-Substrat ausbilden bzw. abscheiden.For example, in embodiments of the present invention, propane (C 3 H 8 ) and silane (SiH 4 ) may also be used as starting materials for depositing silicon carbide epitaxial layers by CVD technique. In general, the use of silanes with the sum formula Si n H 2n + 2 is conceivable. At a temperature which is important for the epitaxial deposition, the silane and the propane can then decompose in the CVD chamber and the silicon carbide epitaxial layer form or deposit on the monocrystalline silicon carbide substrate.
Die Qualität der Siliziumkarbid-Epitaxieschicht und damit beispielsweise auch die Basalflächenversetzungsdichte hängt neben der genauen Fehlorientierung des Siliziumkarbid-Substrates auch von den genauen Prozessparametern bzw. den Prozessparameterbereichen und den entsprechenden Einstellungen für das Abscheiden der Siliziumkarbid-Epitaxieschicht auf dem Siliziumkarbid-Substrat ab.The Quality of the silicon carbide epitaxial layer and thus, for example the basal area dislocation density also depends the exact misorientation of the silicon carbide substrate also of the exact process parameters or the process parameter ranges and the appropriate settings for the deposition the silicon carbide epitaxial layer on the silicon carbide substrate.
Nach dem erfindungsgemäßen Verfahren kann nun eine sehr geringe Basalflächenversetzungsdichte durch die Verwendung eines Siliziumkarbid-Substrates mit einer Fehlorientierung von 2° bis 6° und durch das Anwenden von optimierten Epitaxieprozessparametern bzw. Prozessparameterbereichen für die epitaktische Schichtabscheidung erreicht werden.According to the inventive method Now, a very low basal plane dislocation density can be achieved by using a silicon carbide substrate with a misalignment of 2 ° to 6 ° and by applying optimized epitaxial process parameters or epitaxial layer deposition process parameter ranges.
Gemäß einiger
Ausführungsbeispiele der vorliegenden Erfindung kann nun
aus der Gasphase die Siliziumkarbid-Epitaxieschicht beispielsweise
mittels CVD-Verfahren mit einem Kohlestoff/Siliziumverhältnis
von 0,6 bis 1, von 0,7 bis 0,8, oder z. B. von 0,75 abgeschieden
werden. Die Wachstumsrate kann dabei 5 μm/h bis 30 μm/h,
6 μm/h bis 10 μm/h, oder z. B. 7 μm/h
betragen. Ausgangsstoffe für die Siliziumkarbid-Epitaxie
können beispielsweise Silan und Propan sein. In Ausführungsbeispielen
der vorliegenden Erfindung kann das Abscheiden
In
einigen Ausführungsbeispielen zum Verfahren zur Herstellung
einer Siliziumkarbid-Epitaxieschicht auf ein Siliziumkarbid-Substrat
kann durch das Bereitstellen
Bei dem erfindungsgemäßen Verfahren kann beispielsweise ein Siliziumkarbid-Substrat verwendet werden, das eine p- oder n-Leitung aufweist und eine dementsprechende Dotierung. Für eine p-Leitung kann das Siliziumkarbid-Substrat bzw. die Siliziumkarbid-Epitaxieschicht die typischen Dotieratome Bor (B), Aluminium (Al) oder Indium (In) aufweisen. Für die n-Leitung kann das Siliziumkarbid, also das Substrat und die Epitaxieschichten beispielsweise mit Phosphor (P), Arsen (As), Antimon (Sb) oder Stickstoff (N) dotiert sein. Denkbar ist natürlich auch die Dotierung mit anderen Atomen oder Ionen, um eine entsprechende p- oder n-Leitung zu erzeugen. Für das Dotieren der Siliziumkarbid-Epitaxieschichten und des Siliziumkarbid-Substrates können die in der Halbleitertechnik gängigen Methoden, wie z. B. Einsatz von gasförmigen Precusoren während der Sublimationszüchtung des Kristalls oder des Epitaxieprozesses, Diffusion, Ionenimplantation eingesetzt werden.at the process of the invention can, for example a silicon carbide substrate can be used which has a p or n line has and a corresponding doping. For one p-type line may be the silicon carbide substrate or the silicon carbide epitaxial layer the typical dopant atoms boron (B), aluminum (Al) or indium (In) exhibit. For the n-line, the silicon carbide, ie the substrate and the epitaxial layers, for example with phosphorus (P), arsenic (As), antimony (Sb) or nitrogen (N). Of course, it is also conceivable doping with other atoms or ions to produce a corresponding p or n line. For doping the silicon carbide epitaxial layers and of the silicon carbide substrate may be those in semiconductor technology common methods, such. B. use of gaseous Precursors during sublimation breeding of the Crystal or the epitaxy process, diffusion, ion implantation be used.
Bei
der Siliziumkarbid-Substratschicht kann es sich um eine n- oder
p-halbleitende bzw. leitfähige Schicht handeln. Das Abscheiden
Gemäß einem
weiteren Ausführungsbeispiel der vorliegenden Erfindung
kann das Abscheiden
In einigen Ausführungsbeispielen der vorliegenden Erfindung ist es nicht nötig den Wafer bzw. das Siliziumkarbid-Substrat in geschmolzenes Kaliumhydroxid zu tauchen. Es braucht auch keine Zwischenepitaxieschicht erzeugt werden, die dann mittels chemisch-mechanischer Polierung (CMP) rückpoliert wird, um eine Oberfläche in sogenannter „epiready”-Qualität zu erzielen.In some embodiments of the present invention it is not necessary the wafer or the silicon carbide substrate to dip into molten potassium hydroxide. It does not need any Zwischenepitaxieschicht be generated, which then by means of chemical-mechanical Polishing (CMP) is polished back to a surface in so-called "epiready" quality too achieve.
In
einigen Ausführungsbeispielen der vorliegenden Erfindung
kann das Bereitstellen
Ferner kann durch die Anpassung der verfügbaren Epitaxieprozessparameter eine erzeugte Siliziumkarbid-Epitaxieschicht, die beispielsweise in einem Siliziumkarbid-Bauelement als aktive Schicht dienen kann, wenige oder keine Basalflächenversetzungen aufweisen. Beispielsweise kann in einem Ausführungsbeispiel das Abscheiden der Siliziumkarbid-Epitaxieschicht bzw. das Abscheiden von Epitaxieschichtfolgen aus Siliziumkarbid so durchgeführt werden, dass das Kohlenstoff/Silizium (C/Si)-Verhältnis in der Gasphase 0,75 beträgt und die Wachstumsrate 7 μm/h. Das Schichtwachstum der Siliziumkarbid-Epitaxieschicht kann beispielsweise bei einer Temperatur von 1600°C und bei einem Druck von 125 hPa bei einem Gasgesamtfluss von 60 l/min durchgeführt werden. Gemäß einiger Ausführungsbeispiele der vorliegenden Erfindung kann dann eine Basalflächenversetzungsdichte von weniger als 3 cm–2 in der Epitaxieschicht erzielt werden. Die Basalflächenversetzungsdichte in der Siliziumkarbid-Epitaxieschicht ist dann vergleichbar oder geringer als die von Substraten, die vor der Epitaxie mit Kaliumhydroxid geätzt wurden und bei denen, nach dem Abscheiden und dem Rückpolieren einer Zwischenschicht, die eigentliche Siliziumkarbid-Epitaxieschicht aufgebracht wurde.Further, by adjusting the available epitaxial process parameters, a generated silicon carbide epitaxial layer, which may serve as an active layer in, for example, a silicon carbide device, may have few or no basal plane dislocations. For example, in one embodiment, the deposition of the silicon carbide epitaxial layer or deposition of silicon carbide epitaxial layer sequences may be performed such that the carbon / silicon (C / Si) ratio in the gas phase is 0.75 and the growth rate is 7 μm / h. The layer growth of the silicon carbide epitaxial layer can be carried out, for example, at a temperature of 1600 ° C. and at a pressure of 125 hPa with a total gas flow of 60 l / min. In accordance with some embodiments of the present invention, a basal plane dislocation density of less than 3 cm -2 can then be achieved in the epitaxial layer. The basal area dislocation density in the silicon carbide epitaxial layer is then comparable to or less than that of substrates etched with potassium hydroxide prior to epitaxial growth and where, after depositing and repolishing an interlayer, the actual silicon carbide epitaxial layer has been deposited.
In
In
einem weiteren Ausführungsbeispiel der vorliegenden Erfindung
kann das Abscheiden
Das
Bereitstellen
Zur
Herstellung eines Siliziumkarbid-Bauelementes, wie z. B. einer PN-Diode,
einer Schottky-Diode, einer PiN-Diode, eines Insulated-Gate-Bipolartransistors
(IGBT) oder eines Feldeffekttransistors (Field Effect Transistor
(FET)), kann es ferner nötig sein, ein Abscheiden
Durch das oben beschriebene Verfahren können sowohl bipolare Siliziumkarbid-Bauelemente als auch unipolare Siliziumkarbid-Bauelemente hergestellt werden. Das Verfahren kann beispielsweise dazu eingesetzt werden, um Siliziumkarbid PiN-Dioden, PN-Dioden, Schottky-Dioden, Insulated Gate Bipolartransistoren (IGBT), Bipolar-Transistoren oder einen (Junction-)Feldeffekttransistor (JFET) herzustellen. Bei den Feldeffekttransistoren kann es sich beispielsweise um einen Metall-Oxid-Halbleiter-Feldeffekttransistor handeln (MOSFET) oder um einen Metall-Halbleiter-Feldeffekttransistor (MESFET). Es kann sich bei dem Siliziumkarbid-Bauelement um ein Leistungsbauelement für Leistungsanwendungen handeln, wie z. B. eine Siliziumkarbid PiN-Diode mit einer Sperrspannung von beispielsweise mehr als 3 kV.By The method described above can be both bipolar Silicon carbide devices as well as unipolar silicon carbide devices getting produced. The method can be used, for example silicon carbide PiN diodes, PN diodes, Schottky diodes, Insulated gate bipolar transistors (IGBT), bipolar transistors or to make a (junction) field effect transistor (JFET). The field effect transistors may be, for example, a Metal oxide semiconductor field effect transistor act (MOSFET) or around a metal-semiconductor field effect transistor (MESFET). It can the silicon carbide device is a power device for power applications, such as B. a silicon carbide PiN diode with a blocking voltage of, for example, more than 3 kV.
Durch den Einsatz von Siliziumkarbid-Epitaxieschichten, die gemäß einiger Ausführungsbeispiele nach den oben beschriebenen Verfahren hergestellt wurden, können z. B. bipolare Siliziumkarbid-Bauelemente kostengünstiger, schneller und mit einer höheren Zuverlässigkeit hergestellt werden. Durch die, durch das obige Verfahren ermöglichte Erzeugung von Siliziumkarbid-Epitaxieschichten mit einer geringen Basalflächenversetzungsdichte kann die Stabilität, beispielsweise der SiC-PiN-Dioden, unter Strombelastung erhöht werden und eine frühzeitige Degradation der Bauelemente verhindert bzw. verzögert werden.By the use of silicon carbide epitaxial layers, which according to some Embodiments according to the methods described above were prepared, z. B. bipolar silicon carbide devices cheaper, faster and with a higher Reliability can be established. By, by the The above method enabled production of silicon carbide epitaxial layers with a low basal plane dislocation density, the Stability, for example, the SiC PiN diodes, under current load be increased and early degradation the components are prevented or delayed.
Das
Abscheiden
Wie
in dem schematischen Querschnitt in
In
Der Anwendungsbereich solcher SiC-Bauelemente kann z. B. im Automotivbereich, in industriellen Anwendungen oder in der Luft- und Raumfahrttechnik liegen. Solche SiC-Bauelemente können für Schalter mit hoher Last eingesetzt werden.Of the Scope of such SiC components can, for. In the automotive sector, in industrial applications or in aerospace engineering lie. Such SiC devices can be used for switches be used with high load.
In Ausführungsbeispielen zu dem Verfahren zur Herstellung einer Siliziumkarbid-Epitaxieschicht auf ein Siliziumkarbid-Substrat bzw. zu dem Verfahren zur Herstellung eines Siliziumkarbid-Bauelementes ist gezeigt, dass durch den Einsatz von beispielsweise 4° fehlorientierten Siliziumkarbid-Substraten und der Abscheidung einer Siliziumkarbid-Epitaxieschicht mit entsprechend optimierten Epitaxie-Prozessparametern auf dem SiC-Substrat mehrere bisher angewandte Technologieschritte, wie z. B. das Ätzen des Siliziumkarbid-Substrates mit Kaliumhydroxid, das anschließende Aufbringen einer Zwischen-Epitaxieschicht und das chemisch-mechanische Polieren, um eine epi-ready-Oberfläche zu erzeugen, entfallen können. Dabei kann eine Basalflächenversetzungsdichte von weniger als 10 cm–2 erzielt werden. Dies kann vorteilhafterweise zu einer erheblichen Kosten- und Zeitersparnis für die Herstellung von Siliziumkarbid-Epitaxieschichten auf einem Siliziumkarbid-Substrat und entsprechenden Siliziumkarbid-Bauelementen führen. Beispielsweise können bei der Fertigung von PiN-Dioden die Herstellungsschritte der externen Vorbehandlung des Wafers (Ätzen), die Epitaxie einer Zwischenschicht und das Rückpo lieren der Epitaxieschicht um eine „epi-ready” Oberfläche zu erhalten, eingespart werden.In exemplary embodiments of the method for producing a silicon carbide epitaxial layer on a silicon carbide substrate or on the method for producing a silicon carbide component, it is shown that the use of, for example, 4 ° misoriented silicon carbide substrates and the deposition of a silicon carbide epitaxial layer According to optimized epitaxy process parameters on the SiC substrate several previously used technology steps, such. Example, the etching of the silicon carbide substrate with potassium hydroxide, the subsequent application of an intermediate epitaxial layer and the chemical mechanical polishing to produce an epi-ready surface can be omitted. In this case, a basal area dislocation density of less than 10 cm -2 can be achieved. This can advantageously lead to considerable cost and time savings for the production of silicon carbide epitaxial layers on a silicon carbide substrate and corresponding silicon carbide components. For example, in the fabrication of PiN diodes, the fabrication steps of external wafer pretreatment (etching), epitaxial growth of an interlayer, and backfilling of the epitaxial layer to provide an "epi-ready" surface can be saved.
Durch die Verwendung von 4° fehlorientierten Siliziumkarbid-Substrat-Wafern kann die Basalflächenversetzungsdichte um zwei Größenordnung reduziert werden, wohingegen dies bei einer Fehlorientierung der Substrate von 8° nur um ca. eine Größenordnung erfolgt. Gemäß einem Ausführungsbeispiel der vorliegenden Erfindung können die Siliziumkarbid-Epitaxie-Prozessparameter zum Aufbringen einer Epitaxieschicht auf dem Siliziumkarbid-Substrat so angepasst werden, dass die erzeugten aktiven Siliziumkarbid-Schichten oder die Schichtfolgen wenige oder keine Basalflächenversetzungen beinhalten. Siliziumkarbid-Bauelemente, welche durch das oben beschriebene Verfahren zur Herstellung von Siliziumkarbid-Epitaxieschichten hergestellt werden, können beispielsweise Basalflächenversetzungsdichten von weniger als 10 cm–2 oder auch weniger als 3 cm–2 aufweisen.By using 4 ° misoriented silicon carbide substrate wafers, the basal plane dislocation density can be reduced by two orders of magnitude, whereas with a misorientation of the substrates of 8 ° this is only about an order of magnitude. According to an embodiment of the present invention, the silicon carbide epitaxial process parameters for depositing an epitaxial layer on the silicon carbide substrate may be adjusted so that the silicon carbide active layers or layer sequences produced involve little or no basal area dislocations. Silicon carbide devices manufactured by the above-described method of producing silicon carbide epitaxial layers may have, for example, basal plane dislocation densities of less than 10 cm -2 or even less than 3 cm -2 .
ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- - US 7018554 B2 [0006] - US 7018554 B2 [0006]
Claims (31)